Patent Application
20090274901
This application claims priority to European Patent Application No. 08 103 794.7, filed Apr. 30, 2008, incorporated herein by reference.
The present invention relates to a sheet of vitreous material bearing a multilayer solar control lamination and also a multiple glazing unit incorporating at least one such sheet of vitreous material bearing a solar control lamination.
The solar control lamination structures, also called sunshield laminations, concerned in the present invention comprise at least one infrared reflective functional layer such as a silver-based layer, which is joined to anti-reflective dielectric coatings that also serve as attachment and protection coatings for the functional layer. There can be one, two or even three functional layers, each separated by at least one dielectric coating and each functional layer being surrounded by dielectric coatings. These different layers are deposited, for example, by magnetic field-assisted low-pressure cathodic sputtering using a well known magnetron type device. However, the present invention is not restricted to this particular deposition process.
These solar control laminations are used in the production of solar protection, or sunshield, glazing units in order to reduce the risk of excessive overheating, for example, of an enclosed space having large glazed surfaces as a result of insolation, and thus to reduce the power to be expended for air-conditioning in summer.
In this case, the glazing must allow the least possible amount of total solar energy radiation to pass through, i.e. it must have a relatively low solar factor (SF or g). However, it is highly desirable that it guarantees a certain level of light transmission (LT) in order to provide a sufficient level of illumination inside the building. These somewhat conflicting requirements express the requirement to obtain a glazing unit with an elevated selectivity (S), defined by the ratio of light transmission to solar factor. These solar control laminations also have a low emissivity, which allows a reduction in the heat loss through high wavelength infrared radiation. Thus, they improve the thermal insulation of large glazed surfaces and reduce energy losses and heating costs in cold periods. The light transmission (LT) is the percentage of incident light flux, of illuminant D65, transmitted by the glazing. The solar factor (SF or g) is the percentage of incident energy radiation, which, on the one hand, is directly transmitted by the glazing and, on the other hand, is absorbed by this and then radiated in the opposite direction to the energy source in relation to the glazing.
These sunshield glazing units are generally assembled as double glazing units, in which the glass sheet bearing the lamination structure is joined to another glass sheet, with or without a coating, with the multilayer solar control lamination structure in contact with the inside space between the two glass sheets.
In some cases, it is often necessary to conduct a mechanical strengthening operation on the glazing such as a thermal toughening or tempering of the glass sheet or sheets in order to improve its resistance to mechanical stresses. It may also be expedient to provide the glass sheets with a more or less complex curvature for particular applications by means of a bending operation at elevated temperature. In the production and shaping processes of the glazing units there are some advantages in conducting these thermal treatments on the already coated substrate instead of coating a substrate that has already been treated. These operations are conducted at a relatively high temperature, i.e. a temperature at which the, for example, silver-based infrared reflecting layer tends to deteriorate and lose its optical properties and its properties with respect to infrared radiation. In the case where the coated glass sheet has to undergo a thermal treatment, therefore, quite specific precautions must be taken to form a lamination structure that is able to undergo a thermal toughening or bending treatment, often referred to below by the expression “toughenable”, without losing its optical and/or energy-related properties, for which it is formed.
It is also desirable that the glazing units meet certain aesthetic criteria in terms of light reflection (LR), i.e. the percentage of incident light flux—of illuminant D65—reflected by the glazing, and reflected and transmitted colour. Market demand is for a glazing with low light reflection. The combination of a high selectivity with a low light reflection sometimes results in the formation of purple tints in reflection, which have very little aesthetic appeal.
To reduce the amount of heat that penetrates into the area through the glazing, the invisible infrared heat radiation is prevented from passing through the glazing by reflecting it. This is the role of the functional layer or layers based on a material that reflects infrared radiation. This is an essential element in a solar control lamination. However, a significant portion of the heat radiation is also transmitted by visible radiation. To reduce the transmission of this portion of the heat radiation and go beyond eliminating the supply of energy by infrared radiation, it is necessary to reduce the level of light transmission.
