Stabilized dispersion of behenyl alcohol

Abstract

IR 6 (Cosmetics, Toiletry and Fragrance Association, Inc., 7th ed. 1997). Viscosities are measured using Brookfield viscometers (1,000-20,000 cps, Spindle No. 5, 20 rpm, 60 second run, 25 degrees C.) unless otherwise indicated. 967-00—IR # 6967-00-1-A low viscosity, stable dispersion of behenyl alcohol comprising: (a) 10-40 weight % on an actives basis of behenyl alcohol; (b) 1.0-8.0 weight % of an anionic surfactant selected from the group consisting of sodium lauryl ether sulfate, sodium lauryl sulfate, magnesium lauryl ether sulfate, magnesium lauryl sulfate, calcium lauryl ether sulfate, calcium lauryl sulfate, ammonium lauryl ether sulfate, and ammonium lauryl sulfate; and (c) 1.0-3.0 weight % (on an actives basis) of a betaine selected from the group consisting of C12-18 amidopropylbetaine; wherein the dispersion has a stability of at least 3 months at a temperature of 49 degrees C., a viscosity in the range of 1,000-20,000 centipoise, and no more than 0.2 weight % of cationic material.

Description

BACKGROUND OF INVENTION

[0001] 1. Field of the Invention

[0002] This invention relates to ways of stabilizing dispersions of behenyl alcohol, to create improved pearlizing compositions which can be stable at room temperature.

[0003] 2. Background of the Invention

[0004] The stabilization and use of behenyl alcohol is described in a variety of references.

[0005] U.S. Pat. No. 4,892,728 to Kawa et al describes pumpable cationic fatty alcohol dispersion with a low content of cationic dispersant. The dispersion is made with 0.01-1 weight % of a cationic surfactant containing a quaternary ammonium, pyridinium or imidazolinium group and a linear C8-22 alkyl or 2-hydroxyalkyl group.

[0006] U.S. Pat. No. 4,883,660 to Blackman et al describes gel bases for pharmaceutical compositions comprising behenyl alcohol and a glycol or selected ethoxylated solvent.

[0007] U.S. Pat. No. 5,100,657 to Ansheer-Jackson et al describes hair conditioning compositions which provide cleaner hair than others based on quaternary ammonium compounds and lipid materials. The primary thickening agent is a nonionic long chain alkylated cellulose ether. A fatty alcohol such as behenyl alcohol is used as a conditioning agent.

[0008] U.S. Pat. No. 5,510,100 to Picard et al describes an oil-in-water emulsion containing an auto-emulsifiable composition based on a fatty alcohol and on an alkyl polyoside and a co-emulsifying agent.

[0009] U.S. Pat. No. 5,827,920 to Wanatabe et al describes a surfactant-free emulsion comprising a higher alcohol which is a solid at room temperature, an acrylic acid-methacrylic acid alkyl copolymer and a silicone oil.

[0010] U.S. Pat. No. 5,948,416 to Wagner et al describes stable topical compositions comprising a stable, hydrophobic, structuring agent (which can include behenyl alcohol), and a hydrophilic surfactant.

[0011] U.S. Pat. No. 5,973,066 to Sakuta et al describes an oil-in-water aqueous organopolysiloxane emulsion comprising a quaternary ammonium chloride having 1 or 2 stearyl or behenyl groups.

[0012] U.S. Pat. No. 6,274,130 to Murray et al describes a rinse off conditioning product for hair comprising a cationic surfactant, a selected emulsion polymerized dimethiconol nonionic conditioning polymer, which composition can optionally include behenyl alcohol.

[0013] U.S. Pat. No. 6,419,946 to Sonneville et al describes a nanoemulsion based on mixed esters of a fatty acid or fatty alcohol, of a carboxylic acid and of a glycerol.

[0014] Behenyl alcohol has seen a variety of uses in personal care products, particularly for hair care. It is an object of the invention to provide stabilized forms of behenyl alcohol which are useful as pearlizing agents and which are easier to use than conventional types of behenyl alcohol compositions.

