Solid diamond field emitter

Information

  • Patent Grant
  • 6448700
  • Patent Number
    6,448,700
  • Date Filed
    Monday, October 25, 1999
    25 years ago
  • Date Issued
    Tuesday, September 10, 2002
    22 years ago
Abstract
The present invention provides a “solid” diamond, i.e. greater than 5μ thick, electron emitter that has been “machined” using non-contact techniques to a point having a radius of less than about 100μ, preferably below about 10μ and most preferably between about 3 angstroms and about 3μ. The solid diamond electron emitters of the present invention can perform, even at these small radii, as multi-point emitters depending upon the radius and roughness of the pointed tip and can be used in arrays to obtain relatively large area field emitters for applications where such larger field emissions are necessary. Production of the solid diamond emitters of the present invention is preferably accomplished using non-contact electron or ion beam machining techniques. Residual gas analyzers (RGA) and field emitter extractor gauge analyzers (FERGA) that use the solid diamond emitters are also described.
Description




FIELD OF THE INVENTION




The present invention relates to field emitter electron sources for use in ultra-high vacuum (UHV) and extremely high vacuum (XHV) instrumentation, and more particularly to diamond based such emitters.




BACKGROUND OF THE INVENTION




Present day Ultra High Vacuum and Extremely High Vacuum instrumentation is based primarily on thermoionic electron sources. These sources operate at very high temperatures and consequently, tend to desorb gases from the walls of the vacuum chamber and instrumentation thereby affecting the pressure one is trying to measure. Additionally, at the normal operating current of about 1 mA, they also affect the pressure measurement due to electron stimulated desorption of gases from the vacuum walls as well as the elements of the instruments.




Several attempts have been made to substitute field emitter array cold electron sources for the thermoionic electron sources. However, these field emitters have relatively large surface areas and create problems due to continuous outgassing.




Cold-cathode electron field emitters using diamonds have been suggested in the prior art because of the negative electron affinity of their surfaces, but these emitters are generally based on thin films of diamonds (less than about 5μ) or alternatively, thin layers of diamond particles embedded in a coating material. While these have often provided improved emitters, the density of their emission fields is often hard to control and not sufficient to provide optimum performance for vacuum instrumentation. Additionally, in the case of bonded diamond particles, the coating is a source of additional measurement interference.




SUMMARY OF THE INVENTION




According to the present invention there is provided a “solid” diamond i.e. greater than 5μ thick, electron emitter that has been “machined” using non-contact techniques to a point having a radius of less than about 100μ, preferably below about 10μ, and most preferably between about 3 tenths of an angstrom and about 3μ. The solid diamond electron emitters of the present invention can perform, even at these small radii, as multi-point emitters depending upon the radius and roughness of the pointed tip. The emitters of the present invention can be used in arrays of individual emitters to obtain relatively large area emitter fields for applications where such fields are necessary. Production of the solid diamond emitters of the present invention is preferably accomplished using non-contact electron or ion beam or laser machining techniques.




Residual gas analyzers (RGA), field emitter extractor gauge analyzers (FERGA), Faraday cup detectors and other high and ultra high vacuum devices utilizing the solid diamond emitters of the present invention as well as free electron lasers and Linacs that use the technology described herein are also possible.











DESCRIPTION OF THE DRAWINGS





FIGS. 1-3

depict individual steps in the solid diamond fabrication process described herein.





FIG. 4

is a schematic diagram of the final or finishing step of the manufacturing process used to fabricate the solid diamond electron emitters of the present invention.





FIG. 5

is a schematic diagram of a field emitter extractor gauge (FEG) capable of utilizing an array of the solid diamond emitters of the present invention.





FIG. 6

is a schematic diagram of a field emitter residual gas analyzer (FERGA) capable of utilizing an array of the solid diamond emitters of the present invention.











