Patent Application
20190006544
One or more embodiments of the present invention relate to a solar cell module having excellent light utilization efficiency.
A crystalline solar cell using a crystal semiconductor substrate such as a single crystal silicon substrate or a polycrystalline silicon substrate has a patterned metal electrode on a light receiving surface side. In a bifacial light incident type solar cell, the patterned metal electrode is also provided on a back surface side. In a monofacial light incident type solar cell, in order to effectively utilize light that has reached the back surface without being absorbed by the semiconductor substrate, a light reflective metal electrode is generally provided on the entire back surface side of the cell. Particularly, when a crystal semiconductor substrate having a small thickness is used from the viewpoint of cost reduction and the like, providing a planar metal electrode on the back surface side is effective since an amount of light reaching the back surface of the cell without being absorbed by the semiconductor substrate is large.
Since the crystalline solar cell has a small area of one cell, there is practically used a solar cell string that has a plurality of cells electrically interconnected via a wiring member and is modularized by encapsulating into between a glass plate on the light receiving surface side and a back sheet on the back surface side. In solar cell strings, a gap of approximately 2 to 4 mm is generally provided between cells provided adjacently. By reflecting the light irradiated to this gap and making it incident on the cell, to contribute to power generation, the module conversion efficiency can be improved.
In order to effectively utilize light irradiated to the gap between cells, a light scattering reflective back sheet is used in a monofacial light incident type solar cell module. Patent Literature 1 and Patent Literature 2 propose a method for increasing an incident amount of reflected light from the light receiving surface side or the back surface side of the cell, by providing a reflective material having an uneven shape at a position corresponding to the gap between cells and controlling a reflection direction of light.
As described in Patent Literature 1, in a monofacial light incident type solar cell module using a cell provided with a metal electrode on the entire back surface side, even when reflected light from the back sheet side strikes the back surface of the cell, it does not contribute to power generation. Therefore, it is necessary to adjust an angle of the reflected light such that the reflected light from the back sheet side is reflected again by a glass plate on the light receiving surface side and enters the cell from the light receiving surface side. However, even by adjusting a shape or an angle of unevenness of the reflective material provided on the back sheet, it is not possible to completely eliminate the reflection of light to the back surface of the cell.
In a bifacial light incident type solar cell module, a transparent back sheet is used in order to utilize light from the back surface side. As described above, providing the reflective material at a position corresponding to the gap between the cells allows refection and effective utilization of the light irradiated to the gap between the cells from the light receiving surface (front surface) side. In the bifacial light incident type solar cell module, since the metal electrode on the back surface side of the cell is in the form of a grid, the light reflected on the back sheet side and striking the back surface side of the cell can also be used effectively. However, since the back sheet in a region disposed with the cell is transparent, the light incident on the cell from the light receiving surface side to reach the back surface of the module without being absorbed by the semiconductor substrate is transmitted through the back sheet and dissipated outside the module.
A part of the reflected light from the back sheet to the back surface of the cell in the monofacial light incident type module, and a part of the light transmitted through the back sheet in the bifacial light incident type module are repeatedly reflected and scattered to enter the cell. However, loss occurs in this process. Therefore, an amount of light incident on the cell is small, and there is room for improvement in enhancing light utilization efficiency. In view of the above, one or more embodiments of the present invention provide a solar cell module enabling effective incidence on the cell, of both the light irradiated to the gap between the cells and the light transmitted through the cell and reaching the back surface side, and having high light utilization efficiency.
The solar cell module according to one or more embodiments of the present invention includes a solar cell string in which a plurality of solar cells arranged apart from each other are interconnected via a wiring member, a light-receiving-surface protective member disposed on a light receiving surface side of the solar cell string, and a back-surface protective member disposed on a back surface side of the solar cell string. In some embodiments, the light-receiving-surface protective member is light transmissive. In some embodiments, the back-surface protective member preferably is light reflective. Between the solar cell string and the light-receiving-surface protective member, a light-receiving-surface encapsulant is preferably disposed in one or more embodiments, while a back-surface encapsulant may be preferably disposed between the solar cell string and the back-surface protective member.
