Patent Application
20150270791
The present invention is directed in general to manufacturing processes and test methods for stacked actuators. More particularly, the present invention is directed to actuators having stacked layers of electroactive polymers. The present invention is also directed to actuators having stacked layers of electroactive polymers interspersed with layers of passive elastomers.
A tremendous variety of devices used today rely on actuators of one sort or another to convert electrical energy to mechanical energy. Conversely, many power generation applications operate by converting mechanical action into electrical energy. Employed to harvest mechanical energy in this fashion, the same type of device may be referred to as a generator. Likewise, when the structure is employed to convert physical stimulus such as vibration or pressure into an electrical signal for measurement purposes, it may be characterized as a sensor. Yet, the term “transducer” may be used to generically refer to any of the devices.
A number of design considerations favor the selection and use of advanced dielectric elastomer materials, also referred to as “electroactive polymers,” for the fabrication of transducers. These considerations include force, power density, power conversion/consumption, size, weight, cost, response time, duty cycle, service requirements, environmental impact, etc. As such, in many applications, electroactive polymer technology offers an ideal replacement for piezoelectric, shape-memory alloy and electromagnetic devices such as motors and solenoids.
An electroactive polymer transducer comprises two electrodes having deformable characteristics and separated by a thin elastomeric dielectric material. When a voltage difference is applied to the electrodes, the oppositely charged electrodes attract each other thereby compressing the polymer dielectric layer therebetween. As the electrodes are pulled closer together, the dielectric polymer film becomes thinner (the Z-axis component contracts) as it expands in the planar directions (along the X- and Y-axes), i.e., the displacement of the film is in-plane. The electroactive polymer film may also be configured to produce movement in a direction orthogonal to the film structure (along the Z-axis), i.e., the displacement of the film is out-of-plane. For example, U.S. Pat. No. 7,567,681 discloses electroactive polymer film constructs which provide such out-of-plane displacement—also referred to as surface deformation or as thickness mode deflection.
The material and physical properties of the electroactive polymer film may be varied and controlled to customize the deformation undergone by the transducer. More specifically, factors such as the relative elasticity between the polymer film and the electrode material, the relative thickness between the polymer film and electrode material and/or the varying thickness of the polymer film and/or electrode material, the physical pattern of the polymer film and/or electrode material (to provide localized active and inactive areas), the tension or pre-strain placed on the electroactive polymer film as a whole, and the amount of voltage applied to or capacitance induced upon the film may be controlled and varied to customize the features of the film when in an active mode.
Numerous applications exist that benefit from the advantages provided by such electroactive polymer films whether using the film alone or using it in an electroactive polymer actuator. One of the many applications involves the use of electroactive polymer transducers as actuators to produce haptic, tactile, vibrational feedback (the communication of information to a user through forces applied to the user's body), and the like, in user interface devices. There are many known user interface devices which employ such feedback, typically in response to a force initiated by the user. Examples of user interface devices that may employ such feedback include keyboards, keypads, game controller, remote control, touch screens, computer mice, trackballs, stylus sticks, joysticks, etc. The user interface surface can comprise any surface that a user manipulates, engages, and/or observes regarding feedback or information from the device. Examples of such interface surfaces include, but are not limited to, a key (e.g., keys on a keyboard), a game pad or buttons, a display screen, etc.
The feedback provided by these types of interface devices is in the form of physical sensations, such as vibrations, pulses, spring forces, etc., which a user senses either directly (e.g., via touching of the screen), indirectly (e.g., via a vibrational effect such a when a cell phone vibrates in a purse or bag) or otherwise sensed (e.g., via an action of a moving body that creates a pressure disturbance sensed by the user). The proliferation of consumer electronic media devices such as smart phones, personal media players, portable computing devices, portable gaming systems, electronic readers, etc., can create a situation where a sub-segment of customers would benefit or desire an improved haptic effect in the electronic media device. However, increasing feedback capabilities in every model of an electronic media device may not be justified due to increased cost or increased profile of the device. Moreover, customers of certain electronic media devices may desire to only temporarily improve the haptic capabilities of the electronic media device for certain activities.
Use of electroactive polymer materials in consumer electronic media devices as well as the numerous other commercial and consumer applications highlights the need to increase production volume while maintaining precision and consistency of the films.
