Patent Application
20180354862
The present invention relates to the technical field of material preparation, and in particular, to a sound absorption material preparation method, a sound absorption material and a filling method thereof.
In pursuit of better sound quality, a speaker (SPK) or a speaker box (SPK BOX) has a higher and higher requirement for response frequency (f0). However, restricted by an increasingly thin and small structure and performance characteristics of a miniature speaker, it is required to add a sound absorption material inside the speaker to reduce the response frequency thereof. At present, commonly used sound absorption materials for speakers mainly comprise foamed foam, such as polyurethane and melamine, and non-foamed sound absorption materials, such as activated carbon and zeolite. The acoustic performance of the non-foamed sound absorption materials is better than that of the foamed sound absorption materials. The normal state of the non-foamed sound absorption materials is powder. Thus, considering the feasibility of quantification and process filling, the non-foamed sound absorption materials are prepared to particles first; then the particles are filled into a rear acoustic cavity of the speaker after being packaged by a polypropylene (PP) tray box with non-woven cloth, or non-woven cloth only; or the sound absorption material particles are directly filled into the rear acoustic cavity.
Currently, common granulation solutions of the non-foamed sound absorption materials (such as activated carbon and zeolite) in the industry adopt an extrusion method, a spray granulation method, a boiling granulation method or a disc rolling ball method. The particles obtained by the above method are relatively dense and small in specific surface area and pore volume, so that a mass transfer efficiency of an air flow inside the sound absorption particles is affected when the speaker works, and thus a sound absorption effect is greatly reduced. Although particles with relatively uniform particle sizes and internal physical structures can be obtained through an oil-ammonia column forming method, an oil column forming method or other equivalent methods, it is difficult to make full use of a filling space in the rear acoustic cavity of the speaker due to its complex structure and occupation of a large part of the rear acoustic cavity space by a packaging part of a sound absorber. As a result, the optimization effect of the acoustic performance of speaker products is limited.
An object of the present invention is to provide a new technical solution of a sound absorption material preparation method.
According to a first aspect of the present invention, there is provided a sound absorption material preparation method. The preparation method comprises the following steps: S1, preparing a non-foamed material slurry, and mixing the slurry uniformly; S2, producing a combustible material framework and a cover-shaped container according to a set structure, and placing the combustible material framework in the cover-shaped container; S3, forming the non-foamed material slurry in the cover-shaped container to form a wet formed body, and separating the wet formed body from the cover-shaped container; S4, drying the wet formed body to form a dry formed body; and S5, calcining the dried formed body, wherein the combustible material framework is burned off during the calcining step to form connected channels with a three-dimensional structure in the sound absorption material.
Preferably, the non-foamed material slurry comprises a non-foamed powder material, a binder and a pore-forming agent.
Preferably, the non-foamed powder material is one or more of natural zeolite powder, white carbon black, activated carbon powder and a molecular sieve.
Preferably, the binder is an organic silicone sol binder.
Preferably, the combustible material framework adopts an activated carbon fiber material.
Another object of the present invention is to provide a sound absorption material having an excellent mass transfer efficiency and sound absorption effect.
According to another aspect of the present invention, there is provided a sound absorption material prepared according to the preparation method provided by the present invention.
A yet another object of the present invention is to provide a sound absorption material having an excellent mass transfer efficiency and sound absorption effect.
According to a yet another aspect of the present invention, there is provided a sound absorption material made of a non-foamed material. The sound absorption material has a set space structure in which connected channels with a three-dimensional structure are formed.
Preferably, the specific surface area and the density of the sound absorption material are 150-450 m2/g and 0.3-0.7 g/cm3, respectively.
Preferably, pores are formed inside the sound absorption material, wherein the pore volume is 0.5-1.7 cm3/g, and the macropore diameter is 0.1-50 μm.
In addition, a yet another object of the present invention is to provide a new technical solution of a sound absorption material filling method.
According to yet another aspect of the present invention, there is provided a sound absorption material filling method, comprising the following steps: SS1, preparing a non-foamed material slurry, and mixing the slurry uniformly; SS2, producing a combustible material framework and a cover-shaped container according to the structure of a space to be filled, and placing the combustible material framework in the cover-shaped container; SS3, forming the non-foamed material slurry in the cover-shaped container to form a wet formed body, and separating the wet formed body from the cover-shaped container; SS4, drying the wet formed body to form a dry formed body; SS5, calcining the dried formed body to obtain a sound absorption material block capable of filling the space, wherein the combustible material framework is burned off during the calcining step to form connected channels with a three-dimensional structure in the sound absorption material block; and SS6, filling the sound absorption material block into the space to be filled.
