Patent Application
20180330709
This relates to the field of acoustics and, more particularly, to sound attenuating materials.
Building board, a widely used building construction material, is commonly referred to as drywall, plasterboard, or wallboard. It is used to form the interior walls of buildings, exterior sheathing for weather protection, and interior facing for structures such as stairwells, elevator shafts, and ductwork.
Gypsum board is a popular form of building board. Gypsum building boards are typically made of a cementitious gypsum slurry sandwiched between a pair of fibrous or paper liners. Gypsum slurry is a semi-hydrous form of calcium sulfate. Types of gypsum boards include: (1) paper lined gypsum boards, (2) glass-reinforced gypsum (“GRG”) boards, and (3) embedded glass-reinforced gypsum (“EGRG”) boards.
Conventional building boards provide at least some degree of sound attenuation, but not enough in many circumstances. A wall made of wood studs with a single layer of ½ inch drywall on each side has a sound transmission class (“STC”) rating of 33. Adding fiberglass insulation only raises STC rating to 36. Within this range, loud speech is audible across the wall. Loud speech is not audible at STC=45. Very loud sounds, such as loud music, are inaudible at STC=50. Most sounds are inaudible when STC>60.
Specialized soundproofing wallboards have been developed that include soundproofing materials. One of them is called SILENTFX® (CertainTeed Gypsum, Inc., Malvern, Pa. USA). Walls including SILENTFX® wallboards are reported to have STC=57. Although this is effective, there is still a need for new sound attenuation materials that might attenuate even more sound, especially at frequencies below 125 Hz not normally covered by STC. This may allow soundproofing wallboards to be made of less material than conventional soundproofing wallboards. Such a material could also be used for other acoustic applications besides building boards.
It has been discovered that metal-organic framework materials (MOFs) attenuate sound in the audible frequency range. MOFs are, therefore, useful to dampen sound and to make sound-proofing or other acoustical products.
In one aspect, a method of dampening sound includes positioning a sound attenuation material along a sound travel pathway for attenuating sound waves that travel along the sound travel pathway. The sound attenuation material includes a metal-organic framework material.
Some examples of the sound attenuation material include a wallboard, an acoustic tile, and/or a coating.
Some examples of the metal-organic framework material include aluminum terephthalate, iron-1,3,5-benzene tricarboxylate, copper-1,3,5-benzene tricarboxylate, nickel-2,5-dihydroxyterephthlate, aluminum glutarate, and/or aluminum adipate.
The method may further include a substrate with which the sound attenuation material is in contact and the substrate and sound attenuation material are arranged in adjacent substantially parallel layers. Gypsum is one example of such a substrate.
The metal-organic framework material may be distributed throughout a cementitious wallboard material. The cementitious wallboard material may include gypsum.
The sound attenuation material may be part of a building wallboard.
The sound attenuation material may be part of a building wallboard where the building wallboard includes gypsum and the metal-organic framework material has a density of 0.1 g/cm3 to 0.9 g/cm3.
A compressed pellet of the metal-organic framework material may have a transmission loss of at least 1 dB/mm.
In another aspect, a building construction product includes a building construction substrate having a sound attenuation material in contact therewith. The sound attenuation material includes metal-organic framework material effective for attenuating audible frequency sound.
Some examples of the building construction substrate include a wallboard, an acoustic tile, and/or a coating.
Some examples of the metal-organic framework material include aluminum terephthalate, iron-1,3,5-benzene tricarboxylate, copper-1,3,5-benzene tricarboxylate, nickel-2,5-dihydroxyterephthlate, aluminum glutarate, and/or aluminum adipate.
The substrate and sound attenuation material may be arranged in adjacent substantially parallel layers.
The substrate may include gypsum.
The substrate may be a cementitious wallboard material. The cementitious wallboard material may include gypsum.
The sound attenuation material may be part of a building wallboard.
The sound attenuation material may be part of a building wallboard where the building wallboard includes gypsum and the metal-organic framework material has a density of 0.1 g/cm3 to 0.9 g/cm3.
A compressed pellet of the metal-organic framework material may have a transmission loss of at least 1 dB/mm.
In yet another aspect, a building panel includes a pair of planar sheets of panel material defining a pair of substantially parallel planes, a cementitious material layer positioned between the planar sheets, and a sound attenuation material positioned between the planar sheets or over at least one of the planar sheets. The sound attenuation material includes a metal-organic framework material that attenuates audible frequency sound.
Some examples of the metal-organic framework material include aluminum terephthalate, iron-1,3,5-benzene tricarboxylate, copper-1,3,5-benzene tricarboxylate, nickel-2,5-dihydroxyterephthlate, aluminum glutarate, and/or aluminum adipate.
