20140134504
1. Field
The present disclosure relates generally to electrolytes, and more specifically to solid ceramic electrolytes that may be used in electrochemical devices.
2. Technical Background
Solid electrolytes, also known as fast ion conductors, are materials that can function as solid state ion conductors and can be used in electrochemical devices such as, for example, solid oxide fuel cells and lithium-air batteries. In a lithium-air battery, for instance, lithium ions move from a negative electrode (anode) to a positive electrode (cathode) during discharge (and back when charging) via the solid electrolyte. In some solid electrolytes, such as lithium metal phosphates, lithium ions can be conducted through vacancies in the electrolyte crystal lattice. Additionally, the solid electrolyte can provide a hermetic barrier between the anode and the cathode in order to prevent the anode and cathode from sharing a common electrolyte solution.
Important to the development of various electrochemical devices is the availability of solid, conductive electrolyte materials. A major challenge for such electrolyte materials is the ability to sinter suitable materials to sufficient density such that the electrolyte is hermetic while providing sufficient conductivity and economy, as well as acceptable physical stability. Conventional hermetic electrolytes, which are commonly made using a glass-ceramic process, can be made dense and hermetic, but these attributes typically come at the expense of poor conductivity and high cost. A further challenge facing the conventional glass-ceramic process is the requirement that the desired composition form a stable glass.
In view of the foregoing, it would be desirable to develop an economical, ion-conductive, and mechanically-robust solid ceramic electrolyte for use in electrochemical devices.
The concepts of the present disclosure are generally applicable to solid ceramic electrolytes for use in electrochemical devices. In accordance with one embodiment, a solid ceramic electrolyte may comprise an ion-conducting ceramic and at least one grain growth inhibitor. The ion-conducting ceramic may comprise a lithium metal phosphate or a derivative thereof and the grain growth inhibitor may comprise magnesia or a precursor thereof, titania or a precursor thereof, or both. The solid ceramic electrolyte may have an average grain size of less than about 2 microns. The grain growth inhibitor may comprise between about 0.5 mol. % to about 10 mol. % of the solid ceramic electrolyte.
In accordance with another embodiment, a solid ceramic electrolyte may be formed by a method comprising combining an ion-conducting ceramic with at least one grain growth inhibitor to form a mixture, casting the mixture to form a body, and sintering the body to form the solid ceramic electrolyte.
An electrochemical device may comprise a negative electrode, a positive electrode, and an interposed electrolyte material. The electrolyte that is incorporated into such a device may comprise a solid ceramic electrolyte as disclosed herein.
Additional features and advantages of the subject matter of the present disclosure will be set forth in the detailed description which follows, and in part will be readily apparent to those skilled in the art from that description or recognized by practicing the subject matter of the present disclosure as described herein, including the detailed description which follows, the claims, as well as the appended drawings.
It is to be understood that both the foregoing general description and the following detailed description present embodiments of the subject matter of the present disclosure, and are intended to provide an overview or framework for understanding the nature and character of the subject matter of the present disclosure as it is claimed. The accompanying drawings are included to provide a further understanding of the subject matter of the present disclosure, and are incorporated into and constitute a part of this specification. The drawings illustrate various embodiments of the subject matter of the present disclosure and together with the description serve to explain the principles and operations of the subject matter of the present disclosure. Additionally, the drawings and descriptions are meant to be merely illustrative, and are not intended to limit the scope of the claims in any manner.
The following detailed description of specific embodiments of the present disclosure can be best understood when read in conjunction with the following drawings, where like structure is indicated with like reference numerals and in which:
Reference will now be made in greater detail to various embodiments of the present disclosure, some embodiments of which are illustrated in the accompanying drawings. Whenever possible, the same reference numerals will be used throughout the drawings to refer to the same or similar parts.
The solid ceramic electrolytes described herein may generally comprise an ion-conducting ceramic and at least one grain growth inhibitor. During sintering, the presence of the grain growth inhibitor may aid in producing a solid ceramic electrolyte with a fine-grain, granular structure. A fine-grain granular structure, such as a structure having grains that on average are less than about 2 microns, may have increased mechanical stability. The solid ceramic electrolytes described herein may be useful in electrochemical devices, and particularly useful in lithium-air batteries.
