Patent Application
20230178263
Embodiments of the present disclosure relate generally to a UV curable mixture for forming an electrical insulation layer of a conductor.
Electrical conductors at different electric potential need an electrical insulation in order to prevent short circuits and/or to avoid danger. The electrical conductor may be for example a Roebel bar formed by a plurality of conductor strands and the insulation may avoid a short circuit between different strands of the Roebel bar. A Roebel bar arrangement formed by a plurality of reciprocally insulated conductor strands may for example reduce an overall electric resistance when compared to a conductor of the same section formed by only one conductor strand, i.e. a single wire. The electrical conductor, for example the Roebel bar, also needs to be insulated electrically from the ground and/or from other conductors. A groundwall insulation is therefore needed. Similarly for a coil wire, a stator winding, etc. different windings and/or coil turns need to be reciprocally insulated and to be insulated from bodies at ground potential and/or from other conductors.
The electrical conductor may for example be a coil formed by one or more wires forming one or more windings, typically a plurality of windings. It is necessary to prevent a short circuit between different windings and/or between different portions of the electric conductor in order to ensure a uniform current flow along the whole conductor, for example to maximize a magnetic field induced by a current flowing in the conductor. Therefore, for example, different windings need to be reciprocally insulated.
The electrical conductor may be part of a stator winding.
Furthermore, electrical conductors may need an insulation to ensure safety, for example, avoiding the risk of short circuits and/or electrocution to humans and/or animals.
Traditionally, mica tapes and/or resin impregnation are used to form an electrical insulation. The resin impregnation may include a curing process.
Using mica tapes and/or curing the resin to form an electric insulation is time and energy consuming and may lead to the formation of voids that lead to a non-uniform insulation of the electrical conductor.
In particular for Roebel bars and/or coil wires, the use of mica tapes and/or the use of a curable resin for a resign impregnation may lead to a nonhomogeneous insulation, for example to a nonhomogeneous inter-strand and/or groundwall insulation. A nonhomogeneous insulation layer may for example result from the presence of voids and/or from a nonhomogeneous thickness and/or geometry of the mica tape windings around the conductor and/or the conductor strands to be insulated.
Furthermore, the insulation properties, for example the breakdowns voltage and/or the dielectric strength of the resin may be poor.
Mica tapes and resin impregnation are also time and energy consuming resulting in substantial effort and cost.
In order to obtain a more homogeneous insulation and/or a better insulation, characterized for example by an increased breakdown voltage and dielectric strength while also simplifying and improving the insulation process, further improvements are demanded that overcome the disadvantages of the use of mica tapes and of the use of a curable resin.
An aspect of the present disclosure provides an electrical insulation mixture for forming a layer on a conductor surface. The mixture includes an UV curable thermoset resin and a filler. The filler includes UV transparent platelets made of a platelet material. As used herein, UV transparency is defined for light in a wavelength range between 300 and 420 nm.
According to the present disclosure a material is UV transparent, if in the wavelength range between 300 nm and 420 nm the transparency of the material is substantially similar to or higher than the transparency of synthetic fluorine mica (synmica), also known as fluorphlogopite mica. Here, “substantially similar” is defined with a tolerance of 10% transparency. For example, a transmittance of the UV transparent material in the wavelength range between 300 nm and 420 nm may be, for example, equal to or higher than 90% of the transmittance of synmica, within the stated wavelength range. The transparency may be the same as or higher than the transmittance of synmica.
Another aspect of the present disclosure provides a method for electrically insulating a metallic conductor. The method includes providing a metallic conductor, obtaining an electrical insulation mixture as disclosed herein, forming a jacketing on a surface of the metallic conductor using the mixture which was thus obtained, and exposing the mixture to ultraviolet radiation to cure the mixture, thus forming, from the jacketing, an electrical insulation layer on the surface of the metallic conductor.
Another aspect of the present disclosure provides a metallic conductor, the metallic conductor having an electrical insulation layer obtained by curing the electrical insulation mixture as disclosed herein, optionally obtained with the method as disclosed herein.
Embodiments of the present disclosure will be described in more detail with reference to the drawings, in which:
Mica tapes are not advantageous to form an electrical insulation, due to the difficulties in forming a uniform mica tape winding. A resin for forming an insulating impregnation may be characterized by poor insulating properties, like for example a low dielectric strength.
