Soft magnetic film of iron and process of formation thereof

FIELD OF THE INVENTION
This invention relates to soft magnetic material and, more particularly, to a thin film of iron preferable for a magnetic head of a magnetic recording system.
DESCRIPTION OF THE RELATED ART
High density magnetic recording mediums are available for a magnetic recording system, and the recording density tends to increase. Accordingly, the magnetic head of the recording system is expected to have high saturation magnetic flux density and low coercive force. Soft magnetic materials are large in the saturation magnetic flux density and low in the coercive force, and are preferable for the magnetic head. Thin alloy films in the Ni--Fe system and in the Fe--Al--Si system as well as thin amorphous alloy films in the Co--Nb--Zr system are presently available, and those alloys achieve relatively high saturation magnetic flux density of the order of 1 tesla. However, the alloys are getting close to the limit, and it seems to be hard to further improve the saturation magnetic flux density. A soft magnetic material with the saturation magnetic flux density of about 2 tesla is required, and research and development efforts are now being made on a soft-magnetized iron thin film because of the highest saturation magnetic flux density in the transition metals as large as 2.1 tesla.
In order to improve the soft magnetic properties, it has been proposed to form a thin iron film with a micro crystal grain structure. The micro crystal grain structure is constructed by adding an additive of several per cent into iron or by laminating the thin iron film on an intermediate film. Another approach to improvement of the soft magnetic properties is to epitaxially grow a thin iron film on a small gallium arsenide substrate in a lattice mismatched fashion. Such an epitaxial growth is, by way of example, reported in Journal of Crystal Growth, 1987, vol. 81, page 524.
In general, a thin single crystalline iron film can achieve extremely high saturation magnetic flux density, because no additive is incorporated therein. Moreover, the single crystal is very stable, and is preferable for long service period. For this reason, the thin single crystalline iron film is more preferable than the thin iron films with the micro crystal grain structure. However, when a thin single crystalline iron film is epitaxially grown on a gallium arsenide film, iron is alloyed with gallium arsenide at the interface therebetween, and the saturation magnetic flux density is lowered.
SUMMARY OF THE INVENTION
It is therefore an important object of the present invention to provide a thin single crystalline iron film with a high saturation magnetic flux density which is excellent in soft magnetic properties.
It is also an important object of the present invention to provide a process of forming the thin single crystalline iron film.
To accomplish these objects, the present invention proposes to grow a thin single crystalline iron film on a single crystalline oxide substrate.
In accordance with one aspect of the present invention, there is provided a magnetic film structure comprising a) a substrate formed of single crystalline oxide and having a surface oriented to one of (100) direction, (110) direction and (111) direction, and b) a soft magnetic film formed of single crystalline iron grown over said surface of said substrate.
In accordance with another aspect of the present invention, there is provided a process of forming a magnetic film structure comprising the steps of, a) preparing a substrate formed of single crystalline oxide and having a surface oriented to one of (100) direction, (110) direction and (111) direction, b) creating vacuum ambience with pressure equal to or less than 10.sup.-8 torr around said substrate, and c) epitaxially grown iron on said surface of said substrate by using a source of iron with purity equal to or greater than 99.995 per cent.

BRIEF DESCRIPTION OF THE DRAWINGS
The features and advantages of the soft magnetic film of iron and the process of formation thereof according to the present invention will be more clearly understood from the following description taken in conjunction with the accompanying drawings in which:
FIG. 1 is a cross sectional view showing the structure of a magnetic film structure according to the present invention;
FIG. 2 is a view showing the arrangement of an electron beam evaporating system used for fabricating magnetic film structures according to the present invention;
FIG. 3 is a cross sectional view showing the structure of another magnetic film structure according to the present invention;
FIG. 4 is a cross sectional view showing the structure of yet another magnetic film structure according to the present invention; and
FIG. 5 is a cross sectional view showing the structure of yet another magnetic film structure according to the present invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS
First Embodiment
Referring first to FIG. 1 of the drawings, a soft magnetic film structure embodying the present invention comprises a substrate 1, and a soft magnetic film 2 epitaxially grown on the major (larger) surface of the substrate 1. The substrate 1 is formed of single crystalline magnesium oxide, and the soft magnetic film 2 is of single crystalline iron. The epitaxy is any one of the following orientations.
