Patent Application
20240416686
The present technology relates to a solid tire represented by a pneumatic cushion tire for an industrial vehicle and a method for manufacturing the same, and more particularly, to a solid tire including a radio frequency identification (RFID) tag for product identification and capable of sufficiently ensuring a protection effect of the RFID tag and a method for manufacturing the same.
A pneumatic cushion tire for an industrial vehicle is a solid tire for a forklift having an appearance in terms of shape similar to that of a pneumatic tire. This type of solid tire is used under conditions of low speed and high load, and in some cases, is used under severe conditions such as when a steering wheel is operated while the vehicle is stopped.
A solid tire generally includes a tread rubber layer on a road contact surface side and a base rubber layer on a rim side. The base rubber layer is formed of a hard rubber composition, and the tread rubber layer is formed of a rubber composition for which grip properties, wear resistance, chipping resistance, heat build-up resistance, and rolling resistance are emphasized (for example, refer to Japan Unexamined Patent Publication Nos. H10-147107 A, 2010-163123 A and 2016-117296 A).
In recent years, it is necessary to perform quality control and history management for each product of the solid tire as described above. However, at present, no specific means for efficiently performing quality control and history management for each product of a solid tire has been proposed.
The present technology provides a solid tire including an RFID tag for product identification and capable of sufficiently ensuring a protection effect of the RFID tag, and a method for manufacturing the same.
A solid tire of the present technology includes a tread rubber layer on a road contact surface side and a base rubber layer on a rim side. The base rubber layer has JIS (Japanese Industrial Standard)-A hardness of 80 or higher, and a radio frequency identification (RFID) tag is embedded in the base rubber layer.
In addition, a method (first method) for manufacturing a solid tire of the present technology is a method for manufacturing the above-described solid tire and includes: when forming an unvulcanized tire by winding a rubber sheet into multiple layers, inserting an RFID tag between layers of the rubber sheet in the middle of the winding into multiple layers; and vulcanizing the unvulcanized tire including the RFID tag in a mold.
Furthermore, a method (second method) for manufacturing a solid tire of the present technology is a method for manufacturing the above-described solid tire, and includes: forming an unvulcanized tire by winding a rubber sheet into multiple layers; then attaching an RFID tag to a side surface of the unvulcanized tire: further overlaying and attaching a coating layer made of unvulcanized rubber having a thickness of 0.5 mm to 10 mm on the RFID tag; and then vulcanizing the unvulcanized tire including the RFID tag in a mold.
According to the present technology, in the solid tire including the tread rubber layer on the road contact surface side and the base rubber layer on the rim side, the RFID tag for product identification is embedded in the base rubber layer, so quality control and history management for each product can be performed using the RFID tag. Furthermore, since the JIS-A hardness of the base rubber layer in which the RFID tag is embedded is 80 or higher, the protection effect of the RFID tag can be sufficiently ensured, and quality control and history management for each product can be performed over a long period of time. Note that the JIS-A hardness in the present technology is the durometer hardness measured in accordance with JIS-K6253 using a type A durometer and under a temperature of 23° C.
In the present technology, the RFID tag is preferably disposed near a side surface of the base rubber layer, and more specifically, a distance between the RFID tag and the side surface of the base rubber layer is preferably within a range of 0.5 mm to 10.0 mm. As a result, good response accuracy can be exhibited while the protection effect of the RFID tag is sufficiently ensured.
When the RFID tag is disposed near the side surface of the base rubber layer, the RFID tag is preferably disposed at a position deviating from a rim slippage region defined within a range of −15% to +15% of a rim flange height with an apex of a rim flange as a center. As a result, even when rim slippage occurs in the solid tire, the protection effect of the RFID tag can be sufficiently ensured. The rim flange height is a height in a radial direction of a rim from a rim diameter position on a specified rim to a rim flange apex. The “specified rim” refers to a rim defined, in a standard system that includes standards on which tires are based, by the standards for each tire, and refers, for example, to an applicable rim for The Japan Automobile Tyre Manufacturers Association, Inc. (JATMA). The dimensions of the applicable rim of JATMA are defined by JIS-D6402 “Wheels for industrial vehicles and off the road service-Contours of rims”.