To overcome said disadvantages the present disclosure describes a UV curable mixture for forming an electrical insulation layer of a conductor, wherein the mixture includes an UV curable thermoset resin and a filler, wherein the filler is formed by UV transparent solid platelets. In particular, the UV transparent solid platelets may be synthetic fluorine mica platelets.
In the present disclosure, solid platelets are used as filler in a UV curable thermoset resin to enhance the electrical insulation of high voltage conductor bars.
Mica tapes commercially available as insulation materials for high voltage applications are typically composed of natural micas such as muscovite mica with a dielectric strength of 120-200 kV/mm or phlogopite mica with a dielectric strength of 115-140 kV/mm. Such natural micas, however, are strong energy absorbers in the ultraviolet range, making it impossible to use such mineral fillers for the processing of insulation with UV-curable thermosets.
Laboratory trials have confirmed that the presence of even small quantities of mineral mica have an enormous impact on the curing speed of the UV curable thermoset, where for instance the presence of 5% weight muscovite mica results in a 50% reduction in curing speed of the UV epoxy.
Synthetic fluorine mica (synmica), also known as fluorphlogopite mica, with a dielectric strength in the order of 180 kV/mm, provides a solution for improving an electrical insulation. Due to a small change in the chemical structure with respect to the natural mica, where hydroxyl groups are replaced by fluorine atoms, the synthetic mica (in the following, also referred to as synmica) is rendered UV transparent. Synmica does not absorb electromagnetic radiation in the ultraviolet range of the spectrum, allowing the curing reaction to maintain the same reaction rate as in the case of the processing of a neat thermoset that would not contain any filler material.
Synmica will not compete with the photoinitiator of the UV curable thermoset, allowing the curing reaction to maintain the same reaction rate as in the case of the processing of a neat thermoset that would not contain any filler material. Experiments have confirmed that the addition of up to 20% weight of synmica does not result in any reduction of curing speed of the UV curable thermoset.
The enhancement in the insulating performance of the UV curable thermoset with the addition of synmica has been demonstrated experimentally by means of AC breakdown strength measurements in oil performed according to IEC 60243-1 electric strength of insulating materials—test methods, part 1, test at power frequencies.
This part of IEC 60243 provides test methods for the determination of short-time electric strength of solid insulating materials at power frequencies between 48 Hz and 62 Hz. The measurements were carried out using a pair of spherical equal diameter metal electrodes, each 20 mm in diameter. The surrounding medium used to prevent flash over during the test was transformer oil (Diala S4 ZX-1). The rate of voltage raise used was 2000 V/s.
The test measures the breakdown strength of the material expressed in kV of applied voltage normalized by the thickness of the specimen in mm. A series of measurements is performed and the breakdown strength data is analyzed using a two-parameter Weibull cumulative distribution of the form:
where σ is the breakdown strength value obtained experimentally, i.e. the breakdown strength value forming a random variable, α is a scale parameter corresponding to a 63.2% breakdown strength cumulative probability, and β is a shape parameter indicative of the scattering of the statistical distribution. The higher the value of β, the less scattering of the breakdown strength values and the more robust the insulating properties of the material. Fσ(t) indicates the cumulative distribution function of the random variable a, defined as:
F
σ(t)=P(σ≤t)
i.e. Fσ(t) indicates the probability that σ≤t, i.e. that the random variable σ is less than or equal to the value t.
The addition of 5-15% of synmica causes an initial decrease in the average breakdown strength and the scale parameter α, while these properties significantly improve when 20% synmica is used. Furthermore, the addition of 15% synmica to the UV curable thermoset results in an increase of β from 8.2 (neat epoxy) to 17.3, while the breakdown strength for 0.01% failure is increased from 13.7 kV/mm to 22.5 kV/mm. The measurements demonstrate that the addition of synmica to the UV curable thermoset make the resin a significantly more robust electric insulator while not affecting its processability, since its curing reaction rate is not decreased.
The insulation layer 20 may have a thickness between 0.5 mm to 2.0 mm.
The plurality of conductor strands 15-1, 15-2, 15-3, and 15-4 form an overall electric conductor, for example a Roebel bar, a coil wire and/or coil turn, a stator winding, etc. In the following, the conductor strands 15-1, 15-2, 15-3, and 15-4 may be referred to as conductors for simplicity.
