Patent Application
20220263137
There is a continuing need for high performance battery cells, and their associated cell components, and particularly for high energy density rechargeable lithium metal batteries.
The present disclosure describes solid-state laminate electrode assemblies and various methods for making the solid-state laminate electrode assemblies.
In one aspect the present disclosure provides methods for making a solid-state laminate electrode assembly.
In various embodiments the solid-state laminate electrode assembly comprises a lithium metal layer reactively bonded to a lithium ion conducting sulfide glass layer. Preferably, the reactive bond is sufficiently complete that it forms a continuous solid electrolyte interphase (SEI) at the boundary between the layers.
In various embodiments, to bring about a continuous SEI, the lithium metal layer should have a major surface, which, just prior to bonding (e.g., by laminating), is in a highly reactive state (i.e., it is substantially unpassivated). In various embodiments the method involves making a pristine lithium metal layer having a substantially unpassivated first major surface, and therefore highly reactive, and maintaining the highly reactive surface in its substantially unpassivated state until it has been reactively bonded with the sulfide glass layer.
In various embodiments the method comprises:
A method for making a solid-state laminate electrode assembly, the method comprising the steps of
In various embodiments, the inert protective material layer on the sulfide glass first major surface is a liquid phase layer of a dry hydrocarbon liquid, and the inert protective material layer on the substantially unpassivated lithium metal first major surface is a liquid phase layer of a dry hydrocarbon liquid.
In various embodiments, the hydrocarbon liquid on the lithium metal surface is removed substantially immediately prior to the reactive bonding step, and optionally the hydrocarbon liquid on the sulfide glass is removed substantially immediately prior to reactively bonding step.
In various embodiments, the removal of the hydrocarbon liquid is accelerated by the application of one or more heat (conductive or convective), vacuum suction, blowing a jet of dry Ar or He, and blowing a jet of high vapor pressure protective liquid followed by vacuum suction.
In various embodiments, the step of cleaning the first major surface of the sulfide glass layer under an argon plasma, by ion etching; wherein the cleaning step is performed after the liquid phase layer of protective fluid has been removed.
In various embodiments, the step of treating the clean first major surface of the sulfide glass under a nitrogen containing plasma, wherein the treatment modifies the surface composition of the sulfide glass by introducing nitrogen into/onto the glass surface.
In various embodiments, the step of treating the clean sulfide glass first major surface to form a precursor film consisting of 1 to 5 monolayers of a halogen (e.g., iodine) or an interhalogen, or nitrogen onto the clean glass surface, wherein the monolayer(s) react with lithium on bonding to form a solid electrolyte interphase.
In various embodiments, the step of treating the clean sulfide glass first major surface to form a precursor film of nitrogen molecules on the glass surface.
In various embodiments, the solid electrolyte interphase comprises Li3N.
In various embodiments, a method of making a lithium metal layer having a substantially unpassivated first major surface, and preferably a pristine surface, includes extruding lithium metal directly into a liquid phase of protective fluid (e.g., super dry liquid hydrocarbon).
In various embodiments, a method of making a lithium metal layer having a substantially unpassivated first major surface, and preferably a pristine surface, includes extruding lithium metal and substantially immediately covering the freshly formed lithium metal surfaces with a liquid phase protective fluid.
In various embodiments, the extrusion comprises at least two extrusions performed by roll reduction, and the as-extruded lithium metal layers are substantially immediately covered in liquid phase protective fluid right after each roll reduction step, and maintained under liquid phase protective fluid throughout the process.
In various embodiments, the lithium metal layer is in the form of a long continuous roll, and the method further comprises the step of placing the lithium metal roll into a hermetic canister filled with liquid phase protective fluid, the lithium metal layer completely immersed within the protective fluid.
In various embodiments, the substantially unpassivated first major surface of the lithium metal layer has never been in direct touching contact with a gas phase atmosphere or vacuum.
In various embodiments, a lithium metal laminate structure is provided. The laminate includes:
In various embodiments, the substantially unpassivated lithium metal surface is stable.
In various embodiments, the protective material layer is an liquid phase hydrocarbon liquid, preferably super dry.
In various embodiments, an inorganic solid electrolyte laminate structure is provided. The laminate includes:
In various embodiments, the protective material layer is a liquid phase hydrocarbon liquid, preferably super dry.
In various embodiments, a method for storing a solid-state laminate electrode assembly is provided. The method includes making a solid-state laminate electrode assembly as described herein, and immersing the laminate electrode assembly into a bath of a liquid phase protective fluid (e.g., a super dry liquid hydrocarbon).
In various embodiments, a method for storing a lithium metal layer having a substantially unpassivated first major surface is provided. The method includes making the substantially unpassivated first major surface, and immersing the lithium metal layer into a bath of a liquid phase protective fluid (e.g., a super dry liquid hydrocarbon).
In various embodiments, a method for storing a sulfide glass layer having a clean first major surface is provided. The method includes cleaning the first major surface in an argon plasma, and immersing the sulfide glass layer into a bath of a liquid phase protective fluid (e.g., a super dry liquid hydrocarbon).
In various embodiments, a method for making a battery cell is provided. The method includes making a solid-state electrode assembly as described herein, and placing a positive electrode layer adjacent to the second surface of the sulfide glass layer.
These and other aspects of the present disclosure are described in further detail below, including with reference to the drawings.
Reference will now be made in detail to specific embodiments of this disclosure. Examples of the specific embodiments are illustrated in the accompanying drawings. While this disclosure will be described in conjunction with these specific embodiments, it will be understood that it is not intended to limit this disclosure to such specific embodiments. On the contrary, it is intended to cover alternatives, modifications, and equivalents as may be included within the spirit and scope of this disclosure. In the following description, numerous specific details are set forth in order to provide a thorough understanding of this disclosure. This disclosure may be practiced without some or all of these specific details. In other instances, well known process operations have not been described in detail in order to not unnecessarily obscure this disclosure.
The present disclosure describes solid-state laminate electrode assemblies and various methods for making the solid-state laminate electrode assemblies.
In various embodiments the solid-state laminate electrode assembly comprises a lithium metal layer reactively bonded to a lithium ion conducting sulfide glass layer. Preferably, the reactive bond is sufficiently complete that it forms a continuous solid electrolyte interphase (SEI) at the boundary between the layers.
In various embodiments, to bring about a continuous SEI, the lithium metal layer should have a major surface, which, just prior to bonding (e.g., by laminating), is in a highly reactive state (i.e., it is substantially unpassivated). In various embodiments the method involves making a pristine lithium metal layer having a substantially unpassivated first major surface, and therefore highly reactive, and maintaining the highly reactive surface in its substantially unpassivated state until it has been reactively bonded with the sulfide glass layer.
In various embodiments, the present disclosure provides methods for making a solid-state laminate electrode assembly. Such a method includes:
In various embodiments the reactive bonding step is a lamination process performed in a chamber filled with a dry gas (e.g., dry argon). Typically the laminating step involves applying both heat and pressure.
In various embodiments the inert protective material layer removably covering one or both of the sulfide glass first major surface and the substantially unpassivated lithium metal surface is a liquid phase protective fluid.
In various embodiments the liquid phase protective fluid removably covering the lithium metal surface is removed just prior to the reactive bonding step (e.g., the period of time between removing the liquid phase protective fluid and reactive bonding is less than 10 seconds, and preferably less than 5 seconds, and even more preferably less than 2 seconds).
In various embodiments to ensure that the interface formed between the lithium metal layer and the lithium ion conducting sulfide glass is electrochemically operable or otherwise optimized, an SEI may be engineered by coating a first major surface of the sulfide glass with a thin precursor film that reacts with lithium metal during the bonding step to form a solid electrolyte interphase.
In some embodiments the sulfide glass surface may be treated under a nitrogen containing plasma to incorporate nitrogen into the surface of the glass, and then forming a lithium nitride.
In various embodiments the method further comprises the step of cleaning the first major surface of the sulfide glass under an argon plasma, by ion etching, this step performed after removing the inert protective material layer from of the sulfide glass but before reactive bonding.
In various embodiments the method further comprises the step of treating the clean sulfide glass first major surface to modify its surface composition. In various embodiments the surface composition is modified by placing the clean first major surface of the sulfide glass under a nitrogen containing plasma, wherein the treatment modifies the surface composition of the sulfide glass by introducing nitrogen into/onto the surface.
In various embodiments the method further comprises the step of coating the clean sulfide glass first major surface with a thin precursor film having a composition that will react in direct contact with lithium metal.
