Patent Grant
7834073
This application is the National Stage of PCT/EP05/052168, filed May 12, 2005. The parent application claims priority to German Application No. 10 2004-025 767.1 filed May 26, 2004. The disclosures of both applications are incorporated herein by reference in their entireties.
The present invention relates to stable, low-chloride solutions of hydrosalts of organic acids with cationic N-substituted aminopolysiloxanes, present substantially in the form of T structural units, in a lower alcohol, to the preparation of these solutions, and to their use as adhesion promoters and for coating various substrate materials.
Solutions of organosilane polycondensates and their preparation and use are described in a host of publications.
The promotion of adhesion by functionalized aminopropyltrimethoxysilanes in the coating of metals, copper and iron for example, with polyolefins or epoxy resins is reported in U.S. Pat. No. 4,902,556, EP-A-0 353 766 and U.S. Pat. No. 4,849,294. Adhesion is promoted on glass surfaces in accordance with EP-A-0 338 128, WO 88/00527, U.S. Pat. No. 4,499,152, U.S. Pat. No. 4,382,991, U.S. Pat. No. 4,330,444, DE-A-28 02 242 and EP-A-0 845 040. Adhesion promoters for oxidic fillers in various organic polymers are described in JP-A-01/259369 and EP-A-0 176 062.
Aqueous formulations of such substances with low concentrations of active substance, below 1%, are described in JP-A-62/243624, U.S. Pat. No. 4,499,152, U.S. Pat. No. 4,382,991, U.S. Pat. No. 4,330,444 and DE-A-28 02 242.
DE-A-26 48 240 describes water-soluble silylalkylamine chlorides which are suitable for use as coupling agents between inorganic substrates.
U.S. Pat. No. 5,591,818 and EP-A-0 590 270 disclose organosilanes and their poly-condensation products, which are prepared by hydrolyzing a functional aminosilane hydrosalt or by hydrolytically polymerizing an aminosilane with subsequent functionalization by reaction with a functional alkyl halide. The compounds can be formulated as stable aqueous emulsions and used as adhesion promoters between organic and inorganic materials.
U.S. Pat. No. 5,073,195 discloses compositions for treating porous surfaces to make them water repellent, these compositions being aqueous solutions of a silane coupling agent and an alkyltrialkoxysilane having C1-C6 alkyl groups on the silicon atom. The solutions are used for treating substrate materials such as wood, concrete, lime sandstone or other unreactive surfaces of building materials.
EP-A-0 538 551 is directed to emulsions which contain organosilicon compounds and are intended for impregnating inorganic materials, especially building materials. The emulsions comprise water, at least one alkoxysilane with or without oligomers thereof, one or more anionic surfactants, and also silicon-functional surfactants and customary auxiliaries. The surfactant group is introduced into alkylalkoxysilanes in the form of the hydrochloride salt by reaction with the surfactant radical, in the form of the Na alkoxide, in an organic solvent. Stable emulsions are obtained by using high-pressure homogenizers with two passes at pressures of from 8 to 50 MPa and from 10 to 70 MPa, the pressure reduction in the second pressure stage amounting to 20%. Droplet sizes <1 μm are obtained.
At the 39th annual conference of the Institut für verstarkte Kunststoffe/Verbundwerkstoffe [Institute for Reinforced Plastics/Composites] of the Gesellschaft der Kunststoffindustrie [German Plastics Industry Association] from Jan. 16 through 19, 1984, E. P. Plueddemann reported on silanols and siloxanes as coupling agents and primers.
In U.S. Pat. No. 3,734,763 Plueddemann describes cationic unsaturated amino-functional silane coupling agents. (CH3O)3Si(CH2)3NHCH2CH2NH2 and (CH3O)3Si(CH2)3NHCH2CH2NHCH2C6H4—CH═CH2 were subjected to controlled hydrolysis. The hydrolysate may undergo partial condensation. The patent describes the reaction of numerous organofunctional amines and aminosilanes with organofunctional alkyl halides in organic solvents. The products can be used as adhesion promoters between organic and inorganic surfaces and also as primers.
This object is achieved by means of a stable solution comprising:
at least one lower alcohol;
at least one stabilizer; and
at least one hydrosalt of an organic acid with a N-substituted aminopolysiloxane comprising a T structural unit of the formula:
wherein
the R′ groups are independently of each other, represented by formulae (Ia), (Ib), (Ic) or (Id):
wherein a is 0, 1 or 2, and b is 0 or 1;
wherein a is 0,1, 2, or 3, and b is 0 or 1;
wherein a is 0, 1, or 2, and b is 0 or 1;
wherein a is 0, 1, 2, or 3, and b is 0, 1, or 2; and
wherein
the R groups independently of each other are benzyl or vinylbenzyl,
A is an anion of the organic carboxylic acid, and
a ratio of R′ having formulae (Ib), (Ic) and (Id) to total R′ is at least 0.125,
a % by weight of chloride based on the total weight of the solution is less than 1%.