The sound absorption material preparation method provided by the present invention is simple in operation and allows a set space structure, such as a rear acoustic cavity of a speaker, to be filled with the sound absorption material so as to maximally make use of the space of the rear acoustic cavity. As the combustible material framework is produced according to the set structure, the connected channels with a three-dimensional structure are formed inside the sound absorption material after the combustible material framework is burned off during the calcining step. A sound air flow can rapidly propagate in the connected channels with a three-dimensional structure, so that the mass transfer efficiency of the air flow generated when the speaker product works in the sound absorption material is improved, and the sound absorption area of the non-foamed sound absorption material is increased, thereby improving the sound absorption effect. In addition, the added pore-forming agent further enriches a microscopic pore structure of the sound absorption material, and friction and viscous resistance of air molecules in the sound air flow are increased, so that the sound absorption effect is improved. A sound absorber prepared from the sound absorption material relatively significantly improves the acoustic performance optimization debugging effect of the speaker product.
The sound absorption material provided by the present invention has a set space structure which can be designed according to the structure of a space to be filled. The connected channels with a three-dimensional structure are formed in the space structure, and the sound air flow rapidly propagates in the connected channels with a three-dimensional structure. Thus, the mass transfer efficiency of the air flow generated when the speaker product works in the sound absorption material is improved, and thus the sound absorption effect is improved. The sound absorption material also has a rich microscopic pore structure, and has the characteristics of large specific surface area and pore volume, so that the acoustic performance optimization debugging effect of the speaker product is relatively significantly improved.
The sound absorption material filling method provided by the present invention is simple in operation and high in reliability. The method allows the space to be filled, namely a rear acoustic cavity of a speaker, to be filled with the sound absorption material, so as to maximally make use of the space of the rear acoustic cavity. In addition, the connected channels with a three-dimensional structure are formed inside the sound absorption material, so that the mass transfer efficiency of the air flow generated when the speaker product works in the sound absorption material is improved, and thus the sound absorption effect is improved.
The inventor of the present invention finds that in the prior art, it is difficult to fully utilize a filling space in the rear acoustic cavity of the speaker due to its complicated structure and occupation of a large part of the rear acoustic cavity space by a packaging part of a sound absorber. In addition, an air flow channel of the sound absorption material in the prior art is simple, which affects the acoustic performance optimization effect of the speaker product. Therefore, the technical task to be achieved or the technical problem to be solved by the present invention is unintentional or unanticipated for those skilled in the art, and thus the present invention refers to a novel technical solution.
Further features of the present invention and advantages thereof will become apparent from the following detailed description of exemplary embodiments according to the present invention with reference to the accompanying drawings.
The accompanying drawings, which are incorporated in and constitute a part of the description, illustrate embodiments of the present invention and, together with the description thereof, serve to explain the principles of the present invention.
Description of the reference numerals: 1: combustible material framework; 2: cover-shaped container; and 4: connected channels with a three-dimensional structure.
Various exemplary embodiments of the present invention will now be described in detail with reference to the drawings. It should be noted that the relative arrangement of the components and steps, the numerical expressions, and numerical values set forth in these embodiments do not limit the scope of the present invention unless it is specifically stated otherwise.
The following description of at least one exemplary embodiment is merely illustrative in nature and is in no way intended to limit the invention, its application, or uses.
Techniques, methods and apparatus as known by one of ordinary skill in the relevant art may not be discussed in detail but are intended to be part of the description where appropriate.
In all of the examples illustrated and discussed herein, any specific values should be interpreted to be illustrative only and non-limiting. Thus, other examples of the exemplary embodiments could have different values.
Notice that similar reference numerals and letters refer to similar items in the following figures, and thus once an item is defined in one figure, it is possible that it need not be further discussed in the accompanying drawings.
The present embodiment provides a sound absorption material preparation method. Referring to
In step S1, a non-foamed material slurry is prepared and mixed uniformly. The non-foamed material slurry comprises a non-foamed powder material, a binder and a pore-forming agent. Of course, a template agent, a wet enhancing agent, a dispersant or surfactant, and the like may be added into the slurry during preparation according to actual needs to improve the quality of the slurry. The non-foamed powder material is one or more of natural zeolite powder, white carbon black, activated carbon powder and a molecular sieve. The binder is an organic silicone sol binder, and of course, may be selected from other binders. The prepared slurry should be mixed thoroughly. Alternatively, a quantitative dripping method, an atomization adding method or other equivalent methods are used to improve the uniformity of the slurry.
In step S2, referring to
In step S3, the non-foamed material slurry is formed in the cover-shaped container 2 to form a wet formed body, and the wet formed body is separated from the cover-shaped container 2. Alternatively, the forming method may be an extrusion method, a spray granulation method, a boiling granulation method, a disc rolling ball method, an oil-ammonia column forming method, or an oil column forming method, and of course, may be other equivalent forming methods, which will not be limited in the present invention. The wet formed body needs to be placed for a time after being formed to expel bubbles inside the body. The activated carbon fiber material has many pores into which the slurry will permeate to finally form a fibrous shape (not shown in the figures), and fine fibers mechanically vibrate to convert acoustic energy into thermal energy. Therefore, this structure further improves the sound absorption effect of the sound absorption material.
