SMOOTHING PHOSPHORS FOR AC LED LIGHTING

BACKGROUND OF INVENTION

These teachings relate generally to smoothing phosphors for AC LED lighting, and more particularly to smoothing phosphors being aluminate-based phosphors co-doped with at least manganese, Mn²⁺, and silicon, Si⁴⁺, that substantially reduce flicker of an AC LED (or array of AC LEDs) by way of prolonging the light emission time of an AC LED (or array of AC LEDs) during a ½ cycle response to a phase change of the alternating current.

As diodes, LEDs are direct current components and thus, when subjected to a sinusoidally alternating current (AC), such as provided by typical AC mains, LEDs will only produce light emission during half of the cycle resulting in significant loss of electrical efficiency. In order to take advantage of the full cycle, and therefore increasing electrical efficiency, numerous methods have been employed. For example, LED circuits are designed as rectifiers that invert the phase of the negative half of the cycle, making the full cycle of AC available for use with the LED. Alternatively, circuits are constructed with multiple LEDs such that the full cycle can be used for illumination. In light of these numerous methods employed, such AC-LED chips (or simply “AC-LEDs”) are becoming more attractive for use in low-cost general illumination. However, the light produced by AC-LEDs exhibit an unacceptably high degree of flicker, caused by the rapid alteration in polarity at mains frequency that requires the current to become zero at the points of inflection of the cycle. Since this frequency is typically around 50-60 Hz, this flicker can be irritating, particularly in the case of indoor lighting applications. Shifting the phase of one or more AC LEDs in an array is one possible method in reducing the flicker, but these electronic modifications introduce reactive power consumption, reducing the component's power factor and increasing harmonic distortion in the circuit. Thus, there is a need for alternative methods in addressing the existence of flicker with AC LEDs.

Currently, photoluminescent materials are used in the construction of LEDs to modify the emission by way of energy conversion, so as to provide longer wavelengths then are naturally emitted by the semiconductor chip. For example, cerium doped yttrium aluminum garnet phosphors are used to produce cool white LEDs. Characteristics of color quality, such as correlated color temperature and color rendering index, can be controlled by varying the amount and type of phosphor used for the energy conversion. Unfortunately, most phosphors currently employed with LEDs have an emission decay that is much faster, by several orders of magnitude, than the frequency of the flicker, and therefore are not useful in the reduction of flicker that results in AC LEDs.

There is, therefore, a need for phosphors which are capable of providing a longer emission decay thereby extending the light emission time of an AC LED (or array of AC LEDs) during a ^IA cycle response to a phase change of the AC. It is further desirable to provide such phosphors that not only modify the emission of an AC LED (or array of AC LEDs), but also substantially reduce the flicker produced.

SUMMARY OF INVENTION

The present teachings provide for smoothing phosphors for AC LED lighting that are capable of prolonging the light emission time of an AC LED (or array of AC LEDs) during a ½ cycle response to a phase change of the AC, thereby substantially reducing flicker. The smoothing phosphor of the present teachings comprises a matrix represented by the formula: M_(l-k-r-v)X_(m-p)Al_{2(n-0.5x-0.5y)}O_{3(n-0.5x-0.5y)}: Mn_(x+p),O_(x+p), Si_yO_2y, Eu_k, R_r, Li_vwherein M is at least one of La₂O₃, Ce₂O₃, Gd₂O₃, Lu₂O₃, Ba₂OF₂, Sr₂OF₂, Ca₂OF₂, Ba₂OCl₂, Sr₂OCl₂, Ca₂OCl₂, BaO, SrO, CaO, or ZnO; provided that when M comprises BaO, SrO, CaO, or ZnO, M does not comprise La₂O₃, Ce₂O₃, Gd₂O₃, Lu₂O₃, Ba₂OF₂, Sr₂OF₂, Ca₂OF₂, Ba₂OCl₂, Sr₂OCl₂, or Ca₂OCl₂; X is at least one of MgO or ZnO; R is at least one of Sm, Pr, Tb, Dy, Er, or Ho; m=0 to 2; n=4 to 11; x=0.005 to 1; y=0.005 to 1; p=0 to 1; k=0 to 0.2; r=0 to 0.2; and v=0 to 0.2.

