Stabilization and reduction of TCT of divalent iodide-containing brines

Information

  • Patent Grant
  • 11021645
  • Patent Number
    11,021,645
  • Date Filed
    Tuesday, October 24, 2017
    6 years ago
  • Date Issued
    Tuesday, June 1, 2021
    3 years ago
Abstract
A composition for use in a wellbore activity, the composition comprising a stabilized divalent iodide brine, the stabilized divalent iodide brine comprises a divalent salt system, where the divalent salt system comprises a divalent iodide, an primary iodide stabilizer, the primary iodide stabilizer operable to remove free iodine, prevent the formation of free iodine, and suppress TCT, and an aqueous fluid, where the stabilized divalent iodide brine has a density greater than 11 lb/gal, where the stabilized divalent iodide brines has a TCT of less than or equal to 70 deg F.
Description
BACKGROUND
Technical Field

Described are compositions for use in wellbore fluids in well operations. More specifically, described are fluid compositions with low crystallization temperatures and high densities for use in wellbore fluids in well operations.


Description of the Related Art

When used as a completion fluid, brines can crystallize if exposed to lower temperatures and/or higher pressures. As the density of a brine increases above the salt side of the eutectic point so does the true crystallization temperature (TCT) and pressure crystallization temperature (PCT), which can cause blockage to tubulars in a wellbore or in equipment on the surface if the fluid crystallizes. If crystallization occurs and the solid is filtered from the brine, this will lead to a decrease in fluid density and can cause wellbore stability issues or a blowout. Applying pressure to a divalent brine at a density above the eutectic point will lead to an increase in density, which in turn can lead to crystallization. Crystallization inhibitors can be used to lower the TCT and PCT, but can also result in a reduction of the density of the brine.


Calcium bromide brines can be formulated with densities up to 15.2 pounds per gallon (lb/gal). In deep water and high temperature, high pressure (HTHP) well operations densities up to 14.2 lb/gal are typically used. Zinc salts, such as zinc bromide (ZnBr2) can be used to increase the density above 14.2 lb/gal while maintaining a low crystallization temperature. However, zinc is a marine pollutant and can cause issues in the processing stage if residual zinc is present in the oil sent to the refinery. Cesium formate (CsCHO2) can be used to increase the density of potassium formate above 13.1 lb/gal. Cesium formate is expensive and available only in limited supply making it cost-prohibitive for wellbore operations requiring significant volumes of fluid.


SUMMARY

Described are fluid compositions for use in wellbore fluids in well operations. More specifically, described are compositions with low crystallization temperatures and high densities for use in wellbore fluids in well operations.


In a first aspect, a composition for use in a wellbore activity is provided. The composition including a stabilized divalent iodide brine. The stabilized divalent iodide brine includes a divalent salt system, where the divalent salt system includes a divalent iodide, a primary iodide stabilizer, the primary iodide stabilizer operable to remove free iodine, prevent the formation of free iodine, and suppress TCT, and aqueous fluid, where the stabilized divalent iodide brine has a density greater than 11 lb/gal, where the stabilized divalent iodide brine has a TCT of less than or equal to 70 deg F.


In certain aspects, the divalent iodide is selected from the group consisting of calcium iodide, magnesium iodide, strontium iodide, and combinations of the same. In certain aspects, the divalent iodide is present in the range between 1 wt % and 70 wt %, and further the primary iodide stabilizer is present in the range between 0.1 wt % and 35 wt % of the stabilized divalent iodide brine. In certain aspects, the divalent salt system further includes an additional halide. In certain aspects, the additional halide is selected from the group consisting of a divalent halide, a monovalent halide, and combinations of the same. In certain aspects, the additional halide includes a divalent halide selected from the group consisting of calcium bromide, calcium chloride, magnesium bromide, magnesium chloride, strontium bromide, strontium chloride, and combinations of the same. In certain aspects, the additional halide includes a monovalent halide selected from the group consisting of sodium bromide, sodium chloride, sodium iodide, potassium bromide, potassium chloride, potassium iodide, lithium bromide, lithium chloride, lithium iodide, cesium bromide, cesium chloride, cesium iodide, rubidium bromide, rubidium chloride, rubidium iodide and combinations of the same. In certain aspects, the divalent iodide is present in the range between 1 wt % and 70 wt % of the stabilized divalent iodide brine, the additional halide is present in the range between 1 wt % and 45 wt %, and the primary iodide stabilizer is present in the range between 0.1 wt % and 35 wt % of the stabilized divalent iodide brine. In certain aspects, the primary iodide stabilizer includes a low molecular weight polyol. In certain aspects, the low molecular weight polyol is selected from the group consisting of sorbitol, glycerol, xylitol, mannitol, diglycerol, polyethylene glycol with a molecular weight less than 1000 Da, and combinations of the same. In certain aspects, the stabilized divalent iodide brine further includes a secondary iodide stabilizer. In certain aspects, the secondary iodide stabilizer is selected from the group consisting of amines, amino alcohols, hydroxylamines, hydrazines, erythorbic acid and derivative erythorbate salts, ascorbic acid and derivative ascorbate salts, citric acid and derivative citrate salts, and combinations of the same. In certain aspects, the secondary iodide stabilizer is present in the range between 0.001% v/v and 5% v/v.


