Patent Application
20240286901
The present invention relates to a method for preparing salts of bis(fluorosulfonyl)imide and to a method for preparing alkali metal salts of bis(fluorosulfonyl)imide from said bis(fluorosulfonyl)imide salts. More specifically, the invention provides a new method for producing these salts of bis(fluorosulfonyl)imide which is implementable at industrial scale and providing high-purity bis(fluorosulfonyl)imide salts.
Bis(fluorosulfonyl)imide and salts thereof, in particular the lithium salt of bis(fluorosulfonyl)imide (LiFSI), are useful compounds in a variety of technical fields.
The production of bis(fluorosulfonyl)imide and salts thereof is described in the literature. Among the various technologies described, the majority uses a fluorination reaction with a fluorinating agent in a solvent.
Notably, WO 2017/090877 A1 (CLS) describes a method for producing lithium bis(fluorosulfonyl)imide comprising the steps of: (1) reacting bis(chlorosulfonyl)imide with a fluorinating reagent in a solvent, followed by treatment with an alkaline reagent, thereby producing ammonium bis(fluorosulfonyl)imide; and (2) reacting the ammonium bis(fluorosulfonyl)imide with a lithium base. The solvent used in step (1) is selected from the group consisting of alkyl ketones, including acetone, methyl ethyl ketone, and methyl isopropyl ketone; alcohols, including methanol, anhydrous ethanol, 1-propanol, and isopropanol; alkyl nitriles, including acetonitrile, and propionitrile; and ethers, including tetrahydrofuran, and dialkoxyalkane. The solvent is then removed by distillation and concentration under reduced pressure.
WO 2012/117961 A1 (Nippon Soda) describes a process for producing a fluorosulfonylimide salt, comprising the reaction between a compound of formula [II] Cl—CO2—NH—SO2—R1 wherein R1 is a fluoroalkyl group, a fluorine atom or a chlorine atom with a fluorinating agent [III], preferably of formula NH4F(HF)p with p being from 0 to 10. The reaction between compounds [II] and [III] can be conducted in the presence of a solvent or in the absence of a solvent. However, according to examples 1 and 2, ammonium di(fluorosulfonyl)imide is prepared from di(chlorosulfonyl)imide in acetonitrile. The solvent is then removed by distillation under reduced pressure. As a whole, this patent application does not disclose a process for producing a fluorosulfonylimide salt that is performed in the absence of solvent or in the presence of an amount of solvent lower than 5 wt. % based on the total weight of the reaction mixture.
JP 2016145147 (Nippon Shokubai) relates to a method for providing a fluorosulfonylimide compound represented by the formula (1) by reacting a compound represented by the formula (2) and a compound represented by the composition formula (3) of 1 to 3 equivalence by stoichiometric amount based on 1 mol of the compound in a presence of a solvent of 0 to 4 mass times of the compound.
where R1 is a C1-6 fluoroalkyl group, R6 is halogen or a C1-6 fluoroalkyl group, Cat1+ and Cat2+ are monovalent groups and p is an integer of 1 to 10.
JP 2014201453 (Nippon Shokubai) describes a method for producing an alkali metal salt of fluorosulfonyl imide which comprises a step of synthesizing an alkali metal salt of fluorosulfonyl imide in the presence of a reaction solvent containing at least one solvent selected from the group consisting of a carbonate-based solvent, an aliphatic ether-based solvent, an ester-based solvent, an amide-based solvent, a nitro-based solvent, a sulfur-based solvent and a nitrile-based solvent and, subsequently concentrating an alkali metal salt solution of fluorosulfonyl imide by distilling off the reaction solvent in the coexistence of the reaction solvent and at least one poor solvent for the alkali metal salt of fluorosulfonyl imide selected from the group consisting of an aromatic hydrocarbon-based solvent, an aliphatic hydrocarbon-based solvent and an aromatic ether-based solvent, the concentration step includes the step of mixing the above poor solvent with the reaction solution containing the reaction solvent and an alkali metal salt of fluorosulfonyl imide.
