Patent Application
20160251071
The following disclosure relates generally to shell structures and, more particularly, to splice joints for joining composite fuselage sections and other shell structures together.
The primary structural elements of large passenger jets and other large aircraft are typically made from metal. Fuselage shells for such aircraft, for example, are typically manufactured from high-strength aluminum alloys or similar metals. In an effort to increase performance, however, many aircraft manufacturers are turning to fiber-reinforced resin materials (i.e., “composite” materials) that have relatively high strength-to-weight ratios. Conventional composite materials typically include glass, carbon, or polyaramide fibers in a matrix of epoxy or another type of resin. The use of such materials for primary structures has mostly been limited to smaller aircraft, such as fighter aircraft, high-performance private aircraft, and business jets.
One known method for manufacturing business jet airframes with composite materials is employed by the Raytheon Aircraft Company of Wichita, Kans., to manufacture the Premier I and Hawker Horizon business jets. This method involves wrapping carbon fibers around a rotating mandrel with an automated fiber placement system. The mandrel provides the basic shape of a longitudinal fuselage section. The carbon fibers are preimpregnated with a thermoset epoxy resin, and are applied over the rotating mandrel in multiple plies to form an interior skin of the fuselage section. The interior skin is then covered with a layer of honeycomb core. The fiber placement system then applies additional plies of preimpregnated carbon fibers over the honeycomb core to form an exterior skin that results in a composite sandwich structure.
The Premier I fuselage includes two 360-degree sections formed in the foregoing manner. The Hawker Horizon fuselage includes three such sections formed in this manner. The two 70-inch diameter sections of the Premier I fuselage are riveted and then bonded together at a circumferential splice joint to form the complete fuselage structure. The much larger Hawker Horizon fuselage, with an 84-inch diameter, uses aluminum splice plates at two circumferential joints to join the three fuselage sections together into a complete structure.
To precisely install the aluminum splice plates on the Hawker Horizon fuselage, Raytheon created a special, automated splice machine. This machine aligns the three fuselage sections using a computer-aided laser alignment system, and then drills attachment holes through the aluminum splice plates and the underlying sandwich structure. The machine then probes each hole for size quality and records statistical process control data on each hole. The drill heads also apply sealant and install hi-shear fasteners in approximately 1,800 places along each of the splice joints. (See Raytheon Aircraft news release at http://www.beechcraft.de/presse/2000/100900b.htm entitled “RAYTHEON AIRCRAFT'S HAWKER HORIZON REACHES FUSELAGE MILESTONE,” Oct. 9, 2000).
The present invention is directed generally toward structures and methods for joining composite fuselage sections and other panel assemblies together. A shell structure configured in accordance with one aspect of the invention includes a first panel portion positioned adjacent to a second panel portion. The first panel portion can include a first stiffener attached to a first composite skin, and the second panel portion can include a second stiffener attached to a second composite skin. The shell structure can further include a fitting extending across a first edge region of the first panel portion and a second edge region of the second panel portion. A first end portion of the fitting can be attached to the first stiffener and the first composite skin, and a second end portion of the fitting can be attached to the second stiffener and the second composite skin, to join the first panel portion to the second panel portion.
A method for manufacturing a shell structure in accordance with another aspect of the invention includes attaching at least a first stiffener to a first composite skin, and attaching at least a second stiffener to a second composite skin. The method can further include positioning the first composite skin in edgewise alignment with the second composite skin, attaching a first end of a fitting to the first stiffener and the first composite skin, and attaching a second end of the fitting to the second stiffener and the second composite skin. In one embodiment, the method can additionally include attaching a strap to a first edge region of the first composite skin and an adjacent second edge region of the second composite skin to splice the first and second composite skins together before the fitting is attached.
The following disclosure describes structures and methods for joining composite fuselage sections and other panel assemblies together. Certain details are set forth in the following description and in
Many of the details, dimensions, angles, and other features shown in the Figures are merely illustrative of particular embodiments of the invention. Accordingly, other embodiments can have other details, dimensions, angles, and features without departing from the spirit or scope of the present invention. In addition, further embodiments of the invention can be practiced without several of the details described below.
In the Figures, identical reference numbers identify identical or at least generally similar elements. To facilitate the discussion of any particular element, the most significant digit or digits of any reference number refer to the Figure in which that element is first introduced. For example, element 106 is first introduced and discussed with reference to
The fuselage 102 can further include a passenger cabin 103 configured to hold a plurality of passenger seats 105 ranging in number from about 50 to about 700 seats. For example, in the illustrated embodiment, the passenger cabin 103 can hold from about 150 to about 600 passenger seats 105. In other embodiments, the passenger cabin 103 can be configured to hold more or fewer passenger seats without departing from the spirit or scope of the present disclosure. Each of the barrel sections 104 can include a plurality of window cutouts 140 to provide the passengers seated in the passenger cabin 103 with views out of the aircraft 100.
