Patent Application
20190088995
The present disclosure relates to a solid electrolyte material and a battery.
Japanese Unexamined Patent Application Publication No. 2011-129312 discloses an all-solid battery using a sulfide solid electrolyte.
Japanese Unexamined Patent Application Publication No. 2006-244734 discloses an all-solid battery using a halide containing indium as a solid electrolyte.
In known technologies, it is desired to realize a solid electrolyte material having a high lithium ion conductivity.
In one general aspect, the techniques disclosed here feature a solid electrolyte material represented by the following Compositional Formula (1):
Li6-3zYzX6, where, 0<z<2 is satisfied; and X represents Cl or Br. (1)
According to the present disclosure, a solid electrolyte material having a high lithium ion conductivity can be achieved.
Additional benefits and advantages of the disclosed embodiments will become apparent from the specification and drawings. The benefits and/or advantages may be individually obtained by the various embodiments and features of the specification and drawings, which need not all be provided in order to obtain one or more of such benefits and/or advantages.
Embodiments of the present disclosure will now be described with reference to the drawings.
The solid electrolyte material in Embodiment 1 is a compound represented by the following Compositional Formula (2):
Li3YX6 (2)
where, X represents Cl (chlorine) or Br (bromine).
According to the structure mentioned above, a solid electrolyte material (halide solid electrolytic material) having a high lithium ion conductivity can be achieved. In addition, a solid electrolyte material having a structure stable in an assumed operation temperature range (e.g., a range of −30° C. to 80° C.) of a battery can be achieved. That is, the solid electrolyte material of Embodiment 1 does not have a structure (e.g., the structure in Japanese Unexamined Patent Application Publication No. 2006-244734) in which the phase transition temperature is present within the operation temperature range of the battery. Consequently, even in an environment with temperature change, phase transition does not occur in the operation temperature range of the battery, and a high ionic conductivity can be stably maintained.
According to the structure described above, an all-solid-state secondary battery having excellent charge and discharge characteristics can be achieved by using the solid electrolyte material of Embodiment 1. In addition, an all-solid-state secondary battery not containing sulfur can be achieved by using the solid electrolyte material of Embodiment 1. That is, the solid electrolyte material of Embodiment 1 does not have a structure (e.g., the structure in Japanese Unexamined Patent Application Publication No. 2011-129312) generating hydrogen sulfide when exposed to the atmosphere. Accordingly, an all-solid-state secondary battery not generating hydrogen sulfide and having excellent safety can be achieved.
The solid electrolyte material in Embodiment 1 may include a crystal phase. Examples of the crystal phase include a first crystal phase and a second crystal phase described below.
That is, the solid electrolyte material in Embodiment 1 may include a first crystal phase.
In the first crystal phase, the arrangement of halogen X is the same as that of Br in Li3ErBr6 (hereinafter, also expressed as LEB) having a crystal structure belonging to space group C2/m.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, a crystal structure like the first crystal phase allows X to be more strongly attracted to the periphery of Y. Consequently, a path through which lithium ions diffuse is formed. Accordingly, the lithium ion conductivity is further improved.
As shown in
The first crystal phase having the same halogen arrangement as that of the LEB structure includes, in a unit cell, two of the same compositions represented by Compositional Formula (2).
The lattice constants of the unit cell defined by the LEB structure are a =6.9 to 7.6 angstrom, b=11.9 to 13.1 angstrom, c=6.8 to 7.5 angstrom, α=90°, β=109°, and γ=90°.
The LEB structure can be identified by structural analysis using X-ray diffractometry. When the measurement is performed by a θ-2θ method using Cu—Kα rays (wavelength: 1.5405 angstrom and 1.5444 angstrom) as the X-ray, strong peaks are observed within the ranges of diffraction angle 2θ values of 25° to 28°, 29° to 32°, 41° to 46°, 49° to 55°, and 51° to 58°.
The solid electrolyte material in Embodiment 1 may satisfy ILEB(110)/ILEB(200)<0.01.
Herein, ILEB(200) represents the X-ray diffraction intensity of a first crystal phase plane corresponding to the (200) plane in the crystal structure of Li3ErBr6.
ILEB(110) represents the X-ray diffraction intensity of a first crystal phase plane corresponding to the (110) plane in the crystal structure of Li3ErBr6.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, irregular arrangement of Y can be achieved. Consequently, the conduction path of lithium ions is three-dimensionally connected. Accordingly, the lithium ion conductivity is further improved.
As described above, the arrangement of cations of the solid electrolyte material in Embodiment 1 need not be the same as the arrangement of cations in the LEB structure. That is, at least part of Y (yttrium) and at least part of Li may be irregularly arranged.
The irregularity of the arrangement of cations can be evaluated by the above-mentioned intensity ratio “ILEB(110)/ILEB(200)” in the XRD pattern.
When the arrangement of Y is regular, ILEB(110)/ILEB(200)=about 0.02 (about 2%). The value of ILEB(110)/ILEB(200) decreases with an increase in irregularity. As described above, if ILEB(110)/ILEB(200)<0.01 (1%), sufficiently irregular arrangement of Y can be achieved.
The solid electrolyte material in Embodiment 1 may satisfy FWHM1/2 θc1≥0.015.
Herein, FWHM1 represents the full width at half maximum of an X-ray diffraction peak of a first crystal phase plane corresponding to the (200) plane in the crystal structure of Li3ErBr6.
In the expression, 2 θc1 denotes the diffraction angle at the center of the X-ray diffraction peak (peak central value).
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, a nonuniform lattice constant can be provided. Consequently, a region having a spread in the lattice is formed. Accordingly, the lithium ion conductivity is further improved.
As described above, the lattice constant of the solid electrolyte material in Embodiment 1 need not be completely uniform. That is, the lattice constant may have some nonuniformity. Specifically, the lattice constant distribution may have a full width at half maximum of about 1% or more.
In the solid electrolyte material of Embodiment 1, the structure of the first crystal phase may be distorted, and the atoms may be arranged at slightly different atomic positions.
The solid electrolyte material in Embodiment 1 may include a heterogeneous crystal phase having a crystal structure different from that of the first crystal phase.
In such a case, the heterogeneous crystal phase may lie between the first crystal phases.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, the conduction of lithium ions between the first crystal phases is enhanced by the heterogeneous crystal phase. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 1 may include an amorphous phase.
In such a case, the amorphous phase may lie between the first crystal phases.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, the conduction of lithium ions between the first crystal phases is enhanced by the amorphous phase. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 1 may include a second crystal phase.
In the second crystal phase, the arrangement of halogen X is the same as that of Cl in Li3ErCl6 (hereinafter, also expressed as LEC) having a crystal structure belonging to space group P-3m1.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, a crystal structure like the second crystal phase allows X to be more strongly attracted to the periphery of Y. Consequently, a path through which lithium ions diffuse is formed. Accordingly, the lithium ion conductivity is further improved.
As shown in
The second crystal phase having the same halogen arrangement as that of the LEC structure includes, in a unit cells, three of the same compositions represented by Compositional Formula (2).
The lattice constants of the unit cell defined by the LEC structure are a=10.97 to 11.5 angstrom, b=a, c=5.9 to 6.2 angstrom, α=90°, β=90°, and γ=120°.