As described in the literature, the production of bis(fluorosulfonyl)imide and salts thereof by fluorination takes place in solvents, for example organic solvents, in order to disperse the reactive entities and allow them to react. However, such solvents need to be removed after reaction in order to obtain an as pure as possible product which can be used for battery applications. The step for removing the solvent adds to the complexity of the industrial process, as well as its overall cost. In addition, before being implemented in such processes, the solvents typically have to be treated to remove the residual amount water, as only anhydrous solvent, where the residual amount of water is in the ppm amount, are actually to be used.
An object of the present invention is to provide a simpler production process of salts of bis(fluorosulfonyl)imide, which does not require the distillation of the reaction solvent.
WO 2012/096371 A1 (Sumitomo Electric Ind) relates to a method for producing KN(SO2F)2 by adding HN(SO2Cl)2 (liquid form) drop-wise to KF (powder form) under solvent-free dry conditions, to form an intermediate product, and then allowing the intermediate product and KF to react with each other in an aqueous solvent. More precisely, according to the method described in this document, in a first step, one chlorine element of HN(SO2Cl)2 is substituted with fluorine to lead to an intermediate product which is the alkali metal salt KN(SO2CI)(SO2F); and in a second step, the other chlorine element is substituted with fluorine to lead to the alkali metal salt KN(SO2F)2. In accordance with such a two-stage step, because HN(SO2Cl)2 is converted into an alkali metal salt KN(SO2Cl)(2F), as a result, it becomes possible to use water in the second step, as water dissolves the alkali metal fluoride.
According to this document, the first part of reaction takes place under solvent-free dry conditions, by dropping of the reactant in a liquid form onto the second reactant, which is in powder form. This leads to a paste-like intermediate product, which is very difficult to handle industrially. Additionally, because the overall conversion of HN(SO2Cl)2 into KN(SO2F)2 is conducted in two steps with an individualized intermediate, the yield of the reaction is negatively impacted, as well as the level of impurities of the final product.
An object of the present invention is to provide a method for preparing salts of bis(fluorosulfonyl)imide X1N(SO2F)2, with X1 being K+, Na+ or an onium cation (for example NH4+), such method being implementable at industrial scale and providing high-purity bis(fluorosulfonyl)imide salts. In particular, the method of the present invention is carried out in the presence of the molten reaction product, for example molten KN(SO2F)2 or molten NH4N(SO2F)2, acting to disperse the reactants, and in the absence of solvent (or in the presence of a very limited quantity of solvent).
The present invention relates to a process for preparing a salt of bis(fluorosulfonyl)imide of formula (I):
[F—(SO2)—N−—(SO2)—F]nX1n+ (I)
Cl-—SO2)—NH—(SO2)—Cl (II) or salt thereof
with a fluorinating agent represented by formula (III):
X1n+(F−)n(HF)p
wherein:
The present invention also relates to a salt of bis(fluorosulfonyl)imide of formula (I):
[F—(SO2)—N−—(SO2)—F]nX1n+ (I)
wherein:
The present invention also relates to a process for preparing an alkali salt of bis(fluorosulfonyl)imide of formula (V),
F—(SO2)—NX3—(SO2)—F (IV)
The present invention also relates to a salt of bis(fluorosulfonyl)imide of formula (IV):
F—(SO2)—NX3—(SO2)—F (IV)
as well as to the use of such salt in a battery electrolyte solution.
In the present application:
A first object of the present invention is a process for preparing a salt of bis(fluorosulfonyl)imide of formula (I):
[F—(SO2)—N−—(SO2)—F]nX1n+ (I)
Cl—(SO2)—NH—(SO2)—Cl (II) or salt thereof
with a fluorinating agent represented by formula (III):
X1n+(F−)n(HF)p
The salt (I) described herein is characterized by a low residual amount of solvent, advantageously a non-detectable amount of solvent which makes the salt (I) well-suited for many applications, notably battery applications.
The method of the present invention is performed in the melt in the absence of solvents and diluents. More precisely, the method is carried out in molten salt of bis(fluorosulfonyl)imide of formula (I), for example molten KN(SO2F)2 or molten NH4N(SO2F)2, acting to disperse the reactants and allowing the reactants (II) and (III) to meet and react. Importantly, the method of the present invention is a solvent-free method. In other words, no solvent/diluent, alternatively a very low amount of solvent/diluent, is added to the reaction mixture during the reaction. This is advantageous because first, the step for removing the solvent adds to the complexity of the industrial process, as well as its overall cost. Secondly, the solvents typically need to be treated before being used in such process, as only anhydrous solvent (characterized by a residual amount of water is in the order of the ppm amount) can actually be used.