In a second aspect, a method of using a stabilized divalent iodide brine during a wellbore activity is provided, the method includes the steps of introducing the stabilized divalent iodide brine into a wellbore and completing the wellbore activity.


In certain aspects, the wellbore activity is selected from the group consisting of drilling, reservoir drilling, completion activities, workover activities, well intervention activities, and as a packer fluid.


In a third aspect, a method of creating a stabilized divalent iodide brine is provided. The method includes the steps of adding an amount of a divalent salt system to aqueous fluid, where the divalent salt system includes divalent iodide, and adding an amount of the primary iodide stabilizer.


In certain aspects, the method further includes the step of adding an amount of an secondary iodide stabilizer.







DETAILED DESCRIPTION

While the scope will be described with several embodiments, it is understood that one of ordinary skill in the relevant art will appreciate that many examples, variations and alterations to the apparatus and methods described herein are within the scope and spirit. Accordingly, the exemplary embodiments described herein are set forth without any loss of generality, and without imposing limitations.


The compositions and methods described here are directed to divalent iodide-containing brines for use in wellbore activities. The divalent iodide-containing brines are stabilized forming stabilized divalent iodide brines. In at least one embodiment, the stabilized divalent iodide brines are clear brines.


The use of divalent iodide in a brine is ineffective due to the divalent iodide being unstable in the presence of air or carbon dioxide. Brines can acquire carbon dioxide and oxygen (from air) as the brines are pumped or circulated. The oxygen or carbon dioxide can oxidize the iodide ion (I) to iodine (I2). The presence of iodine results in a brine that is orange in color and can result in the formation of iodine crystals. The reaction of the iodide ion to iodine can produce unwanted by-products that can precipitate and have a negative impact on the properties of the brine and well operations. Divalent iodide brines in the absence of a primary iodide stabilizer can result in the degradation of the brine. The degraded brines can include halogens that can react with the wellbore and can be corrosive. Due to the instability and potential for degradation, divalent iodides are not suitable for use in commercial wellbore applications.


Advantageously, the addition of a primary iodide stabilizer results in a composition that demonstrates the ability to stabilize the divalent iodide brine by removing free iodine and protecting against further oxidation.


Advantageously, the stabilized divalent iodide brines containing both a divalent iodide and an additional halide can have densities greater than brines containing a divalent halide or monovalent halide alone. Advantageously, the stabilized divalent iodide brine compositions are more readily available, and less toxic as compared to brines containing zinc bromide. Advantageously, the stabilized divalent iodide brine compositions have high densities, increased gas hydrate suppression, stability at elevated temperatures, and reduced TCT as compared to divalent iodide brines in the absence of a primary iodide stabilizer. Advantageously, the stabilized divalent iodide brines can be formulated to have the target properties desired for the wellbore activity, such that the formulations can vary based on the density and TCT desired for a given wellbore activity or a set of wellbore and operating conditions.


As used here, “divalent iodide” refers to a compound containing an alkaline earth metal ion and an iodide ion. Examples of divalent iodides can include calcium iodide, magnesium iodide, strontium iodide, and combinations of the same.


As used here, “additional halide” refers to a divalent halide, a monovalent halide, and combinations of the same.


As used here, “divalent halide” refers to a salt compound containing an alkaline earth metal and a halide ion other than iodine. Examples of divalent halides can include calcium bromide, calcium chloride, magnesium bromide, magnesium chloride, strontium bromide, strontium chloride, and combinations of the same.


As used here, “monovalent halide” refers to a salt compound containing an alkali metal ion and a halide ion. Examples of monovalent halides can include sodium bromide, sodium chloride, sodium iodide, potassium bromide, potassium chloride, potassium iodide, lithium bromide, lithium chloride, lithium iodide, cesium bromide, cesium chloride, cesium iodide, rubidium bromide, rubidium chloride, rubidium iodide and combinations of the same.


As used here, “primary iodide stabilizer” refers to a compound that can remove free iodine and prevent the formation of free iodine, while also reducing TCT.


