Soy-modified resins for bonding wood

Abstract

Engineered wood products and binder compositions are provided. In preferred embodiments, the engineered wood products include wax. Methods are also provided for formulating binders for wood comprising unmodified soy flour and synthetic adhesives. The soy-based formulations are prepared by mixing unmodified soy flour with the synthetic adhesive prior to application to the wood or by adding them sequentially to the wood. The present invention provides adequate bonding at reduced cost.

Description

FIELD OF THE INVENTION

The present invention generally relates to the art of formulating binders for engineered wood products. In particular, the binder compositions include unmodified soy product and a synthetic resin.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1A shows the effect of PF resin substitution by unmodified soy flour in a liquid formulation on flexural strength.

FIG. 1B shows the effect of PF resin substitution by unmodified soy flour in a liquid formulation on internal bond.

FIG. 2 shows a comparison of strength of varying levels of soy substitution with PF.

FIG. 3A shows a comparison of the flexural strength of PF versus 5% soy/PF as a shear coating on loblolly pine lap.

FIG. 3B shows a comparison of the flexural modulus of PF versus 5% soy/PF as a shear coating on loblolly pine lap.

FIG. 4A shows a comparison of the flexural strength of PF versus 5% soy/PF as binder for OSB wood panels.

FIG. 4B shows a comparison of the flexural modulus of PF versus 5% soy/PF as binder for OSB wood panels.

FIG. 5A shows a comparison of the flexural strength of OSB wood panels made with a PF and 5% soy/PF binder with a target density of 30 lbs/ft³.

FIG. 5B shows a comparison of the flexural modulus of OSB wood panels made with a PF and 5% soy/PF binder with a target density of 30 lbs/ft³.

FIG. 6 is a microscope image at 10× magnification and illustrates the arrangement of soy particles and PF resin particles in a mixture.

FIG. 7A shows the effect of various mixtures of MDI resin and soy flour on flexural strength.

FIG. 7B shows the effect of various mixtures of MDI resin and soy flour on wet modulus of elasticity.

FIG. 7C shows the effect of various mixtures of MDI resin and soy flour on wet flexural strength.

FIG. 7D shows the effect of various mixtures of MDI resin and soy flour on wet modulus of elasticity.

FIG. 7E shows the effect of various mixtures of MDI resin and soy flour on water absorption.

FIG. 7F shows the effect of various mixtures of MDI resin and soy flour on thickness swell.

FIG. 7G shows the effect of various mixtures of MDI resin and soy flour on internal bond.

BACKGROUND OF THE INVENTION

Binders for bonding wood are used in the manufacture of engineered wood products such as oriented strand board (OSB), flake board, particleboard, veneer, and medium density fiberboard among other products in which lignocellulosic substrate is bonded by a synthetic binder. The cost of the binders is a very significant fraction of the cost of the process or product. Means to decrease the cost of the binder, e.g. by including less expensive components would reduce the cost of the wood product. Moreover, adhesive formulations comprising a combination of urea and formaldehyde structures or a combination of phenol and formaldehyde structures lead to the release of formaldehyde, a regulated chemical designated by the US National Toxicology Program as “known to be a human carcinogen.” Reducing the UF and PF levels in their associated formulations by partially substituting a component that does not release formaldehyde would reduce toxic emissions from the wood product, which would be beneficial both in the manufacturing environment and, where applicable, to the quality of indoor air in contact with the wood product. Substituting synthetic resin with a cheaper alternative has been the subject of much research but is generally unsuccessful from a cost:benefit basis as the engineered wood has lacked the desired functional properties. Accordingly, there is a need for a relatively inexpensive component or components that are compatible with existing binder formulation and which can be mixed therein to reduce the cost of the overall formulation and can also reduce formaldehyde emissions during the manufacture and use of the product board.

Attempts have been made to use alternative adhesives for binder compositions. For example, animal based materials, milk-based proteins, and certain types of vegetable protein have been used for binder compositions. However, such products have lacked the desired product features, including, durability, water resistance, and strength. Distinctions exist with respect to the vegetable proteins previously used as they have required the modification of vegetable protein by copolymerizing the protein.

This disclosure reveals an unexpected and very useful finding whereby the partial substitution of synthetic resin by unmodified soy product reduces the cost of the overall resin formulation while reducing toxic emissions and maintaining or increasing desired product properties.

The use of binders based on soy protein isolates has been disclosed by Lorenz et al. (2015), Mo et al. (2003), Hettiarachchy et al. (1995), Qi et al (2011), Dastidar and Netravali (2013) and Li et al (2009). Soy isolates are components of soy flour, and their extraction from soy flour entails significant processing which adds to cost. As a result, the soy isolates are significantly more expensive than unmodified soy flour. The teachings of the present invention are patentably different from these prior art disclosures because unmodified soy product is used, and the expensive step of isolating soy isolates from soy flour is avoided.

The use of soy flour cross-linked with PF resin has been disclosed in several applications, e.g. by Yang et al. (2006), Lorenz et al (2005), Hse and Lin (2005), Kuo et al (2003), Schwarzkopf (2010) and Huang (2008). Zhang et al. (2014) have disclosed binder formulations containing soy flour in combination with cross-linking agents such as triethanolamine. Resin formulations that include soy flour that is pre-hydrolyzed, cross-linked and otherwise derivatized have been reported. The use of soy flour cross-linked to PF resin or its precursors has been disclosed by Yang et al (2006), Wescott and Frihart (2004), and Lorenz et al (2005). The use of pre-hydrolyzed soy flour in combination with other components has been disclosed by Hse et al. (2000), Huang and Li (2008) and Wescott and Frihart (U.S. Pat. No. 7,345,136). Wescott and Frihart (Canadian patent 2,658,262) have disclosed the art of denaturing soy flour with urea and combining the denatured product with other components for use as a binder.

The teachings of the present inventions are patentably different from this art as the present inventions provide for unmodified soy product to be used directly with synthetic resin without need for expensive pre-application treatments such as crosslinking with other agents. Additionally, in some embodiments the present inventions can provide binder compositions with reduced expense in materials and reduced expense in production of engineered wood products. A further benefit of some embodiments of the present inventions include increased strength in the engineered wood products.

Accordingly, an object of the present invention is to provide binder compositions including soy products.

An additional object of the invention is to reduce the cost of binder material and reduce the amount of hazardous chemicals in the binder.

Still a further object of the invention is to reduce costs in the manufacturing processes for engineered wood products.

