The disclosure relates to a solar cell.
Generally, collective electrodes such as finger electrodes and busbar electrodes formed on a surface of a solar cell are formed by applying conductive paste to the surface of the solar cell by a printing technique such as screen printing.
Japanese Patent Application Publication No. Hei 11-103084 (Patent Document 1) proposes that when collective electrodes are formed, a screen printing process is repeated a plurality of times to reduce uneveness on surfaces of the collective electrodes and reduce the resistance values thereof. Japanese Patent Application Publication No. 2007-224191 (Patent Document 2) proposes that collective electrodes are formed using a conductive paste composition containing silicone resin.
An embodiment of a solar cell includes a photoelectric conversion layer formed on a substrate made of a semiconductor material; and a first finger electrode formed by applying conductive paste to a main surface side of the photoelectric conversion layer by printing, an average of standard deviations of heights of uneveness on a surface of the first finger electrode being 5.0 μm or less.
Embodiments are described below. It should be noted, however, that the following embodiments are merely illustrative examples, and the invention is not limited to the following embodiments. Moreover, in the drawings, members having virtually identical functions may be denoted by the same reference signs.
As illustrated in
An indented structure called a textured structure is provided on at least one of main surfaces of substrate 31. It should be noted that the “textured structure” means an indented structure formed to reduce surface reflection and increase the amount of light absorbed by substrate 31. A specific example of the textured structure is an indented structure with pyramid shapes (square pyramid shapes or square frustum shapes) obtained by performing anisotropic etching on a (100) surface of a single-crystal silicon substrate.
N-type semiconductor layer 32 is disposed on one main surface of substrate 31. N-type semiconductor layer 32 can be formed of, for example, n-type amorphous silicon. An i-type semiconductor layer which is thin enough to provide no substantial contribution to power generation and which is made of a substantially intrinsic semiconductor may be provided between n-type semiconductor layer 32 and substrate 31. The i-type semiconductor layer can be formed of, for example, i-type amorphous silicon.
Transparent conductive oxide film 33 as a translucent or transparent film is disposed on n-type semiconductor layer 32. Transparent conductive oxide film 33 can be formed of, for example, indium tin oxide (ITO) or the like.
N-side electrode 34 is disposed on transparent conductive oxide film 33.
P-type semiconductor layer 35 is disposed on other main surface of substrate 31. P-type semiconductor layer 35 can be formed of, for example, p-type amorphous silicon. An i-type semiconductor layer which is thin enough to provide no substantial contribution to power generation and which is made of a substantially intrinsic semiconductor may be provided between p-type semiconductor layer 35 and substrate 31. The i-type semiconductor layer can be formed of, for example, i-type amorphous silicon. By forming p-type semiconductor layer 35 on substrate 31, a pn junction is formed to function as a photoelectric conversion layer.
Transparent conductive oxide film 36 as a translucent or transparent film is disposed on p-type semiconductor layer 35. Transparent conductive oxide film 36 can be formed of, for example, indium tin oxide (ITO) or the like.
P-side electrode 37 is disposed on transparent conductive oxide film 36. It should be noted that in
Though not shown in the drawing, solar cells 1 are disposed in a filler layer disposed between a first protective member and a second protective member. For example, the first protective member may be formed of a translucent or transparent plate of glass, resin, or the like, and the second protective member may be formed of a resin sheet or the like. Alternatively, both the first protective member and the second protective member may be formed of a glass plate or a resin plate. The filler layer may be formed of, for example, crosslinkable resin such as ethylene-vinyl acetate copolymer (EVA), non-crosslinkable resin such as polyolefin, or the like. It should be noted that in this specification, a light-receiving surface means a side of solar cell 1 on which the transparent first protective member is disposed, and a back surface means a side of solar cell 1 on which the second protective member is disposed.
One ends of wiring tabs 4 are electrically connected to surfaces of second electrodes 3. Other ends of wiring tabs 4 are electrically connected to second electrode (busbar electrode) 3 on a front surface of an adjacent solar cell.
P-side electrode 37 can be formed by applying conductive paste by printing. P-side electrode 37 with small uneveness in which the average of standard deviations of the heights of uneveness is 5.0 μm or less, such as illustrated in
The conductive paste is not particularly limited, but low-temperature curing conductive paste is preferably used. An example of low-temperature curing conductive paste is a conductive paste which thermally cures at temperatures from 150 to 250° C. An example of such a low-temperature curing conductive paste is a conductive paste disclosed in Patent Document 2, which comprises silicone resin, conductive powder, thermosetting components, a curing agent, and a solvent. The thermosetting components may include, for example, epoxy resin with an epoxy equivalent of 1000 or less and epoxy resin with an epoxy equivalent of 1500 or more.
As the silicone resin, a general one can be used. Examples are straight silicone resins such as methyl silicone resin and methylphenyl silicone resin, and modified silicone resins modified with epoxy resin, alkyd resin, polyester, acrylic resin, and the like. These can be used singly or in combination. As the conductive powder, a general one can be used as long as the general one has conductivity. Examples are powder of silver, copper, nickel, aluminum, copper coated with silver, aluminum coated with silver, carbon, and the like. Examples of the thermosetting components are epoxy resins and blocked polyisocyanate compounds. As the curing agent, generally used imidazole and derivatives thereof, tertiary amines, Lewis acids containing boron fluoride, and complexes or salts thereof can be used. The solvent is not particularly limited, but, in the case where the solvent is applied by printing or the like, high-boiling solvents such as ethyl Carbitol acetate, butyl Carbitol acetate, and terpineol can be used.