Conventional fabrication techniques for producing stacked electroactive polymer actuators include batch processes where multiple dielectric layers are laminated or cast in place. However, these techniques are inefficient and difficult to scale to large volume manufacturing. The present disclosure provides semi-continuous manufacturing techniques for producing stacked actuators that are efficient and scalable to high volume manufacturing as compared to conventional batch processes.
Modern manufacturing methods require the flexibility to support multiple design alternatives and materials to support a broad product line. Any such process must be scalable, stable and repeatable and consider both front end and back end assembly processes. For example, it is desirable to assess the quality of individual devices through a test such as voltage withstand yield at the front end of the current stacking process. In addition, final assembly of a stacked actuator into an actuator assembly requires a reliable method of making an electrical connection. Conventional techniques are time consuming and not very scalable. There is also a need for a process of more efficiently creating vias components that is scalable for volume production as part of the back end assembly process.
For high volume manufacturing, care must be taken to minimize process variation and the introduction of defects. Some conventional methods for producing stacked actuators require the application of an adhesive, usually by spraying. Such techniques increase the dielectric thickness of the actuator, which increases operating voltage. Variation in adhesive thickness contributes to variation in yield and overall performance. Dielectric film lamination for stacked actuators on a batch basis is very time consuming and contributes significant opportunities for the occurrence of defects in the form of bubbles and wrinkles. Conventional stacked actuator process may include casting and laminating one or more thick polymer slabs onto the electroactive polymer stack. The process, however, is slow, manual, and prone to defects as it is difficult to manipulate the soft and fragile slabs.
Conventional batch processes are not easily scalable into a high volume manufacturing process. The present disclosure provides efficient and scalable techniques for producing stackable actuators. Some techniques, such as printing dielectric material, may help reduce the thickness of the dielectric layers, lower operating voltages, and eliminate the need for adhesive spraying and dielectric film lamination, and are efficient and scalable for volume manufacturing. These new methods also facilitate the cost-effective manufacturing of new device architectures with enhanced performance.
In one embodiment, a roll-to-sheet method for fabricating a multilayer stack for the production of one or more stacked actuators is provided. The inventive method comprises advancing a first electroactive polymer film to a fixed position; applying a first electrode material to the electroactive polymer film; optionally applying a first adhesive material to the electroactive polymer film; optionally cutting the electroactive polymer film to a sheet of predetermined length; advancing and laminating a second film electroactive polymer film over the first electrode and adhesive materials of the first electroactive polymer film; curing the laminated multilayer stack; applying a second electrode material to the laminated multilayer stack; optionally applying a second adhesive material to the laminated multilayer stack; optionally repeating the steps of applying the electroactive polymer film and the electrode materials; cutting the laminated multilayer stack to a sheet of a predetermined length; stacking the cut laminated sheets; and laminating the cut laminated sheets.
In another embodiment, the electroactive polymer film may be formed from a dielectric resin cast in-line before applying it to the multilayer stack. In yet another embodiment, the adhesive may be applied onto the electroactive polymer film before it is applied to the multilayer stack. In another embodiment, one or more passive polymer layers may be applied to the surfaces of the multilayer stack or interspersed between the active electroactive polymer layers.
In one embodiment, a loop method for fabricating a stacked actuator is provided. The method comprises providing an electroactive polymer multilayer stack in a semi-continuous cyclic process and during each cycle: applying a first dielectric material to the film; applying a first electrode material in at least a first pattern; applying a second dielectric material to the film; and applying a second electrode material in at least a second pattern.
In one embodiment, a loop cast method for fabricating a stacked actuator is provided. The method comprises providing an electroactive polymer multilayer stack in a semi-continuous cyclic process and during each cycle: applying a first dielectric resin to the film; at least partially curing the first dielectric resin; applying a first electrode material in at least a first pattern; applying a second dielectric resin to the film; at least partially curing the second dielectric resin; and applying a second electrode material in at least a second pattern.
In one embodiment, a continuous loop laminating method for fabricating a stacked actuator is provided. The method comprises providing a carrier liner in a continuous cyclic process and during each cycle: laminating a first electroactive polymer film onto the carrier liner, applying at least one electrode material to the first laminated film layer; optionally applying at least one adhesive material to the first laminated film layer; and curing the first laminated film layer.