In one or more embodiments, a solar cell includes a photoelectric conversion part, a patterned light-receiving-surface metal electrode provided on a light receiving surface of the photoelectric conversion part, and a patterned back-surface metal electrode provided on a back surface of the photoelectric conversion part. On the back surface of the solar cell, a metal film is provided between the photoelectric conversion part and the back-surface protective member. On a peripheral edge of the back surface of the solar cell, there is a region (cell exposed region) provided with no metal film. At least a part of the patterned back-surface metal electrode is provided in the cell exposed region.
In one or more embodiments, it is preferable that the metal film is in contact with the photoelectric conversion part. In one or more embodiments, an area of the cell exposed region on the back surface of the solar cell is preferably about 0.05 to 0.5 times an area of a region provided with the metal film.
In one or more embodiments, it is preferable that a light reflection member is provided in a region disposed with no solar cell (a gap between adjacent solar cells) The light reflection member may have a higher reflectance than the back-surface protective member. In one or more embodiments, it is preferable that the light reflection member provided in the gap between the adjacent solar cells has an uneven structure on a surface on the light receiving surface side. A convex portion of the uneven structure may extend in parallel with a side of the solar cell arranged adjacently. When the light reflection member is disposed between the back-surface protective member and the back-surface encapsulant, contact of the light reflection member with the solar cell or a wiring member can be prevented by making a thickness of the back-surface encapsulant larger than a thickness of the light-receiving-surface encapsulant.
In some embodiments, since reflected light can be effectively utilized by disposing the metal film having a smaller area than that of the solar cell in between with the back-surface protective member on the back surface side of the solar cell, a solar cell module with high conversion efficiency can be obtained.
The cell of one or more embodiments includes metal electrodes 60 and 70 on a light receiving surface side and a back surface side of a photoelectric conversion part 50, respectively. As shown in
On the back surface side of the cell of one or more embodiments, a metal film 76 is disposed. In a form shown in
The cell 102 shown in
As the intrinsic silicon-based thin-films 21 and 22 and the conductive silicon-based thin-films 31 and 32, amorphous silicon thin-films, microcrystalline silicon thin-films (thin films containing amorphous silicon and crystalline silicon), and the like are used. Among these, amorphous silicon thin-films may be preferable. In some embodiments these silicon-based thin-films can be formed by, for example, a plasma-enhanced CVD method. As p-type and n-type dopant gases at a time of forming the conductive silicon-based thin-films 31 and 32, B2H6 and PH3 may be preferably used.
As the transparent conductive films 41 and 42, for example, there is used a transparent conductive metal oxide composed of indium oxide, tin oxide, zinc oxide, titanium oxide, composite oxide of these, or the like. Among these, an indium-based composite oxide containing indium oxide as a main component is preferable in some embodiments. The conductivity and reliability of the transparent conductive film can be improved by adding impurities such as Sn, Ti, W, Ce, and Ga to indium oxide.
In one or more embodiments, the light-receiving-surface metal electrode 60 is provided on the transparent conductive film 41, and the back-surface metal electrode 70 is provided on the transparent conductive film 42. These metal electrodes have a predetermined pattern shape, and light can be taken in from a portion provided with no metal electrode. Although the pattern shape of the metal electrodes is not particularly limited, it may be preferable to be formed in the form of a grid formed by a plurality of finger electrodes 71 aligned in parallel, and a bus bar electrode 72 extending perpendicular to the finger electrodes, as shown in
In one or more embodiments, it is preferable to set the number of the finger electrodes and the bus bar electrodes (inter-electrode distance) so as to optimize a balance between an increase of a light intake amount and a reduction of a series resistance. In
In one or more embodiments, by interconnecting metal electrodes of adjacent cells via a wiring member, a solar cell string is formed. As the wiring member, solder-plated copper foil or the like is used. By using the wiring member having an uneven structure on the light receiving surface side (an connecting surface with the back-surface metal electrode), it is possible to scatter light incident on the wiring member and take the re-reflected light at the light-receiving-surface protective member into the cell, thereby enhancing light utilization efficiency. For connection between the metal electrode and the wiring member, a conductive adhesive, solder, or the like is used.