Yet another object of the invention is increase the strength in the engineered wood products.

BRIEF SUMMARY OF THE PREFERRED EMBODIMENTS

Engineered wood products and methods of preparing the same are provided herein according to the invention. Embodiments of the engineered wood products include lignocellulosic material and a binder composition, wherein the binder composition comprises unmodified soy product and a synthetic resin.

The engineered wood products of the invention can be prepared by mixing a binder composition with lignocellulosic material to form a mixture, forming the mixture into a mat, and pressing the mat while simultaneously heating the mat to form a pressed wood composite. The binder material includes unmodified soy product and synthetic resin. In an embodiment, the soy product and the synthetic resin are added separately to the lignocellulosic material, which is formed in a mat then heat-pressed.

While multiple embodiments are disclosed, still other embodiments of the present invention will become apparent to those skilled in the art from the following detailed description, which shows and describes illustrative embodiments of the invention. Accordingly, the drawings and detailed description are to be regarded as illustrative in nature and not restrictive.

DESCRIPTION OF PREFERRED EMBODIMENTS

The present invention relates to engineered wood products, including in particular binders for engineered wood products. The invention also relates to methods of making the engineered wood products. The methods and engineered wood products have many advantages over existing engineered wood products and their methods of manufacture.

The embodiments of this invention are not limited to particular engineered wood products or uses for the engineered wood products, which can vary and are understood by skilled artisans. It is further to be understood that all terminology used herein is for the purpose of describing particular embodiments only, and is not intended to be limiting in any manner or scope. For example, as used in this specification and the appended claims, the singular forms “a,” “an” and “the” can include plural referents unless the content clearly indicates otherwise. Further, all units, prefixes, and symbols may be denoted in its SI accepted form.

Numeric ranges recited within the specification are inclusive of the numbers defining the range and include each integer and fraction within the defined range. Throughout this disclosure, various aspects of this invention are presented in a range format. It should be understood that the description in range format is merely for convenience and brevity and should not be construed as an inflexible limitation on the scope of the invention. Accordingly, the description of a range should be considered to have specifically disclosed all the possible sub-ranges as well as individual numerical values within that range. For example, description of a range such as from 1 to 6 should be considered to have specifically disclosed sub-ranges such as from 1 to 3, from 1 to 4, from 1 to 5, from 2 to 4, from 2 to 6, from 3 to 6 etc., as well as individual numbers within that range, for example, 1, 2¼, 3, 4½, 5, and 6. This applies regardless of the breadth of the range.

Definitions

So that the present invention may be more readily understood, certain terms are first defined. Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which embodiments of the invention pertain. Many methods and materials similar, modified, or equivalent to those described herein can be used in the practice of the embodiments of the present invention without undue experimentation, the preferred materials and methods are described herein. In describing and claiming the embodiments of the present invention, the following terminology will be used in accordance with the definitions set out below.

The term “about,” as used herein, refers to variation in the numerical quantity that can occur, for example, through typical measuring techniques and equipment, with respect to any quantifiable variable, including, but not limited to, mass, volume, time, distance, strength, and modulus. Further, given solid and liquid handling procedures used in the real world, there is certain inadvertent error and variation that is likely through differences in the manufacture, source, or purity of the ingredients used to make the compositions or carry out the methods and the like. Whether or not modified by the term “about,” the claims include equivalents to the quantities.

The terms “engineered wood product,” “wood-containing composite,” and “pressed wood composite,” refer to wood-containing materials, including, but not limited to, chipboard, fiber board, flake board, laminated-strand lumber, oriented strand board (OSB), parallel-strand lumber, particle board, plywood, veneer, and wafer board. The term “fiber board” includes fiber board of any density, including, but not limited to medium density fiberboard and high density fiberboard.

The term “lignocellulosic material” as used herein refers to pieces of wood used to make engineered wood products and includes, but is not limited to, wood strands, wood particles, wood plies, wood fibers, and wood chips.

The term “MDI” is defined as resins prepared from methylene diphenyl di-isocyanate.

The term “PF” is defined as resins prepared from phenol and formaldehyde components.

The term “synthetic resin” is defined herein as a resin of non-biological origin prepared by polymerization of monomers of synthetic, typically hydrocarbon-based, monomers. Examples are PF, UF and MDI.

The term “UF” is defined as resins prepared from urea and formaldehyde components.

The term “soy product” refers to soy flour and/or soy meal, including their unmodified forms and mixtures thereof.

The term “unmodified soy flour” describes soy flour that has not been modified by functionalization, polymerization, copolymerization, cross-linking, or otherwise derivatized.

The term “unmodified soy meal” describes soy meal that has not been modified by functionalization, polymerization, copolymerization, cross-linking, or otherwise derivatized.

Binder Compositions

The binder compositions of the invention include unmodified soy product and a synthetic resin. The binder compositions can optionally include other functional ingredients such as a dye, a pigment, a processing aid, a reinforcing agent, a filler, an oil, a viscosity-modifying agent, wax, and water.

The binder compositions can be prepared as a premix or mixed together with the other components of the wood-containing composite. For example, in some embodiments of the invention the ingredients of the binder compositions can be mixed directly together with other components of the wood-containing composite. The ingredients in the binder composition can be prepared as a premix. For example, in some embodiments of the invention, the unmodified soy product and synthetic resin can be mixed together to form a premix. In a preferred embodiment the unmodified soy product, synthetic resin, and optional functional ingredients can be mixed together as a premix. The binder compositions, including, but not limited to the premix, can be in powder form, liquid form, slurry form, or gel form. Where interaction between soy product and resin components leads to undesirable properties, the soy product and resin can be applied individually and separately to the lignocellulosic matrix.

The soy product can comprise between about 1 wt. % and about 80 wt. % of the binder composition. In a preferred liquid embodiment of the binder composition, the soy product comprises between about 1 wt. % and about 50 wt. % of the liquid binder composition, more preferably between about 5 wt. % and about 20 wt. %. In a preferred powder embodiment of the binder composition, the soy product comprises between about 1 wt. % and about 80 wt. % of the binder composition, more preferably between about 10 wt. % and about 50 wt. %.