In various embodiments, a solid ceramic electrolyte may comprise an ion-conducting ceramic (e.g., lithium ion-conducting ceramic) such as a lithium metal phosphate or a derivative thereof An example lithium metal phosphate is lithium aluminum titanium phosphate (LATP). A composition of LATP, in some embodiments, may be represented by the chemical formula Li1+xAlxTi2-x(PO4)3, where x is between 0 and 0.6. One such composition is Li1.4Al0.4Ti1.6(PO4)3.
LATP may be produced in a solid state process. For example, ammonium phosphate, aluminum oxide, titanium oxide, and lithium carbonate powders may be combined in a stoichiometric ratio to produce LATP. The foregoing precursor materials may be combined with a suitable grain growth inhibitor to form a mixture that can be tape cast and sintered to form a dense membrane.
The grain growth inhibitor may be a refractory material, meaning that the grain growth inhibitor is resistant to a heat treatment. In embodiments, the grain growth inhibitor is not liberated from the solid ceramic electrolyte during sintering. Rather, the grain growth inhibitor, as referred to herein, remains in the solid ceramic electrolyte following sintering. In related embodiments, however, precursors of a grain growth inhibitor may be used which through sintering are converted into the grain growth inhibitor that remains in the post-sintered solid ceramic electrolyte.
In one embodiment, the grain growth inhibitor may comprise magnesia, titania, or both. For example, the grain growth inhibitor may comprise magnesia and titania. In another embodiment, the grain growth inhibitor comprises magnesia, but is substantially free of titania. In another embodiment, the grain growth inhibitor comprises titania, but is substantially free of magnesia. Precursors of magnesia and titania may be converted into magnesia and titania, respectively. Without limitation, suitable precursors of magnesia, for example, include magnesium nitrate and magnesium acetate.
If the grain growth inhibitor comprises both titania and magnesia, the molar ratio of titania to magnesia (titania:magnesia) may be between about 2:1 to about 8:1 (i.e., the ratio of titania to magnesia may be about 2:1, 3:1, 4:1, 5:1, 6:1, 7:1 or 8:1, or may be a range between any of the titania to magnesia ratios disclosed).
A method of forming the solid ceramic electrolyte generally may comprise combining the ion-conducting ceramic with the grain growth inhibitor to form a mixture, casting the mixture to form a body, and sintering the body to form the solid ceramic electrolyte. To form the mixture comprising the ion-conducting ceramic and the grain growth inhibitor, prior to mixing the ion-conducting ceramic with the grain growth inhibitor, the ion-conducting ceramic may be milled to an average particle size of less than about 1 micron (e.g., less than 1, 0.5, 0.2, 0.1 or 0.05 microns). As used herein, a “particle size” or “grain size” refers to the maximum length of the particle or grain in its longest dimension.
The milled ion-conducting ceramic may be combined with the grain growth inhibitor to form the mixture comprising the ion-conducting ceramic and the grain growth inhibitor. The grain growth inhibitor may be in a powder form, and in some embodiments may have a similar average particle size as the milled ion-conducting ceramic. In other embodiments, the average particle size of the grain growth inhibitor may be in the range of between about 50 nm and about 300 nm, such as 50 nm, 100 nm, 150 nm, 200 nm, 250 nm, or 300, nm, or in a range between any disclosed particle sizes.
The grain growth inhibitor may be present in an amount sufficient to enable formation of the fine-grain granular structure at sintering temperatures. In one embodiment, the grain growth inhibitor may comprise between about 0.5 mol. % to about 10 mol. % of the solid ceramic electrolyte. In other embodiments, the grain growth inhibitor may comprise about 0.5, 0.6, 1, 2, 3, 4, 5, 6, 7, 8, 9 or 10 mol. % of the solid ceramic electrolyte (or a range between any two of the mol. % disclosed herein). In one exemplary embodiment, grain growth inhibitor may comprise between about 3 mol. % and 6 mol. % of the solid ceramic electrolyte.
Following the formation of the ion-conducting ceramic/grain growth inhibitor mixture, the mixture may be cast to form a body that may be sintered. In one embodiment, the casting comprises tape casting. In a tape casting process, the ion-conducting ceramic/grain growth inhibitor mixture (optionally comprising milled powders) may be incorporated into a tape casting slip with suitable binders, plasticizers, or both, cast to a tape, dried, cut, and released prior to sintering. One or more binders and/or plasticizers may be dissolved into the ion-conducting ceramic/grain growth inhibitor mixture to make a tape casting slip. In various embodiments, a tape casting slip may optionally include one or both of a binder and a plasticizer, such as various polymers.