From the viewpoint of preventing leakage through the wiring member, in some embodiments adjacent cells are arranged apart from each other by about several millimeters. As shown in
As shown in
In one or more embodiments, the metal film 76 has a function of reflecting light that is incident on the cell from the light receiving surface side and transmitted to the back surface side without being absorbed by the photoelectric conversion part 50, and of making the light re-incident on the cell from the back surface side (cell-transmitted re-incident light LC in
In one or more embodiments, the metal film 76 can be formed by cutting a metal foil such as copper foil or silver foil into a predetermined shape. From the viewpoint of resistance reduction and handleability, a thickness of the metal film may be preferably from 1 to 30 μm, more preferably from 3 to 20 μm, and still more preferably from 5 to 15 μm. The metal film having a predetermined shape may be disposed on the back surface of the cell that has already been connected with the wiring member. As will be described later, encapsulating the solar cell string with the encapsulant enables fixation of a position of the metal film disposed on the back surface of the cell. The metal film 76 does not need to be continuous in the plane, and for example, a metal film may not be provided in a connection region (a region formed with the bus bar electrode 72) of the wiring member 83.
In one or more embodiments, the metal film may be disposed between the photoelectric conversion part 50 and the back-surface metal electrode 70, and between the back-surface metal electrode 70 and the wiring member 83. Further, the metal film may be disposed between the encapsulant 95 and the back-surface protective member 92. However, from the viewpoint of reducing the resistance and increasing an intake amount of the cell-transmitted re-incident light LC to be taken into the cell, the metal film may be preferably arranged to be in contact with the back-surface metal electrode 70, and may be more preferably also in contact with the photoelectric conversion part 50, in addition to the back-surface metal electrode.
By disposing the encapsulant on the light receiving surface side and the back surface side of the solar cell string including the metal film 76 on the back surface side, and encapsulating between the light-receiving-surface protective member 91 and the back-surface protective member 92, a module of one or more embodiments is obtained. As the encapsulant 95, it may be preferable to use a transparent resin such as a polyethylene resin composition containing an olefinic elastomer as a main component, polypropylene, ethylene/α-olefin copolymer, ethylene/vinyl acetate copolymer (EVA), ethylene/vinyl acetate/triallyl isocyanurate (EVAT), polyvinyl butyrate (PVB), silicon, urethane, acrylic, or epoxy. The material of the encapsulant on the light receiving surface side and the back surface side may be the same or different.
In one or more embodiments, the light-receiving-surface protective member 91 is light transmissive, and glass, transparent plastic, or the like is used. As the back-surface protective member 92, a light reflective film may be preferably used. Meanwhile, the back-surface protective member may be light transmissive, but in a case where a light transmissive back-surface protective member is used, a light reflection member may be preferably provided in a region provided with no cell as shown in
By performing heat compression while the encapsulant and the protective member are disposed and laminated on each of the light receiving surface side and the back surface side of the solar cell string, the encapsulant also flows between the cells and to an edge of the module, to cause modularization. A pressure at the time of modularization causes the metal film 76 to deform to be in contact with the surface of the photoelectric conversion part (see
In some embodiments most of the light incident from a light receiving surface side of the module is irradiated to the cell from the light receiving surface side, but a part of the light is irradiated to a gap between adjacent cells and reaches the back surface side of the module. Further, a part of the light incident on the cell from the light receiving surface side reaches the back surface side of the cell without being absorbed by the photoelectric conversion part 50. Reflecting the light reaching the back surface and making the light re-incident on the cell enable improvement of light utilization efficiency and enhancement of the module conversion efficiency.
