Patent Application
20130221373
1. Technical Field
The present invention relates to solar cells, and more particularly to devices and methods which employ a barrier layer between p-type layer formation and intrinsic layer formation.
2. Description of the Related Art
Fabrication of amorphous hydrogenated silicon (a-Si:H) solar cells is performed with the deposition of constituent active layers. The active layers include a p-type layer (or p-layer), an intrinsic layer (or i-layer) and an n-type layer (or n-layer), collectively a p-i-n or pin stack.
In some processes, a surface of the active layer is exposed to reactant by-products that may be present in the chamber or may be left over from previous processing. While solar cell fabrication using a single chamber is manufacturing friendly, this process suffers from the drawback of different species of elements or compounds being left over from previous processing. For example, when diborane is used for a p-type dopant source (e.g., boron), boron is left over in the chamber. If further processing is conducted in the same chamber a higher probability of contamination occurs, which can result in poor device performance.
In another example, trimethylborane(TMB) may be employed as a p-type dopant source. In this case, less boron is left over after depositing p-type a-SiC:H. However, for other materials, e.g., a-Ge:H, a-Si:H, etc., it is extremely difficult to provide boron to these films without contaminating reactants being present (the process is not flexible for all device materials). These contaminants usually settle at interfaces and affect device performance.
A method for forming a photovoltaic device includes depositing a p-type layer on a substrate. A barrier layer is formed on the p-type layer by exposing the p-type layer to an oxidizing agent. An intrinsic layer is formed on the barrier layer, and an n-type layer is formed on the intrinsic layer.
Another method for forming a photovoltaic device includes forming a transparent conductive electrode on a transparent substrate; depositing a p-type layer including silicon doped with boron on the transparent conductive electrode; forming an oxide layer on the p-type layer by exposing a surface of the p-type layer to oxygen; forming an intrinsic layer on the oxide layer; and forming an n-type layer on the intrinsic layer.
A photovoltaic device includes a transparent conductive electrode formed on a transparent substrate. A p-type layer includes silicon doped with boron formed on the transparent conductive electrode. A barrier layer includes an oxide formed at a surface of the p-type layer. An intrinsic layer is formed on the barrier layer. An n-type layer is formed on the intrinsic layer.
These and other features and advantages will become apparent from the following detailed description of illustrative embodiments thereof, which is to be read in connection with the accompanying drawings.
The disclosure will provide details in the following description of preferred embodiments with reference to the following figures wherein:
In accordance with the present principles, devices and methods are provided that result in improved device efficiency and performance. Photovoltaic devices, such as solar cells and the like, employ active layers that include a p-type layer (or p-layer), an intrinsic layer (or i-layer) and an n-type layer (or n-layer), collectively a p-i-n or pin stack. The present principles provide an intentionally formed barrier layer on the p-type layer prior to the formation of the i-layer. The barrier layer, which may include an oxide, may be naturally formed in an ambient environment that includes oxygen or the surface may be treated using an oxidizing agent, such as oxygen plasma. Oxygen is convenient for silicon-based films; however, devices using other materials may benefit from other types of films or layers.
In one embodiment, the p-type layer is formed by a deposition process in a processing chamber on a device or sample. The sample is then unloaded from the chamber and subjected to ambient conditions (e.g., exposed to air). This exposure may be referred to as an air break. The chamber is cleaned to remove any remaining p-type compounds. The sample is then reloaded to continue processing by forming the intrinsic layer and the n-type layer. This provides the option of employing a single chamber for multiple layer processing.
In another embodiment, the sample is not removed from the chamber and instead, the sample is exposed to an oxidizer, such as oxygen plasma, or other substance. The processing may continue in the same chamber by forming the intrinsic layer and the n-type layer.
It is to be understood that the present invention will be described in terms of a given illustrative architecture having substrates and photovoltaic stacks; however, other architectures, structures, substrates, materials and process features and steps may be varied within the scope of the present invention.
It will also be understood that when an element such as a layer, region or substrate is referred to as being “on” or “over” another element, it can be directly on the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly on” or “directly over” another element, there are no intervening elements present. It will also be understood that when an element is referred to as being “connected” or “coupled” to another element, it can be directly connected or coupled to the other element or intervening elements may be present. In contrast, when an element is referred to as being “directly connected” or “directly coupled” to another element, there are no intervening elements present.
A design for a photovoltaic device may be created for integrated circuit integration or may be combined with components on a printed circuit board. The circuit/board may be embodied in a graphical computer programming language, and stored in a computer storage medium (such as a disk, tape, physical hard drive, or virtual hard drive such as in a storage access network). If the designer does not fabricate chips or the photolithographic masks used to fabricate chips or photovoltaic devices, the designer may transmit the resulting design by physical means (e.g., by providing a copy of the storage medium storing the design) or electronically (e.g., through the Internet) to such entities, directly or indirectly. The stored design is then converted into the appropriate format (e.g., GDSII) for the fabrication of photolithographic masks, which typically include multiple copies of the chip design in question that are to be formed on a wafer. The photolithographic masks are utilized to define areas of the wafer (and/or the layers thereon) to be etched or otherwise processed.