The LEC structure can be identified by structural analysis using X-ray diffractometry. When the measurement is performed by a θ-2θ method using Cu—Kα rays (wavelength: 1.5405 angstrom and 1.5444 angstrom) as the X-ray, strong peaks are observed within the ranges of diffraction angle 2θ values of 29.8° to 32°, 38.5° to 41.7°, 46.3° to 50.4°, and 50.8° to 55.4°.
The solid electrolyte material in Embodiment 1 may satisfy ILEC(110)/ILEC(303)<0.3.
Herein, ILEC(303) is the X-ray diffraction intensity of a second crystal phase plane corresponding to the (303) plane in the crystal structure of Li3ErCl6.
ILEC(110) is the X-ray diffraction intensity of a second crystal phase plane corresponding to the (110) plane of the crystal structure of Li3ErCl6.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, irregular arrangement of Y can be achieved. Consequently, the conduction path of lithium ions is three-dimensionally connected. Accordingly, the lithium ion conductivity is further improved.
As described above, the arrangement of cations of the solid electrolyte material in Embodiment 1 need not be the same as the arrangement of cations of the LEC structure. That is, at least part of Y and at least part of Li may be irregularly arranged.
The irregularity of the arrangement of cations can be evaluated by the above-mentioned intensity ratio “ILEB(110)/ILEB(303)” in the XRD pattern.
When the arrangement of Y is regular, ILEC(110)/ILEC(303)≥about 0.45 (about 45%). The value of ILEC(110)/ILEC(303) decreases with an increase in irregularity. As described above, if ILEC(110)/ILEC(303)<0.30 (30%), sufficiently irregular arrangement of Y can be achieved.
The solid electrolyte material in Embodiment 1 may satisfy FWHM2/2 θc2≥0.015.
Herein, FWHM2 represents the full width at half maximum of an X-ray diffraction peak of a second crystal phase plane corresponding to the (303) plane in the crystal structure of Li3ErCl6.
In the expression, 2 θc2 denotes the diffraction angle at the center of the X-ray diffraction peak (peak central value).
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, a nonuniform lattice constant can be provided. Consequently, a region having a lattice spread is formed. Accordingly, the lithium ion conductivity is further improved.
As described above, the lattice constant of the solid electrolyte material in Embodiment 1 need not be completely uniform. That is, the lattice constant may have some nonuniformity. Specifically, the lattice constant distribution may have a full width at half maximum of about 1% or more.
In the solid electrolyte material of Embodiment 1, the structure of the second crystal phase may be distorted, and the atoms may be arranged at slightly different atomic positions.
The solid electrolyte material in Embodiment 1 may include a heterogeneous crystal phase having a crystal structure different from that of the second crystal phase.
In such a case, the heterogeneous crystal phase may lie between the second crystal phases.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, the conduction of lithium ions between the second crystal phases is enhanced by the heterogeneous crystal phase. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 1 may include an amorphous phase.
In such a case, the second crystal phase may lie between the second crystal phases.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, the conduction of lithium ions between the second crystal phases is enhanced by the amorphous phase. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 1 may have any shape, such as an acicular, spherical, or oval spherical shape. For example, the solid electrolyte material in Embodiment 1 may be in a particle form. A plurality of the particles may be laminated and then formed into a pellet or plate by pressurization.
For example, when the solid electrolyte material in Embodiment 1 is in a particle (e.g., spherical) form, the median diameter may be 0.1 μm or more and 100 μm or less.
In Embodiment 1, the median diameter may be 0.5 μm or more and 10 μm or less.
According to the structure described above, the ionic conductivity can be further increased. In addition, a more satisfactory dispersion state of the solid electrolyte material of Embodiment 1 and an active material or the like can be formed.
In Embodiment 1, the solid electrolyte material may have a median diameter smaller than that of the active material.
According to the structure described above, a more satisfactory dispersion state of the solid electrolyte material of Embodiment 1 and an active material or the like can be formed.
The solid electrolyte material in Embodiment 1 can be produced by, for example, the following method.
Raw material powders of binary halides are prepared at a blending ratio giving a target composition. For example, in the case of producing Li3YCl6, LiCl and YCl3 are prepared at a molar ratio of 3:1.
In such a case, X in Compositional Formula (2) can be determined by selecting the types of the raw material powders. The raw material powders are sufficiently mixed and are then mixed, pulverized, and reacted with each other using a mechanochemical milling process. Alternatively, the raw material powders are sufficiently mixed and may be then sintered in vacuum.
Consequently, a solid electrolyte material having a crystal phase described above is given.
The structure of the crystal phase (crystal structure) of the solid electrolyte material can be determined by adjusting the reaction method and reaction conditions for the raw material powders.
Embodiment 2 will now be described. The description overlapping with Embodiment 1 described above is omitted as appropriate.
The solid electrolyte material in Embodiment 2 is a compound represented by Compositional Formula (1):
Li6-3zYzX
where, 0<z<2 is satisfied; and X represents Cl or Br.
According to the structure mentioned above, a solid electrolyte material (halide solid electrolytic material) having a high lithium ion conductivity can be achieved. In addition, a solid electrolyte material having a structure being stable in the assumed operation temperature range (e.g., a range of −30° C. to 80° C.) of the battery can be achieved. That is, the solid electrolyte material of Embodiment 2 does not have a structure (e.g., the structure in Japanese Unexamined Patent Application Publication No. 2006-244734) in which the phase transition temperature is present within the operation temperature range of the battery. Consequently, even in an environment with temperature change, phase transition does not occur in the operation temperature range of the battery, and a high ionic conductivity can be stably maintained.
According to the structure described above, an all-solid-state secondary battery having excellent charge and discharge characteristics can be achieved by using the solid electrolyte material of Embodiment 2. In addition, an all-solid-state secondary battery not containing sulfur can be achieved by using the solid electrolyte material Embodiment 2. That is, the solid electrolyte material of Embodiment 2 does not have a structure (e.g., the structure in Japanese Unexamined Patent Application Publication No. 2011-129312) generating hydrogen sulfide when exposed to the atmosphere. Accordingly, an all-solid-state secondary battery not generating hydrogen sulfide and having excellent safety can be achieved.
The solid electrolyte material in Embodiment 2 satisfies 0.75≤z≤1.5.
According to the structure described above, a solid electrolyte material (halide solid electrolytic material) having a higher lithium ion conductivity can be achieved. In addition, an all-solid-state secondary battery having more excellent charge and discharge characteristics can be achieved.
The solid electrolyte material in Embodiment 2 satisfies 1≤z≤1.25.
According to the structure described above, a solid electrolyte material (halide solid electrolytic material) having a higher lithium ion conductivity can be achieved. In addition, an all-solid-state secondary battery having more excellent charge and discharge characteristics can be achieved.
The solid electrolyte material in Embodiment 2 may include a crystal phase. Examples of the crystal phase include a first crystal phase and a third crystal phase described below.
That is, the solid electrolyte material in Embodiment 2 may include a first crystal phase.
