The presently-disclosed invention relates generally to soft nonwoven fabrics having an embossed bonding pattern including a plurality of icons defined by a plurality of perimeter bonding points and at least one bonding point located within, for example, each of the plurality of icons.
A variety of commercial applications for nonwoven fabrics require abrasion resistance/low-linting while retaining a certain level of softness. By way of example, spunbond nonwoven fabrics have been widely used as various types of everyday items or industrial materials because they have desirable mechanical properties, such as tensile strength, due to the fact that they are formed from continuous fibers.
Of the various types of spunbond nonwoven fabrics available, those made of a polyamide or a polyester exhibit a relatively high softness. Therefore, attempts have been made to use them as materials which make direct contact with the human body, such as in disposable sheets or the top sheets of diapers. However, spunbond filaments forming spunbond nonwoven fabrics, by virtue of their method of formation, must be subjected to a bonding operation to hold the individual filaments together. Bonding operations may facilitate or improve the fabric's abrasion resistance, but may also negatively impact the level of softness of the fabric.
Therefore, there at least remains a need in the art for embossed nonwoven fabrics which exhibit a desirable softness to touch while retaining a desired level of abrasion resistance/low-linting.
One or more embodiments of the invention may address one or more of the aforementioned problems. Certain embodiments according to the invention provide fabrics comprising a nonwoven web including an embossed bonding pattern. The embossed bonding pattern, according to certain embodiments of the invention, may comprise a plurality of icons, in which each of the plurality of icons may be defined by a plurality of perimeter bonding points and from 1 to about 5 (e.g., 1-3) internal bonding points located within at least one of the plurality of icons. In certain embodiments of the invention, each of the icons include from 1 to about 5 internal bonding points located therein. Fabrics according to certain embodiments of the invention may comprise a plurality of icons, in which each of the plurality of icons comprise the same geometric shape. In certain other embodiments of the invention, the plurality of icons may comprise two or more different geometric shapes. In this regard, the embossed bonding pattern of fabrics, in accordance with certain embodiments of the invention, may comprise a plurality of different geometric shapes. Regardless of whether to plurality of icons of the embossed bonding pattern are all the same or not, the plurality of icons may each comprise an icon area from about 1 mm2 to about 50 mm2 (e.g., from about 1 mm2 to about 25 mm2). In this regard, each of the plurality of icons may have the same or different icon area. In accordance with certain embodiments of the invention, for example, the plurality of icons may include a first group of icons (e.g., including a first icon) comprising a first icon area and a second group of icons (e.g., including a second icon) comprising a second icon area, in which the first icon area is different than the second icon area. For example, the plurality of icons may comprise a first icon comprising a first icon area and a second icon comprising a second icon area, in which the first icon area is different than the second icon area.
In accordance with certain embodiments of the invention, each of the plurality of perimeter bonding points may comprise an individual perimeter bonding point area comprising from about 0.01 to about 0.25 mm2. In accordance with certain embodiments of the invention, the plurality of perimeter bonding points may comprise the same or different individual perimeter bonding point area. For example, a set of perimeter bonding points may comprise individual perimeter bonding points having different individual perimeter bonding point areas. Each of the internal bonding points, according to embodiments of the invention, may comprise an individual internal bonding point area comprising from about 0.01 to about 0.25 mm2. In accordance with certain embodiments of the invention, a plurality of internal bonding points may comprise the same or different individual internal bonding point area. For example, a first internal bonding point may comprise a first individual internal bonding area that is different than a second internal bonding point having a second individual internal bonding point area.
In accordance with certain embodiments of the invention, each of the plurality of perimeter bonding points may comprise an individual perimeter bonding point area and each of the internal bonding points may comprise an individual internal bonding point area, in which the individual perimeter bonding point area may be different than the individual internal bonding point area. In according to certain other embodiments of the invention, the individual perimeter bonding point area may be the same as the individual internal bonding point area.
Fabrics according to certain embodiment of the invention include a nonwoven web, in which the nonwoven web comprises a total bond area comprising from about 3% to about 25% of a total area of the nonwoven web. In accordance with certain embodiments of the invention, the nonwoven web may comprise a total bond area comprising from about 5% to about 20% of a total area of the nonwoven web. In accordance with certain such embodiments, the nonwoven web may comprise a total bond area comprising from about 10% to about 18% of a total area of the nonwoven web.
In accordance with certain embodiments of the invention, the one or more internal bonding points being randomly located with the plurality of icons. In certain other embodiments of the invention, however, internal bonding points may define an internal pattern. For example, the internal pattern according to certain embodiments of the invention may comprise any geometric shape, such a circle, a triangle, a square, a rectangle, or a star-shaped pattern. In accordance with certain embodiments of the invention, the internal pattern may be centered within the plurality of icons. In other embodiments of the invention, the internal pattern may not be centered within the plurality of icons. By way of example, each icon of the plurality of icons may each include an internal pattern of internal bonding points either centered or not centered therein. In accordance with certain embodiments of the invention, the plurality of icons include, for example, a third group of icons including a first internal pattern located therein and a fourth group of icons including a second internal pattern located therein, in which the first internal pattern is different than the second internal pattern.
The internal bonding point or points, according to certain embodiments of the invention, may not be located any closer than about 0.25 mm to a nearest perimeter bonding point. In accordance with certain embodiments of the invention, the internal bonding point or points may not be located any closer than about 0.5 mm to a nearest perimeter bonding point. The internal bonding points, according to certain embodiments of the invention, may not be located any closer than about 2 mm to the nearest perimeter bonding point. In accordance with certain embodiments of the invention, the internal bonding point or points may not be located any closer than about 5 mm to a nearest perimeter bonding point. In accordance with certain embodiments of the invention, the internal bonding point or points may not be located any closer than about 8 mm to a nearest perimeter bonding point. In accordance with certain embodiments of the invention, each of the internal bonding points are not located within about 0.2 mm of each other, or within about 0.5 mm of each other, or within about 1 mm of each other.
