The present invention relates to a spark plug.
Heretofore, conventional spark plugs used, for example, in an internal combustion engine, a configuration in which a noble metal tip is provided on a distal end portion of a ground electrode via an intermediate member (see, for example, Japanese Patent Application Laid-Open (kokai) No. 2009-163923). (See also Japanese Patent Application Laid-Open (kokai) No. 2009-158408, Japanese Patent No. 4073636 and Japanese Patent Application Laid-Open (kokai) No. 2008-214734). In the case where a noble metal tip is provided on the ground electrode, when the ground electrode is located so as to be away from a discharge gap, flame-quenching effect, which the ground electrode deprives energy of a flame kernel generated through discharge, can be prevented. Therefore, in the case where the noble metal tip is bonded to the ground electrode, when an intermediate member is provided, the amount of the noble metal employed can be reduced, and a sufficient distance can be secured between the ground electrode and the discharge gap.
Although the aforementioned intermediate member is formed of, for example, a nickel alloy, which is generally known to have very high corrosion resistance, when the intermediate member is employed for a long period of time, the member may corrode to an unacceptable extent. Particularly, in the case of an intermediate member, which is provided in the vicinity of a discharge gap of a spark plug, corrosion due to cooling-heating cycles is likely to occur. Thus, demand has arisen for further improvement of the durability of a structure in which a noble metal tip is attached to a ground electrode via an intermediate member. Since attachment of a noble metal tip via an intermediate member may be applied not only to a ground electrode but also to a center electrode, the aforementioned problems may occur not only in the ground electrode but also in the center electrode.
The present invention has been accomplished for solving the aforementioned problems, and an object of the present invention is to improve the durability of a structure in which a noble metal tip is attached to a ground electrode or a center electrode via an intermediate member.
The present invention has been accomplished for solving the aforementioned problems at least partially, and may be carried out in the following modes or application examples.
In accordance with the present invention, there is provided a spark plug comprising:
a center electrode;
an insulator provided around the center electrode;
a metallic shell provided around the insulator; and
a ground electrode which is provided such that one end thereof is bonded to the metallic shell, and the other end faces the center electrode, characterized in that:
at least one of the center electrode and the ground electrode has thereon an intermediate member which connects the center electrode or the ground electrode to a noble metal tip;
the intermediate member has a tip-bonding portion to which the noble metal tip is bonded, and an electrode-bonding portion which is adjacent to the tip-bonding portion, which has a diameter greater than that of the tip-bonding portion, and which is bonded to the center electrode or the ground electrode;
the intermediate member contains nickel (Ni) as a main component, and also contains chromium (Cr) in an amount of 15 to 25 wt. %; and
the intermediate member contains, in a surface portion thereof, silicon (Si) in an amount per unit volume of 0.04 mg/mm3 to 0.12 mg/mm3, and aluminum (Al) in an amount per unit volume of 0.03 mg/mm3 to 0.10 mg/mm3.
In the spark plug according to application example 1, the intermediate member contains, in a surface portion thereof, silicon (Si) and aluminum (Al) in the aforementioned specific amounts per unit volume. Therefore, the intermediate member exhibits improved durability and corrosion resistance, and the spark plug, which includes the intermediate member, also exhibits improved durability and corrosion resistance.
In accordance with a second embodiment of the present invention, there is provided a spark plug according to application example 1, wherein, in the surface portion, the amount per unit volume of silicon (Si) is greater than that of aluminum (Al).
In the spark plug according to application example 2, there can be deterioration of the durability and corrosion resistance of the spark plug, which would be caused by formation of an intermetallic compound between aluminum (Al) and the noble metal in the intermediate member and/or caused by formation of aluminum nitride (AlN).
In accordance with a third embodiment of the present invention, there is provided a spark plug according to application examples 1 or 2, wherein the following relation is satisfied: 2.5≦Se/St wherein Se represents the area of a region formed by projection of the electrode-bonding portion on an imaginary plane parallel to a bonding surface between the electrode-bonding portion and the center electrode or the ground electrode, and St represents the transverse cross-sectional area of the tip-bonding portion. In the spark plug according to application example 3, heat transfer is likely to occur from the noble metal tip to at least one of the center electrode and the ground electrode via the intermediate member, and temperature elevation can be suppressed in the intermediate member. Therefore, metal diffusion can be suppressed in the intermediate member, and deterioration of the durability and corrosion resistance of the spark plug, which would otherwise be caused by metal diffusion, can be suppressed.