In the context of the present invention, the term “solvent” is intended to mean a compound which presents the following three cumulative properties of 1/being present from the beginning to the end of the reaction, possibly added during the process, 2/ unchanged during the process, in other words non-reactive towards the involved reactants, and 3/ having to be removed at the end of the process in case the reaction product is to be in its pure form. Examples of solvents falling within the scope of this definition are given below. For the sake of clarity, the molten salt of bis(fluorosulfonyl)imide of formula (I) used in the process of the present invention does not fall under the definition of “solvent” above-mentioned.
According to one embodiment of the present invention, the method described herein is carried out or in the presence of a very low amount of solvent, that-is-to-say an amount of solvent less than 5 wt. %, based on the total weight of the reaction mixture. Preferably, according to this embodiment, the amount of solvent is less than 4 wt. %, less than 3 wt. %, less than 2 wt. %, less than 1 wt. %, less than 0.5 wt. %, less than 0.1 wt. %, less than 0.01 wt. %, or less than 0.001 wt. % of solvent, based on the total weight of the reaction mixture. The total weight of the reaction mixture is obtained by adding the weight of the reactants, as well as the weight of the molten salt of bis(fluorosulfonyl)imide of formula (I).
Solvents which are typically used in such processes are well-known and extensively described in the literature. Such solvents may be aprotic, for example polar aprotic solvents, and may selected from the group consisting of:
Typically, the organic solvent used to carry out such processes may be selected from the group consisting of ethyl acetate, isopropyl acetate, butyl acetate, ethylene carbonate, dimethyl carbonate, ethyl methyl carbonate, propylene carbonate, valeronitrile and acetonitrile, as for example in the literature described in the backgroup section.
According to the process of the present invention, a quantity of the salt of bis(fluorosulfonyl)imide of formula (I), for example KN(SO2F)2 and NH4N(SO2F)2, is heated above its melting temperature Tm(I), before the addition of the reactants (or reactive entities), in order to be in a molten state (also called liquid state). The reactants, which can be in a powder form or in a liquid form, are then added into the reaction mixture and allowed to react in order to produce the salt of bis(fluorosulfonyl)imide of formula (I), for example KN(SO2F)2 or NH4N(SO2F)2. This means that the quantity of such reaction product (i.e. salt of bis(fluorosulfonyl)imide of formula (I)) increases over the reaction time. In other words, the molten reaction product is used to provide a medium to disperse the reactants and allow them to meet and react. No solvent is therefore necessary according to the present invention. This is advantageous, as it significantly simplifies the overall production process since such solvent does not need to be removed after the reaction, in order to obtain a high-purity bis(fluorosulfonyl)imide salt. It presents the additional advantage that no additional step is needed to remove the water for the solvent.
According to the present invention, the bis(chlorosulfonyl)imide (II) or its salt:
Cl—(SO2)—NH—(SO2)—Cl (II)
is reacted with a fluorinating agent represented by formula (III):
X1n+(F−)n(HF)p (III)
in which X1n+ and n are as above-mentioned and p varies between 0 and 10, preferably 0.
According to the present invention, X1n+ represents K+, Na+ or an onium cation, wherein an onium cation has its usual meaning for the skilled person.
Examples of the onium cation include phosphonium cation, oxonium cation, sulfonium cation, fluoronium cation, chloronium cation, bromonium cation, iodonium cation, selenonium cation, telluronium cation, arsonium cation, stibonium cation, bismutonium cation; iminium cation, diazenium cation, nitronium cation, diazonium cation, nitrosonium cation, hydrazonium cation, diazenium dication, diazonium dication, imidazolium cation, pyridinium cation, quaternary ammonium cation, tertiary ammonium cation, secondary ammonium cation, primary ammonium cation, ammonium NH4+ cation, piperidinium cation, pyrrolidinium cation, morpholinium cation, pyrazolium cation, guanidinium cation, isouronium cation and isothiouronium cation.
Among these, imidazolium cation, pyridinium cation, quaternary ammonium cation, tertiary ammonium cation, secondary ammonium cation, primary ammonium cation, ammonium NH4+ cation, piperidinium cation, pyrrolidinium cation, morpholinium cation, pyrazolium cation, guanidinium cation, and isouronium cation are more preferred.
