Patent Grant
9908143
The present invention relates generally to manufacturing processes for forming or creating devices which are implantable within a patient, such as medical devices. More particularly, the present invention relates to methods and processes for forming or creating tubular substrates which may be further processed to create medical devices having various geometries suitable for implantation within a patient.
In recent years there has been growing interest in the use of artificial materials, particularly materials formed from polymers, for use in implantable devices that come into contact with bodily tissues or fluids particularly blood. Some examples of such devices are artificial heart valves, stents, and vascular prosthesis. Some medical devices such as implantable stents which are fabricated from a metal have been problematic in fracturing or failing after implantation. Moreover, certain other implantable devices made from polymers have exhibited problems such as increased wall thickness to prevent or inhibit fracture or failure. However, stents having reduced wall thickness are desirable particularly for treating arterial diseases.
Because many polymeric implants such as stents are fabricated through processes such as extrusion or injection molding, such methods typically begin the process by starting with an inherently weak material. In the example of a polymeric stent, the resulting stent may have imprecise geometric tolerances as well as reduced wall thicknesses which may make these stents susceptible to brittle fracture.
A stent which is susceptible to brittle fracture is generally undesirable because of its limited ability to collapse for intravascular delivery as well as its limited ability to expand for placement or positioning within a vessel. Moreover, such polymeric stents also exhibit a reduced level of strength. Brittle fracture is particularly problematic in stents as placement of a stent onto a delivery balloon or within a delivery sheath imparts a substantial amount of compressive force in the material comprising the stent. A stent made of a brittle material may crack or have a very limited ability to collapse or expand without failure. Thus, a certain degree of malleability is desirable for a stent to expand, deform, and maintain its position securely within the vessel.
Accordingly, it is desirable to produce a polymeric substrate having one or more layers which retains its mechanical strength and is sufficiently ductile so as to prevent or inhibit brittle fracture, particularly when utilized as a biocompatible and/or bioabsorbable polymeric stent for implantation within a patient body.
A number of casting processes described herein may be utilized to develop substrates (e.g., cylindrically shaped substrates, ellipsoid shaped substrates, diamond-shaped substrates, etc.) having a relatively high level of geometric precision and mechanical strength. These polymeric substrates can then be machined using any number of processes (e.g., high-speed laser sources, mechanical machining, etc.) to create devices such as stents having a variety of geometries for implantation within a patient, such as the peripheral or coronary vasculature, etc.
An example of such a casting process is to utilize a dip-coating process. The utilization of dip-coating to create a polymeric substrate having such desirable characteristics results in substrates which are able to retain the inherent properties of the starting materials. This in turn results in substrates having relatively high radial strength, ductility and associated fatigue characteristics which are retained through any additional manufacturing processes for implantation. Additionally, dip-coating the polymeric substrate also allows for the creation of substrates having multiple layers.
The molecular weight of a polymer is typically one of the factors in determining the mechanical behavior of the polymer. With an increase in the molecular weight of a polymer, there is generally a transition from brittle to ductile failure. Ductile materials also have a comparatively higher fatigue life. A mandrel may be utilized to cast or dip-coat the polymeric substrate.
In dip-coating the polymeric substrate, one or more high molecular weight biocompatible and/or bioabsorbable polymers may be selected for forming upon the mandrel. The one or more polymers may be dissolved in a compatible solvent in one or more corresponding containers such that the appropriate solution may be placed under the mandrel. As the substrate may be formed to have one or more layers overlaid upon one another, the substrate may be formed to have a first layer of a first polymer, a second layer of a second polymer, and so on depending upon the desired structure and properties of the substrate. Thus, the various solutions and containers may be replaced beneath the mandrel between dip-coating operations in accordance with the desired layers to be formed upon the substrate such that the mandrel may be dipped sequentially into the appropriate polymeric solution.
Parameters such as the number of times the mandrel is immersed, the sequence and direction of dipping, the duration of time of each immersion within the solution, as well as the delay time between each immersion or the drying or curing time between dips and dipping and/or withdrawal rates of the mandrel to and/or from the solution may each be controlled to result in the desired mechanical characteristics. Formation via the dip-coating process may result in a polymeric substrate having substantially less wall thickness while retaining an increased level of strength in the substrate as compared to an extruded or injection-molded polymeric structure.
The immersion times as well as drying times may be uniform between each immersion or they may be varied as determined by the desired properties of the resulting substrate. Moreover, the substrate may be placed in an oven or dried at ambient temperature between each immersion or after the final immersion to attain a predetermined level of crystals, e.g., 20% to 40%, and a level of amorphous polymeric structure, e.g., 60% to 80%. Each of the layers overlaid upon one another during the dip-coating process are tightly adhered to one another and the wall thicknesses and mechanical properties of each polymer are retained in their respective layer with no limitation on the molecular weight and/or crystalline structure of the polymers utilized.
Dip-coating can be used to impart an orientation between layers (e.g., linear orientation by dipping; radial orientation by spinning the mandrel; etc.) to further enhance the mechanical properties of the formed substrate. As radial strength is a desirable attribute of stent design, post-processing of the formed substrate may be accomplished to impart such attributes. Typically, polymeric stents suffer from having relatively thick walls to compensate for the lack of radial strength, and this in turn reduces flexibility, impedes navigation, and reduces arterial luminal area immediately post implantation. Post-processing may also help to prevent material creep and recoil (creep is a time-dependent permanent deformation that occurs to a specimen under stress, typically under elevated temperatures) which are problems typically associated with polymeric stents.