The cementitious material layer may include gypsum.
The sound attenuation material may form a layer between the planar sheets that is substantially parallel to the cementitious material layer.
The metal-organic framework material may be distributed throughout the cementitious material layer.
The pair of planar sheets of panel material may be attached to the cementitious material layer on opposed sides of the cementitious material layer and the cementitious material layer may include gypsum and the metal-organic framework material may have a density of 0.1 g/cm3 to 0.9 g/cm3.
A compressed pellet of the metal-organic framework material may have a transmission loss of at least 1 dB/mm.
This disclosure describes examples of aspects and embodiments, but not all possible aspects embodiments of the sound attenuation materials, acoustic attenuation products, building panels, or related methods. Where a particular feature is disclosed in the context of a particular aspect or embodiment, that feature can also be used, to the extent possible, in combination with and/or in the context of other aspects and embodiments. The sound attenuation materials, acoustic attenuation products, building panels, and related methods may take many different forms and should not be construed as limited to only the aspects and embodiments described here.
A sound attenuation material aspect is first described. The sound attenuation material includes at least one MOF material, which is effective to attenuate sound waves. As discussed in the examples section, MOFs attenuate sound in the audible frequency range.
The acoustic attenuation properties of a material can be measured using conventional techniques. Acoustic attenuation may be expressed as the transmission loss of a sound passing through the material at a given frequency or absorption of sound by a material at a given frequency. Typical units for transmission loss are dB or dB/mm, where mm represents the thickness of the material in millimeters.
Audible frequencies are audible to the average human. They typically range from about 20 Hz to about 20 kHz. The sound attenuation material attenuates sound across at least a part of this frequency range. It is capable of attenuating sound incident on the material and/or passing through the material. Acoustic attenuation may occur by sound absorption, sound insulation, or another sound attenuation mechanism.
The sound attenuation properties of a MOF material may be evaluated by measuring the transmission loss through a compressed pellet of the MOF material. The compressed pellet of the MOF material may have a transmission loss of at least 1 dB/mm for sound having a frequency of 800 Hz, for example.
The sound attenuation material may be constructed in many different ways. It may, for example, be constructed in the form of a coating, a wallboard, or an acoustic tile. It may also be part of an audio speaker or an acoustic transmission line. There are many other possible applications for the sound attenuation material.
When the sound attenuation material is constructed as a liquid coating, the MOF material may be blended with conventional coating materials such as polymers used in building construction. The coating may be applied to a substrate by spraying, rolling, brushing, caulking, or any other conventional coating application technique. The coating may be, for example, a paint, adhesive, or acoustic caulk, or the like.
When the sound attenuation material is constructed as part of a wallboard, the MOF material may be blended with conventional wallboard materials that are then bound together with a binder. The binder is a substance that, when dried, causes the panel materials to stick together to form the rigid structure. Examples of binders that may be suitable include polyvinyl alcohol. The sound attenuation material may also be applied as a coating to the wallboard.
In another example, the sound attenuation material may be compressed together with sufficient force to form a rigid panel with or without a binder.
The MOF materials may be employed in crystalline, polycrystalline, powder, pellet, extrudate, bead and/or monolith form. There may also be other acoustic applications for MOF materials in other forms.
A MOF material is a coordination solid with organic ligands bonded to one or metal ions. They typically include metal ions or metal ion-containing clusters coordinated together with organic ligands or linkers to form one, two, or three-dimensional coordination structures with pores.
MOF materials that may be used as part of a sound attenuation material often have low-densities and high-surface areas. Some suitable MOFs have a density of 0.1 g/cm3 to 0.9 g/cm3. A typical surface area of a MOF is 1 m2/g to 10,000 m2/g.
The list of possible MOFs that may be used in the sound attenuation material is extensive because there are many thousands of different combinations of metal ions and organic linkers that researchers have used to make MOFs. Not all of the possible MOFs that may be used are described in this disclosure.
It is to be understood that, in general, a MOF effective for attenuating audible sound may be suitable for use in the sound attenuation material, regardless of whether the MOF is listed or discussed here.
As mentioned above, MOFs are made of metal ions and organic linkers. Some of the metal ions used to make MOFs include ions of the metals listed in Table 1. Some of the organic linkers that may be used are listed in Table 2.