Examples of onium cations of these types include:
Quaternary ammonium cation, tertiary ammonium cation, secondary ammonium cation, primary ammonium cation, and ammonium cation NH4+ are more preferred, especially those specifically cited in the above list. Ammonium cation NH4+ is the most preferred onium cation.
One of the reactants (also called sometimes raw materials) involved in the process of the present invention is bis(chlorosulfonyl)imide of formula (Cl—SO2)2—NH (II), sometimes abbreviated as HCSI. HCSI is commercially available, or produced by a known method, for example:
The other reactant involved in the process of the present invention is the fluorinating agent (III). It may be used in the process of the present invention in any form, for example in the form of a powder or in the form of a liquid. Fluorinating agents are commercially available, or they may be produced by a known method.
In formula (III), p represents a real number from 0 to 10, preferably from 0 to 4, and more preferably p is an integer from 0 to 4. In some embodiments, p equals 0.
According to one embodiment, the fluorinating agent (III) is according to formula (IIIa):
KF(HF)p (IIIa), wherein p is 0 or 1.
According to another embodiment, the fluorinating agent (III) is according to formula (IIIb):
NaF(HF)p (IIIb), wherein p is 0 or 1.
According to another embodiment, the fluorinating agent (III) is according to formula (IIIc):
X2F(HF)p (IIIc),
in which X2 is an onium cation as defined above, and p is 0 or 1.
According to a preferred embodiment, the fluorinating agent (III) is according to formula (IIId):
NH4F(HF)p (IIId)
in which p varies between 0 and 10. According to this preferred embodiment, specific examples of the fluorinating agent (IIId) include NH4F, NH4F.HF, NH4F.2HF, NH4F.3HF, and NH4F. 4HF. The preferred fluorinating agent (Illd) is NH4F.
According to another preferred embodiment, the fluorinating agent (III) is anhydrous. Moisture content may be preferably below 5,000 ppm, more preferably below 1,000 ppm, below 500 ppm, below 100 ppm, below 50 ppm or even below 10 ppm, as determined by Karl Fisher water titration, for example performed in a glovebox.
In some embodiments, the stoichiometry amount (also called molar amount) of fluorinating agent (III) to bis(chlorosulfonyl)imide (II) is from 0.1:1 to 20:1, for example from 1:1 to 10:1, or from 2:1 to 8:1.
In some embodiments, the stoichiometry amount of fluorinating agent (III) is not less than 1 equivalent per 1 mol of bis(chlorosulfonyl)imide (II), for example between 1 to 10 equivalents per 1 mol of bis(chlorosulfonyl)imide (II). Preferably, the stoichiometry amount of fluorinating agent (III) is between 2 to 8 equivalents per 1 mol of bis(chlorosulfonyl)imide (II), or between 3 to 6 equivalents per 1 mol of bis(chlorosulfonyl)imide (II). More preferably, the stoichiometry amount of fluorinating agent (III) equals to 4±0.8 equivalents or to 4±0.5 per 1 mol of bis(chlorosulfonyl)imide (II).
The process of the present invention may be carried out in a batch, semi-batch or continuous mode.
According to an embodiment, the process is carried out in a continuous or semi-continuous manner, and comprises a step of continuously or semi-continuously withdrawing the salt of bis(fluorosulfonyl)imide (I) from the reaction mixture. It is possible, according to the present invention, to continuously add reactants in the reaction mixture and semi-continuously remove the reaction product.
In some embodiments, the process of the present invention comprises the steps of:
The temperature Ta(° C.) may be equal to or higher than the melting point Tm(I) the salt of bis(fluorosulfonyl)imide (I). For example, Ta may be equal to or higher than Tm(I)+2° C. or Ta may be equal to or higher than Tm(I)+5° C.
It is possible to predisperse one of the reactants, for example the fluorinating agent (III), in the reaction mixture before the introduction of the second reactant, for example the bis(chlorosulfonyl)imide (II).
According to these embodiments, step (ii) may for example itself comprise the steps of:
As explained above, the reactants may be in any form, including in the form of a solid or in the form of a liquid. For example, the fluorinating agent (III) may be added to the molten compound (I) in solid form, e.g. a powder form. The bis(chlorosulfonyl)imide (II) may be in a liquid form and may for example be added dropwise in the reaction mixture.
