Claims
- 1. A ternary alloy comprised of copper, aluminum and zinc having a .beta.-brass type structure falling within the area on a ternary diagram defined by the points:
- ______________________________________A. 78.3% Cu 9.7% Al 12% ZnB. 75.1% Cu 7.5% Al 17.4% ZnC. 67% Cu 4.2% Al 28.8% ZnD. 72.6% Cu 7.9% Al 19.5% Zn______________________________________
- said alloy being in its martensitic state and an M.sub.s temperature of 0.degree. C. or lower and having been deformed from an original configuration to render it heat recoverable, said alloy exhibiting stress stability of at least 1,000 hrs at 125.degree..degree. C. when caused to recover by being warmed to a temperature at which the alloy exists in its austenitic state so that a degree of unresolved recovery remains.
- 2. An alloy in accordance with claim 1 wherein said alloy has an eutectoidal composition, said eutectoidal composition being a composition wherein no metal of the group consisting of copper, aluminum and zinc is present in said alloy in an amount that differs by more than 1% by weight from the amount of said metal present in a composition corresponding to a eutectoidal composition defined by the line XY of the ternary diagram of FIG. 1.
- 3. An alloy in accordance with claim 2 wherein said alloy has an eutectoid composition.
- 4. A process for making a heat recoverable article that exhibits stress stability of at least 1,000 hours at 125.degree. C. when allowed to recover so that a degree of unresolved recovery remains comprising the steps:
- (a) selecting a ternary alloy capable of being rendered heat recoverable comprised of copper, aluminum and zinc having a .beta.-brass type structure and having an M.sub.s temperature of 0.degree. C. or lower falling within the area on a ternary diagram defined by the points:
- ______________________________________A. 78.3% Cu 9.7% Al 12% ZnB. 75.1% Cu 7.5% Al 17.4% ZnC. 67% Cu 4.2% Al 28.8% ZnD. 72.6% Cu 7.9% Al 19.5% Zn______________________________________
- (b) fabricating said article from the selected alloy into an original, heat-stable configuration,
- (c) cooling said article to a temperature at which the alloy exists in its martensitic state, and
- (d) deforming said article to a second, heat-unstable configuration from which recovery occurs when said article is warmed to a temperature at which the alloy reverts to austenite from said martensitic state.
- 5. A process according to claim 4 wherein said alloy has an eutectoidal composition, said eutectoidal composition being a composition wherein no metal of the group consisting of copper, aluminum and zinc is present in an amount that differs by more than 1% by weight from the amount of said metal in a composition corresponding to an eutectoid composition defined by the line XY of FIG. 1.
- 6. A process according to claim 5 wherein said alloy has an eutectoid composition.
Parent Case Info
This is a continuation of application Ser. No. 668,041, filed Mar. 18, 1976, abandoned.
US Referenced Citations (3)
Non-Patent Literature Citations (2)
Entry |
Journal of the Institute of Metals, vol. 93, 1970, pp. 188-192. |
Zeitschrift fur Metallkunde, 24, Heft. 1, Jan. 1932, pp. 1-6, Bauer & Hansen. |
Continuations (1)
|
Number |
Date |
Country |
Parent |
668041 |
Mar 1976 |
|