Rather than referring to MOFs by their chemical names, MOFs are often recognized by shorthand names developed by MOF researchers or their institutions. The shorthand name is essentially a code that helps identify the metal ion(s) and linker(s). Table 3 lists the shorthand names for a few examples of MOFs, some of which are commercially available. Table 4 provides surface area and pore volume data for some MOF examples. Four MOFs are now described in more detail.
MIL-53 (Al) is aluminum terephthalate and is commercially available from Sigma Aldrich under the name BASOLITE A100. MIL-53 (Al) has a reported surface area of 1,100-1,500 m2/g and a density of 0.4 g/cm3.
Fe-BTC is iron-1,3,5-benzene tricarboxylate and is commercially available from Sigma Aldrich under the name BASOLITE F300. Fe-BTC has a reported surface area of 1,300-1,600 m2/g and a density of 0.16-0.35 g/cm3.
Cu-BTC is copper-1,3,5-benzene tricarboxylate and is commercially available from Sigma Aldrich under the name BASOLITE C300. Fe-BTC has a reported surface area of 1,500-2,100 m2/g and a density of 0.35 g/cm3.
Ni-DHTA, also called MOF-74-Ni, is formally nickel-2,5-dihydroxyterephthalate.
A procedure for making Ni-DHTA was reported by Dietzel et al., in Journal of Materials Chemistry, Vol. 19, pages 7362-7370 (2009). To a fresh teflon container was added 2,5-dihydroxyterephthalic acid (1.486 g, 7.5 mmol) followed by THF (25 mL) and a solution of nickel acetate tetrahydrate (3.733 g, 15 mmol) in water (25 mL). The reaction mixture was sonicated for 2 min and then was placed in an autoclave, heated at 100 C for 24 h. Once the reaction mixture was cooled after heating for 24 h, the yellowish-brown product was separated by high speed centrifugation and washed with water (3 times) and by methanol (3 times) to remove any unreacted starting materials. The product was soaked in methanol for 24 h before exchanging the used methanol with fresh methanol. Substantially pure NiDHTA was obtained after 3 solvent exchanges.
The linkers of many MOFs are short, relatively inflexible or rigid, organic ligands such as terephthalic acid, 1,3,5-benzene tricarboxylate, terephthalate, and 2,5 dihydroxyterephthalate. As shown in the Examples section, however, it was discovered that the flexibility of linker ligands affects the acoustic properties of the MOF. Consequently, linker ligands that are relatively flexible may be used to improve the acoustic attenuation properties of MOFs. Examples of some flexible ligands are shown in
Ligand exchange synthesis techniques may be used to exchange the original rigid ligand in a MOF with a more flexible ligand. A useful ligand exchange technique, called “post synthesis ligand exchange” is described in Chem. Eur. J, Vol. 20, pgs. 426-34 (2014), which is incorporated by reference in its entirety. This technique produces MOF sonocrystals.
The synthesis of a MOF with a flexible ligand is illustrated by the reaction scheme in
Because of their different structures, MOF materials have different sound attenuation properties. The transmission loss of sound through a given MOF-containing sound attenuation material depends on the frequency of the sound. Some MOF materials exhibit greater sound attenuation at lower frequencies than at higher frequencies, whereas, the reverse is true for others. This means that sound attenuation properties of the sound attenuation material can be tuned by selecting MOF materials that attenuate sound to a desired degree within a given frequency range. If one desires to attenuate higher frequency sounds, it would be desirable to use a MOF material with favorable sound attenuation at higher frequencies. Mixtures of MOF materials with different sound attenuation properties can be used to obtain good sound attenuation across a desired part of the audible frequency spectrum.
Low frequency sounds such as bass notes and human voices typically have a frequency of about 2 kHz and below. Conventional sound attenuation materials are marginally effective at dampening these low frequency counds. MOFS, however, are particularly advantageous because they are effective for attenuating low frequency sounds.
A method of dampening sound using the sound attenuation material is illustrated in
The sound attenuation material 20 may be positioned along the sound travel pathway by placing it so that the sound is incident on the sound attenuation material 20. The positioning mechanism will vary depending on the application for which the sound attenuation material 20 is used. Several different positioning mechanisms are described herein.
The sound attenuation material is now described in connection with making building construction products, such as wallboards, acoustic tiles, and coatings.
Referring to
The acoustic attenuation substrate 102 may be made, for example, of a substrate material used to make wallboards, such as cementitious materials, including but not limited to plaster, gypsum, or the like. A wallboard itself may serve as the substrate 102 in certain examples, such as when the sound attenuation material 104 is a wallboard coating.
In other examples, the substrate 102 may be an internal panel or layer of a wallboard. In yet other examples, the substrate 102 may be a fibrous mat or paper liner that supports an exterior of a wallboard.