In various embodiments the thin precursor film is formed by condensing between 1 to 5 monolayers of a halogen (e.g., iodine) or interhalogen or nitrogen onto the clean sulfide glass surface; wherein the iodine monolayers leads to reactive wetting during the reactive bonding step.
In various embodiments the method further comprises coating the clean sulfide glass surface to form a precursor film that reacts with lithium during the reactive bonding step to form a solid electrolyte interphase between the lithium metal layer and sulfide glass layer.
In various embodiments the inert protective material layer removably covering one or both of the sulfide glass first major surface and the substantially unpassivated lithium metal surface is a liquid phase protective fluid.
In one aspect the present disclosure provides methods for making a pristine lithium metal layer having a substantially unpassivated first major surface, as defined herein below. In various embodiments the opposing second major surface of the pristine lithium metal layer is adhered to a current collector (e.g., a copper foil)
In various embodiments the pristine lithium metal layer is in the form of a long continuous roll of lithium that is immersed in liquid phase protective fluid for storage and/or downstream processing of battery cells (e.g., the pristine lithium metal layer at least 100 cm in length).
In various embodiments the method involves making the pristine lithium metal layer in a protective inert fluid, and maintaining the pristine lithium metal layer in protective fluid (e.g., protective liquid) to prevent directly exposing the surface to the ambient gaseous atmosphere (including dry argon of a glove box or dry Air of a dry room). In various embodiments the protective fluid is an inert liquid or the vapor of an inert liquid (i.e., protective vapor). In various embodiments the lithium metal layer is in the form of a long continuous ribbon (e.g., more than 50 cm in length).
In various embodiments the method for making the substantially unpassivated lithium metal surface includes an extrusion step that produces a fresh substantially unpassivated lithium first major surface inside or surrounded by protective fluid (e.g., a protective and super dry liquid hydrocarbon). By use of the term super dry it is meant that the amount of moisture in the liquid hydrocarbon is not greater than 0.1 ppm. In various embodiments the pristine lithium metal layer and its substantially unpassivated surface is extruded directly into liquid phase protective fluid (i.e., protective liquid), and then optionally the method further includes winding the lithium metal layer into a long continuous roll while it is immersed in liquid phase protective fluid.
In various embodiments the extrusion step is die extrusion of lithium ingot directly into a super dry liquid hydrocarbon bath. In various embodiments the extrusion step is a roller extrusion wherein the lithium metal foil thickness is roll reduced in protective liquid, and in the process forms fresh lithium substantially unpassivated lithium metal surfaces, wherein the area of the fresh surfaces so formed is proportional to the reduction in thickness of the lithium layer. In various embodiments multiple roll reduction steps are performed (e.g., 2, 3, 4 or 5 or more) in order to produce the desired thickness and to perfect the substantially unpassivated surface (e.g., a pristine surface). In various embodiments, the stock foil used for the roll reduction process has been pre-passivated, to improve reproducibility of the starting surface condition. In a particular embodiment a lithium ingot is die extruded directly into protective fluid to form a pristine lithium metal layer, and then that layer is immediately roll reduced in protective fluid to the desired thickness, and throughout the process the substantially unpassivated lithium metal surface remains covered or immersed in liquid phase protective fluid. The pristine lithium metal as formed may then be wound into a long continuous roll of pristine lithium metal, the winding performed in protective fluid (e.g., the winding performed inside liquid phase protective fluid).
In various embodiments the substantially unpassivated lithium metal surfaces are stored in a canister of protective liquid, or they are formed and immediately transferred into the canister, without exposing the surfaces to the ambient gaseous environment.
In another aspect the present disclosure provides a standalone electrochemical material laminate structure for maintaining a major surface of a battery active material layer in a substantially unpassivated and/or substantially uncontaminated condition during handling, storage and/or battery cell fabrication.
In various embodiments the battery active material layer reacts with water and/or oxygen, and even under fairly dry ambient conditions, such as that of a dry air room or a dry argon filled glove box the battery material surfaces chemically degrade or passivate rather quickly. The laminate structures of the present disclosure protect the battery material surfaces by encapsulating them underneath an inert removable layer, which inhibits moisture and/or oxygen from reaching the surfaces.
Accordingly, the standalone electrochemical material laminate structures of the present disclosure are particularly useful for making, storing and transporting moisture sensitive battery active material layers, and for making downstream battery cells and laminate electrode assemblies from those material layers.
In accordance with the present disclosure, a standalone electrochemical material laminate structure may be composed of two or more continuous material layers, wherein at least one of the material layers (i.e., a first material layer) is a “battery active solid material” having a clean (i.e., substantially uncontaminated) and/or substantially unpassivated surface, and another material layer (i.e., a second material layer) is a “protective material” that is inert, not battery active, and removably covers, in direct contact, a first major surface of the battery active material.
When referring to a material as “battery active” it generally means that the material is active in an electrochemical sense and useful in a battery cell (i.e., it is either an electro-active material or an electrolyte material). As used herein, the term “battery active solid material layer” means either a solid alkali metal or an inorganic solid electrolyte having utility as a continuous solid layer in a battery cell (e.g., a lithium metal layer or a Li-ion conducting sulfide glass sheet, respectively).
In contrast to the battery active material layer, the protective material layer is inert and not battery active. By use of the term “inert” it means that the referenced inert material does not chemically react in contact with the battery active solid material on which it is intended to protect. And when referring to the protective material layer as “not battery active,” it is meant that the material layer is not useful in a battery cell, and is furthermore not intended for use in a battery cell, and not active in a battery/electrochemical sense (i.e., not an electroactive material or alkali metal ion conductor).
In accordance with the present disclosure the protective material layer: i) provides an encapsulating barrier against direct touching exposure between the first major surface of the battery active material layer and the ambient gaseous atmosphere or contaminants in a vacuum chamber about the layer; ii) is inert in direct contact with the first major surface; and iii) is readily removed without physically damaging the surface. To achieve these objectives, in various embodiments the protective material layer is an inert liquid (e.g., a super dry hydrocarbon liquid) that encapsulates the surface on which it is applied, and may be evaporatively removed in the absence of solid to solid touching contact
In a first embodiment, the battery active material layer is an electroactive alkali metal layer having a substantially unpassivated first major surface (e.g., a pristine lithium metal layer), and in such embodiments the standalone electrochemical material laminate structure is generally referred to herein as a standalone alkali metal laminate structure; e.g., a standalone lithium metal laminate structure.
In a second embodiment, the battery active material layer is an inorganic solid electrolyte layer having a substantially uncontaminated first major surface (e.g., a lithium ion conducting sulfide glass sheet), and in such embodiments the standalone electrochemical material laminate structure is generally referred to herein as a standalone solid electrolyte laminate structure; e.g., a standalone sulfide glass laminate structure.
By use of the term “standalone” when referring to an electrochemical material laminate structure, such as a standalone alkali metal laminate structure or a standalone solid electrolyte laminate structure, it is meant to emphasis that the battery active material layer in the standalone laminate is a discrete battery active material layer that has not yet been combined or coupled with a second battery active material layer, or yet been placed in a battery cell.
In another aspect the present disclosure provides methods for making lithium metal layers having substantially unpassivated surfaces and preventing passivation by encapsulating them with inert liquid. In various embodiments the methods include making a lithium metal foil having substantially unpassivated surfaces by die extruding a lithium ingot into a bath of super dry liquid hydrocarbons. In various embodiments the as made substantially unpassivated lithium metal foil may be further reduced in thickness by roller reduction and applying hydrocarbon liquid onto the freshly formed surfaces to ensure that they remain substantially unpassivated. In various embodiments a pre-passivated lithium metal layer of thickness (t) may be roller reduced in a roller mill using multiple roll reduction steps while at all times maintaining liquid hydrocarbon on the freshly formed lithium metal layer surfaces. By using pre-passivated lithium metal (e.g., passivated by exposure to CO2), reproducibility is unproved because the initial surface condition of the lithium is itself reproducible, as opposed to using lithium metal that is passivated in a less or uncontrolled fashion. Moreover, the area of freshly formed lithium is proportional to the decrease in thickness of the layer.
In another aspect the present disclosure provides methods for making inorganic lithium ion conducting sulfide glass sheets having substantially uncontaminated surfaces, and for preventing hydrolysis of those surfaces by encapsulating them underneath an inert super dry hydrocarbon fluid (e.g., liquid). For instance, in various embodiments the inorganic sulfide glass sheets are cleaned by ion etching in an Ar plasma to etch away any contaminated surface(s), and then substantially immediately after the ion etching step, the cleaned sulfide glass sheet may be immersed in a liquid hydrocarbon bath, or the clean surface encapsulated by a protective liquid layer, as described above. In various embodiments, the surface composition of the sulfide glass may be modified during or immediately after cleaning by using an argon/nitrogen plasma mixture for incorporating nitrogen into the surface of the sulfide glass sheet, or the surfaces may be treated sequentially, using a first ion etch in argon plasma, followed by a second treatment in a nitrogen containing plasma (e.g., pure nitrogen or an argon/nitrogen mixture).