In accordance with certain embodiments of the invention, the nonwoven web may comprise a single nonwoven layer or a plurality of nonwoven layers. The nonwoven web, according to certain embodiments of the invention, may comprise a spunbond layer. In accordance with certain embodiments of the invention, the nonwoven web may comprise a nonwoven composite comprising, for example, a spunbond layer, a meltblown layer, a carded layer, a hydroentangled layer, or combinations thereof. In one exemplary embodiment of the invention, the nonwoven composite may comprise a spunbond-meltblown-spunbond structure.
In another aspect, the invention provides an embossing roll including a cylindrical base surface area and a plurality of embossing protrusions extending outwardly from the cylindrical base surface and defining an embossing protrusion pattern. In accordance with certain embodiments of the invention, the embossing protrusion pattern may comprising a plurality of icons, in which each of the plurality of icons may be defined by a first group of embossing protrusions comprising a plurality of perimeter embossing protrusions and from 1 to about 5 (e.g., 1 to about 3) internal embossing protrusions located within at least one of the plurality of icons. In certain embodiments of the invention, each of the icons include from 1 to about 5 internal embossing protrusions located therein.
Embossing rolls according to certain embodiments of the invention may comprise a plurality of icons, in which each of the plurality of icons comprise the same geometric shape. In certain other embodiments of the invention, the plurality of icons may comprise two or more different geometric shapes. In this regard, the embossing protrusion pattern, in accordance with certain embodiments of the invention, may comprise a plurality of different geometric shapes. Regardless of whether to plurality of icons of the embossing protrusion pattern are all the same or not, the plurality of icons may each comprise an icon area from about 1 mm2 to about 50 mm2 (e.g., from about 1 mm2 to about 25 mm2). In this regard, each of the plurality of icons may have the same or different icon area. In accordance with certain embodiments of the invention, for example, the plurality of icons may include a first group of icons (e.g., including a first icon) comprising a first icon area and a second group of icons (e.g., including a second icon) comprising a second icon area, in which the first icon area is different than the second icon area. For example, the plurality of icons may comprise a first icon comprising a first icon area and a second icon comprising a second icon area, in which the first icon area is different than the second icon area.
In accordance with certain embodiments of the invention, each of the plurality of perimeter embossing protrusions may comprise an individual perimeter bonding point area comprising from about 0.01 to about 0.25 mm2 and/or a height (dimension extending from the cylindrical base surface) of from about 0.2 mm to about 1.5 mm (e.g., from about 0.2 mm to about 1.0 mm, from about 0.3 mm to about 0.8 mm, from about 0.4 mm to about 0.7 mm). In accordance with certain embodiments of the invention, the plurality of perimeter embossing protrusions may comprise the same or different individual perimeter embossing protrusion area. For example, a set of perimeter embossing protrusions may comprise individual perimeter embossing protrusions having different individual perimeter embossing protrusion areas. Each of the internal embossing protrusions, according to embodiments of the invention, may comprise an individual internal embossing protrusion area comprising from about 0.01 to about 0.25 mm2. In accordance with certain embodiments of the invention, a plurality of internal embossing protrusions may comprise the same or different individual internal embossing protrusion area. For example, a first internal embossing protrusion may comprise a first individual internal embossing protrusion area that is different than a second internal embossing protrusion having a second individual internal bonding point area. In accordance with certain embodiments of the invention, the plurality of perimeter embossing protrusions and the internal embossing protrusions may comprise the same or different height.
In accordance with certain embodiments of the invention, each of the plurality of perimeter embossing protrusions may comprise an individual perimeter embossing protrusion area and each of the internal embossing protrusions may comprise an individual internal embossing protrusion area, in which the individual perimeter embossing protrusion area may be different than the individual internal embossing protrusion area. In according to certain other embodiments of the invention, the individual perimeter embossing protrusion area may be the same as the individual internal embossing protrusion area.
Embossing rolls according to certain embodiments of the invention may include a total embossing protrusion area comprising from about 3% to about 25% of a total area of the embossing roll. In accordance with certain embodiments of the invention, total embossing protrusion area may comprise from about 5% to about 20% of a total area of the embossing roll. In accordance with certain such embodiments, the total embossing protrusion area may comprise from about 10% to about 18% of a total area of the embossing roll.
In accordance with certain embodiments of the invention, the one or more internal embossing protrusions may be randomly located with the plurality of icons. In certain other embodiments of the invention, however, internal embossing protrusions may define an internal pattern. For example, the internal pattern according to certain embodiments of the invention may comprise any geometric shape, such a circle, a triangle, a square, a rectangle, or a star-shaped pattern. In accordance with certain embodiments of the invention, the internal pattern may be centered within the plurality of icons. In other embodiments of the invention, the internal pattern may not be centered within the plurality of icons. By way of example, each icon of the plurality of icons may each include an internal pattern of internal embossing protrusions either centered or not centered therein. In accordance with certain embodiments of the invention, the plurality of icons include, for example, a third group of icons including a first internal pattern located therein and a fourth group of icons including a second internal pattern located therein, in which the first internal pattern is different than the second internal pattern.
The internal embossing protrusion or protrusions, according to certain embodiments of the invention, may not be located any closer than about 0.25 mm to a nearest perimeter embossing protrusion. In accordance with certain embodiments of the invention, the internal embossing protrusion or protrusions may not be located any closer than about 0.5 mm to a nearest perimeter embossing protrusion. The internal embossing protrusion or protrusions, according to certain embodiments of the invention, may not be located any closer than about 2 mm to the nearest perimeter embossing protrusion. In accordance with certain embodiments of the invention, the internal embossing protrusion or protrusions may not be located any closer than about 5 mm to a nearest perimeter embossing protrusion. In accordance with certain embodiments of the invention, the internal embossing protrusion or protrusions may not be located any closer than about 8 mm to a nearest perimeter embossing protrusion. In accordance with certain embodiments of the invention, each of the internal embossing protrusions are not located within about 0.2 mm of each other, or within about 0.5 mm of each other, or within about 1 mm of each other.