Methods as described herein may be used in the fabrication of photovoltaic devices and/or integrated circuit chips with photovoltaic devices. The resulting devices/chips can be distributed by the fabricator in raw wafer form (that is, as a single wafer that has multiple unpackaged devices/chips), as a bare die, or in a packaged form. In the latter case, the device/chip is mounted in a single chip package (such as a plastic carrier, with leads that are affixed to a motherboard or other higher level carrier) or in a multichip package (such as a ceramic carrier that has either or both surface interconnections or buried interconnections). In any case the devices/chips are then integrated with other chips, discrete circuit elements, and/or other signal processing devices as part of either (a) an intermediate product, such as a motherboard, or (b) an end product. The end product can be any product that includes photovoltaic devices, ranging from toys, energy collectors, solar devices and other applications including computer products or devices having a display, a keyboard or other input device, and a central processor.
It should be further understood that material compounds will be described in terms of listed elements, e.g., SiC, SiGe, etc. These compounds include different proportions of the elements within the compound, e.g., SixCy where x/y≠1, etc. In addition, other elements may be included in the compound and still function in accordance with the present principles.
The present embodiments may be part of a photovoltaic device or circuit, and the circuits as described herein may be part of a design for an integrated circuit chip, a solar cell, a light sensitive device, etc.
Referring now to the drawings in which like numerals represent the same or similar elements and initially to
A first electrode 104 includes a transparent conductive material. Electrode 104 may include a transparent conductive oxide (TCO), such as, e.g., a fluorine-doped tin oxide (SnO2:F, or “FTO”), doped zinc oxide (e.g., ZnO:Al), indium tin oxide (ITO) or other suitable materials. For the present example, a doped zinc oxide is illustratively employed for electrode 104. The TCO 104 permits light to pass through to an active light-absorbing material beneath and allows conduction to transport photo-generated charge carriers away from that light-absorbing material. The TCO 104 may be deposited by a chemical vapor deposition (CVD) process, a plasma-enhanced (PE-CVD), etc.
The light-absorbing material includes a doped p-type layer 106 (e.g., a doped amorphous silicon (a-Si), a doped amorphous silicon carbide, microcrystalline silicon (μc-Si) layer, etc.). In this illustrative structure 100, layer 106 is formed on electrode 104. In one embodiment, p-type layer 106 includes boron as a dopant, although other p-type dopants may be employed. Layer 106 may be deposited by a chemical vapor deposition (CVD) process, or a plasma-enhanced (PE-CVD) using diborane or trimethylborane (TMB) gas. The p-type layer 106 may have a thickness of between about 5-20 nm. In particularly useful embodiments, layer 106 includes amorphous SiC. Other materials may be employed as well, e.g., amorphous Si, microcrystalline Si, etc.
An interface barrier layer 108 is formed on the p-type layer 106. The barrier layer 106 can protect an intrinsic layer 110 from contamination species that may form at the p-type layer/intrinsic layer interface. Barrier layer 108 may include an oxide layer formed by exposing the p-type layer 106 to air or to an oxidizing treatment. In particularly useful embodiments, the barrier layer 108 may be formed by, e.g., a 5-10 minute exposure to an ambient environment or by exposing the p-type layer 106, e.g., to a 25 watt power, oxygen plasma for 2 seconds. Other processes may also be employed. The barrier layer 108 may include one or more monolayers (e.g., 1 to about 20, although more layers may be employed) in thickness. In one example, silicon in layer 106 may form a silicon oxide 0.20-2.0 nm in thickness.
The barrier layer 106 may be formed by providing an air break during the fabrication process. This may include, after forming the p-type layer 106, removing the device 100 from a processing chamber in ambient air. In an alternative embodiment, the device 100 is left in the chamber and exposed to air. In still another embodiment, the device 100 is left in the chamber and exposed to oxygen plasma or other oxidizing agent.
It should be understood that the chamber may include boron reactants and by-products that remain in the chamber after the deposition of layer 106. There is potential that these materials can contaminate the intrinsic layer (110), which is formed on or over the p-type layer 106. In one embodiment, the chamber is purged, in particular, using fluorine based materials to clean the chamber by reacting with the boron based materials.