The at least one stabilizer is selected from the group consisting of 3,5-di-tert-butylcatechol, 2,5-di-tert-butylhydroquinone, 4-tert-butylpyrocatechol, 2,4-di-tert-butylphenol, hydroquinone monomethyl ether, 2,6-di-tert-butyl-p-cresol and a mixture thereof.
The object is also achieved by a process to prepare the above described stable solution by (i) reacting a hydrochloride salt of a N-substituted aminopolysiloxane to be obtained as a hydrosalt of an organic acid with NaOH, in solution in a lower alcohol, to obtain the N-substituted aminopolysiloxane as a free amine; separating off precipitated NaCl; and
reacting the obtained free amine with the organic acid A;
or
(ii) reacting a hydrochloride salt of a N-substituted aminopolysiloxane to be obtained as a hydrosalt of an organic acid, in solution in the lower alcohol, with a sodium salt of the organic acid A; and
separating off precipitated NaCl;
or
(iii) reacting a hydrochloride salt of a N-substituted aminopolysiloxane to be obtained as a hydrosalt of an organic acid, in solution in the lower alcohol, with a sodium alkoxide of the lower alcohol, to obtain the N-substituted aminopolysiloxane as a free amine;
separating off precipitated NaCl; and reacting the resultant free amine with the organic acid A;
and recovering a solution of the hydrosalt of the organic acid A of the N-substituted aminopolysiloxane in the lower alcohol.
The solutions contain <1.0% by weight, preferably <0.5% by weight, of chloride, based on the total weight of the solution.
The amount of cationic N-substituted aminopolysiloxanes in the solutions can be from 0.1 to 80% by weight, preferably from 30% to 60%, more preferably 40% to 50% by weight, based on the total weight of the solution.
A solution according to the invention may further have an alcohol content of from 14% to 99.9% by weight, preferably from 19% to 99.8% by weight, based on the total weight of the solution.
The components or constituents of a solution here in each case total 100% by weight.
The concentration can be adjusted by removing or adding lower alcohol.
The structure of the compounds of the invention is complex, since they comprise mixtures of siloxanes with T structure and also, where appropriate, with different N substitution.
The degree of oligomerization [x, cf. formula (I)] of the cationic N-substituted amino-polysiloxanes is generally ≧2, in particular between 3 and 20. Three-dimensional structures, such as pyramids or cubes, with degrees of oligomerization of 6, 8, 10 and 12 are particularly preferred; however, corresponding transition forms may also occur and be found.
The products generally contain more than 90% of such T structural units. This is apparent from 29Si NMR spectroscopic analyses.
The distribution of the substituents on the aminic nitrogen atoms can be determined by means of GC/MS analyses.
Surprisingly it has additionally been found that the benzyl group tends toward three-fold substitution but that disubstituted products, with substitution on the primary and secondary amino group, also occur. In the case of substitution with the vinylbenzyl group no threefold substitution was found.
Through the choice of the substituents R and the selected reaction partners and reaction conditions (temperature, reaction time, and pH) during the preparation of the cationic aminopolysiloxanes it is possible to control the distribution of the substituents on the available nitrogen atoms and to ensure that substitution takes place not only terminally on the primary amino groups but also on the secondary amino groups.
The preparation of hydrochloride salts of functionalized aminopolysiloxanes by hydrolytic polymerization of an appropriately functionalized aminosilane hydrohalide by hydrolytic polymerization or by hydrolytic polymerization of an aminosilane and subsequent functionalization by reaction of a functional alkyl halide to form oligomeric and polymeric siloxanes is described in EP-A-0 590 270.
In order to ensure substitution on secondary nitrogen atoms, controlled oligomerization is carried out of the organosilane monomer with water, the reaction taking place at elevated temperature, by means of active heating, over a time of at least 2 hours. Suitable stabilizers are used specifically in defined concentrations. This is followed by reaction with sodium methoxide and subsequent neutralization with acid.
The organic acid (A) for forming the hydrosalts is selected from, for example, formic acid, acetic acid, propionic acid, citric acid, oxalic acid, lactic acid and mixtures thereof. Acetic acid is particularly preferred.