P-side electrode 37 of the embodiment and p-side electrode 37 of the reference example are formed using the above-described low-temperature curing conductive paste. As the conductive powder, conductive paste containing silver powder is used. It should be noted, however, that the conductive paste used to form p-side electrode 37 of the embodiment contains a larger amount of solvent and has a lower viscosity than the conductive paste used to form p-side electrode 37 of the reference example. Specifically, 10 ml of solvent is added to 3 kg of conductive paste to reduce the viscosity by 10 pa•s.
The conductive paste prepared as described above is applied by printing using a screen plate to form first electrodes 2 as p-side electrode 37. The width (width with respect to the y direction illustrated in
As described above, a standard deviation σ is found for each of 28 measurement samples, and the respective standard deviations σ of the measurement samples are illustrated in FIG. 5. The horizontal axis represents N-th measurement sample, and the vertical axis represents the standard deviation σ of the measurement sample. The minimum value of the standard deviations σ is 2.9 μm, and the maximum value thereof is 5.8 μm. Moreover, the average of the standard deviations σ of the heights of uneveness on the surface of p-side electrode 37 of this embodiment is 4.2 μm. It should be noted that the average is the arithmetic mean value. The number of samples for calculating the average of standard deviations σ is preferably 20 or more.
For p-side electrode 37 of the reference example, as described above, the standard deviation σ of the heights of uneveness on the surface of the electrode is also found.
The electrical resistance values of p-side electrode 37 of the embodiment and p-side electrode 37 of the reference example are measured to show equivalent values. In the case where p-side electrode 37 of the embodiment is formed, the amount of silver powder in conductive paste can be reduced by 8.0 percent by mass compared to the case where p-side electrode of the reference example is formed. Accordingly, the invention can reduce the loss of conductive paste during the formation of electrodes.
The surface of n-side electrode 34 provided on the light-receiving surface side has a structure similar to that of uneveness shown in the reference example. Specifically, the average of standard deviations of uneveness on the surface of p-side electrode 37 is smaller than the average of standard deviations of uneveness on the surface of n-side electrode 34. From the viewpoint of the electrical resistance value of a finger electrode with respect to the amount of conductive paste used, the average of standard deviations of uneveness on the surface of n-side electrode 34 is also preferably small as in p-side electrode 37. However, if uneveness on the surface of n-side electrode 34 are made large, incident light scatters and reflects, and can be made to re-enter the surface of solar cell 1 to increase power generation. From such a viewpoint, the average of standard deviations uneveness on the surface of p-side electrode 37 is preferably smaller than the average of standard deviations of uneveness on the surface of n-side electrode 34.
It should be noted that though a pn junction is formed on the back surface side in the solar cell of the embodiment, a pn junction may be formed on the light-receiving surface side. In that case, an n-side electrode provided on the back surface side is formed such that the average of standard deviations of the heights of uneveness on the surface thereof is 5.0 μm or less.
In electrodes of a solar cell that are formed of conductive paste, it is desired that the loss of conductive paste during the formation of the electrodes can be reduced without increasing the resistance values of the electrodes. The embodiments explained above provide a solar cell in which the loss of conductive paste during the formation of electrodes can be reduced.
The invention includes other embodiments in addition to the above-described embodiments without departing from the spirit of the invention. The embodiments are to be considered in all respects as illustrative, and not restrictive. The scope of the invention is indicated by the appended claims rather than by the foregoing description. Hence, all configurations including the meaning and range within equivalent arrangements of the claims are intended to be embraced in the invention.
Number | Date | Country | Kind |
---|---|---|---|
2013-117845 | Jun 2013 | JP | national |
This application is a continuation application of International Application No. PCT/JP2014/063972, filed on May 27, 2014, entitled “SOLAR CELL”, which claims priority based on the Article 8 of Patent Cooperation Treaty from prior Japanese Patent Applications No. 2013-117845, filed on Jun. 4, 2013, the entire contents of which are incorporated herein by reference.
Number | Name | Date | Kind |
---|---|---|---|
6091019 | Sakata et al. | Jul 2000 | A |
20050109388 | Murakami | May 2005 | A1 |
20050150543 | Nakashima | Jul 2005 | A1 |
20090250106 | Hayashi | Oct 2009 | A1 |
20120145237 | Tanaka | Jun 2012 | A1 |
Number | Date | Country |
---|---|---|
H11-103084 | Apr 1999 | JP |
2007-224191 | Sep 2007 | JP |
2009-021330 | Jan 2009 | JP |
2011-061109 | Mar 2011 | JP |
2013076861 | May 2013 | WO |
Entry |
---|
JP2007224191 (English translation). |
Number | Date | Country | |
---|---|---|---|
20160071985 A1 | Mar 2016 | US |
Number | Date | Country | |
---|---|---|---|
Parent | PCT/JP2014/063972 | May 2014 | US |
Child | 14940266 | US |