Patent Application
20230335654
The present invention relates to the technical field of photovoltaic devices, and more particularly to a solar cell and a manufacturing method thereof.
Solar cells are semiconductor devices that use sunlight to directly generate electricity. In order to receive sunlight, electrodes disposed on a light-receiving surface of the solar cell are in a form of grids. Sunlight is incident on the light-receiving surface of the solar cell through a gap of a top electrode, and is then converted to electric energy under photovoltaic effect of the solar cell.
Currently, an electron beam evaporation process or a magnetron sputtering process is typically adopted to form the top electrode of the solar cell. Before using the electron beam evaporation process or the magnetron sputtering process to evaporate metal materials, a process of forming a grid mask by a photoresist exposure development process is included. After evaporating metal materials, a process of dissolving the photoresist mask using a special corrosive liquid. After dissolving the photoresist mask, a cleaning process is included to facilitate removing the metal materials formed on the photoresist mask to obtain a complete top electrode.
As mentioned above, since the top electrode of the solar cell is formed using the electron beam evaporation process or the magnetron sputtering process, both of which are excessively complicated and limit the capacity of the solar cell, thereby resulting in that the solar cell can be used only in defined fields.
In view of the deficiencies in the prior art, the present invention provides a technical solution as follows.
According to an aspect of the present invention, provided is a manufacturing method of a solar cell, the method includes:
Optionally, the method of forming the top electrode specifically includes:
Optionally, the method of forming the back electrode specifically includes:
Optionally, after forming the top electrode, the manufacturing method further includes:
Optionally, the method of forming the anti-reflection film specifically includes: sequentially stacking and forming a Ti3O5 layer and a SiO2 layer on the partial region.
Optionally, the method of forming the electricity generation layer on the substrate includes:
Optionally, the substrate is made of an InP material.
Optionally, the electricity generation layer and the ohmic contact layer are made of a Group III-V semiconductor material.
Optionally, before forming the ohmic contact layer, the method further includes: before forming the top electrode, the manufacturing method further includes: cleaning the surface of the ohmic contact layer using a cleaning liquid.
According to another aspect of the present invention, provided is a solar cell made by the manufacturing method as described above.
When the solar cell is manufactured using the manufacturing method of the solar cell provided by the present invention, since the manufacturing process of the top electrode includes only printing and curing processes, the manufacturing process of the top electrode is effectively simplified, thereby improving the capacity of the solar cell.
In order to provide a clearer understanding of the objective, technical solutions and advantages of the present invention, embodiments of the present invention will be further described in detail in conjunction with the accompanying drawings. Examples of these preferred embodiments are illustrated in the accompanying drawings. The embodiments of the present invention illustrated in the accompanying drawings and described in the drawings are exemplary only, and the present invention is not limited to these embodiments. It is further noted here that, in order to avoid obscuring the present invention with unnecessary details, only structural and/or processing steps that are closely associated with the present invention are shown in the drawings while omitting other details that are not closely associated with the present invention.
Further, it will be understood that when an element such as layer, film, region, or substrate is referred to as being “on” another element or a surface of another element, the element can be directly on the other element or the surface of the other element, or an intermediate element may also be present. Optionally, when an element is referred to as being “directly on” another element or a surface of another element, no intermediate element is present.
As described in the background art, an electron beam evaporation process or a magnetron sputtering process is typically adopted to form the top electrode of the solar cell at present. However, since both of the processes described above are excessively complicated and limit the capacity of the solar cell, thereby resulting in that the solar cell can be used only in defined fields.
In order to overcome the above problems in the prior art, a manufacturing method of a solar cell capable of reducing manufacturing steps of a top electrode is provided in accordance with embodiments of the present invention, thereby simplifying the manufacturing process of the solar cell and improving capacity of the solar cell.
The manufacturing method of a solar cell according to the embodiments of the present invention will be described in detail below in conjunction with the drawings.