(1) major surface (001)// iron film (001), major surface [100]// iron film [110]
(2) major surface (110)// iron film (110), major surface [001]// iron film [110]
(3) major surface (111)// iron film (111), major surface [110]// iron film [100]
Although gallium arsenide used in the prior art structure reacts with iron at a relatively low temperature, the iron is not alloyed with the magnesium oxide at 650 degrees in centigrade, and, accordingly, the saturation magnetic flux density of the single crystalline iron for the soft magnetic film 2 is as large as a bulk body of iron. In other words, the soft magnetic film 2 is improved in soft magnetic properties.
A process sequence for fabricating the magnetic film structure starts with preparation of the substrate 1 of magnesium oxide and an electron beam evaporating system 3 shown in FIG. 2. The substrate 1 is placed in a vacuum chamber 3a of the electron beam evaporating system 3, and the vacuum chamber 3a is conducted with a cryopump 3b through a gate valve unit 3c. The cryopump 3b develops vacuum, and the pressure in the vacuum chamber 3a is decreased to or exceeds 10.sup.-8 torr. A heating unit (not shown) is provided on the wall defining the vacuum chamber 3a for developing the extremely high vacuum, and the pressure in the vacuum chamber 3a is monitored by means of a vacuum gauge 3d. In this process sequence, the vacuum chamber 3a is baked at 150 degrees in centigrade for 20 hours for developing the extremely high vacuum equal. However, no baking is carried out for creating a low vacuum ambience.
The substrate 1 is heated by another heating unit 3e, and the temperature of the substrate 1 is variable. Two electron beam evaporation sources 3f and 3g are provided in the vacuum chamber 3a, and one of the electron beam evaporation sources is filled with iron. Another electron beam evaporation source is used for forming a buffer film incorporated in a magnetic film structure implementing a second embodiment, and will be described hereinafter. The electron beam evaporation sources 3f and 3g are spaced apart from the substrate 1, and movable shutter plates 3h and 3i are provided on paths 3j and 3k between the electron beam evaporation sources 3f and 3g and the substrate 1. When the vacuum is well developed and the substrate 1 is heated to the appropriate temperature, one of the movable shutter plates 3h and 3i is removed from one of the paths for iron molecular flux, and the major surface of the substrate 1 is exposed to the iron molecular flux. Quartz oscillators 3m and 3n are provided in the vicinity of the paths 3j and 3k, and one of the quartz oscillators 3m and 3n monitors the depositing speed of iron. Upon completion of the deposition, the single crystal iron film is evaluated through reflection high energy electron diffraction with an electron beam 3p and a phosphor screen 3q.
After the evaluation of the single crystalline iron film 2, the magnetic film structure is taken out from the vacuum chamber 3a, and the soft magnetic properties are evaluated at room temperature. A vibrating sample magnetometer is used for measuring the saturation magnetic flux density and the coercive force.
Specimens 1 to 10 are produced through the process sequence described hereinbefore. The substrate 1 is of the magnesium oxide, and the major surface is oriented to (001) direction. The orientation (001) is equivalent to orientations (100) and (010). The purity of iron are varied from 99.9 per cent to 99.999 per cent, and the vacuum is changed between 1.times.10.sup.-7 torr and 9.times.10.sup.-10 torr. The iron is deposited to about 2000 angstroms on the major surface oriented to (001) direction. The deposition speed is varied from 0.01 angstrom per second to 5 angstroms per second, and the substrate 1 is further changed from 100 degrees to 650 degrees in centigrade. However, the soft magnetic properties are not affected by the deposition speed and the temperature of the substrate 1. Table 1 reports the purity, the vacuum, the epitaxy and the soft magnetic properties of specimens 1 to 10. In Table 1, when the soft magnetic film 2 is epitaxially grown on the substrate 1, the specimen is marked with "*". However, if not, the specimen is marked with "-", and the iron films are polycrystal or of an orientation film.