BRIEF DESCRIPTION OF THE DRAWINGS

The present teachings are illustratively shown and described in reference to the accompany drawings, in which

FIG. 1 shows the emission and excitation spectra of LaAl₁₁O₁₈:Mn_0.15, showing that La³⁺ aluminate compounds are suitable hosts for Mn²⁺ for use as smoothing phosphors in blue AC LED lighting applications;

FIG. 2 shows the emission and excitation spectra (a) of an exemplary smoothing phosphor represented by the formula LaAl₁₁O₁₈:Mn_0.20, Si_0.20, compared to the excitation and emission spectra (b) of LaAl₁₁O₁₈:Mn_0.20to illustrate the impact of charge compensation with Si⁴⁺;

FIG. 3 shows a series of emission spectra of exemplary smoothing phosphors represented by the formula LaAl₁₁O₁₈:Mn_x, Si_y, where the Mn²⁺ content, x, and the Si⁴⁺ content, y, was varied as follows, x=y=0.075, 0.175, 0.20, 0.275, 0.30, 0.35, and 0.425, to investigate the role that Mn²⁺content has on emission intensity;

FIG. 4 shows the excitation and emission spectra of an exemplary smoothing phosphor having the formula LaAl₁₁O₁₈:Mn_0.425, Si_0.425to illustrate the red emission bands produced from Mn-Mn pairs;

FIG. 5 shows the excitation and emission spectra of an exemplary smoothing phosphor having the formula LaAl₁₁O₁₈:Mn_0.30, Si_0.30, SI_0.03to illustrate the effect of further co-doping with Sm³⁺;

FIG. 6 shows the excitation and emission spectra of an exemplary smoothing phosphor having the formula LaAl₁₁O₁₈:Mn_0.30, Si_0.30, EU_0.10to investigate the impact on excitation intensity of Mn²⁺ emission with the further co-doping of Eu²⁺;

FIG. 7 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula CeAl₁₁O₁₈:Mn_0.28, Si_0.28;

FIG. 8A shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula BaAl₁₁O₁₇F:Mn_0.30, Si_0.30;

FIG. 8B shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula BaAl₁₁O₁₇F:Mn_0.30, Si_0.30, Eu_0.06;

FIG. 9 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula BaAl₁₁O₁₇Cl:Mn_0.30, Si_0.30;

FIG. 10 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula Ba_0.5Ca_0.5Al₁₁O₁₇F:Mn_0.20, Si_0.20;

FIG. 11 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula BaMg₂Al₁₆O₂₇:Mn_0.85, Si_0.28;

FIG. 12 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula BaMg₂Al₁₆O₂₇:Mn_0.85, Si_0.28, Eu_0.10;

FIG. 13 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula BaAl₁₂O₁₉:Mn_0.30, Si_0.30; and

FIG. 14 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula SrAl₁₂O₁₉:Mn_0.30, Si_0.30.

DETAILED DESCRIPTION OF THE INVENTION

The present teachings are directed to the creation of smoothing phosphors for AC LED lighting that are capable of reducing flicker of an AC LED (or array of LEDs). The smoothing phosphor of the present teachings comprises a matrix represented by the general formula: M_(l-k-r-y)X_(m-p)Al_{2(n-0.5x-0.5y)}O_{3(n-0.5x-0.5y)}:Mn_(x+p)O_(x+p), Si_yO_2y, EU_k, R_r, Li_v, wherein M is at least one of La₂O₃, Ce₂O₃, Gd₂O₃, Lu₂O₃, Ba₂OF₂, Sr₂OF₂, Ca₂OF₂, Ba₂OCl₂, Sr₂OCl₂, Ca₂OCl₂, BaO, SrO, CaO, or ZnO; provided that when M comprises BaO, SrO, CaO, or ZnO, M does not comprise La₂O₃, Ce₂O₃, Gd₂O₃, Lu₂O₃, Ba₂OF₂, Sr₂OF₂, Ca₂OF₂, Ba₂OCl₂, Sr₂OCl₂, or Ca₂OCl₂; X is at least one of MgO or ZnO; R is at least one of Sm, Pr, Tb, Dy, Er, or Ho; m=0 to 2; n=4 to 11; x=0.005 to 1; y=0.005 to 1; p=0 to 1; k=0 to 0.2; r=0 to 0.2; and v=0 to 0.2.

When an LED (or array of LEDs) are directly pumped or operated from AC, typically 110V/60 Hz or 230V/50 Hz, the instantaneous AC voltage applied has to exceed a minimum threshold value in order for current to flow through the LED (or array of LEDs), making the LED turn on and emit light. Given the AC LED (or array of AC LEDs) minimum threshold value, along with the sinusoidal waveform of AC, the AC LED turns on and off at the same frequency, causing the AC LED (or array of AC LEDs) to flicker when directly connected to an AC power source, thereby affecting the observed quality of light produced.