Advantageously, the fluorinating agent (III) is added to the molten salt of bis(fluorosulfonyl)imide (I) and then, according to an optional step (ii2), the residual amount of water (or aqueous liquids) that the agent (III) may contain, is removed. This optional step advantageously takes place after the fluorinating agent has been added to the reaction mixture. As explained above, the reaction should be performed with as less as possible residual water, in order to obtain a highly pure salt of bis(fluororosulfonyl)imide (II). However, it is almost impossible to completely remove all residual water from the fluorinating agent (III) (dry limit due to moisture inside the crystals). This is however advantageously possible when the fluorinating agent (III), in particular NH4F, is dispersed in the molten salt of bis(fluorosulfonyl)imide (I). This optional step greatly contribute to a highly pure product at the end of the reaction.
Preferably, the optional step (ii2) may be carried out by distillation of the water.
According to step (ii3), the bis(chlorosulfonyl)imide (II) may be heated to a temperature Tb(° C.) ranging from 30 to 150° C., prior to be added to the reaction mixture. The temperature Tb(° C.) may for example range between 35° C. and 125° C., or between 40° C. and 100° C. According to a specific embodiment, the bis(chlorosulfonyl)imide (II) is heated to the temperature Tb(° C.)=Ta(° C.)±10° C., for example Ta(° C.)±5° C. According to another embodiment, the bis(chlorosulfonyl)imide (II) is heated to a temperature Tb(° C.)≤Ta(° C.)±10° C., or Tb(° C.)≤ Ta(° C.).
In some embodiments, step (ii) consists in adding the fluorinating agent (III) and the bis(chlorosulfonyl)imide (II), concomitantly to the molten onium salt of bis(fluorosulfonyl)imide (I).
The addition of the reactants (II) and (III) in the molten onium salt of bis(fluorosulfonyl)imide (I) may be generally performed sequentially, progressively or continuously. The overall quantities of each reactant may also be added incrementally to the reaction vessel, for example in several time, especially if the process is conducted batch-wise.
Batch reactor, extruder and mixing kneader can for example be used in the present invention. Anti-acidic corrosion material (e.g. PTFE) can be coated (in other words, lined) inside the chosen reactor.
Reference can be made to industrialized melt mixers or melt blenders.
Mixing kneaders used can comprise any of the known suitable mixing kneaders which permit heating above the melting point of the salt (I) and enable discharge of gaseous products. Suitable mixing kneaders generally have one, or preferably at least two, rotating shafts which are parallel to the axis, of which the main shaft can have areas with kneading elements arranged on their periphery. The mixing kneader may have a rotor which is operated at a rotation rate in the range from 5 to 50 revolutions per minute, particularly preferably from 7.5 to 40 revolutions per minute, and in particular from 10 to 30 revolutions per minute. An advantage of the mixing kneaders used in the invention is that the residence time can be substantially longer than in an extruder. Venting is moreover substantially easier and can be carried out to a greater extent, thus permitting easy discharge of the gaseous products. The shear rate of the invention can moreover be established more easily in a mixing kneader. Various feed systems for the reactants can be used in a continuously operated mixing kneader. Liquid metering can be used where molten reactants are involved.
Some of the steps or all steps of the method according to the invention are advantageously carried out in equipment capable of withstanding the corrosion of the reaction medium. For this purpose, materials are selected for the part in contact with the reaction medium that are corrosion-resistant, such as the alloys based on molybdenum, chromium, cobalt, iron, copper, manganese, titanium, zirconium, aluminum, carbon and tungsten, sold under the Hastelloy® brands or the alloys of nickel, chromium, iron and manganese to which copper and/or molybdenum are added, sold under the name Inconel® or Monel™, and more particularly the Hastelloy C276 or Inconel 600, 625 or 718 alloys. Stainless steels may also be selected, such as austenitic steels and more particularly the 304, 304L, 316 or 316L stainless steels. A steel having a nickel content of at most 22 wt. %, preferably of between 6 wt. % and 20 wt. % and more preferentially of between 8 wt. % and 14 wt. %, is used. The 304 and 304L steels have a nickel content that varies between 8 wt. % and 12 wt. %, and the 316 and 316L steels have a nickel content that varies between 10 wt. % and 14 wt. %. More particularly, 316L steels are chosen. Use may also be made of equipment consisting of or coated with a polymeric compound resistant to the corrosion of the reaction medium. Mention may in particular be made of materials such as PTFE (polytetrafluoroethylene or Teflon) or PFA (perfluoroalkyl resins). Glass equipment may also be used. It will not be outside the scope of the invention to use an equivalent material. As other materials capable of being suitable for being in contact with the reaction medium, mention may also be made of graphite derivatives. Materials for filtration have to be compatible with the medium used. Fluorinated polymers (PTFE, PFA), loaded fluorinated polymers (Viton™), as well as polyesters (PET), polyurethanes, polypropylene, polyethylene, cotton, and other compatible materials can be used.