SUMMARY OF INVENTION

[0015] A low viscosity, stable dispersion of behenyl alcohol comprising:(a) from about 10 to about 40 weight % on an actives basis (preferably 20-25%) of behenyl alcohol;(b) from about 1.0 to about 8.0 weight % (preferably 1-5%) of an anionic surfactant selected from the group consisting of sodium lauryl ether sulfate, sodium lauryl sulfate, magnesium lauryl ether sulfate, magnesium lauryl sulfate, calcium lauryl ether sulfate, calcium lauryl sulfate (best for avoiding viscosity problems), ammonium lauryl ether sulfate, and ammonium lauryl sulfate;(c) from about 1.0 to about 3.0 weight % (on an actives basis) of a betaine selected from the group consisting of C12-18 amidopropylbetaine (for example, cocamidopropyl betaine); (d) optionally from about 0.3 to about 5.0 weight % of a C12-C20 straight chain or iso-branched alcohol having 2-20 (particularly 2-10) moles of ethoxylation (for example, Isosteareth-2, lsosteareth-4, Isosteareth-10, Laureth 2-20, and especially Laureth-2, Laureth-4 and Laureth-10) (with higher amounts of ethoxylation being used for the longer carbon chains); and(e) optionally a cationic material having less than or equal to 22 carbons (for example, a cationic material such as a C8-22 alkyl ammonium chloride, preferably one selected from the group consisting of cetyl trimethyl ammonium chloride, (also called cetrimonium chloride) and cocotrimethylammonium chloride); wherein the dispersion:(a1) has a stability of at least 3 months at a temperature of 49 degrees C.;(b1) has a viscosity in the range of 1,000-20,000 centipoise (“cps”) (for example, 1,000-20,000 cps, particularly 1,000-15,000 cps, and, more particularly, 1,000 cps-8,000 cps); and(c1) is limited to less than 0.2 weight % of total cationic material.

[0016] The invention also comprises a method for (A) combining the ingredients listed above;(B) melting and mixing the set of ingredients using a temperature in the range of about 80 to about 85 degrees C. to create a combined material;(C) stirring and homogenizing the combined material at a temperature in the range of about 80 to about 85 degrees C. for at least about an hour; (D) cooling the combined material down to a temperature in the range of about 20 to about 25 degrees C. at a cooling rate in the range of about 0.05-0.4 degrees C./minute, preferably 0.15-0.3 and, most preferably, at a rate of 0.2-0.25 degrees C./minute; and(E) holding the combined material at the temperature of about 20 to about 25 degrees C. for at least 2 hours.

DETAILED DESCRIPTION

[0017] The dispersions of the invention are shear thinning. Since the dispersion can increase in viscosity during storage, it is preferred to initially make the dispersion at the lower range of viscosity such as in the range of 1,000-5,000 cps.

[0018] By “stable” is meant that the dispersion is judged by visual observance as giving 0% separation even at temperatures in the range of 49 degrees C.for the 3 month time period described. It has been found that at least 1% of the anionic surfactant and at least 1% of the betaine are needed in order to get the superior stability described for the invention.

[0019] It is preferred to include Isosteareth-2 if a hair conditioning product is to be made since it contributes to the conditioning effect of the final hair care composition.

[0020] The behenyl alcohols included in this invention can include natural as well as synthetically made alcohol. For natural alcohol, it is understood that a distribution of carbon lengths is included. One preferred type of behenyl alcohol useful for this invention is a 72-80% material sold under the tradenames Lanette 22, Stenol 1822 A, Stenol 1822-80, and Lanette 22-80.

[0021] The alcohols are used in this invention to obtain a pearlizing effect (such as in hair care products such as shampoos, conditioners and combination products) and processability.

[0022] The use of dispersions of alcohols (especially behenyl alcohol) is helpful in keeping process costs down since the dispersion allows stable hair car products to be made with a cold process.

[0023] Viscosity is related to particle size control; during the manufacturing process the dispersion must be cooled down to at least 25, most preferably 20 degrees C. and kept at this temperature of 20-25 degrees C. for at least for 2 hours to get a good viscosity result.

[0024] The ingredients described above are commercially available.

[0025] TABLE A shows the impact on viscosity of final temperature for cooling down.

[0026] Procedure: Melt and/or mix up all the ingredients listed for the specific Example. Heat the mixture up to a temperature in the range of 80-85 degrees C. Stir/homogenize the material for 1 hour and then start to cool down with a cooling rate of 0.2-0.25 degrees C./min. Viscosity was measured 24 hours after manufacturing/finishing the compound with Brookfield equipment, RVT, 25 C., Spindle 5, 20 rpm.