Patent Application FR 2 751 666 A1 proposes the insertion of a stainless steel oxide absorbent layer into the lamination to reduce the level of total energy transmission through the glazing. This solution provides a glazing that has good sunshield qualities in association with an aesthetically appealing tint. However, the absorption level provided by the stainless steel oxide is relatively low, particularly when the lamination has to undergo a toughening and/or bending thermal treatment of the glass substrate.
Patent application WO 02/48065 A1 proposes to insert an absorbent layer of TiN into the lamination. One of the problems with this solution is that the TiN absorbent layer oxidises in certain conditions, in particular during thermal treatment, to form TiO2, which is transparent, thus losing part of its reason for being in the lamination. Moreover, the level of oxidation of the absorbent layer will depend on the thermal treatment conditions, which means that it will be difficult to determine the properties of the lamination after toughening.
Patent application WO 2005/012200 A1 proposes to insert an absorbent metal such as titanium into the lamination, e.g. under the silver. This results in a high-performance glazing with a low solar factor. However, once again, titanium oxidises during a high-temperature thermal treatment and loses its absorbent properties, and therefore it is difficult to easily obtain a glazing with a low solar factor on this basis when the lamination must undergo a toughening and/or bending thermal treatment.
The invention relates to a sheet of vitreous material bearing a multilayer solar control lamination comprising at least one functional layer based on a material that reflects infrared radiation surrounded by dielectric coatings, characterised in that the lamination comprises at least one absorbent layer with a thickness of at least 4 nm formed by at least one oxide or oxynitride of an alloy based on at least 20 atom % cobalt and/or copper.
The term “absorbent layer” is understood to mean a layer that absorbs a portion of the visible radiation and that comprises a material, which has a spectral absorption index k(λ) of at least 0.05 on average in the wavelength range of 380-750 nm, the average being calculated on the basis of a value every lo nm.
We have found that the use according to the invention of an absorbent layer of a sufficient thickness formed by at least one oxide of an alloy based on cobalt and/or copper allows glazing units with a solar control lamination having a very low solar factor, a low light reflection and an appealing reflected tint to be readily and easily formed, and that with a wise choice of alloy, the lamination retains its absorbent properties, even when subjected to a high-temperature thermal treatment such as toughening and/or bending.
When an absorbent material is introduced, the absorption is generally more intense over a part of the visible spectrum, which gives a specific colour to the lamination. The problem is to obtain an acceptable colour both in transmission and in reflection. We have found that, irrespective of whether the lamination must undergo a high-temperature thermal treatment or not, the invention allows laminations to be obtained that have an aesthetically appealing tint and comply with market demand.
This result is surprising, since copper oxide gives a brown tint that has little appeal and is not appreciated by the glazing market, and the fact that cobalt is ferromagnetic poses technical problems with respect to its deposition by reduced-pressure cathodic sputtering in a magnetron-type device.
The oxides or oxynitrides of these alloys of copper and/or cobalt in the absorbent layer are obtained by cathodic sputtering in an oxidising reactive atmosphere, possibly containing nitrogen, from a metal target made of the alloy in question. The oxides of these alloys can also be obtained by cathodic sputtering from ceramic targets of the oxides of these alloys. The use of oxide ceramic targets in particular facilitates the formation of a lamination with optical properties that are not spoiled by the high-temperature thermal treatment, so that a toughened coated glazing can be set side by side on the facade of a building with a non-toughened coated glazing, in which the coating lamination has the same structure, without there being any significant visual difference for an informed observer.
It is preferred that when the multilayer solar protection lamination is deposited onto an ordinary clear soda-lime float glass sheet 6 mm thick, the solar factor SF of the coated sheet is less than 45% and the light transmission LT is less than 70%. It is thus possible to obtain an effective solar shield.