In yet another aspect the present disclosure provides methods of making a strongly adhered fully solid-state inorganic laminate electrode assembly having a substantially contaminate free inorganic interface. In various embodiments the method includes providing a first battery active material as a component of a lithium metal laminate structure (e.g., a lithium metal layer having a first major surface which is substantially unpassivated and protected by an inert hydrocarbon liquid layer); providing a second battery active material layer as a component of an inorganic solid electrolyte laminate structure (e.g., a lithium ion conducting sulfide glass sheet having a clean first major surface that is devoid of hydrolysis reaction products and protected by an inert hydrocarbon liquid layer); removing the inert hydrocarbon liquid layers; and then, substantially immediately thereafter, reactively bonding the substantially unpassivated lithium metal surface to the clean inorganic sulfide glass surface, to form a strongly adhered laminate having a clean inorganic interface with a low area resistance (preferably, less than 50Ω-cm2). Preferably the peel strength of the laminate electrode assembly is greater than the tensile strength of its lithium metal layer, such that any attempt to peel off the lithium from the laminate results in the lithium tearing prior to peeling.
In various embodiments, an improved laminate interface is formed by laminating the fluid protected lithium metal surface to a solid electrolyte sheet using techniques whereby the fluid is removed substantially immediately prior to, or during, the laminating step, as the solid electrolyte comes into direct contact with the fluid and the lithium metal layer. In various embodiments, the laminating step effects a three phase boundary of lithium metal layer, solid electrolyte, and protective fluid, and causes the fluid to be removed from the surface substantially instantaneously as the solid electrolyte layer reactively adheres to the pristine lithium metal layer surface.
In another aspect, the present disclosure relates to methods and reagents to form a thin, dense and lithium ion conductive layer between a lithium metal layer and an inorganic solid electrolyte layer (e.g., a lithium ion conducting sulfide glass). The layer is sometimes referred to herein as a solid electrolyte interphase (SEI) as it is formed by reacting a first major surface of the lithium metal layer with a coating on the glass surface that allows for the glass electrolyte to be optimized for high ionic conductivity and processability, regardless of its chemical compatibility with lithium metal.
In another aspect the present disclosure provides methods of making battery cells by combining the fully solid-state inorganic laminate electrode assembly of the present disclosure with a positive electrode (e.g., a lithium ion intercalating positive electrode).
A list of suitable hydrocarbons which may be used as protective fluid (e.g., inert liquid) in accordance with the various embodiments and aspects of the present disclosure is provided below, as well as their structural formulas and vapor pressure (and/or boiling point) values. In various embodiments, the protective fluid is selected from a group of saturated hydrocarbons with the number of carbon atoms from 5 to 15. In one particular case, the protective fluid is isododecane. The protective fluids may be a combination of these various fluids. The fluids generally contain no dissolved or dispersed chemicals (e.g., salts, lubricants and/or greases) that would coat the surface of the lithium metal layer or solid electrolyte layer with a solid film or residue. Accordingly the protective fluid is devoid of any dissolved salts (e.g., lithium salts).
Suitable protective fluids are chemically inert to Li metal or Li alloys and contain less than 0.1 ppm of moisture, less than 1 ppm of moisture, less than 5 ppm of moisture, less than 10 ppm of moisture. In the case when a protective fluid is used in combination with a glass coating designed to form a solid electrolyte interphase (SEI) upon contact with Li, the protective fluid is chosen to be non-reactive with the glass coating.
Protective Fluids
Saturated Hydrocarbons (Alkanes) CnH2n+2
Straight-Chain Alkanes C5-C15
n-Pentane C5H12 BP=36° C., Vapor Pressure: 434 mmHg at 20° C.
n-Hexane C6H14 HP=69° C., Vapor Pressure: 121 mmHg at 20° C.
n-Heptane C7H16 BP=99° C., Vapor Pressure: 46 mmHg at 20° C.
n-Octane C8H18 R BP=125° C., Vapor Pressure: 11 mmHg at 20° C.
n-Nonane C9H20 BP=151° C., Vapor Pressure: 3 8 mmHg at 25° C.
n-Decane C10H22 BP=174° C., Vapor Pressure: 2.7 mmHg at 20° C.
n-Undecane C11H24 BP=196° C., Vapor Pressure: 0.4 mmHg at 25° C.
n-Dodecane C12H26 BP=216° C., Vapor Pressure: 0.14 mmHg at 25° C.
Branched-Chain Alkanes C5-C15
Isopentane C5H12 BP=28° C., Vapor Pressure: 577 mmHg at 20° C.
Isohexane C6H14 BP=61° C., Vapor Pressure: 172 mmHg at 20° C.
Isohentane C7H16 BP=90° C., Vapor Pressure: 66 mmHg at 20° C.
Isooctane C8H18 BP=99° C., Vapor Pressure: 41 mmHg at 21° C.
Tetraethylmethane C9H20 BP=146° C., Vapor Pressure: 7.3 mmHg at 25° C.
Isodecane C10H22 BP=167° C., Vapor Pressure: 2.3 mmHg at 25° C.
3-Methyldecane C11H24 BP=188° C., Vapor Pressure: N/A
Isododecane C12H26 BP=180° C., Vapor Pressure: 0.301 mmHg at 20° C.
Cycloalkanes C6-C8 CnH2n
Cyclohexane C6H12 BP=81° C., Vapor Pressure: 78 mmHg at 20° C.
Cycloheptane C7H14 BP=118° C., Vapor Pressure: 22 mmHg at 20° C.
Cyclooctane C8H16 BP=149° C., Vapor Pressure: 16 mmHg at 37.7° C.
CnH2(n−m−1),
n=number of carbon atoms
m=number of double bonds
Alkenes C6-C11, CnH2n
1-Hexene C6H12 BP=64° C., Vapor Pressure: 155 mmHg at 21° C.
1-Heptene C7H14 BP=94° C., Vapor Pressure: 101 mmHg at 37.7° C.
1-Octene C8H16 BP=122° C., Vapor Pressure: 36 mmHg at 37.7° C.
1-Nonene C9H18 BP=146° C., Vapor Pressure: 11 mmHg at 37.7° C.
1-Docene C10H20 BP=172° C., Vapor Pressure: 1.67 mmHg at 25° C.
1-Undecene C11H22 BP=192° C. Vapor Pressure: N/A
1-Dodecene C12H24 BP=214° C., Vapor Pressure: N/A
Alkadienes: C6-C12 CnH2n−2
1,5-Hexadiene C6H10 BP=60° Vapor Pressure: 367 mmHg at 37.7° C.
2,4-Hexadiene C6H10 BP=82° C. Vapor Pressure: N/A
1,6-Heptadiene C7H12 BP=90° C., Vapor Pressure: N/A
1,7-Octadiene C8H14 BP=118° C., Vapor Pressure: 19 mmHg at 25° C.
1,8-Nonadiene C9H16 BP=141° C., Vapor Pressure: 7 mmHg at 25° C.
1,9-Decadiene C10H18 BP=169° C., Vapor Pressure: 4 mmHg at 20° C.
1,10-Undecadiene C11H20 BP=187° C., Vapor Pressure: N/A
1,11-Dodecadiene C12H22 BP=207° C., Vapor Pressure: N/A
CnH2(n−m),
n=number of carbon atoms
m=number of double bonds
Cycloalkenes C6-C8, CnH2n−2
Cyclohexene C6H10 BP=83° C., Vapor Pressure: 160 mmHg at 20° C.
Cycloheptene C7H12 BP=113° C., Vapor Pressure: 22 mmHg at 20° C.
Cyclooctene C8H14 BP=145° C., Vapor Pressure: N/A
Cycloalkadienes C6-C8, CnH2n−4
1.3-Cyclohexadiene C6H8 BP=80° C., Vapor Pressure: 56 mmHg at 25° C.
1,4-Cyclohexadiene C6H8 BP=88° C., Vapor Pressure: N/A
1.3-Cycloheptadiene C7H12 BP=120° C., Vapor Pressure: N/A
1,3-Cyclooctadiene C8H14 BP=143° C., Vapor Pressure: 13.4 mmHg at 25° C.