Flicker is the periodic change in the instantaneous light output of a light source. Flicker is measured using two different metrics, i.e. percent flicker and flicker index. Percent flicker, sometimes referred to as “modulation index”, is defined as the ratio of the maximum light intensity output value minus the minimum light intensity output value divided by the sum of the maximum and minimum light intensity output values for one AC cycle. Flicker index is defined as the ratio of the area under the light intensity output curve above the average light intensity output value to the total area of the light intensity output curve for one AC cycle. Although both metrics for flicker measurement are relative measures of the cyclic variation in light output of a light source, percent flicker does not take into account the waveform of the light source, nor the duty cycle, whereas flicker index does. Nonetheless, the presence of flicker can substantially impact the quality of light produced and thus perceived by a human observer.

By employing smoothing phosphors in accordance with the present invention, the light emission time of the AC LED (or array of LEDs) is prolonged during a ½ cycle response to a phase change of the AC such that flicker can be reduced. Generally speaking, an AC LED operating at 50 to 120 Hz has an off period that is normally about 1 ms to about 10 ms. When a smoothing phosphor is used, the AC LED continues to emit light during this off period such that the flicker, otherwise produced, is substantially minimized. In order for a smoothing phosphor to be effective in the reduction of flicker of an AC LED, the smoothing phosphor should have an emission lifetime that is substantially similar to the off period of the AC LED. Ions having such an emission lifetime include Mn²⁺, Fe³⁺, 4f rare earth ions, or ions with s electrons in the out-shell, such as Bi³⁺ (6s²), Tl⁺ (6s²), Sb³⁺ (5s²), S_n²⁺ (5_s²), all of which involve spin-forbidden transitions, and thus provide a longer lifetime of emission. However, based on the emission spectrum of an AC LED, along with additional requirements for practical applications of AC LED lighting, Fe³⁺, 4f rare earth ions, or ions with s electrons in the out-shell are not suitable.

In general, Mn²⁺ ions emit light that is characteristically in the green or red region of the electromagnetic spectrum. Mn²⁺ has 5 electrons in its 3d shell, labeled as 3d⁵. The ground state of Mn²⁺ is S-state with zero total orbital angular momentum, total spin 5/2, and the spin multiplet, indicated as a superscript, of 6, thus labeled as ⁶S₀. The first excited state of free Mn²⁺ ions is ⁴G. Above ⁴G, are ⁴P, ⁴D, ²I, ⁴F, ²D, etc. In the cubic crystal field, ⁶S₀is represented as ⁶A₁. The excited state ⁴G, having 9-fold orbital degeneracy, is split into ⁴T₁, ⁴T₂, ⁴E, and ⁴A₁in the cubic representation. A is an orbital singlet, E is a doublet, and Ts are triplets. It can be noticed that all spin-multiplets (S=4 or 2) of excited states are different from the ground state (S=6). Therefore, all the electronic transitions of Mn²⁺ are spin forbidden and thus illustrate an emission lifetime of Mn²⁺ that is substantially similar to the off period of an AC LED (or array of AC LEDs).

Furthermore, this also implies that the electronic transition probability of Mn²⁺ is relatively low, and thus the excitation of Mn²⁺ with that of AC LED emission is weaker than that of a spin allowed transition. To aid in the excitation of Mn²⁺ with that of AC LED emission, a host matrix with strong absorption of AC LED emission through Mn²⁺ was investigated. In addition, the host matrix should also entail a strong, broad, efficient emission in the spectral emission range of Mn²⁺, an emission lifetime that is also substantially similar to the off period of the AC LED, and have a high concentration quenching onset level of the emissive Mn²⁺ ions. In light of the foregoing characteristics, it was determined that suitable host matrices for Mn²⁺ is that of aluminate-based compounds having the general formula: M_(l-k-r-v)X_(m-p)Al_{2(n-0.5x-0.5y)}O_{3(n-0.5x-0.5y)}, wherein M is at least one of La₂O₃, Ce₂O₃, Gd₂O₃, Lu₂O₃, Ba₂OF₂, Sr₂OF₂, Ca₂OF₂, Ba₂OCl₂, Sr₂OCl₂, Ca₂OCl₂, BaO, SrO, CaO, or ZnO; provided that when M comprises BaO, SrO, CaO, or ZnO, M does not comprise La₂O₃, Ce₂O₃, Gd₂O₃, Lu₂O₃, Ba₂OF₂, Sr₂OF₂, Ca₂OF₂, Ba₂OCl₂, Sr₂OCl₂, or Ca₂OCl₂; X is at least one of MgO or ZnO; m=0 to 2; n=4 to 11; x=0.005 to 1; y=0.005 to 1; p=0 to 1; k=0 to 0.2; r=0 to 0.2; and v=0 to 0.2. These suitable host matrices have hexagonal symmetry and contain Al-O spinel blocks, in which Al³⁺ occupies either tetrahedral or octahedral sites of the spinel blocks. Thus, when doped with Mn²⁺, M³⁺ of the host matrix is partially or fully replaced with that of Mn²⁺.