The synthetic resin can be any suitable synthetic resin, including, for example, PF, UF, and MDI. The synthetic resin can comprise from about 20 wt. % to about 99 wt. % of the adhesive solids in the binder composition. In a preferred liquid embodiment of the binder composition, the synthetic comprises between about 50 wt. % and about 99 wt. % of the liquid binder composition, more preferably between about 80 wt. % and about 95 wt. %. In a preferred powder embodiment of the binder composition, the synthetic comprises between about 20 wt. % and about 99 wt. % of the adhesive solids in the binder composition, more preferably between about 50 wt. % and about 90 wt. % of the adhesive solids in the binder composition.

The optional functional ingredients can be added in an amount sufficient to provide the desired functional property, e.g., color or viscosity. Generally, the optional functional ingredients can be added in an amount between about 0 wt. % and about 30 wt. % of the binder compositions, preferably between about 0.01 wt. % and about 20 wt. %.

Wax is a preferred optional functional ingredient. Preferred waxes include petroleum based waxes such as slack wax, among others. Wax can be added to the lignocellulosic material in an amount between about 0.5 wt. % and about 3 wt. %. Preferably the wax is included at about 1 wt. %. Preferably, the wax is distributed uniformly on the wood strands. Inclusion of wax in the engineered wood products of the invention can surprisingly result in an increase strength in the engineered wood products. For example, flexural strength, modulus of elasticity and dry internal bond all improve with the addition of wax. Further, the use of wax in conjunction with the soy substitution of the invention provides superior properties to existing technology employing just resin with wax, and also an improvement of the engineered wood products prepared with the same soy substitution and no wax.

In some embodiments of the invention, the engineered wood products prepared with soy substitution and wax can have an increase in flexural strength over an engineered wood product having the same composition but no soy substitution; preferably the increase in flexural strength is at least about 10%, more preferably at least about 20%.

In some embodiments of the invention, the engineered wood products prepared with soy substitution and wax can have an increase in flexural strength over an engineered wood product having the same composition but no wax; preferably the increase in flexural strength is at least about 10%, more preferably at least about 20%, most preferably at least about 30%.

In some embodiments of the invention, the engineered wood products prepared with soy substitution and wax can have an increase in elastic strength over an engineered wood product having the same composition but no soy substitution; preferably the increase in elastic strength is at least about 10%, more preferably at least about 20%, most preferably at least about 25%.

In some embodiments of the invention, the engineered wood products prepared with soy substitution and wax can have an increase in dry internal over an engineered wood product having the same composition but no soy substitution; preferably the increase in dry internal bond is at least about 10%, more preferably at least about 20%, most preferably at least about 25%.

The binder compositions preferably have a viscosity less than about 1000 cp, more preferably between about 250 cp and about 750 cp.

Surprisingly, it was found that up to about 20% soy product substitution of MDI the viscosity does not rise significantly. Thus, in a preferred composition MDI is substituted with soy product in an amount of between about 5% and about 20%; more preferably between about 10% and about 15%.

The binder composition can be applied at a dosage of about 0.5 wt. % to about 20% of the lignocellulosic material, more preferably between about 1 wt. % and about 15 wt. %.

In an aspect of the invention, the engineered wood products can have less than about 5 wt. % added water, preferably less than about 1% added water, more preferably less than about 0.5 wt. % added water, and most preferably have no added water. Added water is different from water that may be present in certain ingredients, e.g., a dye which may be in an aqueous form.

In a preferred embodiment of the invention, the soy product and the synthetic binder composition can applied to core layers of the mat with an unmodified synthetic binder applied to the face layers of the mat. In another preferred embodiment, the soy flour and the synthetic binder composition can be applied to face layers of the mat with an unmodified synthetic binder applied to the core layers of the mat. Still in another preferred embodiment, the soy flour and synthetic binder composition can be applied to at least one of the core layers of the mat and/or at least one of the face layers of the mat. Preferably, the soy flour and synthetic binder composition is applied to the face layers and at least one of the core layers of the mat. Still more preferably, the soy flour and synthetic binder composition is applied to all of the core layers and both of the face layers of the mat. The core layers of the mat are the internal layers of the pressed wood product, while the face layers of the mat are the exterior layers of the pressed wood product.

Methods of Preparing Engineered Wood Products

Engineered wood is manufactured by pressing lignocellulosic materials, e.g. in the form of sheets, flakes or fiber with an adhesive to form a composite structure used in building materials, furniture and other applications. For example, one of these products is OSB, which is manufactured from heat-cured adhesives and rectangular-shaped wood strands that are arranged in cross-oriented layers and pressed. The adhesive can be a significant component.

Methods have been developed for formulating binders that comprise a mixture of conventional binders known in the art as PF, UF and MDI with unmodified soy product. The teachings of the present invention are improved and patentably different from those existing in the art. For example, an advantage of the present invention is that unmodified soy product is used directly with synthetic resin without need for expensive pre-application treatments such as crosslinking with other agents. This provides a cost benefit and changes the methods of preparing the compositions. Thus, an advantage is that the soy-amended formulations and methods of production can have lower cost than previous binders and methodologies. Additionally, formaldehyde and other volatile compounds emitted from the bonded product during manufacturing and throughout its life cycle that are considered deleterious to human health as well as to the environment are reduced for the product manufactured with the soy-amended binder as compared to products manufactured with prior-art adhesive formulations.

The method of preparing the engineered wood products is influenced to a certain extent by the type of wood-containing composite being prepared, as each type of composite has varying processing settings and conditions. Generally, the method of preparing the engineered wood products comprises mixing the binder composition ingredients, including, at least the unmodified soy product and synthetic resin, whether in liquid or solid form, applying the resulting mixture to lignocellulosic material, forming the mixture of binder and lignocellulosic materials into a mat, and pressing the mixture under heat to form an engineered wood product. Preferably, the applying step is performed by spraying, although it can also be performed by rolling, submerging, pouring, extruding, gravity application, etc.

In some embodiments, the components of the binder composition can be separately mixed with the lignocellulosic material and subsequently combined to form the binder composition and lignocellulosic mixture. For example, the unmodified soy product can be mixed with lignocellulosic material to form a mixture of unmodified soy product and lignocellulosic material; and the synthetic resin can be mixed with lignocellulosic material to form a mixture of synthetic resin and lignocellulosic material. The binder composition can then be formed upon the combination of the mixture of synthetic resin and lignocellulosic material and the mixture of unmodified soy product and lignocellulosic material. In another embodiment where the soy product reacts with the synthetic resin, the soy product and the resin can be rapidly mixed before the reaction has significantly advanced and then blended with the lignocellulosic component. In some embodiments, the mixture of soy product and resin can be applied either to the core layers of the mat or to the face layers of the mat to develop certain desirable board properties.