The module according to one or more embodiments of the present invention is provided with the metal film 76 having a smaller area than the cell on the back surface side of the cell, thereby having high light utilization efficiency. With reference to
In one or more embodiments, light irradiated to a gap between the cells is reflected to the light receiving surface side by the back-surface protective member 92. A part of the light reflected by the back-surface protective member 92 is again transmitted through the gap between the cells and reaches the light receiving surface side, is re-reflected at an air interface of the light-receiving-surface protective member 91, and enters the cell from the light receiving surface side (light-receiving-surface side re-incident light LA).
In one or more embodiments, a part of the light irradiated to the gap between the cells and reflected by the back-surface protective member 92 reaches the back surface of the cell. Most of the reflected light reaching the back surface side of the cell from the back-surface protective member 92 reaches a peripheral region of the cell. In a monofacial light incident type cell provided with a metal electrode on the entire back surface side, light from the back surface side of the cell cannot be taken into the photoelectric conversion part. On the other hand, in the module according to one or more embodiments of the present invention, there is the cell exposed region where the metal film 76 is not provided, on the peripheral edge of the back surface of the cell. Therefore, the light reaching the back surface of the cell from the back-surface protective member 92 can be taken into the cell from the cell exposed region (back-surface side re-incident light LB).
In one or more embodiments where the metal film 76 is not provided on the back surface side of the cell, the light incident on the cell from the light receiving surface side and transmitted to the back surface side without being absorbed by the photoelectric conversion part 50 is, such as light Lx shown by the dotted line in
In the cell exposed region where the metal film 76 is not provided, optical loss occurs due to the cell-transmitted light reaching the back-surface protective member. However, in one or more embodiments reducing an area of the cell exposed region allows reduction of influence of loss of light transmitted through the cell exposed region. On the other hand, providing the cell exposed region causes the back-surface side re-incident light LB to be taken into the cell as described above. Since the increase in the back-surface side re-incident light LB due to the provision of the cell exposed region is smaller than the loss of the cell-transmitted re-incident light, light utilization efficiency as a whole can be improved.
As described above, by providing the metal film 76 on the back surface side of the cell in one or more embodiments, light (mainly infrared light) transmitted through the cell can be reflected by the metal film, to increase the intake amount of the cell-transmitted re-incident light LC. By providing the cell exposed region disposed with no metal film on the peripheral edge on the back surface of the cell, the back-surface side re-incident light LB derived from the reflected light from the back-surface protective member can be taken into the cell. Therefore, the module according to one or more embodiments of the present invention is excellent in light intake efficiency.
In one or more embodiments, the back-surface metal electrode is also formed in the cell exposed region at the peripheral edge of the back surface. Since the metal electrode 71a is provided in the cell exposed region, carriers at the peripheral edge of the cell can be effectively collected. Furthermore, since contact of the metal film 76 with the photoelectric conversion part 50 causes reduction of the in-plane resistance of the surface of the photoelectric conversion part, carrier transport efficiency to the back-surface metal electrode tends to be improved and the fill factor of the module tends to be improved. Particularly, in a case where the transparent conductive film 42 is provided on the surface of the photoelectric conversion part 50 as in the heterojunction cell, since contact of the transparent conductive film 42 with the metal film 76 allows smooth movement of carriers in the plane, the fill factor tends to be improved.
In one or more embodiments, the shape of the metal film 76 and the shape of the cell exposed region, and the size and area ratio of these, may be set from the viewpoint of light intake efficiency and resistance reduction. For example, a ratio W1/W0 of a width W1 of the metal-film disposed region to a cell width W0 may be preferably about 0.8 to 0.95, and more preferably about 0.83 to 0.92. Further, a width from an edge of the cell to the metal-film disposed region, that is, a width W2 of the cell exposed region may be preferably 3 to 30 mm, and more preferably 5 to 20 mm. As the width of the cell exposed region increases, an intake amount of the back-surface side re-incident light LB tends to increase and the intake amount of the cell-transmitted re-incident light LC tends to decrease. As the width W1 of the metal-film disposed region increases, an area ratio of the metal-film disposed region also increases. Therefore, the resistance on the back surface side of the cell tends to decrease and the fill factor of the module tends to be improved. A ratio (S2/S1) of an area S2 of the cell exposed region to an area S1 of the metal-film disposed region may be preferably 0.05 to 0.5, and more preferably 0.125 to 0.35.