Following the formation of the cast body, the cast body may be sintered to form the solid ceramic electrolyte. As used herein, “sintering” refers to any process wherein a material is coalesced into a solid or porous mass by heating it and/or compressing it. A sintering process generally does not involve the liquefaction of the material being sintered. In one embodiment, the sintering may be performed at a temperature of equal to or less than about 950° C. (e.g., less than about 950° C., 925, 900, 875 or 850° C., or in a range between any two maximum sintering temperatures disclosed). It may be desirable to sinter at lower temperatures, because sintering at temperatures above about 950° C. may be more difficult to control in an industrial process and/or may require special equipment that may be more expensive than conventional furnaces or kilns. During the sintering, the binders, plasticizers, or both, may be liberated from the solid ceramic electrolyte due to the temperatures of the sintering process. However, at least a portion or substantially all of the grain growth inhibitor may remain in the solid ceramic electrolyte.
In some embodiments, the sintering may result in a solid ceramic electrolyte membrane having a thickness of less than 200 microns (e.g., less than 200, 150, 100 or 50 microns, or in a range between any two maximum thicknesses disclosed). In combination with any of the disclosed thicknesses, the solid ceramic electrolyte may have a maximum lateral dimension of between about 0.5 cm about 1 meter, such as any size suitable for use in an electrochemical device, such as a device arranged in a stacked configuration.
The resulting material, following sintering, may be a solid ceramic electrolyte which has fine-grain granular structure, is hermetic, is physically stable when in contact with an aqueous solution, and is conductive to ions (e.g., lithium ions). As used herein, a hermetic material is substantially impervious to the diffusion of liquids or gasses. The solid ceramic electrolyte may be fully dense or have a density that is at least 95% (e.g., at least 95, 96, 97, 98, 99, 99.9 or 99.99%) of its maximum (e.g., theoretical) density. In some embodiments, the ion conductivity of the solid ceramic electrolyte is greater than 1.0×10−4 S/cm (e.g., greater than 1×10−4, 1.5×10−4, 2.0×10−4, 2.5×10−4, 3.0×10−4, 3.5×10−4, or 4.0×10−5 S/cm, or a range between any two of the minimum conductivities disclosed herein).
In some embodiments, the solid ceramic electrolyte may have a fine-grain granular structure, which may impart increased mechanical stability to the membrane. In various embodiments, the average grain size of the solid ceramic electrolyte may be less than 2 microns, e.g., less than 2, 1.8, 1.6, 1.4, 1.2, 1.0, 0.8 or 0.6 microns, or within a range between any two of the maximum average grain sizes disclosed herein.
In embodiments, the solid electrolyte materials disclosed herein do not contain glassy phases nor are they glass-ceramic materials that may develop a relatively large grain size during sintering. Additionally, the absence of glass or glass-ceramic materials in the solid ceramic electrolyte may increase conductivity, as glass and glass-ceramic materials generally do not have good conductivity and reduce the conductivity of a solid ceramic electrolyte.
It will be appreciated that LATP is subject to microcracking as a result of a large thermal expansion anisotropy. A critical grain size for microcracking is estimated to be about 2 μm.
The solid ceramic electrolytes described herein may be useful in electrochemical devices, and particularly useful in lithium-air batteries. Referring to
In one embodiment, the solid ceramic electrolyte is a membrane with a thickness of less than about 200 microns (e.g., less than 200, 150, 100 or 50 microns, or in a range between any two maximum thicknesses disclosed). The solid ceramic electrolytes described herein may be substantially free of an electrolytic solution. In one exemplary embodiment, the electrochemical device is a lithium air battery. The properties of the solid ceramic electrolyte described herein, particularly the properties of mechanical stability, hermeticity, physical stability when in contact with an aqueous solution, and conductivity, may be particularly desirable for the application of an electrolyte in a lithium-air battery.
In some embodiments, the solid ceramic electrolyte may be physically stable when in contact with an aqueous solution for at least about 48 hours. In other embodiments, the solid ceramic electrolyte may be physically stable when in contact with an aqueous solution for at least about 48 hours, about 100 hours, about 200 hours, about 500 hours, about 1000 hours, about 3000 hours, about 6000 hours, about 1 year, or about 2 years, or in a range between any two times disclosed. As described herein, a solid ceramic electrolyte is physically stable when in contact with an aqueous solution if it does not exhibit mechanical failure when contacted on one side of a 200 nm or less thick membrane with 1M ammonium chloride. A detailed description of the experimental setup for such a standard is included in the Examples Section of this disclosure.