The ferromagnetic state of pure cobalt makes it very difficult to use in a magnetron device. However, it has been found that its alloy with another metal allows this problem to be resolved much more easily. Different cobalt-based alloys with a non-ferromagnetic metal can be used, e.g. an alloy with about 33 atom % of Ti and about 66 atom % of Co to form Co2TiOx from a metal cathode of the alloy sputtered in an oxidising atmosphere. It is also possible to use a ceramic target of the mixed oxide of the alloy sputtered in a neutral or lightly oxidising atmosphere or an atmosphere containing a little nitrogen. According to the invention, oxide of an alloy is also understood to mean that the oxide can be a mixed oxide formed by co-sputtering from two ceramic targets respectively formed from oxides of the components of the alloy, e.g. oxides of Co and Ti.
Cobalt and/or copper alloy is understood to mean a material that contains one or more elements other than cobalt or copper, but wherein the cobalt or copper is present at a level of at least 20 atom %. The cobalt or copper is preferably present in the material in a higher proportion or in an equal proportion to another element.
The alloy preferably contains at least 40 atom %, advantageously at least 50 atom %, of cobalt or copper.
The absorbent layer is preferably formed by at least one oxide or oxynitride of the following alloys: cobalt-tin, cobalt-titanium, copper-aluminium, cobalt-chromium, copper-zinc, copper-tin, copper-cobalt, copper-titanium or cobalt-copper or mixtures thereof. It has been found that these alloys gave the best results both with respect to absorption stability and as regards the tint presented by the lamination. It is understood that the absorbent layer can be formed not only by cathodic sputtering of a metal target of one of these alloys in an oxidising atmosphere, but also from a ceramic target formed from mixed oxides of the components of the alloy or by co-sputtering separate targets of oxides of the components of the alloy in a neutral or slightly oxidised atmosphere or in the presence of a little nitrogen.
According to a first embodiment of the invention, the absorbent layer is preferably based on one or more of the following oxides: CuAlOx, CuZnOx, CoSnOx, CoTiOx, CuTiOx or CuSnOx. It has been found that these oxides retain a high degree of absorption after thermal treatment of the lamination that contains them without any adverse effect on the “haze” value of the lamination, thus providing a particularly effective solar control lamination. The “haze” value is defined as being the ratio of the diffuse light transmission to the total light transmission multiplied by 100 to obtain a percentage. This value is measured according to ASTM standard D1003. Moreover, these oxides provide a grey, bluish grey, tint essentially in reflection on the vitreous material side that gives an aesthetically pleasing and acceptable visual appearance to the solar control lamination that meets the requirement of the market. Of these oxides, CuAlOx and CuZnOx are especially advantageous, since the sputtering target of metal alloy for their production in an oxidising reactive atmosphere in a magnetron is easy to obtain and can be readily used for large-scale commercial series production. The oxide CuAlOx is particularly advantageous, since in particular it allows thermally treated glazing units that have a high absorption level and an aesthetically pleasing tint without haze to be easily obtained.
Of the oxides cited above, it has been found that oxides CuAlOx, CoSnOx, CoTiOx or CuSnOx are also suitable for solar control laminations that do not have to undergo high-temperature thermal treatment. Without thermal treatment, they provide a high absorption level that allows an effective solar control lamination to be obtained and they provide the lamination with an aesthetically pleasing visual appearance. Once again, CuAlOx is of particular interest in this case because it is easy to obtain a suitable target for large-scale commercial production.
According to a second embodiment of the invention, the absorbent layer is preferably based on one or more of the following oxides: CoCuOx, CoCrOx or CoCrTiOx. It has been found that these oxides were extremely advantageous with respect to absorption and the visual appearance of the laminations containing them when these have not to undergo high-temperature thermal treatment.
Preferably, according to one embodiment or the other of the invention, the absorbent layer has a thickness of at least 10 nm, advantageously in the range between 10 and 80 nm. This thickness range is sufficient to form an effective absorbent layer that nevertheless retains sufficient natural light to illuminate the interior of the building.