The intrinsic layer 110 of compatible material is formed on layer 108. Intrinsic layer 110 may be undoped and may include an amorphous silicon material, e.g., hydrogenated amorphous Si (a-Si:H). The intrinsic layer 110 may include a thickness of between about 100-300 nm, although other thicknesses are contemplated. The intrinsic layer 110 may include a-Si:H or a hydrogenated amorphous silicon carbide (a-SiC:H) and may be deposited by a chemical vapor deposition (CVD) process, or a plasma-enhanced (PE-CVD) using silane gas and hydrogen gas.
In one embodiment, a doped layer 112 (e.g., an n-type layer) is formed on the intrinsic layer 110. Layer 112 may include an n-type hydrogenated microcrystalline (μc-Si:H) or a-Si layer. Layer 112 may be deposited by a chemical vapor deposition (CVD) process, or a plasma-enhanced (PE-CVD). The n-type layer 112 may have a thickness of between about 5-20 nm. A back reflector and/or bottom electrode 114 may be formed by a reflective metal, such as Ag, Al, Au, etc. A suitable metal deposition process may be employed, e.g., physical or chemical vapor deposition, sputtering, electro or electroless plating, etc.
It should be understood that other material selections, layers, structure, etc. may be employed in device 100. These different combinations may benefit from an interface barrier layer 108 as described herein in accordance with the present principles. The barrier layer 108 provides an increase in open circuit voltage over devices fabricated without the barrier layer 108. The following FIGS. will present illustrative experimental results for showing improvements from a device having a barrier layer 108 formed during the fabrication process in accordance with the present principles.
A solar cell may be described in terms of a fill factor (FF). FF is a ratio of the maximum power point (Pm) divided by open circuit voltage (Voc) and short circuit current
Higher open circuit voltage provides greater efficiency if other parameters remain the same. Increased efficiency of photovoltaic devices even by a portion of one percent is of utmost importance in the present energy environment.
Referring to
It should be understood that different process parameters may be employed to provide better results. Different process parameters will be illustratively presented hereinafter.
Referring to
Referring to
Referring to
In one illustrative example, a device with no air break included FF=73, Voc=917 mV. A device with a 5 minute air break included FF=72, Voc=953 mV. A device with a 20 minute air break included FF=70, Voc=958 mV. A device with a 45 minute air break included FF=69, Voc=960 mV. Generally, FF degrades while Voc increases with air break time.
Referring to
Referring to
In block 302, a transparent conductive electrode is formed on a transparent substrate. In block 304, a p-type layer is deposited on the transparent conductive electrode or on the substrate. In one embodiment, the p-type layer includes silicon containing material (e.g., a-Si or a-SiC) doped with boron. In block 306, a barrier layer is formed on the p-type layer. The barrier layer may include an oxide or other material to act as a diffusion barrier between the p-type layer and the intrinsic layer. In one embodiment, the barrier layer is formed by exposing a surface of the p-type layer to oxygen. In one embodiment, the oxide layer includes between 1 to about 20 monolayers of oxide.
In block 308, in one embodiment, the barrier layer is formed in a same processing chamber where the p-type layer is deposited. In block 310, the oxide layer is formed by treating the p-type layer with oxygen plasma. This avoids the need for removing the device from the chamber to form the barrier layer.
In another embodiment, the barrier layer is formed by removing the substrate with the p-type layer from a processing chamber in block 312, and performing an air break or exposure break where the p-type layer is exposed to form the barrier layer in block 314. The air break may include exposing the p-type layer to ambient air conditions. The air break may include exposing the p-type layer for less than about 20 minutes, and more preferably for less than about 5 minutes. Since the FF may decrease with exposure time and Voc increases greatly initially and then levels off as described above, exposure time should be optimized to achieve the best results for a given device structure and application.
In block 316, the processing chamber may be cleaned with a fluorine-based gas before placing the substrate with the p-type layer back into the chamber. The fluorine-based gas may include NF3, SF6, CF4, etc.
In block 318, an intrinsic layer is foamed on the barrier layer. The intrinsic layer may include, e.g., undoped a-Si. The formation of the barrier layer protects the intrinsic layer from exposure to contaminant by-products (e.g., from boron containing compounds, etc.) formed during the deposition of the p-type layer. In block 320, an n-type layer is formed on the intrinsic layer. The n-type layer may include a-Si doped with an n-type dopant (e.g., P).
In block 322, processing continues to form other layers (e.g., a back-reflector, etc.), other structures, etc. and to complete the fabrication of the device(s).
Having described preferred embodiments of a solar cell made using a barrier layer between p-type and intrinsic layers (which are intended to be illustrative and not limiting), it is noted that modifications and variations can be made by persons skilled in the art in light of the above teachings. It is therefore to be understood that changes may be made in the particular embodiments disclosed which are within the scope of the invention as outlined by the appended claims. Having thus described aspects of the invention, with the details and particularity required by the patent laws, what is claimed and desired protected by Letters Patent is set forth in the appended claims.