In the first crystal phase, the arrangement of halogen X is the same as that of Br in Li3ErBr6 (hereinafter, also expressed as LEB) having a crystal structure belonging to space group C2/m.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, a crystal structure like the first crystal phase allows X to be more strongly attracted to the periphery of Y. Consequently, a path through which lithium ions diffuse is formed. Accordingly, the lithium ion conductivity is further improved.
As shown in
The first crystal phase having the same halogen arrangement as that of the LEB structure includes, in a unit cell, two of the same composition represented by Compositional Formula (1).
The lattice constants of the unit cell defined by the LEB structure are a=6.9 to 7.6 angstrom, b=11.9 to 13.1 angstrom, c=6.8 to 7.5 angstrom, α=90°, β=109°, and γ=90°.
The LEB structure can be identified by structural analysis using X-ray diffractometry. When the measurement is performed by a θ-2θ method using Cu—Kα rays (wavelength: 1.5405 angstrom and 1.5444 angstrom) as the X-ray, strong peaks are observed within the ranges of diffraction angle 2θ values of 25° to 28°, 29° to 33, 41° to 47°, 49° to 55°, and 51° to 58°.
The solid electrolyte material in Embodiment 2 may satisfy ILEB(110)/ILEB(200)<0.01.
Herein, ILEB(200) represents the X-ray diffraction intensity of a first crystal phase plane corresponding to the (200) plane in the crystal structure of Li3ErBr6.
ILEB(110) represents the X-ray diffraction intensity of a first crystal phase plane corresponding to the (110) plane in the crystal structure of Li3ErBr6.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, irregular arrangement of Y can be achieved. Consequently, the conduction path of lithium ions is three-dimensionally connected. Accordingly, the lithium ion conductivity is further improved.
As described above, the arrangement of cations of the solid electrolyte material in Embodiment 2 need not be the same as the arrangement of cations of the LEB structure. That is, at least part of Y and at least part of Li may be irregularly arranged.
The irregularity of the arrangement of cations can be evaluated by the above-mentioned intensity ratio “ILEB(110)/ILEB(200)” in the XRD pattern.
When the arrangement of Y is regular, ILEB(110)/ILEB(200)=about 0.02 (about 2%). The value of ILEB(110)/ILEB(200) decreases with an increase in irregularity. As described above, if ILEB(110)/ILEB(200)<0.01 (1%), sufficiently irregular arrangement of Y can be achieved.
The solid electrolyte material in Embodiment 2 may satisfy FWHM1/2 θc1≥0.015.
Herein, FWHM1 represents the full width at half maximum of an X-ray diffraction peak of a first crystal phase plane corresponding to the (200) plane in the crystal structure of Li3ErBr6.
In the expression, 2 θc1 denotes the diffraction angle at the center of the X-ray diffraction peak (peak central value).
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, a nonuniform lattice constant can be provided. Consequently, a region having a lattice spread is formed. Accordingly, the lithium ion conductivity is further improved.
As described above, the lattice constant of the solid electrolyte material in Embodiment 2 need not be completely uniform. That is, the lattice constant may have some nonuniformity. Specifically, the lattice constant distribution may have a full width at half maximum of about 1% or more.
In the solid electrolyte material of Embodiment 2, the structure of the first crystal phase may be distorted, and the atoms may be arranged at slightly different atomic positions.
The solid electrolyte material in Embodiment 2 may include a heterogeneous crystal phase having a crystal structure different from that of the first crystal phase.
In such a case, the heterogeneous crystal phase may lie between the first crystal phases.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, the conduction of lithium ions between the first crystal phases is enhanced by the heterogeneous crystal phase. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 2 may include an amorphous phase.
In such a case, the amorphous phase may lie between the first crystal phases.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, the conduction of lithium ions between the first crystal phases is enhanced by the amorphous phase. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 2 may include a third crystal phase.
In the third crystal phase, the arrangement of halogen X is the same as that of Cl in Li3YbCl6 (hereinafter, also expressed as LYC) having a crystal structure belonging to space group Pnma.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, a crystal structure like the third crystal phase allows X to be more strongly attracted to the periphery of Y. Consequently, a path through which lithium ions diffuse is formed. Accordingly, the lithium ion conductivity is further improved.
As shown in
The third crystal phase having the same halogen arrangement as that of the LYC structure includes, in a unit cell, three of the same compositions represented by Compositional Formula (1).
The lattice constants of the unit cell defined by the LYC structure are a=12.8 to 13.5 angstrom, b=11.1 to 12.0 angstrom, and c=5.90 to 6.10 angstrom.
The LYC structure can be identified by structural analysis using X-ray diffractometry. When the measurement is performed by a θ-2θ method using Cu—Kα rays (wavelength: 1.5405 angstrom and 1.5444 angstrom) as the X-ray, strong peaks are observed within the ranges of diffraction angle 2θ values of 29.8° to 32°, 38.5° to 41.7°, 46.3° to 50.4°, and 50.8° to 55.4°.
The solid electrolyte material in Embodiment 2 may satisfy FWHM3/2 θc3≥0.015.
Herein, FWHM3 represents the full width at half maximum of an X-ray diffraction peak of a third crystal phase plane corresponding to the (231) plane in the crystal structure of Li3YbCl6.
In the expression, 2 θc3 denotes the diffraction angle at the center of the X-ray diffraction peak (peak central value).
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, a nonuniform lattice constant can be provided. Consequently, a region having a lattice spread is formed. Accordingly, the lithium ion conductivity is further improved.
As described above, the lattice constant of the solid electrolyte material in Embodiment 2 need not be completely uniform. That is, the lattice constant may have some nonuniformity. Specifically, the lattice constant distribution may have a full width at half maximum of about 1% or more.
In the solid electrolyte material of Embodiment 2, the structure of the third crystal phase may be distorted, and the atoms may be arranged at slightly different atomic positions.
The solid electrolyte material in Embodiment 2 may include a heterogeneous crystal phase having a crystal structure different from that of the third crystal phase.
In such a case, the heterogeneous crystal phase may lie between the third crystal phases.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, the conduction of lithium ions between the third crystal phases is enhanced by the heterogeneous crystal phase. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 2 may include an amorphous phase.
In such a case, the amorphous phase may lie between the third crystal phases.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, the conduction of lithium ions between the third crystal phases is enhanced by the amorphous phase. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 2 may have any shape, such as an acicular, spherical, or oval spherical shape. For example, the solid electrolyte material in Embodiment 2 may be in a particle form. A plurality of the particles may be laminated and then formed into a pellet or plate by pressurization.
For example, when the solid electrolyte material of Embodiment 2 is in a particle (e.g., spherical) form, the median diameter may be 0.1 μm or more and 100 μm or less.
In Embodiment 2, the median diameter may be 0.5 μm or more and 10 μm or less.
According to the structure described above, the ionic conductivity can be further increased. In addition, a more satisfactory dispersion state of the solid electrolyte material of Embodiment 2 and an active material or the like can be formed.
In Embodiment 2, the solid electrolyte material may have a median diameter smaller than that of the active material.
According to the structure described above, a more satisfactory dispersion state of the solid electrolyte material of Embodiment 2 and an active material or the like can be formed.
The solid electrolyte material in Embodiment 2 can be produced by, for example, the following method.
Raw material powders of binary halides are prepared at a blending ratio giving a target composition. For example, in the case of producing Li3YCl6, LiCl and YCl3 are prepared at a molar ratio of 3:1.