DETAILED DESCRIPTION




The development of instrumentation useful in extremely high vacuum environments that do not cause measurement disruptive releases of adsorbed gases has been a perplexing problem. Since most such prior art devices rely of thermoionic electron emitters the release of the interfering gases is an inherent property of the emission process. As described above, attempts to solve the problem using cold field emitters have proven largely similarly ineffective due to the relatively large surface areas of such emitters that also desorb gases. The use of thin films of diamonds (<5μ) or diamond chips embedded in a suitable matrix has also proven of limited effectiveness.




It has now been discovered that the use of single or arrays of “solid” diamond emitters obviate the interference/disturbance problems indicated with prior art systems. According to the present invention there is provided a “solid” diamond i.e. greater than 5μ thick—(T in FIG.


2


)—, emitter that has been “machined” using non-contact techniques to a point having a radius of less than about 10μ and preferably between about 5 and about 10 angstroms.




As shown in

FIGS. 1-3

, preparation of the solid diamond field emitters of the present invention first involves (

FIG. 1

) selection of a raw diamond


10


having octahedrons at a level of between about 700-900 per carat or between about 0.5 and 0.6 mm in size. The raw diamond should be free of flaws, inclusions, free carbon, and cracks and demonstrate a good octahedral shape.




The raw diamond


10


is then sawed in the (001) or cube plane as shown in FIG.


2


.




The sawed diamond


10


is then mounted on a suitable steel shank


12


(

FIG. 3

) using a titanium-based “adhesive”


14


applied using well known and conventional techniques under high vacuum. A CuAgTi alloy is preferred as the “adhesive” material. Alternatively, electron beam deposited palladium and titanium metals form adherent coatings on diamond surfaces and can be used to adhere diamond


10


to shank


12


.




“Machining” is accomplished as shown in FIG.


4


. Sawed diamond


10


, mounted on steel shank


12


via “adhesive” layer


14


is angularly rotated, preferably at a 30° angle, as required in ion beam


16


to achieve the desired shape described below. An electron beam that incorporates no ions could also be used to etch diamond


10


in the manner described. Ion beam


16


is similar to that used in transmission electron microscopy for purposes of preparing samples under examination. If an electron beam is used, conventional such beams that are known to etch diamond are satisfactory. An ion gun of the type supplied by Commonwealth Scientific Corporation has been found suitable for this application.




Because of the thickness of the tip of diamond


10


in its final form, described below, mechanical methods cannot be used to achieve the polishing or shaping of diamond


10


since the mechanical pressures applied will result in breakage of diamond


10


. Thus, some non-contact “machining” means such as ion or electron beam must be used. The use of lasers as non-contact machining tools is generally impossible in this application due to the thermal shock imparted to diamond


10


in such a laser machining process. Laser machining using femtosecond or picosecond pulses may, however, be possible since at these short pulse widths, heating or thermal shock is not as much of a problem. Chemical etching techniques are of course not useful because of the inertness of diamond.




In the practical instrumentation applications of the solid diamond field emitters of the present invention it is desirable to have large field emission currents on the order of milliamperes and low voltage. To fulfill these requirements, the material tip should be very sharp. In order to obtain such a sharp tip, preferably on the order of from about 3 angstroms up to about 100μ, and preferably from about 5 angstroms up to about 10μ and most preferably, as in the case of high current instruments operating in the range of 100 volts, from about 3 angstroms up to about 3μ, diamond


10


is manipulated in ion or electron beam


16


using conventional manipulation techniques to achieve the desired tip radius.




Since even with fine radii of the dimensions just described, the surface of diamond


10


after ion or electron beam machining will not be perfectly smooth, a single solid diamond tip of the type described herein may act as an array of tips depending upon the surface roughness of the tip. For the larger radii tips a surface roughness (peak height) of between about 20 angstroms and about 1μ is preferred. Most preferred, however, is a surface roughness of less than about 10 angstroms for those applications wherein single point electron field emission is desired.