As shown in
Step S1, forming an electricity generation layer 2 on a substrate 1. Specifically, a back-surface field layer 21, a photovoltaic layer 22, and a window layer 23 are sequentially formed on the substrate 1. After connection of the back-surface field layer 21 and the photovoltaic layer 22, a higher barrier is formed, which acts as reflection for a few carriers flowing to the back-surface field layer 21 and may also reduce a surface state of the photovoltaic layer 22, lower a recombination rate of photon-generated carriers, and increase collection efficiency of the photon-generated carriers; the photovoltaic layer 22 can generate photon-generated carriers in an environment with sunlight exposure; the window layer 23 is the same as the back-surface field layer 21, and is connected with the photovoltaic layer 22 to form a higher barrier, which acts as reflection for a few carriers flowing to the window layer 23 to reduce the recombination rate of the photon-generated carriers and improve the collection efficiency of the photon-generated carriers. Preferably, the electricity generation layer 2 is made of a Group III-V semiconductor material.
Step S2, forming an ohmic contact layer 3 on a surface of the electricity generation layer 2 facing away from the substrate 1. The ohmic contact layer 3 is used to form ohmic contact with a metal material, which can reduce electrical energy loss caused by series resistance. Preferably, the ohmic contact layer 3 is made of a Group III-V semiconductor material.
Step S3, forming a back electrode 4 on a surface of the substrate 1 facing away from the electricity generation layer 2. Specifically, a Ti layer, a Pt layer, and an Au layer are sequentially stacked on the surface of the substrate 1 facing away from the electricity generation layer 2. Then, annealing is performed on the stacked Ti layer, Pt layer, and Au layer in an Ar gas environment to form the back electrode.
Step S4, forming a top electrode 5 on a surface of the ohmic contact layer 3 facing away from the electricity generation layer 2 using a printing process. Specifically, a screen printing plate is disposed on the ohmic contact layer 3, and then a nano silver paste layer is printed at a printing speed of 130 mm/s to 160 mm/s. Annealing and curing are performed on the nano silver paste layer to form the top electrode 5, in which the number of printed mesh counts of the screen printing plate is from 300 mesh to 500 mesh.
As mentioned above, when the solar cell is manufactured using the manufacturing method of the solar cell provided by the present embodiment, since the manufacturing process of the top electrode 5 includes only printing and curing processes, the manufacturing process of the top electrode 5 is effectively simplified, thereby improving the capacity of the solar cell.
Specifically, in the present embodiment, the top electrode 5 is a grid electrode including a plurality of metal strips arranged in parallel, in which a connecting portion is provided between two adjacent metal strips. The connecting portion between two adjacent metal strips is used to achieve conductive connection thereof. As another example, the top electrode 5 may also be a grid electrode.
Preferably, in the present embodiment, the substrate 1 is made of an InP material in order to guarantee epitaxial growth of the electricity generation layer 2.
Preferably, before the top electrode 5 is formed for good ohmic contact between the top electrode 5 and the ohmic contact layer 3, the manufacturing method further includes a step of cleaning the surface of the ohmic contact layer 3 using a cleaning liquid. The cleaning liquid is an acidic solution for cleaning an oxide film formed on the surface of the ohmic contact layer 3, thereby opening dangling bonds on the surface of the ohmic contact layer 3 to improve ohmic contact between the top electrode 5 and the ohmic contact layer 3.
Different from the first embodiment, in order to improve photovoltaic efficiency of the solar cell, the manufacturing method in the present embodiment further includes a step of forming an anti-reflection film 6. Specifically, as shown in
As shown in
It should be noted that relational terms, such as first and second and the like, are used herein only to distinguish one entity or operation from another entity or operation without necessarily requiring or implying any such actual relationship or order between such entities or operations. Moreover, terms “comprise/comprising”, “contain/containing” or any other variants thereof are non-exclusive, so that a process, method, article or device including a series of elements contains not only these elements, but also other elements not listed clearly, or further contains inherent elements of the process, method, article or device. An element preceded by “comprises” does not, without more constraints, preclude the existence of additional identical elements in the process, method, article, or apparatus that comprises the element.
Although embodiments of the present invention have been illustrated and described, it should be understood that various changes, substitutions, variations, alterations, and modifications can be made to these embodiments by those skilled in the art without departing from the principle and spirit of the present invention, and the present invention is defined by the appended claims and equivalents thereof
| Number | Date | Country | Kind |
|---|---|---|---|
| 202010933895.X | Sep 2020 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2021/099062 | 6/9/2021 | WO |