The present invention relates generally to spas and, more particularly, to a cover for a spa and method of manufacturing a cover for a spa.
Spas, also commonly known as hot tubs, are popular fixtures that are used in many homes. They generally include a deep, vacuum formed tub having a smooth acrylic liner that is filled with heated water and which is used for soaking and relaxation. Spas typically include water jets for massage purposes.
Typically, the acrylic liner is formed into shapes that provide a variety of seating arrangements within the tub. Each seat is usually equipped with hydrotherapy jets that allow a pressurized flow of water to be directed at various parts of a user's body. The water flow may be aerated for additional effect, and some or all of the jets may also automatically move or rotate, causing the changing pressure of the water on the body to provide a massage-like effect.
Because many spas/hot tubs are located outdoors, they are often equipped with covers for enclosing the tub when not in use. These covers help prevent dirt, leaves and other debris from entering the water, and provide a safety function by preventing children and animals from falling into the water. Moreover, spa covers are often insulated so as to limit heat loss from the water when the spa is not in use for purposes of energy efficiency and readiness of use.
As will be readily appreciated, however, existing covers for spas are heavy and cumbersome, making them difficult for a user to remove prior to using the spa and to place back over the spa when it is no longer in use. Lighter, foam-core covers are often not vey structurally sounds, and can become waterlogged over time.
In view of the above, there remains a need for a cover for a spa that is water impervious.
It is an object of the present invention to provide a spa cover.
It is another object of the present invention to provide a spa cover having a water impervious coating.
These and other objects are achieved by the present invention.
According to an embodiment of the present invention, a cover for a spa includes a core, a hydrophobic coating encasing the core, and a membrane encasing the core and hydrophobic coating.
According to another embodiment of the invention, a method of manufacturing a cover for a spa includes the steps of providing a core and encasing the core with a hydrophobic coating.
According to yet another embodiment of the present invention, a cover for a spa includes a core having a cellular structure, a hydrophobic spray coating encasing the core, and a flexible membrane and/or a hard shell encasing the core and coating.
The present invention will be better understood from reading the following description of non-limiting embodiments, with reference to the attached drawings, wherein below:
Referring to
For example, with reference to
In an embodiment, the coating 14 is a water impervious (or substantially water impervious), or hydrophobic coating and may be, for example, a urea or polyurethane hydrophobic coating. In an embodiment, the coating is a two-part polyurethane coating. In one embodiment, the coating 14 is a spray-on elastomeric protective coating, such as the coating manufactured and sold under the trade name Bullet Liner RPM from Accella. In another embodiment, the coating is a polyurea or pure urea spray elastomer such as the coating manufactured and sold under the trade name Intellathane 7100LV by Carlisle Polyurethane Systems.
In an embodiment, a block of EPS material is first formed to shape by processes known in the art such as by cutting, shaving, sanding, and the like, to form core 12. In an embodiment, the coating 14 is then applied directly to the core 12 (regardless of construction/composition) via spraying. In an embodiment, the coating is applied to a thickness of 0.015 to 0.030 inches to sea the core 12 from moisture intrusion. The coating is then allowed to dry. Importantly, the coating 14 substantially encases the core 12 and makes it stronger and prevents water from contacting the core 12. The core with impervious coating 14 is then wrapped in or otherwise covered by a skin or membrane 16. In an embodiment, the skin or membrane 16 may be formed from any material known in the art such as vinyl or the like. In an embodiment, the skin or membrane 16 may be formed from acrylic and/or ABS, polyethylene or other materials, and may be formed or deposited by vacuum forming, drape molding, blow molding, or the like. In an embodiment, the membrane 16 is a decorative or aesthetically-pleasing covering. In an embodiment, the membrane 16 may be omitted such that the coating 14 forms the outermost layer of the cover 10.
While the present invention discloses that the coating 14 is applied directly to the foam core 12 by spraying, it is not intended that the present invention be so limited in this regard. In particular, it is contemplated that the coating 14 may be applied directly to the foam core 12 by immersion coating, roll coating, and the like, or by any of the other techniques disclosed herein.
The cover 10 may then be further modified or adapted to enable use of the cover with a lift assembly for a spa, such as disclosed in U.S. Pat. No. 10,865,579, which is hereby incorporated by reference herein in its entirety.
In an embodiment, the coating 14 is intended to be used on both hard covers and soft covers. For example, with reference to
In an embodiment, the cover members 102, 104 are manufactured from an acrylic material. For example, in the preferred embodiment, the cover members 102, 104 may be manufactured from one of acrylonitrile butadiene styrene (ABS) and polyvinyl chloride (PVC). In other embodiments, the cover members 102, 104 may be manufactured from other materials such as, for example, polyethylene (PE), without departing from the broader aspects of the present invention. In an embodiment, the cover members 102, 104 may be joined together with an adhesive and/or include cooperative locking features to inhibit decoupling of the cover members 102, 104, once joined.