In such a case, X in Compositional Formula (1) can be determined by selecting the types of the raw material powders. In addition, the value of “z” in Compositional Formula (1) can be adjusted by adjusting the mixing ratio of the raw material powder including Y.
The raw material powders are sufficiently mixed and are then mixed, pulverized, and reacted with each other using a mechanochemical milling process. Alternatively, the raw material powders may be sufficiently mixed and then sintered in vacuum or in an inert atmosphere (for example, in an argon atmosphere or nitrogen atmosphere).
Consequently, a solid electrolyte material having a crystal phase described above is given.
The structure of the crystal phase (crystal structure) of a solid electrolyte material can be determined by adjusting the reaction method and reaction conditions for the raw material powders.
The composition of a solid electrolyte material can be determined by, for example, ICP emission spectroscopy, an inert gas melting-infrared absorption method, or an electron probe micro analyzer (EPMA) method.
Embodiment 3 will now be described. The description overlapping with Embodiment 1 or 2 described above is omitted as appropriate.
The solid electrolyte material in Embodiment 3 is a compound represented by Compositional Formula (1):
Li6-3zYzX6
where 0<z<2 is satisfied; and X represents Cl or Br.
The solid electrolyte material in Embodiment 3 may include a crystal phase. Examples of the crystal phase include a fourth crystal phase and a fifth crystal phase described below.
That is, the solid electrolyte material in Embodiment 3 may include a fourth crystal phase.
In the fourth crystal phase, X is Br. In the fourth crystal phase, when the structural analysis using X-ray diffractometry is performed by a θ-2θ method using Cu—Kα rays (wavelength: 1.5405 angstrom and 1.5444 angstrom) as the X-ray, peaks are observed within the ranges of diffraction angle 2θ values of 13.1° to 14.5°, 26.6° to 28.3°, 30.8° to 32.7°, 44.2° to 47.1°, 52.3° to 55.8°, and 54.8° to 58.5°.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, it is conceivable that the ionic conductivity is improved by the following effect. That is, a crystal structure like the fourth crystal phase allows Br to be more strongly attracted to the periphery of Y. Consequently, a path through which lithium ions diffuse is formed. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 3 may satisfy FWHM4/2 θc4≥0.015.
Herein, FWHM4 represents the full width at half maximum of an X-ray diffraction peak observed within the range of 26.6° to 28.3°.
In the expression, 2 θc4 denotes the diffraction angle at the center of the X-ray diffraction peak (peak central value).
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, it is conceivable that the ionic conductivity is improved by the following effect. That is, the structure mentioned above can provide a nonuniform lattice constant. Consequently, a region having a lattice spread is formed. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 3 may satisfy I2/I1<0.1, more preferably I2/I1<0.01.
Herein, I1 represents the intensity of the diffraction peak appearing within the range of 26.6° to 28.3°.
I2 represents the intensity of the diffraction peak within a range of 15.0° to 16.0°. If no peak was observed in this range, I2=0.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, it is conceivable that the ionic conductivity is improved by the following effect. That is, the structure described above can provide irregular arrangement of Y. Consequently, the conduction path of lithium ions is three-dimensionally connected. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 3 may include a heterogeneous crystal phase having a crystal structure different from that of the fourth crystal phase.
In such a case, the heterogeneous crystal phase may lie between the fourth crystal phases.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, it is conceivable that the ionic conductivity is improved by the following effect. That is, the conduction of lithium ions between the fourth crystal phases is enhanced by the heterogeneous crystal phase. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 3 may include an amorphous phase.
In such a case, the amorphous phase may lie between the fourth crystal phases.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, it is conceivable that the ionic conductivity is improved by the following effect. That is, the conduction of lithium ions between the fourth crystal phases is enhanced by the amorphous phase. Accordingly, the lithium ion conductivity is further improved.
In a fifth crystal phase, X is Cl. In the fifth crystal phase, when the structural analysis using X-ray diffractometry is performed by a θ-2θ method using Cu—Kα rays (wavelength: 1.5405 angstrom and 1.5444 angstrom) as the X-ray, peaks are observed within the ranges of diffraction angle 2θ values of 15.3° to 16.3°, 29.8° to 32°, 38.5° to 41.7°, 46.3° to 50.4°, and 50.8° to 55.4°.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, it is conceivable that the ionic conductivity is improved by the following effect. That is, a crystal structure like the fifth crystal phase allows Cl to be more strongly attracted to the periphery of Y. Consequently, a path through which lithium ions diffuse is formed. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 3 may satisfy FWHM5/2 θc5≥0.015.
Herein, FWHM5 represents the full width at half maximum of an X-ray diffraction peak appearing within the range of 29.8° to 32°.
In the expression, 2 θc5 denotes the diffraction angle at the center of the X-ray diffraction peak (peak central value).
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, it is conceivable that the ionic conductivity is improved by the following effect. That is, the structure mentioned above can provide a nonuniform lattice constant. Consequently, a region having a lattice spread is formed. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 3 may satisfy I4/I3<0.3.
Herein, I3 represents the intensity of the diffraction peak appearing within the range of 29.8° to 32°.
Herein, I4 represents the intensity of the diffraction peak appearing within the range of 15.3° to 16.3°.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, it is conceivable that the ionic conductivity is improved by the following effect. That is, the structure described above can provide irregular arrangement of Y. Consequently, the conduction path of lithium ions is three-dimensionally connected. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 3 may include a heterogeneous crystal phase having a crystal structure different from that of the fifth crystal phase.
In such a case, the heterogeneous crystal phase may lie between the fifth crystal phases.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, it is conceivable that the ionic conductivity is improved by the following effect. That is, the conduction of lithium ions between the fifth crystal phases is enhanced by the heterogeneous crystal phase. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 3 may include an amorphous phase.
In such a case, the amorphous phase may lie between the fifth crystal phases.
According to the structure described above, a solid electrolyte material having a higher lithium ion conductivity can be achieved. Specifically, it is conceivable that the ionic conductivity is improved by the following effect. That is, the conduction of lithium ions between the fifth crystal phases is enhanced by the amorphous phase. Accordingly, the lithium ion conductivity is further improved.
The solid electrolyte material in Embodiment 3 can be produced by, for example, the following method.
Raw material powders of binary halides are prepared at a blending ratio giving a target composition. For example, in the case of producing Li3YCl6, LiCl and YCl3 are prepared at a molar ratio of 3:1.
In such a case, X in Compositional Formula (1) can be determined by selecting the types of the raw material powders. In addition, the value of “z” in Compositional Formula (1) can be adjusted by adjusting the mixing ratio of the raw material powder including Y.
The raw material powders are sufficiently mixed and are then mixed, pulverized, and reacted with each other using a mechanochemical milling process. Alternatively, the raw material powders may be sufficiently mixed and then sintered in vacuum or in an inert atmosphere (for example, in an argon atmosphere or nitrogen atmosphere).
Consequently, a solid electrolyte material having a crystal phase described above is given.
The structure of the crystal phase of a solid electrolyte material can be determined by X-ray powder diffractometry. The measurement of X-ray powder diffraction of a sample is preferably performed in an inert atmosphere (for example, in an argon atmosphere or nitrogen atmosphere) or in a dry atmosphere with a dew point −30° C. or less.