Generally, the protective inert liquid layer is devoid of dissolved and/or dispersed chemicals (e.g., salts, lubricants and/or greases) that would coat the surface of the battery active material layer with a solid film or leave behind a sticky residue. Accordingly, the protective inert liquid layer is generally devoid of dissolved salts (e.g., lithium salts, or more generally alkali metal salts).
In order to be inert in direct contact with the battery active material layer, the liquid hydrocarbon(s) should have a very low concentration of moisture. Preferably the concentration of moisture in the inert liquid hydrocarbon layer is less than 10 ppm of water, more preferably less than 5 ppm of water, even more preferably less than 1 ppm of water, and yet even more preferably less than 0.1 ppm of water (i.e., super dry). In various embodiments the inert liquid is actively dried in the presence of sacrificial alkali metal surfaces (e.g., pieces/chips of lithium or sodium metal) that getter oxygen, water and nitrogen impurities. Moreover, the liquid hydrocarbons may be passed through a drying a chamber in order to maintain very low moisture levels. The drying chamber may contain drying agents and oxygen getters. Examples of drying agents for liquid hydrocarbons include molecular sieves (3A, 4A, or 5A depending on the hydrocarbon type), magnesium oxide, zinc chloride, calcium sulfate, calcium chloride, calcium hydride, and alumina (neutral or basic). In various embodiments, the cumulative area of the sacrificial alkali metal surfaces in direct contact with the inert liquid is greater than the first major surface of the battery active material layer on which the inert liquid covers in direct contact, for instance when the battery active material layer is disposed in a protective liquid bath, as described in more detail herein below.
In one aspect the present disclosure provides methods for making a solid-state laminate electrode assembly. In various embodiments, the solid-state laminate electrode assembly is a lithium metal layer reactively bonded with a lithium ion conducting sulfide glass layer.
With reference to
The process includes initial steps 10 and 20, for making or providing a first and a second standalone electrochemical material laminate structure, respectively. Notably, first and second electrochemical material laminate structures are not the same.
As used herein, the term electrochemical material laminate structure means a laminate of two or more continuous material layers, wherein at least one of the material layers (i.e., a first material layer) is a “battery active solid material layer” having a clean (i.e., substantially uncontaminated) and/or substantially unpassivated first major surface, and another material layer (i.e., a second material layer) is a “protective material layer” that is inert, not battery active, and removably covers, in direct intimate contact, the first major surface of the battery active material layer. In various embodiments the protective material layer is a liquid phase layer of a protective fluid, such as a super dry hydrocarbon liquid that is spread out evenly over the first major surface of the battery active material layer.
Generally, the battery active material layer is highly reactive with water and/or oxygen, and its surfaces chemically degrade or passivate rather quickly, even under dry or vacuum conditions, including that of a dry air room suited for handling lithium metal (e.g., having a dew point between −20 to −40° C.) or a dry argon filled glove box (e.g., having a low moisture and oxygen content of between 1 to 5 ppm). Accordingly, the electrochemical laminate structure is used to shield a battery active material layer against adverse reactions with the environment in which the battery active material layer is made, processed and/or stored. And by the term “solid battery active material layer” it is meant either a solid alkali metal layer (e.g., typically embodied herein as a lithium metal layer) or an inorganic solid electrolyte layer (e.g., typically embodied herein as a lithium ion conducting sulfide glass). When the battery active material layer is a lithium metal layer, the laminate structure is referred to generally as an alkali metal laminate structure (or more specifically in this case as a lithium metal laminate structure), and when the battery active material layer is an inorganic lithium ion conducting sulfide glass, the laminate structure is referred generally as a solid electrolyte laminate structure (or more specifically in this case as a sulfide glass laminate structure). Furthermore, by use of the term “standalone” when referring to an electrochemical material laminate structure, such as a standalone alkali metal laminate structure or a standalone solid electrolyte laminate structure, it is meant to emphasis that the battery active material layer in the standalone laminate is a discrete battery active material layer that has not yet been combined or coupled with a second battery active material layer, or yet been placed in a battery cell. For instance, when standalone lithium laminate structures are absent of an electrolyte and standalone sulfide glass solid electrolyte laminate structures are absent of battery electroactive materials.
Continuing with reference to
Once the protective material layer has been removed, it is important to minimize any exposure to gaseous or vacuum environments in order to maintain the respective battery active material layer surfaces clean and unpassivated. Accordingly, in some embodiments the chamber or conduit through which the battery active material layers are translated may be filled with vapor phase protective fluid right up until the layers are combined for lamination, according to process step 30, wherein the layers are reactively bonded to each other.
In various embodiments, once the liquid phase layer of protective fluid has been removed from the surface of the sulfide glass, the glass first major surface may be processed and/or treated prior to laminating with lithium metal in order to engineer a solid electrolyte interphase (SEI) with improved electrochemical properties, or when the sulfide glass is not chemically compatible with lithium metal. As described in more detail herein below, the sulfide glass may undergo a cleaning process 24A, exemplified by an ion etch treatment under an Ar plasma followed by a surface treating process 24B, wherein the cleaned glass surface may be coated with a thin lithium metal reactive precursor film or treated to modify the surface composition of the glass (e.g., by placing the glass first major surface under a nitrogen containing plasma).
The material laminate structures, methods and processes briefly described above with reference to process flow diagram in
In one aspect the present disclosure provides a standalone electrochemical material laminate structure for maintaining a major surface of a battery active material layer in a substantially unpassivated and/or substantially uncontaminated condition during storage and/or battery cell component fabrication (e.g., fabrication of a fully solid-state laminate electrode assembly).
In accordance with the present disclosure, the standalone electrochemical material laminate structure is composed of two or more continuous material layers, wherein at least one of the material layers (i.e., a first material layer) is a “battery active solid material layer” having a clean (i.e., substantially uncontaminated) and/or substantially unpassivated first major surface, and another material layer (i.e., a second material layer) is a “protective material layer” that is inert, not battery active, and removably covers, in direct contact, the first major surface of the battery active material layer.
In various embodiments the battery active material layer is highly reactive with water and/or oxygen, and its surfaces will chemically degrade or passivate rather quickly, even under fairly dry conditions of a dry Air room (e.g., having a dew point of −20° C.) or a dry argon filled glove box (e.g., having a low moisture and oxygen content of between 1 to 5 ppm).
In accordance with the present disclosure the protective material layer: i) minimizes, and preferably prevents, direct touching exposure between the first major surface of the battery active material layer and the ambient gaseous atmosphere or vacuum environment about the layer (e.g., during handling, processing and/or storage); ii) is inert in direct contact with the first major surface; and iii) is readily removed without physically damaging the surface. Accordingly, in various embodiments the protective material layer is an inert liquid (e.g., a super dry hydrocarbon liquid) that encapsulates the surface on which it is applied, and may be evaporatively removed in the absence of solid to solid touching contact.
In a first inventive embodiment, the battery active material layer is an electroactive alkali metal layer having a substantially unpassivated first major surface (e.g., a pristine lithium metal layer), and in such embodiments the standalone electrochemical material laminate structure is generally referred to herein as a standalone alkali metal laminate structure; e.g., a standalone lithium metal laminate structure. Preferably, the first major surface is pristine.
In a second inventive embodiment, the battery active material layer is an inorganic solid electrolyte layer (e.g., a lithium ion conducting sulfide glass sheet), and in such embodiments the standalone electrochemical material laminate structure is generally referred to herein as a standalone solid electrolyte laminate structure; e.g., a standalone sulfide glass laminate structure. In various embodiments the sulfide glass layer has a first major surface that is clean (i.e., substantially uncontaminated).
The standalone electrochemical material laminate structure of the present disclosure can be constructed using a number of different architectures, some of which are described in more detail herein below
With reference to
With reference to
With reference to
With reference to
Preferably, the inert liquid of layer 102/202 completely wets out surface 101i/201i as well as the surface of release layer 104/204, and this leads to the formation of a liquid bridge between the layers and an associated wet adhesive force that assists in maintaining the release layer on the battery active material during handling and processing. The degree of wettability may be determined by the contact angle (θ). Accordingly, in various embodiments one criterion that may be used for selecting the protective liquid is based, in part, on its ability to fully wet out the battery active material surface on which it is disposed. To effect wetting the contact angle that the liquid makes with the solid surface should be in the range of 0°≥θ<90°, and preferably θ is near 0° for complete wet out (ε.γ., θ=0°). Preferably the ability of the inert liquid to wet out both surface 101i/201i and layer 104/204 is sufficient to spread the inert liquid layer evenly and intimately over surface 101i/201i, to encapsulate it (the first major surfaces) and prevent the solid release layer from touching the battery active material. Preferably, inert liquid layer 102/202 is thin enough to bring about a tight liquid bridge that is capable of maintaining the solid release on the battery active material during handling and processing.