The RFID tag is preferably embedded substantially parallel to the side surface of the base rubber laver. This can enhance the response accuracy of the RFID tag.
The RFID tag is preferably disposed near the side surface of the base rubber layer that is on an outer side of a vehicle when mounted on the vehicle. This enhances convenience of a communication work with the RFID tag.
Short fibers are preferably blended in a rubber composition constituting the base rubber layer. As a result, deformation of the base rubber layer can be suppressed, and the protection effect of the RFID tag can be enhanced. In addition, the short fibers are blended into the rubber composition constituting the base rubber layer, so that the rim slippage is suppressed, and from this standpoint as well, the protection effect of the RFID tag can be enhanced. The short fibers preferably contain 1 phr to 10 phr of vinylon fibers having a fiber length of 2 mm to 10 mm and a fiber diameter of 5 μm to 50 μm (weight with respect to 100 parts by weight of rubber).
The RFID tag is preferably coated with an adhesive. As a result, the adhesion between the RFID tag and the rubber can be enhanced, and a tire failure caused by peeling between the RFID tag and the rubber can be prevented.
The RFID tag is preferably coated with polyphenylene sulfide resin. The durability of the RFID tag can be improved by coating the RFID tag with the polyphenylene sulfide resin having heat resistance.
The RFID tag is preferably coated with ceramic. The durability of the RFID tag can be improved by coating the RFID tag with ceramic having heat resistance and rigidity.
The RFID tag is preferably coated with a plurality of reinforcing fiber cords. Alternatively, the RFID tag is preferably coated with a reinforcing fabric. By coating the RFID tag with the reinforcing fiber cord or reinforcing fabric, the durability of the RFID tag can be improved.
According to the method (first method) for manufacturing a solid tire of the present technology, when forming an unvulcanized tire by winding a rubber sheet into multiple layers, an RFID tag is inserted between layers of the rubber sheet in the middle of the winding into multiple layers, whereby the RFID tag can be embedded at a desired position of the solid tire. In particular, when winding the rubber sheet into multiple layers, a winding position of the rubber sheet in the radial direction of the unvulcanized tire is calculated in accordance with a winding length and a thickness of the rubber sheet, and the RFID tag is inserted in accordance with the winding position, whereby the RFID tag can be embedded with high accuracy.
In addition, according to the method (second method) for manufacturing a solid tire of the present technology, an unvulcanized tire is formed by winding a rubber sheet into multiple layers, an RFID tag is attached to a side surface of the unvulcanized tire, and a coating layer made of unvulcanized rubber having a thickness of 0.5 mm to 10 mm is overlaid and attached on the RFID tag, whereby the RFID tag can be embedded at a desired position of the solid tire.
Configurations of embodiments of the present technology will be described in detail below with reference to the accompanying drawings.
As illustrated in
The tread rubber layer 1 is formed of a rubber composition mainly composed of a diene rubber such as natural rubber, styrene-butadiene rubber, or butadiene rubber. Carbon black or silica can be added as a reinforcing agent to the rubber composition constituting the tread rubber layer 1, and in the case of silica, an organic silane coupling agent or the like can be added together. Examples of the organic silane coupling agent may include bis(triethoxy-silylpropyl)tetrasulfide (TESPT). Further, the rubber composition constituting the tread rubber layer 1 may contain other blending agents that are generally used.
The JIS-A hardness of the tread rubber layer 1 is not particularly limited but preferably ranges from 50 to 75, for example. If the JIS-A hardness of the tread rubber layer 1 is less than 50, an amount of distortion in the tire radial direction becomes too large and the horizontal rigidity becomes too small due to a reduction in rigidity. On the other hand, if the JIS-A hardness of the tread rubber layer 1 exceeds 75, the amount of distortion in the tire radial direction is reduced due to an increase in rigidity, and the vibration-absorbing property is lowered, thereby deteriorating the ride comfort.