Embodiment 4 will now be described. The description overlapping with any one of Embodiments 1 to 3 described above is omitted as appropriate.
The battery of Embodiment 4 is assembled using the solid electrolyte material described in any of Embodiments 1 to 3.
The battery of Embodiment 4 includes a solid electrolyte material, a positive electrode, a negative electrode, and an electrolyte layer.
The electrolyte layer is disposed between the positive electrode and the negative electrode.
At least one of the electrolyte layer and the negative electrode contains the solid electrolyte material of any one of Embodiments 1 to 3.
According to the structure described above, the charge and discharge characteristics of the battery can be improved.
The battery of Embodiment 4 will now be specifically described.
The battery 1000 of Embodiment 4 includes a positive electrode 201, a negative electrode 203, and an electrolyte layer 202.
The positive electrode 201 includes positive electrode active material particles 204.
The electrolyte layer 202 is disposed between the positive electrode 201 and the negative electrode 203.
The electrolyte layer 202 includes an electrolyte material (for example, solid electrolyte material).
The negative electrode 203 includes negative electrode active material particles 205 and solid electrolyte particles 100.
The solid electrolyte particles 100 are particles consisting of the solid electrolyte material of any one of Embodiments 1 to 3 or particles mainly composed of the solid electrolyte material of any one of Embodiments 1 to 3.
The positive electrode 201 contains a material having properties of occluding and releasing metal ions (for example, lithium ions). The positive electrode 201 includes, for example, a positive electrode active material (for example, positive electrode active material particles 204).
Examples of the positive electrode active material include lithium-containing transition metal oxides (e.g., Li(NiCoAl)O2 and LiCoO2), transition metal fluorides, polyanion and fluorinated polyanion materials, transition metal sulfides, transition metal oxyfluorides, transition metal oxysulfides, and transition metal oxynitrides.
The positive electrode active material particles 204 may have a median diameter of 0.1 μm or more and 100 μm or less. If the median diameter of the positive electrode active material particles 204 is larger than 100 μm, the diffusion of lithium in the positive electrode active material particles 204 slows down. Accordingly, high output operation of the battery may be difficult.
The positive electrode 201 may have a thickness of 10 to 500 μm. If the thickness of the positive electrode is smaller than 10 μm, it may be difficult to ensure a sufficient energy density of the battery. If the thickness of the positive electrode is larger than 500 μm, high output operation may be difficult.
The electrolyte layer 202 includes an electrolyte material. The electrolyte material is, for example, a solid electrolyte material. That is, the electrolyte layer 202 may be a solid electrolyte layer.
The solid electrolyte layer may be constituted of only the solid electrolyte material of any one of Embodiments 1 to 3.
Alternatively, the solid electrolyte layer may be constituted of only a solid electrolyte material different from the solid electrolyte material of any one of Embodiments 1 to 3. Examples of the solid electrolyte material different from the solid electrolyte material of any one of Embodiments 1 to 3 include Li2MgX4, Li2FeX4, Li(Al,Ga,In)X4, Li3(Al,Ga,In)X6, and LiI (X: F, Cl, Br, or I).
The solid electrolyte layer may be constituted of both the solid electrolyte material of any one of Embodiments 1 to 3 and the above-mentioned solid electrolyte material different from the solid electrolyte material of any one of Embodiments 1 to 3. In such a case, both materials may be uniformly dispersed. A layer of the solid electrolyte material of any one of Embodiments 1 to 3 and a layer of a solid electrolyte material different from the solid electrolyte material of any one of Embodiments 1 to 3 may be successively arranged in the lamination direction of the battery.
The solid electrolyte layer may have a thickness of 1 μm or more and 100 μm or less. A thickness of the solid electrolyte layer of smaller than 1 μm enhances the risk of short-circuiting between the positive electrode 201 and the negative electrode 203. In contrast, if the thickness of the solid electrolyte layer is larger than 100 μm, high output operation may be difficult.
The negative electrode 203 contains a material having properties of occluding and releasing metal ions (e.g., lithium ions). The negative electrode 203 includes, for example, a negative electrode active material (e.g., negative electrode active material particles 205).
Examples of the negative electrode active material include metal materials, carbon materials, oxides, nitrides, tin compounds, and silicon compounds. The metal material may be a simple metal substance. Alternatively, the metal material may be an alloy. Examples of the metal material include lithium metal and lithium alloys. Examples of the carbon material include natural graphite, coke, carbon during graphitization, carbon fibers, spherical carbon, artificial graphite, and amorphous carbon. From the viewpoint of capacity density, silicon (Si), tin (Sn), silicon compounds, and tin compounds can be preferably used. In the case of using a negative electrode active material having a low average reaction voltage, the electrolysis-suppressing effect of the solid electrolyte material of any one of Embodiments 1 to 3 is further highly exhibited.
The negative electrode active material particles 205 may have a median diameter of 0.1 μm or more and 100 μm or less. If the median diameter of the negative electrode active material particles 205 is smaller than 0.1 μm, a risk of failing to form a satisfactory dispersion state of the negative electrode active material particles 205 and the solid electrolyte particles 100 in the negative electrode is caused. Consequently, the charge and discharge characteristics are deteriorated. In contrast, if the median diameter of the negative electrode active material particles 205 is larger than 100 μm, the diffusion of lithium in the negative electrode active material particles 205 slows down. Accordingly, high output operation of the battery may be difficult.
The negative electrode active material particles 205 may have a median diameter larger than that of the solid electrolyte particles 100. In such a case, a satisfactory dispersion state of the negative electrode active material particles 205 and a halide solid electrolyte material can be formed.
Regarding the volume ratio between the negative electrode active material particles 205 and the solid electrolyte particles 100, “v:100-v”, contained in the negative electrode 203, the value of v may satisfy 30≤v≤95. If the value of v is lower than 30, it may be difficult to ensure a sufficient energy density of the battery. If the value of v is higher than 95, high output operation may be difficult.
The negative electrode 203 may have a thickness of 10 μm or more and 500 μm or less. If the thickness of the negative electrode is smaller than 10 μm, it may be difficult to ensure a sufficient energy density of the battery. If the thickness of the negative electrode is larger than 500 μm, high output operation may be difficult.
At least one of the positive electrode 201, the electrolyte layer 202, and the negative electrode 203 may contain a sulfide solid electrolyte or an oxide solid electrolyte for enhancing the ionic conductivity. Examples of the sulfide solid electrolyte include Li2S—P2S5, Li2S—SiS2, Li2S—B2S3, Li2S—GeS2, Li3.25Ge0.25P0.75S4, and Li10GeP2S12. Examples of the oxide solid electrolyte include NASICON-type solid electrolytes, such as LiTi2(PO4)3 and element substitutes thereof; (LaLi)TiO3 perovskite-type solid electrolytes; LISICON-type solid electrolytes, such as Li14ZnGe4O16, Li4SiO4, and LiGeO4 and element substitutes thereof; garnet-type solid electrolytes, such as Li7La3Zr2O12 and element substitutes thereof; Li3N and H substitutes thereof; and Li3PO4 and N substitutes thereof.