For post-processing, a predetermined amount of force may be applied to the substrate where such a force may be generated by a number of different methods. One method is by utilizing an expandable pressure vessel placed within the substrate. Another method is by utilizing a braid structure, such as a braid made from a super-elastic or shape memory alloy like NiTi alloy, to increase in size and to apply the desirable degree of force against the interior surface of the substrate.
Yet another method may apply the expansion force by application of a pressurized inert gas such as nitrogen within the substrate lumen. A completed substrate may be placed inside a molding tube which has an inner diameter that is larger than the cast cylinder. A distal end or distal portion of the cast cylinder may be clamped or otherwise closed and a pressure source may be coupled to a proximal end of the cast cylinder. The entire assembly may be positioned over a nozzle which applies heat to either the length of the cast cylinder or to a portion of cast cylinder. The increase in diameter of the cast cylinder may thus realign the molecular orientation of the cast cylinder to increase its radial strength. After the diameter has been increased, the cast cylinder may be cooled.
Once the processing has been completed on the polymeric substrate, the substrate may be further formed or machined to create a variety of device. One example includes stents created from the cast cylinder by cutting along a length of the cylinder to create a rolled stent for delivery and deployment within the patient vasculature. Another example includes machining a number of portions to create a lattice or scaffold structure which facilitates the compression and expansion of the stent.
In other variations, in forming the stent, the substrate may be first formed at a first diameter, as described herein by immersing a mandrel into at least a first polymeric solution such that at least a first layer of a biocompatible polymer substrate is formed upon the mandrel and has a first diameter defined by the mandrel. In forming the substrate, parameters such as controlling a number of immersions of the mandrel into the first polymeric solution, controlling a duration of time of each immersion of the mandrel, and controlling a delay time between each immersion of the mandrel are controlled. With the substrate initially formed, the first diameter of the substrate may be reduced to a second smaller diameter and processed to form an expandable stent scaffold configured for delivery and deployment within a vessel, wherein the stent scaffold retains one or more mechanical properties of the polymer resin such that the stein scaffold exhibits ductility upon application of a load.
With the stent scaffold formed and heat set to have an initial diameter, it may be reduced to a second delivery diameter and placed upon a delivery catheter for intravascular delivery within a patient body comprising positioning the stent having the second diameter at a target location within the vessel, expanding the stent to a third diameter that is larger than the second diameter (and possibly smaller than the initial diameter) at the target location utilizing an inflation balloon or other mechanism, and allowing the stent to then self-expand into further contact with the vessel at the target location such that the stent self-expands over time back to its initial diameter or until it is constrained from further expansion by the vessel walls.
In manufacturing implantable devices from polymeric materials such as biocompatible and/or biodegradable polymers, a number of casting processes described herein may be utilized to develop substrates, e.g., cylindrically shaped substrates, having a relatively high level of geometric precision and mechanical strength. These polymeric substrates can then be machined using any number of processes (e.g., high-speed laser sources, mechanical machining, etc.) to create devices such as stents having a variety of geometries for implantation within a patient, such as the peripheral or coronary vasculature, etc.
An example of such a casting process is to utilize a dip-coating process. The utilization of dip-coating to create a polymeric substrate having such desirable characteristics results in substrates which are able to retain the inherent properties of the starting materials. This in turn results in substrates having a relatively high radial strength which is mostly retained through any additional manufacturing processes for implantation. Additionally, dip-coating the polymeric substrate also allows for the creation of substrates having multiple layers. The multiple layers may be formed from the same or similar materials or they may be varied to include any number of additional agents, such as one or more drugs for treatment of the vessel, as described in further detail below. Moreover, the variability of utilizing multiple layers for the substrate may allow one to control other parameters, conditions, or ranges between individual layers such as varying the degradation rate between layers while maintaining the intrinsic molecular weight and mechanical strength of the polymer at a high level with minimal degradation of the starting materials.
Because of the retention of molecular weight and mechanical strength of the starting materials via the casting or dip-coating process, polymeric substrates may be formed which enable the fabrication of devices such as stents with reduced wall thickness which is highly desirable for the treatment of arterial diseases. Furthermore these processes may produce structures having precise geometric tolerances with respect to wall thicknesses, concentricity, diameter, etc.
One mechanical property in particular which is generally problematic with, e.g., polymeric stents formed from polymeric substrates, is failure via brittle fracture of the device when placed under stress within the patient body. It is generally desirable for polymeric stents to exhibit ductile failure under an applied load rather via brittle failure, especially during delivery and deployment of a polymeric stent from an inflation balloon or constraining sheath, as mentioned above. Percent (%) ductility is generally a measure of the degree of plastic deformation that has been sustained by the material at fracture. A material that experiences very little or no plastic deformation upon fracture is brittle.
The molecular weight of a polymer is typically one of the factors in determining the mechanical behavior of the polymer. With an increase in the molecular weight of a polymer, there is generally a transition from brittle to ductile failure. An example is illustrated in the stress-strain plot 10 which illustrate the differing mechanical behavior resulting from an increase in molecular weight. The stress-strain curve 12 of a sample of polylactic acid (PLLA) 2.4 shows a failure point 18 having a relatively low tensile strain percentage at a high tensile stress level indicating brittle failure. A sample of PLLA 4.3, which has a relatively higher molecular weight than PLLA 2.4, illustrates a stress-strain curve 14 which has a region of plastic failure 20 after the onset of yielding and a failure point 22 which has a relatively lower tensile stress value at a relatively higher tensile strain percentage indicating a degree of ductility. Yield occurs when a material initially departs from the linearity of a stress-strain curve and experiences an elastic-plastic transition.