Any of the methods above may further comprise repeating the steps of applying a dielectric material to the multilayer stack and applying the electrode materials to build up the number of layers desired. The electrodes with the first electrode pattern are aligned through all the layers; similarly the electrodes with the second electrode pattern are aligned through all the layers.
In one embodiment, the cyclic process may include multiple applications of dielectric resin before applying the electrode pattern to build up the thickness of the dielectric layer. In yet another embodiment, an adhesive may be applied onto the electroactive polymer film before it is applied to the multilayer stack. In other embodiments, one or more passive polymer layers may be applied to the surfaces of the multilayer stack or interspersed between the active electroactive polymer layers.
The application of the dielectric layers, electrode layers, adhesive layers, and passive polymers layers may be distributed at different locations around the loop. In one embodiment, the loop is supported by a web driven by at least two rollers. In another embodiment, the loop is supported by a rigid drum.
In one embodiment, a stacked actuator is provided. The stacked actuator comprises a plurality of active electroactive polymer layers arranged in a stack; a first passive polymer layer attached to a first surface of the stacked plurality of active electroactive polymer layers; and a second passive polymer layer attached to a second surface of the stacked plurality of active electroactive polymer layers, wherein the second surface is opposite the first end.
In another embodiment, a stacked actuator with enhanced stroke performance is provided. The stacked actuator comprises a plurality of active electroactive polymer layers arranged in a stack and a plurality of passive polymer layers interspersed between the active electroactive polymer layers.
In one embodiment, a method of producing an actuator assembly is provided, the method comprises providing electrical connections to all of the layers in the multilayer stacked transducer by piercing at least a first via through all of the first electrode patterns; piercing at least a second via through all of the second electrode patterns; and filling the vias with a conductive material. In some embodiments, it is advantageous to position the vias near the center of the footprint of the device.
In one embodiment, a method of producing an actuator assembly is provided, the method comprises providing at least two stacked actuators; piercing at least one via through each of the at least two stacked actuators; and filling the at least one via with a conductive material.
These and other features and advantages of the invention will become apparent to those persons skilled in the art upon reading the details of the invention as more fully described below. In addition, variations of the processes and devices described herein include combinations of the embodiments or of aspects of the embodiments where possible are within the scope of this disclosure even if those combinations are not explicitly shown or discussed.
The invention is best understood from the following detailed description when read in conjunction with the accompanying drawings. To facilitate understanding, the same reference numerals have been used (where practical) to designate similar elements are common to the drawings. Included in the drawings are the following:
Variation of the invention from that shown in the figures is contemplated.
Examples of electroactive polymer devices and their applications are described, for example, in U.S. Pat. Nos. 7,394,282; 7,378,783; 7,368,862; 7,362,032; 7,320,457; 7,259,503; 7,233,097; 7,224,106; 7,211,937; 7,199,501; 7,166,953; 7,064,472; 7,062,055; 7,052,594; 7,049,732; 7,034,432; 6,940,221; 6,911,764; 6,891,317; 6,882,086; 6,876,135; 6,812,624; 6,809,462; 6,806,621; 6,781,284; 6,768,246; 6,707,236; 6,664,718; 6,628,040; 6,586,859; 6,583,533; 6,545,384; 6,543,110; 6,376,971; 6,343,129; 7,952,261; 7,911,761; 7,492,076; 7,761,981; 7,521,847; 7,608,989; 7,626,319; 7,915,789; 7,750,532; 7,436,099; 7,199,501; 7,521,840; 7,595,580; 7,567,681; 7,595,580; 7,608,989; 7,626,319; 7,750,532; 7,761,981; 7,911,761; 7,915,789; 7,952,261; 8,183,739; 8,222,799; 8,248,750, and in U.S. Patent Application Publication Nos. 2007/0200457; 2007/0230222; 2011/0128239; and 2012/0126959, the entirety of each of which is incorporated herein by reference.
Described hereinbelow are various embodiments of manufacturing processes for manufacturing stacked actuators. In various embodiments, a stacked actuator may be manufactured using sheet stacking processes, a roll-to-sheet lamination process including a vacuum belt process, various loop cast processes, and a semi-continuous lamination process. These processes are described hereinbelow.