If both the soy product and the resin are in powdered form then agitating the two materials together can provide a mixed product. Preferably, the powders can be agitated by mixing or blending in any suitable manner, e.g., in a drum mixer, paddle mixer, etc. However, mixing powdered soy products with a liquid resin can be problematic. For example, in Cowan et al. (U.S. Pat. Publ. No. 2006/0231968), soy flour was added to MDI resin to form a modified binder; however, it resulted in gelation requiring the modified binder to be used immediately upon mixing. Gelation increases viscosity, which can prevent the ability to use a sprayer in applying the binder composition to the wood and increase the difficulty of rolling or spreading the binder.

Thus, in a preferred embodiment, the soy product can be added in an amount of up to about 20 wt. % simultaneously with the resin without increasing the viscosity above about 1000 cp. Preferably the soy product is added in an amount of at least about 5 wt. % and less than about 20 wt. % without increasing viscosity of the composition above about 1000 cp. More preferably the soy product is added in an amount between about 10 wt. % and about 15 wt. % without increasing the viscosity above about 750 cp.

Surprisingly, it was found that if soy product is added to the lignocellulosic material and adding the resin next does not lead to the viscosity problems. Thus, if the soy product is added in an amount above about 20 wt. %, it is preferable to first add the soy product to the lignocellulosic material and then add the resin as this was found not to detrimentally increase the viscosity.

Preferably the viscosity is less than about 1000 cp, more preferably the viscosity is between about 250 cp and about 750 cp. This viscosity is desired such that the compositions can flow freely and be rolled on the engineered wood products and/or to permit application of the compositions by sprayer.

In certain embodiments where the binder composition has a viscosity that is too high at room temperature to enable even-spreading of the formulation on the lignocellulosic materials (e.g., greater than about 1000 cp), the binder composition can be heated to lower the viscosity to an appropriate level. In a preferred embodiment of the invention, the binder composition can be heated between about 25° C. and about 90° C. for between about 0.1 minutes to about 20 minutes prior to blending with the lignocellulosic material. In a more preferred embodiment of the invention, the binder composition can be heated between about 40° C. and about 60° C. for between about 5 minutes to about 15 minutes prior to blending with the lignocellulosic material.

When adding wax to the engineered wood products, it is preferably added to the lignocellulosic materials prior to addition of the soy product and/or resin, although it can be added simultaneously or subsequently as well. Preferably, the wax is added to the lignocellulosic materials and tumbled to provide a uniform distribution on the lignocellulosic materials.

The methods of the invention can employ any suitable density of the lignocellulosic materials. For example, the density can be between about 20 lbs/cubic feet and 60 lbs/cubic feet.

The methods of preparing the engineered wood products can be done in continuous method or in batch methods. Similarly, the methods of preparing the binder compositions can be done in a continuous process or in a batch process.

The following examples, which are merely illustrative of the present invention, demonstrate application of the present invention, as well as demonstrate the benefits associated therewith.

EXAMPLES

Embodiments of the present invention are further defined in the following non-limiting Examples. It should be understood that these Examples, while indicating certain embodiments of the invention, are given by way of illustration only. From the above discussion and these Examples, one skilled in the art can ascertain the essential characteristics of this invention, and without departing from the spirit and scope thereof, can make various changes and modifications of the embodiments of the invention to adapt it to various usages and conditions. Thus, various modifications of the embodiments of the invention, in addition to those shown and described herein, will be apparent to those skilled in the art from the foregoing description. Such modifications are also intended to fall within the scope of the appended claims.

Example 1

Formulating Unmodified Soy Flour with a Powdered PF Resin

In one preferred embodiment, unmodified soy flour (Bakers 7B from Archer Daniels Midland) was added to a liquid formulation containing PF at various substitutions. The resin comprising the mixture of unmodified soy flour and PF resin was blended with wood flakes, pressed into boards and representative elements of the boards subjected to strength tests. The formulation was prepared by mixing unmodified soy flour with liquid PF resin obtained as GP 240C11 RESI-STRAN until the mixture was uniform. Pine strands prepared for the manufacture of oriented strand board were dried at 100° C. for 4 hours. The dried strands were added to a bag with the formulated soy/PF resin and the bag shaken until the strands were coated with resin. The coated strands were transferred to a 21.0 mm×31.1 mm forming box and pressed between two metal plates such that the resulting panels were formed at a thickness of 11.1 mm. No wax was applied. The samples were loaded into the press with the temperature of both platens of the press maintained at 204° C. with a total pressing pressure of 2.0 MPa for 4 minutes. The boards were cut into 22.9 cm×3.8 cm strips (3 samples per board). Density was calculated according to ASTM D1037-12. The strips were tested on a Zwick/Roell Z010 Static Material Testing Machine with the longer strands facing downwards to ensure that maximum breaking force was achieved. The flexural strength and flexure modulus of the boards were measured with ASTM D1037-12 tests.

The effect of the soy-amended formulation on flexural strength and internal bond of boards prepared from pine flakes is illustrated in FIG. 1. The results for 6% substitution is statistically identical to the values for the control (0% soy flour substitution) demonstrating that at least 6% of the PF resin can be replaced by unmodified soy flour without incurring a statistically significant loss in flexural strength or in internal bond. This is an unexpected and very useful outcome because unmodified soy flour is of significantly lower cost than PF resin. Furthermore, formaldehyde is released from PF resin during the manufacturing process and also via degassing throughout its life cycle. Reduction of the PF level in the resin formulation leads to a concomitant reduction in formaldehyde emissions.

The use of binders based on soy protein isolates has been disclosed by Lorenz et al. (2015), Mo et al. (2003), Hettiarachchy et al. (1995), Qi et al (2011), Dastidar and Netravali (2013) and Li et al (2009). Soy isolates are components of soy flour, and their extraction from soy flour entails significant processing which adds to cost. As a result, the soy isolates are significantly more expensive than unmodified soy flour. The teachings of the present invention are patentably different from these prior art disclosures because unmodified soy flour is used, and the expensive step of isolating soy isolates from soy flour is avoided.