The base rubber layer 2 is formed of a rubber composition mainly composed of a diene rubber such as natural rubber, styrene-butadiene rubber, or butadiene rubber. Carbon black and further a phenol resin can be added as a reinforcing agent to the rubber composition constituting the base rubber layer 2, and hexamethylenetetramine or the like can be added together as a curing agent for the phenol resin. Further, the rubber composition constituting the base rubber layer 2 may contain other blending agents that are generally used.
JIS-A hardness of the base rubber layer 2 is 80 or higher. If the JIS-A hardness of the base rubber layer 2 is less than 80, the amount of distortion in the tire radial direction becomes too large and the horizontal rigidity becomes too small due to a reduction in rigidity. When the rigidity of the base rubber layer 2 is insufficient, rim slippage due to contact between the base rubber layer 2 and the rim flange is likely to occur during driving.
Two or more bead cores 3 continuing annularly along a tire circumferential direction are disposed inside the base rubber layer 2. The bead cores 3 are disposed symmetrically with respect to a tire equatorial plane. As the bead core 3, a bead core formed by winding a plurality of bead wires multiple times (so-called strand bead wire), a bead core formed by winding a single bead wire multiple times, a bead core formed of a single steel ring, or the like can be used. In order to ensure adhesion to the base rubber layer 2, when a bead wire is used, the surface thereof is generally subjected to zinc plating or brass plating of tin and copper, and when a steel ring is used, the surface thereof is generally coated with various vulcanizing adhesives. In addition, instead of providing the bead core 3, short fibers may be blended into the rubber composition constituting the base rubber layer 2. If necessary, short fibers may be blended into the rubber composition constituting the base rubber layer 2 simultaneously with the provision of the bead cores 3. As such short fibers, short fibers made of organic fibers such as nylon, polyester, rayon, aramid and vinylon can be used.
In the above-described solid tire 10, an RFID tag 11 is embedded in the base rubber layer 2. In
As described above, in the solid tire 10 including the tread rubber layer 1 on the road contact surface side and the base rubber layer 2 on the rim side, the RFID tag 11 for product identification is embedded in the base rubber layer 2, so quality control and history management for each product can be performed using the RFID tag 11. That is, it is possible to perform quality control by associating an identification number stored in the RFID tag 11 with a manufacturing condition, and to ensure traceability after shipment by using the identification number stored in the RFID tag 11. In addition, since the JIS-A hardness of the base rubber layer 2 in which the RFID tag 11 is embedded is 80 or higher, the protection effect of the RFID tag 11 can be sufficiently ensured, and quality control and history management for each product can be performed over a long period of time.
In the solid tire 10, the RFID tag 11 is preferably disposed near the side surface S of the base rubber layer 2. More specifically, as illustrated in
In the solid tire 10, the RFID tag 11 is preferably embedded substantially parallel to the side surface S of the base rubber layer 2. As a result, the response accuracy of the RFID tag 11 can be improved. Note that the state in which the RFID tag 11 is substantially parallel to the side surface S of the base rubber layer 2 is a state in which an angle between the sheet-shaped RFID tag 11 and the side surface S of the base rubber layer 2 is within ±20°. If the angle deviates from the range of ±20°, the reception sensitivity tends to decrease.
In the solid tire 10, the RFID tag 11 is preferably disposed near one of both side surfaces of the base rubber layer 2, which is on the outer side of the vehicle when mounted on the vehicle. In this case, since the RFID tag 11 is disposed on the outer side of the vehicle in a state in which the solid tire 10 is mounted on the vehicle, convenience of a communication work with the RFID tag 11 is enhanced. In the solid tire 10 on which a mounting direction with respect to the vehicle is designated (displayed), the RFID tag 11 is disposed near the side surface of the base rubber layer 2 that is on the outer side of the vehicle in the designated mounting state.