The functional layer can contain silver, copper, gold, palladium or aluminium, or a mixture or alloy thereof.
The functional layer is preferably silver-based. This is a particularly effective noble metal for reflecting infrared radiation. It is easily used in a magnetron device and its cost price is not prohibitive, particularly considering its efficacy. The silver can be doped with palladium or copper, for example, to a rate of 1 to 10%, for example, or a silver alloy can be used.
In some configurations, the lamination comprises at least two silver-based functional layers, and three silver-based layers, for example. By suitably adjusting the interference play of the dielectric layers, it is thus possible to achieve a high level of reflection of infrared radiation while retaining a relatively high light transmission.
The invention is most particularly suitable for laminations that must undergo a toughening and/or bending type of high-temperature thermal treatment. It has been found that some oxides or oxynitrides of cobalt and/or copper alloy provide a high level of absorption and surprisingly retain this high level of absorption after the high-temperature thermal treatment, and that, moreover, it provides the lamination with an appealing tint in reflection and transmission that complies with market demand. This is particularly the case with oxides of copper-aluminium, copper-zinc, copper-tin, cobalt-tin and cobalt-titanium alloys or mixtures thereof.
However, these oxides obviously also provide a high level of absorption in the lamination before thermal treatment. Since some of these oxides provide the lamination with an advantageous tint, it has been found that the invention is also highly suitable for non-toughenable laminations. In this case, it would be preferred to use oxides of copper-aluminium, copper-tin, copper-cobalt, cobalt-titanium, cobalt-copper, cobalt-tin and cobalt-chromium alloy or mixtures thereof, and in particular the oxynitride of cobalt-chromium-titanium alloy.
Transparent dielectric coatings are well known in the field of layers deposited by cathodic sputtering. There are numerous suitable materials and it is not expedient to list them here. In general, these are metal oxides, oxynitrides or nitrides. Of those most commonly used, SiO2, TiO2, SnO2, ZnO, ZnAlOx, Si3N4, AlN, Al2O3, ZrO2, Nb2O5, TiZrYOx, TiNbOx and Bi2O3 can be mentioned by way of example. With respect to the outer coating, SnO2 is a dielectric material that is particularly well suited when the lamination does not have to undergo high-temperature thermal treatment.
At least one of the dielectric coatings preferably comprises at least one zinc-tin mixed oxide-based layer containing at least 20% tin. This oxide is highly suitable as dielectric coating to protect the absorbent layer, in particular in the case of thermal treatment of the lamination.
The lower dielectric coating arranged between the sheet of vitreous material and the functional layer preferably comprises at least one zinc-tin mixed oxide containing at least 20% tin, and the outer dielectric coating also comprises at least one zinc-tin mixed oxide containing at least 20% tin. This arrangement is very advantageous for protecting the absorbent layer both with respect to oxidation from the outside and from oxygen coming from the vitreous material.
The dielectric coating arranged below the or each functional layer preferably comprises a zinc oxide-based layer, possibly doped with aluminium, in direct contact with the functional layer or layers. Zinc oxide has a particularly favourable effect on the stability and corrosion resistance of the functional layer, in particular when silver is concerned. Zinc oxide is also advantageous with respect to the decomposition resistance of the functional layer, particularly when it is silver based, during high-temperature thermal treatment of the lamination. In the event of a thermal treatment, it is also advantageous for improving the electrical conductivity of a silver-based layer, and therefore for achieving a low emissivity.
Advantageously, the dielectric coating arranged below the or each functional layer comprises a zinc-tin mixed oxide-based layer that does not contain more than about 20% tin and at least about 80% zinc, preferably not more than about 10% tin and at least about 90% zinc, in direct contact with the functional layer or layers. This mixed oxide with a high zinc oxide content below and in direct contact with the functional layer, particularly when it is silver-based, is particularly advantageous for the resistance of the functional layer to the toughening and/or bending type high-temperature thermal treatment. The combination of this mixed oxide with a high zinc content below the functional layer with a zinc-tin mixed oxide containing at least 20% tin in the lower and outer dielectric layers represents the most advantageous structure for favourable resistance of the lamination during a high-temperature thermal treatment.