In yet another aspect, the invention provides a method of producing an embossed fabric. In accordance with certain embodiments of the invention, the method may comprise a step of directing a nonwoven web into a nip formed between an embossing roll according one or more of the embossing roll embodiments disclosed herein and an anvil roll and imparting an embossed bonding pattern corresponding to the embossing protrusion pattern of the embossing roll. In accordance with certain embodiments of the invention, the embossing roll may comprise an embossing roll material and the anvil roll may comprise an anvil roll material, in which the anvil roll material is softer than the embossing roll material. In accordance with certain embodiments of the invention, the nonwoven web may comprise a single nonwoven layer or a plurality of nonwoven layers. The nonwoven web, according to certain embodiments of the invention, may comprise a spunbond layer. In accordance with certain embodiments of the invention, the nonwoven web may comprise a nonwoven composite comprising, for example, a spunbond layer, a meltblown layer, a carded layer, a hydroentangled layer, or combinations thereof. In one exemplary embodiment of the invention, the nonwoven composite may comprise a spunbond-meltblown-spunbond structure.
The invention now will be described more fully hereinafter with reference to the accompanying drawings, in which some, but not all embodiments of the invention are shown. Indeed, this invention may be embodied in many different forms and should not be construed as limited to the embodiments set forth herein; rather, these embodiments are provided so that this disclosure will satisfy applicable legal requirements. Like numbers refer to like elements throughout.
The invention now will be described more fully hereinafter with reference to the accompanying drawings, in which some, but not all embodiments of the invention are shown. Indeed, this invention may be embodied in many different forms and should not be construed as limited to the embodiments set forth herein; rather, these embodiments are provided so that this disclosure will satisfy applicable legal requirements. As used in the specification, and in the appended claims, the singular forms “a”, “an”, “the”, include plural referents unless the context clearly dictates otherwise.
The invention includes, according to certain embodiments, soft nonwoven fabrics having an embossed bonding pattern thereon. The embossed bonding pattern, according to certain embodiments of the invention, may include a plurality of icons defined by a plurality of perimeter bonding points. The embossed bonding pattern may also include at least one internal bonding point (e.g., from 1 to about 10) located within, for example, each of the plurality of icons. The internal bonding point or points, for instance, may facilitate and/or provide an improved resistance to abrasion and/or linting without sacrificing the level of softness of the embossed fabric.
The terms “substantial” or “substantially” may encompass the whole amount as specified, according to certain embodiments of the invention, or largely but not the whole amount specified according to other embodiments of the invention.
The terms “polymer” or “polymeric”, as used interchangeably herein, may comprise homopolymers, copolymers, such as, for example, block, graft, random, and alternating copolymers, terpolymers, etc., and blends and modifications thereof. Furthermore, unless otherwise specifically limited, the term “polymer” or “polymeric” shall include all possible structural isomers; stereoisomers including, without limitation, geometric isomers, optical isomers or enantionmers; and/or any chiral molecular configuration of such polymer or polymeric material. These configurations include, but are not limited to, isotactic, syndiotactic, and atactic configurations of such polymer or polymeric material. The term “polymer” or “polymeric” shall also include polymers made from various catalyst systems including, without limitation, the Ziegler-Natta catalyst system and the metallocene/single-site catalyst system. The term “polymer” or “polymeric” shall also include polymers produced by fermentation process or biosourced.
The terms “nonwoven” and “nonwoven web”, as used herein, may comprise a web having a structure of individual fibers, filaments, and/or threads that are interlaid but not in an identifiable repeating manner as in a knitted or woven fabric. Nonwoven fabrics or webs, according to certain embodiments of the invention, may be formed by any process conventionally known in the art such as, for example, meltblowing processes, spunbonding processes, hydroentangling, air-laid, and bonded carded web processes.
The term “layer”, as used herein, may comprise a generally recognizable combination of similar material types and/or functions existing in the X-Y plane.
The term “spunbond”, as used herein, may comprise fibers which are formed by extruding molten thermoplastic material as filaments from a plurality of fine, usually circular, capillaries of a spinneret with the diameter of the extruded filaments then being rapidly reduced. According to an embodiment of the invention, spunbond fibers are generally not tacky when they are deposited onto a collecting surface and may be generally continuous. It is noted that the spunbond used in certain composites of the invention may include a nonwoven described in the literature as SPINLACE®.
The term “meltblown”, as used herein, may comprise fibers formed by extruding a molten thermoplastic material through a plurality of fine die capillaries as molten threads or filaments into converging high velocity, usually hot, gas (e.g. air) streams which attenuate the filaments of molten thermoplastic material to reduce their diameter, which may be to microfiber diameter, according to certain embodiments of the invention. According to an embodiment of the invention, the die capillaries may be circular. Thereafter, the meltblown fibers are carried by the high velocity gas stream and are deposited on a collecting surface to form a web of randomly disbursed meltblown fibers. Meltblown fibers are microfibers which may be continuous or discontinuous and are generally tacky when deposited onto a collecting surface.
The term “hydroentangle” or “hydroentangled”, as used herein, may comprise a process for bonding a nonwoven fabric by using high pressure water jets to intermingle the fibers. Several rows of water jets are directed against the fiber web, which is supported by a movable fabric. Fiber entanglements are introduced by the combined effects of the water jets and the turbulent water created in the web, which intertwines neighboring fibers.
The term “laminate”, as used herein, may be a structure comprising two or more layers, such as a film layer and a fibrous layer. The two layers of a laminate structure may be joined together such that a substantial portion of their common X-Y plane interface, according to certain embodiments of the invention.
As used herein, the terms “consolidation” and “consolidated” may comprise the bringing together of at least a portion of the fibers of a nonwoven web into closer proximity or attachment there-between (e.g., fused together) to form a bonding site, or bonding sites, which function to increase the resistance of the nonwoven to external forces (e.g., abrasion and tensile forces), as compared to the unconsolidated web. The bonding site or bonding sites, for example, may comprise a discrete or localized region of the web material that has been softened or melted and optionally subsequently or simultaneously compressed to form a discrete or localized deformation in the web material. Furthermore, the term “consolidated” may comprise an entire nonwoven web that has been processed such that at least a portion of the fibers are brought into closer proximity or attachment there-between (e.g., fused together), such as by thermal bonding as merely one example. Such a web may be considered a “consolidated nonwoven” according to certain embodiments of the invention. Additionally, a specific, discrete region of fibers that is brought into close proximity or attachment there-between (e.g., fused together), such as an individual bond site, can be described as “consolidated”.