In accordance with a fourth embodiment of the present invention, there is provided a spark plug according to application example 3, wherein the transverse cross-sectional area St of the tip-bonding portion is 0.64 mm2 or more.
In the spark plug according to application example 4, heat transfer is likely to occur from the noble metal tip to at least one of the center electrode and the ground electrode via the intermediate member, and temperature elevation can be suppressed in the intermediate member. Therefore, degradation of the noble metal tip, which would otherwise occur in association with use of the spark plug, can be suppressed, and the spark plug exhibits improved durability.
In accordance with a fifth embodiment of the present invention, there is provided a spark plug according to any of application examples 1 to 4, wherein the intermediate member contains iron (Fe) in an amount by weight of 500 ppm or less.
In the spark plug according to application example 5, the intermediate member contains substantially no iron (Fe). Therefore, even when the spark plug is subjected to repeated cooling-heating cycles, the spark plug can maintain its durability and corrosion resistance.
The present invention may be carried out in various modes other than those described above; for example, in a mode of a spark plug production method.
A. Structure of Spark Plug:
The insulator 10 is formed through firing of a ceramic material such as alumina. The insulator 10 is a cylindrical member having, in the center thereof, an axial hole 12 in which the center electrode 20 and the metal terminal 40 are accommodated. The insulator 10 has a middle body portion 19 which has a large outer diameter and is provided at the middle of the insulator in an axial direction. A rear-end-side body portion 18 for achieving insulation between the metal terminal 40 and the metallic shell 50 is provided on the side of the metal terminal 40 with respect to the middle body portion 19. A front-end-side body portion 17 having an outer diameter smaller than that of the rear-end-side body portion 18 is provided on the side of the center electrode 20 with respect to the middle body portion 19. Furthermore, an elongated leg portion 13 is provided at the front end of the front-end-side body portion 17. The elongated leg portion 13 has an outer diameter which is smaller than that of the front-end-side body portion 17, and which decreases toward the side of the center electrode 20.
The metallic shell 50 is a cylindrical shell for surrounding and holding a portion of the rear-end-side body portion 18 to the elongated leg portion 13 of the insulator 10. In the present embodiment, the metallic shell 50 is formed of low-carbon steel. The metallic shell 50 includes a tool engagement portion 51, a threaded attachment portion 52, and a sealing portion 54. The tool engagement portion 51 of the metallic shell 50 is fitted with a tool (not illustrated) for attaching the spark plug 100 to the engine head 200. The threaded attachment portion 52 of the metallic shell 50 has a thread which is screwed into the threaded attachment hole 201 of the engine head 200. The sealing portion 54 of the metallic shell 50 is formed at the base of the threaded attachment portion 52 so as to assume a flange-like shape, and a circular gasket 5 formed through bending of a plate is inserted between the sealing portion 54 and the engine head 200. The front end surface 57 of the metallic shell 50 has a hollow circular shape, and, at the center thereof, the center electrode 20 projects from the elongated leg portion 13 of the insulator 10.
The center electrode 20, which is a rod-like member, includes a bottomed cylindrical electrode matrix 21, and a core 25 which is embedded in the electrode matrix 21 and has thermal conductivity higher than that of the electrode matrix 21. In the present embodiment, the electrode matrix 21 is formed of a nickel alloy containing nickel as a main component, and the core 25 is formed of copper or an alloy containing copper as a main component. The center electrode 20 is inserted into the axial hole 12 of the insulator 10 such that the front end of the electrode matrix 21 projects from the axial hole 12 of the insulator 10, and the center electrode 20 is electrically connected to the metal terminal 40 via a ceramic resistor 3 and a sealing body 4.
