Soil substitute

Abstract

Soil substitute capable of supporting plant growth is produced in quantities suitable for substitution on a large scale, such as in landscaping operations. Shredded treebark is intimately mixed with quarry stone particles and silica sand particles and are then composted while mixed with the quarry stone particles and sand particles. Composting is performed by laying out the mixture in windrows and aerating the shredded treebark by mechanically turning material in the windrows so that composting proceeds within the temperature range 42-60 degrees Celcius.

Description

TECHNICAL FIELD

This invention relates to soil substitutes capable of supporting plant growth. More particularly, it enables production of a soil substitute in quantities suitable for soil substitution on a large scale, such as in landscaping operations.

At present, landscaping operations consume large quantities of natural top soil harvested from soil supply site. The resulting degradation of large tracts of land around major population centers is a major environmental problem which can only be overcome by the development of a soil substitute which will support plant growth and which is of such mechanical strength and workability that it can be used for large scale landscaping purposes. Currently available soil substitutes do not meet these requirements and are generally limited to small scale applications such as for potting mixes. The present invention enables the production of a soil substitute which can be produced economically in large quantities without the environmental problems associated with the harvesting of naturally occurring top soil.

DISCLOSURE OF THE INVENTION

According to the invention there is provided a method of producing a soil substitute comprising intimately mixing shredded treebark with quarry stone particles and silica sand particles and composting the shredded treebark particles while mixed with the quarry stone particles and sand particles.

The term "composting" is made in this specification to refer to a process of rapid decomposition of the organic material, and includes partial decomposition to produce desired characteristics.

The composting step may include the addition of water to the mixture of shredded treebark, quarry stone particles and sand particles to bring the water content of the mixture into the range 40 to 60% by weight.

Preferably, the shredded treebark, quarry stone particles and sand particles are mixed in the following proportions by volume:

Shredded Treebark 50-75% Quarry stone particles 10-40% Silica sand particles 5-25%

Lignite may also be added in the proportion 0-15% by volume.

Minor minerals may be included in the mixture as required.

Preferably further, the quarry stone particles comprise particles of a relatively coarse aggregate with a range of particle sizes up to about 9.50 mm and a relatively fine aggregate with a range of particle sizes up to about 6.70 mm. More particularly, it is preferred that the coarse aggregate particles comprise between 10 to 15% by volume of the mixture and that the fine aggregate particles also comprise between 10 to 15% by volume of the mixture.

Preferably further, the silica sand particles comprise particles of relatively coarse and fine and aggregates. A major proportion of the coarse sand aggregate particles may fall in the size range 75 micron to 1.18 mm and a major proportion of the fine sand particles may fall in the size range 300 micron to 2.36 micron.

Preferably, the coarse sand particles comprise between 5 to 10% by volume of the mixture and the fine sand particles comprise between 10 to 15% by volume of the mixture.

The shredded treebark may be obtained from the bark of Pinus radiata or from the bark of slash Pine (Pinus elliottii) or from alternative barks as disclosed in Table A herein.

Preferably, composting of the shredded treebark is performed by laying out the mixture of shredded treebark particles, stone aggregate particles and sand particles in windrows, and aerating the shredded treebark by mechanically turning the material in the windrows so that composting proceeds within the temperature range 42-60 degrees Celcius.

The invention extends to any soil substitute produced by the above-described method and more generally extends to a soil substitute comprised of an intimate mixture of shredded and composted treebark, stone aggregate particles and silica sand particles.

Preferably, the composted treebark is such that a major proportion of its particles are such as to pass through a 15 mm sieve.

BEST MODES OF CARRYING OUT THE INVENTION

In order that the invention may be more fully explained the presently preferred materials and production process will now be described in some detail.

The main constituents used in the production process are:

Shredded Treebark Course aggregate stone particles Fine aggregate stone particles Course silica sand particles Fine silica sand particles Minor Lignite minerals and chemicals as required Water

The basic specifications of these materials are as follows:

Shredded Treebark

Treebark is obtained from the bark of pinus radiata, or from the bark of the Pinus elliotti (Slash Pine). Alternate materials that can be used are shown as Table A.

The bark is trucked into the plant in random sizes, and is basically size separated through a trommel screen.

It is then further separated into smaller sizes by partially drying and is then mixed with sand, aggregates, dusts, chemicals and water in a single pass through a mechanical blending plant.

The chemical additives are: Nitrogen Lime 0-2% Iron 0-0.5% Trace elements 0-2% Phosphoros 0-2% Gypsum 0-5%

The trace elements which may be used are manganese, boron, copper, zinc and molybdenum.