	TABLE A
	Ingredient	Ex. 1A	Ex. 2A	Ex. 3A
	Water	QS	QS	QS
	Sodium Lauryl 2EO	6.0	6.0	6.0
	Sulfate
	Cocamidopropyl	1.0	1.0	1.0
	betaine
	Laureth-4	1	1	1
	Behenyl alcohol	25.0	25.0	25.0

[0027] Cooled-down to 30° C. 25,000 mpas Cooled down to 25° C. 15,000 mpascooled down to 25° C. and 5000 mPascals kept 2 hours at 25degrees C. It is preferred to have the combination of Isosteareth-2 and Betaine. Also, when fatty alcohol ethoxylates are ethoxylates are used, the maximum amount should preferably be kept to 2%, for example, between 1-2%,

EXAMPLES

[0028] The following Examples are offered as illustrative of the invention and are not to be construed as limitations thereon. In the Examples and elsewhere in the description of the invention, chemical symbols and terminology have their usual and customary meanings. In the Examples as elsewhere in this application values for viscosity, molecular weights and degree of ethoxylation or propoxylation are averages. Temperatures are in degrees C. unless otherwise indicated. As is true for the rest of the application as well, the amounts of the components are in weight percents based on the standard described; if no other standard is described then the total weight of the composition is to be inferred. Various names of chemical components include those listed in the CTFA International Cosmetic Ingredient Dictionary

Example A

[0029] General Method To the main mixing vessel is added water and the anionic surfactant (such as sodium laureth sulfate). The mixture is stirred with heating to a temperature of 80-85 degrees C. Then the pH is adjusted to pH 7-8. After this adjustment the alkylamidopropylbetaine and the nonionic surfactant are added while maintaining the temperature is at 80-85 degrees C. When addition of the surfactant is completed the behenyl alcohol is added in molten liquid (such as Lanette-22 (72-80%) or slowly in solid state so that the temperature is maintained at 80-85 degrees C. The contents of the mixing vessel are stirred for at least 45-60 minutes at 80 to 85 degrees C. Next the vessel is cooled down at a cooling rate of 0.05-0.4 degrees C./minute, preferably 0.1 5-0.3 and, most preferably, at a rate of 0.2-0.25 degrees C./min. After the mixture is cooled to about 20-25 degrees C. the specifications are checked. The mixture is then stirred for another 1-2 hours at 20-25 degrees C. Viscosity may be measured, if desired, using the equipment and conditions described above.

Examples 1-15

[0030] The General Method described in Example A may be used to make 5 kg size batches using the types and amounts of ingredients listed in Tables B-D. Examples 1-6 are comparative examples to show formulations outside of the invention.

TABLE B
Single Surfactant Systems
Ingredient	Ex. 1	Ex. 2	Ex. 3	Ex. 4	Ex. 5	Ex. 6
Water	QS	QS	QS	QS	QS	QS
Sodium Lauryl 2EO	1.0	8.0	0	0	0	0
Sulfate
Cocamidopropyl	0	0	2.0	4.0	0	0
betaine
Cetrimonium chloride	0	0	0	0	0.80	5.0
Behenyl alcohol	10.0	40.0	10.0	30.0	10.0	40.0
Total	100	100	100	100	100	100

[0031] Viscosity measurements were:Example 1: non-homogeneous, lumpy, 100 mpasExample 2: sticky paste, lumpy,>100000 mpasExample 3: non-homogeneous, lumpy, 100 mpasExample 4: non-homogeneous, lumpy, 200 mpasExample 5: non-homogeneous, lumpy, 1000 mpasExample 6: paste, lumpy thick, white cream>100000 mpas

TABLE C
Multiple Surfactant Systems With Isosteareth-2
Ingredient	Ex 7	Ex 8	Ex 9	Ex 13	Ex 14
Water	QS	QS	QS	QS	QS
Sodium Pareth 2EO Sulfate	0	0	0	0	4.0
Sodium Lauryl 2EO Sulfate	2.0	4.0	1.0	2.5	0
Cocamidopropyl betaine	1.0	2.0	1.0	1.0	0
Cetrimonium chloride	0	0	0.5	0.2	0
Isosteareth-2	2.0	1.0	0.5	0.5	2.0
Behenyl alcohol	25.0	25.0	25.0	25.0	25.0
Laureth 1-10	0	0	0	1.0	0
Total	100	100	100	100	100
Stability	stable	stable	unstable	borderline	unstable