The reflection high energy electron diffraction results in the epitaxy of (001)Fe//(001)Substrate, [110]Fe//[100]Substrate, and an x-ray diffraction confirms the orientation.
TABLE 1______________________________________ Saturation magneticSpe- flux Coerciveci- Purity Vac. Orien- Epi- density forcemen (%) (torr) tation taxy (tesla) (oersted)______________________________________1 99.9 8 .times. 10.sup.-10 (100) -- 1.95 182 99.99 8 .times. 10.sup.-10 (100) -- 2.00 183 99.995 3 .times. 10.sup.-7 (100) -- 1.99 104 99.995 1 .times. 10.sup.-8 (100) * 2.05 1.25 99.995 5 .times. 10.sup.-9 (100) * 2.00 1.66 99.995 8 .times. 10.sup.-10 (100) * 2.02 1.77 99.999 1 .times. 10.sup.-7 (100) -- 1.98 128 99.999 1 .times. 10.sup.-8 (100) * 2.10 1.29 99.999 7 .times. 10.sup.-9 (100) * 2.08 1.310 99.999 9 .times. 10.sup.-10 (100) * 2.05 1.4______________________________________
As will be understood from Table 1, the soft magnetic films 2 of the single crystalline iron are epitaxially grown on the respective substrate in the vacuum ambience at or higher than 10.sup.-8 torr by using iron with purity not less than 99.995, and the soft magnetic films 2 have excellent soft magnetic properties. This is because of the fact that the high purity and the extremely high vacuum eliminate undesirable inhibition factor against movement of domain walls from the single crystalline iron films.
Using magnesium oxide substrates with major surfaces oriented to (001) direction, (110) direction and (111) direction, specimens 11 to 28 are produced through the process sequence, and the process parameters are similar to those of the specimens 1 to 10. Table 2 reports the results.
TABLE 2______________________________________ Saturation magneticSpe- flux Coerciveci- Purity Vac. Orien- Epi- density forcemen (%) (torr) tation taxy (tesla) (oersted)______________________________________11 99.9 3 .times. 10.sup.-6 (100) -- 1.93 2012 99.9 8 .times. 10.sup.-10 (100) -- 1.95 1813 99.99 4 .times. 10.sup.-7 (110) -- 1.97 2514 99.99 8 .times. 10.sup.-10 (100) -- 2.00 1815 99.995 3 .times. 10.sup.-7 (100) -- 1.99 1016 99.995 1 .times. 10.sup.-8 (100) * 2.05 1.217 99.995 1 .times. 10.sup.-8 (110) * 2.08 0.1018 99.995 1 .times. 10.sup.-8 (111) * 2.05 0.0719 99.995 5 .times. 10.sup.-9 (100) * 2.12 1.320 99.995 5 .times. 10.sup.-9 (110) * 2.00 0.1021 99.995 8 .times. 10.sup.-10 (111) * 2.02 0.0822 99.999 1 .times. 10.sup.-7 (100) -- 1.98 1223 99.999 1 .times. 10.sup.-8 (100) * 2.10 1.224 99.999 1 .times. 10.sup.-8 (110) * 2.06 0.0925 99.999 1 .times. 10.sup.-8 (111) * 2.08 0.0826 99.999 7 .times. 10.sup.-9 (100) * 2.10 1.427 99.999 7 .times. 10.sup.-9 (110) * 2.08 0.0928 99.999 9 .times. 10.sup.-10 (111) * 2.05 0.09______________________________________
The reflection high energy electron diffraction shows the following orientations, and the x-ray diffraction confirms the orientations.