B. Structure of Ground Electrode:
An intermediate member 60 having corrosion resistance is connected to a side surface of the distal end portion 31 of the ground electrode 30, the side surface facing the front end portion 22 of the center electrode 20 with respect to the axis O. The intermediate member 60 includes a tip-bonding portion 61 to which a ground electrode tip 70 is welded, and an electrode-bonding portion 62 which is provided adjacent to the tip-bonding portion 61 (i.e., stacked on the tip-bonding portion 61), and which is welded to the ground electrode 30. The cross section of the electrode-bonding portion 62 perpendicular to the axis O (hereinafter the cross section may be referred to as “transverse cross section”) has an area greater than the transverse cross-sectional area of the tip-bonding portion 61. In the present embodiment, each of the tip-bonding portion 61 and the electrode-bonding portion 62 has a generally circular columnar shape; i.e., the transverse cross-sectional diameter (hereinafter the transverse cross-sectional diameter may be referred to simply as “diameter”) is almost uniform in the entirety of each of the portions 61 and 62. The electrode-bonding portion 62 has a diameter greater than that of the tip-bonding portion 61; i.e., the electrode-bonding portion 62 is radially enlarged with respect to the tip-bonding portion 61 so as to assume a flange-like shape. The intermediate member 60 having the aforementioned shape may be formed through any known technique, such as machining. In the present embodiment, the intermediate member 60 is formed through plastic processing (header processing).
Before discussing the welding of the ground electrode tip 70 or the ground electrode 30, it should be pointed out that each of the tip-bonding portion 61 and the electrode-bonding portion 62 of the intermediate member 60 does not necessarily strictly need to have a circular columnar shape; i.e., a circular flat end surface. For example, a protrusion may be provided on the surface of the electrode-bonding portion 62 which is welded to the ground electrode 30. Each of the tip-bonding portion 61 and the electrode-bonding portion 62 forming the intermediate member 60, the ground electrode tip 70, and the center electrode tip 90 may assume a shape other than a circular columnar shape; for example, a rectangular columnar shape.
Preferably, the tip-bonding portion 61 has a diameter greater than the transverse cross-sectional diameter of the ground electrode tip 70 so as to secure a sufficient bonding strength between the tip-bonding portion 61 and the ground electrode tip 70. In order to secure uniform flame propagation, the tip-bonding portion 61, which is provided in the vicinity of the spark gap, preferably has a small size; i.e., the tip-bonding portion 61 preferably has a small diameter. Therefore, in the present embodiment, the tip-bonding portion 61 is formed so as to have a diameter nearly equal to that of the ground electrode tip 70.
The reason why the electrode-bonding portion 62 is formed so as to have a diameter greater than that of the tip-bonding portion 61 is to facilitate welding of the intermediate member 60 to the ground electrode 30, and to enhance the bonding strength between the intermediate member 60 and the ground electrode 30 for improving bonding reliability. Also, in the present embodiment, the corrosion resistance of the intermediate member 60 is improved by adjusting the ratio of the transverse cross-sectional area Se (see
In the case where the intermediate member 60 is formed through plastic processing as described above, the percent processing increases as the diameter of the electrode-bonding portion 62 increases, and thus cracking is likely to occur in the electrode-bonding portion 62 during processing. Therefore, in consideration of processing accuracy, yield, etc., preferably, the maximum value of the ratio of the transverse cross-sectional area Se of the electrode-bonding portion 62 to the transverse cross-sectional area St of the tip-bonding portion 61 is adjusted to 3.5 (Se/St≦3.5).
Also, in the present embodiment, the durability of the ground electrode tip 70 is improved by achieving the relation: 2.5≦Se/St, and adjusting the transverse cross-sectional area St of the tip-bonding portion 61 to 0.64 mm2 or more. Hereinbelow will be described in detail the effect of improving the durability of the ground electrode tip 70 by adjusting the transverse cross-sectional area St of the tip-bonding portion 61 to the aforementioned value.