In
In one or more embodiments, the metal film can also be formed using other than the metal foil. For example, the metal film may be formed by a printing method such as inkjet or screen printing, or a wet process such as a plating method, and the metal film may be formed by a dry process such as a vacuum deposition method, a sputtering method, or a CVD method. These metal films may be formed either before or after the back-surface metal electrode 70 (the finger electrode and the bus bar electrode). Further, the back-surface metal electrode and the metal film may be formed at the same time. For example, as shown in
The module according to one or more embodiments of the present invention may be provided with a light reflection member having a higher reflectance than that of the back-surface protective member, in a region disposed with no cell. Providing the light reflection member at a position provided with no cell allows efficient reflection of light irradiated to the gap between the cells and an increase in the light-receiving-surface side re-incident light LA and the back-surface side re-incident light LB, and enables enhancement of light utilization efficiency.
In one or more embodiments, in accordance with an increase of an angle θ formed by the bottom surface of the light reflection member and the inclination of the convex portion, a propagation angle θ1 of the light reflected on the light receiving surface of the module increases. As the angle θ1 increases, the reflectance at the air interface of the light-receiving-surface protective member 91 increases. A refractive index of resin and glass is about 1.4 to 1.5, and a critical angle at the air interface is about 40°. Since total reflection occurs when the θ1 becomes larger than the critical angle, the light-receiving-surface side re-incident light LA can be further increased. On the other hand, when the inclination angle θ of the convex portion of the light reflection member is excessively large, there is a tendency that the amount of light that is reflected by the light reflection member to reach the metal-film disposed region on the back surface of the cell becomes large. Therefore, the inclination angle θ of the convex portion of the light reflection member may be preferably 200 to 450, and more preferably 25°≤θ≤40°.
From the viewpoint of controlling a reflection direction of light from the light reflection member, it may be preferable in one or more embodiments to provide the convex portions 981 to 986 extending in a predetermined direction as shown in
As shown in
In one or more embodiments, a width of the light reflection member may be equal to an interval between adjacent cells (a width of the region Q disposed with no cell), or may be different from the interval between the cells. From the viewpoint of enhancing utilization efficiency of reflected light, it may be preferable that the width of the light reflection member is larger than the interval between adjacent cells, and the reflecting member is disposed over the entire region where the cell is not disposed.
In one or more embodiments, when the width of the light reflection member is larger than the interval between adjacent cells, the region disposed with the light reflection member and the region disposed with the cell overlap each other. Therefore, in one or more embodiments, it is preferable to select the thickness and shape of the light reflection member, the material and thickness of the encapsulant, and the like, so as not to cause insulation failure or cell breakage due to contact between the light reflection member and the cell. For example, insulation failure and cell breakage may be prevented by increasing the thickness of the encapsulant provided between the cell and the back-surface protective member. Further, increasing the thickness of the encapsulant on the back surface side can also prevent insulation failure due to contact between the light reflection member and the wiring member. On the other hand, an increase of the thickness of the protective member is likely to cause optical loss due to light absorption of the encapsulant existing between the light-receiving-surface protective member 91 and the cell. Therefore, in one or more embodiments, it is preferable to increase the thickness of the back-surface encapsulant disposed between the cell and the back-surface protective member without changing the thickness of the light-receiving-surface encapsulant disposed between the cell and the light-receiving-surface protective member. The thickness of the back-surface protective member may be preferably, for example, 1.2 times or more the thickness of the light-receiving-surface side protective member, and more preferably 1.5 times or more.