For a Roebel bar the conductor strands, whose section is shown in
Between the different conductor strands a gap G is provided, for example in order to increase an overall number of windings/turns of a coil and/or to avoid a short circuit between conductor strands of a Roebel bar.
An AC current flows in a direction substantially orthogonal to the plane of
For example, only one conductor 15-1 may be present, or two (15-1, 15-2), three (15-1, 15-2, 15-3), or any finite number n of conductors (15-1, 15-2, 15-3, . . . , 15-n) can be arranged in a plurality of spatial positions. For example, one or more of the conductors may have different cross-sectional shapes, such as square, square with rounded corners, rectangular, circular etc. In the example of
For example, dividing the conductor into a plurality of conductor strands 15-1, 15-2, 15-3, 15-4, allows to increase the windings/turns of a coil and/or allows to reduce an overall resistance of the conductor in the presence of skin effect, in particular when the conductor strands are longitudinally interwoven and/or permuted regularly. It is necessary to keep the conductor strands reciprocally insulated to avoid a short circuit that would for example reduce the generated magnetic field in the coil and/or increase an electric resistance in a Roebel bar.
Furthermore, a gap is also present between the conductor and the ground and/or any body (not shown) at ground electric potential.
The insulation layer 20 insulates the different conductor strands in order to avoid a short circuit between conductor strands. The insulation layer 20 may therefore form both an inter-strand insulation and/or a groundwall insulation.
The conductor, for example formed by the conductor strands, together with the insulation layer 20 forms a conductor arrangement 10 that may be used for example in an electric machine, like for example a generator or a motor, forming for example a coil.
The conductor, for example formed by the conductor strands, together with the insulation layer 20 forms a conductor arrangement 10 that may be used for example for transferring electric energy from a generator to a load in an electric circuit, forming for example a Roebel bar arrangement.
The insulation layer 20 according to the present disclosure includes an insulation material obtained through a curing process of a thermosetting material, wherein solid electrically insulating elements 25, such as mica platelets, are present inside the thermoset material. The relationship (volume ratios) of the solid insulating elements to the thermosetting material component of the insulation material is between (at least) 20:80, may be between (at least) 25:75 and typically about (at least) 30:70 by volume in the uncured state. The solid insulating elements may have a volume of at least 20%, may be at least 25%, and particularly may be at least 30% of the total volume of the insulation material in the uncured state, and the thermosetting material may be makes up essentially the remainder of the volume. Thus, the thermosetting material may be has a volume of at most 80%, may be at most 75% and typically at most 70% by volume.
An upper bound for the volume of the solid insulating elements is 40%, may be 35%, and particularly may be 30%. A lower bound for the volume of the thermosetting material is 60%, may be 65%, and particularly may be 70%.
From another perspective, the volume fraction of the solid insulating elements to the thermosetting material component of the insulation material is between 20:80 (20% to 80%), may be between 25:75 (25% to 75%) and typically about 30:70 (30% to 70%) by volume in the uncured state. A particularly upper limit for the platelet content is 50% or even 40% by volume. This platelet content is particularly to improve the electrical insulation mixture ensuring an efficient UV curing (e.g., by allowing sufficient penetration of the UV light for a fast and effective curing) while providing adequate characteristics of the cured mixture together with good dielectric strength.
Alternatively or in addition, in an uncured state the volume of the platelets may for example be 20% of the volume of the electrical insulation mixture and the volume of the thermoset resin may be 80% of the volume of the electrical insulation mixture; or the volume of the platelets may for example be 25% of the volume of the electrical insulation mixture and the volume of the thermoset resin may be 75% of the volume of the electrical insulation mixture; or the volume of the platelets may for example be 30% of the volume of the electrical insulation mixture and the volume of the thermoset resin may be 70% of the volume of the electrical insulation mixture. Alternatively, the volume of the platelets may be 20% or more of the volume of the electrical insulation mixture and the remaining volume of the electrical insulation mixture is occupied by the thermoset resin, in particular the volume of the platelets may be 20% or more or 25% or more or 30% or more, the remaining volume of the electrical insulation mixture being filled out by thermoset resin.