Lithium aluminum titanium phosphate (LATP) solid ceramic electrolytes were prepared by solid state processes. Ammonium phosphate, aluminum oxide, titanium oxide and lithium carbonate powders were mixed in a stoichiometric ratio to produce Li1.4Al0.4Ti1.6(PO4)3. The powder batch was calcined for 2 hours at 700° C. The resulting material was milled to an average particle size of about 10 μm and then calcined again for 2 hours at 700° C. The resulting material was then milled to ˜0.3 μm average particle size in a solvent. Suitable solvents include ethanol, butanol and propylene glycol, which may be optionally combined with a dispersant such as Phospholan 236 (commercially available from AkzoNobel N.V. of Amsterdam, Netherlands).
Membrane samples were prepared using various additives, which may act as grain growth inhibitors in some samples. Samples were also prepared with no additives. In the case of an additive being used, 3-6 mol % of an additive was added to the LATP batch. A polymer such as polyvinyl butyral (PVB) was added to make a slip. The slip was tape cast with 14-18 mil blades. It was dried for 2-12 hours at room temperature and released from the carrier film. The resulting green body was then fired to density at various sintering temperatures with a 400° C. hold for 1 hour to burn out the green tape polymer binder. The fired membranes were 50-150 μm thick.
SEM images for the samples showed approximate density and grain size of the samples.
Samples were tested for their physically stability when in contact with an aqueous solution using two testing methods. In the first testing method, fired solid ceramic electrolyte samples were tested by submerging weighed pieces of the solid ceramic electrolyte in de-ionized water. The conductivity of the de-ionized water was measured daily and the data was normalized per mg of sample (μS/cm-mg). Higher conductivity corresponded to decreased stability in aqueous solutions, as solid ceramic electrolyte dissolved into the de-ionized water which increased conductivity.
The second testing method was a one-side aqueous solution stability test. LATP solid ceramic electrolytes with various additives were prepared as described herein. A piece of the each sample LATP solid ceramic electrolyte membrane was attached to the end of a glass tube with a water resistant epoxy. This allows only one side of the solid ceramic electrolyte to be exposed to the aqueous test solution. The tube was filled with the test solution and suspended over a catch cup. In this case, 1 M ammonium chloride test was used to fill the tube as the aqueous solution. The solid ceramic electrolyte membrane was monitored for leaks or mechanical failure hourly for about 8 hours. After the first 8 hours the membrane was checked daily for failure and observations are recorded in Table 1. The samples made without sintering aids were too porous for this test. The samples made with lithium nitrate or lithium borate were too fragile to mount for this test. Samples made with LATP and phosphoric acid failed in less than 24 hours exposure. Samples made with LATP and magnesia and titania survived over 6000 hours of one sided exposure.
As used herein, the singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to a “additive” includes examples having two or more such “additive” unless the context clearly indicates otherwise.
Ranges can be expressed herein as from “about” one particular value, and/or to “about” another particular value. When such a range is expressed, examples include from the one particular value and/or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent “about,” it will be understood that the particular value forms another aspect. It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint, and independently of the other endpoint.
Unless otherwise expressly stated, it is in no way intended that any method set forth herein be construed as requiring that its steps be performed in a specific order. Accordingly, where a method claim does not actually recite an order to be followed by its steps or it is not otherwise specifically stated in the claims or descriptions that the steps are to be limited to a specific order, it is no way intended that any particular order be inferred.
It is also noted that recitations herein refer to a component being “configured” or “adapted to” function in a particular way. In this respect, such a component is “configured” or “adapted to” embody a particular property, or function in a particular manner, where such recitations are structural recitations as opposed to recitations of intended use. More specifically, the references herein to the manner in which a component is “configured” or “adapted to” denotes an existing physical condition of the component and, as such, is to be taken as a definite recitation of the structural characteristics of the component.
It will be apparent to those skilled in the art that various modifications and variations can be made to the present invention without departing from the spirit and scope of the invention. Since modifications, combinations, sub-combinations and variations of the disclosed embodiments incorporating the spirit and substance of the invention may occur to persons skilled in the art, the invention should be construed to include everything within the scope of the appended claims and their equivalents.