For example, in an embodiment, manufacturing the cover 100 includes first cutting an EPS foam core 12 to shape (to correspond closely to the shape and interior dimensions of top and bottom cover members 102, 104). As disclosed above, however, the core can take any form known in the art. The core 12 is then sprayed with a water impervious coating 14 such as, for example, Intellathane 7100LV by Carlisle Polyurethane Systems, although other coatings of the type disclosed above may also be utilized without departing from the broader aspects of the invention. In an embodiment, the water impervious coating is applied to a thickness of 0.015 to 0.030 inches to seal the foam core from moisture intrusion inside of the hard cover shell. The coating 14 is then allowed to dry. The inside surfaces of one or both of the rigid shell members 102, 104 are then sprayed with an adhesive such as, for example, Intellathane SL-50 by Carlisle Polyurethane Systems, which provides for a slower set-up time of about 20 seconds. Other urethane adhesives may also be utilized. The coated EPS core 12 with coating 14 is then inserted into the interior space of the shell members 102, 104 so that it is in contact with the adhesive on the interior surfaces of the shell members 102, 104. The SL-50 adhesive binds the core 12 to the shell member(s) 102, 104 and provides a thermal set glue and rigidizer that will not melt under the high temperatures that the cover 100 may see in direct sunlight.
Turning now to
In an embodiment, manufacturing the cover 200 includes first cutting an EPS foam core 204 to shape (to correspond closely to the shape and interior dimensions of top cover member 202). As disclosed above, however, the core can take any form known in the art. The core 204 is then sprayed with a water impervious coating such as, for example, Intellathane 7100LV by Carlisle Polyurethane Systems, although other coatings of the type disclosed above may also be utilized without departing from the broader aspects of the invention. In an embodiment, the water impervious coating is applied to a thickness of 0.015 to 0.030 inches, and more preferably about 0.030 inches, to seal the foam core from moisture intrusion inside of the hard cover shell 202. The coating is then allowed to dry. The inside surfaces of the rigid shell member 202 are then sprayed with an adhesive such as, for example, Intellathane SL-50 by Carlisle Polyurethane Systems, which provides for a slower set-up time of about 20 seconds. The coated EPS core 204 is then inserted into the interior space of the shell member 202 so that it is in contact with the adhesive on the interior surfaces of the shell member 202. After curing, the core 204 is adhered/affixed to the shell member 202.
In an embodiment, after coating the foam core to a thickness of about 0.030 inches and prior to joining the core to the cover member 202, a pattern is created on the bottom surface of the core in the coating. In an embodiment, the pattern is a decorative pattern which may match a pattern formed on an exterior surface of the top shell member 202. Importantly, this improves the aesthetics of the cover 200, which has the coated foam core 204 as the exposed bottom surface of the cover 200.
Importantly, it has been discovered that the cover 200 is substantially water impervious, provides optimal rigidity and is relatively immune from damage or caving, and can be manufactured at a lower cost and more quickly than typical spa hardcovers that have heretofore required rigid material to form the entirety of the cover.
Turning finally to
Importantly, the structural member 40 around the outside of the foam core 12 provides a rigid structure to resist curling (bending) of the cover under a large thermal gradient, particularly in cold weather. In particular, existing spa covers can be prone to curling or bending, particularly at the corners, in cold weather (due to the different in temperature between the heated water within the spa and cold ambient temperatures outside the spa). When this happens, the corners of the cover can curl up and away from the spa, causing steam to leak from the openings that are created and creating a loss of energy from the water in the spa. This lowers the temperature of the spa water requiring the heater to activate and reheat the water. The structural member 40, however, inhibits curling or bending at the corners, ensuring that a tight seal is maintained between the cover and the spa at all points, preventing and/or minimizing heat leakage. In addition, the polyurethane and urethane materials used herein (e.g., the water impermeable coating, material of the core and/or the adhesive that bonds the core to the hard outer shell (where utilized) are thermal set plastics, which means after they set up, they cannot be melted again. This property makes them ideal for resisting the high temperatures that can result on the surface of the cover from direct exposure to sunlight in warm climates.
Although this invention has been shown and described with respect to the detailed embodiments thereof, it will be understood by those of skill in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiments disclosed in the above detailed description, but that the invention will include all embodiments falling within the scope of this disclosure.
This application claims the benefit of U.S. Provisional Application Ser. No. 63/425,061, filed on Nov. 14, 2022, which is hereby incorporated by reference herein in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 63425061 | Nov 2022 | US |