As used here, “secondary iodide stabilizer” refers to a compound that can scavenge free oxygen or carbon dioxide present in a brine to prevent further oxidation of the iodide to iodine and can react with the iodine to produce iodide and stabilize the brine. Advantageously, the secondary iodide stabilizers can also stabilize the primary iodide stabilizer.


As used herein, “low molecular weight polyols” means polyols with a molecular weight of less than 1000 daltons (da).


As used herein, “true crystallization temperature” or “TCT” refers to the temperature at which crystals form in a brine for a given brine density. The true crystallization temperature is defined as the temperature corresponding to the maximum temperature reached following the super-cooling minimum. In a plot of temperature during a cooling cycle, TCT is the maximum temperature reached following the super-cooling minimum or the inflection point in cases with no super-cooling. If there is no super-cooling TCT will equal first crystal to appear (FCTA). TCT is the measured crystallization temperature nearest the temperature at which a brine will naturally crystallize in pumps, lines, filtration units, and tanks. Further described in API Recommended Practice 13J, Testing of Heavy Brines, 5th Ed. October 2014. By way of example, in a divalent brine containing only a divalent salt and water, as the brine density changes, the TCT changes.


As used herein, “suppress TCT” refers to a reduced TCT as compared to a brine that does not include a primary iodide stabilizer.


As used herein, “clear brine” refers to a solids-free liquid brine, where the salts are soluble and completely dissolve. Advantageously, clear brines have sufficient densities to maintain well control while minimizing potential damage to the producing zone of the well that might arise from undissolved solids.


As used here, “aqueous fluid” refers to a water-containing fluid that can be used in wellbore activities. Examples of aqueous fluid can include water, brine, water-based drilling fluids, and combinations of the same.


As used here, “brine” refers a liquid fluid containing water and soluble salts.


The stabilized divalent iodide brine can contain a divalent salt system, a primary iodide stabilizer, and aqueous fluid. In at least one embodiment, the stabilized divalent iodide brine can include a divalent salt system, a primary iodide stabilizer, an aqueous fluid, and a secondary iodide stabilizer.


The divalent salt system can include a divalent iodide alone or a divalent iodide in combination with an additional halide. In at least one embodiment, where the divalent salt system contains only a divalent iodide, the stabilized divalent iodide brine can include the divalent iodide, a primary iodide stabilizer, and an aqueous fluid. In at least one embodiment, where the divalent salt system contains a combination of a divalent iodide and an additional halide, the stabilized divalent iodide brine can include the divalent iodide, the additional halide, a primary iodide stabilizer, and an aqueous fluid. In at least one embodiment, the stabilized divalent iodide brine can include a divalent iodide, an additional halide, a primary iodide stabilizer, an aqueous fluid, and a secondary iodide stabilizer.


Examples of the primary iodide stabilizer can include low molecular weight polyols. Examples of low molecular weight polyols can include sorbitol, glycerol, xylitol, mannitol, diglycerol, polyethylene glycol with a molecular weight less than 1000 Da, and combinations of the same.


Examples of the secondary iodide stabilizer can include amines, amino alcohols, hydroxylamines, hydrazines, erythorbic acid and derivative erythorbate salts, ascorbic acid and derivative ascorbate salts, citric acid and derivative citrate salts, and combinations of the same. Examples of amines include ethylenediamine (EDA), diethylenetriamine (DETA), triethylenetetramine (TETA), tetraethylenepentamine (TEPA), pentaethylenehexamine (PEHA), aminoethylpiperazine (AEP), hexaethyleneheptamine (HEHA), piperazine, methoxypropylamine (MOPA), morpholine, n-aminopropylmorpholine (APM), and combinations of the same. Examples of amino alcohols include monoethanolamine (MEA), diethanolamine (DEA), triethanolamine (TEA), diethylaminoethanol (DEAE), dimethylethanolamine (DMEA), N-[3-aminopropyl]diethanolamine, aminoethylethanolamine (AEEA), 4-[2-hydroxyethyl]morpholine, diglycolamine, and combinations of the same. Examples of hydroxylamines include diethylhydroxylamine (DEHA), dimethylhydroxylamine (DMHA), hydroxylamine, and combinations of the same. Examples of derivative erthyorbate salts include sodium erthyorbate. Examples of derivative ascorbate salts include sodium ascorbate, potassium ascorbate, magnesium ascorbate, calcium ascorbate and combinations of the same. Examples of derivative citrate salts include mono-, di-, and tri-sodium citrate, potassium citrate, magnesium citrate, calcium citrate, and combinations of the same. In at least one embodiment, the secondary iodide stabilizer is MEA. In at least one embodiment, the secondary iodide stabilizer can include MEA, AEEA, DEHA, and combinations of the same.