FIG. 1 shows the excitation and emission spectrum of LaAl₁₁O₁₈:Mn_0.15under 450 nm blue LED excitation, in which all excitation peaks are labeled in cubic field representations. The excitation is strong at around 450 nm with spectral width at around 20 nm and the peak of the emission is at around 520 nm, which is characteristically in the green region of the electromagnetic spectrum. This shows that certain Mn²⁺ doped aluminate phosphors are suitable for use in blue AC LED lighting applications.

It was further determined that the Mn²⁺ doped aluminate phosphors, possess a charge defect as a result of the oxygen vacancies created by the partial or full substitution of Mn²⁺ for that of Al³⁺. A charge defect refers to defects in the crystalline matrix of a phosphor as a result of the replacement, partial or full, of one atom for another in the matrix that is not an exact match in charge (valence state), thereby resulting in altered photoluminescent characteristics, such as e.g., decrease of emission intensity. Thus, in order to minimize the charge defects produced by such substitution, the smoothing phosphors of the present teachings are also further co-doped with Si⁴⁺. As an example, FIG. 2 shows the excitation and emission spectra (a) of an exemplary smoothing phosphor represented by the formula LaAl₁₁O₁₈:Mn_0.20, Si_0.20compared to the excitation and emission spectra (b) of LaAl₁₁O₁₈:Mn_0.20under 450 nm blue LED excitation, to investigate the effect the incorporation of Si⁴⁺ has on emission intensity. The emission intensity of LaAl₁₁O₁₈:Mn_0.20, Si_0.20is more than approximately 20% greater than that of LaAl₁₁O₁₈:Mn_0.20. This further illustrates the impact the presence of charge defect(s) within the crystalline matrix of a phosphor has on emission intensity and the effectiveness of charge compensation.

The concentration of Mn²⁺ within the smoothing phosphor should be as a high as possible to maximize the excitation intensity of Mn²⁺. However with too high Mn²⁺ content, concentration quenching can occur, thereby reducing the emission intensity of the smoothing phosphor. Thus, there is a balance that exists between the excitation intensity, the emission intensity, and Mn²⁺ content of the smoothing phosphor. The role that Mn²⁺ content has on the emission intensity of the smoothing phosphors of the present teachings was investigated. FIG. 3 depicts a series of emission spectra of exemplary smoothing phosphors represented by the formula LaAl₁₁O₁₈:Mn_x, Si_r, under 450 nm blue LED excitation, where the Mn²⁺ content, x, and the Si⁴⁺ content, y, was varied as follows, x=y=0.075, 0.175, 0.20, 0.275, 0.30, 0.35, and 0.425. As illustrated in FIG. 3, the maximum emission intensity reached before concentration quenching occurs is shown to be at a Mn²⁺ content of about 0.30 mols. Furthermore, as shown in FIG. 3, as concentration quenching begins to occur, a decrease in emission intensity results.

FIG. 4 is the excitation and emission spectra of an exemplary smoothing phosphor having the formula LaAl₁₁O₁₈:Mn_0.425, Si_0:425. As seen in FIG. 4, at a Mn²⁺ content of about 0.425 mol, the emission peak at about 675 nm becomes strong and broad, which can be beneficial in white lighting applications. The emission intensity increases nonlinearly and rapidly with Mn²⁺ content. Therefore, the emission of Mn²⁺ in the red region of the electromagnetic spectrum is not due to other high field sites, but rather is presumably due to Mn-Mn pairs. The number of pairs should increase as squared concentration. It should be noted that in some instances where the contribution of Mn²⁺ emission in the red region of the electromagnetic spectrum is considered, concentration quenching resulting in the reduction of emission intensity at about 520 nm may not substantially impact the overall emission intensity of the smoothing phosphor. Furthermore, it should be noticed that the excitation spectrum of the red emission band is similar to the excitation spectrum of single Mn²⁺ ions, and therefore indicates that the emission of the Mn-Mn pairs results from the energy transfer through single-Mn²⁺ ions, along with having an emission lifetime as long as single-Mn²⁺ ions.