At least one of the positive electrode 201, the electrolyte layer 202, and the negative electrode 203 may contain a solid organic polymer electrolyte for enhancing the ionic conductivity. As the solid organic polymer electrolyte, for example, a compound composed of a polymer and a lithium salt can be used. The polymer may have an ethylene oxide structure. The ethylene oxide structure allows to contain a large amount of the lithium salt to further enhance the ionic conductivity. Examples of the lithium salt include LiPF6, LiBF4, LiSbF6, LiAsF6, LiSO3CF3, LiN(SO2CF3)2, LiN(SO2C2F5)2, LiN(SO2CF3)(SO2C4F9), and LiC(SO2CF3)3. As the lithium salt, one selected from these lithium salts may be used alone. Alternatively, a mixture of two or more selected from these lithium salts may be used as the lithium salt.
At least one of the positive electrode 201, the electrolyte layer 202, and the negative electrode 203 may contain a nonaqueous electrolyte solution, a gel electrolyte, and an ionic liquid for facilitating delivery and receipt of lithium ions and improving the output characteristics of the battery.
The nonaqueous electrolyte solution contains a nonaqueous solvent and a lithium salt dissolved in the nonaqueous solvent. Examples of the nonaqueous solvent include cyclic carbonate solvents, chain carbonate solvents, cyclic ether solvents, chain ether solvents, cyclic ester solvents, chain ester solvents, and fluorine solvents. Examples of the cyclic carbonate solvent include ethylene carbonate, propylene carbonate, and butylene carbonate. Examples of the chain carbonate solvent include dimethyl carbonate, ethyl methyl carbonate, and diethyl carbonate. Examples of the cyclic ether solvent include tetrahydrofuran, 1,4-dioxane, and 1,3-dioxolane. Examples of the chain ether solvent include 1,2-dimethoxyethane and 1,2-diethoxyethane. Examples of the cyclic ester solvent include γ-butyrolactone. Examples of the chain ester solvent include methyl acetate. Examples of the fluorine solvent include fluoroethylene carbonate, methyl fluoropropionate, fluorobenzene, fluoroethyl methyl carbonate, and fluorodimethylene carbonate. As the nonaqueous solvent, one selected from these nonaqueous solvents may be used alone. Alternatively, a combination of two or more selected from the nonaqueous solvents may be used as the nonaqueous solvent. The nonaqueous electrolyte solution may contain at least one fluorine solvent selected from the group consisting of fluoroethylene carbonate, methyl fluoropropionate, fluorobenzene, fluoroethyl methyl carbonate, and fluorodimethylene carbonate. Examples of the lithium salt include LiPF6, LiBF4, LiSbF6, LiAsF6, LiSO3CF3, LiN(SO2CF3)2, LiN(SO2C2F5)2, LiN(SO2CF3)(SO2C4F9), and LiC(SO2CF3)3. As the lithium salt, one selected from these lithium salts may be used alone. Alternatively, a mixture of two or more selected from these lithium salts may be used as the lithium salt. The concentration of the lithium salt is, for example, in a range of 0.5 to 2 mol/L.
As the gel electrolyte, a polymer material impregnated with a nonaqueous electrolyte solution can be used. Examples of the polymer material include poly(ethylene oxide), polyacrylonitrile, poly(vinylidene fluoride), poly(methyl methacrylate), and polymers having ethylene oxide bonds.
The cation constituting the ionic liquid may be, for example, an aliphatic chain quaternary salt, such as tetraalkylammonium and tetraalkylphosphonium; an aliphatic cyclic ammonium, such as pyrrolidiniums, morpholiniums, imidazoliniums, tetrahydropyrimidiniums, piperaziniums, and piperidiniums; or a nitrogen-containing aromatic heterocyclic cation, such as pyridiniums and imidazoliums. The anion constituting the ionic liquid may be, for example, PF6−, BF4−, SbF6−, AsF6−, SO3CF3−, N(SO2CF3)2−, N(SO2C2F5)2−, N(SO2CF3)(SO2C4F9)−, or C(SO2CF3)3−. The ionic liquid may contain a lithium salt.
At least one of the positive electrode 201, the electrolyte layer 202, and the negative electrode 203 may contain a binder for enhancing the adhesion between the particles. The binder is used for improving the binding properties of the materials constituting the electrodes. Examples of the binder include poly(vinylidene fluoride), polytetrafluoroethylene, polyethylene, polypropylene, aramid resins, polyimide, polyimide, polyamideimide, polyacrylonitrile, poly(acrylic acid), poly(methyl acrylate), poly(ethyl acrylate), poly(hexyl acrylate), poly(methacrylic acid), poly(methyl methacrylate), poly(ethyl methacrylate), poly(hexyl methacrylate), poly(vinyl acetate), polyvinyl pyrrolidone, polyether, polyether sulfone, hexafluoro polypropylene, styrene butadiene rubber, and carboxymethyl cellulose. The binder can be a copolymer of two or more materials selected from tetrafluoroethylene, hexafluoro ethylene, hexafluoropropylene, perfluoroalkyl vinyl ether, vinylidene fluoride, chlorotrifluoroethylene, ethylene, propylene, pentafluoro propylene, fluoromethyl vinyl ether, acrylic acid, and hexadiene. Alternatively, the binder may be a mixture of two or more selected from these binders.
At least one of the positive electrode 201 and the negative electrode 203 may contain a conductive assistant as needed.
The conductive assistant is used for reducing the electrode resistance. Examples of the conductive assistant include graphites, such as natural graphite and artificial graphite; carbon blacks, such as acetylene black and Ketjen black; conductive fibers, such as carbon fibers and metal fibers; metal powders, such as carbon fluoride and aluminum; conductive whiskers, such as zinc oxide and potassium titanate; conductive metal oxides, such as titanium oxide; and conductive polymers, such as polyaniline, polypyrrole, and polythiophene. The use of a carbon conductive assistant as the conductive assistant can reduce the cost.
The battery in Embodiment 4 can be constituted to have any shape, such as a coin-like, cylindrical, rectangular, sheet-like, button-like, flat, or laminar shape.
The present disclosure will now be described in detail using examples and comparative examples.
Raw material powders, LiBr and YBr3, were weighed at a molar ratio of LiBr:YBr3=3:1 in a dry atmosphere with a dew point of −30° C. or less and were pulverized and mixed in a mortar. Subsequently, the mixture was subjected to milling treatment with a planetary ball mill at 600 rpm for 25 hours.
Consequently, a powder of Li3YBr6 including a crystal phase was prepared as the solid electrolyte material of Example A1.
A pressure molding die 300 is constituted of an electronically insulated polycarbonate frame 301 and electron-conductive stainless steel upper punch 303 and lower punch 302.
The ionic conductivity was evaluated using the structure shown in
The powder of the solid electrolyte material of Example 1 was loaded in the pressure molding die 300 in a dry atmosphere with a dew point of −30° C. or less and was uniaxially pressed at 400 MPa to produce a conductivity measurement cell of Example A1.
Under the pressurizing condition, leads were taken from the upper punch 303 and the lower punch 302, respectively, and were connected to a potentiostat (VersaSTAT4, Princeton Applied Research) equipped with a frequency response analyzer, and the ionic conductivity at room temperature was measured by an electrochemical impedance measurement technique.