Continuing with reference to
The wet decal architecture, as described above, has a number of advantages, including: i) protecting surface 101i/102i against physical damage during handling; ii) enhancing the utility and/or the ability to use medium to high vapor pressure inert liquids by lessening their effective evaporation rate; iii) improving protection against degradation of surface 101i/201i against impurity molecules from the ambient atmosphere, as the release layer itself provides an additional barrier against contaminating molecules entering the protective liquid from the ambient atmosphere; iv) extending storage shelf life and service lifetimes due to the additional barrier properties and lower evaporation rate of the inert liquid layer; and finally v) the solid release layer may serve as an interleave for winding or stacking the laminate structures.
With reference to
In various embodiments the laminate thickness, as measured from the second major surface of the battery active material layer 101ii/201ii to the top surface of inert liquid layer 102/202 is no greater than lmm thick, and more typically no greater than 500 um thick. For instance, in various embodiments the laminate thickness (as defined above) is less than 500 um, and typically less than 200 um, and in some embodiments less than 100 um, or less than 50 um (e.g., between 5-100 um). The laminate thickness, as defined above, does not include the thickness of the solid release layer, or backing layer when present.
In accordance with the present disclosure one function of protective material layer 102/202 (e.g., inert liquid layer) is to removably cover and protect (e.g., encapsulate) at least the first major surface of the battery active material layer, and thereon provide a degree of protection against facile degradation caused by direct exposure of the lithium metal layer or sulfide glass layer to ambient gaseous atmospheres during handling, processing anollor storage. By use of the term “removably cover and protect” when describing the protective inert liquid layer it is meant that the layer: i) covers the first surface of the battery active material in a manner that sufficiently protects the surface against chemical attack; ii) remains on the first surface during handling and storage; and iii) can be controllably removed without damaging the battery active material layer. By use of the term “controllably remove” or “controllably removed” when referring to the protective material layer it is meant that the laminate structure is engineered to facilitate removal of the protective material layer in a controlled fashion, and is otherwise not easily removed (e.g., by happenstance, such as incidental evaporation during handling and processing of downstream components). Accordingly, the chemical make-up and physical properties of the protective material layer is properly selected to enable its controlled removal without damaging the battery active material layer, and the laminate structure engineered to ensure that the inert material layer stays intact as a protective layer for the desired time frame.
In various embodiments protective material layer 102/202 is an inert liquid that intimately covers and spans substantially the first major surface of the battery active material layer (i.e., it is a continuous inert liquid layer). Accordingly, in various embodiments the composition of the inert liquid is selected, in part, based on it having a lower surface energy than the battery active material layer surface, and therefore capable of wetting out the battery active first major surface, and, thus, intimately covering it in direct contact, the liquid flowing and spreading out evenly to span substantially the entire surface (i.e., encapsulate the surface); e.g., encapsulate the first major surface.
Preferably inert liquid layer 102/202 readily wets the first major surface of the battery active material layer. In various embodiments, the wetting angle (θ) that the inert liquid makes in contact with the battery active material layer is less than 90° (e.g., 0≥θ<90°), preferably less than 60°, more preferably less than 30°, even more preferably θ is less than 10°, and yet even more preferably about 0°. Accordingly, in various embodiments, the ability of the inert liquid layer to wet the battery active material layer surface is sufficient to encapsulate the one or more surfaces that it covers in direct contact.
Generally, the thickness of inert liquid layer 102/202 is less than 1 mm. In embodiments the thickness of the continuous inert liquid layer is in the range of 500 to 1000 um; or in the range of 200 to 500 um; or in the range of 100 to 200 um; or in the range of 50 to 100 um; or in the range of 20-50 um; or in the range of 10-20 um or in the range of 5-10 um; or in the range of 1-5 um; or, in some embodiments, it is contemplated that it may be less than 1 um.
In various embodiments, in order to retain inert liquid layer 102/202 on surface of the battery active material layer during handling and processing, and controllably remove it (the inert liquid layer) without imparting damage or leaving behind a chemical residue, the inert liquid is selected based on a combination of its vapor pressure and boiling point.
In various embodiments, in order to mitigate uncontrolled evaporation of inert liquid layer 102/202, while facilitating its controlled removal, the inert liquid of the protective material layer (i.e., the inert liquid layer) is selected, in part, based on having a room temperature vapor pressure in the range of 0.1-10 mmHg (e.g., 0.1-1 mmHg), and/or based, in part, on having a boiling temperature in the range of 100-200° C.
In various embodiments, the inert liquid of protective material layer 102/202 is selected based on having a sufficiently low vapor pressure at room temperature (e.g., less than 10 mmHg, or less than 1 mmHg).
In various embodiments, the inert liquid of protective material layer 102/202 is selected based on having a sufficiently high boiling point temperature (e.g., greater than 100° C., or greater than 150° C. or greater than 200° C.).
In various embodiments the inert liquid of protective material layer 102/202 is selected based on having a room temperature vapor pressure that is less than 10 mmHg and a boiling point temperature greater than 100° C.
In various embodiments protective material layer 102/202 is composed of one or more inert hydrocarbon liquids (e.g., isododecane). Particularly suitable hydrocarbon liquids for use as a protective material layer are saturated hydrocarbons (e.g., having a number of carbon atoms per molecule ranging from 5 to 15).
In various embodiments the inert hydrocarbon liquid is a saturated hydrocarbon liquid.
In some embodiments the protective inert liquid saturated hydrocarbon is a straight chain alkane (typically having between 5 and 15 carbon atoms per molecule), such as n-pentane, n-hexane, n-heptane, n-octane, n-nonane, n-decane, n-undecane, n-dodecane.
In some embodiments the protective inert liquid saturated hydrocarbon is a branched chain alkane (typically having 5 to 15 carbon atoms per molecules), such as isopentane, isodecane, isoheptane, isooctane, tetraethylmethane, isodecane, 3-methyldecane, isododecane.
In some embodiments the protective inert liquid saturated hydrocarbon is a cycloalkane, such as cyclohexane, and cycloheptane, cyclooctane.
In some embodiments the protective inert liquid hydrocarbon is an unsaturated acyclic hydrocarbon (e.g., CnH2(n−m−1) wherein n is the number of carbon atoms and m is the number of double bonds), such as alkenes (e.g., 1-hexane, 1-octane, 1-nonene, 1-docene, 1-undecene, 1-dodecene, or alkadienes (e.g., 1,5-hexadiene; 2,4-hexadiene; 1,6-heptadiene; 1,7-octadiene; 1,8-nonadiene; 1,9-decadiene; 1,10-undecadiene; and 1,11-dodecadiene.
In various embodiments the inert hydrocarbon liquid is an unsaturated hydrocarbon liquid.
In some embodiments the protective inert liquid is an unsaturated cyclic hydrocarbon (e.g., of the type CnH2(n−m) wherein n is the number of carbon atoms and m is the number of double bonds), such as cyclohexane, cycloheptane, and cyclooctene).
In some embodiments the protective inert liquid is an unsaturated cyclic hydrocarbon (e.g., one or more cycloalkadienes), such as 1,3-cyclohexadiene; 1,4-cyclohexadiene; 1,3-cyclotreptadiene; and 1,3-cyclooctadiene).
Generally, protective inert liquid layer 102/202 is devoid of dissolved and/or dispersed chemicals (e.g., salts, lubricants and/or greases) that would coat the surface of the battery active material layer with a solid film or leave behind a sticky residue. Accordingly, the protective inert liquid layer is generally devoid of dissolved salts (e.g., lithium salts, or more generally alkali metal salts).
In order to be inert in direct contact with the battery active material layer, the liquid hydrocarbon(s), and, more generally, the protective inert liquid layer should have a very low concentration of moisture. Preferably the concentration of moisture in the inert liquid hydrocarbon layer is less than 10 ppm of water, more preferably less than 5 ppm of water, even more preferably less than 1 ppm of water, and yet even more preferably less than 0.1 ppm of water (i.e., super dry). In various embodiments the inert liquid is actively dried in the presence of sacrificial alkali metal surfaces (e.g., pieces/chips of lithium metal) that getter oxygen, water and nitrogen impurities. In various embodiments, the cumulative area of the sacrificial alkali metal surfaces in direct contact with the inert liquid is greater than the first major surface of the battery active material layer on which the inert liquid covers in direct contact, for instance, when the battery active material layer is disposed in a protective liquid bath, as described in more detail herein below.