[0032]

TABLE D
Multiple Surfactant Systems Without Isosteareth-2
Ingredient	Ex 10	Ex 11	Ex 12	Ex 15
Water	QS	QS	QS	QS
Sodium Lauryl 2EO Sulfate	4.0	0.5	0.5	3.0
Cocamidopropyl betaine	1.0	0.5	0.25	3.0
Behenyl alcohol	25.0	15.0	25.0	25.0
Laureth 1-10	2.0	1.0	4.0	0
Total	100	100	100	100
Stability	stable	unstable	unstable	stable

Claims

1. A low viscosity, stable dispersion of behenyl alcohol comprising: about 10-40 weight % on an actives basis of behenyl alcohol; about 1.00-8.0 weight % of an anionic surfactant selected from the group consisting of sodium lauryl ether sulfate, sodium lauryl sulfate, magnesium lauryl ether sulfate, magnesium lauryl sulfate, calcium lauryl ether sulfate, calcium lauryl sulfate, ammonium lauryl ether sulfate, and ammonium lauryl sulfate; about 1.0-3.0 weight % (on an actives basis) of a betaine selected from the group consisting of C12-18 amidopropylbetaines; optionally about 0.3-5.0 weight % of a C12-C20 straight chain or iso-branched alcohol having 2-20 moles of ethoxylation; optionally a cationic material having less than or equal to 22 carbons; wherein the dispersion: has a stability of at least 3 months at a temperature of 49 degrees C.; has a viscosity in the range of 1,000-20,000 centipoise; and is limited to less than 0.2 weight % of total cationic material.

2. A low viscosity, stable dispersion of behenyl alcohol according to claim 1 comprising about 20 to 25% of behenyl alcohol; and about 1 to 5% of the anionic surfactant.

3. A low viscosity, stable dispersion of behenyl alcohol according to claim 1 having a viscosity in the range of 1,000-15,000 cps.

4. A low viscosity, stable dispersion of behenyl alcohol according to claim 1 having a viscosity in the range of 1,000-8,000 cps.

5. A low viscosity, stable dispersion of behenyl alcohol according to claim 1 wherein the betaine is cocoamidopropyl betaine.

6. A low viscosity, stable dispersion of behenyl alcohol according to claim 1 wherein the anionic surfactant is calcium lauryl sulfate.

7. A low viscosity, stable dispersion of behenyl alcohol according to claim 1 wherein the C12-C20 straight chain or iso-branched alcohol having 2-20 moles of ethoxylation is selected from the group consisting of Isosteareth-2, lsosteareth-4, Isosteareth-10, and Laureth 2-20.

8. A process for making a stable dispersion of behenyl alcohol wherein the dispersion has a stability of at least 3 months at a temperature of 49 degrees C.; a viscosity in the range of 1,000-20,000; and no more than 0.2 weight % of a cationic material, wherein the method comprises: combining a set of ingredients comprising: 10-40 weight % on an actives basis of behenyl alcohol; 1.0-8.0 weight % of an anionic surfactant selected from the group consisting of sodium lauryl ether sulfate, sodium lauryl sulfate, magnesium lauryl ether sulfate, magnesium lauryl sulfate, calcium lauryl ether sulfate, calcium lauryl sulfate, ammonium lauryl ether sulfate, and ammonium lauryl sulfate; 1.0-3.0 weight % (on an actives basis) of a betaine selected from the group consisting of C12-18 amidopropylbetaines; and optionally 0.3-5.0 weight % of a C12-C20 straight chain or iso-branched alcohol having 2-20 moles of ethoxylation; melting and mixing the set of ingredients using a temperature in the range of 80-85 degrees C. to create a combined material; stirring and homogenizing the combined material at a temperature in the range of 80-85 degrees C. for at least an hour; cooling the combined material down to a temperature in the range of 20-25 degrees C. at a cooling rate in the range of 0.05-0.4 degrees C./minute; and holding the combined material at the temperature of 20-25 degrees C. for at least 2 hours.