The shape of the solid diamond tip is not particularly critical, i.e. it can be a wide cone, a narrow cone or even an asymmetric shape, so long as some portion of its extreme surface is pointed within the radius parameters just described.




Where a wide field emission is required, a plurality of the solid diamond emitters of the present invention can be arrayed to provide whatever breadth of electron field is desired. Indeed, the appropriate surface roughness, as just described, may provide a sufficient number of diamond points to provide a broader field of electron emission than would be achieved with a “smoother” solid diamond surface. Arrays of the emitters of the present invention that include the pointed solid diamond electron emitter mounted or adhered to an appropriate conductive shank as described above are useful in many types of instrumentation.





FIG. 5

schematically depicts a field emitter extractor gauge (FEG) of the type in which the solid diamond emitter of the present is useful. As shown in

FIG. 5

, FEG


20


comprises field emitter


22


or


24


. In the case of field emitter


22


, the device is called a Top FEG while in the case where field emitter


24


is present the device is called a Side FEG. Anode grid


26


surrounds the volume


28


and serves to direct the flow of electrons from either field emitter


22


or field emitter


24


toward focus plate


30


having aperture


32


therein. Reflector


34


reflects electrons passing through aperture


32


at an obtuse angle back toward focus plate


30


. Aperture


36


in reflector


34


allows passage of a focused electron beam to collector


38


. Arrays of the solid diamond emitters of the present invention are useful as either the top or side FEG configurations.





FIG. 6

depicts schematically a field emitter residual gas analyzer (FERGA) that can utilize the solid diamond field emitters of the present invention. As shown in

FIG. 6

, the FERGA


40


comprises: 1) a field emitter array


42


that can be a solid diamond field emitter or an array of such emitters of the type described herein; an anode grid


44


enclosing volume


46


to direct electrons from field emitter array


42


; focus plate


50


having aperture


52


therein that permits passage of a focused electron beam through focus plate


50


, and quadrupole


54


.




As the invention has been described, it will be apparent to those skilled in the art that the same may be varied in many ways without departing from the spirit and scope of the invention. Any and all such modifications are intended to be included within the scope of the appended claims.



Claims
  • 1. A solid diamond electron emitter comprising a diamond greater than 5 μm in thickness having a pointed surface with a radius of less than about 100 μm, said pointed surface having a roughness of between about 20 angstroms and about 10 μm.
  • 2. The solid diamond electron emitter of claim 1 wherein said point has a surface roughness below about 10 angstroms.
  • 3. The solid diamond electron emitter of claim 1 wherein said radius is less than about 10 μm.
  • 4. The solid diamond electron emitter of claim 1 wherein said radius ranges form about 3 angstroms to about 3 μm.
  • 5. The solid diamond electron emitter of claim 1 further including a conductive shank to which said diamond is adhered.
  • 6. The solid diamond electron emitter of claim 4 wherein said diamond is adhered to said conductive shank by a vapor deposited layer of palladium or titanium.
  • 7. The solid diamond field emitter of claim 5 wherein said radius is less than about 10 μm.
  • 8. The solid diamond electron emitter of claim 5 wherein said radius ranges from about 3 angstroms to about 3 μm.
  • 9. The solid diamond electron field emitter of claim 4 wherein said point is produced using a non-contact machining technique.
  • 10. The solid diamond electron emitter of claim 8 wherein said non-contact machining technique is selected from the group consisting of electron beam, ion beam and laser machining techniques.
  • 11. A field emitter extractor gauge comprising a field emitter array, an anode grid, a focus plate, a reflector and a collector wherein said field emitter array comprises an array of solid diamond electron emitters each comprising a diamond greater than 5 μm in thickness having a pointed surface with a radius of less than about 100 μm, said pointed surface having a roughness of between about 20 angstroms and about 10 μm.
US Referenced Citations (2)
Number Name Date Kind
5825122 Givargizov et al. Oct 1998 A
6184611 Saito et al. Feb 2001 B1