In accordance with certain embodiments of the invention, consolidation may be achieved by methods that apply, for example, heat and/or pressure to the fibrous web (e.g., nonwoven web) via one or more embossing rolls. One non-limiting and exemplary method comprises thermal bonding. Thermal bonding can be accomplished by passing the fibrous web (e.g., nonwoven web) through a pressure nip formed by two rolls, one of which comprising an embossing roll which may be heated and contain a plurality of raised protrusions having one or more geometric shapes (e.g., points, diamond shaped, circular, elliptical, dog-bone shaped, etc.) on its surface which impart or form corresponding discrete thermal bond sites on the fibrous web (e.g., nonwoven web). Such an operating step, for example, may be referred to as “calendaring” or “embossing” in which the nonwoven web is drawn between an embossing roll having an embossing pattern allowing only part of the web to become exposed to heat and pressure and a second roll (e.g., an anvil roll). The degree or extent of consolidation may be expressed as a percentage of the total surface area of the web that has been consolidated or subjected to consolidation and may be referred to as a “bonding area” or “consolidation area”. Stated somewhat differently, the terms “bonding area” and “consolidated area”, as used interchangeably herein, may comprise the area per unit area occupied by the localized sites formed by bonding the fibers into bond sites and may be expressed as a percentage of the total unit area of the consolidated nonwoven. For example, consolidated nonwovens (e.g., subjected to thermal bonding via an embossing roll) may comprise a plurality of discrete, spaced-apart bond sites or points (e.g., perimeter and internal bond sites or points) formed by bonding only the fibers of the nonwoven web in the area of localized energy input. Fibers or portions of fibers remote from the localized energy input remain substantially unbonded to adjacent fibers.
The term “icon”, as used herein, may comprise a single, discrete, design or geometric shape being defined by, at least partially, a plurality of bonding points (e.g., a plurality of perimeter bonding points). For example, an icon may comprise a caricature (e.g., an animal, flower, logo, etc.) or other design. In certain embodiments of the invention, an icon may, for example, may comprise a variety of geometric shapes including triangles, squares, rectangles, circles, ovals, arcs, stars, or combinations thereof.
The term “bicomponent fibers”, as used herein, may comprise fibers formed from at least two different polymers extruded from separate extruders but spun together to form one fiber. Bicomponent fibers are also sometimes referred to as conjugate fibers or multicomponent fibers. The polymers are arranged in a substantially constant position in distinct zones across the cross-section of the bicomponent fibers and extend continuously along the length of the bicomponent fibers. The configuration of such a bicomponent fiber may be, for example, a sheath/core arrangement wherein one polymer is surrounded by another, or may be a side-by-side arrangement, a pie arrangement, or an “islands-in-the-sea” arrangement, each as is known in the art of multicomponent, including bicomponent, fibers. The “bicomponent fibers” may be thermoplastic fibers that comprise a core fiber made from one polymer that is encased within a thermoplastic sheath made from a different polymer or have a side-by-side arrangement of different thermoplastic fibers. The first polymer often melts at a different, typically lower, temperature than the second polymer. In the sheath/core arrangement, these bicomponent fibers provide thermal bonding due to melting of the sheath polymer, while retaining the desirable strength characteristics of the core polymer. In the side-by-side arrangement, the fibers shrink and crimp creating z-direction expansion.
The terms “lint” and “lint level”, as used herein, may comprise the tendency of a web to shed particles when manipulated. This tendency may be measured in accordance to the standard test method WSP 400.0 (05).
I. Embossed Fabrics
In one aspect, the invention provides fabrics comprising a nonwoven web including an embossed bonding pattern. The embossed bonding pattern, according to certain embodiments of the invention, may comprise a plurality of icons, in which each of the plurality of icons may be defined by a plurality of perimeter bonding points and from 1 to about 5 (e.g., 1-3) internal bonding points located within at least one of the plurality of icons. In certain embodiments of the invention, each of the icons include from 1 to about 5 internal bonding points located therein. In accordance with certain embodiments of the invention, the number of internal bonding points within a given icon may comprise from 1 to about 10 (e.g., 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10) discrete internal bonding points.
Fabrics according to certain embodiments of the invention may comprise a plurality of icons, in which each of the plurality of icons comprise the same geometric shape. In certain other embodiments of the invention, the plurality of icons may comprise two or more different geometric shapes (e.g., an oval and a square). In this regard, the embossed bonding pattern of fabrics, in accordance with certain embodiments of the invention, may comprise a plurality of different geometric shapes as described above. Regardless of whether to plurality of icons of the embossed bonding pattern are all the same or not, the plurality of icons may each independently comprise an icon area from about 1 mm2 to about 50 mm2 (e.g., from about 1 mm2 to about 25 mm2). In accordance with certain embodiments of the invention, the plurality of icons may each independently comprise an icon area from at least about any of the following: 1 mm2, 5 mm2, 10 mm2, 15 mm2, 20 mm2 and 25 mm2 and/or at most about 50 mm2, 45 mm2, 40 mm2, 35 mm2, 30 mm2 and 25 mm2 (e.g., about 1-25 mm2, about 10-35 mm2, etc.). In this regard, each of the plurality of icons may have the same or different icon area. In accordance with certain embodiments of the invention, for example, the plurality of icons may include a first group of icons (e.g., including a first icon) comprising a first icon area and a second group of icons (e.g., including a second icon) comprising a second icon area, in which the first icon area is different than the second icon area. For example, the plurality of icons may comprise a first icon comprising a first icon area and a second icon comprising a second icon area, in which the first icon area is different than the second icon area.
In accordance with certain embodiments of the invention, the plurality of icons may comprise a variety of different geometric shapes. By way of example,
In accordance with certain embodiments of the invention, each of the plurality of perimeter bonding points may comprise an individual perimeter bonding point area comprising from about 0.01 to about 0.25 mm2. In accordance with certain embodiments of the invention, the plurality of perimeter bonding points may comprise the same or different individual perimeter bonding point area. For example, a set of perimeter bonding points may comprise individual perimeter bonding points having different individual perimeter bonding point areas. In accordance with certain embodiments of the invention, each of the plurality of perimeter bonding points may independently comprise an individual perimeter bonding point area from at least about any of the following: 0.01 mm2, 0.05 mm2, 0.1 mm2, 0.15 mm2, and 0.2 mm2 and/or at most about 0.5 mm2, 0.45 mm2, 0.4 mm2, 0.35 mm2, 0.3 mm2 and 0.25 mm2 (e.g., about 0.1-0.25 mm2, about 0.01-0.5 mm2, etc.).
