The present invention relates to an SPF booster for use in alcohol based sunscreen formulations. In particular, the present invention relates to an SPF booster comprising a multistage polymeric particle, comprising: a core comprising polymerized units of a monoethylenically unsaturated carboxylic acid core monomer and a non-ionic ethylenically unsaturated core monomer; an inner shell comprising polymerized units of a non-ionic ethylenically unsaturated inner shell monomer; a monoethylenically unsaturated carboxylic acid inner shell monomer and an aliphatic inner shell monomer; an outer shell comprising polymerized units of a non-ionic ethylenically unsaturated outer shell monomer; an aliphatic outer shell monomer; a monoethylenically unsaturated non-carboxylic acid outer shell monomer and an ethylenically unsaturated surfactant outer shell monomer; wherein the core, when dry, contains a void; and wherein the multistage polymeric particle has an average particle size, when dry, of 50 to 1,000 nm.
The damaging effects of sunlight on human skin are well documented. Six percent of the solar energy reaching the Earth's surface is ultraviolet (UV) radiation having a wavelength of 290 to 400 nm. This radiation is divided into two components: (i) low energy UVA radiation having a wavelength of 320 to 400 nm and (ii) high energy UVB radiation having a wavelength of 290 to 320 nm. While the UV portion of solar energy is relatively small, it induces nearly 99% of all the side effects from sunlight exposure. High energy UVB radiation, for example, is responsible for producing sunburn, appearance of skin aging and skin cancer. Low energy UVA radiation, for example, is responsible for inducing direct tanning and erythema (abnormal redness) of the skin and contributes to the appearance of skin aging.
By avoiding direct exposure to sunlight, individuals can avoid the serious effects caused by exposure to UV radiation. However, because of the nature of their work, it is challenging for some people to avoid such exposure. In addition, other people voluntarily expose their skin to the sun, e.g., to tan, sometimes to extremes. Therefore, protection against the harmful effects of the sun is important.
Protection from the harmful effects of UV radiation exposure is available in the form of both topically applied formulation containing at least one physical UV blocker, or at least one chemical UV absorber, or combinations thereof. Physical blockers include active ingredients such as, titanium dioxide, zinc oxide and red petrolatum. Chemical absorbers include active ingredients, such as, paraaminobenzoic acid (more commonly known as PABA), which are generally transparent when applied and act by absorbing UV radiation, offering selective protection against certain UV wave bands, depending on the absorption spectrum of the active ingredient in the formulation.
The effectiveness of a given sunscreen formulation is assessed by how well it protects the skin in terms of a Sun Protection Factor (SPF) which is defined as the ratio of the amount of energy required to produce a minimal erythema on sunscreen protected skin to the amount of energy required to produce the same level of erythema on unprotected skin.
A number of the chemical absorbers and physical blockers, herein after referred to as “UV radiation absorbing agents,” typically used in sunscreen formulations reportedly have adverse toxicological effects. Therefore, it is desirable to reduce the level of UV radiation absorbing agents present in sunscreen formulations without reducing the SPF protection. Accordingly, a variety of SPF boosters have been developed for use in water based sunscreen formulations to reduce the level of UV radiation absorbing agents without a reduction in the SPF protection provided.
To that end, an approach to improving UV radiation absorption of a composition containing at least one UV radiation absorbing agent through the incorporation of a voided latex particle is disclosed in U.S. Pat. No. 5,663,213 to Jones et al. Jones et al. disclose a method for improving UV radiation absorption of a composition, comprising: adding to said composition from about 0.1 weight percent to about 50 weight percent of latex particles, based on total weight non-volatiles, wherein the composition comprises at least one UV radiation absorbing agent, wherein the latex particles contain a void and have a particle size of from about 100 nm to about 380 nm, and wherein the latex particles are added to increase the UV radiation absorption of the composition.
Notwithstanding, alcohol-based sunscreen products (e.g., sprays) account for up to 50% of the market. High alcohol content (e.g., >60 wt % ethanol) sunscreens are a popular format for which many conventional SPF booster offerings are unsuited.
Accordingly, there remains a need for new SPF booster compositions that provide effective SPF boosting capability and that are suited for incorporation in alcohol based sunscreen formulations.
The present invention provides an SPF booster for use in alcohol based sunscreen formulations, wherein the SPF booster comprises a multistage polymeric particle, comprising: (i) a core, wherein the core comprises, as polymerized units, 20 to 60 wt %, based on weight of the core, of a monoethylenically unsaturated carboxylic acid core monomer; and 40 to 80 wt %, based on weight of the core, of a non-ionic ethylenically unsaturated core monomer; (ii) an inner shell, wherein the inner shell comprises, as polymerized units, 90 to 99.9 wt %, based on weight of the inner shell, of a non-ionic ethylenically unsaturated inner shell monomer; 0.01 to 9.95 wt %, based on weight of the inner shell, a monoethylenically unsaturated carboxylic acid inner shell monomer; and 0.05 to 9.99 wt %, based on weight of the inner shell, of an aliphatic inner shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof; (iii) an outer shell, wherein the outer shell comprises, as polymerized units, 10 to 45 wt %, based on weight of the outer shell, of a non-ionic ethylenically unsaturated outer shell monomer; 50 to 88.9 wt %, based on weight of the outer shell, of an aliphatic outer shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof; 0.1 to 10 wt %, based on weight of the outer shell, of a monoethylenically unsaturated non-carboxylic acid outer shell monomer; and, 1 to 25 wt %, based on weight of the outer shell, of an ethylenically unsaturated surfactant outer shell monomer; wherein the core, when dry, contains at least one void; and wherein the multistage polymeric particle has an average particle size, when dry, of 50 to 1,000 nm.
The present invention provides an SPF booster for use in alcohol based sunscreen formulations, wherein the SPF booster comprises a multistage polymeric particle, comprising: (i) a core, wherein the core comprises, as polymerized units, 20 to 60 wt %, based on weight of the core, of a monoethylenically unsaturated carboxylic acid core monomer; and 40 to 80 wt %, based on weight of the core, of a non-ionic ethylenically unsaturated core monomer; (ii) an inner shell, wherein the inner shell includes a first inner shell and a second inner shell; wherein the first inner shell comprises, as polymerized units, 90 to 99.9 wt %, based on weight of the first inner shell, of a non-ionic ethylenically unsaturated first inner shell monomer; and 0.1 to 10 wt %, based on weight of the first inner shell, a monoethylenically unsaturated carboxylic acid first inner shell monomer; and a second inner shell, wherein the second inner shell comprises, as polymerized units, 90 to 99.5 wt %, based on weight of the second inner shell, of a non-ionic ethylenically unsaturated second inner shell monomer; and 0.5 to 10 wt %, based on weight of the second inner shell, of an aliphatic second inner shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof; (iii) an outer shell, wherein the outer shell comprises, as polymerized units, 10 to 45 wt %, based on weight of the outer shell, of a non-ionic ethylenically unsaturated outer shell monomer; 50 to 88.9 wt %, based on weight of the outer shell, of an aliphatic outer shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof; 0.1 to 10 wt %, based on weight of the outer shell, of a monoethylenically unsaturated non-carboxylic acid outer shell monomer; and, 1 to 25 wt %, based on weight of the outer shell, of an ethylenically unsaturated surfactant outer shell monomer; wherein the core, when dry, contains at least one void; and wherein the multistage polymeric particle has an average particle size, when dry, of 50 to 1,000 nm.