The process of the present invention may be carried out at atmospheric pressure or under reduced pressure. Preferably, the process of the present invention is carried out under reduced pressure. Performing the reaction under reduced pressure is preferable as it facilitates the removal of the chlorine atoms from the bis(chlorosulfonyl)imide of formula (II) during the process. There is no particular limitation on the pressure that can be applied to the process. The process may, for example, be carried out at a pressure between 0.5 bar and 3 bars, for example a pressure between 0.7 and 2.5 bars, or between 0.9 and 2 bars.
The process of the present invention may advantageously be carried out under inert atmosphere to avoid moisture contamination. The process of the present invention may for example be carried out under azote.
The process of the present invention may be carried out at a temperature of less than 150° C., for example less than 125° C., or less than 100° C. The process of the present invention may preferably be carried out at a temperature between the melting temperature (Tm(I)) of the onium salt of bis(fluorosulfonyl)imide of formula (I), for example KN(SO2F)2 and NH4N(SO2F)2 and 150° C.
The reaction time of the process of the present invention can be selected freely depending for example on the reactor used, the reaction temperature and the reactant quantities involved. It is preferable that the reaction time is from 1 to 12 hours, particularly from 1.5 to 10 hours or from 2 to 9 hours.
The process may comprise a step consisting in heating a quantity Qo of the salt of bis(fluorosulfonyl)imide (I) so that the salt (I) is in a molten state or a substantially molten state. In some embodiments, this step consists in heating a quantity Q0 of the salt of bis(fluorosulfonyl)imide (I) at a temperature Ta(° C.) equals to or higher than its melting point Tm(I), to produce a molten salt of bis(fluorosulfonyl)imide (I). The quantity Q0 of molten salt of bis(fluorosulfonyl)imide (I), in order words the minimal quantity of molten product used to perform the process, may not be less than 20 wt. % of the total weight of the reaction mixture when all the reactive materials have been added. For example, such quantity Qo may be at least 30 wt. %, at least 35 wt. %, at least 40 wt. %, at least 45 wt. %, at least 50 wt. %, at least 55 wt. %, at least 60 wt. %, at least 65 wt. %, at least 70 wt. %. Such quantity Q0 may be less than 95 wt. %, less than 90 wt. % or less than 85 wt. %. The total weigh of the reaction mixture when all the reactive materials have been added, may be calculated by adding the weights of all the reactants involved in the process plus the weight of the molten salt of bis(fluorosulfonyl)imide (I). According to an embodiment, the quantity Qo is 50±10 wt. % of the total weight of the reaction mixture when all the reactive materials have been added.
It is advantageous for the present invention to select the reaction conditions in such a way that conversion C at the end of the process is at least 95%, particularly preferably at least 98%, in particular at least 99%. For the purposes of the present invention, conversion C is the molar proportion of reactive groups that have been reacted, i.e. bis(chlorosulfonyl)imide (II) and fluorinating agent (III). Surprisingly, it has been found that the conversion of reactants (II) and (III) is very high in the process conditions described herein, despite the absence of any solvent or diluent.
In some preferred embodiments, the process is such that the conversion C is at least 95%, at least 98%, at least 99%, at least 99.5%, at least 99.9% or at least 99.99%.
The process of the present invention may further comprise cooling the reaction mixture to temperature Tc(° C.) of less than 80° C., for example less than 60° C.