A sample of PLLA 8.4, which has yet a higher molecular weight than PLLA 4.3, illustrates a stress-strain curve 16 which has a longer region of plastic failure 24 after the onset of yielding. The failure point 26 also has a relatively lower tensile stress value at a relatively higher tensile strain percentage indicating a degree of ductility. Thus, a high-strength tubular material which exhibits a relatively high degree of ductility may be fabricated utilizing polymers having a relatively high molecular weight (e.g., PLLA 8.4, PLLA with 8.28 IV, etc.). Such a tubular material may be processed via any number of machining processes to form an implantable device such as a stent which exhibits a stress-strain curve which is associated with the casting or dip-coating process described herein. The resultant device can be subjected to relatively high levels of strain without fracturing.
An example of a mandrel which may be utilized to cast or dip-coat the polymeric substrate is illustrated in the side view of
The assembly 30 may be isolated on a vibration-damping or vibrationally isolated table to ensure that the liquid surface held within container 44 remains completely undisturbed to facilitate the formation of a uniform thickness of polymer material along mandrel 40 and/or substrate 50 with each deposition The entire assembly 30 or just a portion of the assembly such as the mandrel 40 and polymer solution may be placed in an inert environment such as a nitrogen gas environment while maintaining a very low relative humidity (RH) level, e.g., less than 30% RH, and appropriate dipping temperature, e.g., at least 20° C. below the boiling point of the solvent within container 44 so as to ensure adequate bonding between layers of the dip-coated substrate. Multiple mandrels may also be mounted along bracket arm 38 or directly to column 34.
Various drying methods may be utilized, e.g., convection, infrared, or other conventional drying techniques within a controlled environment are generally desirable as high humidity levels with high temperatures can induce hydrolysis which affects the crystallinity level and mechanical properties of the substrates during drying. For instance, PLA 8.4 substrates have a percentage of crystallinity level between, e.g., 20% to 40% or more particularly between 27% to 35%, which generally exhibit good ductility during tensile tests. If the substrates have a crystallinity that approaches 60% (which is typically the crystallinity of resin), the substrates will generally exhibit brittle failure.
Convection drying may be typically employed to uniformly heat and dry the substrates to a residual solvent level of, e.g., less than 100 ppm, while vacuum drying and/or infrared drying can be employed to shorten or reduce the typical drying time of 10 or up to 40 days depending on type of polymers used. Infrared drying can be employed to dry the surface layers at a temperature which is higher than a drying temperature of the inner layers which may contain heat sensitive drugs. In this case, the drugs within the inner layers are prevented or inhibited from degrading within the matrix. Moreover, infrared drying may prevent or inhibit the inner layers from thermal degradation if a different polymer of different glass transition temperature is used whereas convection drying for such a combination substrate may be less desirable. Generally, the drying temperature maybe performed at 5° to 10° C. below or higher than the glass transition temperature.
The mandrel 40 may be sized appropriately and define a cross-sectional geometry to impart a desired shape and size to the substrate 50. Mandrel 40 may be generally circular in cross section although geometries may be utilized as desired. In one example, mandrel 40 may define a circular geometry having a diameter ranging from 1 mm to 20 mm to form a polymeric substrate having a corresponding inner diameter. Moreover, mandrel 40 may be made generally from various materials which are suitable to withstand dip-coating processes, e.g., stainless steel, copper, aluminum, silver, brass, nickel, titanium, etc. The length of mandrel 40 that is dipped into the polymer solution may be optionally limited in length by, e.g., 50 cm, to ensure that an even coat of polymer is formed along the dipped length of mandrel 40 to limit the effects of gravity during the coating process. Mandrel 40 may also be made from a polymeric material which is lubricious, strong, has good dimensional stability, and is chemically resistant to the polymer solution utilized for dip-coating, e.g., fluoropolymers, polyacetal, polyester, polyamide, polyacrylates, etc.
Mandrel 40 may be made alternatively from a shape memory material, such as a shape memory polymer (SMP) or a shape memory alloy, to assist in the removal of a substrate 50 from the mandrel 40 by inducing a temporary shape of a uniform tubular form in the mandrel 40 during dipping. Additionally and/or alternatively, a layer of SMP may be utilized as a layer for dip coating substrate 50. After drying, the substrate 50 and mandrel 40 maybe subjected to temperature change, T>Tg by 5° to 10° C. to induce a small deformation of less than 5% in the mandrel 40 to assist in the removal of the substrate 50 and/or for delaminating the SMP layer to further assist in removing the substrate 50. The mandrel 40 may be comprised of various shape memory alloys, e.g., Nickel-Titanium, and various SMPs may comprise, e.g., physically cross-linked polymers or chemically cross-linked polymers etc. Examples of physically cross-linked polymers may include polyurethanes with ionic or mesogenic components made by prepolymer methods. Other block copolymers which may also be utilized may include, e.g., block copolymers of polyethyleneterephthalate (PET) and polyethyleneoxide (PEO), block copolymers containing polystyrene and poly(1,4-butadiene), ABA triblock copolymer made from poly(2-methyl-2-oxazoline) and poly(Tetrahydrofuran), etc.
Moreover, mandrel 40 may be made to have a smooth surface for the polymeric solution to form upon. In other variations, mandrel 40 may define a surface that is coated with a material such as polytetrafluoroethylene to enhance removal of the polymeric substrate formed thereon. In yet other variations, mandrel 40 may be configured to define any number of patterns over its surface, e.g., either over its entire length or just a portion of its surface, that can be mold-transferred during the dip-coating process to the inner surface of the first layer of coating of the dip-coated substrate tube. The patterns may form raised or depressed sections to form various patterns such as checkered, cross-hatched, cratered, etc. that may enhance endothelialization with the surrounding tissue after the device is implanted within a patient, e.g., within three to nine months of implantation.