In an embodiment of the stabilized divalent iodide brine, where the divalent salt system contains only a divalent iodide, the divalent iodide can be present in the range between 1 percent by weight (wt %) and 70 wt % of the stabilized divalent iodide brine and alternately between 5 wt % and 65 wt % of the stabilized divalent iodide brine. In an embodiment of the stabilized divalent iodide brine, where the divalent salt system contains only a divalent iodide, the primary iodide stabilizer can be present in the range between 0.1 wt % and 35 wt % of the stabilized divalent iodide brine, alternately between 1 wt % and 30 wt % of the stabilized divalent iodide brine, and alternately between 2 wt % and 25 wt % of the stabilized divalent iodide brine. In an embodiment of the stabilized divalent iodide brine, where the divalent salt system contains only a divalent iodide, the secondary iodide stabilizer can be present in an amount between 0.001 volume per volume percent (v/v %) and 5 v/v %.


In an embodiment of the stabilized divalent iodide brine, where the divalent salt system contains both a divalent iodide and an additional halide, the divalent iodide can be present in the range between 1 wt % and 70 wt % of the stabilized divalent iodide brine. In an embodiment of the stabilized divalent iodide brine, where the divalent salt system contains both a divalent iodide and an additional halide, the additional halide can be present in the range between 1 wt % and 45 wt % of the stabilized divalent iodide brine. In an embodiment of the stabilized divalent iodide brine, where the divalent salt system contains both a divalent iodide and a divalent halide, the primary iodide stabilizer can be present in the range between 0.1 wt % and 35 wt %. In an embodiment of the stabilized divalent iodide brine, where the divalent salt system contains both a divalent iodide and a divalent halide, the secondary iodide stabilizer can be present in an amount between 0.001 volume per volume percent (v/v %) and 5 v/v %.


The stabilized divalent iodide brine is an aqueous mixture, such that the remainder of the stabilized divalent iodide brine includes the aqueous fluid. In at least one embodiment, the aqueous fluid is water. In at least one embodiment, the aqueous fluid is brine.


The density of the stabilized divalent iodide brine can be at least 11 lb/gal, and alternately between 11 lb/gal and 17.5 lb/gal, and alternately between 14.2 lb/gal and 17.5 lb/gal.


The TCT of the stabilized divalent iodide brine can be less than or equal to 70 degrees Fahrenheit (deg F.).


The stabilized divalent iodide brine can be prepared by mixing the divalent salt system and the aqueous fluid in amounts to achieve the desired density. In a second step the primary iodide stabilizer can be mixed. In at least one embodiment, additional additives are added in a third step. The stabilized divalent iodide brine can be prepared at the wellsite or can be prepared offsite from the wellsite and delivered premade to the wellsite. In at least one embodiment, when the stabilized divalent iodide brine is prepared at the wellsite, additional amounts of the components can be added after the initial preparation of the stabilized monovalent iodide brine. In at least one embodiment, when the stabilized divalent iodide brine is prepared offsite from the wellsite additional amounts of the components can be added after being delivered to the wellsite to adjust the properties as necessary.


The stabilized divalent iodide brines described here can be used in any wellbore activity during the drilling and completion phases of an oil and gas producing well that requires a brine-based fluid. Wellbore activities can include drilling, reservoir drilling, completion activities, workover activities, well intervention activities, and as a packer fluid.


The stabilized divalent iodide brine is in the absence of zinc compounds, including zinc bromide (ZnBr2), such that the stabilized divalent iodide brine does not contain zinc compounds. The stabilized divalent iodide brine is in the absence of cesium formate, such that the stabilized divalent iodide brine does not contain cesium formate. The stabilized divalent iodide brine is in the absence of earth nitrate salts, such that the stabilized divalent iodide brine does not contain earth nitrate salts.


EXAMPLES

For each of the examples, samples were developed based on a matrix approach targeting density and TCT. In the matrix approach, a test matrix was developed based on varying the amount of the divalent iodide salt used and the properties were measured. A larger matrix was then conducted and the samples were formulated from this larger matrix to meet predetermined specifications.


Example 1

Example 1 analyzed the properties of brines with a divalent salt system containing calcium bromide and calcium iodide. Measurements of density, TCT, and pH were taken before the stability testing. Sample 1 was a comparison sample containing only calcium bromide. The stability test was performed by allowing the samples to stand at room temperature (70 deg F. (21 deg C.)) for two months. As used in Table 1, “pH, neat” refers to the pH of the undiluted brine being measured in the absence of any additives.