Each of the internal bonding points, according to embodiments of the invention, may comprise an individual internal bonding point area comprising from about 0.01 to about 0.25 mm2. In accordance with certain embodiments of the invention, a plurality of internal bonding points may comprise the same or different individual internal bonding point area. For example, a first internal bonding point may comprise a first individual internal bonding area that is different than a second internal bonding point having a second individual internal bonding point area. In accordance with certain embodiments of the invention, each of the internal bonding points may independently comprise an individual internal bonding point area from at least about any of the following: 0.01 mm2, 0.05 mm2, 0.1 mm2, 0.15 mm2, and 0.2 mm2 and/or at most about 0.5 mm2, 0.45 mm2, 0.4 mm2, 0.35 mm2, 0.3 mm2 and 0.25 mm2 (e.g., about 0.1-0.25 mm2, about 0.01-0.5 mm2, etc.).
In accordance with certain embodiments of the invention, each of the plurality of perimeter bonding points may comprise an individual perimeter bonding point area and each of the internal bonding points may comprise an individual internal bonding point area, in which the individual perimeter bonding point area may be different than the individual internal bonding point area. In according to certain other embodiments of the invention, the individual perimeter bonding point area may be the same as the individual internal bonding point area.
Fabrics according to certain embodiment of the invention may include a nonwoven web, in which the nonwoven web comprises a total bond area comprising from about 3% to about 25% of a total area of the nonwoven web. In accordance with certain embodiments of the invention, the nonwoven web may comprise a total bond area comprising from about 5% to about 20% of a total area of the nonwoven web. In accordance with certain such embodiments, the nonwoven web may comprise a total bond area comprising from about 10% to about 18% of a total area of the nonwoven web. For example, in certain embodiments of the invention, the nonwoven web may comprise a total bond area comprising from at least about any of the following: 1, 2, 3, 5, 8, and 10% of a total area of the nonwoven web and/or at most about 30, 25, 20, 18, 15, 12, and 10% of a total area of the nonwoven web (e.g., about 2-20% of a total area of the nonwoven web, about 10-15% of a total area of the nonwoven web, etc.).
In accordance with certain embodiments of the invention, the one or more internal bonding points may be randomly located with the plurality of icons. In certain other embodiments of the invention, however, internal bonding points may define an internal pattern. For example, the internal pattern according to certain embodiments of the invention may comprise any geometric shape, such a circle, a triangle, a square, a rectangle, or a star-shaped pattern. In accordance with certain embodiments of the invention, the internal pattern may be centered within the plurality of icons. In other embodiments of the invention, the internal pattern may not be centered within the plurality of icons. By way of example, each icon of the plurality of icons may each include an internal pattern of internal bonding points either centered or not centered therein. In accordance with certain embodiments of the invention, the plurality of icons include, for example, a third group of icons including a first internal pattern located therein and a fourth group of icons including a second internal pattern located therein, in which the first internal pattern is different than the second internal pattern.
The internal bonding point or points, according to certain embodiments of the invention, may not be located any closer than about 0.25 mm to a nearest perimeter bonding point. In accordance with certain embodiments of the invention, the internal bonding point or points may not be located any closer than about 0.5 mm to a nearest perimeter bonding point. The internal bonding points, according to certain embodiments of the invention, may not be located any closer than about 2 mm to the nearest perimeter bonding point. In accordance with certain embodiments of the invention, the internal bonding point or points may not be located any closer than about 5 mm to a nearest perimeter bonding point. In accordance with certain embodiments of the invention, the internal bonding point or points may not be located any closer than about 8 mm to a nearest perimeter bonding point. In accordance with certain embodiments of the invention, each of the internal bonding points are not located within about 0.2 mm of each other, or within about 0.5 mm of each other, or within about 1 mm of each other.
In accordance with certain embodiments of the invention, the nonwoven web may comprise a single nonwoven layer or a plurality of nonwoven layers. The nonwoven web, according to certain embodiments of the invention, may comprise a spunbond layer. In accordance with certain embodiments of the invention, the nonwoven web may comprise a nonwoven composite comprising, for example, a spunbond layer, a meltblown layer, a carded layer, a hydroentangled layer, or combinations thereof. In one exemplary embodiment of the invention, the nonwoven composite may comprise a spunbond-meltblown-spunbond structure. According to certain embodiments of the invention, for example, the nonwoven web may comprise a plurality of nonwoven webs (e.g., a laminate or composite). Exemplary configurations include, but are not limited to, S1S1S2, S1S1S2S2, and S1S2 S2, where S1=a first nonwoven web structure and S2=a second nonwoven web structure. In further embodiments, for instance, one or more meltblown and/or submicron-fiber-containing layer may be located directly or indirectly between any two of the spunbond layers. For example, the nonwoven web, as noted above, may comprise an SMS configuration, where S=spunbond and M=meltblown.
In accordance with certain embodiments of the invention, one or more of the layers of the nonwoven web may comprise a variety of synthetic or natural polymeric materials. For example, the nonwoven web may comprise a spunbond layer including a polypropylene, such as an isotactic polypropylene. In certain embodiments of the invention, for example, the spunbond may comprise a a polyrpopylen, polyethylene, or both. In such embodiments of the invention, for instance, the spunbond may comprise high density polypropylene or high density polyethylene, low density polypropylene or low density polyethylene, linear low density polypropylene or linear low density polyethylene, a copolymer of polypropylene or ethylene, and any combination thereof. In some embodiments of the invention, the nonwoven web (e.g., a spunbond layer) may comprise at least one of a polypropylene, a polyethylene, a polyester, a polyamide, or combinations thereof. In accordance with certain embodiments of the invention, the nonwoven web may comprise one or more layers comprising a biopolymer (e.g., polylactic acid (PLA) polyhydroxyalkanoates (PHA), and poly(hydroxycarboxylic) acids). In accordance with certain embodiments of the invention, the nonwoven web may comprise an interior layer comprising a biopolymer being sandwiched, either directly or indirectly, between two spunbond layers.