The direction that mandrel 40 is dipped within polymeric solution 46 may also be alternated or changed between layers of substrate 50. In forming substrates having a length ranging from, e.g., 1 cm to 40 cm or longer, substrate 50 may be removed from mandrel 40 and replaced onto mandrel 40 in an opposite direction before the dipping process is continued. Alternatively, mandrel 40 may be angled relative to bracket arm 38 and/or polymeric solution 46 during or prior to the dipping process.
This may also be accomplished in yet another variation by utilizing a dipping assembly as illustrated in
Dipping mandrel 40 and substrate 50 in different directions may also enable the coated layers to have a uniform thickness throughout from its proximal end to its distal end to help compensate for the effects of gravity during the coating process. These values are intended to be illustrative and are not intended to be limiting in any manner. Any excess dip-coated layers on the linkages 56, 58 may simply be removed from mandrel 40 by breaking the layers. Alternating the dipping direction may also result in the polymers being oriented alternately which may reinforce the tensile strength in the axial direction of the dip coated tubular substrate 50.
With dip-coating assembly 30, one or more high molecular weight biocompatible and/or bioabsorbable polymers may be selected for forming upon mandrel 40. Examples of polymers which may be utilized to form the polymeric substrate may include, but is not limited to, polyethylene, polycarbonates, polyamides, polyesteramides, polyetheretherketone, polyacetals, polyketals, polyurethane, polyolefin, or polyethylene terephthalate and degradable polymers, for example, polylactide (PLA) including poly-L-lactide (PLLA), poly(DL-Lactide), poly-glycolide (PGA), poly(lactide-co-glycolide) (PLGA) or polycaprolactone, caprolactones, polydioxanones, polyanhydrides, polyorthocarbonates, polyphosphazenes, chitin, chitosan, poly(amino acids), and polyorthoesters, and copolymers, terpolymers and combinations and mixtures thereof.
Other examples of suitable polymers may include synthetic polymers, for example, oligomers, homopolymers, and co-polymers, acrylics such as those polymerized from methyl cerylate, methyl methacrylate, acryli acid, methacrylic acid, acrylamide, hydroxyethy acrylate, hydroxyethyl methacrylate, glyceryl scrylate, glyceryl methacrylate, methacrylamide and ethacrylamide; vinyls such as styrene, vinyl chloride, binaly pyrrolidone, polyvinyl alcohol, and vinyls acetate; polymers formed of ethylene, propylene, and tetrifluoroethylene. Further examples may include nylons such as polycoprolactam, polylauryl lactam, polyjexamethylene adipamide, and polyexamethylene dodecanediamide, and also polyurethanes, polycarbonates, polyamides, polysulfones, poly(ethylene terephthalate), polyactic acid, polyglycolic acid, polydimethylsiloxanes, and polyetherketones.
Examples of biodegradable polymers which can be used for dip-coating process are polylactide (PLA), polyglycolide (PGA), poly(lactide-co-glycolide) (PLGA), poly(e-caprolactone), polydioxanone, polyanhydride, trimethylene carbonate, poly(β-hydroxybutyrate), poly(g-ethyl glutamate), poly(DTH iminocarbonate), poly(bisphenol A iminocarbonate), poly(ortho ester), polycyanoacrylate, and polyphosphazene, and copolymers, terpolymers and combinations and mixtures thereof. There are also a number of biodegradable polymers derived from natural sources such as modified polysaccharides (cellulose, chitin, chitosan, dextran) or modified proteins (fibrin, casein).
Other examples of suitable polymers may include synthetic polymers, for example, oligomers, homopolymers, and co-polymers, acrylics such as those polymerized from methyl cerylate, methyl methacrylate, acryli acid, methacrylic acid, acrylamide, hydroxyethy acrylate, hydroxyethyl methacrylate, glyceryl scrylate, glyceryl methacrylate, methacrylamide and ethacrylamide; vinyls such as styrene, vinyl chloride, binaly pyrrolidone, polyvinyl alcohol, and vinyls acetate; polymers formed of ethylene, propylene, and tetrifluoroethylene. Further examples may include nylons such as polycoprolactam, polylauryl lactam, polyjexamethylene adipamide, and polyexamethylene dodecanediamide, and also polyurethanes, polycarbonates, polyamides, polysulfones, poly(ethylene terephthalate), polyacetals, polyketals, polydimethylsiloxanes, and polyetherketones.
These examples of polymers which may be utilized for forming the substrate are not intended to be limiting or exhaustive but are intended to be illustrative of potential polymers which may be used. As the substrate may be formed to have one or more layers overlaid upon one another, the substrate may be formed to have a first layer of a first polymer, a second layer of a second polymer, and so on depending upon the desired structure and properties of the substrate. Thus, the various solutions and containers may be replaced beneath mandrel 40 between dip-coating operations in accordance with the desired layers to be formed upon the substrate such that the mandrel 40 may be dipped sequentially into the appropriate polymeric solution.