The present invention provides an SPF booster for use in alcohol based sunscreen formulations, wherein the SPF booster comprises a multistage polymeric particle, comprising: (i) a core, wherein the core comprises, as polymerized units, 20 to 60 wt %, based on weight of the core, of a monoethylenically unsaturated carboxylic acid core monomer; and 40 to 80 wt %, based on weight of the core, of a non-ionic ethylenically unsaturated core monomer; (ii) an inner shell, wherein the inner shell includes a first inner shell and a second inner shell; wherein the first inner shell comprises, as polymerized units, 90 to 99.9 wt %, based on weight of the first inner shell, of a non-ionic ethylenically unsaturated first inner shell monomer; and 0.1 to 10 wt %, based on weight of the first inner shell, a monoethylenically unsaturated carboxylic acid first inner shell monomer; and a second inner shell, wherein the second inner shell comprises, as polymerized units, 90 to 99.5 wt %, based on weight of the second inner shell, of a non-ionic ethylenically unsaturated second inner shell monomer; and 0.5 to 10 wt %, based on weight of the second inner shell, of an aliphatic second inner shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof;
(iii) an outer shell, wherein the outer shell comprises, as polymerized units, 10 to 45 wt %, based on weight of the outer shell, of a non-ionic ethylenically unsaturated outer shell monomer; 50 to 88.9 wt %, based on weight of the outer shell, of an aliphatic outer shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof; 0.1 to 10 wt %, based on weight of the outer shell, of a monoethylenically unsaturated non-carboxylic acid outer shell monomer; and, 1 to 25 wt %, based on weight of the outer shell, of an ethylenically unsaturated surfactant outer shell monomer; wherein the ethylenically unsaturated surfactant outer shell monomer is selected from the group consisting of an anionic surfactant monomer according to Formula I, a non-ionic surfactant monomer according to Formula II and mixtures thereof;
wherein a is an average of 1-3, wherein b is an average of 1-3, wherein c is an average of 0-5, wherein d is 4-100, wherein A is an anion, wherein M is a cation charge balancing the anion; wherein the core, when dry, contains at least one void; and wherein the multistage polymeric particle has an average particle size, when dry, of 50 to 1,000 nm.
We have surprisingly found that multistage polymeric particles provide SPF boosting and opacity when incorporated into alcohol based sunscreen formulations, wherein the multistage polymer particles, comprise: (i) a core, wherein the core comprises, as polymerized units, a monoethylenically unsaturated carboxylic acid core monomer and a non-ionic ethylenically unsaturated core monomer; (ii) an inner shell, wherein the inner shell comprises, as polymerized units, a non-ionic ethylenically unsaturated inner shell monomer; a monoethylenically unsaturated carboxylic acid inner shell monomer and an aliphatic inner shell monomer; (iii) an outer shell, wherein the outer shell comprises, as polymerized units, a non-ionic ethylenically unsaturated outer shell monomer; an aliphatic outer shell monomer; a monoethylenically unsaturated non-carboxylic acid outer shell monomer and an ethylenically unsaturated surfactant outer shell monomer; wherein the core, when dry, contains at least one void; and wherein the multistage polymeric particle has an average particle size, when dry, of 50 to 1,000 nm.
Unless otherwise indicated, ratios, percentages, parts, and the like are by weight.
The term “polymerized units” as used herein and in the appended claims refers to the remnant of the indicated monomer; thus a structural unit of ethyl acrylate is illustrated:
where the dotted lines represent the points of attachment to the polymer backbone.
The term “(meth)acrylic acid” as used herein and in the appended claims is intended to serve as a generic expression embracing both acrylic acid and methacrylic acid.
The term “(meth)acrylate” as used herein and in the appended claims is intended to serve as a generic expression embracing both acrylate and methacrylate.
The term “(meth)acrylamide” as used herein and in the appended claims is intended to serve as a generic expression embracing both acrylamide and methacrylamide.
The term “(meth)acryloxypropionic acid” as used herein and in the appended claims is intended to serve as a generic expression embracing both acryloxypropionic acid and methacryloxypropionic acid.
Preferably, the SPF booster, or the present invention, for use in alcohol based sunscreen formulations, wherein the SPF booster comprises a multistage polymeric particle of the present invention, comprises: (i) a core, wherein the core comprises, as polymerized units, 20 to 60 wt % (preferably, 30 to 50 wt %; more preferably, 35 to 45 wt %), based on weight of the core, of a monoethylenically unsaturated carboxylic acid core monomer; and 40 to 80 wt % (preferably, 50 to 70 wt %; more preferably, 55 to 65 wt %), based on weight of the core, of a non-ionic ethylenically unsaturated core monomer; (ii) an inner shell, wherein the inner shell comprises, as polymerized units, 90 to 99.9 wt % (preferably, 92.5 to 99.5 wt %; more preferably, 95 to 99 wt %; most preferably, 96 to 98 wt %), based on weight of the inner shell, of a non-ionic ethylenically unsaturated inner shell monomer; 0.01 to 9.95 wt % (preferably, 0.05 to 7.5 wt %; more preferably, 0.1 to 5 wt %; most preferably, 0.2 to 4 wt %), based on weight of the inner shell, a monoethylenically unsaturated carboxylic acid inner shell monomer; and 0.05 to 9.99 wt % (preferably, 0.5 to 8 wt %; more preferably, 1 to 6 wt %; most preferably, 1.5 to 5 wt %), based on weight of the inner shell, of an aliphatic inner shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof; (iii) an outer shell, wherein the outer shell comprises, as polymerized units, 10 to 45 wt % (preferably, 15 to 40 wt %; more preferably, 17.5 to 37.5 wt %; most preferably, 20 to 35 wt %), based on weight of the outer shell, of a non-ionic ethylenically unsaturated outer shell monomer; 50 to 88.9 wt % (preferably, 50 to 80 wt %; more preferably, 50 to 75 wt %; most preferably, 55 to 65 wt %), based on weight of the outer shell, of an aliphatic outer shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof; 0.1 to 10 wt % (preferably, 0.5 to 7.5 wt %; more preferably, 1 to 5 wt %; most preferably, 2 to 3 wt %), based on weight of the outer shell, of a monoethylenically unsaturated non-carboxylic acid outer shell monomer; and, 1 to 25 wt % (preferably, 2 to 20 wt %; more preferably, 2.5 to 17.5 wt %; most preferably, 3 to 15 wt %), based on weight of the outer shell, of an ethylenically unsaturated surfactant outer shell monomer; wherein the core, when dry, contains at least one void; wherein the multistage polymeric particle has an average particle size, when dry, of 50 to 1,000 nm (400 to 900 nm; 450 to 850 nm; 500 to 800).
