Stabilized aqueous aluminum zirconium solutions

Abstract

The present invention describes a method and compositions by which introducing PO4−3 ion at particular stage in the preparation of aluminum/zirconium solutions surprisingly results in significantly improved zirconium molecular weight stability.

Description

BACKGROUND OF THE INVENTION

1. Field of Invention

This invention relates generally to the field of stabilized aqueous aluminum zirconium solutions useful in antiperspirant formulations, methods of making same and compositions thereof.

2. Description of Related Art

Aluminum zirconium chlorohydrate-glycine aqueous solutions are used in various antiperspirant formulations as the active ingredient. It is known that lower molecular weight zirconium polymers are more efficacious than larger molecular weight zirconium polymers. In these solutions and in the formulas (i.e., clear gels) these materials rapidly polymerize, reducing their effectiveness.

The following references are disclosed. U.S. Pat. No. 5,118,497 (Katsoulis), U.S. Pat. No. 5,202,123 (Katsoulis), U.S. Pat. No. 5,225,187 (Carmody), U.S. Pat. No. 5,589,196 (Callaghan et al.), U.S. Pat. No. 5,672,340 (Sun et al.), U.S. Pat. No. 5,770,196 (Callaghan et al.), U.S. Pat. No. 6,403,069 (Chopra et al), U.S. Pat. No. 6,726,901 (Yin et al.), U.S. Pat. No. 6,783,755 (Kajino et al.), U.S. Pat. No. 6,835,374 (Parekh et al.), U.S. Publication No. 2003/0021757 (Carillo et al.), U.S. Publication No. 2003/0211060 (Yin et al.), U.S. Publication No. 2004/00011795 (Li et al.), U.S. Publication No. 2004/022750 (Lee et al.), U.S. Publication No. 2004/0136934 (Carrillo et al.), U.S. Publication No. 2005/0019287 (Li et al.).

BRIEF SUMMARY OF THE INVENTION

The present invention describes compositions of, and a method for making the compositions, where introducing a phosphate ion such as PO₄⁻³, at a certain stage in the preparation of the Aluminum/Zirconium (Al/Zr) solutions surprisingly results in significantly improved zirconium molecular weight stability.

DETAILED DESCRIPTION OF THE INVENTION

The present invention describes various methods of introducing a phosphate (PO₄⁻³) ion at a certain stage in the preparation of the Al/Zr solutions which surprisingly results in significantly improved zirconium molecular weight stability. The present invention is directed to such methods, compositions thereof, and methods of using same in compositions such as in antiperspirant compositions and the like.

Method:

A phosphate ion, such as PO₄⁻³, is to introduced in the initial dissolution of the zirconium salt.

The phosphate (PO₄⁻³) to zirconium ratio should be approximately weight/weight 0.02:1-0.151:1.

The PO₄⁻³ ion may be from H₃PO₄ or a variety of salts; for example, Na₃PO₄, K₃PO₄, etc. and the invention is not intended on being limited to any particular salt.

Several routes of manufacture for stabilized Al/Zr solutions are disclosed in the present invention: one utilizing Zirconium Carbonate paste (Zr(CO₃)₂) or another source or zirconium ion, another utilizing Zirconium Oxychloride (ZrOCl₂) or another source of zirconium ion.

1. An Example of the Zr(CO₃)₂ Route:

Combine 35.88 grams of 20° baume HCl and 0.5 grams 85% H₃PO₄

Combine HCl/H₃PO₄ mixture with 64.1 grams of Zr(CO₃)₂ paste.

Mix well. Once dissolved, allow to stand at about room temperature for approximately 24 hours.

To the zirconium solution add buffer (preferably a glycine buffer) at a molar ratio of approximately 1:1 with zirconium.

The zirconium solution may now be combined with an aqueous aluminum salt to a desired Al:Zr molar ratio which may be about 1:1 to about 11:1, and preferably about 2:1 to about 10:1.

2. An Example of the ZrOCl₂ Route:

Combine 50 grams H₂O+0.5 grams 85% H₃PO₄

Add 50 grams ZrOCl₂ crystals. Mix well. Allow to sit for 24 hours once dissolved.

To the zirconium solution add a buffer (preferably glycine) at a molar ratio of approximately 1:1 with zirconium.