In the example shown in
A different example of an acoustic attenuation product 100b, is shown in
These examples of the acoustic attenuation product, among other possible examples, may be used as a component of a building panel, such as a wallboard or the like.
The building panels 200a, 200b may be adapted to form conventional gypsum-type wallboards. In that case, the substrate 102 may be a cementitious material such as gypsum and the panel material 106 is a thin, flexible sheet of paper, fabric, fibrous mat, or the like.
The conventional construction of different types of gypsum boards is known. A gypsum board typically includes a core of calcium sulfate dihydrate that is sandwiched between opposing paper sheets. This core is initially deposited in the form of a slurry of calcium sulfate hemihydrate (CaSO4.½H2O) and water. Once the slurry is deposited, it is rehydrated to form gypsum.
Materials may be combined with the gypsum core to modify its properties. One such material is starch. Starch can be added prior to rehydration. Starch functions as a binder within set gypsum and yields boards with higher compressive and flexural strength. It also strengthens the edges of the resulting board and improves the paper liner's bond to the core.
The gypsum core may include a plurality of internal voids to reduce the overall weight of the board. One example of a technique for achieving this is described in U.S. Pat. No. 6,706,128 to Sethuraman. Sethuraman discloses a method for adding air bubbles of different relative stabilities, whereby the air bubbles do not rupture before the slurry sets sufficiently to prevent the slurry from filing the void spaces left behind by ruptured bubbles. The result is a gypsum board with internal voids and with reduced weight.
The acoustic attenuation products may be used to at least partially soundproof a room. Referring to
A corresponding method aspect includes forming a wall of a room of a building by positioning a building panel at a boundary of the room. The building panel includes the sound attenuation material. The sound attenuation material includes at least one metal-organic framework material.
The sound attenuation material 104 may be incorporated into an acoustic panel. An acoustic panel is a sound dampening wall, ceiling, or floor panel that is used to dampen sound. Acoustic panels include items such as ceiling tiles, floor tiles, and wall tiles. They may be mounted onto a wall, floor, or ceiling. In this context the substrate 102 of
The sound attenuation material 104 may be incorporated into a coating. Coatings include materials such as paints, adhesives, caulks, or the like. In this context, the coating is illustrated by
These examples show that MOFs attenuate sound in the audible frequency range. The scope of the possible embodiments is not limited to what these examples teach.
Preparation of MOF Sound Attenuation Material.
MOF-containing sound attenuation materials were prepared by making compressed disc-shaped pellets of MOF samples. MOF crystals were pulverized to a fine powder with a mortar and pestle. The powder was loaded into a die and pressure of 6-7 tons was applied to the powder for about 1 minute to compress the powder particles together. The diameter of each pellet was about 100 mm and the thickness was about 2 to 3 mm.
The mechanical integrity of the pellets was enhanced in some samples by mixing several drops of 5% polyvinyl alcohol (PVA) with the powder prior to compression. In these cases 35-40 tons of pressure was applied without imparting substantial defects to the pellets.
Sound Attenuation Measurements.
The sound attenuation properties of different MOFs were measured in an acoustic impedance tube.
Effect of the Binder.
The terephthalate ligand of MIL-53(Al) was substituted with the two flexible ligands glutarate and ad-pate. In
MIL53(Al)-AA and MIL53(Al)-GA were prepared by the following procedure. 500 mg of MIL-53 was mixed with 100-375 mg of the flexible ligands and of 25 ml THF was added to the mixture. The mixture was sonicated for one minute. The mixture was then transferred to a Teflon autoclave, which was tightly sealed and heated to 120° C. for 24 h. After cooling, the resulting solids were separated by centrifugation. The suspension was centrifuged and the solid obtained was thoroughly washed with dimethyl formamide (DMF, 10 mL) two times and with THF (10 mL, 2 times) to remove unreacted flexible ligand from the reaction mixture. The solid obtained was dried and its identity was confirmed with powder X-ray diffraction, water sorption, and BET surface area measurements.
Wallboard samples and MOF pellets were evaluated for sound attenuation properties. EASILITE® wallboard samples were combined with MOF pellets. The composite was held together by compression and without an adhesive. The transmission loss measurement results for different configurations of the MOF pellet relative to the incident acoustic wave are shown in
The legend in each of the graphs indicates how the pellets were configured. MOF-WALLBOARD-WALLBOARD means that the MOF pellet was positioned closer to the sound source. WALLBOARD-MOF-WALLBOARD means that the MOF pellet was positioned between two EASILITE® pellets. This example can be illustrated by