The use of soy flour cross-linked with PF resin has been disclosed in several applications, e.g. by Yang et al. (2006), Lorenz et al (2005), Hse and Lin (2005), Kuo et al (2003), Schwarzkopf (2010) and Huang (2008). Zhang et al. (2014) have disclosed binder formulations containing soy flour in combination with cross-linking agents such as triethanolamine. Resin formulations that include soy flour that is pre-hydrolyzed, cross-linked and otherwise derivatized have been reported. The use of soy flour cross-linked to PF resin or its precursors has been disclosed by Yang et al (2006), Wescott and Frihart (2004), and Lorenz et al (2005). The use of pre-hydrolyzed soy flour in combination with other components has been disclosed by Hse et al. (2000), Huang and Li (2008) and Wescott and Frihart (U.S. Pat. No. 7,345,136). Wescott and Frihart (Canadian patent 2,658,262) have disclosed the art of denaturing soy flour with urea and combining the denatured product with other components for use as a binder. The teachings of the present invention are patentably different from these prior art disclosures because unmodified soy flour is combined directly with synthetic resin without need for expensive pre-application treatments such as crosslinking with other agents.

Example 2

Formulating Unmodified Soy Flour with Powdered PF Resin

In another preferred embodiment, PF resin in powdered form is substituted by unmodified soy flour at 21% by weight. The powder resin was GP 190080 Woodweld. The unmodified soy flour and the powder resin were first shaken in a bag and the mixture then blended with the flakes following the procedure described in Example 1. The remaining steps of forming the flakes, pressing the mat into a board and testing the board followed the protocol described in Example 1. The effect of the soy-amended formulation on various bond properties of boards prepared from pine flakes is illustrated in Table 1. The properties of wet boards were obtained after soaking the boards in water for 24 hours. No statistically significant loss of properties is incurred with unmodified soy flour substitution.

TABLE 1
	PF only	21% soy substitution
Dry Internal bond (MPa)	0.31 ± 0.09	0.28 ± 0.05
Wet Internal bond (MPa)	0.009 ± 0.002	0.005 ± 0.002
Moisture absorption (%)	44 ± 3	45 ± 1
Thickness swell (%)	53 ± 6	52 ± 7
Flexural Strength (MPa)	26 ± 4	27 ± 7
Modulus of elasticity (MPa)	4,000 ± 500	4,300 ± 500

Example 3

Producing Board with Flakes Treated Separately with PF Resin and Unmodified Soy Flour

In another preferred embodiment, unmodified soy flour is blended first with wood flakes, following which powder PF resin is blended with the soy-treated wood flakes. The flakes are then pressed into boards and representative elements of the boards subjected to strength tests. The procedure for forming the flakes, pressing the mat into a board and testing the board followed the protocol described in Example 1. The effect of the soy-amended formulation on flexural strength and internal bond of boards prepared from pine flakes is illustrated in Table 2. No statistical loss of strength properties is incurred at levels of unmodified soy flour substitution of up to 25%.

	TABLE 2
		PF only	10% soy substitution
	Dry Internal bond (MPa)	0.16 ± 0.02	0.15 ± 0.05
	Moisture absorption (%)	108 ± 2	117 ± 2
	Thickness swell (%)	55 ± 8	72 ± 4
	Flexural Strength (MPa)	17 ± 7	15 ± 2
	Modulus of elasticity (MPa)	2900 ± 1000	3300 ± 600

Example 4

Formulating Unmodified Soy Flour with MDI Resin

In another preferred embodiment, unmodified soy flour is added to a MDI resin at various substitutions. The MDI resin was MONDUR 541 from Bayer Material Science. The viscosity of the formulation of unmodified soy flour and MDI resin was high when the level of unmodified soy flour substitution was at 25% or a higher level. It is desirable to reduce the viscosity of the formulation to facilitate uniform blending with the flakes. The viscosity of formulations containing unmodified soy flour at 25% or more was reduced by heating the soy/MDI formulation to about 45° C. for ten minutes. Where the soy substitution was below 25% the soy/MDI formulation was applied without heating. Allen and Spraul (U.S. patent application 20150086775) have disclosed a method of reducing the viscosity of soy-based liquid adhesive formulations by grinding the unmodified soy flour so that at least 70% of the unmodified soy flour particles have a particle size of less than 30 microns. The teachings of the present invention are patentably different from the Allen disclosure because the need for grinding is avoided. Grinding is associated with high capital and operating costs. Yang and Yang (U.S. Pat. No. 8,057,892) have disclosed a method of reducing the viscosity of an adhesive formulation by adding a viscosity modifier to the binder formulation. The teachings of the present invention are patentably different because the need for adding chemicals for viscosity modification is avoided.

The procedure for forming the flakes, pressing the mat into a board and testing the board followed the protocol described in Example 1. The effect of the soy-amended formulation on flexural strength and internal bond of boards prepared from pine flakes is illustrated in Table 3. No statistically significant loss of strength properties is incurred at levels of 20% unmodified soy flour substitution. A higher level of substitution can be accommodated if a small loss of strength can be tolerated in the interests of reducing cost.

TABLE 3
		20% soy	30% soy
	MDI only	substitution	substitution
Dry Internal bond (MPa)	0.38 ± 0.1	0.37 ± 0.08	0.17 ± 0.04
Wet Internal bond (MPa)	0.009 ± 0.002	0.05 ± 0.01	0.01 ± 0.007
Moisture absorption (%)	95 ± 9	82 ± 7	102 ± 8
Thickness swell (%)	53 ± 6	28 ± 7	61 ± 7
Flexural Strength (MPa)	25 ± 5	42 ± 10	33 ± 8
Modulus of elasticity (MPa)	4000 ± 500	4800 ± 1000	4600 ± 1000

Without meaning to limit the scope and applicability of the invention in any way, it is believed that the unmodified soy flour is hydrolyzed during pressing of the wood product by the steam present in the wood mat produced by the action of the hot platens of the press on the water contained in the wood. The movement of steam through the mat is known to be responsible for the heat transfer from the platens to the wood. The intimate contact between the steam and unmodified soy flour is believed to lead to hydrolysis of the unmodified soy flour. The protein released during hydrolysis interacts with synthetic resin components and with wood tissue. The in-situ hydrolysis of unmodified soy flour in the wood mat under the conditions of temperature and time that occur during pressing is unexpected and is patentably different from the prior art. Significantly, in-situ hydrolysis does not incur the costs associated with pretreatment of unmodified soy flour.

Example 5

Flexural Strength and Modulus Studies

ProCote 4200 (a soy isolate from DuPont) was mixed with PF at substitutions of 10 wt. %, 20 wt. %, and 30 wt. %. The powdered soy was added to the PF along with water to achieve the same solids content as the PF control. Shear tests were run on loblolly pine lap samples according to standard DIN EN 205. The results are shown in FIG. 2. The soy significantly increased the strength of the PF resin.