Alternatively or in addition to the Mn-Mn pairs emission, the smoothing phosphors of the present teachings may also emit light in the red region of the electromagnetic spectrum with the further co-doping of rare earths such as Sm³⁺, Tb³⁺, Dy³⁺, Er³⁺, or Ho³⁺. For example, FIG. 5 illustrates the excitation and emission spectra of an exemplary smoothing phosphor having the formula LaAl₁₁O₁₈:Mn_0.30, Si_0.30, Sm_0.03. As seen in FIG. 5, the presence of Sm³⁺ adds three narrow emission peaks at around 560 nm, 598 nm, and 645 nm. It should be noted that the excitation spectrum monitoring at Sm³⁺ emission peaks is similar to that of the Mn²⁺ excitation spectrum, thereby implying that the Sm³⁺ emission results from energy transfer from Mn²⁺, along with the Sm³⁺ emission lifetime being substantially similar to the emission lifetime of Mn²⁺. In other words, Sm³⁺ not only contributes to the smoothing phosphors emission of light in the red region of the electromagnetic spectrum, which is beneficial in white lighting applications, but also to the reduction of flicker of an AC driven LED (or array of LEDs). It should be noted that in some instances, the smoothing phosphors of the present teachings may also be further co-doped with Li⁺ to function as a charge compensator for the charge defect that may result with the presence of Sm³⁺.

In another aspect of the present teachings, the smoothing phosphors may be further co-doped with Eu²⁺ so as to enhance the excitation intensity, and thus the emission intensity, of Mn²⁺. The emission spectrum of Eu²⁺ overlaps with the excitation spectrum of Mn²⁺, therefore it is possible through energy transfer from Eu²⁺ to Mn²⁺ to increase excitation in the spectral range of about 360 to 410 nm of the smoothing phosphors of the present teachings. As an example, FIG. 6 illustrates the excitation and emission spectra of an exemplary smoothing phosphor having the formula LaAl₁₁O₁₈:Mn_0.30, Si_0.30, Eu_0.10under 450 nm blue LED excitation. As shown in FIG. 6, the energy transfer that occurs between Eu²⁺ and Mn²⁺ is efficient, thereby increasing the excitation intensity of the Mn²⁺ emission in the spectral range of about 365-380 nm. This increase of Mn²⁺ excitation intensity indicates that such material is an exemplary smoothing phosphor that is also suitable for use in UV AC LED lighting applications.

Other exemplary smoothing phosphors in accordance with the present teachings are illustrated in FIGS. 7-10, in which La₂O₃is partially or fully replaced with at least one of Ce₂O₃, Gd₂O₃, Lu₂O₃, Ba₂OF₂, Sr₂OF₂, Ca₂OF₂, Ba₂OCl₂, Sr₂OCl₂, or Ca₂OCl₂. FIG. 7 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula CeAl₁₁O₁₈:Mn_0.28, Si_0.28under 450 nm blue LED excitation. The strong excitation peak at about 310 nm originates from Ce³⁺5d transition. Since this excitation peak appears in the excitation spectrum of Mn²⁺ emission, energy transfer from Ce³⁺ to Mn²⁺ is indicated. Furthermore, when such smoothing phosphor was pumped at the excitation peak of Ce³⁺ at about 310 nm, the residual weak emission from Ce³⁺ that results also indicates that energy transfer from Ce³⁺ to Mn²⁺ occurred. FIG. 8A shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula BaAl₁₁O₁₇F:Mn_0.30, Si_0.30under 450 nm blue LED excitation. It can be seen that a strong excitation peak appears at about 450 nm which is similar to the exemplary smoothing phosphor lanthanum aluminate co-doped with Mn²⁺ and Si⁴⁺. FIG. 8B shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula BaAl₁₁O₁₇F:Mn_0.30, Si_0.30, Eu_0.06under 450 nm blue LED excitation. It can be seen that a strong excitation peak appears at about 330 nm, and strong energy transfer from Eu²⁺ to Mn²⁺ occurs. FIG. 9 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula BaAl₁₁O₁₇Cl:Mn_0.30, Si_0.30under 450 nm blue LED excitation. FIG. 10 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula Ba_0.5Ca_0.5Al₁₁O₁₇F:Mn_0.20, Si_0.20under 450 nm blue LED excitation.