A solution according to the invention preferably has a pH of less than 10, more preferably a pH of from 6 to 9.
The lower alcohol used even when preparing the hydrochloride salts is preferably also used as solvent for preparing the hydrosalts of organic carboxylic acids according to the invention.
The lower alcohol is selected from methanol, ethanol, isopropanol, n-propanol, isobutanol, n-butanol and t-butanol and mixtures thereof.
In addition to the stabilization of the cationic N-substituted aminopolysiloxanes by formation of a hydrosalt with an organic carboxylic acid it is possible with advantage to use further stabilizers in amounts of from 0.01% to 6%, preferably from 0.05% to 4%, more preferably from 0.1% to 1% by weight, based on the total weight of the solution.
Examples of suitable stabilizers include 3,5-di-tert-butylcatechol, 2,5-di-tert-butyl-hydroquinone, 4-tert-butylpyrocatechol, 2,4-di-tert-butylphenol, hydroquinone mono-methyl ether, and 2,6-di-tert-butyl-p-cresol.
The stabilized solutions according to the invention are suitable with advantage for coating different substrate materials, where appropriate following dilution with water.
Thus, for example, from 0.1 to 100 parts by weight, preferably from 2 to 20 parts by weight, of a solution according to the invention, with an active substance content of about 40% by weight in particular, can be mixed with 300 parts by weights of water, the mixture giving rise, advantageously within less than 2 minutes, to a clear preparation which is ready for application.
Substrate materials used may be glass, glass fibers, metals and their oxides, such as aluminum, copper and steel, galvanized surfaces, titanium, zirconium, mixed oxides of titanium and zirconium, silicon, inorganic fillers, such as Al(OH)3, Mg(OH)2, mica, Al2O3, and synthetic polymers, especially polar and functional polymers, such as polyamide and polyesters, and polar polymers, such as polyolefins, which where appropriate may have been functionalized by physical pretreatment, and natural substances which have corresponding functional groups, such as paper, cotton, silk and leather.
The solutions of cationic N-substituted aminopolysiloxanes according to the invention can be used as adhesion promoters between organic and inorganic surfaces. They can also be used in connection with the reinforcement of organic polymers with inorganic fillers, glass fibers or metallic particles or in connection with the reinforcement of organic polymers with inorganic oxidic fillers. They also find use in the coating of inorganic surfaces with organic polymers or in the coating of metal, metal oxides or glass with organic polymers.
Entirely surprisingly it has been found that the T structures break up on application to substrate materials and produce a substantially more homogeneous, and thicker, coat than coats applied from monomeric functionalized silanes.
When using monomeric silanes it is possible to obtain coats of only from 10 to 50 nm, preferably about 20 nm. With the oligomeric aminopolysiloxanes according to the invention, however, coat thicknesses of up to 800 nm, in particular from 20 to 200 nm, are possible.
The coat thicknesses can be determined from the time taken for the coat to wear away under cathode ray atomization.
Without being tied to any one theory it is assumed that a coat is formed from a network in which the organic radicals R have undergone upward orientation and accumulation at the surface of the coat.
This concentration gradient can be determined by means of Auger spectroscopy, measuring the elements Si, O and C.
The invention is illustrated with reference to the following examples, without restriction of its subject-matter.
The examples are carried out using 4-necked flasks with a capacity of 1 liter or 2 liters, respectively, fitted in each case with an intensive condenser, stirrer, dropping funnel, thermometer, temperature-regulated oil bath, nitrogen atmosphere, ice-bath cooling and pressure filters or suction filters.
145 g of N′-aminoethyl-N-aminopropyltrimethoxysilane and 84.7 g of methanol are mixed. Subsequently 17.5 g of water are added. The reaction mixture is thereafter stirred for 1 hour. The oil bath is set to a temperature of 50° C. When this temperature has been reached 99.5 g of vinylbenzyl chloride are metered in over the course of one hour. The liquid phase reaches a temperature of 64° C. The subsequent reaction time amounts to 2 hours. Subsequently 120.3 g of a 30% strength by weight solution of sodium methoxide in methanol are added rapidly dropwise. The reaction mixture is cooled by means of an ice bath during this dropwise addition. The resultant sodium chloride salt is filtered off on a pressure suction filter. The NaCl is washed with 52 g of methanol. The methanol used for rinsing is combined with the filtrate and stabilized and neutralized with 0.5 g of 4-(tert-butyl)pyrocatechol in solution in 39 g of acetic acid. This gives 500 g of product solution in methanol (100% of theory). 58.5 g of NaCl are isolated. The practical yield of target product amounts to 440 g (88%). Losses arise as a result of contamination of the separated salt.