Analogous measurements were made with 5% soy flour substitution of PF resin. Results for flexural strength and flexural modulus are shown in FIGS. 3A and 3B, respectively. The increase caused by the soy flour is statistically significant with p values of 0.08 and 0.05, respectively.

The soy flour was also used to make OSB wood panels at a target density of 30 lbs/ft³ and a thickness of 7/16″ for all boards. Four boards were formed: two controls of liquid PF and two with 5 wt. % soy and 95 wt. % PF. The strength and modulus were also normalized for density by dividing by the density. Results for flexural strength and flexural modulus are shown in FIGS. 4A and 4B, respectively. The 5% soy/PF board showed a higher strength (p value=0.07) and modulus (p value=0.05) than the PF control board.

The addition of soy flour at lower densities showed an equal performance in strength and stiffness when compared to the PF control at lower panel densities. Results for flexural strength and flexural modulus are shown in FIGS. 5A and 5B, respectively. In FIGS. 5A and 5B, the circle data points are of the PF control and the triangle data points are of the 5% soy substitution. This performance demonstrates that one can make panels of equivalent strength but at lower costs assuming soy flour costs are significantly lower than PF costs. The benefit of this is that manufacturers can make panels cheaper by adding soy but without a reduction in strength.

In summary, the above results clearly demonstrate that soy flour can be used to partially substitute PF in the resin without compromising or even improving the properties tested. The cost of the resin is, therefore, significantly reduced when compared to the base case where PF resin is used alone. While the application is exemplified by an application to OSB, it is noted that the approach can also be applied to plywood, strandboard, medium density fiberboard and other products where an adhesive is used to bond wood components. The approach can also be applied where fillers such as wood pulp and walnut shells are added along with the resin.

Example 6

Formulating Unmodified Soy Flour with Powdered PF Resin in a Random Flake Board

PF resin in powdered form was substituted with unmodified soy flour at 10, 21, and 30% by weight. Emulsified wax (Hexion Bord'N-Seal™ FMH-XD) was not used in the 10% soy substitution but was used for all other instances, including the PF control formulations. The soy flour was Bakers 7B obtained from Archer Daniels Midland. The powder resin was GP 190080 Woodweld. The unmodified soy flour and the powder resin were first shaken in a bag and the mixture then blended with pine strands. The wax was applied to the strands before the resin in the instances that included wax.

While nominally a mixture, the PF and soy particles can remain substantially separate as shown by microscopic analysis. The association of soy flour particles with powdered PF particles was studied by shaking equal weights of each component in a plastic bag and examining the properties of the mixture under a microscope with 10× magnification. An illustration of the level of mixing is provided in FIG. 6. The large particle is soy flour and the smaller particles are powdered PF. FIG. 6 shows that while there is some association between the two components there are also several unassociated particles.

The strands were pre-dried at 100° C. for 4 hours. The coated strands were transferred to a 21.0 mm×31.1 mm forming box and pressed between two metal plates such that the resulting panels were formed at a thickness of 11.1 mm. The samples were loaded into the press with the temperature of both platens of the press maintained at 204° C. with a total pressing pressure of 2.0 MPa for 4 minutes. The boards were cut into 22.9 cm×3.8 cm strips (3 samples per board). Density was calculated according to ASTM D1037-12. The strips were tested on a Zwick/Roell Z010 Static Material Testing Machine with the longer strands facing downwards to ensure that maximum breaking force was achieved. The flexural strength (MOR) and flexural modulus (MOE) of the boards were measured with ASTM D1037-12 tests.

The effect of the soy-amended formulation on various bond properties of boards prepared from pine flakes is illustrated in Table 4. The properties of wet boards were obtained after soaking the boards in water for 24 hours. The properties of the soy-modified product are generally statistically equivalent to or better than the properties of the product made from PF only.

TABLE 4
		10% soy	21% soy	30% soy
	PF resin only	substitution	substitution	substitution
	with wax	without wax	with wax	with wax
Flexural	12 ± 4	17 ± 3	22 ± 4	29 ± 7
Strength
(MPa)
Modulus	3,700 ± 1500	3,400 ± 500	5,700 ± 900	6100 ± 500
of
elasticity
(MPa)
Dry	0.13 ± 0.08		0.21 ± 0.06	0.29 ± 0.07
Internal
bond
(MPa)
Thickness	54 ± 10	63 ± 10	35 ± 3	43 ± 5
swell
(%)
Wet	3.1 ± 1.1	3.3 ± 0.8	4.1 ± 1.3	4.1 ± 2.0
MOR
(MPa)
Wet	190 ± 70	330 ± 240	470 ± 140	300 ± 60
MOE
(MPa)

The results in this Table demonstrate an improvement over compositions prepared with a traditional resin and wax and with no soy substitution. Further, the results also demonstrate an unexpected improvement with the addition of wax over compositions prepared with the same soy substitution percentage and no wax. For example, FIG. 1A (from Example 1) shows the flexural strength of an engineered wood product prepared with PF resin and about 21% soy substitution, which had a flexural strength of about 16 MPa. Thus, Table 4 shows a significant improvement where a similar composition including about 21% soy substitution and the addition of wax had a flexural strength of about 22 MPa.

Example 7

Separate Addition of Soy Flour and MDI Resin to Lignocellulosic Furnish

Soy flour and MDI resin were added to flakes sequentially. In one instance, the soy flour was added first to the flakes followed by MDI resin. In another instance, the MDI resin was added first followed by soy flour. Emulsified wax was applied before resin application. The procedure for forming the flakes, pressing the mat into a board and testing the board followed the protocol described in Example 6. The effect of the presence of soy on MOR, MOE, wet MOR and MOE, water absorption, thickness swell, and internal bond is illustrated in FIGS. 7A-7G, where the designation A>B represents the first addition of component A followed by the second addition of component B and A+B represents mixture of A and B before application. No statistical loss of properties is observed across the conditions tested and the compositions including soy flour substitution had improved flexural strength, flexural modulus, and internal bond compared to the compositions with just PF resin and no soy flour substitution.