Depending upon the desired wall thickness of the formed substrate, the mandrel 40 may be dipped into the appropriate solution as determined by the number of times the mandrel 40 is immersed, the duration of time of each immersion within the solution, as well as the delay time between each immersion or the drying or curing time between dips. Additionally, parameters such as the dipping and/or withdrawal rate of the mandrel 40 from the polymeric solution may also be controlled to range from, e.g., 5 mm/min to 1000 mm/min. Formation via the dip-coating process may result in a polymeric substrate having half the wall thickness while retaining an increased level of strength in the substrate as compared to an extruded polymeric structure. For example, to form a substrate having a wall thickness of, e.g., 200 μm, built up of multiple layers of polylactic acid, mandrel 40 may be dipped between, e.g., 2 to 20 times or more, into the polymeric solution with an immersion time ranging from, e.g., 15 seconds (or less) to 240 minutes (or more. Moreover, the substrate and mandrel 40 may be optionally dried or cured for a period of time ranging from, e.g., 15 seconds (or less) to 60 minutes (or more) between each immersion. These values are intended to be illustrative and are not intended to be limiting in any manner.
Aside from utilizing materials which are relatively high in molecular weight, another parameter which may be considered in further increasing the ductility of the material is its crystallinity, which refers to the degree of structural order in the polymer. Such polymers may contain a mixture of crystalline and amorphous regions where reducing the percentage of the crystalline regions in the polymer may further increase the ductility of the material. Polymeric materials not only having a relatively high molecular weight but also having a relatively low crystalline percentage may be utilized in the processes described herein to form a desirable tubular substrate.
The following Table 1 show examples of various polymeric materials (e.g., PLLA IV 8.28 and PDLLA 96/4) to illustrate the molecular weights of the materials in comparison to their respective crystallinity percentage. The glass transition temperature, Tg, as well as melting temperature, Tm, are given as well. An example of PLLA IV 8.28 is shown illustrating the raw resin and tube form as having the same molecular weight, Mw, of 1.70×106 gram/mol. However, the crystallinity percentage of PLLA IV 8.28 Resin is 61.90% while the corresponding Tube form is 38.40%. Similarly for PDLLA 96/4, the resin form and tube form each have a molecular weight, Mw, of 9.80×105 gram/mol; however, the crystallinity percentages are 46.20% and 20.90%, respectively.
As the resin is dip coated to form the tubular substrate through the methods described herein, the drying procedures and processing helps to preserve the relatively high molecular weight of the polymer from the starting material and throughout processing to substrate and stent formation. Moreover, the drying processes in particular may facilitate the formation of desirable crystallinity percentages, as described above. Furthermore, the molecular weight and crystallinity percentages, which define the strength of the substrate, are uniform within each layer as well as throughout the entire structure thereby creating a substrate that is isotropic in nature.
The resulting substrate, and the stent formed from the substrate, generally exhibits an equivalent strength in all directions. For example, the resulting stem may exhibit a radial strength which is equal to an axial or tangential strength of the stent. This feature may allow for the substrate and stent to handle loads imparted by the surrounding tissue at any number of angles. This may be particularly desirable in peripheral vessels such as the superficial femoral artery (SFA), where an implanted stent needs to be able to resist a complex and multi-axis loading condition. As strength in tubular polymeric structures are generally directional and in the case of stents, the radial strength is typically higher than the relative strengths in either the axial and tangential direction. Accordingly, the preservation of the starting polymer molecular weight helps to result in a stent having equivalent strength in all directions.
The isotropic property cannot be achieved by such processes as injection molding, extrusion and blow molding. The injection molding and extrusion processes induce axial strength while the blow molding process induces a circumferential orientation. As the result, stents that are fabricated using these processes have a preferential strength specific to the axis of orientation. In many stent designs, the isotropic material characteristics are advantageous since deformation of such material are more predictable and the prosthesis created from such substrates may have a more uniform distribution of stresses under loading conditions.
Aside from the crystallinity of the materials, the immersion times as well as drying times may be uniform between each immersion or they may be varied as determined by the desired properties of the resulting substrate. Moreover, the substrate may be placed in an oven or dried at ambient temperature between each immersion or after the final immersion to attain a predetermined level of crystals, e.g., 20% to 40%, and a level of amorphous polymeric structure, e.g., 60% to 80%. Each of the layers overlaid upon one another during the dip-coating process are tightly adhered to one another and the mechanical properties of each polymer are retained in their respective layer with no limitation on the molecular weight of the polymers utilized. The dipping process also allows the operator to control molecular weight and crystallinity of the tubular structure which becomes the base for the resulting prosthesis. Depending on the molecular weight and crystallinity combination chosen, the resulting prosthesis may be able to provide high radial strength (e.g., 10 N per 1 cm length at 20% compression), withstand considerable amount of strain without fracturing (e.g., 150% strain), and exhibit high fatigue life under physiological conditions (e.g, 10 million cycles under radial pulse load).
Varying the drying conditions of the materials may also be controlled to effect desirable material parameters. The polymers may be dried at or above the glass transition temperature (e.g., 10° to 20° C. above the glass transition temperature, Tg) of the respective polymer to effectively remove any residual solvents from the polymers to attain residual levels of less than 100 ppm, e.g., between 20 to 100 ppm. Positioning of the polymer substrate when drying is another factor which may be controlled as affecting parameters, such as geometry, of the tube. For instance, the polymer substrate may be maintained in a drying position such that the substrate tube is held in a perpendicular position relative to the ground such that the concentricity of the tubes is maintained. The substrate tube may be dried in an oven at or above the glass transition temperature, as mentioned, for a period of time ranging anywhere from, e.g., 10 days to 30 days or more. However, prolonged drying for a period of time, e.g., greater than 40 days, may result in thermal degradation of the polymer material.
