The present invention relates to the field of acoustic technology, and more particularly, to a speaker module and a sound-adsorbing material.
With the progress of the society and the development of technology, wearable electronic products have become increasingly lighter and thinner, and traditional sound-adsorbing materials have failed to meet the demand for tuning and calibrating acoustic performance of speakers in the miniature speaker industry. Therefore, people begin to constantly try or develop new types of sound-adsorbing materials. It has been verified that placing a porous sound-adsorbing material in the rear acoustic cavity of the speaker device can effectively improve the acoustic performance of the speaker.
At present, commonly used new sound-adsorbing materials with good effects include natural zeolite, activated carbon, white carbon black, sepiolite fibers, artificial synthetic zeolite powder with a silica-alumina mass ratio of 200 or more, or a mixture of the above materials. Although the above sound-adsorbing material has a good effect of improving the acoustic performance of the speaker, it has been found during the later long-term (from several hours to dozens of days) application monitoring process that the above sound-adsorbing material has serious failure problems, especially in extreme environments (in environments with a high temperature, high humidity, an organic volatile solvent atmosphere and the like), the speed and extent of failure are more apparent.
Therefore, there is an urgent need for a speaker module that is filled with a special sound-adsorbing material in the rear sound cavity to ensure long-term stability of the acoustic performance of the speaker in various environments.
In view of the above problems, an object of the present invention is to provide a speaker module to solve the problem that the current sound-adsorbing material inside the speaker cannot be used for a long period of time, and the sound absorption deteriorates and may even fail.
The speaker module provided by the present invention includes a housing and a speaker unit accommodated in the housing. The speaker unit separates the cavity formed by the housing into a front sound cavity and a rear sound cavity, wherein a sound-adsorbing material is filled in the rear sound cavity; heteroatoms are doped in a crystal structure of the sound-adsorbing material, wherein
The heteroatoms are sodium ions or arsenic ions.
The heteroatoms generate a repulsive force on alien molecules adsorbed by the sound-adsorbing material.
The sound-adsorbing material is one or a mixture of two or more of natural zeolite, activated carbon, white carbon black, sepiolite fibers, zeolite powder.
The sound-adsorbing material is doped with heteroatoms by a replacement method or hydrothermal synthesis method.
The heteroatoms partially replace original elements in the sound-adsorbing material or fill the defective elements in the sound-adsorbing material.
A compound containing heteroatoms is added in a sound-adsorbing material and a curing reaction is performed.
A compound containing heteroatoms is added to a raw material for synthesizing the sound-adsorbing material, and a crystallization reaction is performed.
A sound hole is provided on the housing, the front sound cavity communicates with the sound hole, and the rear sound cavity is sealed; a damping hole is arranged on a position of the housing corresponding to the rear sound cavity, and a damping net is arranged at a position of the housing corresponding to the damping hole.
The speaker unit comprises a unit housing, a magnetic circuit system accommodated in a cavity formed by the unit housing, and a vibration system. The magnetic circuit system includes a magnetic conduction yoke fixed to the unit housing, a magnet disposed at a central position of the magnetic conduction yoke, and a washer arranged on one side of the magnet far away from the magnetic conduction yoke. The vibration system includes a vibrating diaphragm, a voice coil fixed on one side of the vibrating diaphragm, and a reinforcing part fixed at a central position of the vibrating diaphragm.
With the speaker module according to the present invention described above, particular heteroatoms are intentionally doped into the crystal structure of the sound-adsorbing material to replace part of the atoms in the sound-adsorbing material or to dispose the heteroatoms in the lattice of the sound-adsorbing material (a space grillwork where atoms are orderly arranged in crystals), and a repulsive force exerted on the adsorbed alien molecules by specific heteroatoms prevents the adsorption of alien molecules by the sound-adsorbing material or reduces the adsorption degree of the alien molecules and ensures that the performance does not fail during use. This will ensure long-term stability of the acoustic performance of the speaker module.