Preferably, the multistage polymeric particle of the present invention, comprises a core, wherein the core comprises, as polymerized units, 20 to 60 wt % (preferably, 30 to 50 wt %; more preferably, 35 to 45 wt %), based on weight of the core, of a monoethylenically unsaturated carboxylic acid core monomer; and 40 to 80 wt % (preferably, 50 to 70 wt %; more preferably, 55 to 65 wt %), based on weight of the core, of a non-ionic ethylenically unsaturated core monomer. More preferably, the multistage polymeric particle of the present invention, comprises 1 to 25 wt %, based on weight of the multistage polymeric particle, of a core; wherein the core comprises, as polymerized units, 20 to 60 wt % (preferably, 30 to 50 wt %; more preferably, 35 to 45 wt %), based on weight of the core, of a monoethylenically unsaturated carboxylic acid core monomer; and 40 to 80 wt % (preferably, 50 to 70 wt %; more preferably, 55 to 65 wt %), based on weight of the core, of a non-ionic ethylenically unsaturated core monomer. Still more preferably, the multistage polymeric particle of the present invention, comprises 2 to 12 wt %, based on weight of the multistage polymeric particle, of a core; wherein the core comprises, as polymerized units, 20 to 60 wt % (preferably, 30 to 50 wt %; more preferably, 35 to 45 wt %), based on weight of the core, of a monoethylenically unsaturated carboxylic acid core monomer; and 40 to 80 wt % (preferably, 50 to 70 wt %; more preferably, 55 to 65 wt %), based on weight of the core, of a non-ionic ethylenically unsaturated core monomer. Yet still more preferably, the multistage polymeric particle of the present invention, comprises 3 to 10 wt %, based on weight of the multistage polymeric particle, of a core; wherein the core comprises, as polymerized units, 20 to 60 wt % (preferably, 30 to 50 wt %; more preferably, 35 to 45 wt %), based on weight of the core, of a monoethylenically unsaturated carboxylic acid core monomer; and 40 to 80 wt % (preferably, 50 to 70 wt %; more preferably, 55 to 65 wt %), based on weight of the core, of a non-ionic ethylenically unsaturated core monomer. Most preferably, the multistage polymeric particle of the present invention, comprises 3.5 to 7.5 wt %, based on weight of the multistage polymeric particle, of a core; wherein the core comprises, as polymerized units, 20 to 60 wt % (preferably, 30 to 50 wt %; more preferably, 35 to 45 wt %), based on weight of the core, of a monoethylenically unsaturated carboxylic acid core monomer; and 40 to 80 wt % (preferably, 50 to 70 wt %; more preferably, 55 to 65 wt %), based on weight of the core, of a non-ionic ethylenically unsaturated core monomer.
Preferably, the monoethylenically unsaturated carboxylic acid core monomer is selected from monoethylenically unsaturated monomers that contain at least one carboxylic acid group. More preferably, the monoethylenically unsaturated carboxylic acid core monomer is selected from the group consisting of (meth)acrylic acid, (meth)acryloxypropionic acid, itaconic acid, aconitic acid, maleic acid, maleic anhydride, fumaric acid, crotonic acid, citraconic acid, maleic anhydride, monomethyl maleate, monomethyl fumarate, monomethyl itaconate, and other derivatives such as corresponding anhydride, amides, and esters. Still more preferably, the monoethylenically unsaturated carboxylic acid core monomer is selected from the group consisting of acrylic acid, methacrylic acid and mixtures thereof. Yet still more preferably, the monoethylenically unsaturated carboxylic acid core monomer includes methacrylic acid. Most preferably, the monoethylenically unsaturated carboxylic acid core monomer is methacrylic acid.
Preferably, the non-ionic ethylenically unsaturated core monomer is selected from the group consisting of ethylene, vinyl acetate, vinyl chloride, vinylidene chloride acrylonitrile, (meth)acrylamide, methyl (meth)acrylate, ethyl (meth)acrylate, n-butyl (meth)acrylate, i-butyl (meth)acrylate, t-butyl (meth)acrylate, cyclo-hexyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, lauryl (meth)acrylate, oleyl (meth)acrylate, palmityl (meth)acrylate, stearyl (meth)acrylate and mixtures thereof. More preferably, the non-ionic ethylenically unsaturated core monomer is selected from the group consisting of methyl methacrylate, butyl acrylate and mixtures thereof. Still more preferably, the non-ionic ethylenically unsaturated core monomer includes methyl methacrylate. Most preferably, the non-ionic ethylenically unsaturated core monomer is methyl methacrylate.