In one or more embodiments, the light reflection member 98 may be simply placed on the back-surface protective member 92, but it may be preferable to fix the light reflection member 98 by bonding or the like to the surface of the back-surface protective member. Alternatively, there may be used a back-surface protective member with a light reflection member buried inside. In order to improve efficiency of the module production process, it may be preferable to perform encapsulating while stacking the back-surface protective member having the light reflection member fixed on the surface and the solar cell string such that the cell is arranged in a region provided with no light reflection member.
Hereinafter, one or more embodiments of the present invention will be described in more detail by comparing examples and comparative examples, but the present invention is not limited to the following examples.
On a light receiving surface side of a 6-inch n-type single crystal silicon substrate (semi-square type having a side length of 156 nm) with a thickness of 160 μm on which texture is formed on the front and back, an intrinsic amorphous silicon layer with a film thickness of 4 nm and a p-type amorphous silicon layer with a film thickness of 6 nm were formed by a plasma-enhanced CVD method. Thereafter, on a back surface side of the silicon substrate, an intrinsic amorphous silicon layer with a film thickness of 5 nm and an n-type amorphous silicon layer with a film thickness of 10 nm were formed by a plasma-enhanced CVD method. On each of the p layer and the n layer, an ITO layer with a film thickness of 100 nm was formed by a sputtering method. After that, according to a method described in an example of WO 2013/077038, a patterned collector electrode in the form of a grid including a finger electrode and a bus bar electrode was formed on each of the front and back ITO layers, to obtain a heterojunction solar cell. Three bus bar electrodes were provided on both of the light receiving surface and the back surface, and the number of the finger electrodes on the back surface side was set to twice the number of the finger electrodes of the light receiving surface electrode.
A wiring member was connected to the light receiving surface electrode and the back surface electrode of the cell via a conductive adhesive, to produce a solar cell string in which nine solar cells were interconnected in series. An interval between adjacent cells was 2 mm. As the wiring member, a diffusion tab made by coating, with silver, a surface of a copper foil having an uneven structure.
A total of 54 solar cells were interconnected in series by placing an EVA sheet on a white sheet glass as the light-receiving-surface side protective member, then arranging six rows of solar cell strings on the EVA sheet such that a distance between adjacent strings was 2 mm, and providing an electrical connection at an edge as shown in
A solar cell module was produced in the same manner as in Example 1, except that the size of the copper foil was changed such that a length of one side was 136 mm, and a region of 10 mm from the edge of the cell was made to be the cell exposed region.
A solar cell module was produced in the same manner as in Example 1, except that the size of the copper foil was changed such that a length of one side was 126 mm, and a region of 15 mm from the edge of the cell was made to be the cell exposed region.
There was used a back-surface protective member made by bonding the same diffusion tab (width 5 mm, the inclination angle θ of the convex portion θ=30°) as that used as the wiring member at the time of producing the solar cell string, on a light receiving surface side of the back sheet. The diffusion tab was located between adjacent cells in the solar cell string and between cells between adjacent solar cell strings, and arranged such that an extending direction of the convex portion was parallel to a side of the adjacent cell. A solar cell module was produced in the same manner as in Example 2, except that there was used a back sheet bonded with the diffusion tab as the light reflection member.
A solar cell module was produced in the same manner as in Example 1, except that the copper foil was not disposed between the solar cell and the EVA sheet on the back surface side.
A solar cell module was produced in the same manner as in Example 1, except that the size of the copper foil was changed such that a length of one side was 156 mm, that is, the same size as the cell, and no cell exposed region was provided.
Measurement was made on conversion properties (short-circuit current (Isc), open-circuit voltage (Voc), fill factor (FF), and maximum output (Pmax)) of the solar cell modules of the above examples and comparative examples. Table 1 shows the width W2 of the cell exposed region of each module, a ratio S2/S1 of an area of the cell exposed region to an area of the metal-film disposed region, the presence or absence of disposition of the light reflection member in an interval between the cells, and module characteristics. It should be noted that the module characteristics in Table 1 are shown as relative values with the characteristic 1 of the solar cell module of Comparative Example 1 taken as 1.