TABLE 1







Properties of divalent iodide/bromide brines
















Wt %
Wt %
Wt %
Density
TCT
pH,
Initial
Color after



CaI2
CaBr2
Water
(lb/gal)
(° F.)
neat
Color
stability test


















Sample 1
0
53.1
46.9
14.2
10
6.5
colorless
colorless


Sample 2
8
52
40
14.43
−35
7.46
Orange
Black with ppt


Sample 3
16
42
42
14.62
−53
7.74
Orange
Black with ppt


Sample 4
6
57.3
36.7
15.8
72.6
5.86
Orange
Black with ppt


Sample 5
7
48.4
44.6
15.9
73.6
4.76
Orange
Black with ppt


Sample 6
20
39.8
40.2
16.04
52.4
5.7
Orange
Black with ppt









The data in Table 1 demonstrate that the use of a divalent salt system in a brine that includes both calcium iodide and calcium bromide results in an increased brine density and lower TCT than a brine containing only calcium bromide. The transition in color of samples 2 through 6 suggests that the iodide was oxidized to form I2. As a result of the oxidation, samples 2-6 contain calcium iodide, calcium bromide, and I2.


Example 2

Example 2 assessed the properties of brines with a divalent salt system containing calcium iodide. Measurements of density, TCT, and pH were taken before the stability testing. The stability test was performed by allowing the samples to stand at room temperature (70 deg F. (21 deg C.)) for two months.









TABLE 2







Properties of divalent iodide brines














Wt %
Wt %
Density
TCT
Initial
Color after



CaI2
Water
(lb/gal)
(° F.)
Color
stability test
















Sample 1
61.5
38.4
17.49
   65  
Orange
Black with ppt


Sample 2
57.1
42.9
16.53
 −15.6
Orange
Black with ppt


Sample 3
53.3
46.1
15.56
<-50* 
Orange
Black with ppt


Sample 4
50
50
14.86
<-50  
Orange
Black with ppt





*<- means less than or equal to






As shown in Table 2, the use of a divalent salt system in a brine that includes only calcium iodide can produce high density brines with low TCT values. The transition in color of the samples demonstrate that the iodide was oxidized to form I2. As a result of the oxidation, the samples contain calcium iodide and I2.


Example 3

Example 3 compared stabilized divalent iodide brines to brines containing only calcium bromide and glycerol. The primary iodide stabilizer in Example 3 was glycerol. Measurements of density, TCT, and pH were taken before the stability testing. The stability test was performed by allowing the samples to stand at room temperature (70 deg F. (21 deg C.)) for two months.









TABLE 3







Comparison of stabilized divalent iodide brines to calcium bromide brines
















Wt %
Wt %
Wt %
Wt %
Density
TCT
Initial
Color after



CaI2
CaBr2
Water
Glycerol
(lb/gal)
(° F.)
Color
stability test


















Sample 1
4.2
47.1
38.7
10
14.58
−2.7
colorless
colorless


Sample 2

52.7
37.3
10
14.6
5
colorless
colorless


Sample 3
16.1
44.3
32.9
6.7
14.76
<-50
colorless
colorless


Sample 4

53.9
39.1
7
14.8
28
colorless
colorless


Sample 5
19
38.0
38.3
4.7
15.66
34.2
colorless
colorless


Sample 6
6.6
48.1
36.1
9.2
15.16
34.6
colorless
colorless


Sample 7

55.7
35.3
9
15.2
50
colorless
colorless


Sample 8
5.4
52.2
33.4
9
15.02
27.8
colorless
colorless


Sample 9

54.5
36.5
9
15.0
39.5
colorless
colorless









The data in Table 3 reveal that stabilized divalent iodide brines have increased densities, reduced TCT, and stabilization of the divalent iodide ions. The addition of glycerol to the divalent iodide brines reduced or prevented the oxidation of the iodide ions to produce I2, as can be seen because the samples were colorless at both the initial time and after the stability test. Comparing sample 1 to sample 2, Sample 3 to Sample 4, Sample 6 to Sample 7, and Sample 8 to Sample 9 shows divalent brines with similar density, but the samples containing calcium iodide have reduced TCT as compared to the samples containing only calcium bromide. Sample 5 illustrates the ability to achieve greater densities than brines containing only calcium bromide while still possessing a TCT that is acceptable for process conditions.


Example 4

Example 4 assessed the use of sorbitol as a primary iodide stabilizer. Measurements of density, TCT, and pH were taken before and after the stability testing. The stability test was performed by allowing the samples to stand at room temperature (70 deg F. (21 deg C.)) for two months.