The solar control lamination preferably has a neutral tint when examined in reflection on the vitreous material side, i.e. when values for a* and b* (CIELAB 1976 L*a*b* values) are such that −8<a*<2 and −18<b*<0, preferably −5<a*<0 and −15<b*<0, and advantageously −3<a*<0 and −12<b*<−2. This neutral tint is advantageously slightly bluish. The lamination is thus highly appealing aesthetically and complies with market demand.
The invention extends to a multiple glazing unit comprising at least one sheet of vitreous material, on which is formed a lamination such as defined above. The invention provides a very useful sunshield multiple glazing.
The multiple glazing according to the invention preferably has a solar factor equal to or less than 35%, equal to or less than 28% and advantageously equal to or less than 22%, and a light reflection less than 18%. As a result, a particularly effective sunshield multiple glazing is obtained that does not generate glare when observed from outside the building where it is installed.
The multiple glazing according to the invention preferably has a light transmission less than 55% and preferably less than 42%. This allows the total energy transmission through the glazing to be greatly reduced.
The invention shall now be described in more detail in a non-restrictive manner on the basis of the following preferred exemplary embodiments.
A 2 m by 1 m, 6 mm thick sheet of ordinary clear soda-lime float glass is placed in a magnetron-type magnetic field-assisted cathodic sputtering device at reduced pressure (about 0.3 Pa). A multilayer solar control lamination is deposited on this glass sheet comprising, in sequence:
a) a lower dielectric coating formed from two oxide layers deposited in a reactive atmosphere formed from a mixture of argon and oxygen from zinc-tin alloy cathodes of different compositions. The first zinc-tin mixed oxide with a thickness of about 30 nm is formed from cathodes of a zinc-tin alloy with 52% by weight of zinc and 48% by weight of tin to form the spinel structure of zinc stannate Zn2SnO4. The second zinc-tin mixed oxide ZnSnOx with a thickness of about 7 nm is deposited from targets of a zinc-tin alloy with 90% by weight of zinc and 10% by weight of tin.
b) An infrared reflecting functional layer formed from about 20 nm of silver from a target of practically pure silver in a neutral atmosphere of argon.
c) A double sacrificial metal layer formed from a first layer of NiCr with a thickness of 1 nm deposited from a target of an alloy with 80% Ni and 20% Cr, and a second layer of Ti with a thickness of 2.5 nm deposited from a titanium target. These layers are both deposited in a flux of argon lightly contaminated with oxygen from adjacent chambers. It should be noted that the oxidising atmosphere of the plasma during deposition of the following layer, described below, completely oxidises the layer of titanium so that at the end of the deposition process of the second dielectric the titanium is oxidised to form a compact layer of TiO2. As a variant, it is also possible to deposit the layer in the form of partially oxidised TiOx. This layer can also be deposited, for example, from a TiOx ceramic target and oxidised by the plasma used for deposition of the following layer.
d) An absorbent layer comprising 15 nm of CoTiOx formed from a metal target of an alloy of 66 atom % of Co, the rest being Ti. As a variant, this absorbent layer can be deposited from a ceramic target formed from mixed oxide in the same relative proportions of the metals Ti and Co.
e) An outer dielectric coating formed from two layers of zinc-tin mixed oxides deposited in a reactive atmosphere formed by a mixture of oxygen and argon from cathodes of zinc-tin alloys of different compositions. The first zinc-tin mixed oxide with a thickness of about 15 nm is deposited from a metal target of an alloy of ZnSn with 90% Zn and 10% Sn (by weight). The second zinc-tin mixed oxide with a thickness of about 25 nm is deposited from a target of an alloy of ZnSn with 52% Zn and 48% Sn (by weight) to form the spinel structure of zinc stannate Zn2SnO4.
f) Then, a 4 nm final protective layer of TiN deposited from a metal target of Ti in a nitrogen atmosphere. As a variant, a 4 nm layer of TiZrOx can be deposited from a ceramic target as protective layer.