(1) (001)Fe//(001)Substrate, [110]Fe//[100]Substrate
(2) (110)Fe//(110)Substrate, [110]Fe//[001]Substrate
(3) (111)Fe//(111)Substrate, [100]Fe//[110]Substrate
As will be understood from Table 1, the soft magnetic films 2 of the single crystalline iron are epitaxially grown on the respective substrate in the vacuum ambience at or higher than 10.sup.-8 torr by using iron with purity not less than 99.995, and the soft magnetic films 2 have excellent soft magnetic properties. Therefore, the magnetic film structure shown in FIG. 1 is preferable for a magnetic head, and the magnetic head is available for a magnetic recording system for an extremely high density magnetic recording medium. Moreover, Table 2 further teaches us that the substrates 1 with the major surfaces in (110) and (111) directions drastically decrease the coercive force rather than the substrate 1 with the major surface in (100) direction, and are, accordingly, conducive to further improvement of the soft magnetic properties.
Second Embodiment
Turning to FIG. 3 of the drawings, another magnetic film structure embodying the present invention largely comprises a substrate 4 formed of single crystalline strontium titanate, and a soft magnetic film 5 of single crystalline iron epitaxially grown on the major surface of the substrate 4. The epitaxy is any one of the following orientations.
(1) major surface (001)//iron film (001), major surface [100]// iron film [110]
(2) major surface (110)//iron film (110), major surface [001]// iron film [110]
(3) major surface (111)//iron film (111), major surface [110]// iron film [100]
The iron is also not alloyed with the strontium titanate at 650 degrees in centigrade, and, accordingly, the saturation magnetic flux density of the single crystalline iron for the soft magnetic film 2 is as large as a bulk body of iron. In other words, the soft magnetic film 2 is improved in soft magnetic properties.
Using the process sequence applied to the first embodiment, specimens 29 to 46 are produced. The substrates 4 are formed of strontium titanate expressed by the molecular formula of SrTiO.sub.3, and the major surfaces are oriented to (001) direction, (110) direction and (111) direction. The results are summarized in Table 3.
The epitaxial soft magnetic films 5 with excellent soft magnetic properties are produced under the vacuum ambience at or higher than 10.sup.-8 torr in so far as the purity is not less than 99.995 per cent. Moreover, the soft magnetic films 5 of the single crystalline iron are epitaxially grown on the respective substrate in the vacuum ambience at or higher than 10.sup.-8 torr by using iron with purity not less than 99.995, and the soft magnetic films 5 have excellent soft magnetic properties. Therefore, the magnetic film structure shown in FIG. 3 is preferable for a magnetic head, and the magnetic head is available for a magnetic recording system for an extremely high density magnetic recording medium.
TABLE 3______________________________________ Saturation magneticSpe- flux Coerciveci- Purity Vac. Orien- Epi- density forcemen (%) (torr) tation taxy (tesla) (oersted)______________________________________29 99.9 3 .times. 10.sup.-7 (100) -- 1.92 2330 99.9 8 .times. 10.sup.-10 (100) -- 1.90 1931 99.99 4 .times. 10.sup.-7 (110) -- 1.95 2232 99.99 8 .times. 10.sup.-10 (100) -- 1.99 1833 99.995 3 .times. 10.sup.-7 (100) -- 2.00 934 99.995 1 .times. 10.sup.-8 (100) * 2.03 1.335 99.995 1 .times. 10.sup.-8 (110) * 2.00 0.0936 99.995 1 .times. 10.sup.-8 (111) * 2.02 0.0837 99.995 5 .times. 10.sup.-9 (100) * 2.00 1.338 99.995 5 .times. 10.sup.-9 (110) * 2.01 0.0639 99.995 8 .times. 10.sup.-10 (111) * 2.05 0.0740 99.999 1 .times. 10.sup.-7 (100) -- 1.99 1841 99.999 1 .times. 10.sup.-8 (100) * 2.08 1.442 99.999 1 .times. 10.sup.-8 (110) * 2.09 0.0843 99.999 1 .times. 10.sup.-8 (111) * 2.01 0.0744 99.999 3 .times. 10.sup.-9 (100) * 2.03 1.345 99.999 3 .times. 10.sup.-9 (110) * 2.05 0.0846 99.999 7 .times. 10.sup.-10 (111) * 2.10 0.08______________________________________
Using the iron with purity not less than 99.995 per cent in the vacuum ambience at or higher than 10.sup.-8 torr, the soft magnetic properties are surely improved. Table 3 further teaches us that the substrates 4 with the major surfaces in (110) and (111) directions drastically decrease the coercive force rather than the substrate with the major surface in (100)direction, and are, accordingly, conducive to further improvement of the soft magnetic properties.