The intermediate member 60 is formed of, for example, a nickel alloy containing nickel (Ni) as a main component, and also containing at least chromium (Cr), silicon (Si), and aluminum (Al). More specifically, the intermediate member 60 contains chromium (Cr) in an amount of 15 to 25 wt. %, silicon (Si) in an amount (by weight) per unit volume of 0.04 mg/mm3 to 0.12 mg/mm3, and aluminum (Al) in an amount (by weight) per unit volume of 0.03 mg/mm3 to 0.10 mg/mm3. In the present embodiment, the entire intermediate member 60 has a uniform composition. Particularly preferably, the silicon (Si) content per unit volume of the intermediate member is greater than the aluminum (Al) content per unit volume thereof. When the intermediate member 60 has the aforementioned composition, the intermediate member 60 exhibits improved corrosion resistance. The relationship between the composition of the intermediate member 60 and the corrosion resistance thereof will be described hereinbelow in detail. The amount per unit volume of each component contained in the intermediate member may be determined, for example, as follows. Specifically, a sample having a specific size (e.g., 2 mm×2 mm) is obtained from the intermediate member (i.e., measurement target) through cutting, and the weight of the thus-cut sample is measured, to thereby determine the density of the intermediate member. The thus-cut sample is subjected to quantitative analysis by means of an EPMA (electron probe microanalyzer), to thereby determine the concentration (wt. %) of each component (element) forming the intermediate member (measurement target). The amount per unit volume of each component can be calculated by multiplying the above-determined density by the concentration of the component.
Preferably, the intermediate member 60, which is formed of an alloy, contains substantially no iron (Fe). However, even in the case where iron (Fe) is not intentionally added during production of the intermediate member 60, when a material forming the intermediate member 60 contains iron (Fe) as an impurity, iron (Fe) is inevitably incorporated into the intermediate member 60. In consideration of such inevitable incorporation of iron (Fe), preferably, the amount (by weight) of iron (Fe) contained in the intermediate member 60 is adjusted to 500 ppm or less.
Bonding between the intermediate member 60 and the ground electrode tip 70 may be carried out through, for example, fusion welding. Specifically, in the present embodiment, laser welding is carried out. Through fusion welding between the ground electrode tip 70 and the intermediate member 60, a fusion portion 80 is formed at the boundary between them. Bonding between the intermediate member 60 and the ground electrode 30 may be carried out through, for example, pressure welding. Specifically, in the present embodiment, resistance welding is carried out.
The ground electrode tip 70 is a member provided for the purpose of improving the spark erosion resistance of the ground electrode 30, and is a noble metal tip containing, as a main component, a noble metal having a high melting point. The ground electrode tip 70 may be formed of, for example, platinum (Pt), iridium (Ir), ruthenium (Ru), rhodium (Rh), or an alloy thereof. In the present invention, the ground electrode tip 70 is formed of a Pt—Rh alloy. The ground electrode tip 70 is formed so as to assume a generally circular columnar shape. As described above, the transverse cross-sectional diameter of the ground electrode tip 70 is almost equal to that of the tip-bonding portion 61.
C. Improvement of Durability and Corrosion Resistance of Spark Plug 100:
C-1. Composition of Intermediate Member 60
In the case of a chromium (Cr)-containing nickel (Ni) alloy such as Inconel (registered trademark) alloy, invasion of oxygen into the alloy is suppressed through formation of a chromium oxide coating film on the surface thereof, whereby high corrosion resistance is achieved. When the intermediate member 60 is formed of such a chromium-containing nickel alloy, the corrosion resistance of the intermediate member 60 can be improved. However, the intermediate member 60 is subjected to cooling-heating cycles (i.e., repeated temperature elevation and lowering) in association with repeated ignition of the spark plug. When the intermediate member 60 undergoes repeated expansion and contraction through such cooling-heating cycles, the chromium oxide coating film formed on the surface of the intermediate member 60 is damaged due to expansion and contraction, and oxygen may invade into the intermediate member 60, resulting in progress of corrosion of the intermediate member 60. When the vicinity of the intermediate member 60 is exposed to a high-temperature environment, metal diffusion proceeds in the intermediate member 60 or in the ground electrode tip 70 adjacent thereto, and an intermetallic compound or the like is formed in the member in which metal diffusion has proceeded. Thus, corrosion of the intermediate member 60 further proceeds through formation of such an intermetallic compound or the like therein.
When the intermediate member 60 of the present embodiment is formed through plastic processing as described above, in the interior of the intermediate member 60, residual strain exists at the site of bonding (i.e., joint) between the tip-bonding portion 61 and the electrode-bonding portion 62, and residual stress occurs at the bonding site. The progress of corrosion is promoted at a site where residual stress occurs, as compared with a site where residual stress does not occur. Therefore, when the chromium oxide coating film covering the surface of the aforementioned bonding site (joint) is damaged, corrosion proceeds from the damaged portion, and a portion of the intermediate member 60 (tip-bonding portion 61) may be removed (i.e., separated) from the bonding site. Thus, when corrosion of the intermediate member 60 progressed, ultimately, the ground electrode tip 70, which is bonded to the intermediate member 60, may be removed (i.e., become separated) therefrom. Therefore, suppression of corrosion of the intermediate member 60 is important for prolonging the service life of the spark plug 100.