In one embodiment, a sheet stacking manufacturing process includes printing a dielectric material on a polymer film and laminating (stacking) multiple layers of printed polymer films. Although practical devices can be made with up to four layers of laminated polymer film, there is no limitation to the number of layers than can be stacked. The multiple layers can be stacked manually or automatically with automatic assembly machines from McClellan Automation Systems of NH, for example. Current batch frames and printing processes can be utilized in this technique and may be ideally suited for development purposes. In one embodiment, the polymer film may be pre-strained prior to the free standing dielectric screen printing process.
In another embodiment, another sheet stacking manufacturing process includes laminating a polymer film coming off of a stretcher to a platen or flat plate. Electrodes and adhesive can be screen printed on one side. It is acceptable to have the bottom layer inactive and electrically isolated. Another layer of polymer film can be laminated to the stack on the platen/plate prior to the next printing step. No pre-strain of the polymer film would be required for accurate printing. Layer-to-layer alignment may be simplified by printing dielectric material on clear polymer films. Accurate layer-to-layer printing on opaque film is also contemplated but may require mechanical alignment techniques and the polymer film will need to be mounted to a stable base. This technique may be better suited for large scale manufacturing than Process #1.
In one embodiment, the web may be about 1 m in width and move in a continuous manner at about 1 m/min. Other widths and speeds, however, are contemplated and are within the scope of the present disclosure. The process can also be carried out in a step-and-repeat manner. Deposition methods for electrode and adhesive at stations 106/120, 108/122 may be selected from a wide range of solutions including aerosol jet, ultrasonic spray, screen printing, rotary screen, flexographic, gravure, etc.
The Stacked actuator 700 comprises top and bottom passive layers 702, 704 with layers of electroactive polymer films 706 stacked to a desired thickness. In the illustrated embodiment, the stacked actuator 700 is comprised of stacks active layers of film 706 and pattered electrode up to a desired height. It has been demonstrated, however, that the use of an enhanced ground interface design improves the stroke of a stacked actuator. A passive layer at the ground and load interfaces enables all active electroactive polymer layers to fully deform under an electrical input. In one embodiment, the stacked actuator 700 may comprise 20 dielectric layers of dielectric with alternate A/B pattern electrodes and fabricated on a 0.030″ (0.762 mm) silicone slab. Un-patterned adhesive is used between layers, which may be fabricated in various lengths and widths.
It is relatively easy to add force to a stacked actuator 700, 800 by increasing the actuator area. Stroke, however, generally requires adding layers with a relatively small incremental improvement in stroke with each added layer or the use of a separate mechanical transmission device to convert force into stroke. Either approach adds cost and complexity to the system solution. An enhanced ground interface provides an improvement over basic stacked actuator design because it replaces active electroactive polymer layers with a passive layer at the points connected to solid surfaces. This is effective in small layer count devices with relatively thin passive layers, but it reaches limits of effectiveness as the layer count is increased.
Interspersing the passive elastomer layers 906 into a stack of active electroactive polymer layers 908 increases the displacement/stroke of the stroke transmission multiplier stacked actuator 900. The passive elastomer polymer layers 906 are interspersed between and bonded to the active electroactive polymer layers 908. An actuated active electroactive polymer film layer 908 expands in area (x-y) while thinning (z). A passive polymer layer 906 is deformed in the same manner by the motion of the active electroactive polymer layers 908 above and below. The result is greater stroke for a stacked actuator for the same number of active electroactive polymer layers 908. Thus, for the same number, area, shape, and thickness of active electroactive polymer layers 908 (e.g., capacitance) the stroke transmission multiplier stacked actuator 900 is able to produce more stroke under the same electric energy input. The use of inactive or passive polymer layers 906 to amplify the stroke, and may reduce the overall cost of a stacked actuator compared to an equivalent corresponding increase in active electroactive layer count where increased stoke is desired.
Furthermore, the process 1300 provides a method for creating robust electrical and mechanical connections from the stack actuator to a metallic conductor (e.g., a conductive pad on a printed circuit board [PCB]), by one or more of the following techniques: (1) dipping the ends of stacked actuator in a conductive elastomer and curing it; (2) inserting the actuator and a printed circuit board into the cavity of a die and injection molding conductive elastomer to form terminals that join them; and (3) providing a base with conductive anchoring elements that protrude in the vias and are captured by the conductive elastomer when it is cured, to provide a mechanical armature that resists pull-out of the terminal and adds conductive area to the metal/elastomer interface in order to reduce contact resistance.