In accordance with certain embodiments of the invention, the nonwoven web may comprise one or more individual layers, in which one or more of the individual layers include multi-component fibers, such as bicomponent fibers having a sheath-core configuration. For example, certain embodiments of the invention may comprise bicomponent fibers comprising a sheath comprising, by way of example only, a polyethylene or a propylene and a core comprising, by way of example only, at least one of a polypropylene, a polyethylene, a polyester, or a biopolymer (e.g., polylactic acid (PLA) polyhydroxyalkanoates (PHA), and poly(hydroxycarboxylic) acids.
II. Embossing Rolls
In another aspect, the invention provides an embossing roll including a cylindrical base surface area and a plurality of embossing protrusions extending outwardly from the cylindrical base surface and defining an embossing protrusion pattern. In accordance with certain embodiments of the invention, the embossing protrusion pattern may comprising a plurality of icons, in which each of the plurality of icons may be defined by a first group of embossing protrusions comprising a plurality of perimeter embossing protrusions and from 1 to about 5 (e.g., 1 to about 3) internal embossing protrusions located within at least one of the plurality of icons. In certain embodiments of the invention, each of the icons include from 1 to about 10 (e.g., 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10) internal embossing protrusions located therein.
Embossing rolls according to certain embodiments of the invention may comprise a plurality of icons, in which each of the plurality of icons comprise the same geometric shape. In certain other embodiments of the invention, the plurality of icons may comprise two or more different geometric shapes (e.g., an oval and a square). In this regard, the embossing protrusion pattern, in accordance with certain embodiments of the invention, may comprise a plurality of different geometric shapes. Regardless of whether to plurality of icons of the embossing protrusion pattern are all the same or not, the plurality of icons may each comprise an icon area from about 1 mm2 to about 50 mm2 (e.g., from about 1 mm2 to about 25 mm2). In accordance with certain embodiments of the invention, the plurality of icons may each independently comprise an icon area from at least about any of the following: 1 mm2, 5 mm2, 10 mm2, 15 mm2, 20 mm2 and 25 mm2 and/or at most about 50 mm2, 45 mm2, 40 mm2, 35 mm2, 30 mm2 and 25 mm2 (e.g., about 1-25 mm2, about 10-35 mm2, etc.). In this regard, each of the plurality of icons may have the same or different icon area. In accordance with certain embodiments of the invention, for example, the plurality of icons may include a first group of icons (e.g., including a first icon) comprising a first icon area and a second group of icons (e.g., including a second icon) comprising a second icon area, in which the first icon area is different than the second icon area. For example, the plurality of icons may comprise a first icon comprising a first icon area and a second icon comprising a second icon area, in which the first icon area is different than the second icon area.
In accordance with certain embodiments of the invention, each of the plurality of perimeter embossing protrusions may comprise an individual perimeter bonding point area comprising from about 0.01 to about 0.25 mm2 and/or a height (dimension extending from the cylindrical base surface) of from about 0.2 mm to about 1.5 mm (e.g., from about 0.2 mm to about 1.0 mm, from about 0.3 mm to about 0.8 mm, from about 0.4 mm to about 0.7 mm). In accordance with certain embodiments of the invention, the plurality of perimeter embossing protrusions may comprise the same or different individual perimeter embossing protrusion area. For example, a set of perimeter embossing protrusions may comprise individual perimeter embossing protrusions having different individual perimeter embossing protrusion areas. In accordance with certain embodiments of the invention, each of the plurality of perimeter embossing protrusion may independently comprise an individual perimeter embossing protrusion area from at least about any of the following: 0.01 mm2, 0.05 mm2, 0.1 mm2, 0.15 mm2, and 0.2 mm2 and/or at most about 0.5 mm2, 0.45 mm2, 0.4 mm2, 0.35 mm2, 0.3 mm2 and 0.25 mm2 (e.g., about 0.1-0.25 mm2, about 0.01-0.5 mm2, etc.). In accordance with certain embodiments of the invention, each of the plurality of perimeter embossing protrusion may independently comprise an individual height (dimension extending from the cylindrical base surface) of from at least about any of the following: 0.1 mm, 0.2 mm, 0.3 mm, 0.4 mm, and 0.5 mm and/or at most about 1.5 mm, 1.25 mm, 1.0 mm, 0.8 mm, and 0.7 mm (e.g., about 0.1-0.8 mm, about 0.4-0.7 mm, etc.).
Each of the internal embossing protrusions, according to embodiments of the invention, may comprise an individual internal embossing protrusion area comprising from about 0.01 to about 0.25 mm2. In accordance with certain embodiments of the invention, a plurality of internal embossing protrusions may comprise the same or different individual internal embossing protrusion area. For example, a first internal embossing protrusion may comprise a first individual internal embossing protrusion area that is different than a second internal embossing protrusion having a second individual internal bonding point area. In accordance with certain embodiments of the invention, the plurality of perimeter embossing protrusions and the internal embossing protrusions may comprise the same or different height. In accordance with certain embodiments of the invention, each of the internal embossing protrusion(s) may independently comprise an individual internal embossing protrusion area from at least about any of the following: 0.01 mm2, 0.05 mm2, 0.1 mm2, 0.15 mm2, and 0.2 mm2 and/or at most about 0.5 mm2, 0.45 mm2, 0.4 mm2, 0.35 mm2, 0.3 mm2 and 0.25 mm2 (e.g., about 0.1-0.25 mm2, about 0.01-0.5 mm2, etc.). In accordance with certain embodiments of the invention, each of the internal embossing protrusion(s) may independently comprise an individual height (dimension extending from the cylindrical base surface) of from at least about any of the following: 0.1 mm, 0.2 mm, 0.3 mm, 0.4 mm, and 0.5 mm and/or at most about 1.5 mm, 1.25 mm, 1.0 mm, 0.8 mm, and 0.7 mm (e.g., about 0.1-0.8 mm, about 0.4-0.7 mm, etc.).