The zirconium solution may now be combined with an aqueous aluminum salt to a desired Al:Zr molar ratio previously specified and a desired (Al+Zr):Cl molar ratio. The desired (Al+Zr):Cl molar ratio is in the approximate range of about 0.2:1 to about 2.5:1, preferably about 0.9:1 to about 2.1:1.

The order of addition when preparing the final Al/Zr solution should be:

1. Zr solution

2. Aluminum solution

3. Acid/water

We have made the following observations using a Wyatt Dawn Light Scattering instrument to measure zirconium molecular weight in Al/Zr glycine aqueous solutions.

Freshly prepared Al/Zr solution: no PO₄⁻³ has a molecular weight of 18,000. Within 24 hours, the molecular weight increases to 50,000.

In contrast, a freshly prepared Al/Zr solution containing PO₄⁻³ ion has a molecular of 18,000 after 24 hours, no molecular weight increase is noted. The monitoring of the molecular weight for one month shows an increase to only 30,000 molecular weight.

Polymerically Stable Zirconium Salts

Zirconium salts and aqueous solutions of these salts are used in a variety of applications, including antiperspirants, oil field applications, catalysts, ceramics, electronics, leather tanning, textile dyeing, paper manufacturing, and production of other zirconium chemicals. Zirconium salts consist of zirconium polymeric species of varying distribution. The distributions of these polymers have a significant impact on the salts performance in said application. Further, zirconium salts and especially the aqueous solutions of these salts are not stable with respect to this polymer distribution.

We describe a method to produce a polymerically stabilized zirconium carbonate paste by introducing phosphate (PO₄⁻³) ion at a particular proper stage in the preparation of the zirconium carbonate paste. This stabilized zirconium carbonate may then be further processed to produce other stable zirconium salts and stable aqueous solutions of these salts.

We also describe various methods by which a molecular weight stable aluminum zirconium chlorohydrate glycine aqueous solution for use in antiperspirants can be produced by the addition of a phosphate ion (e.g., PO₄⁻³) ion at a certain stage of manufacture. These solutions may then be used as solutions or dried to produce a powder. It is known that lower molecular weight zirconium polymers are more effective in the reduction of perspiration than are larger molecular weight zirconium polymers. It is also known that zirconium in aqueous solutions and the formulations (i.e., clear gels) they are used in rapidly polymerize resulting in reduced effectiveness. The dried form of these salts also exhibit polymerization to a lesser extent than solutions.

Method:

We describe several processes to produce polymerically stable zirconium carbonate.

1. Zirconium Oxychloride (ZrOCl₂) Route:

A solution containing one or more of the following bases is prepared: ammonium carbonate, ammonium bicarbonate, sodium carbonate, sodium bicarbonate. A solution of zirconium oxychloride is prepared and PO₄⁻³ ion is added using phosphoric acid or a PO₄⁻³ containing salt. The PO₄⁻³ content should be in a molar ratio of P:Zr of 0.01:1-0.15:1. The zirconium solution is then added to the base solution with mixing, heating, and then pH adjustment to precipitate zirconium carbonate. The approximate heating temperature is about 50-120 degrees C. with a heating time of about 1-3 hours. The pH should be adjusted between about 2.0 and about 7.0 and be stable for 30 minutes at the final reading. The zirconium carbonate should be washed and then separated from the liquid.

2. Zirconium Sulfate Route:

A solution containing one or more of the following bases is prepared: ammonium carbonate, ammonium bicarbonate, sodium carbonate, sodium bicarbonate. The base concentration should be in the approximate range of about 1-15% as CO₃. A solution of zirconium sulfate is prepared and the PO₄⁻³ ion is added using phosphoric acid or a PO₄⁻³ containing salt. The PO₄⁻³ content should be in a molar ratio of P:Zr of about 0.01:1-0.15:1. The zirconium solution is then added to the base solution with mixing, heating, and pH adjustment to precipitate zirconium carbonate. Zirconium carbonate should be washed and then separated from liquid.

We describe several methods for the manufacture of stabilized Al/Zr solutions:

1. Zirconium Carbonate Route:

Combine 35.88 grams 20 baume HCl and 0.5 grams 85% H₃PO₄.

Combine HCl/H₃ PO₄ mixture with 64.1 grams zirconium carbonate paste.