In step S4, the wet formed body is dried to form a dry formed body. Further, drying is performed in air or in an inert gas, wherein the drying temperature is 40-150° C., and the drying time is 0.5-96 hour(s). Those skilled in the art can easily understand that the lower the drying temperature is, the longer the drying time is; and vice versa.
In step S5, the dried formed body is roasted, and the combustible material framework 1 is burned off in the calcining process so as to form the connected channels with a three-dimensional structure 4 in the sound absorption material. Further, the calcining temperature is 120-850° C., the temperature rising speed is 20-120° C./h, and the calcining time is 0.5-96 hour(s). Those skilled in the art can easily understand that the lower the calcining temperature is, the longer the calcining time is; and vice versa. Referring to
The sound absorption material preparation method provided by the present invention is simple in operation and allows the space of the set structure, such as a rear acoustic cavity of a speaker, to be filled with the sound absorption material so as to maximally make use of the space of the rear acoustic cavity. As the combustible material framework 1 is produced according to the set structure, the connected channels with a three-dimensional structure 4 are formed inside the sound absorption material after the combustible material framework 1 is burned off during the calcining step. A sound air flow can rapidly propagate in the connected channels with a three-dimensional structure 4, so that the mass transfer efficiency of the air flow generated when the speaker product works in the sound absorption material is improved, and the sound absorption area of the non-foamed sound absorption material is increased, thereby improving the sound absorption effect. In addition, the added pore-forming agent further enriches the microscopic pore structure of the sound absorption material, and friction and viscous resistance of air molecules in the sound air flow are increased, so that the sound absorption effect is improved. A sound absorber prepared from the sound absorption material relatively significantly improves the acoustic performance optimization debugging effect of the speaker product.
The embodiment provides a sound absorption material applied to a rear acoustic cavity of a speaker. The sound absorption material is prepared by the preparation method provided by the present invention.
In particular, a non-foamed material slurry adopted in this embodiment comprises a non-foamed powder material, a binder and a pore-forming agent. A template agent, a wet enhancing agent, a dispersant or surfactant may be added into the slurry during preparation to improve the quality of the slurry. The non-foamed powder material may be natural zeolite powder, and of course, may be one or more of white carbon black, activated carbon powder and a molecular sieve. The binder is an organic silicone sol binder. The binder is added to increase the viscosity of the slurry so as to form spherical particles more conveniently. A person skilled in the art can set the mass ratio of the binder according to the type and the viscosity of the binder. The template agent plays a structural directing role. The combustible material framework 1 adopts an activated carbon fiber material. In the present embodiment, drying is performed in air at a drying temperature of 80° C. and with a drying time of 50 hours to obtain a qualified dry formed body. During calcining, the temperature is 500° C., the temperature rising speed is 80° C./h, and the calcining time is 60 hours. The activated carbon fiber material framework is burned off during calcining to form the connected channels with a three-dimensional structure 4. In this embodiment, the density, the specific surface area, the pore volume and the macropore diameter of an obtained sound absorption material formed body are 0.5 g/cm3, 280 m2/g, 1.3 cm3/g and 10 μm, respectively.
In another embodiment, drying is performed in an inert gas at a drying temperature of 40° C. and with a drying time of 96 hours to obtain a qualified dry formed body. During calcining, the temperature is 120° C., the temperature rising speed is 20° C./h, and the calcining time is 96 hours. The activated carbon fiber material framework is burned off during calcining to form the connected channels with a three-dimensional structure 4. The density, the specific surface area, the pore volume and the macropore diameter of an obtained sound absorption material formed body are 0.3 g/cm3, 150 m2/g, 0.5 cm3/g and 0.1 μm, respectively.
In a yet another embodiment, drying is performed in an inert gas at a drying temperature of 150° C. and with a drying time of 0.5 hour to obtain a qualified dry formed body. During calcining, the temperature is 850° C., the temperature rising speed is 120° C./h, and the calcining time is 0.5 hour. The activated carbon fiber material framework is burned off during calcining to form the connected channels with a three-dimensional structure 4. The density, the specific surface area, the pore volume and the macropore diameter of an obtained sound absorption material formed body are 0.7 g/cm3, 450 m2/g, 1.7 cm3/g and 50 μm, respectively.
Implementations not described in the present embodiment are the same as those described in Embodiment 1.
The connected channels with a three-dimensional structure 4 are formed inside the sound absorption material provided by the present embodiment, so that the mass transfer efficiency of the air flow generated when the speaker product works in the sound absorption material is improved, and thus the sound absorption effect is improved. The sound absorption material also has a rich microscopic pore structure, and has the characteristics of large specific surface area and pore volume, so that the acoustic performance optimization debugging effect of the speaker product is relatively significantly improved.