In the above-described solid tire 10, as illustrated in
The short fibers 5, which are not limited to a particular fiber, can contain, for example, 1 phr to 10 phr of vinylon fibers having a fiber length of 2 mm to 10 mm and a fiber diameter of 5 μm to 50 μm. Such a vinylon fiber is suitable as a reinforcing material for the base rubber layer 2. Here, if the blending amount of the vinylon fibers is less than 1 phr, the modulus in the low-elongation region becomes small, the rigidity of the base rubber layer 2 decreases, and the base rubber layer 2 is easily bent, so that the protection effect of the RFID tag 11 decreases. On the other hand, if the blending amount of the vinylon fibers exceeds 10 phr, the modulus in the low-elongation region becomes too large, and mountability on rims is deteriorated. In addition, if the fiber length is less than 2 mm, the modulus in the low-elongation region becomes small, and thus the protection effect of the RFID tag 11 is reduced, whereas if the fiber length exceeds 10 mm, the modulus in the low-elongation region becomes excessively large, and thus mountability on rims is deteriorated. Further, if the fiber diameter is less than 5 μm, the dispersibility of the short fibers is reduced during rubber kneading, whereas if the fiber diameter exceeds 50 μm, the modulus in the low-elongation region is reduced due to a reduction in specific surface area of the vinylon fiber, and thus the protection effect of the RFID tag 11 is reduced. Furthermore, if the fiber diameter is too large, it becomes a foreign matter, which is not preferable.
In
In
In
In
In
In the method for manufacturing the solid tire 10 described above, when winding the rubber sheet 20 into multiple layers, an outer diameter position of the forming drum D is used as a reference, a winding position of the rubber sheet 20 in the radial direction of the unvulcanized tire 10X is calculated in accordance with a winding length and a thickness of the rubber sheet 20, and the RFID tag 11 may be inserted in accordance with the winding position. That is, the RFID tag 11 may be inserted in the middle of the winding into multiple layers. Specifically, when a predetermined position is reached, the winding may be stopped once, the RFID tag 11 may be installed, and then the winding may be resumed. This operation may be performed multiple times when inserting a plurality of RFID tags 11. In addition, for example, in a tire having a two-layered structure with a 5.00-8 size, the base rubber sheet has a width of 120 mm and a thickness of 8 mm, and the winding is stopped once at the time when the base rubber sheet is wound into four layers, the RFID tag 11 is installed, and the base rubber sheet is further wound into two layers. Thereafter, the unvulcanized tire 10X with a total winding height of 110 mm of the tread rubber sheet is completed. When this is vulcanized in a predetermined mold to obtain a product, the RFID tag 11 is embedded at a position of about 200% of the rim flange height H. As a result, the RFID tag 11 can be embedded with high accuracy. In addition, when the winding position of the rubber sheet 20 in the radial direction of the unvulcanized tire 10X is calculated in accordance with the winding length and the thickness of the rubber sheet 20 and the RFID tag 11 is inserted in accordance with the winding position, the insertion operation of the RFID tag 11 can also be automated.
In the present technology, the structure of the solid tire is not particularly limited as long as the solid tire includes the tread rubber layer on the road contact surface side and the base rubber layer on the rim side and the JIS-A hardness of the base rubber layer is 80 or higher. For example, it is also possible to adopt a structure in which an additional reinforcing member made of steel, organic fiber, or high-hardness rubber is embedded in the solid tire, or a structure in which an additional cushioning member made of low-hardness rubber is embedded in the solid tire.
In pneumatic cushion tires for industrial vehicles having a tire size of 5.00-8 and including a tread rubber layer on a road contact surface side and a base rubber layer on a rim side, a plurality of types of test tires (Comparative Examples 1 to 7 and Examples 1 to 9) were manufactured in which an RFID tag was embedded in the base rubber layer and the JIS-A hardness of the base rubber layer was varied.