It should be noted that all the layers of ZnSnOx are sufficiently oxidised to be as transparent as possible. It should also be noted that the thicknesses of Ti, TiOx and TiN are given as equivalent thickness of TiO2 (i.e. as a result of the oxidation of Ti, TiOx or TiN), which is their state in the finished product after thermal treatment, and is already the state even in the intermediate glazing that is suitable to undergo a thermal treatment with respect to Ti.
The coated glazing with the multilayer solar control lamination formed on the glass sheet then undergoes a thermal toughening operation, during which it is subjected to a temperature of 670° C. for 8 minutes and 30 seconds, then cooled abruptly by jets of cold air. During this thermal treatment, thin films of NiCr of the barrier layers oxidise sufficiently to be transparent, while forming an effective and stable shield to protect the silver layers. The upper protective layer of TiN itself oxidises to form TiO2.
After this treatment, the coated and toughened glazing has the following properties:
This coated glazing is then assembled as double glazing with another 4 mm thick clear glass sheet, wherein the coating is arranged on the side of the internal space of the double glazing. The space between the two sheets is 15 mm and the air therein is replaced by 90% argon. When looking at the double glazing on the glass side of the coated glazing with lamination structure placed in position 2, i.e. when the glazing provided with the lamination is firstly viewed from the glass side, and then the clear glass sheet without a layer is viewed, the following properties are noted:
In the present invention, the following collective terms are used for the measured or calculated values. Light transmission (LT), light reflection (LR), light absorption (LA) (percentage of light flux—of illuminant D65—absorbed by the glazing) and tint in transmission (1976 CIELAB L*a*b* values) are measured with illuminant D65/2°. With respect to the tint in reflection, the 1976 CIELAB values (L*a*b*) are measured with illuminant D65/10°. The solar factor (SF or g) is calculated in accordance with standard EN410. The value U (coefficient k) and emissivity (ε) are calculated in accordance with standards EN673 and ISO 10292.
Visual examination in reflection of the double glazing shows a uniform tint and appearance over the entire surface. The invention allows the formation of a double glazing with a low solar factor, which retains an adequate light transmission and has a very high aesthetic appeal.
Unless otherwise indicated, the following Examples 2 to 11 are conducted in a similar manner to Example 1 above, but with different structures. Example ii has a structure with three Ag layers. Example C is a comparative example that is not in accordance with the invention. The corresponding structures of the laminations are given in Table 1 below with the following explanation of the abbreviations used:
15
Co
28
Cu
72
O
20
Co
50
Zn
50
O
TZO
27
AZO
Co
80
Cr
20
O
AZO
TNO
18
15
Co
74
Cr
18
Ti
8
ON
TXO
TXO
Co
67
Sn
33
O
TZO
29
TXO
Cu
52
Al
48
O
TXO
30
TZO
Cu
63
Zn
37
O
TNO
21
TNO
AZO
TXO
AZO
Ti
50
Co
50
O
x
TZO
15
TXO
TXO
Cu
50
Al
50
O
TZO
26
AZO
TZO
Cu
50
Sn
50
O
TXO
TiN
70
8
TXO
Cu
50
Al
50
O
TXO
TXO
TZO
The coated glazing units of the laminations according to Examples 2 to 11 and C are then subjected to a thermal toughening, during which they were subjected to a temperature of 690° C. for 6 minutes, then abruptly cooled by jets of cold air. The optical and energy-related properties of the coated glazing units assembled as double glazing in the same manner as in Example 1 with a 4 mm clear glass sheet and a 15 mm space filled to 90% with argon, are given in Table 2. The glazing is observed with the lamination placed in position 2 on the outer sheet inside the double glazing, i.e. the glass bearing the coating is firstly viewed from the glass side and then the glass sheet without a layer is viewed. The number of the example followed by “nt” indicates that the given values relate to the non-toughened glazing or the glazing before toughening and “at” indicates after toughening.