Preferably, the multistage polymeric particle of the present invention, comprises an inner shell, wherein the inner shell comprises 90 to 99.9 wt % (preferably, 92.5 to 99.5 wt %; more preferably, 95 to 99 wt %; most preferably, 96 to 98 wt %), based on weight of the inner shell, of a non-ionic ethylenically unsaturated inner shell monomer; 0.01 to 9.95 wt % (preferably, 0.05 to 7.5 wt %; more preferably, 0.1 to 5 wt %; most preferably, 0.2 to 4 wt %), based on weight of the inner shell, a monoethylenically unsaturated carboxylic acid inner shell monomer; and 0.05 to 9.99 wt % (preferably, 0.5 to 8 wt %; more preferably, 1 to 6 wt %; most preferably, 1.5 to 5 wt %), based on weight of the inner shell, of an aliphatic inner shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof. More preferably, the multistage polymeric particle of the present invention, comprises 15 to 80 wt %, based on weight of the multistage polymeric particle, of an inner shell, wherein the inner shell comprises, as polymerized units, 90 to 99.9 wt % (preferably, 92.5 to 99.5 wt %; more preferably, 95 to 99 wt %; most preferably, 96 to 98 wt %), based on weight of the inner shell, of a non-ionic ethylenically unsaturated inner shell monomer; 0.01 to 9.95 wt % (preferably, 0.05 to 7.5 wt %; more preferably, 0.1 to 5 wt %; most preferably, 0.2 to 4 wt %), based on weight of the inner shell, a monoethylenically unsaturated carboxylic acid inner shell monomer; and 0.05 to 9.99 wt % (preferably, 0.5 to 8 wt %; more preferably, 1 to 6 wt %; most preferably, 1.5 to 5 wt %), based on weight of the inner shell, of an aliphatic inner shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof. Still more preferably, the multistage polymeric particle of the present invention, comprises 25 to 75 wt %, based on weight of the multistage polymeric particle, of an inner shell, wherein the inner shell comprises, as polymerized units, 90 to 99.9 wt % (preferably, 92.5 to 99.5 wt %; more preferably, 95 to 99 wt %; most preferably, 96 to 98 wt %), based on weight of the inner shell, of a non-ionic ethylenically unsaturated inner shell monomer; 0.01 to 9.95 wt % (preferably, 0.05 to 7.5 wt %; more preferably, 0.1 to 5 wt %; most preferably, 0.2 to 4 wt %), based on weight of the inner shell, a monoethylenically unsaturated carboxylic acid inner shell monomer; and 0.05 to 9.99 wt % (preferably, 0.5 to 8 wt %; more preferably, 1 to 6 wt %; most preferably, 1.5 to 5 wt %), based on weight of the inner shell, of an aliphatic inner shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof. Yet still more preferably, the multistage polymeric particle of the present invention, comprises 30 to 60 wt %, based on weight of the multistage polymeric particle, of an inner shell, wherein the inner shell comprises, as polymerized units, 90 to 99.9 wt % (preferably, 92.5 to 99.5 wt %; more preferably, 95 to 99 wt %; most preferably, 96 to 98 wt %), based on weight of the inner shell, of a non-ionic ethylenically unsaturated inner shell monomer; 0.01 to 9.95 wt % (preferably, 0.05 to 7.5 wt %; more preferably, 0.1 to 5 wt %; most preferably, 0.2 to 4 wt %), based on weight of the inner shell, a monoethylenically unsaturated carboxylic acid inner shell monomer; and 0.05 to 9.99 wt % (preferably, 0.5 to 8 wt %; more preferably, 1 to 6 wt %; most preferably, 1.5 to 5 wt %), based on weight of the inner shell, of an aliphatic inner shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof. Most preferably, the multistage polymeric particle of the present invention, comprises 40 to 50 wt %, based on weight of the multistage polymeric particle, of an inner shell, wherein the inner shell comprises, as polymerized units, 90 to 99.9 wt % (preferably, 92.5 to 99.5 wt %; more preferably, 95 to 99 wt %; most preferably, 96 to 98 wt %), based on weight of the inner shell, of a non-ionic ethylenically unsaturated inner shell monomer; 0.01 to 9.95 wt % (preferably, 0.05 to 7.5 wt %; more preferably, 0.1 to 5 wt %; most preferably, 0.2 to 4 wt %), based on weight of the inner shell, a monoethylenically unsaturated carboxylic acid inner shell monomer; and 0.05 to 9.99 wt % (preferably, 0.5 to 8 wt %; more preferably, 1 to 6 wt %; most preferably, 1.5 to 5 wt %), based on weight of the inner shell, of an aliphatic inner shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof.
Preferably, the non-ionic ethylenically unsaturated inner shell monomer is selected from the group consisting of acrylonitrile, (meth)acrylamide, methyl (meth)acrylate, ethyl (meth)acrylate, n-butyl (meth)acrylate, i-butyl (meth)acrylate, t-butyl (meth)acrylate, cyclo-hexyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, lauryl (meth)acrylate, oleyl (meth)acrylate, palmityl (meth)acrylate, stearyl (meth)acrylate, and iso-bornyl (meth)acrylate. More preferably, the non-ionic ethylenically unsaturated inner shell monomer is selected from the group consisting of methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, butyl acrylate, butyl methacrylate, isobutyl acrylate, isobutyl methacrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate, dimethylaminoethyl methacrylate, dimethylaminopropyl methacrylamide and mixtures thereof. Still more preferably, the a non-ionic ethylenically unsaturated inner shell monomer is selected from the group consisting of at least one of butyl methacrylate and methyl methacrylate. Most preferably, the non-ionic ethylenically unsaturated inner shell monomer includes both butyl methacrylate and methyl methacrylate.
Preferably, the monoethylenically unsaturated carboxylic acid inner shell monomer is selected from monoethylenically unsaturated monomers that contain at least one carboxylic acid group. More preferably, the monoethylenically unsaturated carboxylic acid inner shell monomer is selected from the group consisting of (meth)acrylic acid, (meth)acryloxypropionic acid, itaconic acid, aconitic acid, maleic acid, fumaric acid, crotonic acid, citraconic acid, maleic anhydride monomethyl maleate, monomethyl fumarate, monomethyl itaconate, derivatives thereof (e.g., corresponding anhydride, amides, esters) and mixtures thereof. Still more preferably, the monoethylenically unsaturated carboxylic acid inner shell monomer is selected from the group consisting of acrylic acid, methacrylic acid and mixtures thereof. Yet still more preferably, the monoethylenically unsaturated carboxylic acid inner shell monomer includes methacrylic acid. Most preferably, the monoethylenically unsaturated carboxylic acid inner shell monomer is methacrylic acid.
Preferably, the aliphatic inner shell monomer is selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof. More preferably, the aliphatic inner shell monomer includes allyl methacrylate. Most preferably, the aliphatic inner shell monomer is allyl methacrylate.
Preferably, the multistage polymeric particle of the present invention, comprises an inner shell, wherein the inner shell includes multiple inner shells. More preferably, the multistage polymeric particle of the present invention comprises an inner shell, wherein the inner shell includes: a first inner shell and a second inner shell. Most preferably, the multistage polymeric particle of the present invention comprises an inner shell, wherein the inner shell includes: (a) a first inner shell, wherein the first inner shell comprises, as polymerized units, 90 to 99.9 wt % (preferably, 92.5 to 99.5 wt %; more preferably, 95 to 99 wt %; most preferably, 96 to 98 wt %), based on weight of the first inner shell, of a non-ionic ethylenically unsaturated first inner shell monomer (preferably, wherein the non-ionic ethylenically unsaturated first inner shell monomer is selected from the group consisting of butyl methacrylate, methyl methacrylate and mixtures thereof; more preferably, wherein the non-ionic ethylenically unsaturated first inner shell monomer includes both butyl methacrylate and methyl methacrylate; most preferably, wherein the non-ionic ethylenically unsaturated first inner shell monomer is a mixture of butyl methacrylate and methyl methacrylate); and 0.1 to 10 wt % (preferably, 0.5 to 7.5 wt %; more preferably, 1 to 5 wt %; most preferably, 2 to 4 wt %), based on weight of the first inner shell, a monoethylenically unsaturated carboxylic acid first inner shell monomer (preferably, wherein the monoethylenically unsaturated carboxylic acid first inner shell monomer is selected from the group consisting of acrylic acid, methacrylic acid and mixtures thereof; more preferably, wherein the monoethylenically unsaturated carboxylic acid first inner shell monomer includes methacrylic acid; most preferably, wherein the monoethylenically unsaturated carboxylic acid first inner shell monomer is methacrylic acid); and (b) a second inner shell, wherein the second inner shell comprises, as polymerized units, 90 to 99.5 wt % (preferably, 92 to 99 wt %; more preferably, 94 to 98 wt %; most preferably, 95 to 97.5 wt %), based on weight of the second inner shell, of a non-ionic ethylenically unsaturated second inner shell monomer (preferably, wherein the non-ionic ethylenically unsaturated second inner shell monomer includes methyl methacrylate; more preferably, wherein the non-ionic ethylenically unsaturated second inner shell monomer is methyl methacrylate); and 0.5 to 10 wt % (preferably, 1 to 8 wt %; more preferably, 2 to 6 wt %; most preferably, 2.5 to 5 wt %), based on weight of the second inner shell, of an aliphatic second inner shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof (preferably, wherein the aliphatic second inner shell monomer is allyl methacrylate).