In the present embodiment, as described above, the intermediate member 60 contains silicon (Si) in an amount per unit volume of 0.04 mg/mm3 to 0.12 mg/mm3 and aluminum (Al) in an amount per unit volume of 0.03 mg/mm3 to 0.10 mg/mm3. Thus, since the intermediate member 60 contains, in a surface portion thereof, specific amounts of silicon (Si) and aluminum (Al), a layer of an alumina-silica mixture (hereinafter may be referred to simply as “mixture layer”) is formed inside of the chromium oxide coating film at the surface portion of the intermediate member 60. Conceivably, improvement of the durability of the intermediate member 60 in the present embodiment is attributed to the fact that the mixture layer formed inside of the chromium oxide coating film exhibits the effect of reinforcing the chromium oxide coating film and suppressing damage to the film (i.e., anchoring effect). Therefore, conceivably, even when the intermediate member 60 is subjected to cooling-heating cycles, expansion/contraction and damage of the chromium oxide film are suppressed, resulting in improvement of durability.
The greater the amounts of silicon (Si) and aluminum (Al) contained in a surface portion of the intermediate member 60, the greater the amount (thickness) of the mixture layer formed at the surface of the intermediate member 60. Therefore, in order to obtain sufficient effects through formation of the mixture layer, preferably, the silicon (Si) content per unit volume of the intermediate member 60 is adjusted to 0.04 mg/mm3 or more, and the aluminum (Al) content per unit volume of the intermediate member 60 is adjusted to 0.03 mg/mm3 or more.
Meanwhile, when the aluminum (Al) content of the intermediate member 60 is excessively high, an intermetallic compound is likely to be formed between aluminum (Al) and a noble metal diffused from the ground electrode tip 70 or the fusion portion 80 (e.g., platinum (Pt) or iridium (Ir)) at a site where aluminum (Al) is present (e.g., at the surface portion of the intermediate member 60). Since the thus-formed intermetallic compound is harder and more brittle than the nickel alloy forming the intermediate member 60, formation of the intermetallic compound may cause deterioration of the strength and durability of the intermediate member 60. Therefore, when aluminum (Al) is caused to be present at least at the surface portion of the intermediate member 60, preferably, the aluminum (Al) content per unit volume of the intermediate member 60 is adjusted to 0.10 mg/mm3 or less, in order to suppress corrosion of the intermediate member 60 and to improve the durability thereof.
When the silicon (Si) content of the intermediate member 60 is excessively high, a eutectic structure is likely to be formed between silicon (Si) and a noble metal diffused from the ground electrode tip 70 or the fusion portion 80 (e.g., platinum (Pt)) at a site where silicon (Si) is present (e.g., at the surface portion of the intermediate member 60). The thus-formed eutectic structure has a melting point lower than that of the nickel alloy, and, upon use of the spark plug 100, the temperature of the intermediate member 60 may become higher than the melting point of the eutectic structure. When the temperature of the intermediate member 60 becomes higher than the melting point of the eutectic structure, the eutectic structure may liquefy in the intermediate member 60, resulting in deterioration of the strength and durability of the intermediate member 60. In addition, when the silicon (Si) content of the intermediate member 60 is high, the silicon (Si) content of the fusion portion 80 also increases, resulting in an increase in amount of silicon (Si) which diffuses in the ground electrode tip 70. Thus, an increasing amount of a low-melting-point eutectic structure is formed between silicon (Si) and a noble metal (e.g., platinum (Pt)) in the ground electrode tip 70 or the fusion portion 80, and spark erosion resistance is impaired. Therefore, when silicon (Si) is caused to be present at least at the surface portion of the intermediate member 60, preferably, the silicon (Si) content of the intermediate member 60 is adjusted to 0.12 mg/mm3 or less, in order to improve the durability of the intermediate member 60.