The stiffeners 214 can be positioned on the first skin 112a so that the first flange portions 226a of one stiffener 214 are aligned with the corresponding second flange portions 226b of an adjacent stiffener 214. By aligning the flange portions 226 in the foregoing manner, the flange portions 226 can form a plurality of at least approximately continuous support surfaces 228 (identified individually as support surfaces 228a and 228b) extending between the raised portions 224 of the stiffeners 214.
The first panel portion 210a can further include part of a support member or frame 216a. In the illustrated embodiment, the frame 216a is a two-piece frame that includes a first frame section 218 and a second frame section 219. The first frame section 218 can be attached directly to the support surfaces 228 as described in detail in U.S. patent application Ser. No. 10/851,381. In other embodiments, the first frame section 218 can be attached to the first panel portion 210a using other methods. In still further embodiments, the first panel portion 210a can include parts of other frames composed of more or fewer frame sections. Alternatively, the frame 216a can be omitted.
The second panel portion 210b can be at least generally similar in structure and function to the first panel portion 210a described above. Accordingly, the second panel portion 210b can include a plurality of stiffeners 214 (identified individually as stiffeners 214f-j) attached to the second skin 112b. The second panel portion 210b can further include a second frame 216b that is attached to flange portions of the stiffeners 214 in the manner described above for the first panel portion 210a.
Referring next to
In the illustrated embodiment, the strap 220 can be at least approximately as thick as the skins 112, but thicker than the adjacent flange portions 226 of the stiffeners 214. To avoid a step between adjacent surfaces, shim pads or fillers 222 (identified individually as first fillers 222a and second fillers 222b) are positioned on the flange portions 226 adjacent to the strap 220. In one embodiment, the fillers 222 can include composite materials, including graphite-epoxy or similar materials. In other embodiments, the fillers 222 can include aluminum and other metals. In yet other embodiments, the strap 220, the skins 112, and/or the flange portions 226 can have other relative thicknesses and/or the fillers 222 can be omitted.
Referring next to
The fittings 230, the stiffeners 214, the strap 220, and the skins 112 can include composite materials, including graphite-epoxy and/or other suitable composite materials. For example, in one embodiment, the skins 112 can be manufactured with toughened epoxy resin and carbon fibers, e.g., intermediate carbon fibers from Toray Composites America, Inc. of 19002 50th Avenue East, Tacoma, Wash. 98446. In this embodiment, the skins 112 can include fiber tape pre-impregnated with resin (i.e., “prepreg”) and outer plies of prepreg fabric. In another embodiment, the strap 220 and the fittings 230 can also be manufactured from epoxy resin and carbon fibers. The skins 112, the strap 220, and the fittings 230 can have quasi-isotropic lay-ups, i.e., lay-ups having an equal (or approximately equal) number of plies with 0, +45, −45, and 90 degree orientations. The stiffeners 214 can have axial-dominated fiber orientations. In other embodiments, the skins 112, the strap 220, the fittings 230, and the stiffeners 214 can have other fiber orientations.
One advantage of using composite materials instead of metals is that the fittings 230 and the underlying structures (e.g., the skins 112 and the stiffeners 214) will have at least generally similar coefficients of thermal expansion. As a result, temperature fluctuations experienced during operation of the aircraft 100 (
In addition to composites and metal materials, in yet other embodiments, the skins 112, the strap 220, the fittings 230, and the stiffeners 214, and combinations thereof, can include other materials, including hybrid materials such as fiber/metal laminates. Such laminates include fiberglass/aluminum laminates and titanium reinforced graphite laminates (Ti/Gr). One hybrid laminate that includes alternating layers of aluminum and fiberglass is referred to as “GLARE™.” This laminate may offer better fatigue properties than conventional aluminum. A Ti/Gr laminate may offer weight advantages over conventional aluminum or graphite-epoxy, but this laminate may also be more expensive.
One feature of the splice joint 106b illustrated in
One feature of the fittings 230 of the illustrated embodiment are the first and second upstanding edge portions 236a and 236b. The upstanding edge portions 236 can add stiffness to the fittings 230, and can be positioned proximate to the raised portions 224 of the stiffeners 214. One advantage of this configuration is that it can increase the stability of the splice joint 106b, especially under compression loads.
Yet another feature of the illustrated embodiment is that the raised portions 224 of opposing stiffeners 214 are not spliced together across the splice joint 106b. One advantage of this feature is that it makes the fittings 230 relatively easy to install because the raised portions 224 do not have to be in perfect alignment. While the raised portions 224 could be spliced together in other embodiments, doing so would most likely add time and cost to manufacturing of the splice joint because of the various alignment and shimming considerations involved. Further, splicing the raised portions 224 together could close off the ends of the stiffeners 214, thereby preventing sufficient water drainage and preventing visual inspection of any fasteners positioned under the raised portions 224.