In accordance with the standalone electrochemical material laminate structure embodiments described with reference to
In various embodiments alkali metal layer 101 is a dense alkali metal layer. In various embodiments it is a lithium metal layer or sodium metal layer. It is also contemplated that the alkali metal layer may be a lithium metal alloy or a sodium metal alloy, which may include one or more of the following alloying elements, including Ca, Mg, Sn, Ag, Zn, Bi, Al, Cd, Ga, In and Sb. In various embodiments alkali metal layer 101 is a lithium metal layer.
In various embodiments thickness of lithium metal layer 101 is typically no greater than 50 microns, and more typically no greater than 25 microns (e.g., 50 μm≥t>30 μm; or 30 μm t≥20 μm; or 20 μm≥t>10 μm; or 10 μm≥t≥5 μm). In some embodiments lithium metal layer 101 is a thin film coating on a current collector having a scant amount of lithium, with thickness no greater than 5 um thick, and typically thinner, such as about 4 μm or about 3 μm or about 2 μm or about 1 μm, or less than 1 μm. (e.g., 5 μm>t≥0.1 μm). For example, the thin film of lithium metal may be coated by evaporation onto a copper current collector in a vacuum chamber, and then prior to backfilling the chamber with a dry inert gas, such as argon or helium, the first major surface of the coated film is immersed in protective liquid or coated with a layer of inert protective liquid.
In accordance with the present disclosure, in various embodiments, lithium metal surface 101i is substantially unpassivated and preferably pristine, as defined herein below. And even more preferably, lithium metal surface 101i is 100% unpassivated. Preferably, lithium metal surface 101i is 100% unpassivated and molecularly or atomically clean.
Continuing with reference to the lithium metal laminate structures described herein above with reference to
By use of the term “pristine surface” with reference to alkali metal layer 101 (e.g., a lithium metal layer), it is meant a substantially unpassivated lithium metal surface that is also sufficiently clean to i) facilitate complete reactive bonding to an opposing solid electrolyte layer, wherein the adherence created by the complete bond is sufficiently strong to prevent mechanical non-destructive release or delamination between the layers; and ii) effectuate a sufficiently uncontaminated interface (with the solid electrolyte layer) that is conductive to Li ions and does not result in a prohibitively large interface resistance (preferably no greater than 50Ω-cm2) between the alkali metal layer (e.g., a lithium metal layer) and the solid electrolyte layer (e.g., a sulfide glass layer).
By “substantially unpassivated” when referring to an alkali metal layer surface (e.g., a lithium metal surface) it is meant that the surface is predominately defined by a continuous unpassivated and substantially unoxidized surface region that accounts for at least 70% of the area of the referenced lithium metal surface (e.g., first major surface 101i). When referring to a lithium metal layer surface as pristine it is meant that the continuous unpassivated and substantially unoxidized surface region accounts for at least 90% of the area of the referenced lithium metal surface, and preferably at least 95%, and even more preferably the pristine surface is entirely unpassivated (i.e., 100% of the surface is unpassivated). In various embodiments, as described in more detail herein below, the substantially unpassivated or pristine surface may contain a certain amount of discrete passivated surface portions (i.e., passivated islands).
By “sufficiently clean” when referring to the pristine lithium metal surface, it is meant that the continuous unpassivated and substantially unoxidized surface region, as described above, is not poisoned by an unduly thick non-self-limiting surface-layer, which, if otherwise present would preclude complete reactive bonding and strong adherence to a reactive solid electrolyte layer (e.g., as defined with respect to peel strength), and would degrade electrochemical interface properties (e.g., as defined by interface resistance, and uneven plating and stripping reactions). Notwithstanding the preference to eliminate any poisoning of the pristine surface, a minimal non-self-limiting surface-layer covering the continuous unpassivated region may be acceptable, as described in more detail herein below.
Top down and cross sectional depictions of alkali metal layers (e.g., lithium metal layers) having pristine surfaces in accordance with various embodiments of the present disclosure are depicted in
Briefly, in
With reference to
With reference to
With reference to
With reference to
With reference to
As described above, the present disclosure provides methods and apparatus' for making lithium metal layers having substantially unpassivated and preferably pristine surfaces, and, in particular, for making lithium metal layers wherein at least one major surface is maintained in its pristine or substantially unpassivated condition under, or immersed in, a protective fluid (e.g., a protective liquid).
With reference to
Apparatus' 400A-D may be divided into two main sections or regions. First section 410i (typically a staging section) is where the initial stock of lithium metal 430 (e.g., an ingot or foil of lithium) is positioned for entry or disposition into second section 410ii (surface generating section), and, in particular, surface forming chatAber 450 wherein lithium layer 101 and/or its pristine first surface 101i (and optionally 101i) are formed in direct contact with protective fluid 402 (e.g., super dry inert hydrocarbon liquid as described above). Chamber 450 includes enclosure 451, and is equipped with surface forming device 452, and interior environmental controls not shown. Once created, as-formed lithium layer 101 may be wound and/or stored in protective liquid of the same or different composition as that in which the layer itself (or at least its first surface) was generated. As shown in
In various embodiments, a lithium decal (as shown in
With reference to
Surface forming device 452 contacts protective liquid 402 such that as lithium metal layer 101 is formed, or surface 101i and/or surface 101i is created, the as-formed surfaces substantially instantaneously become immersed in protective fluid (e.g., inert liquid). Once the layer is formed, the inert liquid is caused to remain on the freshly created lithium layer surfaces (e.g., by using a solid release layer on that surface), typically fully encompassing (i.e., encapsulating) the surface, and thereon protecting it (the pristine surface) from direct contact with lithium reactive constituents that may be present as contaminats in of the ambient environment about the layer. In various embodiments, the protective fluid in which pristine lithium metal surface 101a is formed may be exchanged with protective fluid having a different composition for downstream processing and/or storage. For instance, surface 101i formed in or under a first protective liquid having a first vapor pressure or boiling point and that first inert liquid is replaced by a second inert liquid having a second vapor pressure or boiling point (e.g., the second liquid having a higher vapor pressure and lower boiling point than the first liquid, or vice-versa).
In various embodiments, surface forming device 452 is fully, or at least partially, immersed in protective fluid 402. For instance, active surface forming component 456, may be fully submerged or encompassed inside a bath of protective liquid. To contain protective liquid 102, surface generating section 410ii includes enclosure 451 (e.g., an environmental chamber). In various embodiments, the surface forming device, and in particular its surface forming components, are also housed in the enclosure.
In various embodiments protective fluid 402 is a liquid at room temperature 18° C. to 25° C.) and standard pressure (1 atm), and is primarily contained in the enclosure as a liquid. In various embodiments the interior environment of the enclosure is substantially filled by inert liquid, and as described above, and in more detail herein below, in various embodiments surface forming component 456 is immersed in the inert liquid phase protective fluid, and specficially that portion of the surface forming component which directly contacts lithium metal surface 101i is immersed in the liquid phase. Accordingly, surface 101i, or both surfaces 101i and 101bii, are formed in direct contact with liquid phase protective fluid, and preferably the as-formed surfaces are fully encompassedlencapsulated by the liquid phase, and as such the surfaces are formed in the absence of direct contact with a gaseous phase environment (e.g., dry air or an inert gas phase environment, including one or more noble gases), and thus also not formed in a vacuum environment. For instance, the lithium metal layer and/or its associated surfaces are fully formed immersed in a protective liquid. For example, formed inside a bath of protective liquid or inside a chamber filled with protective vapor of an inert liquid.
As described in more detail herein below, once formed within the protective liquid, lithium metal layer 101, or its first and/or second major surface(s) 101i/101ii are maintained in the protective liquid for subesequent winding to form a roll of lithium metal foil 101-R (typically on a spool) and/or storage. By this expedient, as-formed lithium metal layer 101, and/or surface 101i, or both surfaces 101i and 101ii, have never been exposed to a gaseous phase environment or to a vacuum environment. In such embodiments, the lithium metal foil and its associated pristine surfaces, are formed, and thereafter stored in a pristine state, never exposed in direct contact with a gaseous atmosphere. For example, the foils so formed are maintained pristine during storage inside a bath of protective liquid for more than 24 hours, or more than 1 week, or more than 1 month. The pristine foils may then be sold and/or transported as such to a facility for manufacture of downstream battery cell components, including solid-state electrode laminates and battery cells of the present disclosure. In various embodiments the lithium foils are stored under protective liquid, and are preferably never been exposed in direct contact with gaseous atmospheres, including dry noble gases such as dry argon gas, or dry Helium gas, or some combination thereof, or even dry air (i.e., air having a very low moisture content, such as that typical of a dry room). When rolled with a solid release layer, the release removably covers and protects the substantially unpassivated lithium metal surface 101i, and optionally its opposing surface 101ii, When a solid release is used the inert liquid layer is formed and sandwiched between the solid release layer and the lithium metal laver, and this laminate structure is sometimes referred to herein as a wet-decal architecture, or more simply a wet-decal. Preferably, the inert liquid is capable of wetting out both the lihtium metal surface and the release layer.