TABLE 4







Properties of divalent iodide brines















Wt %
Wt %
Wt %
Density
TCT
Initial
Color after



CaI2
Water
Sorbitol
(lb/gal)
(° F.)
Color
stability test

















Sample 1
57.1
42.9
0
16.53
−15.6
Orange
Black ppt


Sample 2
53
40
7
16.32
<-50
colorless
Clear pale orange


Sample 3
55.1
41.4
3.5
16.33
<-50
colorless
Clear pale orange









The data in Table 4 show that sorbitol can stabilize divalent iodide ions.


Example 5

Example 5 tested the stability of divalent iodide brines at elevated temperatures. In Table 5, Sample 1 was a stabilized divalent iodide brine containing 37.9 wt % CaBr2, 19 wt % CaI2, 38.3 wt % water, 4.7 wt % glycerol, and 0.30% v/v MEA. In Table 6, Sample 2 was a stabilized divalent iodide brine containing 46.7 wt % CaI2, 29.3 wt % water, 24 wt % glycerol, and 0.30% v/v MEA. In Table 6, Sample 3 was a stabilized divalent brine containing 46.7 wt % CaI2, 29.3 wt % water, and 24 wt % glycerol. To test thermal stability, each sample was aged at 275 deg F. for 7 days in a high pressure thermal aging cells pressurized with 300 psi nitrogen gas.









TABLE 5





Thermal Stability of Sample 1 at 275 deg F. for 7 days.
















Color before aging
Pale straw color


Color after aging 1 week @ 275 deg F.
Straw color, slightly darker


pH after 1 week @ 275 deg F.
6.79


TCT before aging
34.2 deg F.


TCT after aging
31.2 deg F.
















TABLE 6







Thermal Stability of Samples 2 and 3 at 275 deg F. for 7 days.










Sample 2
Sample 3













Secondary iodide stabilizer
MEA 0.30% v/v
None


Color before aging
Pale straw color
Pale straw color


Color after aging 1 week @ 275
colorless
colorless


deg F.


pH before aging
8.04
7.78


pH after 1 week @ 275 deg F.
7.73
6.85









The results in Table 5 show that there is little impact on the TCT of the sample after exposure to elevated temperatures. This suggests that stabilized divalent iodide brines can be exposed to an elevated bottom hole temperature statically for extended periods of time without detriment to the performance of the stabilized divalent iodide brine. The results in Table 6 show that the components of the fluid do not decompose when exposed to elevated temperatures. Table 6 also illustrates that the addition of MEA assists in maintaining a greater pH and a smaller drop in pH during the aging process. This suggests that the addition of MEA to a stabilized divalent iodide brine enhances corrosion protection and stability.


Although the present embodiments have been described in detail, it should be understood that various changes, substitutions, and alterations can be made hereupon without departing from the principle and scope. Accordingly, the scope should be determined by the following claims and their appropriate legal equivalents.


The singular forms “a,” “an,” and “the” include plural referents, unless the context clearly dictates otherwise.


Optional or optionally means that the subsequently described event or circumstances can or may not occur. The description includes instances where the event or circumstance occurs and instances where it does not occur.


Ranges may be expressed herein as from about one particular value, and/or to about another particular value. When such a range is expressed, it is to be understood that another embodiment is from the one particular value and/or to the other particular value, along with all combinations within said range.


As used herein and in the appended claims, the words “comprise,” “has,” and “include” and all grammatical variations of the same are each intended to have an open, non-limiting meaning that does not exclude additional elements or steps.


It is to be understood that that the mere use of the term “primary” and “secondary” does not require that there be any “tertiary” or “third” component, although that possibility is contemplated under the scope of the embodiments.