Conductive silicone adheres to both the end of a stack actuator and to a printed circuit board or wire. Thus, a single material and process both fastens and electrically connects the actuator to copper-based conductors which can be soldered or terminated with conventional connectors. Molding the silicone around a mechanical/electrical anchor soldered to a copper wire or copper pad on a printed circuit board increases pull-out strength and lowers electrical resistance. Overmolding a compliant insulating layer of silicone provides further mechanical robustness and prevents unintended electrical connections.
The process 1300 increases productivity of fabricating stacked actuators over conventional techniques and can be scaled to high volume production. The process step of creating via connections allows for the possibility of in-process quality control, which may be desired for efficient process development. It also addresses some scaling issues and process enables automation.
Printing the dielectric enables thinner layers of dielectric which will help achieve desired operating voltage levels. It also replaces two difficult and time consuming process steps (adhesive deposition and film lamination) with one. The adhesive deposition involves a high degree of process variation and adds to dielectric thickness, resulting in poorer product consistency and higher operating voltages. The second process replaced is film lamination, which can be time consuming and laborious, and prone to defects such as bubbles, wrinkles, and dielectric film damage. Printing dielectric is not only much faster than the processes it replaces, it also doesn't have any of the negative consequences described above. Stencil printing is a much faster and more efficient way to produce thick passive layers in comparison to conventional methods.
The process 1300 may be employed to fabricate a actuator assembly by combining two stacked actuators having, for example, 20 dielectric layers each, as shown and described in connection with
Turning now to the process 1300, which starts at 1302, the substrate is prepared 1304 by applying a mixture of silicone gel 1324 and silicone elastomer 1326 onto a shim interposed between release liners. The substrate is heat pressed to flatten and cure, the shims and liners are removed and the substrate is cut to size. The substrate in inserted into an aluminum platen. A frame is employed such that multiple substrates can be processed simultaneously and then singulated into individual components later in the process 1300 (e.g., at step 1314). The substrate can alternatively be prepared by any other suitable technique including, without limitation, stencil printing and slot die coating. Singulation can be done with any suitable technique including, without limitation, knife or blade cutting, die cutting, laser cutting, ultrasonic cutting, and water jet cutting. Components can be separated one at a time or simultaneously in multiples with, for example, an array or roller of cutting dies.
Adhesive 1328 is applied to the substrate and cured 1306. The adhesive 1328 may preferably be a silicone with tensile modulus <1 MPa diluted with solvent to a viscosity suitable for spraying. The adhesive 1328 may be applied using any suitable technique where in one example technique the adhesive 1328 is sprayed onto the substrate with a spray gun. After application of the adhesive 1328, the substrate is pre-cured at 80° C. for about two minutes, for example.
Dielectric film 1330 and electrode 1334 materials are laminated and printed 1308 onto the substrate. The process steps 1306 and 1308 are repeated until a desired number of dielectric layers is formed. For the dielectric film 1330 lamination portion of the process step 1308, the dielectric film 1330 is prepared on a batch frame. The first liner is removed and the dielectric film 1330 is rolled onto the stack and then the second liner is removed. A single or several patterns of electrodes 1334 may be used. Electrode 1334 patterns may be alternated on each layer. In one embodiment, the electrodes are screen printed on each layer.
Once a desired number of multiple layers of the stacked actuator have been fabricated, vias are pierced into the stack and filled 1310 with an electrically conductive material such as an elastomer loaded with conductive particles of, for example, carbon black, or silver 1334. The actuator is then tested 1312 for voltage withstand, resistance, and capacitance. Because the process has been carried on a frame with multiple substrates, the stacked actuators may now be singulated 1314 into individual components ready for the actuator assembly 1316 process. For the actuator assembly process 1316, a printed circuit board 1336 with ring-shaped armatures 1330 soldered thereon is prepped and placed along with two stacked actuators into a mold. Conductive elastomer 1340 is injected and cured. The actuators are then placed into a potting mold and potting elastomer 1342, 1344 is injected and cured to provide an encapsulation layer. The actuator assembly is tested 1348 and data 1346 is collected and analyzed. At decision block 1320 it is determined if the actuator assembly passed or failed the test. If it passed the test, it is placed in inventory 1322. Otherwise it is rejected 1348.