The term composition generally refers to a mixture or a compound of the materials that are involved. Particularly, a composition of a thermosetting material and mica elements may be obtained by mixing the uncured thermosetting material and the insulating elements. For example, the thermosetting material and mica platelets are fed, typically gravimetrically fed, into a mixer that produces the composition. The composition may generally be a mica platelet-filled liquid resin compound. The thermosetting material may be an UV-curable thermosetting resin. The insulating elements may be mica particles, typically mica platelets, having a predetermined average particle size. The insulation material, or the thermosetting material component thereof, is typically cured accordingly.
For example,
As schematically shown, the conductor strand 15-1 may be insulated by an insulation layer 20 that forms a groundwall insulation and/or an inter-strand insulation and/or that insulates the conductor 15-1 from other conductors and/or windings and/or coil turns.
In some embodiments of the present disclosure, the insulation layer 20 may be formed by a UV curable mixture including an UV curable thermoset resin and a filler, wherein the filler is formed by UV transparent solid platelets 25, for example by synthetic fluorine mica platelets.
According to embodiments of the present disclosure, an electrical insulation mixture for forming a layer on a conductor surface is provided, wherein the mixture includes an ultraviolet (UV) curable thermoset resin and a filler, wherein the filler includes UV transparent platelets 25 made of a platelet material, wherein UV transparency is given for light in a wavelength range between 300 and 420 nm.
A platelet may have substantially flake-like shape with its (average) thickness (in a direction perpendicular to a local flake plane) being much smaller than its length and width (measured for a flattened flake if the flake is not completely flat). In one possible definition, a platelet may be considered to be transparent for example if a radiant flux of UV light incident on the local flake plane is substantially transmitted through the whole platelet and passes through the whole platelet without being attenuated significantly. For example, the radiant flux transmitted thought the thickness of the flake and exiting the flake may be for example 85% or more of the incident radiant flux that is incident onto the flake-like platelet.
The surfaces of the platelet may not reflect the UV light back and the platelet material of the platelet may not dissipate or absorb the UV light to a larger degree than expressed by the above threshold.
The purpose of the UV radiation is to interact with the thermoset resin to activate the photoinitiators that catalyze the cross-linking reaction of the thermoset material. The insulation mixture filled with synmica platelets interacts with the UV radiation substantially in the same way as the insulation mixture composed of neat resin (i.e. without synmica platelets) does. This can be achieved when the platelets are substantially UV transparent.
UV light may be a light with a wavelength between 380 and 420 nm and may, for example, be produced by a source with an irradiance at the UV emitting window of 4 W/cm{circumflex over ( )}2 for an emitting window e.g. of 300 mm×20 mm. A total UV power of 240 W may be irradiated by a source that may be e.g. a UV LED, e.g. a UV LED based on SLM Technology.
For example, in the wavelength range between 0.38 and 0.42 μm a transmittance of 85% or more through the synmica platelets may be obtained.
The maximum depth of penetration of an UV beam into a non-transparent material has a finite constant value as long as the intensity is not increased. The maximum depth of penetration may be a maximum depth at which the radiating flux of the UV light is above a fraction of the radiating flux incident to the non-transparent material.
For materials that interact with an UV radiation beam, the intensity of the beam decays as a function of penetrated depth.
For the present disclosure, the thickness of the insulation layer is significantly smaller than the maximum penetration depth, therefore there is substantially no resin curing gradient from the surface to the insulation-conductor interface; the degree of curing is the same throughout the thickness of the insulation layer.
It is for example possible to measure the transparency of a platelet, shining UV light onto a surface of the platelet, for example, emitting a light that propagates in a direction perpendicular to the local flake plane and measuring the radiant flux that passes through the flake plane exiting on the opposite side of the flake as a fraction of the radiant flux incident on the flake. In practice the measurement may be carried out focusing a UV light beam onto a surface of the platelet, measuring the radiating power of said beam incident on the flake and the radiating power of the UV light emitted through the flake on the side opposite to the side where the beam is directed towards the flake. For example, a transmittance of the platelet with the flake-like shape, i.e. the radiating power passing through the platelet/flake and reemitted by the platelet/flake as a fraction of the incident power, may be 85% or more for wavelengths above 0.2 micrometers, e.g. 0.3 micrometers and/or below 1.0 micrometers, e.g. below 0.4 micrometers.