Claims
  • 1. A composition for use in a wellbore activity, the composition consisting essentially of: a stabilized divalent iodide brine, the stabilized divalent iodide brine comprises:a divalent salt system, the divalent salt system comprises a divalent iodide, wherein the divalent iodide is selected from the group consisting of calcium iodide, magnesium iodide, strontium iodide, and combinations of the same;a primary iodide stabilizer, the primary iodide stabilizer operable to remove free iodine, prevent the formation of free iodine, and suppress true crystallization temperature (TCT), wherein the primary iodide stabilizer comprises a low molecular weight polyol selected from the group consisting of sorbitol, glycerol, xylitol, mannitol, diglycerol, polyethylene glycol with a molecular weight less than 1000 Da, and combinations of the same;a secondary iodide stabilizer, the secondary iodide stabilizer operable to scavenge free oxygen or carbon dioxide and prevent oxidation of the iodide to iodine, the secondary iodide stabilizer selected from the group consisting of amines, amino alcohols, hydroxylamines, hydrazines, erythorbic acid and derivative erythorbate salts, ascorbic acid and derivative ascorbate salts, citric acid and derivative citrate salts, and combinations of the same;and an aqueous fluid,where the stabilized divalent iodide brine has a density greater than 11 lb/gal, and where the stabilized divalent iodide brine has a TCT of less than or equal to 70 deg F.
  • 2. The composition of claim 1, wherein the divalent iodide is present in the range between 1 wt % and 70 wt %, and further wherein the primary iodide stabilizer is present in the range between 0.1 wt % and 35 wt % of the stabilized divalent iodide brine.
  • 3. The composition of claim 1, wherein the secondary iodide stabilizer is present in the range between 0.001% v/v and 5% v/v.
  • 4. The composition of claim 1, where the secondary iodide stabilizer comprises an amine selected from the group consisting of ethylenediamine (EDA), diethylenetriamine (DETA), triethylenetetramine (TETA), tetraethylenepentamine (TEPA), pentaethylenehexamine (PEHA), aminoethylpiperazine (AEP), hexaethyleneheptamine (HEHA), piperazine, methoxypropylamine (MOPA), morpholine, n-aminopropylmorpholine (APM), and combinations of the same.
  • 5. The composition of claim 1, where the secondary iodide stabilizer comprises an amino alcohol selected from the group consisting of monoethanolamine (MEA), diethanolamine (DEA), triethanolamine (TEA), diethylaminoethanol (DEAE), dimethylethanolamine (DMEA), N-[3-aminopropyl]diethanolamine, aminoethylethanolamine (AEEA), 4-[2-hydroxyethyl]morpholine, diglycolamine, and combinations of the same.
  • 6. The composition of claim 1, where the secondary iodide stabilizer comprises an hydroxylamine selected from the group consisting of diethylhydroxylamine (DEHA), dimethylhydroxylamine (DMHA), hydroxylamine, and combinations of the same.
  • 7. The composition of claim 1, where the secondary iodide stabilizer comprises sodium erthyorbate.
  • 8. The composition of claim 1, where the secondary iodide stabilizer comprises a derivative ascorbate salt selected from the group consisting of sodium ascorbate, potassium ascorbate, magnesium ascorbate, calcium ascorbate and combinations of the same.
  • 9. The composition of claim 1, where the secondary iodide stabilizer comprises a derivative citrate salt selected from the group consisting of mono-, di-, and tri-sodium citrate, potassium citrate, magnesium citrate, calcium citrate, and combinations of the same.
  • 10. The composition of claim 1, where the secondary iodide stabilizer is selected form the group consisting of monoethanolamine (MEA), aminoethylethanolamine (AEEA), diethylhydroxylamine (DEHA), and combinations of the same.
  • 11. The composition of claim 1, wherein the divalent iodide is present in the range between 1 wt % and 70 wt %, and further wherein the primary iodide stabilizer is present in the range between 2 wt % and 25 wt % of the stabilized divalent iodide brine.
US Referenced Citations (71)
Number Name Date Kind
1911195 Kepfer May 1933 A
2191312 Cannon Feb 1940 A
2898294 Priest et al. Aug 1959 A
3275552 Kern et al. Sep 1966 A
4292183 Sanders Sep 1981 A
4444668 Walker et al. Apr 1984 A
4465601 Pasztor, Jr. Aug 1984 A