The chemical addition is by weight, and the amounts vary according to the client/end use need.

TABLE A______________________________________The treebark may be obtained from one or more of the followingtimber species:______________________________________SOFTWOODPinus radiata Monterey PinePinus elliottii Slash PinePinus pinaster Maritime PinePinus sylvestris Scotch PinePinus strobus White PinePinus echinrta Short leaf PinePinusa taeda Loblolly PinePinus plaustris Long leaf PinePinus ponderosa Ponderosa PinePinus monticola Western White PinePinus contorta Lodgepole PinePinus lambertiana Sugar PineSequoia sempervirens RedwoodLibocedrus decurrens California Intense CedarTaidium distichum CypressLarix occidentalis Western LarchTsuga canadensis Eastern HemlockAbies magnifica Red FirAbies concolor White FirPseudotsuga menziessil Douglas FirPicea englemanii Engelman SpreuceAraucaria cunninghamii Hoop PineHARDWOODQuercus velutina Black OakQuercus alba White OakQuercus falcata Red OakQuercus stellata Post OakCarya spp. HickoryLiquidamber styraciflua Yellow PoplarCastanea dentata ChestnutJuglans nigra Black Walnut______________________________________

Coarse Aggregate

Two types of stone aggregates are used in the blend and these are generally in accordance with the specifications laid down by the Road Construction Authority of Victoria, and generally supported by the general specifications laid down in Australian Standard 2758.1 (Aggregates and Rock for Engineering Purposed-Part 1-Concrete Aggregates.)

In general, the course aggregates comply with R.C.A. Specification 812, and more particularly Table 812.021.

More specifically, the material added will comply with AS 2758.1, Table 1, Single Size Aggregate.

The mass of sample passing by % will be within the range:

______________________________________Sieve Size Range % Pass______________________________________6.70 mm 100%4.75 mm 85-100%2.36 mm 0-40% 0.075 mm 0-2%______________________________________

The desired range for "stone dust" is therefore 0.75 mm to 5.0 mm.

Sand

These basically apply to sands that are added to the blend, two types are added-- a "coarse" sand and a "fine" sand.

Fine aggregate grading requirements are shown in Australian Standard 2758.1 (Concrete Aggregates), and more specifically defined in R.C.A. Specification 610, Part 16, "Fine Aggregates".

The grading parameters are as follows:

______________________________________Sieve Size Range % Pass by Mass______________________________________4.75 mm 90-100%2.36 mm 75-100%1.18 mm 50-90%0.6 mm 30-60%0.3 mm 10-30%0.15 mm 2-10% 0.075 mm 0.3%______________________________________

The correct formulated blend may be obtained by using two types of sand, with the following specific individual grading limits:

______________________________________Fine SandSieve Size Range % Pass By Mass______________________________________2.36 mm 99-100%1.18 mm 97-100%600 micron 85-96%300 micron 45-70%150 micron 5-50% 75 micron 0-3%______________________________________

The desired range of fine sand is therefore 75 micron to 1.18 mm.

Coarse Sand

The specification for coarse sands is derived from R.C.A. Specification 702 (Subsurface Drainage), and the relevant table is 702.051 "Grading Requirements for Granular Filter Material".

The grading requirements are:

______________________________________Sieve Size Range % Pass by Mass______________________________________2.36 mm 100%1.18 mm 95-100%600 micron 70-98%300 micron 30-60%150 micron 0-12% 75 micron 0%______________________________________

This grading is defined as Al single and first stage filter material.

The desired range is between 300 micron and 2.36 micron.

The coarser range is required to allow high hydraulic conductivity of water, and to prevent binding of the other components. In addition the use of coarse sand allows root growth to go downwards, rather than becoming root bound because of an impervious and inpenetrable barrier.

Water Quality

Water is a critical material in the composting process and should be within the following range:

______________________________________Acid/alkali range [pH] 5.5 to 7.5Total dissolved salts 1000 parts per millionnot to exceed______________________________________

Lignite

Lignite may be added in the range 0-15% by weight. The source of lignite is from the fine gradings of brown coal less than 5 mm diameter.

Production Process

The consistent materials are firstly prepared and mixed as follows:

(a) Treebark is graded and prepared (b) Coarse aggregate is added (c) Fine aggregate is added (d) Coarse sand is added (e) Fine sand is added (f) Lignite (g) Minor minerals are added. Minor minerals are generally known as "clay minerals" and include materials such as zealyte, Kaolite, Bentonite etc.