In the case where the intermediate member 60 contains aluminum (Al) and silicon (Si), when the amount by mole of aluminum (Al) is nearly equal to that of silicon (Si), a ternary intermetallic compound of aluminum (Al), silicon (Si), and a noble metal (e.g., Pt) is likely to be segregated. Segregation of such an intermetallic compound may progress corrosion of the intermediate member 60. Therefore, preferably, the amount by mole of aluminum (Al) is not equal to that of silicon (Si) in the intermediate member 60.
Furthermore, when the aluminum (Al) content of the intermediate member 60 is greater than the silicon (Si) content thereof, aluminum (Al) is likely to react with nitrogen which has passed through the chromium oxide coating film, to thereby form aluminum nitride (AlN). When aluminum nitride (AlN) is formed in the intermediate member 60, cracks may be generated in the intermediate member 60, and elongation of cracks may occur therein, resulting in progress of corrosion. In the case where an alumina-silica mixture layer is formed, when the aluminum (Al) content of the intermediate member 60 is higher, the alumina content of the mixture layer becomes higher, whereas when the silicon (Si) content of the intermediate member 60 is higher, the silica content of the mixture layer becomes higher. Since the nitrogen impermeability of silica is superior to that of alumina, when the silica content of the mixture layer is increased by increasing the silicon (Si) content of the intermediate member 60, the ability of the intermediate member 60 to block nitrogen can be enhanced. Thus, when the ability of the intermediate member 60 to block nitrogen is enhanced, formation of aluminum nitride (AlN) can be suppressed, and corrosion resistance can be improved. Therefore, at least, the silicon (Si) content per unit volume of the intermediate member 60 is preferably adjusted to be higher than the aluminum (Al) content per unit volume thereof.
Aluminum (Al) has an atomic weight of 27.0, and silicon (Si) has an atomic weight of 28.1. That is, when the silicon (Si) content per unit volume of the intermediate member is adjusted to be 1.04 times the aluminum (Al) content per unit volume thereof, the amount by mole of silicon (Si) becomes equal to that of aluminum (Al). Therefore, preferably, the silicon (Si) content per unit volume of the intermediate member is adjusted to be more than 1.04 times the aluminum (Al) content per unit volume thereof.
C-2. Configuration of Intermediate Member 60
As shown in
Since the nickel-chromium alloy forming the intermediate member 60 has a thermal conductivity lower than that of the noble metal forming the ground electrode tip 70, heat transfer is less likely to occur from the ground electrode tip 70 to the ground electrode 30 via the intermediate member 60. When heat cannot be transferred to the ground electrode 30, the temperature of the intermediate member 60 or the fusion portion 80 becomes higher, and thus metal diffusion is likely to occur. When metal diffusion proceeds, as described above, an increasing amount of an intermetallic compound or a eutectic structure is formed, and the durability and corrosion resistance of the intermediate member 60 are impaired. Particularly, in the case of the present embodiment, in which the intermediate member 60 is produced through plastic processing, and residual stress occurs in the vicinity of the bonding site between the tip-bonding portion 61 and the electrode-bonding portion 62, durability is likely to be impaired in the vicinity of the bonding site. In the present embodiment, the contact area between the electrode-bonding portion 62 and the ground electrode 30 is increased by adjusting the ratio Se/St to fall within the aforementioned range, so that heat is likely to be transferred to the ground electrode 30 via the intermediate member 60. When such heat transfer is likely to occur, temperature elevation can be suppressed in the intermediate member 60, and progress of corrosion of the intermediate member 60, which would otherwise be caused by cooling-heating cycles, can be suppressed. In addition, in the present embodiment, heat is likely to be transferred from the ground electrode tip 70 to the ground electrode 30 via the tip-bonding portion 61 by adjusting the transverse cross-sectional area St of the tip-bonding portion 61 to fall within the aforementioned range. Thus, when heat is likely to be transferred from the ground electrode tip 70 to the ground electrode 30, the temperature elevation of the ground electrode tip 70 in association with ignition of the spark plug can be suppressed, and the deterioration over time of the ground electrode tip 70, which would otherwise be caused by temperature elevation, can be suppressed.
A plurality of intermediate members (samples) were prepared under the same conditions, except for aluminum (Al) content per unit volume, silicon (Si) content per unit volume, and Se/St. The durability and corrosion resistance of each of the thus-prepared intermediate members were evaluated.