Preferably, the multistage polymeric particle of the present invention, comprises an outer shell, wherein the outer shell comprises, as polymerized units, 10 to 45 wt % (preferably, 15 to 40 wt %; more preferably, 17.5 to 37.5 wt %; most preferably, 20 to 35 wt %), based on weight of the outer shell, of a non-ionic ethylenically unsaturated outer shell monomer; 50 to 88.9 wt % (preferably, 50 to 80 wt %; more preferably, 50 to 75 wt %; most preferably, 55 to 65 wt %), based on weight of the outer shell, of an aliphatic outer shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof; 0.1 to 10 wt % (preferably, 0.5 to 7.5 wt %; more preferably, 1 to 5 wt %; most preferably, 2 to 3 wt %), based on weight of the outer shell, of a monoethylenically unsaturated non-carboxylic acid outer shell monomer; and, 1 to 25 wt % (preferably, 2 to 20 wt %; more preferably, 2.5 to 17.5 wt %; most preferably, 3 to 15 wt %), based on weight of the outer shell, of an ethylenically unsaturated surfactant outer shell monomer. More preferably, the multistage polymeric particle of the present invention, comprises 15 to 80 wt %, based on weight of the multistage polymeric particle, of an outer shell, wherein the outer shell comprises, as polymerized units, 10 to 45 wt % (preferably, 15 to 40 wt %; more preferably, 17.5 to 37.5 wt %; most preferably, 20 to 35 wt %), based on weight of the outer shell, of a non-ionic ethylenically unsaturated outer shell monomer; 50 to 88.9 wt % (preferably, 50 to 80 wt %; more preferably, 50 to 75 wt %; most preferably, 55 to 65 wt %), based on weight of the outer shell, of an aliphatic outer shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof; 0.1 to 10 wt % (preferably, 0.5 to 7.5 wt %; more preferably, 1 to 5 wt %; most preferably, 2 to 3 wt %), based on weight of the outer shell, of a monoethylenically unsaturated non-carboxylic acid outer shell monomer; and, 1 to 25 wt % (preferably, 2 to 20 wt %; more preferably, 2.5 to 17.5 wt %; most preferably, 3 to 15 wt %), based on weight of the outer shell, of an ethylenically unsaturated surfactant outer shell monomer. Still more preferably, the multistage polymeric particle of the present invention, comprises 25 to 75 wt %, based on weight of the multistage polymeric particle, of an outer shell, wherein the outer shell comprises, as polymerized units, 10 to 45 wt % (preferably, 15 to 40 wt %; more preferably, 17.5 to 37.5 wt %; most preferably, 20 to 35 wt %), based on weight of the outer shell, of a non-ionic ethylenically unsaturated outer shell monomer; 50 to 88.9 wt % (preferably, 50 to 80 wt %; more preferably, 50 to 75 wt %; most preferably, 55 to 65 wt %), based on weight of the outer shell, of an aliphatic outer shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof; 0.1 to 10 wt % (preferably, 0.5 to 7.5 wt %; more preferably, 1 to 5 wt %; most preferably, 2 to 3 wt %), based on weight of the outer shell, of a monoethylenically unsaturated non-carboxylic acid outer shell monomer; and, 1 to 25 wt % (preferably, 2 to 20 wt %; more preferably, 2.5 to 17.5 wt %; most preferably, 3 to 15 wt %), based on weight of the outer shell, of an ethylenically unsaturated surfactant outer shell monomer. Yet still more preferably, the multistage polymeric particle of the present invention, comprises 30 to 60 wt %, based on weight of the multistage polymeric particle, of an outer shell, wherein the outer shell comprises, as polymerized units, 10 to 45 wt % (preferably, 15 to 40 wt %; more preferably, 17.5 to 37.5 wt %; most preferably, 20 to 35 wt %), based on weight of the outer shell, of a non-ionic ethylenically unsaturated outer shell monomer; 50 to 88.9 wt % (preferably, 50 to 80 wt %; more preferably, 50 to 75 wt %; most preferably, 55 to 65 wt %), based on weight of the outer shell, of an aliphatic outer shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof; 0.1 to 10 wt % (preferably, 0.5 to 7.5 wt %; more preferably, 1 to 5 wt %; most preferably, 2 to 3 wt %), based on weight of the outer shell, of a monoethylenically unsaturated non-carboxylic acid outer shell monomer; and, 1 to 25 wt % (preferably, 2 to 20 wt %; more preferably, 2.5 to 17.5 wt %; most preferably, 3 to 15 wt %), based on weight of the outer shell, of an ethylenically unsaturated surfactant outer shell monomer. Most preferably, the multistage polymeric particle of the present invention, comprises 40 to 50 wt %, based on weight of the multistage polymeric particle, of an outer shell, wherein the outer shell comprises, as polymerized units, 10 to 45 wt % (preferably, 15 to 40 wt %; more preferably, 17.5 to 37.5 wt %; most preferably, 20 to 35 wt %), based on weight of the outer shell, of a non-ionic ethylenically unsaturated outer shell monomer; 50 to 88.9 wt % (preferably, 50 to 80 wt %; more preferably, 50 to 75 wt %; most preferably, 55 to 65 wt %), based on weight of the outer shell, of an aliphatic outer shell monomer selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof; 0.1 to 10 wt % (preferably, 0.5 to 7.5 wt %; more preferably, 1 to 5 wt %; most preferably, 2 to 3 wt %), based on weight of the outer shell, of a monoethylenically unsaturated non-carboxylic acid outer shell monomer; and, 1 to 25 wt % (preferably, 2 to 20 wt %; more preferably, 2.5 to 17.5 wt %; most preferably, 3 to 15 wt %), based on weight of the outer shell, of an ethylenically unsaturated surfactant outer shell monomer.