The solid electrolyte material of Example A1 had an ionic conductivity of 3.0×10−4 S/cm measured at 22° C.
The results shown in
That is, the conductivity measurement cell of Example A1 was placed in a thermostat chamber, and the temperature dependence of conductivity was measured in a temperature-rising process and a temperature-falling process within a range of −30° C. to 80° C.
As shown in
The results shown in
That is, the crystal structure of the solid electrolyte was analyzed by measuring the X-ray diffraction pattern in a dry environment with a dew point of −45° C. or less with an X-ray diffraction apparatus (MiniFlex600, RIGAKU Corporation), using Cu—Kα rays as the X-ray source.
Regarding the solid electrolyte material of Example A1, the resulting X-ray diffraction pattern was analyzed. The results indicated that the X-ray diffraction pattern of the solid electrolyte material of Example A1 corresponded to the X-ray diffraction pattern of a crystal structure having the same anion arrangement as that of an LEB structure when the lattice constants were a=6.93, b=11.96, c=6.84, α=90°, β=109°, and γ=90°.
The rate of the diffraction peak intensity (ILEB(110)) corresponding to the (110) plane to the diffraction intensity (ILEB(200)) in the vicinity of the diffraction peak corresponding to the LEB structure (200) plane, ILEB(110)/ILEB(200), was less than 1%.
The relationship between the full width at half maximum (FWHM) and the peak central value 2 θc of the diffraction peak (2θ=27.4°) corresponding to the LEB structure (200) plane was expressed as FWHM/2 θc=2.3%.
The solid electrolyte material Li3YBr6 of Example A1 and an active material LiCoO2 (hereinafter, expressed as LCO) were weighed at a volume ratio of 50:50 in an argon glove box and were mixed in an agate mortar to produce a mixture.
The solid electrolyte material of Example A1 in an amount corresponding to a thickness of 700 μm and 12.3 mg of the mixture described above were stacked in this order in an insulation outer casing. The stacked product was pressure-molded at a pressure of 360 MPa to obtain a first electrode and a solid electrolyte layer.
Subsequently, a metal In (thickness: 200 μm) was stacked on the solid electrolyte layer on the side opposite to the side being in contact with the first electrode. The stacked product was pressure-molded at a pressure of 80 MPa to produce a laminate composed of the first electrode, the solid electrolyte layer, and a second electrode.
Subsequently, stainless steel current collectors were placed on the top and bottom of the laminate, and a collector lead was attached to each of the current collectors.
Finally, the inside of the insulation outer casing was blocked and sealed from the outside atmosphere by insulation ferrules.
Consequently, a secondary battery of Example A1 was produced. Charge and discharge test
The results shown in
That is, the secondary battery of Example A1 was placed in a thermostat chamber of 25° C.
The battery was constant-current charged at a current value of 0.05 C rate (20 hour rate) with respect to the theoretical capacity of the battery, and the charge was terminated when the voltage reached 3.7 V.
Subsequently, the battery was discharged at a current value of the same 0.05 C rate as above, and the discharge was terminated when the voltage reached 1.9 V.
As a result of the measurement described above, the initial discharge capacity of the secondary battery of Example A1 was 126 μAh.
LiCl and YCl3 were used as the raw material powers of a solid electrolyte and were mixed at a molar ratio of LiCl:YCl3=3:1. Consequently, Li3YCl6 was prepared as the solid electrolyte material of Example A2.
Excepting the above, evaluation and analysis were implemented as in Example A1.
The ionic conductivity measured at 22° C. was 1.1×10−4 S/cm.
The temperature dependence of conductivity did not indicate phase transition within a range of −30° C. to 80° C.
The XRD pattern of the solid electrolyte material of Example A2 is shown in
The analysis of the resulting X-ray diffraction pattern showed that the X-ray diffraction pattern corresponded to the X-ray diffraction pattern of a crystal structure having the same anion arrangement as that of an LEC structure when the lattice constants were a=11.202, b=11.202, c=6.032, α=90°, β=90°, and γ=120°.
The rate of the diffraction peak intensity (ILEC(110)) corresponding to the (110) plane to the diffraction intensity (ILEC(303)) in the vicinity of the diffraction peak corresponding to the LEC structure (303) plane, ILEC(110)/ILEC(303), was 26%.
The relationship between the full width at half maximum (FWHM) and the peak central value 2 θc of the diffraction peak (2θ=31.4°) corresponding to the LEC structure (303) plane was expressed as FWHM/2 θc=1.8%.
The solid electrolyte material of Example A2 was used as the solid electrolyte used in the mixture and the solid electrolyte layer.
Excepting the above, production and a charge and discharge test of a secondary battery were implemented as in Example A1.
The initial discharge capacity of the secondary battery of Example A2 was 70 μAh.
Raw material powders, LiBr and InBr3, were weighed at a molar ratio of LiBr:InBr3=3:1 in a dry atmosphere with a dew point of −30° C. or less and were pulverized and mixed in a mortar. Subsequently, the mixture was pressure-molded into a pellet shape to prepare a sample. The sample was vacuum-sealed in a glass tube and was fired at 200° C. for one week.
Consequently, Li3InBr6 was prepared as the solid electrolyte material of Comparative Example 1.
Excepting the above, the ionic conductivity and phase transition were evaluated as in Example A1.
The ionic conductivity measured at 22° C. was less than 1×10−7 S/cm.
The temperature dependence of the ionic conductivity of the solid electrolyte material of Comparative Example 1 is shown in
As shown in
LiCl and FeCl2 were used as the raw material powers of a solid electrolyte and were mixed at a molar ratio of LiCl:FeCl2=2:1. Consequently, Li2FeCl4 was prepared as the solid electrolyte material of Comparative Example 2.
Excepting the above, the ionic conductivity was evaluated as in Example A1.
The measured ionic conductivity was 8.7×10−6 S/cm.
The solid electrolyte material of Comparative Example 2 was used as the solid electrolyte used in the mixture and the solid electrolyte layer.
Excepting the above, production and a charge and discharge test of a secondary battery were implemented as in Example A1.
The initial discharge characteristics of the secondary battery of Comparative Example 2 are shown in
The initial discharge capacity of the secondary battery of Comparative Example 2 was less than 1 μAh. That is, in the secondary battery of Comparative Example 2, the charge and discharge operation was not observed.
Table 1 shows the structures in Examples A1 and A2 and Comparative Examples 1 and 2 and the results of each evaluation.
Comparison of Examples A1 and A2 with Comparative Example 1 revealed that Li3YX6 does not cause phase transition within a range of −30° C. to 80° C. That is, it was demonstrated that the structures in Examples A1 and A2 are stable in the assumed operation temperature range of the batteries.
Comparison of Examples A1 and A2 with Comparative Examples 1 and 2 revealed that Li3YX6 shows a high ionic conductivity of 1×10−5 S/cm or more at around room temperature.
In both Examples A1 and A2, the charge and discharge operation of the battery was observed at room temperature. In contrast, in Comparative Example 2, almost no discharge capacity was obtained, and battery operation was not observed.