In comparison between Comparative Example 1 in which the metal film was not provided on the back surface and Example 2 in which the metal film was provided on the back surface such that the region 10 mm from the edge of the cell was made to be the cell exposed region, it is shown that, in Example 2, the Isc was improved by 0.5%, the FF was improved by 0.5%, and the Pmax was improved by 1% as compared with Comparative Example 1. On the other hand, in comparison between Comparative Example 1 with Comparative Example 2 in which the metal film was provided on the entire back surface of the cell, it is shown that, in Comparative Example 2, the FF was improved by 0.6% as compared with Comparative Example 1, but the Isc decreased by 1% and the Pmax decreased by 0.4%.
Improvement of the FF in Example 2 and Comparative Example 2 is considered to be resulting from reduced resistance of the back surface side of the cell by providing the metal film to be in contact with the back surface of the cell. In Examples 1 to 3 and Comparative Example 2, it is considered that the reduction in resistance due to the provision of the metal film on the back surface side contributes to the improvement of the FF, also from the fact that the FF tends to improve as the width W2 of the cell exposed region is smaller and the area of the metal film is larger.
In Comparative Example 2, it is considered that the cell-transmitted re-incident light LC is increased as compared with Comparative Example 1 by providing the metal film on the back surface of the cell. However, it is considered that the Isc has decreased because the incidence of the back-surface side re-incident light LB, which is the reflected light from the back sheet, on the cell is hindered. On the other hand, in Example 2, the Isc is considered to have increased because there is the region (cell exposed region) having the width of 10 mm and provided with no metal film at the peripheral edge of the cell, so that the cell-transmitted re-incident light LC is taken into the cell in the region provided with the metal film, and the back-surface side re-incident light LB is incident on the cell from the cell exposed region.
Even in Example 1 in which the width W2 of the cell exposed region was 5 mm, the Isc was improved as in Example 2 as compared with Comparative Example 1 and Comparative Example 2. On the other hand, in Example 3 in which the width W2 of the cell exposed region was 15 mm, the FF was improved as compared with Comparative Example 1 in which no metal film was provided on the back surface of the cell, but the Isc was equivalent to Comparative Example 1. It is considered that, since most of the back-surface side re-incident light LB is incident on the cell from the peripheral edge of the back surface of the cell, a significant increase in the back-surface side re-incident light LB cannot be expected even by increasing the W1 as compared with the predetermined value, but the cell-transmitted re-incident light LC decreases with an increase in the W2 (decrease in the area of the metal film). That is, it is considered that Example 3 has shown the Isc equivalent to that of Comparative Example 1 since the increase in the cell-transmitted re-incident light LC due to the provision of the metal film on the back surface of the cell is substantially equal to the decrease in the back-surface side re-incident light LB.
These results have shown that, while the FF tends to increase with an increase in the area of the metal film, there is an optimum value of the area of the metal film (a width of the exposed region) that maximizes the Isc due to the balance between the back-surface side re-incident light LB and the cell-transmitted re-incident light LC. Considering these factors, it is possible to obtain a module excellent in conversion efficiency by setting the size of the metal film to be provided on the back surface of the cell.
In Example 4 in which the light reflection member was provided at a position corresponding to the gap between adjacent cells, the Isc was further improved by 1% as compared with Example 2. This is considered to be resulting from that, since the convex portion of the light reflection member has an inclination, an angle of the light reflected on the light receiving surface of the module becomes constant, and the light reflection at the glass-air interface has increased to increase the light-receiving-surface side re-incident light LA, in addition to the increase in the back-surface re-incident light LB to the exposed region as the light incident on the gap between the cells is specularly reflected by the surface of the light reflection member.
Although the disclosure has been described with respect to only a limited number of embodiments, those skilled in the art, having benefit of this disclosure, will appreciate that various other embodiments may be devised without departing from the scope of the present invention. Accordingly, the scope of the invention should be limited only by the attached claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2016-046978 | Mar 2016 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2017/002167 | Jan 2017 | US |
| Child | 16126682 | US |