Some of the individual steps in the actuator assembly process 1316 are now explained in additional detail. In the printed circuit board 1336 preparation step, for example, ring-shaped test-points (two per printed circuit board element) are soldered to the printed circuit boards 1336 that comprise the bases of the actuator assemblies. Any residual soldering flux is then removed.
Prior to inserting the prepped printed circuit board 1336 into the mold with the two stacked actuator components (actuators), any residual material is cleared from the mold ports and cavities. One the mold is loaded, it is closed, and vacuum is applied to remove any residual air from the assembly.
The conductive elastomer 1340 is then injected into the mold at, for example, 45 PSI (0.31 MPa), although other suitable pressures are contemplated to be within the scope of the present disclosure. The entire mold is then placed in an oven to cure the conductive elastomer 1340. Once the conductive elastomer 1340 has cured, the mold is removed from the oven and the molded actuators are ejected. Any flash or burrs left by the molding process are preferably trimmed away.
The potting die is prepared by cleaning the injection ports and cavities. The actuators are then loaded into the potting dies so that the printed circuit board bases 1336 rest on an inner shoulder. This defines a void on the actuator side of the printed circuit board into which potting compound is injected. The mold is then closed.
A two-part elastomer potting compound 1342, 1344 is mixed, degassed under vacuum, and injected into the cavity through injection ports. The injection ports are then closed and the filled mold is cured in an oven. After curing, the mold is opened, the actuators are ejected, and any molding flash trimmed away.
Next, an electrical shield may optionally be laminated over the actuators. The layer may be comprised of, for example, two insulating layers of thermoplastic urethane (TPU) sandwiching a conductive layer of metallized fabric. To facilitate assembly, a sheet of this composite shield may be vacuum-formed and trimmed to fit the actuators.
As used herein dielectric elastomer film may include, without limitation, silicone elastomers, acrylic elastomers, polyurethanes, thermoplastic elastomers, copolymers comprising polyvinylidene difluoride, pressure-sensitive adhesives, fluoroelastomers, polymers comprising silicone and acrylic moieties, and the like. The polymer matrix of the dielectric elastomer film may be a homopolymer or copolymer, cross-linked or uncross-linked, linear or branched, etc. As will be apparent to those skilled in the art, combinations of some of these materials may be used as the polymer matrix in methods of this invention. Copolymers and blends fall within the class of suitable polymers.
As used herein passive polymer materials include, without limitation, at least the following materials silicone elastomers, acrylic elastomers, polyurethanes, thermoplastic elastomers, copolymers comprising polyvinylidene difluoride, pressure-sensitive adhesives, fluoroelastomers, polymers comprising silicone and acrylic moieties, and the like.
As used herein electrode materials include, without limitation, carbon or metal filled formulations, metal which may be textured or patterned, conductive polymers, and combinations thereof.
As used herein adhesive materials include, without limitation, at least the following materials, polyurethanes, silicones, olefinic polymers and copolymers, polyesters, acrylates, methacrylates, styrenic polymers and copolymers, vinyl polymers, thermoplastic elastomers, polyamides, cyanoacrylates, and combinations of these materials.
As for other details of the present invention, materials and alternate related configurations may be employed as within the level of those with skill in the relevant art. The same may hold true with respect to process-based aspects of the invention in terms of additional acts as commonly or logically employed. In addition, though the invention has been described in reference to several examples, optionally incorporating various features, the invention is not to be limited to that which is described or indicated as contemplated with respect to each variation of the invention. Various changes may be made to the invention described and equivalents (whether recited herein or not included for the sake of some brevity) may be substituted without departing from the true spirit and scope of the invention. Any number of the individual parts or subassemblies shown may be integrated in their design. Such changes or others may be undertaken or guided by the principles of design for assembly.