4486340 Glass, Jr. Dec 1984 A
4566976 House et al. Feb 1986 A
5076364 Hale et al. Dec 1991 A
5330683 Sufrin Jul 1994 A
5415230 Fisk, Jr. et al. May 1995 A
5728652 Dobson, Jr. Mar 1998 A
5846914 Finkelstein et al. Dec 1998 A
6080704 Halliday et al. Jun 2000 A
6100222 Vollmer et al. Aug 2000 A
6124244 Murphey Sep 2000 A
6489270 Vollmer et al. Dec 2002 B1
6617285 Crews Sep 2003 B2
6635604 Halliday et al. Oct 2003 B1
6730234 Symens May 2004 B2
6843931 Sapienza Jan 2005 B2
7048961 Knauf May 2006 B2
7078370 Crews Jul 2006 B2
7306039 Wang et al. Dec 2007 B2
7825073 Welton et al. Nov 2010 B2
7910524 Welton et al. Mar 2011 B2
7960315 Welton et al. Jun 2011 B2
8003578 Monroe et al. Aug 2011 B2
8030254 Phatak et al. Oct 2011 B2
8067342 Lin et al. Nov 2011 B2
8071059 Filippi et al. Dec 2011 B2
8381537 Morita et al. Feb 2013 B2
8697611 Zhang Apr 2014 B2
8853135 Phatak et al. Oct 2014 B2
8936111 Maghrabi et al. Jan 2015 B2
8950492 Maghrabi et al. Feb 2015 B2
9593276 Livanec Mar 2017 B2
9868890 Alleman Jan 2018 B2
20030092581 Crews May 2003 A1
20040124013 Wiesner et al. Jul 2004 A1
20050038199 Wang et al. Feb 2005 A1
20050101491 Vollmer May 2005 A1
20050253110 Chauhan et al. Nov 2005 A1
20080093579 Knauf Apr 2008 A1
20080269081 Lin et al. Oct 2008 A1
20090048126 Phatak et al. Feb 2009 A1
20100016180 Scoggins et al. Jan 2010 A1
20100093565 Phatak et al. Apr 2010 A1
20100130388 Phatak et al. May 2010 A1
20100163255 Horton et al. Jul 2010 A1
20100303737 Hurtig Dec 2010 A1
20100311621 Kesavan et al. Dec 2010 A1
20120118569 Deville May 2012 A1
20130098615 Perez et al. Apr 2013 A1
20130168095 Loveless Jul 2013 A1
20130231268 Ghosh et al. Sep 2013 A1
20140148366 Reyes Bautista May 2014 A1
20140221256 Holtsclaw et al. Aug 2014 A1
20140262283 Savari et al. Sep 2014 A1
20140352961 Dobson, Jr. et al. Dec 2014 A1
20150096808 Misino et al. Apr 2015 A1
20160177698 Schultheiss et al. Jun 2016 A1
20160208158 Monahan et al. Jul 2016 A1
20170088762 Zhang et al. Mar 2017 A1
20170145284 Davidson et al. May 2017 A1
20170158939 Chen et al. Jun 2017 A1
20170158976 O'Rear et al. Jun 2017 A1
20170190954 Schultheiss et al. Jul 2017 A1
20170292055 Alleman Oct 2017 A1
20180016484 Ray et al. Jan 2018 A1
Foreign Referenced Citations (15)
Number Date Country
106928930 Jul 2017 CN
0194254 Sep 1986 EP
2463350 Jun 2012 EP
1863890 Oct 2014 EP
2250761 Jun 1992 GB
2334279 Aug 1999 GB
56098482 Aug 1981 JP
20040043935 May 2004 KR
9821291 May 1998 WO
03064555 Aug 2003 WO
2004050557 Jun 2004 WO
2009126548 Oct 2009 WO
20015068865 May 2015 WO
2016025137 Feb 2016 WO
2017165754 Sep 2017 WO
Non-Patent Literature Citations (14)
Entry
Collins et al. “Exploitation of Minerals in Disposal Brines” SPE 3453 (1971) (8 pages); (Year: 1971).
Oddo et al. “A Discussion of Calcium Carbonate Scaling Problems and Solutions with Respect to Produced Brines” SPE 19763 (1989) (14 pages) (Year: 1989).
Kaminski, et al., “Clearly Different”, Reprinted from Oilfield Technology, Jul. 2012, 4 pgs.
Section B14 Solubility in Non-Aqueous Solvents, Formate Technical Manual, Mar. 2013, 1-4, Version 1, Cabot Specialty Fluids, 4 pgs.
Chen, et al.; Effect of Cryoprotectants on Eutectics of NaCl 2H2O/ice and KCl/ice Studied by Temperature Wave Analysis and Differential Scanning Calorimetry; Thermochimica Acta 431 (2005) 106-112; 7 pgs.
PCT/US2017/023995 International Search Report and Written Opinion dated May 24, 2017; 15 Pgs.
PCT/US2017/023996 International Search Report and Written Opinion dated May 24, 2017; 16 Pgs.
PCT/US2017/024008 International Search Report and Written Opinion dated May 24, 2017; 16 Pgs.
Telang, et al., Effective Inhibition of Mannitol Crystallization in Frozen Solutions by Sodium Chloride, Pharmaceutical Research (Apr. 2003), vol. 20, No. 4, 660-667; 8 pgs.
U.S. Appl. No. 15/468,940 Final Office Action dated Jan. 2, 2019 (10 pages).
International Search Report and Written Opinion for related PCT application PCT/US2018/057202 dated Jan. 7, 2019.
International Search Report and Written Opinion for related PCT application PCT/US2018/057205 dated Dec. 14, 2018.
U.S. Appl. No. 15/468,842 Final Office Action dated Apr. 25, 2019 (12 pages).
International Search Report and Written Opinion for related PCT application PCT/US2018/057200 dated Dec. 14, 2018.
Related Publications (1)
Number Date Country
20190119556 A1 Apr 2019 US