In accordance with certain embodiments of the invention, each of the plurality of perimeter embossing protrusions may comprise an individual perimeter embossing protrusion area and each of the internal embossing protrusions may comprise an individual internal embossing protrusion area, in which the individual perimeter embossing protrusion area may be different than the individual internal embossing protrusion area. In according to certain other embodiments of the invention, the individual perimeter embossing protrusion area may be the same as the individual internal embossing protrusion area.
Embossing rolls according to certain embodiments of the invention may include a total embossing protrusion area comprising from about 3% to about 25% of a total area of the embossing roll (e.g. a sum of the base surface area and the total embossing protrusion area). In accordance with certain embodiments of the invention, total embossing protrusion area may comprise from about 5% to about 20% of a total area of the embossing roll. In accordance with certain such embodiments, the total embossing protrusion area may comprise from about 10% to about 18% of a total area of the embossing roll. For example, in certain embodiments of the invention, the embossing roll may comprise a total embossing protrusion area comprising from at least about any of the following: 1, 2, 3, 5, 8, and 10% of a total area of the embossing roll and/or at most about 30, 25, 20, 18, 15, 12, and 10% of a total area of the embossing roll (e.g., about 2-20% of a total area of the embossing roll, about 10-15% of a total area of the embossing roll, etc.).
In accordance with certain embodiments of the invention, the one or more internal embossing protrusions may be randomly located with the plurality of icons. In certain other embodiments of the invention, however, internal embossing protrusions may define an internal pattern. For example, the internal pattern according to certain embodiments of the invention may comprise any geometric shape, such a circle, a triangle, a square, a rectangle, or a star-shaped pattern. In accordance with certain embodiments of the invention, the internal pattern may be centered within the plurality of icons. In other embodiments of the invention, the internal pattern may not be centered within the plurality of icons. By way of example, each icon of the plurality of icons may each include an internal pattern of internal embossing protrusions either centered or not centered therein. In accordance with certain embodiments of the invention, the plurality of icons include, for example, a third group of icons including a first internal pattern located therein and a fourth group of icons including a second internal pattern located therein, in which the first internal pattern is different than the second internal pattern.
The internal embossing protrusion or protrusions, according to certain embodiments of the invention, may not be located any closer than about 0.25 mm to a nearest perimeter embossing protrusion. In accordance with certain embodiments of the invention, the internal embossing protrusion or protrusions may not be located any closer than about 0.5 mm to a nearest perimeter embossing protrusion. The internal embossing protrusion or protrusions, according to certain embodiments of the invention, may not be located any closer than about 2 mm to the nearest perimeter embossing protrusion. In accordance with certain embodiments of the invention, the internal embossing protrusion or protrusions may not be located any closer than about 5 mm to a nearest perimeter embossing protrusion. In accordance with certain embodiments of the invention, the internal embossing protrusion or protrusions may not be located any closer than about 8 mm to a nearest perimeter embossing protrusion. In accordance with certain embodiments of the invention, each of the internal embossing protrusions are not located within about 0.2 mm of each other, or within about 0.5 mm of each other, or within about 1 mm of each other.
III. Methods of Producing an Embossed Fabric
In yet another aspect, the invention provides a method of producing an embossed fabric. In accordance with certain embodiments of the invention, the method may comprise a step of directing a nonwoven web into a nip formed between an embossing roll according one or more of the embossing roll embodiments disclosed herein and, for example, an anvil roll and imparting an embossed bonding pattern corresponding to the embossing protrusion pattern of the embossing roll. In accordance with certain embodiments of the invention, the embossing roll may comprise an embossing roll material and the anvil roll may comprise an anvil roll material, in which the anvil roll material is softer than the embossing roll material.
In accordance with certain embodiments of the invention, the nonwoven web may comprise a single nonwoven layer or a plurality of nonwoven layers. The nonwoven web, according to certain embodiments of the invention, may comprise a spunbond layer. In accordance with certain embodiments of the invention, the nonwoven web may comprise a nonwoven composite comprising, for example, a spunbond layer, a meltblown layer, a carded layer, a hydroentangled layer, or combinations thereof. In one exemplary embodiment of the invention, the nonwoven composite may comprise a spunbond-meltblown-spunbond structure. According to certain embodiments of the invention, for example, the nonwoven web may comprise a plurality of nonwoven webs (e.g., a laminate or composite). Exemplary configurations include, but are not limited to, S1S1S2, S1S1S2S2, and S1S2 S1, where S1=a first nonwoven web structure and S2=a second nonwoven web structure. In further embodiments, for instance, one or more meltblown and/or submicron-fiber-containing layer may be located directly or indirectly between any two of the spunbond layers. For example, the nonwoven web, as noted above, may comprise an SMS configuration, where S=spunbond and M=meltblown.
In accordance with certain embodiments of the invention, one or more of the layers of the nonwoven web may comprise a variety of synthetic or natural polymeric materials. For example, the nonwoven web may comprise a spunbond layer including a polypropylene, such as an isotactic polypropylene. In certain embodiments of the invention, for example, the spunbond may comprise a a polyrpopylen, polyethylene, or both. In such embodiments of the invention, for instance, the spunbond may comprise high density polypropylene or high density polyethylene, low density polypropylene or low density polyethylene, linear low density polypropylene or linear low density polyethylene, a copolymer of polypropylene or ethylene, and any combination thereof. In some embodiments of the invention, the nonwoven web (e.g., a spunbond layer) may comprise at least one of a polypropylene, a polyethylene, a polyester, a polyamide, or combinations thereof. In accordance with certain embodiments of the invention, the nonwoven web may comprise one or more layers comprising a biopolymer (e.g., polylactic acid (PLA) polyhydroxyalkanoates (PHA), and poly(hydroxycarboxylic) acids). In accordance with certain embodiments of the invention, the nonwoven web may comprise an interior layer comprising a biopolymer being sandwiched, either directly or indirectly, between two spunbond layers.
In accordance with certain embodiments of the invention, the nonwoven web may comprise one or more individual layers, in which one or more of the individual layers include multi-component fibers, such as bicomponent fibers having a sheath-core configuration. For example, certain embodiments of the invention may comprise bicomponent fibers comprising a sheath comprising, by way of example only, a polyethylene or a propylene and a core comprising, by way of example only, at least one of a polypropylene, a polyethylene, a polyester, or a biopolymer (e.g., polylactic acid (PLA) polyhydroxyalkanoates (PHA), and poly(hydroxycarboxylic) acids.