To achieve the foregoing and related objectives, one or more aspects of the present invention include the features hereinafter specifically described and particularly pointed out in the claims. The following description and accompanying drawings set forth in detail certain illustrative aspects of the present invention. However, these aspects are indicative of only a few of the various ways in which the principles of the invention may be employed. In addition, the present invention is intended to include all these aspects and their equivalents.
By reference to the following description in combination with the drawings and the claims, and with a fuller understanding of the present invention, other objects and results of the present invention will be clearer and easily understood. In the drawings:
The reference numerals include: oxygen defect 01, silicon defect 02, heteroatom 03, steel sheet 1, 1′, housing 2, 2′, sound-adsorbing material 3, 3′, damping hole 4, 4′, and isolation net 5, 5′.
The same reference numbers in all drawings indicate similar or corresponding features or functions.
In the following description, for the purposes of explanation, numerous specific details are elaborated in order to provide a thorough understanding of one or more embodiments. However, it is apparent that these embodiments may also be implemented without these specific details. In other instances, well-known structures and devices are shown in block diagrams in order to facilitate description of one or more embodiments.
At present, sound-adsorbing materials easily adsorb alien molecules (for example, solvents such as ethanol, and aromatic hydrocarbon volatiles of small molecules, etc.), and thus cause blockages in microscopic pore-channel structures thereof, and cannot be desorbed rapidly in a short time, thereby causing irreversible failure in improving acoustic performance of the speaker by the sound-adsorbing materials.
Further, from the microscopic point of view, it is inevitable that heteroatoms or missing atoms enter the crystal system of the sound-adsorbing material during the crystal growth process of the sound-adsorbing material, or there exists a lattice defect during the crystal growth of the sound-adsorbing material crystal. These abnormal points will cause instable crystal charge distribution, form a “defective point” with a polarity, further cause the sound-adsorbing material (or sound-adsorbing particles) to easily adsorb alien molecules in the course of use and not to easily be desorbed, and eventually result in performance failure in the sound-adsorbing material.
To this end, the present invention intentionally “dopes” certain heteroatoms into the crystal structure of the sound-adsorbing material to replace the original atoms of the sound-adsorbing material or to fill up the defect points of the sound-adsorbing material. Through the repulsive force generated by these specific heteroatoms to the adsorbed alien molecules, the sound-adsorbing material does not adsorb alien molecules or to some extent reduce the degree of adsorption of alien molecules, thereby ensuring that the sound-adsorbing material will not gradually fail during use.
To describe in detail the speaker module and the method of doping the heteroatoms in the sound-adsorbing material of the present invention, specific embodiments of the present invention will be described in detail below with reference to the accompanying drawings.
The speaker module of the embodiment of the present invention includes a housing and a speaker unit accommodated in the housing. The speaker unit separates a cavity formed by the housing into a front sound cavity and a rear sound cavity. A sound-adsorbing material is filled in the rear sound cavity of the speaker module, and specific heteroatoms are doped in the crystal structure of the sound-adsorbing material to ensure long-term effectiveness of the sound-adsorbing material.
Specifically, in a specific embodiment of the present invention, the sound-adsorbing material may be one or a mixture of two or more of natural zeolite, activated carbon, white carbon black, sepiolite fibers, artificial synthetic zeolite powder having a silica-alumina mass ratio of 200 or more; heteroatoms may be sodium ions or arsenic ions, etc. Here, the type of heteroatoms added to the sound-adsorbing material is determined based on the type of the alien molecules adsorbed by the sound-adsorbing material, as long as it can be ensured that the incorporation of heteroatoms does not have an excessive effect on the performance of the sound-adsorbing material, and heteroatoms capable of making the sound-adsorbing material generate repulsion to the adsorbed alien molecules can be added to the sound-adsorbing material. Specifically, the heteroatoms may be adjusted and replaced correspondingly according to difference in the production requirements and the use environment of the speaker module, and are not specifically limited in the present invention.