Each intermediate member (sample) was formed from a nickel alloy containing nickel (Ni) in an amount of about 73 wt. % and chromium (Cr) in an amount of 25 wt. %. A noble metal tip (ground electrode tip) formed of platinum (Pt) and having the same size (transverse cross-sectional diameter: 0.7 mm) was welded to each intermediate member (sample). When Se/St was varied, the diameter of a tip-bonding portion was maintained constant (diameter: 0.7 mm, St=0.38 mm2) in the respective intermediate members (samples), and the diameter of an electrode-bonding portion was varied therein.
The durability and corrosion resistance of each intermediate member (sample) were evaluated as follows. Specifically, each intermediate member (sample) was subjected to 5,000 cooling-heating cycles, each cycle including heating by means of a gas burner at 1,200° C. and stop of the heating, and then a cross section of the intermediate member was observed. FIGS. 5(A) and 5(B) show an intermediate member which was subjected to the aforementioned cooling-heating cycles.
In
As shown in
As shown in
Each of the intermediate members (samples 17 and 18) and a noble metal tip formed of platinum (Pt) were attached to a ground electrode of a spark plug having the same configuration. The spark plug incorporating the intermediate member was attached to an engine having the same configuration (naturally aspirated 6-cylinder engine, 2,000 cc). Thereafter, the engine was operated in the same manner as in the case where an automobile was operated for repeated cycles, each including full-throttle acceleration and idling. The aforementioned operation cycles were repeated for 100 hours, and then the spark plug was removed from the engine. Subsequently, a cross section of the intermediate member attached to the spark plug was observed in the same manner as shown in
As shown in
“Gap increase” shown in
D. Modifications:
The present invention is not limited to the aforementioned examples and embodiments, and various other embodiments may be implemented without departing from the scope of the invention. For example, the below-described modifications may be carried out.
D1. Modification 1
In the aforementioned embodiments, the silicon (Si) and aluminum (Al) contents per unit volume of the intermediate member 60 are uniform throughout the member 60. However, the silicon (Si) or aluminum (Al) content per unit volume of the intermediate member 60 may be non-uniform therein, so long as the silicon (Si) and aluminum (Al) contents per unit volume of the intermediate member 60 fall within the aforementioned ranges at least in a surface portion of the member 60. As described above, the effect obtained by adjusting the silicon (Si) and aluminum (Al) contents per unit volume of the intermediate member to fall within specific ranges is attributed to the fact that an alumina-silica mixture layer is formed inside of a chromium oxide coating film formed at the surface of the intermediate member. Therefore, the silicon (Si) or aluminum (Al) content per unit volume of the intermediate member may be non-uniform therein, so long as the silicon (Si) and aluminum (Al) contents per unit volume of the intermediate member fall within the aforementioned ranges in a surface portion thereof in which an alumina-silica mixture layer can be formed through migration of silicon (Si) and aluminum (Al) toward the surface by metal diffusion (e.g., at least a portion having a thickness of 200 μm as measured from the surface).
For production of an intermediate member in which the composition of a surface portion differs from that of another portion (center portion), for example, a circular columnar member having, at the center thereof, a through-hole extending in a height direction (member corresponding to the surface portion) may be provided, and a circular columnar member corresponding to the center portion may be pressed into the through-hole, or a material forming the center portion may be charged into the through-hole. Alternatively, a circular columnar member corresponding to the center portion may be provided, and a metal film having a composition corresponding to that of the surface portion may be formed on the side surface of the member through, for example, plating treatment. For production of an intermediate member having a structure including a tip-bonding portion and an electrode-bonding portion, a circular columnar member having the aforementioned dual structure may be subjected to plastic processing (header processing).
D2. Modification 2
In the embodiments described above, the intermediate member 60 is provided on the ground electrode 30. However, the present invention may be applied to the center electrode 20 in place of or in addition to the ground electrode 30. Specifically, an intermediate member having the same configuration as described in the embodiments may be provided between the center electrode 20 and the center electrode tip 90. Even in such a case, similar effects can be obtained through improvement of the durability and corrosion resistance of the intermediate member.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2011-029414 | Feb 2011 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2012/000937 | 2/13/2012 | WO | 00 | 8/9/2013 |