Other exemplary smoothing phosphors in accordance with the present teachings are illustrated in FIGS. 11-14, in which La₂O₃is fully replaced with at least one of BaO, SrO, CaO, or ZnO. In other words, in instances where at least one of BaO, SrO, CaO or ZnO is incorporated into the host matrix of the smoothing phosphor of the present teachings, La₂O₃, Ce₂O₃, Gd₂O₃, Lu₂O₃, Ba₂OF₂, Sr₂OF₂, Ca₂OF₂, Ba₂OCl₂, Sr₂OCl₂, or Ca₂OCl₂are not present within the host matrix. FIG. 11 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula BaMg₂Al₁₆O₂₇:Mn_0.85, Si_0.28under 450 nm blue LED excitation. The emission peak is located at about 520 nm, which is similar to the exemplary smoothing phosphor lanthanum aluminate co-doped with Mn²⁺ and Si⁴⁺, and the excitation peak at about 450 nm remains strong, but a broad and strong excitation band of Mn²⁺ is at about 330 nm. FIG. 12 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula BaMg₂Al₁₆O₂₇:Mn_0.85, Si_0.28, Eu_0.10under 450 nm blue LED excitation. It can be seen that a strong and broad excitation band of Eu²⁺ overlaps with the Mn²⁺ excitation band of about 330 nm and extends to about 410 nm. The emission peak at about 520 nm is measured by pumping the overlapped band at about 400 nm. Thus, when compared to the excitation peak of Mn²⁺ at about 450 nm, the intensity of the emission peak indicates that the energy transfer from Eu²⁺ to Mn²⁺ contributes to most of the emission of the Mn²⁺ ions. This increase of Mn²⁺ excitation intensity indicates that such exemplary smoothing phosphor is also suitable for use in UV AC LED lighting applications. FIG. 13 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula BaAl₁₂O₁₉:Mn_0.30, Si_0.30under 450 nm blue LED excitation. The strongest excitation peak is located at about 450 nm, which is similar to the smoothing phosphor lanthanum aluminate co-doped with Mn²⁺ and Si⁴⁺. FIG. 14 shows the emission and excitation spectra of an exemplary smoothing phosphor having the formula SrAl₁₂^O₁₉:Mn_0.30, Si_0.30under 450 nm blue LED excitation. Similar to that of FIG. 13, the strongest excitation peak of this exemplary smoothing phosphor is located at about 450 nm.

A number of methods may be used to synthesize the smoothing phosphors of the present teachings such as, liquid mixing methods, solid chemical reaction methods, etc. Liquid mixing methods include methods such as co-precipitation and sol-gel techniques. In solid chemical reaction methods, a flux, such as H₃BO₃or B₂O₃, is used to stimulate the solid chemical reaction. A solid chemical reaction method may include admixing various starting materials in a predetermined ratio and pre-sintering them in a furnace, followed by grinding and sintering in the furnace at a higher temperate. For example in instances of lab scale, one method may include weighing the starting materials of the smoothing phosphor into a weighing dish, followed by admixing the materials and grinding into a mortar with a pestle until uniform. The ground material is then placed in an alumina combustion boat and placed in an oven at around 900° C. in air or in a forming gas mixture of 97% N₂, and 3% H₂at a rate of 50 cm³/min for four hours. The material is then cooled and ground again in a mortar with a pestle, followed by again placing the material into an alumina combustion boat and sintered at around 1350° C. to 1450° C. for four hours in the forming gas mixture of 97% N₂and 3% H₂at a rate of 50 cm³/min. The material is then cooled and ground to a powder of the desired particle size to yield a smoothing phosphor in accordance with the present teachings.

For the purposes of describing and defining the present teachings, it is noted that the term “substantially” is utilized herein to represent the inherent degree of uncertainty that may be attributed to any quantitative comparison, value, measurement or other representation. The term “substantially” is also utilized herein to present the degree by which a quantitative representation may vary from a stated reference without resulting in a change in the basic function of the subject matter at issue.

Although the teachings have been described with respect to various embodiments, it should be realized that these teachings are also capable of a wide variety of further and other embodiments within the spirit and scope of the appended disclosure.

	Number	Date	Country
Parent	14051488	Oct 2013	US
Child	15620977		US

SMOOTHING PHOSPHORS FOR AC LED LIGHTING

Information

Publication Number

Date Filed

Date Published

Inventors

Original Assignees

CPC

International Classifications

Abstract

Description

Claims

Continuations (1)