The process of the present invention preferably further comprises filtering the reaction mixture. The step of filtration is in order to remove the reaction by-products and/or impurities. The reaction by-products and/or impurities may for example be X1CI and/or X1HF2 wherein X1 is K+, Na+or an onium cation as described above. If the fluorinating agent is NH4F for example, the reaction by-products and/or impurities may be NH4Cl and NH4HF2.
Filtration products (funnels, membranes, Nutsche or glass filters, dryers . . . ) are preferably used for the filtration.
According to the present invention, a pure or substantially pure salt of bis(fluorosulfonyl)imide of formula (I) is obtained at the end of the reaction in a molten form. While bis(fluorosulfonyl)imide of formula (I) may be maintained at a temperature such that it remains liquid, it may also be post-treated so that to be in a powder form, for example in a crystallized form. The bis(fluorosulfonyl)imide of formula (I), obtained form the process of the present invention may be used in its molten form or in a crystalized form. For example, the molten salt of bis(fluorosulfonyl)imide of formula (I) may be added to an organic solvent at a colder temperature, for example trifluoroethanol, and crystallized before further use. According to yet another embodiment, the salt (I) may be crystallized in the melt, at least partially, and then extracted or reused/recycled in a new reaction cycle.
The process of the present invention may also comprise additional steps of measuring and/or monitoring at least one of the following reaction parameters:
A second object of the present invention is a salt of bis(fluorosulfonyl)imide of formula (I):
[F—(SO2)—N−—(SO2)—F]nX1n+ (I)
wherein:
Such salt (I) may advantageously be obtained by the process described above.
The salt of bis(fluorosulfonyl)imide of formula (I) of the present invention may for example be in a molten state or in a crystallized form.
According to the present invention, the salt (I) is such that its average crystal length is advantageously at least 400 μm, for example at least 450 μm, at least 500 μm, at least 600 μm or even at least 700 μm. The salt of the prior art is around 300 μm, which means that the salt is not a crystal type.
Advantageously, due to the fact that no solvent is used in the process of the present invention, such salt is pure or substantially pure with no trace of solvent or with a very low amount of residual solvent. This is advantageous because the solvents that are usually used to prepare the salts (I) need to be removed after reaction in order to obtain an as pure as possible product. Indeed, only very pure products can be used for battery applications.
In some preferred embodiments, the amount of solvent in the salt of bis(fluorosulfonyl)imide of formula (I) is less than 100 ppm, for example less than 90 ppm, less than 80 ppm, less than 70 ppm, less than 60 ppm, less than 50 ppm, less than 40 ppm, less than 30 ppm, less than 20 ppm, less than 10 ppm, or even less than 1. This is an advantageous feature of the salt obtained by the process of the present invention. The remaining solvent content may be determined by GC (alternatively headspace GC).
The salt of bis(fluorosulfonyl)imide of formula (I) described here is obtained by a process comprising the fluorination of a bis(chlorosulfonyl)imide of formula (II):
Cl—(SO2)—NH—(SO2)—Cl (II) or salt thereof
with a fluorinating agent represented by formula (III):
X1n+(F−)n(HF)p
Such a salt of formula (I) may advantageously be obtained directly from the fluorination of bis(chlorosulfonyl)imide of formula (II), without any additional purification or separation steps.
The salt of bis(fluorosulfonyl)imide of formula (I) is preferably one of the following salts:
F—(SO2)—NK—(SO2)—F (Ia),
F—(SO2)—NNa—(SO2)—F (Ib), or
F—(SO2)—NNH4—(SO2)—F (Ic).
A step of filtration may be used in addition to the above-described process, in order to remove the reaction by-products and/or impurities. The reaction by-products and/or impurities may for example be X1n+Cl− and/or X1n+HF2− wherein X1 is K+, Na+or an onium cation as described above.
A preferred embodiment of the present invention is directed to an ammonium salt of bis(fluorosulfonyl)imide of formula (Ic):
F—(SO2)—NNH4—(SO2)—F (Ic)
In this preferred embodiment, the salt may contain at least one of the following impurities:
The impurities, such as NH4Cl and NH4HF2, may for example be present in the salt (Ic) in a residual amount of less than 1,000 ppm, less than 500 ppm, less than 200 ppm or less than 100 ppm, preferably less than 90 ppm. Such impurities may be present in the salt (Ic) in an amount of more than 1 ppm, for example more than 5 ppm or more than 10 ppm.