Additionally and/or optionally, a shape memory effect may be induced in the polymer during drying of the substrate. For instance, a shape memory effect may be induced in the polymeric tubing to set the tubular shape at the diameter that was formed during the dip-coating process. An example of this is to form a polymeric tube by a dip-coating process described herein at an outer diameter of 5 mm and subjecting the substrate to temperatures above its glass transition temperature, Tg. At its elevated temperature, the substrate may be elongated, e.g., from a length of 5 cm to 7 cm, while its outer diameter of 5 mm is reduced to 3 mm. Of course, these examples are merely illustrative and the initial diameter may generally range anywhere from, e.g., 3 mm to 10 mm, and the reduced diameter may generally range anywhere from, e.g., 1.5 mm to 5 mm, provided the reduced diameter is less than the initial diameter.
Once lengthened and reduced in diameter, the substrate may be quenched or cooled in temperature to a sub-Tg level, e.g., about 20° C. below its Tg, to allow for the polymeric substrate to transition back to its glass state. This effectively imparts a shape memory effect of self-expansion to the original diameter of the substrate. When such a tube (or stent formed from the tubular substrate) is compressed or expanded to a smaller or larger diameter and later exposed to an elevated temperature, over time the tube (or stent) may revert to its original 5 mm diameter. This post processing may also be useful for enabling self-expansion of the substrate after a process like laser cutting (e.g., when forming stents or other devices for implantation within the patient) where the substrate tube is typically heated to its glass transition temperature, Tg.
An example of a substrate having multiple layers is illustrated in
An example of this is illustrated in the cross-sectional end view of
For instance, the molecular weight of different layers can also be tailored, e.g. when the first outer layer (with the minimum molecular weight Mn1) degrades to certain levels, large amounts of oligomers or monomers are formed and the degradation rates of the layers are accelerated due to these low molecular weight degradation products diffused into the layers. By selecting different polymers to form the composition of this outer layer, the time needed to trigger this accelerated degradation of the other layers may be tailored. For example, any of the layers (such as the outer layer or inner layer) may be a co-polymer of 50% PLA/50% PGA where a degradation rate of the PGA is relatively faster than a degradation rate of the PLA. Thus, a layer formed of this co-polymer may have the PGA degrade relatively faster than the PLA, which in turn accelerates the degradation of the PLA itself. Alternatively or additionally, a single layer such as the outer layer may be made from such a co-polymer where degradation of the PGA in the outer layer may accelerate not only the outer layer but also the inner layer as well. Other variations may be accomplished as well depending upon the desired degradation rate and order of degradation between differing layers.
Moreover, any one or more of the layers may be formed to impart specified mechanical properties to the substrate 50 such that the composite mechanical properties of the resulting substrate 50 may specifically tuned or designed. Additionally, although three layers are illustrated in this example, any number of layers may be utilized depending upon the desired mechanical properties of the substrate 50.
Moreover, as multiple layers may be overlaid one another in forming the polymeric substrate, specified layers may be designated for a particular function in the substrate. For example, in substrates which are used to manufacture polymeric stents, one or more layers may be designed as load-bearing layers to provide structural integrity to the stent while certain other layers may be allocated for drug-loading or eluting. Those layers which are designated for structural support may be formed from high-molecular weight polymers, e.g., PLLA or any other suitable polymer described herein, to provide a high degree of strength by omitting any drugs as certain pharmaceutical agents may adversely affect the mechanical properties of polymers. Those layers which are designated for drug-loading may be placed within, upon, or between the structural layers.
An example of utilizing layer-specific substrates may include the incorporation of one or more bio-beneficial layers that can be used to reduce the risk of blood interaction with an internal layer of a prosthesis such as the formation of thrombosis. Representative bio-beneficial materials include, but are not limited to, polyethers such as poly(ethylene glycol), copoly(ether-esters) (e.g. PEO/PLA), polyalkylene oxides such as poly(ethylene oxide), poly(propylene oxide), poly(ether ester), polyalkylene oxalates, polyphosphazenes, phosphoryl choline, choline, poly(aspirin), polymers and co-polymers of hydroxyl bearing monomers such as hydroxyethyl methacrylate (HEMA), hydroxypropyl methacrylate (HPMA), hydroxypropylmethacrylamide, poly(ethylene glycol)acrylate (PEGA), PEG methacrylate, 2-methacryloyloxyethylphosphorylcholine (MPC) and n-vinyl pyrrolidone (VP), carboxylic acid bearing monomers such as methacrylic acid (MA), acrylic acid (AA), alkoxymethacrylate, alkoxyacrylate, and 3-trimethylsilylpropyl methacrylate (TMSPMA), poly(styrene-isoprene-styrene)-PEG (SIS-PEG), polystyrene-PEG, polyisobutylene-PEG, polycaprolactone-PEG (PCL-PEG), PLA-PEG, poly(methyl methacrylate)-PEG (PMMA-PEG), polydimethylsiloxane-co-PEG (PDMS-PEG), poly(vinylidene fluoride)-PEG (PVDF-PEG), PLURONICT™ surfactants (polypropylene oxide-co-polyethylene glycol), poly(tetramethylene glycol), hydroxy functional poly(vinyl pyrrolidone), molecules such as fibrin, fibrinogen, cellulose, starch, collagen, dextran, dextrin, hyaluronic acid, fragments and derivatives of hyaluronic acid, heparin, fragments and derivatives of heparin, glycosamino glycan (GAG), GAG derivatives, polysaccharide, elastin, chitosan, alginate, silicones, PolyActive, and combinations thereof. In some embodiments, a coating described herein can exclude any one of the aforementioned polymers. The term PolyActive refers to a block copolymer having flexible poly(ethylene glycol) and poly(butylene terephthalate) blocks (PEGT/PBT). PolyActive is intended to include AB, ABA, BAB copolymers having such segments of PEG and PBT (e.g., poly(ethylene glycol)-block-poly(butyleneterephthalate)-block poly(ethylene glycol) (PEG-PBT-PEG).