The flake-like platelets made of synmica (fluorphlogopite mica) may have a length/size between 3.2 μm and 14.3 μm. A thickness of the platelets may be between 0.30 μm and 0.35 μm. The aspect ratio of the synmica platelets may be 3.2/0.35=9 to 14.3/0.30=48.
The UV transparent light is not reflected back from a surface of the platelets and effectively penetrates the platelet material and the electrical insulation mixture.
Moreover, due to the transparency of the platelet material, the UV light absorbed by a surface of the platelet material, further propagates in the platelet material. The UV radiation transmitted through a surface of the platelet material further propagates in the platelet material at least for a depth d corresponding to a maximum diameter/size d of the platelets.
According to the present disclosure the material of the platelets is UV transparent, if in the wavelength range between 300 nm and 420 nm the transparency of the material of the platelets is substantially similar to (i.e., at least substantially the same as, with a tolerance of, e.g., about 10%) the transparency of synthetic fluorine mica (synmica), also known as fluorphlogopite mica. The platelet material may be considered UV transparent, if a transmittance of the platelet material is substantially similar to the transmittance of synmica. For example, a transmittance of the UV transparent material of the platelets in the wavelength range between 300 nm and 420 nm may be similar to the transmittance of synmica within this wavelength range, for example 90% of the transmittance of synmica or more. The transmittance may be a transmittance with respect to a maximum diameter/size of the platelets. The transmittance may be a function of the wavelength. It is intended that for each wavelength in the range between 300 nm and 420 nm the transmittance of a layer of thickness d of the platelet material is at least 90% of the transmittance of a layer of thickness d of synmica for the same wavelength and for an arbitrary thickness d, for example a maximum or average thickness/size of the platelets.
Here, “substantially similar” is defined with a tolerance of 10% transparency. For example, a transmittance of the UV transparent material in the wavelength range between 300 nm and 420 nm may be, for example, equal to or higher than 90% of the transmittance of synmica, within the stated wavelength range. The transparency may be the same as or higher than the transmittance of synmica.
Therefore, the platelets and/or the platelet material is considered to be UV transparent if for each wavelength in the range between 300 nm and 420 nm the transmittance of a layer of thickness d of the platelet material is at least 90% of the transmittance of a layer of thickness d of synmica for the same wavelength and for an arbitrary thickness d, for example a maximum or average thickness/size of the platelets.
For example, the platelets and/or the platelet material is considered to be UV transparent if for each wavelength in the range between 200 nm and 420 nm the transmittance of a layer of thickness d of the platelet material is at least 90% of the transmittance of a layer of thickness d of synmica for the same wavelength and for an arbitrary thickness d, for example a maximum or average thickness of the platelets.
In some embodiments, the platelet material is also characterized by a dielectric strength that is substantially the same dielectric strength as synmica, for example 90% or more of the dielectric strength of synmica.
The platelets do not need to be made of pure platelet material and/or the platelets do not need to be made of pure synmica. The platelet material and/or the synmica may contain impurities as long as the transparence/transmittance and/or the dielectric strength is not substantially affected, for example as long as the transmittance is 90% or more of the transmittance of pure synmica and the dielectric strength is 90% or more of the dielectric strength of pure synmica.
For example, the platelet material may have a dielectric strength between 115-180 kV/mm, for example 140 kV/mm.
The platelet material may be synmica or may be a material with substantially similar properties of synmica.
The UV transparent solid platelets 25 ensure that less UV light is absorbed by the mixture that includes the UV curable thermoset resin and the filler including the UV transparent platelets. Therefore, the electrical insulation mixture can be advantageously cured by UV light and in particular an elevated curing speed can be maintained to form the insulation layer and in addition the dielectric strength of the insulation layer is increased.
In particular, the UV transparent solid platelets 25 may include synthetic fluorine mica platelets. The UV transparent solid platelets 25 provide the improved dielectric strength of the electrical insulation mixture, due to the insulation properties of the synthetic fluorine mica and further allow a fast and rapid curing of the UV curable thermoset resin in said mixture as a consequence of the UV transparency of the solid platelets 25. In particular, the synthetic fluorine mica platelets being substantially UV transparent ensure that the UV light effectively penetrates the mixture curing the UV curable thermoset resin of the mixture. UV opaque platelets, formed, for example, by natural mica, may still improve the dielectric strength, but absorbing UV light would prevent an effective and rapid curing of the UV curable thermoset resin in order to rapidly form the insulation layer of the electric conductor.