In Comparative Examples 1 to 7 and Examples 1 to 9, the blending of the base rubber layer, the JIS-A hardness of the tread rubber layer, and the JIS-A hardness of the base rubber layer are as shown in Table 1. Four bead cores are embedded in the base rubber layer of each test tire. As the RFID tag, a passive type RFID tag (fine ceramics tag type A manufactured by KYOCERA CORPORATION) having dimensions of 5 mm×15 mm×thickness 1.7 mm was used, the distance between the RFID tag and the side surface of the base rubber layer was set to 2.0 mm, and the RFID tag was embedded at (A) a position of 30% of the rim flange height. (B) a position of 100% of the rim flange height, and (C) a position of 200% of the rim flange height, respectively (refer to
The test tires were subjected to the following actual vehicle test. That is, the test tire was mounted to a rim having a rim size of 8×3.00D, which was then mounted on each of the left and right rear wheels of a forklift, and the forklift having a load weight of 500 kg was driven at a driving speed of 8.8 km/h for 100 hours on a test course having a dry flat road surface paved with concrete. The test course is a circuit illustrated in
As can be seen from Table 1, in the tires of Examples 1 to 9, the rim slippage width was small, and all the RFID tags operated normally. On the other hand, in the tires of Comparative Examples 1 to 7, since the JIS-A hardness of the base rubber layer was less than 80, the rim slippage width was large, and at least a part of the RFID tags did not operate.
Next, in pneumatic cushion tires for industrial vehicles having a tire size of 5.00-8 and including a tread rubber layer on a road contact surface side and a base rubber layer on a rim side, a plurality of types of test tires (Examples 11 to 18) were manufactured in which an RFID tag was embedded in the base rubber layer and an amount of short fibers blended into a rubber composition constituting the base rubber layer was varied. As the short fiber, a vinylon fiber (vinylon fiber 1) having a fiber length of 4 mm and a fiber diameter of 12 μm or a vinylon fiber (vinylon fiber 2) having a fiber length of 8 mm and a fiber diameter of 24 μm was used.
In Examples 11 to 18, the blending of the base rubber layer, the JIS-A hardness of the tread rubber layer, the JIS-A hardness of the base rubber layer, and the modulus at 10% elongation of the base rubber layer are as shown in Table 2. Four bead cores are embedded in the base rubber layer of each test tire. As the RFID tag, a passive type RFID tag (fine ceramics tag type A manufactured by KYOCERA CORPORATION) having dimensions of 5 mm×15 mm×thickness 1.7 mm was used, the distance between the RFID tag and the side surface of the base rubber layer was set to 2.0 mm, and the RFID tag was embedded at (A) a position of 30% of the rim flange height, (B) a position of 100% of the rim flange height, and (C) a position of 200% of the rim flange height, respectively (refer to
For the test tires, in the same manner as described above, after performing the actual vehicle test, the ratio (%) of the rim slippage width was obtained, and the operation confirmation test was performed for the RFID tags (A, B, and C). However, the driving time was 1.2 times that of the test of Table 1. The results are shown in Table 2.
As can be seen from Table 2, in the tires of Examples 11 to 18, the rim slippage width was small, and all the RFID tags operated normally.
Next, Example 4 and Examples 19 and 20 in which the distance between the RFID tag and the side surface of the base rubber layer in Example 4 was changed to 6.0 mm or 10.0 mm were manufactured, and the response accuracy of the RFID tag was evaluated by the following test method. That is, “∘” indicates that the RFID tag can be read from a position 20 cm away from the surface of the base rubber layer in the tire axial direction, “Δ” indicates that the RFID tag can be read from a position 10 cm away from the surface of the base rubber layer in the tire axial direction, and “x” indicates that the RFID tag cannot be read from a position 10 cm away from the surface of the base rubber layer in the tire axial direction. The results are shown in Table 3.
As can be seen from Table 3, by setting the distance between the RFID tag and the side surface of the base rubber layer to 10.0 mm or less, good responsiveness could be secured.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2021-210774 | Dec 2021 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2022/042193 | 11/4/2022 | WO |