In another variation, the bio-beneficial material can be a polyether such as poly(ethylene glycol) (PEG) or polyalkylene oxide. Bio-beneficial polymers that can be used to attract endothelium cells can also be coated as this first layer. These polymers, such as NO-generating polymers which may synthesized using the following strategy: (1) dispersed non-covalently hound small molecules where the diazeniumdiolate group is attached to amines in low molecular weight compounds; (2) diazeniumdiolate groups covalently bound to pendent polymer side-chains; and (3) covalently bound diazeniumdiolate groups directly to the polymer backbone. Such polymers may use diethylamine (DEA/N2O2) and diazeniumdiolated-spermine (SPER/N2O2) as the non-covalently bound species blended into both poly(ethylene glycol) (PEG) and polycaprolactone, grafting dipropylenetriamine onto a polysaccharide and by treating polyethyleneimine (PEI) with NO to form a diazeniumdiolate NO donor covalently linked directly to the polymer backbone, and 4) NO-donor that has been utilized in developing NO-releasing polymers are S-nitrosothiols (RSNOs). (Frost et al., Biomaterials, 2005, 26(14), page 1685).
In yet another example, a relatively higher molecular weight PLLA “backbone” layer, i.e., a layer which provides structural strength to a prosthesis, may be coupled with one or more various layers of other types of polymeric materials, such as poly-ε-caprolactone (PCL) or a copolymer of PCL. The backbone layer may provide strength while the PCL layer provides overall ductility to the prosthesis. The combination of layers provides a structure having both high strength and ductility. Of course, other combinations of various materials may be combined depending upon the desired resulting characteristics. For instance, another example may include a prosthesis having an inner layer made of PCL or other elastomeric polymers with a relatively high coefficient of friction. When the prosthesis is ultimately crimped onto an intravascular delivery balloon, this relatively high friction inner layer may prevent or inhibit lateral movement of the prosthesis relative to the inflation balloon to enhance stent retention on the delivery device.
Additionally, multiple layers of different drugs may be loaded within the various layers. The manner and rate of drug release from multiple layers may depend in part upon the degradation rates of the substrate materials. For instance, polymers which degrade relatively quickly may release their drugs layer-by-layer as each successive layer degrades to expose the next underlying layer. In other variations, drug release may typically occur from a multilayer matrix via a combination of diffusion and degradation. In one example, a first layer may elute a first drug for, e.g., the first 30 to 40 days after implantation. Once the first layer has been exhausted or degraded, a second underlying layer having a second drug may release this drug for the next 30 to 40 days, and so on if so desired. In the example of
In other examples, rather than having each successive layer elute its respective drug, each layer 62, 64 (optionally layer 60 as well), may elute its respective drug simultaneously or at differing rates via a combination of diffusion and degradation. Although three layers are illustrated in this example, any number of layers may be utilized with any practicable combination of drugs for delivery. Moreover, the release kinetics of each drug from each layer may be altered in a variety of ways by changing the formulation of the drug-containing layer.
Examples of drugs or agents which may be loaded within certain layers of substrate 50 may include one or more antipoliferative, antineoplastic, antigenic, anti-inflammatory, and/or antirestenotic agents. The therapeutic agents may also include antilipid, antimitotics, metalloproteinase inhabitors, anti-sclerosing agents. Therapeutic agents may also include peptides, enzymes, radio isotopes or agents for a variety of treatment options. This list of drugs or agents is presented to be illustrative and is not intended to be limiting.
Similarly certain other layers may be loaded with radio-opaque substances such as platinum, gold, etc. to enable visibility of the stent under imaging modalities such as fluoroscopic imaging. Radio-opaque substances like tungsten, platinum, gold, etc. can be mixed with the polymeric solution and dip-coated upon the substrate such that the radio-opaque substances form a thin sub-micron thick layer upon the substrate. The radio-opaque substances may thus become embedded within layers that degrade in the final stages of degradation or within the structural layers to facilitate stent visibility under an imaging modality, such as fluoroscopy, throughout the life of the implanted device before fully degrading or losing its mechanical strength. Radio-opaque marker layers can also be dip-coated at one or both ends of substrate 50, e.g., up to 0.5 mm from each respective end. Additionally, the radio-opaque substances can also be spray-coated or cast along a portion of the substrate 50 between its proximal and distal ends in a radial direction by rotating mandrel 40 when any form of radio-opaque substance is to be formed along any section of length of substrate 50. Rings of polymers having radio-opaque markers can also be formed as part of the structure of the substrate 50.
In an experimental example of the ductility and retention of mechanical properties, PLLA with Iv 8.4 (high molecular weight) was obtained and tubular substrates were manufactured utilizing the dip-coating process described herein. The samples were formed to have a diameter of 5 mm with a wall thickness of 200 μm and were comprised of 6 layers of PLLA 8.4. The mandrel was immersed 6 times into the polymeric solution and the substrates were dried or cured in an oven to obtain a 60% crystalline structure. At least two samples of tubular substrates were subjected to tensile testing and stress-strain plot 70 was generated from the stress-strain testing, as shown in
As shown in plot 70, a first sample of PLLA 8.4 generated a stress-strain curve 72 having a region of plastic failure 76 where the strain percentage increased at a relatively constant stress value prior to failure indicating a good degree of sample ductility. A second sample of PLLA 8.4 also generated a stress-strain curve 74 having a relatively greater region of plastic failure 78 also indicating a good degree of sample ductility.