The insulation thickness, i.e. the thickness of the insulation layer, may have be for example between 0.5 mm to 2.0 mm.
The concentration of the platelets in the mixture may be between 0 to 20% in weight.
The method 300 for electrically insulating the metallic conductor starts according to 1001. The method includes obtaining 1002 an electrical insulation mixture, the mixture including a UV curable thermoset resin and a filler. The method further includes forming 1003 a jacketing on a surface of the conductor using the mixture obtained in 1002 and exposing 1004 the mixture to ultraviolet (UV) radiation to cure the mixture, thus forming, from the jacketing, an electrical insulation layer 20 on the surface of the metallic conductor.
In some embodiments, at least one of obtaining 1002 the mixture, forming 1003 a jacketing, and exposing 1004 the mixture to UV radiation is repeated 1005 one or more times until the whole surface of the conductor is electrically insulated. In particular, during the repetitions different longitudinal sections of the conductor may be electrically insulated. For example, during the repetitions a jacketing unit may be translated along a longitudinal axis of the conductor and forming 1003 the jacketing and exposing 1004 the mixture to UV radiation is carried out iteratively for each longitudinal section of the longitudinally extending conductor.
Analogously the repeating 1005 may be carried out along a wire or a group of wires that may form a coil and/or along turns forming a coil in an electric machine.
The synthetic fluorine mica of
The maximum jacketing speed is defined as a maximum speed for which the insulation layer on the conductor has been sufficiently cross-linked by the curing reaction to consider that the thermoset material has hardened. The cross-linking reaction is driven by the photoinitiator present in the thermoset resin, and the photoinitiator only reacts during the time that it is exposed to UV radiation.
For example, after the curing is completed the insulating layer is e.g. sufficiently regular and/or uniform, for example without voids and/or cracks and/or variations along a longitudinal axis of the conductor.
Depending on parameters like, for example, the geometry of the electrical conductor and/or the speed at which the thermoset resin, e.g. the epoxy resin, is provided and/or the power of the UV light during curing, the maximum jacketing speed may vary. Nevertheless, when synmica is added the maximum jacketing speed remains substantially constant in function of the percentage of synmica added to the UV curable thermoset resin and/or a decrease of the maximum jacketing speed in function of the percentage of mica added to the epoxy resin is much lower than for the addition of natural mica.
Therefore,
The breakdown strength a of the insulation layer, once the curing is completed, forms a real-valued nonnegative random variable with a cumulative distribution Fσ(t) of the form:
The cumulative distribution is a two-parameter Weibull cumulative distribution.
The breakdown strength a is a real-valued nonnegative random variable and the cumulative distribution Fσ(t) indicates the probability that σ≤t, therefore Fσ(t)=P(σ≤t).
The parameter α forms a scale parameter and β forms a shape parameter.
For t=α, Fσ(t)=Fσ(α)=1−e−(1)
F
σ(α)=P(σ≤α)≅0.632
The shape parameter β indicates a scattering of the statistical distribution Fσ(t). When β increases the cumulative distribution function Fσ(t) becomes steeper. We observe that
Therefore when β→+∞, the probability density function converges to a Dirac delta distribution centered at a and Fσ(t) to a unit step function centered in a and with Fσ(α)≅0.632 according to the previous equation.
The breakdown strength a may be measured, for example, in kV/mm.
Therefore, for a value β→+∞ the probability that the breakdown strength value is less than α is zero and the probability that the breakdown strength value is less than α+ε is one for any value ε>0.
This means that for β→+∞, when applying an electric field that is strictly less than α an electric breakdown does not occur, whereas for any electric field that is strictly greater than α an electric breakdown does certainly occur.
For a finite positive value of β the transition of Fσ(t) in correspondence of α would have a finite positive slope, with steepness increasing with increasing value of β.
It is therefore desirable to have a possibly big value of α and a value of β that is as great as possible.
The addition of 5-15% of synmica can cause an initial decrease in the average breakdown strength and/or the scale parameter α, but when 20% synmica is used the breakdown strength and the scale parameter α significantly improve.
For example, for the addition of 15% synmica to the UV curable thermoset resin, the shape parameter β increases to 17.3 compared to the shape parameter β for neat epoxy of only 8.2. This results in a significant improvement of the steepness of the cumulative distribution Fσ(t) and in a reduced scattering around α.