Preferably, the non-ionic ethylenically unsaturated outer shell monomer is selected from the group consisting of acrylonitrile, (meth)acrylamide, methyl (meth)acrylate, ethyl (meth)acrylate, n-butyl (meth)acrylate, i-butyl (meth)acrylate, t-butyl (meth)acrylate, cyclo-hexyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, lauryl (meth)acrylate, oleyl (meth)acrylate, palmityl (meth)acrylate, stearyl (meth)acrylate, and iso-bornyl (meth)acrylate. More preferably, the non-ionic ethylenically unsaturated outer shell monomer is selected from the group consisting of methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, butyl acrylate, butyl methacrylate, isobutyl acrylate, isobutyl methacrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate, dimethylaminoethyl methacrylate, dimethylaminopropyl methacrylamide and mixtures thereof. Still more preferably, the a non-ionic ethylenically unsaturated outer shell monomer includes methyl methacrylate. Most preferably, the non-ionic ethylenically unsaturated outer shell monomer is methyl methacrylate.
Preferably, the aliphatic outer shell monomer is selected from the group consisting of allyl acrylate, allyl methacrylate and mixtures thereof. More preferably, the aliphatic outer shell monomer includes allyl methacrylate. Most preferably, the aliphatic outer shell monomer is allyl methacrylate.
Preferably, the monoethylenically unsaturated non-carboxylic acid outer shell monomer is selected from monoethylenically unsaturated monomers containing at least one non-carboxylic acid type acid group. More preferably, the monoethylenically unsaturated non-carboxylic acid outer shell monomer is selected from the group consisting of allyl sulfonic acid, allyl phosphonic acid, allyl oxybenzene sulfonic acid, 2-acrylamido-2-methylpropane sulfonic acid, 2-hydroxy-3-2-propenyloxy)propane sulfonic acid, 2-methyl-2-propene-1-sulfonic acid, 2-methacrylamido-2-methyl-1-propane sulfonic acid, 3-methacrylamido-2-hydroxy-1-propane sulfonic acid, 3-sulfopropyl acrylate, 3-sulfopropyl methacrylate, isopropenyl phosphonic acid, vinyl phosphonic acid, phosphoethyl methacrylate, styrene sulfonic acid, vinyl sulfonic acid, alkali metal salts thereof, ammonium salts thereof and mixtures thereof. Still more preferably, the monoethylenically unsaturated non-carboxylic acid outer shell monomer is selected from the group consisting of 2-acrylamido-2-methylpropane sulfonic acid, styrene sulfonic acid, sodium styrene sulfonate and mixtures thereof. Yet still more preferably, the monoethylenically unsaturated non-carboxylic acid outer shell monomer includes sodium styrene sulfonate. Most preferably, the monoethylenically unsaturated non-carboxylic acid outer shell monomer is sodium styrene sulfonate.
Preferably, the ethylenically unsaturated surfactant outer shell monomer is selected from the group consisting of an anionic surfactant monomer, a non-ionic surfactant monomer and mixtures thereof. More preferably, the ethylenically unsaturated surfactant outer shell monomer includes an anionic surfactant monomer. Most preferably, the ethylenically unsaturated surfactant outer shell monomer is an anionic surfactant monomer.
Preferably, the anionic surfactant monomer is selected from the group of anionic surfactant monomers of Formula I
wherein a is an average of 1-3 (preferably, 1-2; most preferably 2); wherein b is an average of 1-3 (preferably, 2-3; most preferably, 2); wherein c is an average of 0-5 (preferably, 0-2; most preferably, 0); wherein d is 4-100 (preferably, 5-50; more preferably, 7.5 to 20; most preferably, 10 to 20); wherein A is an anion (preferably, a SO3− or a PO32−; more preferably, SO3−); and wherein M is a cation (preferably, a Na+, K+ or an NH4+; more preferably, NH4+) charge balancing the anion. More preferably, the anionic surfactant monomer is selected from the group of anionic surfactant monomers of Formula I, wherein a is an average of 2, wherein b is an average of 2, wherein c is 0, and wherein d is an average of 10 to 20. Still more preferably, the anionic surfactant monomer is selected from the group of anionic surfactant monomers of Formula I, the anionic surfactant monomer is selected from the group of anionic surfactant monomers of Formula I, wherein a is an average of 2, wherein b is an average of 2, wherein c is 0, wherein d is an average of 10 to 20 and wherein A is SO3−. Most preferably, the anionic surfactant monomer is selected from the group of anionic surfactant monomers of Formula I, the anionic surfactant monomer is selected from the group of anionic surfactant monomers of Formula I, wherein a is an average of 2, wherein b is an average of 2, wherein c is 0, wherein d is an average of 10 to 20, wherein A is SO3− and wherein M is NH4+.
Preferably, the non-ionic surfactant monomer is selected from the group of non-ionic surfactant monomers of Formula II
wherein a is an average of 1-3 (preferably, 1-2; most preferably, 2); wherein b is an average of 1-3 (preferably, 2-3; most preferably, 2); wherein c is an average of 0-5 (preferably, 0-2; most preferably, 0); and wherein d is 4-100 (preferably, 5-50; more preferably, 7.5 to 20; most preferably, 10 to 20).
Preferably, the multistage polymeric particle of the present invention, comprises an inner shell and an outer shell, wherein the outer shell comprises at least 25 wt % of the combined weight of the inner shell and the outer shell. More preferably, the multistage polymeric particle of the present invention, comprises an inner shell and an outer shell, wherein the outer shell comprises at least 35 wt % of the combined weight of the inner shell and the outer shell. Most preferably, the multistage polymeric particle of the present invention, comprises an inner shell and an outer shell, wherein the outer shell comprises at least 45 wt % of the combined weight of the inner shell and the outer shell.
Preferably, the multistage polymeric particle of the present invention comprises a core, wherein the core, when dry, contains at least one void. More preferably, the multistage polymeric particle of the present invention comprises a core, wherein the core, when dry, contains at least one void having a void fraction of 5 to 70 vol %, based on the volume occupied by the multistage polymeric particle. Still more preferably, the multistage polymeric particle of the present invention comprises a core, wherein the core, when dry, contains at least one void having a void fraction of 10 to 60 vol %, based on the volume occupied by the multistage polymeric particle. Yet still more preferably, the multistage polymeric particle of the present invention comprises a core, wherein the core, when dry, contains at least one void having a void fraction of 20 to 50 vol %, based on the volume occupied by the multistage polymeric particle. Most preferably, the multistage polymeric particle of the present invention comprises a core, wherein the core, when dry, contains at least one void having a void fraction of 25 to 45 vol %, based on the volume occupied by the multistage polymeric particle. The void fraction is determined by comparing the volume occupied by a plurality of the multistage polymer particles after compaction from a dilute dispersion in a centrifuge to the volume of non-voided multistage polymeric particles having the same composition.