Although the splice joint 106b of the illustrated embodiment is built up from a number of separate parts (e.g., the strap 220 and the fittings 230), in other embodiments, two or more of these parts can be integrated into a single part that performs the function and/or has the features of the two or more parts. For example, in one other embodiment, the splice joint 106b can be at least partially formed by a single part that integrates the features of the strap 220 and the fittings 230. In another embodiment, the splice joint 106b can include a single part that integrates the features of the strap 220 and the adjacent fillers 222. Although integrating parts may have the advantages of reducing part count and/or increasing strength, using separate parts may have the advantage of simplifying part construction and/or simplifying installation procedures.
Referring next to
One feature of the strap 320 is that the aperture 324 extends completely around the window cutout 140. One advantage of this feature is that the strap 320 acts as a one-piece doubler, thereby providing an efficient load path around the window cutout 140. A further advantage of this feature is that it reduces part count by combining the window doubler feature with the splice strap feature in a single, integrated part.
In the illustrated embodiment, the strap 320 is thicker than the adjacent flange portions 226 of the stiffeners 214. To avoid a step between adjacent surfaces, the first fillers 222a and the second fillers 222b are positioned on the flange portions 226 adjacent to the strap 320 in those portions of the splice joint 106b positioned away from the window cutout 140. Narrower fillers 322 (identified individually as third fillers 322a and fourth fillers 322b) are positioned on the stiffener flange portions 226 in those areas proximate to the window cutout 140.
Referring next to
One feature of the embodiments described above and illustrated in
The subject matter of copending U.S. patent application Ser. No. 10/646,509, entitled “MULTIPLE HEAD AUTOMATED COMPOSITE LAMINATING MACHINE FOR THE FABRICATION OF LARGE BARREL SECTION COMPONENTS,” filed Aug. 22, 2003; Ser. No. 10/717,030, entitled “METHOD OF TRANSFERRING LARGE UNCURED COMPOSITE LAMINATES,” filed Nov. 18, 2003; Ser. No. 10/646,392, entitled “AUTOMATED COMPOSITE LAY-UP TO AN INTERNAL FUSELAGE MANDREL,” filed Aug. 22, 2003; Ser. No. 10/630,594, entitled “COMPOSITE FUSELAGE MACHINE,” filed Jul. 28, 2003; Ser. No. 10/646,316, entitled “UNIDIRECTIONAL, MULTI-HEAD FIBER PLACEMENT,” filed Aug. 22, 2003; Ser. No. 10/301,949, entitled “PARALLEL CONFIGURATION COMPOSITE MATERIAL FABRICATOR,” filed Nov. 22, 2002; Ser. No. 10/799,306, entitled “SYSTEMS AND METHODS ENABLING AUTOMATED RETURN TO AND/OR REPAIR OF DEFECTS WITH A MATERIAL PLACEMENT MACHINE,” filed Mar. 12, 2004; Ser. No. 10/726,099, entitled “SYSTEMS AND METHODS FOR DETERMINING DEFECT CHARACTERISTICS OF A COMPOSITE STRUCTURE,” filed Dec. 2, 2003; Ser. No. 10/628,691, entitled “SYSTEMS AND METHODS FOR IDENTIFYING FOREIGN OBJECTS AND DEBRIS (FOD) AND DEFECTS DURING FABRICATION OF A COMPOSITE STRUCTURE,” filed Jul. 28, 2003; and [Attorney Docket No. 7784-000696], entitled “SYSTEMS AND METHODS FOR USING LIGHT TO INDICATE DEFECT LOCATIONS ON A COMPOSITE STRUCTURE, filed Apr. 12, 2004, is incorporated herein in its entirety by reference. In addition, the subject matter of U.S. Pat. No. 6,168,358 is also incorporated herein in its entirety by reference.
From the foregoing, it will be appreciated that specific embodiments of the invention have been described herein for purposes of illustration, but that various modifications may be made without deviating from the spirit and scope of the invention. For example, aspects described in the context of particular vehicles, such as aircraft, can equally apply to other vehicles, such as helicopters, rockets, watercraft, etc. Further, aspects described in the context of particular embodiments can be combined or eliminated in other embodiments. Accordingly, the invention is not limited, except as by the appended claims.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13300487 | Nov 2011 | US |
| Child | 14525218 | US | |
| Parent | 12016258 | Jan 2008 | US |
| Child | 13300487 | US | |
| Parent | 10949848 | Sep 2004 | US |
| Child | 12016258 | US |