In alternative embodiments the interior environment of chamber 450 is primarily composed of protective fluid as a vapor. In such embodiments, the vapor molecules may condense on the as-formed lithium metal surfaces. When a vapor phase protective fluid is used, the enclosure is typically vacuum evacuated, followed by evaporating the protective liquid inside the chamber to form the inert vapor. Notably, when referring to vapor phase protective fluid it is not meant a noble gas such as argon or Helium, or the like. By protective fluid in the vapor phase it is meant vapor of the inert liquid.
With reference to
As-formed, layer 405 is generally substantially upassivated and preferably pristine upon exiting die 444. If formed in direct contact with a gaseous dry room environment the freshly made lithium metal surface would immediately start chemically reacting with the oxygen and carbon dioxide in the dry room, which would passivate the exposed surfaces. With respect to various embodiments of the present disclosure, because layer 405 is formed direcly in protective liquid 102, its major opposing surfaces 105a/105b are fully covered in direct contact with protective liquid 102 substantially immediately upon formation (e.g., in less than one second). In the instant embodiment, thickness of layer 405 is reduced in a subsequent roll reduction step, as shown in section 410ii of
Continuing with reference to
As shown in
As shown in
With reference to
As described above, in various embodiments protective fluid 402 is a liquid. In sonic embodiments the interior environment of the chamber is held under a dynamic vacuum with protective fluid in the vapor phase. In some embodiments the protective fluid is present in the chamber in both the vapor and liquid phases. In some embodiments the chamber is substantially filled with liquid phase protective fluid (e.g., more than 90% of chamber volume is accounted for by protective liquid). Generally the protective fluid is a hydrocarbon composed of one or snore hydrocarbon molecules that do not react in direct contact with lithium atoms.
With reference to
With reference to
With reference to
In accordance with the methods and apparatus' shown in
With reference to
Preferably cartridge 500 is sufficiently hermetic, and the protective liquid sufficiently dry (e.g., super dry), that lithium metal layer 101 is able to maintain its substantially unpassivated or pristine surface condition for at least 60 minutes, or at least 5 hours, or at least 10 hours, or at least 24 hours, or at least several days, weeks, or months (e.g., more than 3 days, more than 7 days, or more than 30 days).
In accordance with the standalone electrochemical material laminate structure embodiments described with reference to
Continuing with reference to
In other embodiments inorganic solid electrolyte layer 201 is a polycrystalline ceramic or a glass-ceramic layer (e.g., a garnet solid electrolyte layer). These include Li6BaLa2Ta2O12; Li7La3Zr2O12, Li5La3Nb2O12, Li5La3M2O12 (M═Nb, Ta)Li7+xAxLa3−xZr2O12 where A may be Zn. These materials and methods for making them are described in U.S. Patent Application Pub. No.: 2007/0148533 (application Ser. No. 10/591,714) and is hereby incorporated by reference in its entirety and suitable garnet like structures, are described in International Patent Application Pub. No.: WO/2009/003695 which is hereby incorporated by reference for all that it contains. Suitable ceramic ion active metal ion conductors are described, for example, in U.S. Pat. No. 4,985,317 to Adachi et al., incorporated by reference herein in its entirety and for all purposes. LiM2(PO4)3 where M may be Ti, Zr, Hf, Ge) and related compositions such as Li those into which certain ion substitutions are made including Li1+xTi2−xAlx(PO4)3 and the like which are known in the lithium battery arts.
Generally, the thickness of the inorganic sold electrolyte layer is in a range that is sensible for use in a battery cell, and generally depends, in part, on its ionic conductivity. In various embodiments the thickness of the solid electrolyte layer is in the range of 200-1 um thick, and more typically in the range of 100-5 μm, and even more typically in the range of 50-10 μm thick (e.g., about 10 μm or about 15 μm or about 20 μm or about 25 μm or about 30 μm or about 35 μm or about 40 μm or about 45 μm or about 50 μm thick).
Solid Electrolyte Interphase (Engineered SEI)
With reference to
In various embodiments the sulfide glass surface 201i is not chemically compatible in contact with lithium metal, and so coatings on the glass surface are described herein which are useful for creating a solid electrolyte interphase (SEI), the SRI forming as result of the coating reacting With the substantially unpassivated lithium metal surface during the step of reactive bonding e.g., during lamination of the layers, typically using heat and pressure).
In various embodiments, after ion etching, sulfide glass layer 201 is translated via the carrier web into surface treating chamber 630. In various embodiments surface treating chamber 630 is a second plasma unit, and glass 201 is subjected to nitrogen plasma and/or a nitrogen/argon plasma mixture, the process cleans the glass and also modifys the glass surface composition by introducing nitrogen into/onto the surface. Thereafter, the glass is wound into roll 610-R and immersed in protective liquid 602, as described above. In alternative embodiments, as opposed to bringing the cleaned and nitrogen treated glass into protective fluid (e.g., liquid or vapor phase), it is stored in a dry oxygen free argon filled enclosure.
Continuing with reference to
In various embodiments the sulfide glass first major surface is treated in chamber 630 to form a thin precursor film that reacts with lithium metal to form an engineered solid electrolyte interphase (SEI). Various processes, reagents and treatments for engineering the SEI are described below.
With reference to
In one embodiment precursor layer 640 is a halogen or interhalogen (diatomic or multi-atomic). For instance a monolayer, or several monolayers (e.g., up to 5 monolayers) of iodine or bromine molecules on the solid electrolyte glass surface is formed by condensation from the gas or liquid phase (e.g., gaseous or liquid phase iodine).
In one embodiment precursor layer is nitrogen. For example, a monolayer or several monolayers (e.g., up to 5 monolayers) of nitrogen molecules on the surface of the solid electrolyte gas is formed by condensation of nitrogen onto the solid electrolyte surface (from a gas or liquid phase). In a particular embodiment the nitrogen coated onto the surface of the solid electrolyte glass via a liquid carrier, such as liquid hydrocarbons, containing dissolved nitrogen molecules. The liquid hydrocarbons should be dry, as defined above, especially if the solid electrolyte is sensitive to moisture. Preferably the solubility of nitrogen in the hydrocarbon is large. For instance, the liquid carrier (e.g., liquid hydrocarbon) having a room temperature solubility of greater than 1 mole (nitrogen molecule) per mole of the liquid hydrocarbon, and preferably a ratio that is greater than 1.1, and even more preferably greater than 1.2. Particularly suitable liquid hydrocarbons include n-Octane, n-Nonane, n-Decane, n-Undecane, and n-Dodecane.
In other embodiments the solid electrolyte surface may be coated with a precursor of SO2 or sulfur molecules, as described in more detail herein below.
While lithium is primarily referenced as the akali metal layer material herein, it should be understood that other alkali metals or alloys of lithium may also be used.
1. Halogens or Interhalogens (Diatomic or Multi-Atomic)
A monolayer, a few layers or condensed films are formed by iodine or bromine molecules on a glass surface from gas phase or from liquid phase. Halogen coating on the glass surface helps to improve wettahility of Li metal towards glass (reactive wetting). In this case, the SEI formed on the clean Li surface consists of LiHal, in particular LiI or LiBr.
In order to minimize the coating thickness the source of iodine or bromine vapor is not a molecular halogen, but a halogen-containing compound having a lower halogen vapor pressure. The coating thickness can be optimized by using halogen-containing compounds with appropriate vapor pressure and by adjusting duration and temperature of the coating process. Among the compounds that are used as sources of halogen vapor are solid polyhalogens. Solid polyiodides with various cations described in (Per H. Svensson, Lars Kloo, Chemical Reviews, 2003, Vol. 103, No. 5) can be used as iodine sources (these compositions are incorporated by reference herein). Applicable polyhalogens include quaternary ammonium-polyhalogen compounds, in particular, tetraalkylammonium polyhalogens, inorganic polyiodides, such as RhI3 CsI3 and Cu—(NH3)4]I4, charge transfer complexes between dioxane, pyridine, polyvinyl, pyrrolidone, polyethyleneoxide and halogens (as acceptors), such poly(2vinylpyridine)iodine and poly(4-vinylpyridine)bromine complexes. Other examples include metal-halogen compounds, for instance, CuI.