The optical properties of Examples 5 to 11 vary very little following high-temperature thermal treatment. A toughened glazing according to these examples can therefore be placed side by side with a non-toughened glazing bearing the same lamination without an observer being able to perceive a difference in optical appearance. In fact, it can be seen in Table 2 that the variation in tint ΔE* between the values obtained for non-toughened glazing units (“nt”) and the values obtained for toughened glazing units (“at”) is very slight and less than 2. The variation in tint during the thermal treatment is calculated on the basis of the formula ΔE*=√{square root over ((ΔL*)2+(Δa*)2+(Δb *)2)}{square root over ((ΔL*)2+(Δa*)2+(Δb *)2)}{square root over ((ΔL*)2+(Δa*)2+(Δb *)2)}, in which ΔL*, Δa* and Δb* are the differences in values L*, a*, b* between the toughened and non-toughened versions of the same structures. The value ΔE* is preferably less than 3, advantageously less than 2, so that an observer does not perceive a difference in optical appearance. For Examples 5 to 11 of Table 2, the value of ΔE* does not reach 2 (square root of 3 for Examples 5 and 7). This can be compared to the value ΔE* of 4 for the comparative example C.
The aesthetic appearance of all these examples is excellent and uniform over the entire surface. It is seen that as a result of the invention a relatively low solar factor can be easily obtained, while retaining a high selectivity and an appealing aesthetic appearance that meets market demand. The selectivity of the examples is higher than 1.1 and even higher than 1.5 for the majority of examples. It is higher than 1.7 for many of them and even higher than 1.8 for some. The tint in reflection on the glass side is neutral to bluish, while avoiding red or purple tints that are of little appeal. It is also noted that the level of total energy absorption, partly due to the composition of the cobalt- and/or copper-based alloy according to the invention, is largely retained after thermal treatment.
In Example 7 the Ag—Pd alloy of the second functional layer (IR2) reinforces the effect of the absorbent layer by slightly increasing the absorption of the lamination.
The characteristics of the comparative example show that the TiN absorbent layer has oxidised to TiO2 during the thermal treatment and has therefore lost its absorption characteristics. In contrast, CuAlO, for example, is practically insensitive to oxidation during the thermal treatment and therefore retains its absorbent properties. On the other hand, TiN sandwiched between 2 oxides requires a change in the deposition atmosphere, which is not the case with CuAlO, for example.
The above written description of the invention provides a manner and process of making and using it such that any person skilled in this art is enabled to make and use the same, this enablement being provided in particular for the subject matter of the appended claims, which make up a part of the original description.
As used herein, the words “a” and “an” and the like carry the meaning of “one or more.”
The phrases “selected from the group consisting of,” “chosen from,” and the like include mixtures of the specified materials. Terms such as “contain(s)” and the like are open terms meaning ‘including at least’ unless otherwise specifically noted.
All references, patents, applications, tests, standards, documents, publications, brochures, texts, articles, etc. mentioned herein are incorporated herein by reference. Where a numerical limit or range is stated, the endpoints are included. Also, all values and subranges within a numerical limit or range are specifically included as if explicitly written out.
The above description is presented to enable a person skilled in the art to make and use the invention, and is provided in the context of a particular application and its requirements. Various modifications to the preferred embodiments will be readily apparent to those skilled in the art, and the generic principles defined herein may be applied to other embodiments and applications without departing from the spirit and scope of the invention. Thus, this invention is not intended to be limited to the embodiments shown, but is to be accorded the widest scope consistent with the principles and features disclosed herein. In this regard, certain embodiments within the invention may not show every benefit of the invention, considered broadly.