The ingredient materials are blended in the following ratios by volume:

______________________________________Shredded Treebark 50-75%Coarse aggregates 10-20%Fine aggregates 10-20%Coarse sand 5-10%Fine sand 10-15%Lignite 0-15%Minor trace elements as required.______________________________________

The composting process consists of:

After single pass the material is laid out in windrows of any length, preferably about two meters high, and five meters wide.

Aeration of the windrows is carried out by mechanical means so that the product temperature is constantly within the range of 42-60 degrees Celcius.

If necessary water is added to replace losses caused by evaporation and microbial activity.

The final size of the composted treebark is within the range as follows:

______________________________________Passing 15 mm sieve 100%Retained on 8 mm sieve 25-35%Passing 3 mm sieve 30-40%______________________________________

These size parameters are chosen as research and testing indicates that this size range allows the greatest root growth to take place under the widest range or climatic conditions.

In addition, this size range allows the overall correct particle size to be achieved when mixed with other ingredients.

It has been found that the most desirable characteristics or specifications for the final material are as follows:

(a) Bulk density less than 1 (one). (b) Water content--Between 40% and 60%, as measured in Appendix F of the draft Australian Standard for Potting Mixes. (c) Salt level--not to exceed 1000 S/cm. (d) pH--between 6.5 and 7.5 as measured in Appendix G of Draft Australian Standard. (e) Ammonium ion content not to exceed 100 p.p.m. as measured in Appendix C of Draft Standards. (f) Nitrogen content (ammonium plus nitrate ions) must not exceed 250 p.p.m. as measured in Appendix C of the Draft Regulations. (g) Bio--assay--the root length of germinating radish. Seeds must reach a minimum of 80% of the root length of a control as measured in Appendix E of the Draft Australian Standard for Potting Mixes.

The above specifications can be achieved in material produced in large quantities in accordance with the production process described above. This material has excellent plant propagating properties and its physical properties are such that it can be used as a soil substitute in large scale landscaping. However, the particular materials and process parameters which have been described in some detail are advanced by way of example only and they could be varied or modified according to the availability of materials and particular requirements for soil substitutes in some applications. It is accordingly to be understood that the invention is in no way limited to these particular materials and process perameters and that many modifications and variations will fall within the scope of the appended claims.

Claims

1. A method for making a soil substitute comprising intimately mixing by volume from 50 to 70% of shredded treebark particles, from 10 to 40% of quarry stone particles and from 5 to 25% of silica sand particles to form a mixture and thereafter composting the shredded treebark particles while in the mixture; the quarry stone particles comprising relatively coarse aggregate having a range of particle sizes up to about 9.5 mm and relatively fine aggregate having a range of particle sizes up to about 6.7 mm; and the silica sand particles comprising relatively coarse and fine sand aggregates, a major proportion of the coarse sand particles falling within a size range of from 300 microns to 2.36 mm and a major proportion of the fine sand particles falling within a size range of from 75 microns to 1.18 mm.

2. The method of claim 1, wherein the composting of the shredded treebark is performed by laying out the mixture in windrows, adding water to said mixture to bring the water content of the mixture into the range 40 to 60% by weight, and aerating the shredded treebark by mechanically turning the mixture in the windrows so that composting proceeds within a temperature range of from 42.degree.-60.degree. C.

3. The method of claim 1, wherein from 0-15% by volume of lignite is added to the mixture prior to the composting step.

4. The method of claim 1, wherein the coarse particles comprise from 10 to 15% by volume of the mixture and the fine particles comprise from 10 to 15% by volume of the mixture.

5. The method of claim 1, wherein the coarse sand particles comprise from 5 to 10% by volume of the mixture and the fine sand particles comprise from 10 to 15% by volume of the mixture.

6. A soil substitute comprising an intimate mixture of from 50 to 70% of shredded and composted treebark particles, from 10 to 40% of quarry stone particles and from 5 to 25% of silica sand particles, a major proportion of the composted treebark particles being such as to pass through a 15 mm sieve, the quarry stone particles comprising relatively coarse aggregate having a range of particle sizes up to about 9.5 mm and relatively fine aggregate having a range of particle sizes up to about 6.7 mm, and the silica sand particles comprising relatively coarse and fine sand aggregates such that a major proportion of the coarse sand particles fall within a size range of from 300 microns to 2.36 mm and a major proportion of the fine sand particles fall within a size range of from 75 microns to 1.18 mm.