As an example, the speaker module of the present invention and the heteroatoms doped in the sound-adsorbing material thereof will be described in detail in the following by taking the sound-adsorbing material of zeolite powder with a silica-alumina mass ratio of 200 or more as an example.
Specifically,
In a specific embodiment of the present invention, doping mainly refers to utilizing other elements or atomic groups with properties similar to that of silicon and aluminum to partially replace the silicon and aluminum in the zeolite frame, or fill up defective elements to form a new frame. Specifically, the method for doping the heteroatoms in the sound-adsorbing material mainly includes the following two methods: a replacement method and a hydrothermal synthesis method.
Among them, the replacement method is mainly to place a highly volatile compound containing a doping atom and the zeolite powder in a certain temperature environment for solid-phase reaction; the synthesis method is mainly to add a compound containing a doping element to the synthetic raw material at a certain temperature to perform the crystallization reaction. The purpose of doping with heteroatoms mainly includes two aspects: on one hand, due to the fact that crystal materials (sound-adsorbing materials) cannot be perfectly latticed during the growth process, there must be some missing atoms. The missing sites are relatively strong in activity, quite easy to adsorb and combine with alien molecules, and are difficult to desorb, thus results in failure in improving acoustic performance of the speaker by the sound-adsorbing material. At this time, the purpose of doping the heteroatoms is to make up for the defective sites of the sound-adsorbing material crystal and reduce the absorption of the alien molecules by the sound-adsorbing material.
As shown in
On the other hand, most of the alien molecules are polar molecules. While in the alumina tetrahedron of zeolite material, aluminum shows positive tervalence, therefore the alumina tetrahedron will carry a negative charge, and the zeolite material can easily adsorb alien molecules. By doping specific heteroatoms, the polarity of the sound-adsorbing material is changed or canceled so that the zeolite material generates a repulsive force to the alien molecules. The alien molecules cannot adsorb the material, which can ensure that the microscopic pore-channel structure of the sound-adsorbing material is unblocked, the sound-adsorbing material does not gradually fail during use, and further the stability of the new type of sound-adsorbing material in improving acoustic performance of the miniature speaker products is improved.
Specifically, the following process of performing heteroatom doping to the sound-adsorbing material is described in detail with reference to specific embodiments.
As shown in
The speaker unit comprises a unit housing, a magnetic circuit system accommodated in a cavity formed by the unit housing, and a vibrating system. The magnetic circuit system includes a magnetic conduction yoke fixed to the unit housing, a magnet disposed at the center of the magnetic conduction yoke, and a washer arranged on a side of the magnet far from the magnetic conduction yoke. The vibrating system includes a vibrating diaphragm, a voice coil fixed on one side of the vibrating diaphragm, and a reinforcing part fixed at the center of the vibrating diaphragm. The rear sound cavity 3 is filled with a sound-adsorbing material 3 doped with heteroatoms, and is isolated from the cavity which is not filled with the sound-adsorbing material 3 by a partition net 5.
In the first embodiment, the sound-adsorbing material 3 is zeolite powder having a silica-alumina mass ratio of 200 or more. The sound-adsorbing material 3 is directly filled into the rear sound cavity of the speaker module, and is doped with sodium ions by the sodium ion replacement method. The conditions for reliability test of the speaker module are as follows: thirty sample speaker modules (the rear sound cavity of each speaker module sample is filled with a sound-adsorbing material 3 doped with sodium ions), thirty speaker modules with unfilled rear sound cavities, and thirty speaker modules with the rear sound cavities filled with common sound-adsorbing materials, and all are energized at 50° C. for 48 hours. The comparison of the test results (the average value of thirty test results are taken respectively) is shown in Table 1 below:
From the comparison results in Table 1, it can be seen that the new sound-adsorbing material 3 after being doped with sodium ions slightly reduces the effect in improving the acoustic performance of the speaker module (F0 becomes higher by 8 Hz), but from the results of the reliability test (high-temperature power-on), the failure rate of the speaker modules filled with a sound-adsorbing material undoped with sodium ions is about 32%, and the failure rate of speaker modules filled with a sound-adsorbing material doped with sodium ions is only 13%. It can be seen that the sound-adsorbing material after heteroatom doping treatment is significantly more stable than the untreated sound-adsorbing material during use of the speaker module.