312 g of N′-aminoethyl-N-aminopropyltrimethoxysilane and 158 g of methanol are mixed. Subsequently 158 g of water are added. The reaction mixture is thereafter stirred for 1 hour. The oil bath is set to a temperature of 50° C. When this temperature has been reached 177 g of vinylbenzyl chloride are metered in over the course of one hour. The liquid phase reaches a temperature of 64° C. The subsequent reaction time amounts to 2 hours. Subsequently 252 g of a 30% strength by weight solution of sodium methoxide in methanol are added rapidly dropwise. The reaction mixture is cooled by means of an ice bath during this dropwise addition. The resultant sodium chloride salt is filtered off on a pressure suction filter. The NaCl is washed with 104 g of methanol. The methanol used for rinsing is combined with the filtrate and stabilized and neutralized with 0.25 g of 2,6-di-tert-butyl-p-cresol in solution in 88 g of acetic acid. This gives 1000 g of product solution in methanol (100% of theory). 129 g of NaCl are isolated. The practical yield of target product amounts to 940 g (94%). Losses arise as a result of contamination of the separated salt.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2004 025 767 | May 2004 | DE | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2005/052168 | 5/12/2005 | WO | 00 | 11/20/2006 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2005/118599 | 12/15/2005 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4226793 | Kotzsch et al. | Oct 1980 | A |
| 5591818 | Standke et al. | Jan 1997 | A |
| 5629400 | Standke et al. | May 1997 | A |
| 5679147 | Standke et al. | Oct 1997 | A |
| 5808125 | Standke et al. | Sep 1998 | A |
| 5817854 | Horn et al. | Oct 1998 | A |
| 5849942 | Standke et al. | Dec 1998 | A |
| 5863509 | Standke et al. | Jan 1999 | A |
| 5885341 | Standke et al. | Mar 1999 | A |
| 5932757 | Standke et al. | Aug 1999 | A |
| 6054601 | Standke et al. | Apr 2000 | A |
| 6118015 | Haas et al. | Sep 2000 | A |
| 6133466 | Edelmann et al. | Oct 2000 | A |
| 6139622 | Gobel et al. | Oct 2000 | A |
| 6176918 | Glausch et al. | Jan 2001 | B1 |
| 6177582 | Jenkner et al. | Jan 2001 | B1 |
| 6228936 | Standke et al. | May 2001 | B1 |
| 6239194 | Standke et al. | May 2001 | B1 |
| 6251989 | Edelmann et al. | Jun 2001 | B1 |
| 6255513 | Standke et al. | Jul 2001 | B1 |
| 6255516 | Jenkner et al. | Jul 2001 | B1 |
| 6288256 | Standke et al. | Sep 2001 | B1 |
| 6361871 | Jenkner et al. | Mar 2002 | B1 |
| 6395858 | Mack et al. | May 2002 | B1 |
| 6403228 | Mack et al. | Jun 2002 | B1 |
| 6426150 | Jenkner et al. | Jul 2002 | B1 |
| 6491838 | Standke et al. | Dec 2002 | B1 |
| 6500883 | Mack et al. | Dec 2002 | B1 |
| 6534667 | Standke et al. | Mar 2003 | B1 |
| 6641870 | Bartkowiak et al. | Nov 2003 | B2 |
| 6685766 | Standke et al. | Feb 2004 | B2 |
| 6713186 | Jenkner et al. | Mar 2004 | B1 |
| 6767982 | Standke et al. | Jul 2004 | B2 |
| 6770327 | Edelmann et al. | Aug 2004 | B2 |
| 6841197 | Standke et al. | Jan 2005 | B2 |
| 7611753 | Bartkowiak et al. | Nov 2009 | B2 |
| 20020127415 | Standke et al. | Sep 2002 | A1 |
| 20020192385 | Jenkner et al. | Dec 2002 | A1 |
| 20040138355 | Saito et al. | Jul 2004 | A1 |
| 20060185555 | Giessler et al. | Aug 2006 | A1 |
| 20080058489 | Edelmann et al. | Mar 2008 | A1 |
| 20080210130 | Giessler-Blank et al. | Sep 2008 | A1 |
| 20090011246 | Giessler-Blank et al. | Jan 2009 | A1 |
| 20090022898 | Standke et al. | Jan 2009 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20080003448 A1 | Jan 2008 | US |