Preferably, the multistage polymeric particle of the present invention, comprises an inner shell and an outer shell, wherein the Tg (as measured by DSC) of the inner shell and the outer shell are high enough to support the at least one void contained in the core. More preferably, the multistage polymeric particle of the present invention, comprises an inner shell and an outer shell, wherein the Tg (as measured by DSC) of at least one of the inner shell and the outer shell is greater than 50° C. Still more preferably, the multistage polymeric particle of the present invention, comprises an inner shell and an outer shell, wherein the Tg (as measured by DSC) of at least one of the inner shell and the outer shell is greater than 60° C. Most preferably, the multistage polymeric particle of the present invention, comprises an inner shell and an outer shell, wherein the Tg (as measured by DSC) of at least one of the inner shell and the outer shell is greater than 70° C.
Preferably, the multistage polymeric particles of the present invention have an average particle size, when dry, of 50 to 1,000 nm, as measured by a Brookhaven BI-90. More preferably, the multistage polymeric particles of the present invention have an average particle size, when dry, of 400 to 900 nm, as measured by a Brookhaven BI-90. Still more preferably, the multistage polymeric particles of the present invention have an average particle size, when dry, of 450 to 850 nm, as measured by a Brookhaven BI-90. Most preferably, the multistage polymeric particles of the present invention have an average particle size, when dry, of 500 to 800 nm, as measured by a Brookhaven BI-90.
Preferably, the multistage polymeric particle of the present invention, contains, as polymerized units, less than 10 wt %, based on weight of the multistage polymeric particle, of total styrene monomer in the backbone chain of the core, the inner shell and the outer shell combined. More preferably, the multistage polymeric particle of the present invention, contains, as polymerized units, less than 5 wt %, based on weight of the multistage polymeric particle, of total styrene monomer in the backbone chain of the core, the inner shell and the outer shell combined styrene. Still more preferable, the multistage polymeric particle of the present invention, contains, as polymerized units, less than 2.5 wt %, based on weight of the multistage polymeric particle, of total styrene monomer in the backbone chain of the core, the inner shell and the outer shell combined styrene. Yet more preferably, the multistage polymeric particle of the present invention, is substantially free (i.e., less than 0.001 wt % (preferably, less than 0.0001 wt %; most preferably, less than 1 part per million by weight), based on weight of the multistage polymeric particle,) of polymerized units of styrene monomer in the backbone chain of the core, the inner shell and the outer shell combined. Most preferably, the multistage polymeric particle of the present invention, is free (i.e., contains 0 wt %, based on weight of the multistage polymeric particle,) of polymerized units of styrene monomer in the backbone chain of the core, the inner shell and the outer shell combined.
Preferably, the multistage polymeric particles of the present invention are prepared using conventional polymerization techniques. More preferably, the multistage polymeric particles of the present invention are prepared using a single polymerization step or a sequence of polymerization steps. Still more preferably, the multistage polymeric particles of the present invention are prepared via a sequential emulsion polymerization process. Preferably, the monomers used in the emulsion polymerization of the shell(s) comprise one or more non-ionic ethylenically unsaturated monomer(s).
Aqueous emulsion polymerization processes are typically conducted in an aqueous reaction mixture, which contains at least one monomer and various synthesis adjuvants, such as free radical sources, buffers, chain transfer agents and reductants in an aqueous reaction medium. The aqueous reaction medium is the continuous fluid phase of the aqueous reaction mixture and contains more than 50 weight % water and optionally one or more water miscible solvents, based on the weight of the aqueous reaction medium. Suitable water miscible solvents include, for example, methanol, ethanol, propanol, acetone, ethylene glycol ethyl ethers, propylene glycol propyl ethers, and diacetone alcohol.
Preferably, in the process of manufacturing the multistage polymeric particles of the present invention, the void is formed by swelling the core with a swelling agent containing one or more volatile components. The swelling agent permeates the shell(s) to swell the core. The volatile components of the swelling agent can then be removed by drying the multistage polymeric particles, causing a void to be formed within the core. Preferably, the swelling agent includes an aqueous base, such as, for example ammonia, ammonium hydroxide, alkali metal hydroxides (e.g., sodium hydroxide) and volatile amines (e.g., trimethylamine, triethylamine).
Preferably, the multistage polymeric particles of the present invention are dried. More preferably, the multistage polymeric particles of the present invention are spray dried using well known processing techniques.
Some embodiments of the present invention will now be described in detail in the following Examples.
The multicomponent polymeric particles in each of Comparative Example C1 and Examples 1-5, comprised 4.7 wt % of a core, 22.1 wt % of a first inner shell, 26.8 wt % of a second inner shell and 46.4 wt % of an outer shell. The multicomponent polymeric particles in each of Comparative Example C1 and Examples 1-5 all comprised the same composition for the core, the first inner shell and the second inner shell, as described in T
The multicomponent polymeric particles of Example 1 were prepared by adding 718.1 g of deionized water to a 3 liter, 4 neck round bottom flask equipped with an overhead stirrer, a thermocouple, a heating mantle, an adapter inlet, a Claisen head fitted with a water condenser and a nitrogen inlet. The flask contents were then heated to 84° C. under nitrogen. Then a solution of deionized water (19.1 g), citric acid (0.26 g) and sodium persulfate (1.39 g) was added to the flask. Then an aqueous dispersion (58.6 g) of 31 wt % solids poly (60 MMA/40 MAA) acrylic seed (core) polymer, having an average particle diameter of ˜185 to 205 nm, was added to the flask. While maintaining the temperature of the flask contents at 82° C., a monomer emulsion containing deionized water (37.3 g), a 23% aqueous solution of sodium dodecylbenzenesulfonate (SDBS)(1.88 g), MMA (76.7 g), BMA (7.4 g) and MAA (2.6 g) was metered into the flask contents over a period of 90 minutes followed by a deionized water rinse of the transfer lines. Next a solution of sodium persulfate (0.5 g) in deionized water (44.5 g) was added to the flask contents over a period of 90 minutes. The temperature set point for the flask contents was then raised to 90° C., concurrent with the transfer to the flask contents of a second monomer emulsion containing deionized water (58.7 g), a 23% aqueous solution of SDBS (2.10 g), MMA (98.3 g), ALMA (3.2 g) and linseed oil fatty acid (0.60 g) over a period of 30 minutes, minutes followed by a deionized water rinse of the transfer lines. Then, a solution of deionized water (38 g) and 28% aqueous ammonium hydroxide (8.1 g) was added to the flask contents. The flask contents were held for 10 minutes, before adding a third monomer emulsion containing deionized water (54.8 g), a 23% aqueous solution of SDBS (3.91 g), a 29% aqueous solution of E-Sperse® RS-1684 reactive surfactant (61.81 g), ALMA (110.5 g), MMA (50.2 g), sodium styrene sulfonate (5.0 g) to the flask contents at 91° C. over a period of 60 minutes; followed by a deionized water rinse of the transfer lines. Then (3.0 g) of an aqueous solution containing FeSO4.7H2O (0.06 g) and versene (0.6 g) was added to the contents of the flask. Then a solution of t-butylhydrogen peroxide (70%)(2.8 g) in deionized water (8.0 g) was added to the flask contents as a shot. Then a solution of isoascorbic acid (1.4 g) in deionized water (25.2 g) was added to the flask contents over a period of 40 minutes. Then for 30 minutes the flask contents were maintained with a temperature set point at 90° C. before removing the heating source and allowing the flask contents to cool to room temperature providing a latex containing the multicomponent polymer particles.