The increase shows that an electrical insulation mixture for forming a layer on a conductor surface including an UV curable thermoset resin and a filler wherein the filler includes UV transparent platelets including synmica (synthetic fluorine mica) according to the present disclosure is beneficial for an improved electrical insulation, increasing a shape parameter β and/or the breakdown strength for a 0.01% failure, while maintaining an elevate maximum jacketing speed as illustrated in
In some embodiments of the present disclosure, an electrical insulation mixture for forming a layer on a conductor surface is provided, wherein the mixture includes an UV curable thermoset resin and a filler, wherein the filler includes UV transparent platelets made of a platelet material, wherein UV transparency is given for light in a wavelength range between 300 and 420 nm.
In some embodiments the UV transparent platelets include solid platelets having a predominantly crystalline molecular structure with a density above 2 g/cm{circumflex over ( )}3.
In some embodiments the platelet material of the UV transparent platelets includes synthetic fluorine mica platelets.
In some embodiments, the relation of the UV transparent platelets with respect to the mixture is less than or equal to 25% wt.-%, optionally less than or equal to 20% wt.-% or less than or equal to 15% wt-%.
In some embodiments, the platelet material has a dielectric strength of at least 180 kV/mm.
In some embodiments, the mixture has a dielectric strength, for a failure probability of 0.01%, of more than 17 kV/mm, optionally more than 22 kV/mm or more than 22.5 kV/mm.
Some embodiments of the present disclosure are formed by a method for electrically insulating a metallic conductor, the method including obtaining an electrical insulation mixture according any one of the preceding claims, forming a jacketing on a surface of the metallic conductor using the mixture thus obtained, and exposing the mixture to ultraviolet radiation to cure the mixture, thus forming, from the jacketing, an electrical insulation layer on the surface of the metallic conductor. The thickness of the insulation layer is not particularly limited. For example, the space in between two strands can be entirely filled by the insulation layer(s).
The platelets are, in particular, transparent with respect to the ultraviolet radiation (i.e., at least with respect to a main wavelength of the ultraviolet radiation and/or with respect to at least 80% of a wavelength-dependent intensity of the ultraviolet radiation). Thereby, a UV curing of the electrical insulation mixture is improved, because less UV light is absorbed by the UV transparent platelets.
In some embodiments, the metallic conductor includes one or more conductor strands, and the electrical insulation layer is formed on each of one or more of the conductor strands, optionally on each of the conductor strands.
In some embodiments, an electrical insulation layer is formed on each of at least two adjacent conductor strands for providing simultaneously an inter-strand insulation and an outer groundwall insulation of the metallic conductor.
Some embodiments of the present disclosure are formed by a metallic conductor with an electrical insulation layer obtained by curing the electrical insulation mixture.
In some embodiments, the metallic conductor has an electrical insulation obtained with methods of the present disclosure.
The technology described in the present disclosure may help to improve in an electrical insulation mixture and a method for electrically insulating a metallic conductor and a metallic conductor with an electrical insulation layer. According to the present disclosure, the electrical insulation layer can be obtained curing with UV radiation the mixture after forming a jacketing on a surface of the conductor; the jacketing can be carried out at a jacketing speed that does not decrease in the presence of an increasing percentage of UV transparent synthetic mica platelets in the filler of the mixture; the UV transparent synthetic mica platelets in the filler of the mixture allow a fast jacketing and curing, while providing good and improved characteristics of the electrical insulation layer, like for example an increased shape parameter β, and/or an increased breakdown strength, characterized for example by a higher breakdown strength for a 0.01% failure and/or a higher scale parameter α of a cumulative distribution function Fσ(t) of the breakdown strength σ and/or an increased average breakdown strength, for example, a measured average breakdown strength of the insulation layer.
| Number | Date | Country | Kind |
|---|---|---|---|
| 20173534.7 | May 2020 | EP | regional |
This patent application is a National Stage Entry of PCT/EP2021/062192 filed on May 7, 2021, which claims the benefit and priority of European Patent Application No. 20173534.7 filed on May 7, 2020, the disclosures of which are incorporated by reference herein in their entirety as part of the present application.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2021/062192 | 5/7/2021 | WO |