Mix well and allow to sit for approximately 24 hours.

To the zirconium solution add a buffer (preferably a glycine buffer) at a glycine:zirconium molar ratio of about 0.51-1.5:1.

The zirconium solution may now be combined with an aqueous aluminum salt to the desired to Al:Zr molar ratios and (Al+Zr): Cl molar ratios identified above (note always add the aluminum to the zirconium). The solution may be used as is or dried in conventional means to form a powder.

2. Zirconium Oxychloride Route:

Combine 50 grams water and 0.5 grams 85% H₃PO₄.

Add 50 grams of zirconium oxychloride. Mix well. Let sit for approximately 24 hours.

To the zirconium solution add a buffer (preferably glycine) at a glycine:zirconium molar ratio of 0.5:1 to 1.5:1.

The zirconium solution may now be combined with an aqueous aluminum salt to the desired Al:Zr molar ratios and (Al+Zr):Cl molar ratios previously described. (Note, always add aluminum to zirconium). The solution may be used as is or dried in a conventional manner to form a powder.

We have made the following observations on the above Al/Zr solutions using a Wyatt Dawn Light Scattering instrument.

Freshly prepared Al/Zr solutions with or without PO₄⁻³ ion have a molecular weight of 18,000. The solution not containing PO₄⁻³ shows an increase in molecular weight to 50,000 in 24 hours. In contrast, the solution containing PO₄⁻³ does not increase in 24 hours and shows an increase to only 30,000 after 30 days.

Without further elaboration the foregoing will so fully illustrate our invention that others may, by applying current or future knowledge, adapt the same for use under various conditions of service.

Claims

1. A stabilized aqueous solution composition comprising aluminum ion, zirconium ion, phosphate ion, and chloride ion, wherein the phosphate ion to zirconium ion ratio is about 0.02:1-0.151:1 weight/weight, further wherein the zirconium is polymerically stable.

2. The composition of claim 1 wherein the phosphate ion is PO4−3.

3. The composition of claim 1 wherein (Al+Zr):Cl is present in a molar ratio of about 0.3:1 to about 2.5:1.

4. The composition of claim 3 wherein the phosphate ion is PO4−3.

5. A stabilized aqueous solution composition comprising aluminum ion, zirconium ion, phosphate ion, glycine and chloride ion, wherein the glycine is at a molar ratio of about 0.5:1 to 1.5:1 with zirconium ion, and wherein Al:Zr is present in a molar ratio of about 1:1 to about 11:1, further wherein the zirconium is polymerically stable.

6. A stabilized aqueous solution composition comprising aluminum ion, zirconium ion, and phosphate ion, wherein the phosphate ion to zirconium ion ratio is about 0.02:1-0.151:1 weight/weight, further wherein the zirconium is polymerically stable.

7. A stabilized aqueous solution composition comprising aluminum ion, zirconium ion, phosphate ion, and chloride ion, made by the method comprising the steps of: (a) combining a chloride-containing acid and a source of phosphate ion to form a phosphate mixture; (b) combining the phosphate mixture with a zirconium ion source and mixing well to dissolve; (c) allowing the product of step (b) to stand at about room temperature for about 24 hours; (d) mixing a buffer at a molar ratio of about 1:1 with zirconium; (e) combining the product of step (d) with aqueous aluminum salt to an Al:Zr molar ratio of about 1:1 to about 11:1 and an (Al+Zr):Cl molar ratio of about 0.3:1 to about 2.5:1; and (f) optionally, drying to form a powder, further wherein the zirconium is polymerically stable.

8. The composition of claim 7 wherein the phosphate ion to zirconium ion ratio is about 0.02:1-0.151:1 weight/weight.

9. The composition of claim 7 wherein the zirconium ion source is a Zr(CO3)2 paste.

10. The composition of claim 7 wherein the zirconium ion source is zirconium oxychloride.

11. The composition of claim 7 wherein the buffer is a glycine buffer.

12. The composition of claim 7 wherein the phosphate ion is PO4−3.

13. The composition of claim 7 wherein the Al:Zr molar ratio is about 2:1 to about 10:1.

14. The composition of claim 7 wherein the (Al+Zr):Cl molar ratio is about 0.9:1 to about 2.1:1.