Third Embodiment
Turning to FIG. 4 of the drawings, yet another magnetic film structure embodying the present invention comprises a substrate 6, a buffer film 7 epitaxially grown on the major surface of the substrate 6, and a soft magnetic film 8 epitaxially grown on the buffer film 7. The substrate 6 is formed of single crystalline magnesium oxide or single crystalline strontium titanate, and the buffer film 7 is formed of single crystalline chromium. The magnetic film 8 is made of single crystalline iron. Although iron is mismatched with magnesium oxide or with strontium titanate at 3.76 per cent or at 3.80 per cent, the buffer film 7 decreases the mismatching rate. In fact, iron is mismatched with chromium at only 0.45 per cent, and, for this reason, the buffer film 7 is effective against the lattice mismatch. The smaller the lattice defect is, the better the soft magnetic properties are. Therefore, if the soft magnetic film 8 is relatively thin, the buffer film 7 is preferable for the soft magnetic properties.
If the substrates 6 with the respective major surfaces in (100), (110) and (111) directions and the buffer films 7 are respectively formed of single crystalline magnesium oxide and chromium, the magnesium oxide and the chromium are fallen into the following relation.
(001)Cr// (001)Substrate, [110]Cr// [100]Substrate
(110)Cr// (110)Substrate, [110]Cr// [001]Substrate
(111)Cr// (111)Substrate, [100]Cr// [110]Substrate
The iron are epitaxially grown on the chromium with the crystal faces and the orientations parallel to each other. When strontium titanate substrates 6 are used instead of the magnesium oxide, the above epitaxial relation is also established between the substrates 6 and the buffer films 7.
A process sequence for fabricating the magnetic film structure implementing the third embodiment is similar to that of the first embodiment except for usage of the two electron beam evaporation sources 3f and 3g shown in FIG. 2. Namely, one of the electron beam evaporation sources 3f and 3g is filled with high purity iron, and the other electron beam evaporation source is filled with chromium. Specimens 47 to 56 are produced as follows. The chromium is evaporated in the presence of electron beam, and is grown in high vacuum ambience to thickness of about 1000 angstroms on the substrates 6 heated at 350 degrees to 700 degrees in centigrade. The evaporation speed is regulated to 0.05 angstrom per second to 1 angstrom per second. Although the buffer film 7 is grown by using another process such as a sputtering technique, it is desirable to grow the buffer film 7 in a chamber used for epitaxial growth of iron.
After the growth of the buffer films 7 of chromium, the soft magnetic films 8 are epitaxially grown to thickness of about 2000 angstroms on the single crystalline chromium buffer films 7 with the respective major surfaces of (100), (110) and (111) directions. The vacuum ambience and the purity of the iron are changed from 2.times.10.sup.-7 torr to 9.times.10.sup.-10 and from 99.9 per cent to 99.999 per cent. The evaporation speed is changed from 0.01 angstrom per second to 5 angstroms per second, and the substrate 6 is heated to 100 degrees to 650 degrees in centigrade. However, the soft magnetic properties are not affectable with the evaporation speed and the temperature of the substrate 6.