These and other modifications and variations to the invention may be practiced by those of ordinary skill in the art without departing from the spirit and scope of the invention, which is more particularly set forth in the appended claims. In addition, it should be understood that aspects of the various embodiments may be interchanged in whole or in part. Furthermore, those of ordinary skill in the art will appreciate that the foregoing description is by way of example only, and it is not intended to limit the invention as further described in such appended claims. Therefore, the spirit and scope of the appended claims should not be limited to the exemplary description of the versions contained herein.
This application claims priority under 35 U.S.C. § 119(e) to U.S. Provisional Application Ser. No. 62/268,194, filed on Dec. 16, 2015, which is expressly incorporated by reference herein in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3616157 | Smith | Oct 1971 | A |
| 3855046 | Hansen et al. | Dec 1974 | A |
| 3973068 | Weber | Aug 1976 | A |
| 4091137 | Miller | May 1978 | A |
| 4741941 | Englebert et al. | May 1988 | A |
| 5009651 | Kamishioiri | Apr 1991 | A |
| 5370764 | Alikhan | Dec 1994 | A |
| 5424115 | Stokes | Jun 1995 | A |
| 5620779 | Levy | Apr 1997 | A |
| 5858515 | Stokes et al. | Jan 1999 | A |
| 5964742 | McCormack et al. | Oct 1999 | A |
| 5993714 | Sawyer et al. | Nov 1999 | A |
| 6093665 | Sayovitz et al. | Jul 2000 | A |
| 6319239 | Daniels | Nov 2001 | B1 |
| 6361784 | Brennan et al. | Mar 2002 | B1 |
| D463137 | Monroe et al. | Sep 2002 | S |
| 6537644 | Kauschke et al. | Mar 2003 | B1 |
| 6610390 | Kauschke | Aug 2003 | B1 |
| 6638605 | Ankuda, Jr. | Oct 2003 | B1 |
| 6752947 | Lanigan et al. | Jun 2004 | B1 |
| 6986825 | Squires | Jan 2006 | B1 |
| D516318 | Hasenoehrl et al. | Mar 2006 | S |
| D516319 | Hasenoehrl et al. | Mar 2006 | S |
| 7914723 | Kim et al. | Mar 2011 | B2 |
| D702047 | Rhodes, III | Apr 2014 | S |
| 9096961 | Jones et al. | Aug 2015 | B2 |
| D738632 | Seitzinger | Sep 2015 | S |
| D747887 | Seitzinger | Jan 2016 | S |
| D773833 | Hannen | Dec 2016 | S |
| D777451 | Hunt | Jan 2017 | S |
| 10132042 | Maladen | Nov 2018 | B2 |
| 20030041953 | Farell et al. | Mar 2003 | A1 |
| 20040241399 | Marmon | Dec 2004 | A1 |
| 20040267220 | Hull, Jr. | Dec 2004 | A1 |
| 20050148260 | Kopacz et al. | Jul 2005 | A1 |
| 20050159063 | Hill et al. | Jul 2005 | A1 |
| 20050241088 | Brunner et al. | Nov 2005 | A1 |
| 20060063456 | Carter | Mar 2006 | A1 |
| 20060113049 | Knobloch | Jun 2006 | A1 |
| 20060169301 | Haskett | Aug 2006 | A1 |
| 20060286885 | Schuh | Dec 2006 | A1 |
| 20070087169 | McFall | Apr 2007 | A1 |
| 20070130713 | Chen et al. | Jun 2007 | A1 |
| 20070256803 | Sheehan | Nov 2007 | A1 |
| 20080182048 | Ouellette et al. | Jul 2008 | A1 |
| 20090188090 | Munstermann | Jul 2009 | A1 |
| 20090297781 | Huss | Dec 2009 | A1 |
| 20100305543 | Klaska | Dec 2010 | A1 |
| 20110223381 | Sauter | Sep 2011 | A1 |
| 20110244749 | Fujiwara | Oct 2011 | A1 |
| 20110319846 | Rinnert | Dec 2011 | A1 |
| 20120059343 | Kume | Mar 2012 | A1 |
| 20120244320 | Sauter | Sep 2012 | A1 |
| 20120315440 | Ichikawa | Dec 2012 | A1 |
| 20130236700 | Yamanaka | Sep 2013 | A1 |
| 20130260111 | Kelsey | Oct 2013 | A1 |
| 20130280481 | Mitsuno | Oct 2013 | A1 |
| 20130316135 | Rawat | Nov 2013 | A1 |
| 20140044934 | Bills | Feb 2014 | A1 |
| 20140263033 | Fu | Sep 2014 | A1 |
| 20150001783 | Gann-Fetter | Jan 2015 | A1 |
| 20150086760 | Castillo | Mar 2015 | A1 |
| 20170014280 | Moritani | Jan 2017 | A1 |
| 20170027774 | Ashraf | Feb 2017 | A1 |
| 20170151101 | Isele | Jun 2017 | A1 |
| 20170151102 | Isele | Jun 2017 | A1 |
| 20190161897 | Mecl | May 2019 | A1 |
| Number | Date | Country |
|---|---|---|
| 199692133 | Aug 1997 | CL |
| 1322806 | Sep 2005 | EP |
| 2031039 | Apr 1980 | GB |
| 57167442 | Oct 1982 | JP |
| 1998027257 | Jun 1998 | WO |
| 1998055295 | Dec 1998 | WO |
| 2002048440 | Jun 2002 | WO |
| 2006004871 | Jan 2006 | WO |
| 2008066417 | Jun 2008 | WO |
| 2010066284 | Jun 2010 | WO |
| Entry |
|---|
| Full manual translation of JP S57/167442A (Year: 2019). |
| International Search Report and Written Opinion of corresponding International Application No. PCT/US2016/066095 dated Mar. 22, 2017. |
| Number | Date | Country | |
|---|---|---|---|
| 20170175313 A1 | Jun 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62268194 | Dec 2015 | US |