The present embodiment provides a sound absorption material made of a non-foamed material. The acoustic performance of the non-foamed material is better than that of a foamed material. The sound absorption material has a set space structure in which connected channels with a three-dimensional structure 4 are formed. In particular, the specific surface area and the density of the sound absorption material are 150-450 m2/g and 0.3-0.7 g/cm3, respectively. Further, pores are formed inside the sound absorption material, wherein the pore volume is 0.5-1.7 cm3/g and the macropore diameter is 0.1-50 μm.
The connected channels with a three-dimensional structure 4 are formed inside the sound absorption material provided by the present embodiment, so that the mass transfer efficiency of the air flow generated when the speaker product works in the sound absorption material is improved, and thus the sound absorption effect is improved. The sound absorption material also has a rich microscopic pore structure, and has the characteristics of large specific surface area and pore volume, so that the acoustic performance optimization debugging effect of the speaker product is relatively significantly improved.
The present embodiment provides a sound absorption material filling method. A space to be filled provided by this embodiment is a rear acoustic cavity of a speaker. Referring to
In step SS1, a non-foamed material slurry is prepared and mixed uniformly. The non-foamed material slurry comprises a non-foamed powder material, a binder and a pore-forming agent. Of course, a template agent, a lubrication-enhancing agent, a dispersant or surfactant, and the like may be added into the slurry during preparation according to actual needs. The non-foamed powder material is one or more of natural zeolite powder, white carbon black, activated carbon powder and a molecular sieve. The prepared slurry should be mixed thoroughly. The binder is an organic silicone sol binder, and of course, may be selected from other binders.
In step SS2, a combustible material framework 1 and a cover-shaped container 2 are produced according to the structure of the rear acoustic cavity, and the combustible material framework 1 is placed in the cover-shaped container 2. For example, the set structure is the rear acoustic cavity of the speaker, and the cover-shaped container 2 and the combustible material framework 1 are produced according to the structure of the rear acoustic cavity. The combustible material framework 1 is burned off in a calcining step so as to form connected channels with a three-dimensional structure 4 inside a formed sound absorption material. Therefore, a sound air flow can flow out rapidly, and thus the mass transfer efficiency and the sound absorption effect are improved. The combustible material framework 1 adopts an activated carbon fiber material, and of course, may also adopt another combustible material.
In step SS3, the non-foamed material slurry is formed in the cover-shaped container 2 to form a wet formed body, and then the wet formed body is separated from the cover-shaped container 2. Alternatively, the forming method may be an extrusion method, a spray granulation method, a boiling granulation method, a disc rolling ball method, an oil-ammonia column forming method or an oil column forming method, and of course, may also be other equivalent forming methods. The wet formed body needs to be placed for a time after being formed to expel bubbles inside the body. The activated carbon fiber material has many pores into which the slurry will permeate to finally form a fibrous shape (not shown in the figures), and fine fibers mechanically vibrate to convert acoustic energy into thermal energy. Therefore, this structure further improves the sound absorption effect of the sound absorption material.
In step SS4, the wet formed body is dried to form a dry formed body. Further, drying is performed in air or in an inert gas, wherein the drying temperature is 40-150° C., and the drying time is 0.5-96 hour(s).
In step SS5, the dried formed body is roasted, wherein the combustible material framework 1 is burned off in the calcining process so as to form the connected channels with a three-dimensional structure 4 in the sound absorption material. Further, the calcining temperature is 120-850° C., the temperature rising speed is 20-120° C./h, and the calcining time is 0.5-96 hour(s). A sound absorption material block having the connected channels with a three-dimensional structure 4 therein and having the set structure is finally formed.
In step SS6, the sound absorption material block is filled into the space to be filled.
The sound absorption material filling method provided by the present invention is simple in operation and high in reliability. As there is no need of polypropylene (PP) tray box or non-woven cloth for packaging, the space to be filled, namely the rear acoustic cavity of the speaker, will be filled with the sound absorption material so as to maximally make use of the space of the rear acoustic cavity. In addition, the connected channels with a three-dimensional structure 4 are formed inside the sound absorption material. Thus, the mass transfer efficiency of the air flow generated when the speaker product works in the sound absorption material is improved, and the sound absorption area of the non-foamed sound absorption material is increased, thereby improving the sound absorption effect.
Although some specific embodiments of the present invention have been demonstrated in detail with examples, it should be understood by a person skilled in the art that the above examples are only intended to be illustrative but not to limit the scope of the present invention. It should be understood by those skilled in the art that the above embodiments can be modified without departing from the scope and spirit of the present invention. The scope of the present invention is defined by the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201510560859.2 | Sep 2015 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2015/095003 | 11/19/2015 | WO | 00 |