Varnell (U.S. Pat. Publ. No. 2016/0257815) has disclosed the addition of a protein source such as soy flour to a mixture of lignocellulosic material and a curative such as an epichlorohydrin derivative. The curative must be dissolved or suspended in water prior to application. The added water is an essential component of the Varnell formulation because it must dissolve both the protein and curative to enable reaction, because the curative has no bonding properties by itself. In the absence of any interaction with protein the curative would be a deadload. The present invention does not require the resin and soy components to be in intimate contact because either component can act as an adhesive in its own right without the need to react with the other component. As described in Example 6, many of the soy particles and PF resin particles remain physically separate even after mixing. It is believed that the soy component cross links with the PF resin when the two components are in intimate contact. However, both resin and the soy component can provide bonding without contacting each other. Varnell recognizes that the presence of excess water can lead to catastrophic failure of the composites structural shape during pressing because of the pressure of the steam built up. The negative effects of internal steam pressure caused by high wood moisture have been discussed by Cai et al (2009).

The present invention is patentably different from the art, including Varnell and Cowan for several distinctive reasons. For example, Cowan et al., U.S. Pat. Publ. 2006/0231968 disclosed binder compositions in a premix containing unmodified soy flour and MDI resin. However, the soy flour reacts rapidly with the MDI resin and leads to a viscous mixture which renders impossible the application of the mixture through a nozzle. This problem is overcome by the present invention.

Further with respect to Varnell, there is no need to add water, which is a detriment because of press blows within the panel as discussed by Cai et al (2009). In the present application, the wood moisture does not need to be controlled to a low value and a broad range of wood moisture content can be accommodated from oven dried to some upper specification where steam pressure is limiting. Indeed, the MDI resin of the present invention can be used at wood moisture of over 20% (Pichelin et al. 2001). The Varnell invention cannot be used at these high wood moisture levels because it would provide additional moisture. The water present in wood prior to pressing is bound water, i.e. water bound to the cell walls of the wood, which is distinct from free water, which is bulk water located in the void space of the cell wall. Bound water cannot dissolve added substances such as the curative of Varnell. The present invention requires no free water to be present, which is patentably different from Varnell where the presence of added free water is required. Varnell's requirement that the curative be applied in water teaches away from the present invention where the presence of water is a detriment.

Another requirement of Varnell's disclosure is that the curative and the soy flour be added separately to the lignocellulosic material in separate mixing operations. Otherwise, contact of the protein source powder with the curative would lead to deposits in the blender. Direct mixing of the two components in a single blender is not recommended by Varnell. Mixing of the lignocellulosic material with curative, and then mixing of soy flour with the combination of lignocellulosic material and curative requires separate unit operations. The present invention does not have this limitation and the resin, soy product and lignocellulosic material can be mixed in a single blender.

Example 8

Viscosity Testing

Compositions were prepared with varying substitution of soy flour for MDI and one substitution with PF. Viscosity measurements at ambient temperature were made after adding soy flour to MDI or liquid PF resin. The viscosity changes after various time periods after mixing the flour with the resin are provided in Table 5. Viscosity changes over 10 seconds after mixing soy flour into MDI resin. Previously there has not been an appreciation that viscosity changes occur within a few seconds after soy flour in mixed with resin. For example, Cowan makes no mention of a time limitation in controlling binder viscosity. However, it was found to be essential that the application of the soy-amended resin be rapid enough to minimize an increase in viscosity. Manufacturing facilities that use the base unmodified resin will wish to maintain the viscosity of the soy-modified resin to as close as possible to that of the base resin. Preferably, this would be between about 250 cp and about 750 cp.

TABLE 5
Soy flour	Viscosity (cp)
substitution		After 10	Value at	Value at
(%)	Initial	seconds	~2 min	1-5 hr
MDI
10	312	360	465	750
15	265	1,029	1,065	2,058
20	312	2,283	1,631	8,100
30	252	12,020	8,721	15,200
PF
10	500	1,841	32,000

The inventions being thus described, it will be obvious that the same may be varied in many ways. Such variations are not to be regarded as a departure from the spirit and scope of the inventions and all such modifications are intended to be included within the scope of the following claims.

REFERENCES

• A. J. Allen, B. K. Spraul, Soy-based adhesives with improved lower viscosity, U.S. patent application 20150086775.
• Z. Cai, M. Birkeland, J. M. Wescott, J. O'Dell, J. E. Winandy, Effects of press size on internal steam pressure during particleboard hot-pressing process, Forest Prod. J., 59(4), 40-44 (2009).
• J. Cowan, D. L. Atkinson, R. A. Breyer, J. D. Rivers, C. E. Vest, U.S. patent application 20060231968.
• T. G. Dastidar, A. N. Netravali, A soy flour based thermoset resin without the use of any external crosslinker, Green Chem, 2013, 15, 3243-3251
• C. R. Frihart, M. J. Birkeland, Soy Properties and SoyWood Adhesives, https://www.fpl.fs.fed.us/documnts/pdf2007/fpl_2007_frihart001.pdf
• C. R. Frihart, C. G. Hunt, M. J. Birkeland, Recent Advances in Adhesion Science and Technology, W. Gutowski, H. Dodiuk, Eds., CRC press, 2914, p. 284.
• N. S. Hettiarachchy, U. Kalapathy, D. J. Myers, Alkali-modified soy protein with improved adhesive and hydrophobic properties, J Am Oil Chem Soc, 72, 1461-1464, 1995.
• C-Y. Hse, F. Fu, B. S. Bryant, Development of formaldehyde-based wood adhesives with co-reacted phenol/soybean flour, Wood Adhesives 13-19, 2000.
• C. Y. Hse, L. Lin, Hydrolyzates of soybeans or other soy products as components of thermosetting resins. U.S. Pat. No. 0,272,892A1, 2005.
• J. Huang, K. Li, A new soy flour-based adhesive for making interior Type I plywood J Am Oil Chem Soc, 85 63-70, 2008.
• M. Kuo, D. J. Meyers, H. Heemstra, D. Curry, D. O. Adams, D. D. Stokke, Soybean-based adhesive resins and composite products utilizing such adhesives, U.S. Pat. No. 6,518,387 B2, 2003.
• X. Li, Y. Li, Zhong, D. Wang, J. A. Ratto, K. Sheng, S. X. Sun, Mechanical and water soaking properties of medium density fiberboard with wood fiber and soybean protein adhesive, Bioresource Tech, 100, 3556-3562, 2009.
• L. F. Lorenz, M. Birkeland, C. Daurio, C. R. Frihart, Soy flour adhesive strength compared with that of purified soy proteins, Forest Prod. J., 65 (1/2) 26-30, 2015.
• L. Lorenz, C. R. Frihart, J. M. Wescott, Analysis of soy flour/phenol-formaldehyde adhesives for bonding wood, Wood Adhesives, 501-505, 2005.
• X. Mo, E. Cheng, D Wang, X. S. Sun, Physical properties of medium-density wheat straw particle board using different adhesives, Ind Crops and Prod, 18, 47-53, 2003.
• F. Pichelin, A. Pizzi, A. Fruhwald, P. Triboulot, Exterior OSB preparation technology at high moisture content—Part 1: Transfer mechanisms and pressing parameters, Holz als Roh and Werkstoff, 59, 256-265 (2001).
• G. Qi, X. S. Sun, Soy protein adhesive blends with synthetic latex on wood veneer, J Am Oil Chem Soc, 88, 271-281, 2011.
• M. J. Schwarzkopf, Development and evaluation of oriented strand board bonded with soy-based formaldehyde-free adhesives, MS thesis, Oregon State University, 2010.
• D. F. Varnell, Method of making lignocellulosic components, U.S. Pat. Publ. No. 2016/0257815.
• J. M. Wescott, C. R. Frihart, Stable adhesives from urea-denatured soy flour, Canadian patent 2,658,262.
• J. M. Wescott, C. R Frihart, Water-resistant vegetable protein adhesive dispersion compositions, U.S. Pat. No. 7,345,136.
• J. M. Wescott, C. R. Frihart, Competitive soybean flour/phenol formaldehyde adhesives for oriented strandboard, 38^th Intl Wood Composites Symp Pullman, Wash., 2004.
• I. Yang, M. Kuo, D. J. Myers, Bond quality of soy-based phenolic adhesives in Southern Pine plywood, JAOCS, Vol. 83, 231-237, 2006.
• G. Yang, B. Yang, Wood adhesive and method of preparing thereof, U.S. Pat. No. 8,057,892, U.S. patent application 20100258033.
• M. Zhang, P. F. Miele, J. Asrar, Formaldehyde-free protein-containing binder compositions, U.S. Pat. No. 8,809,477.