The epitaxial relation between the single crystalline chromium buffer films 7 and the soft magnetic films 8 of iron is confirmed by using the reflection reflection high energy electron diffraction as well as the x-ray diffraction. The crystal faces and orientations of the single crystalline soft magnetic films 8 of iron are surely in parallel to the crystal faces and orientations of the single crystalline chromium buffer films 7.
TABLE 4______________________________________ Saturation magneticSpe- flux Coerciveci- Purity Vac. Orien- Epi- density forcemen (%) (torr) tation taxy (tesla) (oersted)______________________________________47 99.9 8 .times. 10.sup.-10 (100) -- 1.90 2048 99.99 9 .times. 10.sup.-10 (100) -- 1.90 1949 99.995 3 .times. 10.sup.-7 (100) -- 1.93 1450 99.995 1 .times. 10.sup.-8 (100) * 1.99 1.651 99.995 5 .times. 10.sup.-9 (100) * 1.98 1.752 99.995 7 .times. 10.sup.-10 (100) * 1.95 1.553 99.999 2 .times. 10.sup.-7 (100) -- 1.95 1054 99.999 1 .times. 10.sup.-8 (100) * 1.98 1.455 99.999 2 .times. 10.sup.-9 (100) * 1.97 1.856 99.999 8 .times. 10.sup.-10 (100) * 1.95 2.0______________________________________
As will be understood from Table 4, the soft magnetic films 8 of the single crystalline iron are epitaxially grown on the respective buffer films 7 in the vacuum ambience at or higher than 10.sup.-8 torr by using iron with purity not less than 99.995, and the soft magnetic films 2 have excellent soft magnetic properties.
Specimens 57 to 74 are fabricated through the same process sequence of the specimens 47 to 56 with the exception that the soft magnetic films 8 are grown to the thickness of about 1800 angstroms.
The epitaxial relation between the single crystalline chromium buffer films 7 and the soft magnetic films 8 of iron is confirmed by using the reflection high energy electron diffraction as well as the x-ray diffraction. The crystal faces and orientations of the single crystalline soft magnetic films 8 of iron are surely in parallel to the crystal faces and orientations of the single crystalline chromium buffer films 7.
TABLE 5______________________________________ Saturation magneticSpe- flux Coerciveci- Purity Vac. Orien- Epi- density forcemen (%) (torr) tation taxy (tesla) (oersted)______________________________________57 99.9 2 .times. 10.sup.-7 (100) -- 1.90 2858 99.9 8 .times. 10.sup.-10 (100) -- 1.90 2059 99.99 4 .times. 10.sup.-7 (110) -- 1.92 2360 99.99 9 .times. 10.sup.-10 (100) -- 1.90 1961 99.995 3 .times. 10.sup.-7 (100) -- 1.93 1462 99.995 1 .times. 10.sup.-8 (100) * 1.99 1.663 99.995 1 .times. 10.sup.-8 (110) * 2.00 0.1164 99.995 1 .times. 10.sup.-8 (111) * 1.97 0.1065 99.995 5 .times. 10.sup.-9 (100) * 1.93 1.766 99.995 5 .times. 10.sup.-9 (110) * 1.98 0.0967 99.995 7 .times. 10.sup.-10 (111) * 1.95 0.1068 99.999 2 .times. 10.sup.-7 (100) -- 1.95 1069 99.999 1 .times. 10.sup.-8 (100) * 1.98 1.470 99.999 1 .times. 10.sup.-8 (110) * 1.97 0.1071 99.999 1 .times. 10.sup.-8 (111) * 1.95 0.0972 99.999 2 .times. 10.sup.-9 (100) * 1.94 1.273 99.999 2 .times. 10.sup.-9 (110) * 1.97 0.0874 99.999 8 .times. 10.sup.-10 (111) * 1.95 0.08______________________________________
As will be understood from Table 5, the soft magnetic films 8 of the single crystalline iron are also epitaxially grown on the respective buffer films 7 in the vacuum ambience at or higher than 10.sup.-8 torr by using iron with purity not less than 99.995, and the soft magnetic films 8 have excellent soft magnetic properties. Table 5 further teaches us that the substrates 6 with the major surfaces in (110) and (111) directions drastically decrease the coercive force rather than the substrate with the major surface in (100) direction, and are, accordingly, conducive to further improvement of the soft magnetic properties.