The glass surface is coated with halogens by its treatment in solutions containing molecular halogens (iodine, bromine) or polyhalogens that are dissolved in dry (less than 1 ppm of moisture), non-polar solvents. In the preferred case, the solvents are selected from a group of unsaturated hydrocarbons or benzene and its homologues. In another case, the solvents are halogenated hydrocarbons, in particular, carbon tetrachloride. In another case, the solvent is carbon disulfide. The glass surface is brought into contact with or the glass is immersed into a solvent containing dissolved coating material (halogens or polyhalogens). Then the solvent is allowed to evaporate. In one case, Li—Mg or Li—Ca alloys (solid solution range) are used instead of Li metal. As a result, the SEI consists of LiI or LiBr doped with corresponding halides of Mg or Ca and has increased Li ion conductivity due to formation of Li cation vacancies (Schottky defects). In one case, both the glass surface and Li are treated in halogen vapor containing atmosphere. As a result, the halogen coating (preferentially, a very thin coating that consists of one or two molecular layers) is formed on the glass surface and a thin layer of LiHal is formed on the Li surface. After Li lamination onto glass, halogen molecules react with LiHal layer on Li forming an SEI consisting of a LiHal layer with increased thickness.
2. Nitrogen
A monolayer, a few layers or condensed films formed by nitrogen molecules on a glass surface from gas phase or from liquid phase at RT or low temperatures. At RT only one or two layers of nitrogen molecules are adsorbed onto metal surfaces. nitrogen can be adsorbed onto glass surfaces either in pure nitrogen atmosphere (the volume having been previously evacuated to high vacuum) or in a mixed nitrogen/inert gas atmosphere (Ar/N2). In order to coat a long strip of glass, either a flow of pure nitrogen or a flow of carrier gas (Ar) mixed with nitrogen can be used.
In various embodiments, the resulting SEI is, or includes, Li3N with a high Li ion conductivity.
In various embodiments the molecular nitrogen precursor layer is formed by coating the surface of the solid electrolyte glass sheet with a thin layer of a liquid hydrocarbon containing an amount of dissolved nitrogen molecules. In various embodiments the mole ratio of nitrogen molecules dissolved in the hydrocarbon carrier liquid is at least 0.05 moles of nitrogen molecules per mole of liquid hydrocarbon (N2-moles/liq.hyd-moles). For instance, at least 0.1 N2-moles/liq.hyd-moles, at least 0.2 N2-moles/liq.hyd-moles, at least 0.3 N2-moles/liq.hyd-moles, at least 0.4 N2-moles/liq.hyd-moles, at least 0.5 N2-moles/liq.hyd-moles, at least 1.0 N2-moles/liq.hyd-moles. Particular suitable liquid hydrocarbon carriers are n-octane, n-nonane, n-decane, n-undecane, and n-dodecane.
When using a liquid carrier containing dissolved nitrogen molecules, the SEI formed when the nitrogen coated solid electrolyte layer is directly contacted with lithium metal is a lithium nitride compound (e.g., Li3N), preferably fully reduced and highly conductive to lithium ions. As described above, the formation of the SEI may be effected during the lamination step, and the liquid hydrocarbons on the surface of the solid electrolyte layer and/or the lithium metal layer removed prior to and/or as a result of bond laminating the layers together.
3. SO2
4. Sulfur
With reference to
The quality of inorganic interface 705 is a key aspect for determining how well the laminate electrode assembly will operate in a battery cell. Preferably, inorganic interface 705 is substantially uncontaminated by organic material, including organic residues of any inert liquid that may have been used in making, storing and processing of the laminate structures. In various embodiments the inorganic interface may be further characterized as “sufficiently uncontaminated by passivated alkali metal.” by which it is meant that at least 70% of the geometric area of the solid-state interface is uncontaminated by the presence of passivated alkali metal, such as patches of passivated alkali metal film (i.e., filmy patches), as well as pieces of passivated alkali metal that break off during battery cell cycling and/or handling, and could become trapped at the interface in the form of solid flakes, flecks or material bits of passivated alkali metal. Preferably, at least 80% of the geometric area of the solid-state interface is uncontaminated as such, and more preferably at least 90%, and even more preferably at least 95%, and yet even more preferably the entire geometric area of the solid-state interface is uncontaminated by the presence of passivated alkali metal flakes, flecks, filmy patches or material bits. To achieve an inorganic interface that is sufficiently uncontaminated by passivated alkali metal, surface 101i of lithium metal layer 101 should be substantially unpassivated prior to bonding, and preferably the lithium metal layer surface is pristine. Additionally, the surface of the sulfide glass should be cleaned (e.g., by ion etching) immediately prior to bonding in order to remove solid products of sulfide glass hydrolysis.
When the reactive bond between the layers is continuous and complete, the laminate should exhibit exceptional adherence. In various embodiments the reactively bonded solid-state interface imparts exceptionally high peel strength to the standalone solid-state laminate electrode assembly (i.e., room temperature peel strength). For instance, the room temperature peel strength of the solid-state laminate electrode assembly is significantly greater than the tensile strength of the lithium metal layer to which it is bonded, such that during room temperature peel strength testing the lithium metal layer starts to deform, or tears, prior to peeling.
With reference to
Once the liquid layer has been removed from sulfide glass surface 201i, the surface may be cleaned in ion etching chamber 820 using argon plasma (as described above with reference to chamber 620 in
Laminate electrode assembly 700, which may be formed as described above, includes second major surface 201ii of the sulfide glass, and which may be highly sensitive to moisture. Accordingly, in various embodiments, after laminate electrode assembly 700 has been formed it may be stored in a sealed cartridge 900, as shown in
With reference to
It is understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to persons skilled in the art. Although various details have been omitted for clarity's sake, various design alternatives may be implemented. Therefore, the present examples are to be considered as illustrative and not restrictive, and the disclosure is not to be limited to the details given herein, but may be modified within the scope of the appended claims.
This application is a continuation of U.S. patent application Ser. No. 15/929,959, filed May 29, 2020, titled SOLID-STATE LAMINATE ELECTRODE ASSEMBLIES AND METHODS OF MAKING, which is a continuation of U.S. patent application Ser. No. 15/592,102, filed May 10, 2017, titled SOLID-STATE LAMINATE ELECTRODE ASSEMBLIES AND METHODS OF MAKING, which claims priority to U.S. Provisional Patent Application No. 62/334,327, filed May 10, 2016, titled PRISTINE LITHIUM METAL LAYERS AND ASSOCIATED COMPOSITIONS, STRUCTURES, COMPONENTS, BATTERY CELLS AND METHODS; 62/351,211, filed Jun. 16, 2016, titled PRISTINE LITHIUM METAL LAYERS AND ASSOCIATED COMPOSITIONS, STRUCTURES, COMPONENTS, BATTERY CELLS AND METHODS; 62/352,972, filed Jun. 21, 2016, titled PRISTINE LITHIUM METAL LAYERS AND ASSOCIATED COMPOSITIONS, STRUCTURES, COMPONENTS, BATTERY CELLS AND METHODS; 62/424,240, filed Nov. 18, 2016, titled PRISTINE LITHIUM METAL LAYERS AND ASSOCIATED COMPOSITIONS, STRUCTURES, COMPONENTS, BATTERY CELLS AND METHODS; 62/447,637, filed Jan. 18, 2017, titled PRISTINE LITHIUM METAL LAYERS AND ASSOCIATED COMPOSITIONS, STRUCTURES, COMPONENTS, BATTERY CELLS AND METHODS; 62/448,817, filed Jan. 20, 2017, titled STANDALONE LITHIUM METAL LAYER STRUCTURES, STANDALONE Li-ION CONDUCTIVE SOLID ELECTROLYTE LAYER STRUCTURES, AND ASSOCIATED COMPOSITIONS, LAMINATE STRUCTURES, COMPONENTS, BATTERY CELLS AND METHODS; the disclosures of which are incorporated by reference herein in their entirety and for all purposes.
This invention was made with Government support under Award No.: DE-AR0000772 awarded by the Advanced Research Projects Agency—Energy (ARPA-E), U.S. Department of Energy. The Government has certain rights in this invention.
| Number | Date | Country | |
|---|---|---|---|
| 62448817 | Jan 2017 | US | |
| 62447637 | Jan 2017 | US | |
| 62424240 | Nov 2016 | US | |
| 62352972 | Jun 2016 | US | |
| 62351211 | Jun 2016 | US | |
| 62334327 | May 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15929959 | May 2020 | US |
| Child | 17453033 | US | |
| Parent | 15592102 | May 2017 | US |
| Child | 15929959 | US |