Methods for synthesis and evaluation of Li6-3zYzBr6 will now be described.
Raw material powders, LiBr and YBr3, were weighed at a molar ratio of LiBr:YBr3=6-3z:z in a glove box kept in a dry and low-oxygen atmosphere with a dew point of −90° C. or less and an oxygen value of 5 ppm or less.
The “value of z” in each of Examples B1 to B8 is shown in Table 2 below.
Excepting the above, the solid electrolyte materials of Examples B1 to B8 were respectively produced as in Example A1.
Conductivity measurement cells of Examples B1 to B8 were respectively produced as in Example A1 in a glove box kept in a dry and low-oxygen atmosphere with a dew point of −90° C. or less and an oxygen value of 5 ppm or less.
Excepting the above, ionic conductivity was measured as in Example A1.
Each of the conductivity measurement cells of Examples B1 to B8 was placed in a thermostat chamber, and the temperature dependence of conductivity was measured in a temperature-rising process and a temperature-falling process within a range of −30° C. to 80° C. As a result, in all Examples, no sharp change in conductivity indicating phase transition was observed.
The crystal structure of each of the solid electrolyte materials of Examples B1 to B8 was analyzed as in Example A1.
The resulting X-ray diffraction pattern of each of the solid electrolyte materials of Examples B1 to B8 was analyzed. The results revealed that in all Examples B1 to B8, the solid electrolyte material had a crystal structure having the same anion arrangement as that of the LEB structure. In Example B3 where “z=1” (i.e., Li3YBr6), the X-ray diffraction pattern corresponded to the X-ray diffraction pattern when the lattice constants were a=6.93 angstrom, b=11.96 angstrom, c=6.84 angstrom, α=90°, β=109°, γ=90°.
Table 2 shows the relationship between the full width at half maximum (FWHM) of the LEB (200) diffraction peak (2θ=28°) and the peak center 2 θc. In all Examples B1 to B8, FWHM/2 θc≥0.015.
The respective solid electrolyte materials of Examples B1 to B8 and an active material LiCoO2 were weighed at a molar ratio of 50:50 in a glove box kept in a dry and low-oxygen atmosphere with a dew point of −90° C. or less and an oxygen value of 5 ppm or less. The materials were mixed in an agate mortar to produce mixtures of Examples B1 to B8.
Excepting the above, secondary batteries of Examples B1 to B8 were produced as in Example A1.
A charge and discharge test of the secondary batteries of Examples B1 to B8 was performed as in Example A1.
Table 2 shows the structures in Examples B1 to B8 and the results of each evaluation.
Methods for synthesis and evaluation of Li6-3zYzCl6 will now be described.
Raw material powders, LiCl and YCl3, were weighed at a molar ratio of LiCl:YCl3=6-3z:z in a glove box kept in a dry and low-oxygen atmosphere with a dew point of −90° C. or less and an oxygen value of 5 ppm or less.
The “value of z” in each of Examples C1 to C8 is shown in Table 3 below.
Excepting the above, the solid electrolyte materials of Examples C1 to C8 were respectively produced as in Example A1.
Conductivity measurement cells of Examples C1 to C8 were respectively produced as in Example A1 in a glove box kept in a dry and low-oxygen atmosphere with a dew point of −90° C. or less and an oxygen value of 5 ppm or less.
Excepting the above, ionic conductivity was measured as in Example A1.
Each of the conductivity measurement cells of Examples C1 to C8 was placed in a thermostat chamber, and the temperature dependence of conductivity was measured in a temperature-rising process and a temperature-falling process within a range of −30° C. to 80° C. As a result, in all Examples, no sharp change in conductivity indicating phase transition was observed.
The crystal structure of each of the solid electrolyte materials of Examples C1 to C8 was analyzed as in Example A1.
The resulting X-ray diffraction pattern of each of the solid electrolyte materials of Examples C1 to C8 was analyzed. The results revealed that in all Examples C1 to C8, the solid electrolyte material had a crystal structure having the same anion arrangement as that of the LYC structure. In Example C3 where “z=1” (i.e., Li3YCl6), the X-ray diffraction pattern corresponded to the X-ray diffraction pattern when the lattice constants (lattice constants of the unit cell defined by the LYC structure) were a=12.93 angstrom, b=11.202 angstrom, c=6.04 angstrom, α=90°, β=90°, and γ=90°.
Table 3 shows the relationship between the full width at half maximum (FWHM) of the LYC(231) diffraction peak and the peak center 2 θc. In all Examples C1 to C8, FWHM/2 θc≥0.015.
The respective solid electrolyte materials of Examples C1 to C8 and an active material LiCoO2 were weighed at a molar ratio of 50:50 in a glove box kept in a dry and low-oxygen atmosphere with a dew point of −90° C. or less and an oxygen value of 5 ppm or less. The materials were mixed in an agate mortar to produce mixtures of Examples C1 to C8.
Excepting the above, secondary batteries of Examples C1 to C8 were produced as in Example A1.
A charge and discharge test of the secondary batteries of Examples C1 to C8 was performed as in Example A1.
Table 3 shows the structures in Examples C1 to C8 and the results of each evaluation.
Comparison of Examples B1 to B8 and C1 to C8 with Comparative Example 1 revealed that in Examples B1 to B8 and C1 to C8, phase transition does not occur within a range of −30° C. to 80° C. That is, it was demonstrated that the structures in Examples B1 to B8 and C1 to C8 are stable in the assumed operation temperature range of the batteries.
Comparison of Examples B1 to B8 and C1 to C8 with Comparative Examples 1 and 2 revealed that in Examples B1 to B8 and C1 to C8, a high ionic conductivity of 1×10−5 S/cm or more was shown at around room temperature.
In addition, in all Examples B1 to B8 and C1 to C8, the charge and discharge operation of the battery was observed in room temperature. In contrast, in Comparative Example 2, almost no discharge capacity was obtained, and battery operation was not observed.
Comparison of Examples B2 to B7 and C2 to C7 with Examples B1, B8, C1, and C8 revealed that in Examples B2 to B7 and C2 to C7, a high ionic conductivity of 1×10−4 S/cm or more was shown at around room temperature. Consequently, it is demonstrated that a higher ionic conductivity is achieved by satisfying 0.75≤z≤1.5.
Comparison of Examples B3 to B5 and C3 to C5 with Examples B1, B2, B6 to B8, C1, C2, and C6 to C8 revealed that in Examples B3 to B5 and C3 to C5, a high ionic conductivity of 3×10−4 S/cm or more was shown at around room temperature. Consequently, it is demonstrated that a higher ionic conductivity is achieved by satisfying 1≤z≤1.25.
Consequently, it is demonstrated that the solid electrolyte material according to the present disclosure is an electrolyte material not generating hydrogen sulfide and capable of stably maintaining a high lithium ion conductivity. It is furthermore demonstrated that the solid electrolyte material can achieve an all-solid battery that does not generate hydrogen sulfide and has excellent charge and discharge characteristics.
The battery of the present disclosure can be used as, for example, an all-solid-state lithium secondary battery.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2016-153736 | Aug 2016 | JP | national |
| 2017-113102 | Jun 2017 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2017/024934 | Jul 2017 | US |
| Child | 16198762 | US |