Claims

1. A method of preparing a pressed wood composite comprising: heating a binder composition, wherein the binder composition comprises unmodified soy product and a synthetic resin; wherein the synthetic resin comprises MDI;applying a binder composition to a lignocellulosic material to form a mixture, wherein the soy product is between about 1 wt. % and about 50 wt. % of the binder composition, wherein the binder has a viscosity of less than about 1000 cp;forming the mixture into a mat; andpressing the mat while simultaneously heating the mat to form a pressed wood composite; wherein the pressed wood composite is a chipboard, a medium density fiberboard, a high density fiberboard, a flake board, a laminated-strand lumber, an oriented strand board, a parallel-strand lumber, a particle board, a plywood, a veneer, or a wafer board.

2. The method of claim 1, wherein the unmodified soy product is selected from the group consisting of soy flour, soy meal, and a mixture thereof; wherein the synthetic resin further comprises PF, UF, or a mixture thereof; and wherein the binder composition is applied at a dosage of 0.5% to 20% by weight of wood.

3. The method of claim 2, further comprising a step of adding wax to the lignocellulosic materials prior to the mixing step.

4. The method of claim 2, wherein the binder composition is applied to core layers of the mat with an unmodified synthetic resin applied to the face layers of the mat.

5. The method of claim 2, wherein the soy flour and the synthetic binder composition is applied to face layers of the mat with an unmodified synthetic resin applied to the core layers of the mat.

6. The method of claim 1, wherein the soy product is between about 10 wt. % and about 50 wt. % of the binder composition.

7. The method of claim 1, wherein the applying step is performed by spraying the binder on the lignocellulosic material, and wherein the binder has a viscosity of between about 250 cp and about 750 cp.

8. A method of preparing a pressed wood composite comprising: (a) mixing an unmodified soy product with lignocellulosic material,(b) adding a synthetic resin to the unmodified soy product with lignocellulosic material to form a mixture, wherein the unmodified soy product and synthetic resin form a binder composition, and wherein the unmodified soy product is in an amount less than about 20 wt. % of the binder composition; wherein the synthetic resin comprises MDI;(c) forming the mixture into a mat; and(d) pressing the mat while simultaneously heating the mat to form a pressed wood composite;

9. The method of claim 8, wherein the unmodified soy product is selected from the group consisting of soy flour, soy meal, and a mixture thereof; wherein the synthetic resin further comprises PF, UF, or a mixture thereof; and wherein the binder composition is applied at a dosage of 0.5% to 20% by weight of wood.

10. The method of claim 9, further comprising a step of adding wax to the lignocellulosic materials prior to step (a).

11. The method of claim 9, wherein the binder composition is applied to core layers of the mat with an unmodified synthetic resin applied to the face layers of the mat; or wherein the soy flour and the synthetic binder composition is applied to face layers of the mat with an unmodified synthetic resin applied to the core layers of the mat.

12. A method of preparing a pressed wood composite comprising: heating a binder composition, wherein the binder composition comprises unmodified soy product and synthetic resin, wherein the synthetic resin comprises MDI, and wherein the binder composition has a viscosity of less than about 1000 cp;spraying the binder composition on a lignocellulosic material to form a mixture;forming the mixture into a mat;pressing the mat while simultaneously heating the mat to form a pressed wood composite; wherein the pressed wood composite is a chipboard, a medium density fiberboard, a high density fiberboard, a flake board, a laminated-strand lumber, an oriented strand board, a parallel-strand lumber, a particle board, a plywood, a veneer, or a wafer board.

13. The method of claim 12, wherein the binder composition has a viscosity of between about 250 cp and about 750 cp.

14. The method of claim 12, wherein the unmodified soy product is in an amount less than about 20 wt. % of the binder composition.

15. The method of claim 12, wherein the unmodified soy product is in an amount between about 10 wt. % to about 15 wt. % of the binder composition.

16. The method of claim 12, wherein the binder composition is sprayed on the lignocellulosic material within 2 minutes of the creation of the binder composition.

17. The method of claim 12, wherein the binder composition is sprayed on the lignocellulosic material within 10 seconds of the creation of the binder composition.

18. The method of claim 12, wherein the binder composition further comprises one or more of the following functional ingredients: a dye, a pigment, a processing aid, a reinforcing agent, a filler, an oil, a viscosity-modifying agent, a wax, and water.