The multicomponent polymeric particles of Comparative Example C1 and Examples 2-5 were prepared using the same process as described above for Example 1, with appropriate changes in monomer amounts as recited in T
The average particle size of the multicomponent polymeric particles in the latexes of Comparative Example C1 and Examples 1-5 were measured using a Brookhaven BI-90 particle size analyzer available from Brookhaven Instruments Corporation. The results are provided in T
The percent void fraction for the multicomponent polymeric particles in the latexes of Comparative Example C1 and Examples 1-5 was determined by taking a 10 wt % dispersion of the multicomponent polymeric particles in propylene glycol, which was then mixed and poured into a weight-per-gallon cup which was capped and weighed. A 10 wt % water blank was also measured, and the difference in the weight was used to calculate the density of the sample, from which the percent void fraction was calculated. The results are provided in T
1SunSpheres
TM SPF Booster available from The Dow Chemical Company
Multicomponent polymeric particles prepared according to each of Comparative Example C1-C2 and Examples 1-5 were spray dried according to the following procedure in Comparative Example SDC1-SDC2 and Examples SD1-SD5, respectively. Polyethylene glycol (HallStar® PEG 400-ML esterification product from the reaction of coco-derived fatty acid and polyethylene glycol available from HallStar) (12 wt %) was added into the latex containing the multicomponent polymeric particles as a dust control aid. A two-fluid nozzle atomizer was equipped on a Mobile Minor Spray Dryer (available from GEA Process Engineering Inc.). The spray drying was performed under an inert nitrogen atmosphere. Nitrogen was supplied to the atomizer at ambient temperature and was set at 1 bar with a 50% flow, which provided a 6.0 kg/hour of nitrogen flow rate through the atomizer. The multicomponent polymeric particles with polyethylene glycol was fed to the atomizer at a flow rate of 30 mL/min using a peristaltic pump (Masterflex L/S). Heated nitrogen was used to evaporate the water from the latex. The drying gas was nitrogen with an inlet temperature set at 140° C. The outlet temperature was equilibrated at 40 to 50° C. through modulation of the latex feed rate. The resulting spray dried, multicomponent polymeric particle powder was collected in a glass jar attached to the cyclone and vacuum dried at room temperature to remove any residual moisture.
Alcohol based sunscreens were prepared in each of Comparative Examples SC1-SC3 and Examples S1-S5 having the generic formulation noted in T
1Epitex
TM AC powder water resistant polymer available from The Dow Chemical Company.
The particle size distribution was observed for the spray dried, multicomponent polymer particle powders from Comparative Examples SDC1-SDC2 and Examples SD1-SD5 diluted in ethanol and shaken by hand prior to addition into the test chamber of a Malvern MS-2000 with Mastersizer 2000 software. The primary particle volume % in the particle size distribution having a particle size <1 μm is reported in T
The particle size distribution was also observed for the multicomponent polymer particles in the sunscreen formulations prepared according to Comparative Examples SC1-SC2 and Examples S1-S5. The sunscreen formulations according to Comparative Example SC1-SC2 and Examples S1-S5 were subjected to both a low energy and a medium energy homogenization technique.
The low energy table shaker homogenization technique performed using an Eberbach's Benchtop Fixed Speed Reciprocal Shaker. Test vials containing the sunscreen formulations were subjected to a reciprocal shaking at the low speed setting for two hours prior to addition into the test chamber of a Malvern MS-2000 with Mastersizer 2000 software. The primary particle volume % in the particle size distribution having a particle size <1 μm is reported in T
The medium energy vortex mixer homogenization technique testing was performed using a FlackTek SpeedMixer DAC 150 FV-K. The sunscreen formulations were loaded into a sample cell together with grinding beads (cerium stabilized zirconia with a nominal diameter of 0.5 mm) and vortex mixing at 2,000 rpm for two minutes prior to addition into the test chamber of a Malvern MS-2000 with Mastersizer 2000 software. The primary particle volume % in the particle size distribution having a particle size <1 μm is reported in T
The particle size distribution for the multicomponent polymer particles in the sunscreen formulations prepared according to Example S3 was retested after aging at room temperature for 20 days. The aged sunscreen formulation was subjected to medium energy mixing prior to addition into the test chamber of a Malvern MS-2000 with Mastersizer 2000 software. The particle size distribution of the aged formulation was observed to be essentially unchanged from that of the unaged formulation.
The SPF boosting efficacy of the sunscreen formulations prepared according to Comparative Example SC3 and Example S3 were evaluated by measuring the sun protection factor (SPF) of the sunscreen formulations. The sunscreen formulations were spread-coated on a 5 cm×5 cm poly methyl methacrylate (PMMA) plate at a level of 50 mg using finger cots. The SPF was measured using a UV-2000S with an integrating sphere and SPF Operating Software supplied by LabSpheres (North Sutton, N.H., USA). The UV-2000S measures the UV absorbance of a sample over UV radiation wavelengths (290-400 nm) for each sample and calculates an SPF value based on the observed UV absorbance spectrum. In comparison with the control (Comparative Example SC3), the sunscreen formulation of Example S3 containing the SPF boosting, multicomponent polymeric particles of the present invention was observed to exhibit a boost efficacy of about 25% per 1 wt % of added multicomponent polymeric particles.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2018/039981 | 6/28/2018 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2019/022913 | 1/31/2019 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4427836 | Kowalski et al. | Jan 1984 | A |
| 5663213 | Jones et al. | Sep 1997 | A |
| 6384104 | Chang et al. | May 2002 | B1 |
| 9051341 | Palmer, Jr. | Jun 2015 | B2 |
| 9102775 | Bardman et al. | Aug 2015 | B2 |
| 9255206 | Palmer, Jr. et al. | Feb 2016 | B2 |
| 20090035234 | Cunningham et al. | Feb 2009 | A1 |
| 20140017186 | Wang | Jan 2014 | A1 |
| Number | Date | Country |
|---|---|---|
| 2381099 | Jun 1999 | AU |
| 1092421 | Apr 2001 | EP |
| 2010048124 | Apr 2010 | WO |
| 2017058713 | Apr 2017 | WO |
| 2018144298 | Aug 2018 | WO |
| Entry |
|---|
| “Reactive Surfactants for Emulsion Polymerization,” Ethox Technical Bulletin, E-Sperse RS-Series. |
| Number | Date | Country | |
|---|---|---|---|
| 20210085573 A1 | Mar 2021 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62538041 | Jul 2017 | US |