The invention relates to a steel strip having a low silicon content, in particular a hot dip galvanised steel strip, more particularly a hot dip galvanised dual phase or complex phase steel strip.
Dual phase (DP) steel strip having balanced properties regarding strength and ductility (formability) is well known in the art. In cold rolled DP steel strip silicon is a very common alloying element for reason of cost reduction and/or control, solid solution strengthening, avoiding carbide precipitation, which is favourable in view of ductility (elongation). However, Si induces surface-related problems.
Si oxides formed during processing in the hot strip mill and annealing line increase the risk of the occurrence of so-called “tiger stripes”, which affect appearance and coatability. Therefore, commonly the use of silicon in DP steel is restricted, especially in hot dip galvanized (HDG) DP steel. Typically Si content in DP steel is 0.2-0.3 wt. % in HDG DP sheet and 0.2-0.5 wt. % in uncoated steel sheet.
From EP 2169091 A1 a high-strength hot-dip galvanized steel sheet with low yield strength is known. The steel composition comprises, in mass percent, 0.01-0.12% C, 0.2% or less Si, less than 2% Mn, 0.04% or less P, 0.02% or less S, 0.3% or less sol. Al, 0.01% or less N, 0.3-2% Cr, also satisfying the condition 2.1≦[Mneq]≦3 and 0.24≦[% Cr]/[% Mn], the balance being iron and inevitable impurities. The steel microstructure is composed of ferrite and a second phase, wherein the area ratio of the second phase is 2-25%, the area ratio of pearlite or bainite in the second phase is 0-20%, the average grain diameter of the second phase is 0.9-7 micrometer, and the area ratio of grains with a grain diameter of less than 0.8 micrometer in the second phase is less than 15%. The steel composition is exemplified by a number of examples based on a low Si and low Al alloying philosophy.
It is an object of the present invention to provide a steel composition, such as a dual phase (DP) or complex phase (CP) steel composition, which combines desired microstructure properties regarding strength and ductility with sufficient surface quality, in particular avoiding the occurrence of tiger stripes.
It is another object of the invention to provide such a steel composition having a good coatability.
According to the invention a steel strip having an ultimate tensile strength Rm in the 600 MPa steel category is provided which comprises, in mass percent, the following elements:
Surprisingly it has been found that the steel composition according to the invention does not show tiger stripes at an acceptable level of strength and formability properties comparable to traditional (HDG) DP steel strip at the 600 MPa level.
Regarding the metallurgical aspects the following guidelines are deemed to apply:
C is 0.08-0.11%, in view of spot weldability. If C is below 0.08%, then the carbon content is too low to create DP or CP microstructures.
Si is at most 0.1%. Si has shown to be the major factor responsible for tiger stripes. In order to avoid the risk of the occurrence of these surface defects in a secure way, the amount is limited to a maximum of 0.1%. Preferably the Si content is in the range of 0.02-0.08%.
Usually the addition of Al and Si has a similar beneficial effect on the formability of steels. However, in view of tiger stripes Al has a negligible effect.
Therefore Al is in the range of 0.01-1.5%, such as 0.01-1.10%. Preferably, the minimum amount of Al is more than 0.1%, more preferably more than about 0.2%, and Al content is advantageously less than 0.5%, such as about 0.3%.
Mn is present at a level of 1.7-2.20%, preferably 1.70-1.95 thereby compensating the reduction of strength caused by the low Si content.
Cr, Mo and Ni are also present for strength and hardening reasons determining the DP or CP microstructure of the steel strip of the invention. According to the invention the total sum of these elements is at least 0.5%. The amounts of the individual elements are
The steel strip composition may optionally comprise other alloying elements in small amounts. The sum of inevitable impurities and other alloying elements is advantageously less than 1.25%. Preferably the upper limits of the additional alloying elements and individual impurities are
Preferably the steel strip according to the invention has a microstructure comprising martensite 2-50%, preferably at least 5%; ferrite 50-98%; and optionally pearlite less than 3%, preferably about 0%. Advantageously the grain size is about 30 micrometer or less.
In a preferred embodiment the steel strip is coated with a coating comprising Zn. Although the coating can be applied in various ways, hot dip galvanising is preferred using a standard GI coating bath. Other Zn coatings may also be applied. An example comprises a Zn alloy coating according to WO 2008102009, in particular a zinc alloy coating layer consisting of 0.3-4.0% Mg and 0.05%-6.0% Al and optionally at most 0.2% of one or more additional elements along with unavoidable impurities and the remainder being zinc. An additional element typically added in a small amount of less than 0.2 weight %, could be selected from the group comprising Pb or Sb, Ti, Ca, Mn, Sn, La, Ce, Cr, Ni, Zr or Bi. Pb, Sn, Bi and Sb are usually added to form spangles.
Preferably, the total amount of additional elements in the zinc alloy is at most 0.2%. These small amounts of an additional element do not alter the properties of the coating nor the bath to any significant extent for the usual applications.
Preferably, when one or more additional elements are present in the zinc alloy coating, each is present in an amount <0.02 weight %, preferably each is present in an amount <0.01 weight %. Additional elements are usually only added to prevent dross forming in the bath with molten zinc alloy for the hot dip galvanising, or to form spangles in the coating layer.
The invention will be further illustrated by means of the following examples:
Sheets having a composition as indicated in Table 1 were manufactured by a usual cold rolling and continuous annealing process. After hot rolling the strip was cold rolled to a final thickness of listed in Table 2. For Examples 1-2 cold rolled strip is made via standard steel making and rolling routes. After cold rolling the material is continuously annealed in standard annealing lines. The relevant data for examples 1 and 2 are presented in Table 3. After heating to a temperature T1, slow cooling (rate 1-10° C./s) to T2 is carried out and subsequently a rapid cooling (rate 20-60° C./s) to temperature T3. Next, the material is galvanized. Examples 3-4 were prepared in a similar manner.
The sheets were also visually examined for the presence of tiger stripes. Tiger stripes were not observed. Surface quality is nearly full-finish. Also a good coatability was achieved.