The results of elemental analysis of the sound-adsorbing material before and after being doped with sodium ions are shown in Table 2 below:
It can be seen from Table 2 that the content of sodium element in the sound-adsorbing material after the sodium ion replacement treatment is significantly increased, and the repelling ability of the sound-adsorbing material against alien molecules also becomes stronger.
As shown in
The speaker unit comprises a unit housing, a magnetic circuit system accommodated in a cavity formed by the unit housing, and a vibrating system. The magnetic circuit system includes a magnetic conduction yoke fixed to the unit housing, a magnet arranged at the center of the magnetic conduction yoke and a washer arranged on one side of the magnet far from the magnetic conduction yoke. The vibrating system includes a vibrating diaphragm, a voice coil fixed on one side of the vibrating diaphragm, and a reinforcing part fixed at the center of the vibrating diaphragm. The rear sound cavity is filled with a sound-adsorbing material 3′ doped with heteroatoms, and is isolated from the cavity which is not filled with the sound-adsorbing material by a partition net 5′.
In this second embodiment, the sound-adsorbing material is zeolite powder having a silica-alumina mass ratio of 200 or more. The sound-adsorbing material 3′ is directly filled into the rear sound cavity of the speaker module, and the sound-adsorbing material 3′ is doped with sodium ions through a sodium ion hydrothermal synthesis method. The conditions for reliability test of the speaker module are as follows: thirty sample speaker modules (the rear sound cavity of each speaker module sample is filled a sound-adsorbing material 3′ doped with sodium ions), thirty speaker modules with unfilled rear sound cavities, and thirty speaker modules with the rear sound cavities filled with common sound-adsorbing materials, all are energized at 50° C. for 48 hours. The comparison of the test results (the average value of thirty test results are taken respectively) is shown in Table 3 below:
From the comparison results in Table 3, it can be seen that the new sound-adsorbing material 3′ doped with sodium ions slightly reduces its effectiveness in improving the acoustic performance of the speaker module (F0 becomes higher by 8 Hz), but results from the reliability test (high-temperature energization), the failure rate of the speaker module filled with a sound-adsorbing material undoped with sodium ions is about 26%, and the failure rate of the speaker module filled with a sound-adsorbing material doped with sodium ions is only 9.24%. It can be known that the sound-adsorbing material 3′ after heteroatom doping treatment is significantly more stable than the untreated sound-adsorbing material during use of the speaker module.
According to the speaker module of the present invention, the doping of the heteroatoms will reduce the effect in improvement of acoustic performance of the speaker by the sound-adsorbing material to a certain extent. This is mainly because the doped heteroatoms may have a destructive effect on the crystal structure of the original sound-adsorbing material. As a result, the pore-channel structure of the material is changed, and the effect of improving the acoustic performance of the miniature speaker is deteriorated. However, the slight doping of heteroatoms will only reduce the improvement effect by about 5%. Seen from the results of the reliability tests, the addition of heteroatoms can improve the stability of the sound-adsorbing material in improving acoustic performance of the speaker module during long-term energization. Thus, stable performance of the speaker during a long period of use, a simple process and an apparent effect are ensured.
The speaker module according to the present invention is described above by way of example with reference to the accompanying drawings. However, those skilled in the art should understand that, for the speaker module proposed by the present invention described above, various improvements can be made without departing from the content of the present invention. Therefore, the scope of the present invention is subject to the attached claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201510510460.3 | Aug 2015 | CN | national |
This application is a continuation of International Application No. PCT/CN2015/098051, filed on Dec. 21, 2015, which claims priority to Chinese Patent Application No. 201510510460.3, filed on Aug. 19, 2015, both of which are hereby incorporated by reference in their entireties.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2015/098051 | 12/21/2015 | WO | 00 |