Claims
- 1. A method for making a solid electrolytic capacitor, which comprises providing an electrode, forming a dielectric film on said electrode, and forming a counter electrode on said dielectric film, wherein said counter electrode comprises a first conductive polymer layer which is formed by chemical polymerization, and is made of a polymer of pyrrole or its derivative doped with a mixed dopant comprising both a polyvalent anion and a monovalent anion comprising a sulfonate anion dissociated from an anionic surface active agent, wherein the mole ratio of polyvalent anion to monovalent anion is 1:9 to 1:999.
- 2. A method according to claim 1, wherein the chemical polymerization comprises immersing the dielectric film-bearing electrode in a monomer solution comprising pyrrole or its derivative and the anionic surface active agent, further immersing the thus immersed electrode in an oxidant solution comprising the polyvalent anion, and repeating the above steps until the resultant conductive polymer of pyrrole or its derivative is formed on said dielectric film in a given thickness.
- 3. A method according to claim 2, wherein said monomer solution comprises a liquid medium comprising water and an alcohol.
- 4. A method according to claim 3, wherein said alcohol is a member selected from the group consisting of methanol, ethanol, propanol, ethylene glycol, propylene glycol, glycerin and mixtures thereof.
- 5. A method according to claim 2, wherein said monomer solution further comprises a phenolic compound.
- 6. A method according to claim 5, wherein said phenolic compound is a member selected from the group consisting of phenol, nitrophenol, cyanophenol, hydroxybenzoic acid, hydroxyphenol, acetophenol and mixtures thereof.
- 7. A method according to claim 1, wherein the chemical polymerization comprises immersing the dielectric film-bearing electrode in a polymerization system comprising pyrrole or its derivative, the anionic surface active agent and an oxidant capable of yielding the polyvalent anion until the resultant conductive polymer of pyrrole or its derivative is formed in a given thickness.
- 8. A method according to claim 7, wherein said polymerization system comprises a liquid medium comprising water and an alcohol.
- 9. A method according to claim 8, wherein said alcohol is a member selected from the group consisting of methanol, ethanol, propanol, ethylene glycol, propylene glycol, glycerin and mixtures thereof.
- 10. A method according to claim 7, wherein said polymerization system farther comprises a phenolic compound.
- 11. A method according to claim 10, wherein said phenolic compound is a member selected from the group consisting of phenol, nitrophenol, cyanophenol, hydroxybenzoic acid, hydroxyphenol, acetophenol and mixtures thereof.
- 12. A method according to claim 1, wherein said electrode is made of a valve metal and said dielectric film is formed by anodization of said valve metal.
- 13. A method according to claim 12, wherein said valve metal is a member selected from the group consisting of aluminum and tantalum.
- 14. A method according to claim 1, wherein said dielectric film consists of a polymer thin film.
- 15. A method according to claim 14, wherein said polymer thin film is formed by spin coating of a solution of a polymer.
- 16. A method according to claim 15, wherein said polymer is made of a polyimide.
- 17. A method according to claim 1, further comprising forming a manganese dioxide layer after the formation of said dielectric film.
- 18. A method according to claim 17, wherein said manganese dioxide layer is formed by thermal decomposition of a manganese salt.
- 19. A method according to claim 17, wherein said manganese dioxide layer is formed by reduction of a permanganate.
- 20. A method according to claim 1, further comprising forming, prior to the formation of said first conductive polymer layer, a second conductive polymer layer on said dielectric film, said second conductive polymer layer comprising a polymer of a thiophene derivative of the following formula wherein A represents an unsubstituted or substituted alkylene group.
- 21. A method according to claim 20, wherein said second conductive polymer layer is formed by chemical polymerization.
- 22. A method according to claim 21, wherein the chemical polymerization comprises immersing the dielectric film-bearing electrode in a monomer solution comprising the thiophene derivative and an anionic surface active agent, and further immersing the thus immersed electrode in an oxidant solution comprising a sulfate thereby forming a conductive polymer of the thiophene derivative on said dielectric film.
- 23. A method according to claim 22, wherein said sulfate consists of ferric sulfate.
- 24. A method according to claim 22, wherein said anionic surface active agent comprising a sulfonate anion.
- 25. A method according to claim 22, wherein said monomer solution further comprises a phenolic compound.
- 26. A method according to claim 25, wherein said phenolic compound is a member selected from the group consisting of phenol, nitrophenol, cyanophenol, hydroxybenzoic acid, hydroxyphenol, acetophenol and mixtures thereof.
- 27. A method according to claim 21, wherein the chemical polymerization comprises immersing the dielectric film-bearing electrode in a polymerization system comprising the thiophene derivative, an anionic surface active agent capable of yielding a monovalent anion, and an oxidant capable of yielding the polyvalent anion until the resultant conductive polymer of pyrrole or its derivative is formed in a given thickness.
- 28. A method according to claim 20, wherein said second conductive polymer layer is formed by immersing the dielectric film in a solution of a conductive polymer of the thiophene derivative.
- 29. A method according to claim 20, further comprising forming a third conductive polymer layer on said first conductive polymer layer on a side opposite to the side where said second conductive polymer layer has been formed, said third conductive polymer layer comprising a polymer of a thiophene derivative of the following formula wherein A represents an unsubstituted or substituted alkylene group.
- 30. A method according to claim 29, wherein said third conductive polymer layer is formed by chemical polymerization.
- 31. A method according to claim 29, wherein said third conductive polymer layer is formed by immersing the dielectric film in a conductive polymer solution.
- 32. A method according to claim 1, wherein said first conductive polymer layer is formed by electrolytic polymerization.
- 33. A method according to claim 32, wherein said electrolytic polymerization is conducted in an aqueous medium.
- 34. A method according to claim 33, wherein said electrolytic polymerization is conducted in an aqueous solution of pyrrole or its derivative comprising a phenolic compound.
- 35. A method according to claim 34, wherein said phenolic compound is a member selected from the group consisting of phenol, nitrophenol, cyanophenol, hydroxybenzoic acid, hydroxyphenol, acetophenol and mixtures thereof.
Priority Claims (2)
Number |
Date |
Country |
Kind |
8-082320 |
Apr 1996 |
JP |
|
8-244397 |
Sep 1996 |
JP |
|
Parent Case Info
This application is a divisional of application Ser. No. 08/840,445 filed Apr. 1, 1997 now U.S. Pat. No. 5,812,367.
US Referenced Citations (11)
Foreign Referenced Citations (7)
Number |
Date |
Country |
0 652 576 A2 |
May 1995 |
EP |
0 654 804 A2 |
May 1995 |
EP |
63-158829 |
Jul 1988 |
JP |
63-173313 |
Jul 1988 |
JP |
1-253226 |
Oct 1989 |
JP |
2-15611 |
Jul 1990 |
JP |
8-293436 |
Apr 1995 |
JP |
Non-Patent Literature Citations (2)
Entry |
“The Technical Report at the 58th Meeting of the Electrochemical Society”, pp. 251-252, See attached English Abstract titled, “Application of Polyimide Thin Film Prepared by Electrodeposition for Dielectric of Capacitor”, Hashizume et al., pp. 4, No Date. |
“Effective Doping of Polymer Anion During Chemical Polymerization of Pyrrole Using Fe(OH)3 Oxidant”, Ohtani et al., Bull Chem. Soc. Jpn., vol. 62, No. 1, pp. 234-238, 1989. |