The impurities, such as OFSI and OSI, may for example be present in the salt (Ic) in a residual amount of less than 1,000 ppm, less than 500 ppm, less than 400 ppm or less than 300 ppm, preferably less than 250 ppm or even less than 200 ppm. Such impurities may be present in the salt (Ic) in an amount of more than 1 ppm, for example more than 5 ppm or more than 10 ppm.
The salts (I) of the present invention also preferably exhibit at least one of the following contents of chemical entities:
Fluoride and chloride contents may for example be measured by titration by argentometry using ion selective electrodes (or ISE). Sulfate content may alternatively be measured by ionic chromatography or by turbidimetry.
Elemental impurity content may for example be measured by ICP-AES (inductively coupled plasma); more specifically, Na content can be measured by AAS (atomic absorption spectroscopy).
A third object of the present invention is a process for preparing an alkali salt of bis(fluorosulfonyl)imide of formula (IV):
F—(SO2)—NX3—(SO2)—F (IV)
This process comprises the steps of:
According to the present invention, as described above, a pure or substantially pure salt of bis(fluorosulfonyl)imide of formula (I) is obtained. This means that, according to an embodiment, step (b) may be performed directly with the salt (I), for example in a molten form, as obtained according to step (a), for example without any further purification. Alternatively, the molten salt of bis(fluorosulfonyl)imide of formula (I) may be added to an organic solvent, for example trifluoroethanol, which may be cooler. In that case, it is expected that the salt (I) crystallize before performing step (b). According to yet another embodiment, the salt (I) may be crystallized in the melt, at least partially an then extracted or reused/recycled in a new reaction cycle.
A fourth object of the present invention is a salt of bis(fluorosulfonyl)imide of formula (IV):
F—(SO2)—NX3—(SO2)—F (IV)
wherein X3 represents Li or Cs, preferably Li.
Such salts (IV) may preferably be obtained by the process described above.
The salts (IV) of the present invention also preferably exhibit at least one of the following contents of chemical entities:
A fifth object of the present invention is directed to the use of the salt of bis(fluorosulfonyl)imide of formula (IV) in a battery electrolyte solution.
Should the disclosure of any patents, patent applications, and publications which are incorporated herein by reference conflict with the description of the present application to the extent that it may render a term unclear, the present description shall take precedence.
The invention will be now described in more detail with reference to the following examples, whose purpose is merely illustrative and not intended to limit the scope of the disclosure.
Under nitrogen, 63.5 g of NH4F (1.71 mol, 4.4 eq vs HCSI) was mixed with 250 g of NH4FSI (1.26 mol) and stirred for 1 hour at 90° C. Liquid HCSI was then added continuously to the reaction mixture at a rate of 40 g/h and up to 83.3 g (0.39 mol) using a feeding funnel with a heat belt. The stirring was continued for 12 hours. The temperature of the reaction was continuously monitored and kept below 100° C. The reaction mixture was then cooled to 60° C. in 1 hour. 320 g of TFE was then added to the mixture. The solid was isolated by filtration. The filtrated solution was then cooled to 10° C. in 2 hours. Crystals were isolated by filtration at 25° C., then washed with 160 g of fresh TFE. The solid was dried under vacuum at room temperature for 12 hours.
The product was then analysed.
The conversion was 87.6%, as measured by 19F NMR (FSI-).
Under nitrogen atmosphere, a solution of 6.9 g NH4FSI (0.35 mmol), as obtained form Example 1, was prepared in 60 g of Ethyl Methyl Carbonate (EMC). 14.6 g of solid LiOH·H2O (0.35 mmol) was added to the vessel at room temperature in 10 minutes. After 1 hour of stirring, the conversion of NH4+ ions (as measured by a NaOH titration) was greater than 90%. The medium was concentrated a first time under reduced pressure (P=20 mbar, T=0° C.). 120 mL of EMC was added and the concentration was performed a second time under the same conditions. The concentrated solution was dried under vacuum pressure at 30° C. for 24 hours. 5 g of a viscous transparent liquid was obtained. 19F NMR analysis indicated a purity above 99 wt. %. No other fluorinated species was detected.
| Number | Date | Country | Kind |
|---|---|---|---|
| 21305798.7 | Jun 2021 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2022/065529 | 6/8/2022 | WO |