Also, it is contemplated that any optional feature of the inventive variations described may be set forth and claimed independently, or in combination with any one or more of the features described herein. Reference to a singular item, includes the possibility that there are plural of the same items present. More specifically, as used herein and in the appended claims, the singular forms “a,” “an,” “said,” and “the” include plural referents unless the specifically stated otherwise. In other words, use of the articles allow for “at least one” of the subject item in the description above as well as the claims below. It is further noted that the claims may be drafted to exclude any optional element. As such, this statement is intended to serve as antecedent basis for use of such exclusive terminology as “solely,” “only” and the like in connection with the recitation of claim elements, or use of a “negative” limitation. Without the use of such exclusive terminology, the term “comprising” in the claims shall allow for the inclusion of any additional element—irrespective of whether a given number of elements are enumerated in the claim, or the addition of a feature could be regarded as transforming the nature of an element set forth in the claims. Stated otherwise, unless specifically defined herein, all technical and scientific terms used herein are to be given as broad a commonly understood meaning as possible while maintaining claim validity.
Various aspects of the subject matter described herein are set out in the following numbered clauses:
1. A method of fabricating a stacked electroactive transducer, the method comprising: providing a multilayer stack in a cyclic process and during each cycle, applying a first dielectric material layer to the multilayer stack; applying to the first dielectric material layer a first electrode material in at least a first pattern; applying a second dielectric material layer to the multilayer stack; and applying to the multilayer stack a second electrode material in at least a second pattern.
2. The method according to Claim 1, wherein applying the first dielectric material comprises applying to the film and at least partially curing a polymer resin.
3. The method according to Claim 1, wherein applying the first dielectric material comprises laminating a polymer film from a roll.
4. The method according to any one of Claims 1 to 3 further comprising applying an adhesive to the polymer film.
5. The method according to any one of Claims 1 to 4 further comprising applying at least one passive polymer layer as part of the stacked electroactive transducer.
6. The method according to any one of Claims 1 to 5, wherein the cyclic process comprises a continuous loop process.
7. The method according to Claim 6, wherein the continuous loop process includes a belt supported by at least two rollers to support the polymer film.
8. The method according to Claim 6, wherein the continuous loop process includes a rotating drum to support the polymer film.
9. The method according to any one of Claims 6 to 8, wherein film application and electrode application and optionally adhesive application and passive layer application occur at sites distributed around the continuous loop.
10. The method according to any one of Claims 1 to 5 further comprising: applying and advancing the first dielectric material a fixed length; applying the first electrode material to the first dielectric material; optionally, applying a first adhesive material to the first dielectric material; optionally, cutting the first dielectric material to a predetermined length; applying the second dielectric material over the first electrode and adhesive material of the first dielectric material to form a multilayer stack; optionally, curing the multilayer stack; applying the second electrode material to the multilayer stack; optionally, applying a second adhesive material to the multilayer stack; optionally, repeating the steps of applying dielectric material and applying electrode material; optionally, applying a passive polymer layer over the multilayer stack; cutting the multilayer stack to a sheet of a predetermined length; and optionally, stacking and laminating the cut multilayer stack sheets.
11. The method according to any one of Claims 1 to 10 further comprising: providing first vias to connect electrode layers with the first electrode pattern and second vias to connect the electrode layers with the second electrode pattern and filling the first and second vias with a conductive material; and optionally, singulating one or more individual devices from the multilayer stack.
12. A stacked transducer made according to the method of any one of Claims 1 to 11.
13. The stacked transducer according to Claim 12, wherein the first and second vias are positioned within the footprint of the transducer.
14. The stacked transducer according to Claim 13, wherein the first and second vias are positioned substantially at the center of the footprint of the transducer.
15. An actuator comprising a stacked transducer made according to the method of Claim 12 or 13.
16. A method of producing an actuator assembly, the method comprising: providing at least two stacked actuators; piercing at least one via through each of the at least two stacked actuators; and filling the at least one via with a conductive material.
This application claims the benefit, under 35 USC §119(e), of U.S. Provisional Application Nos. 61/722,954 filed Nov. 6, 2012 entitled “STACKED ACTUATOR MANUFACTURING CONCEPTS”; 61/823,534 filed May 15, 2013 entitled “STACKED ACTUATOR MANUFACTURING PROCESSES AND TEST METHODS”; and 61/810,328 filed Apr. 10, 2013 entitled “STACKED ACTUATOR MANUFACTURING PROCESSES AND TEST METHODS”; the entirety of each of which is incorporated herein by reference.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US13/68650 | 11/6/2013 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 61722954 | Nov 2012 | US | |
| 61810328 | Apr 2013 | US | |
| 61823534 | May 2013 | US |