Fourth Embodiment
Turning to FIG. 5 of the drawings, yet another magnetic film structure embodying the present invention comprises a substrate 11, a buffer film 12 epitaxially grown on the major surface of the substrate 11, and a soft magnetic film 13 epitaxially grown on the buffer film 12. The substrate 11 is formed of single crystalline magnesium oxide or single crystalline strontium titanate, and the buffer film 12 is formed of single crystalline silver. The major surface of the substrate 11 is oriented to (100) direction, (110) direction or (111) direction, and the magnetic film 13 is made of single crystalline iron. Although silver has a face centered cubic lattice, iron with [110] direction is mismatched with silver with [100] direction at only 0.80 per cent, and the buffer film 12 of silver is also effective against the lattice mismatch, and improves the soft magnetic properties when the soft magnetic film 13 is relatively thin.
If the substrates 11 with the respective major surfaces in (100), (110) and (111) directions and the buffer films 12 are respectively formed of single crystalline magnesium oxide and silver, the magnesium oxide and the silver are fallen into the following relation.
(001)Ag// (001)Substrate, [100]Ag // [100]Substrate
(110)Ag// (110)Substrate, [001]Ag// [001]Substrate
(111)Ag// (111)Substrate, [110]Ag// [110]Substrate
When strontium titanate substrates are used instead of the magnesium oxide, the above epitaxial relation is also established between the substrates 11 and the buffer films 12.
A process sequence for fabricating the magnetic film structure implementing the fourth embodiment is similar to that of the first embodiment except for usage of the two electron beam evaporation sources 3f and 3g shown in FIG. 2. Namely, one of the electron beam evaporation sources 3f and 3g is filled with high purity iron, and the other electron beam evaporation source is filled with silver. The silver is evaporated in the presence of electron beam, and is grown in high vacuum ambience to thickness of about 1000 angstroms on the substrates 11 heated at 100 degrees to 400 degrees in centigrade. The evaporation speed is regulated to 0.1 angstrom per second to 5 angstroms per second. Although the buffer film 12 is grown by using another process such as a sputtering technique, it is desirable to grow the buffer film 12 in a chamber used for epitaxial growth of iron.
After the growth of the buffer films 12 of single crystalline silver in (100), (110) and (111) directions, the soft magnetic films 13 are epitaxially grown to thickness of about 2000 angstroms on the single crystalline silver buffer films 12. The vacuum ambience and the purity of the iron are changed from 2.times.10.sup.-7 torr to 9.times.10.sup.-10 and from 99.9 per cent to 99.999 per cent. The evaporation speed is changed from 0.01 angstrom per second to 5 angstroms per second, and the substrate 11 is heated to 100 degrees to 650 degrees in centigrade. However, the soft magnetic properties are not affectable with the evaporation speed and the temperature of the substrate 11.
The epitaxial relation between the single crystalline silver buffer films 12 and the soft magnetic films 13 of iron is confirmed by using the reflection high energy electron diffraction as well as the x-ray diffraction as follows.
(001)Fe// (001)Ag, [110]Fe// [100]Ag
(110)Fe// (110)Ag, [110]Fe// [001]Ag
(111)Fe// (111)Ag, [100]Fe// [110]Ag
Specimens 75 to 92 thus produced are reported in Table 6.
TABLE 6______________________________________ Saturation magneticSpe- flux Coerciveci- Purity Vac. Orien- Epi- density forcemen (%) (torr) tation taxy (tesla) (oersted)______________________________________75 99.9 2 .times. 10.sup.-7 (100) -- 1.89 2276 99.9 9 .times. 10.sup.-10 (100) -- 1.90 1977 99.99 3 .times. 10.sup.-7 (100) -- 1.90 2878 99.99 8 .times. 10.sup.-10 (100) -- 1.93 2579 99.995 3 .times. 10.sup.-7 (100) -- 1.91 1480 99.995 1 .times. 10.sup.-8 (100) * 1.99 1.381 99.995 1 .times. 10.sup.-8 (110) * 1.96 0.1082 99.995 1 .times. 10.sup.-8 (111) * 1.95 0.0883 99.995 5 .times. 10.sup.-9 (100) * 1.96 1.484 99.995 5 .times. 10.sup.-9 (110) * 1.95 0.0985 99.995 6 .times. 10.sup.-10 (111) * 1.98 0.1086 99.999 4 .times. 10.sup.-7 (100) -- 1.97 1287 99.999 2 .times. 10.sup.-8 (100) * 2.02 1.288 99.999 2 .times. 10.sup.-8 (110) * 2.00 0.1089 99.999 2 .times. 10.sup.-8 (111) * 1.98 0.1090 99.999 1 .times. 10.sup.-9 (100) * 1.95 1.491 99.999 1 .times. 10.sup.-9 (110) * 1.97 0.0992 99.999 7 .times. 10.sup.-10 (111) * 2.01 0.09______________________________________
As will be understood from Table 6, the soft magnetic films 13 of the single crystalline iron are also epitaxially grown on the respective buffer films 12 in the vacuum ambience at or higher than 10.sup.-8 torr by using iron with purity not less than 99.995, and the soft magnetic films 13 have excellent soft magnetic properties. Moreover, Table 6 further teaches us that the substrates 11 with the major surfaces in (110) and (111) directions drastically decrease the coercive force rather than the substrate 11 with the major surface in (100) direction, and are, accordingly, conducive to further improvement of the soft magnetic properties.
Although particular embodiments of the present invention have been shown and described, it will be obvious to those skilled in the art that various changes and modifications may be made without departing from the spirit and scope of the present invention.

Number	Date	Country	Kind
2-307650	Nov 1990	JPX
2-312038	Nov 1990	JPX

Number	Name	Date	Kind
5079219	Barnes	Jan 1992
5130294	Char	Jul 1992

Soft magnetic film of iron and process of formation thereof

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (2)

Parent Case Info

US Referenced Citations (2)

Non-Patent Literature Citations (6)

Continuations (1)

Entry
Koon et al "Direct Evidence for Perpendicular Spin Orientations and Enhanced Hyperfine Fields in Ultrathin Fe(100) Films on Ag(100)"; Phys. Rev. Letters; vol. 59, 21; 23 Nov. 1987.
G. S. Swei, J. B. Lando, S. E. Rickert, K. A. Mauritz, "Epitaxial Processes" in Encyclopedia of Polymer Science and Engineering, 2nd ed., vol. 6, 1986, pp. 209,210.
European Search Report for Application No. EP 91 11 6868.
"Large magnetization induced in single crystalline iron films by high-dose nitrogen implantation", Nakajima et al., Appl. Phys. Lett. 56(1), Jan., 1990, pp. 92-94.
"Checkerboard Domain Patterns on Epitaxially Grown Single-Crystal Thin Films of Iron, Nickel, and Cobalt", Sato et al., Journal of Applied Physics, vol. 34, No. 4 (Part 2), Apr. 1963, pp. 1062-1064.
MBE Growth of Single Crystal Alpha-Fe Films on ZnSe (001) and (110), Journal of Crystal Growth, 1987, vol. 81, pp. 524-529, by B. T. Jonker, et al.