Polymeric stents and other implantable devices made from such substrates may accordingly retain the material properties from the dip-coated polymer materials. The resulting stents, for instance, may exhibit mechanical properties which have a relatively high percentage ductility in radial, torsional, and/or axial directions. An example of this is a resulting stent having an ability to undergo a diameter reduction of anywhere between 5% to 70% when placed under an external load without any resulting plastic deformation. Such a stent may also exhibit high radial strength with, e.g., 0.1 N to 5 N per one cm length at 20% deformation. Such a stent may also be configured to self-expand when exposed to normal body temperatures.
The stent may also exhibit other characteristic mechanical properties which are consistent with a substrate formed as described herein, for instance, high ductility and high strength polymeric substrates. Such substrates (and processed steins) may exhibit additional characteristics such as a percent reduction in diameter of between 5% to 70% without fracture formation when placed under a compressive load as well as a percent reduction in axial length of between 10% to 50% without fracture formation when placed under an axial load. Because of the relatively high ductility, the substrate or stent may also be adapted to curve up to 180° about a 1 cm curvature radius without fracture formation or failure. Additionally, when deployed within a vessel, a stent may also be expanded, e.g., by an inflatable intravascular balloon, by up to 5% to 80% to regain diameter without fracture formation or failure.
These values are intended to illustrate examples of how a polymeric tubing substrate and a resulting stent may be configured to yield a device with certain mechanical properties. Moreover, depending upon the desired results, certain tubes and stents may be tailored for specific requirements of various anatomical locations within a patient body by altering the polymer and/or copolymer blends to adjust various properties such as strength, ductility, degradation rates, etc.
A sample of 96/4 PDLLA was also formed and tested to generate stress-strain curve 75 having a point of failure 75′ which exhibited a relatively lower percent elongation characteristic of brittle fracture. The resulting load at failure was between 100 N to 300 N with an elastic modulus of between 1000 to 3000 MPa, which was similar to the PLLA 8.28 samples. However, the percent elongation was between 10% to 40% at failure.
In yet another experimental example of the ductility and retention of mechanical properties, PLLA with Iv 8.28 (high molecular weight) was obtained and tubular substrates were manufactured utilizing the dip-coating process described herein. The samples were formed to have a diameter of 5 mm with a wall thickness of 200 μm and were comprised of 8 layers of PLLA 8.28. The mandrel was immersed 8 times into the polymeric solution and the substrates were dried or cured in an oven to obtain a 25% to 35% crystalline structure. At least four samples of tubular substrates were subjected to tensile testing and the stress-strain plot 91 was generated from the stress-strain testing, as shown in
The samples of PLLA 8.28 generally resulted in a percent elongation of between 97% to 123% at failure when placed under a 73 to 77 MPa stress load. As shown in the plot of
Dip-coating can be used to impart an orientation between layers (e.g., linear orientation by dipping; radial orientation by spinning the mandrel; etc.) to further enhance the mechanical properties of the formed substrate. As radial strength is a desirable attribute of stent design, post-processing of the formed substrate may be accomplished to impart such attributes. Typically, polymeric stents suffer from having relatively thick walls to compensate for the lack of radial strength, and this in turn reduces flexibility, impedes navigation, and reduces arterial luminal area immediately post implantation. Post-processing may also help to prevent material creep and recoil (creep is a time-dependent permanent deformation that occurs to a specimen under stress, typically under elevated temperatures) which are problems typically associated with polymeric stents. By using a relatively high molecular weight in a range of e.g., 259,000 g/mol to 2,120,000 g/mol, and controlling dipping parameters such as speed and temperature as well as the drying condition, the dipped substrates will have the following desirable properties: (1) high radial strength; (2) ductility; (3) malleability; and (4) isotropicity.
In further increasing the radial or circumferential strength of the polymeric substrate, a number of additional processes may be applied to the substrate after the dip-coating procedure is completed (or close to being completed). A polymer that is amorphous or that is partially amorphous will generally undergo a transition from a pliable, elastic state (at higher temperatures) to a brittle glass-like state (at lower temperature) as it transitions through a particular temperature, referred as the glass transition temperature (Tg). The glass transition temperature for a given polymer will vary, depending on the size and flexibility of side chains, as well as the flexibility of the backbone linkages and the size of functional groups incorporated into the polymer backbone. Below Tg, the polymer will maintain some flexibility, and may be deformed to a new shape. However, the further the temperature below Tg the polymer is when being deformed, the greater the force needed to shape it.
Moreover, when a polymer is in glass transition temperature its molecular structure can be manipulated to form an orientation in a desired direction. Induced alignment of polymeric chains or orientation improves mechanical properties and behavior of the material. Molecular orientation is typically imparted by application of force while the polymer is in a pliable, elastic state. After sufficient orientation is induced, temperature of the polymer is reduced to prevent reversal and dissipation of the orientation.
In one example, the polymeric substrate may be heated to increase its temperature along its entire length or along a selected portion of the substrate to a temperature that is at or above the Tg of the polymer. For instance, for a substrate fabricated from PLLA, the substrate may be heated to a temperature between 60° C. to 70° C. Once the substrate has reached a sufficient temperature such that enough of its molecules have been mobilized, a force may be applied from within the substrate or along a portion of the substrate to increase its diameter from a first diameter D1 to a second increased diameter D2 for a period of time necessary to set the increased diameter. During this setting period, the application of force induces a molecular orientation in a circumferential direction to align the molecular orientation of polymer chains to enhance its mechanical properties. The re-formed substrate may then be cooled to a lower temperature typically below Tg, for example, by passing the tube through a cold environment, typically dry air or an inert gas to maintain the shape at diameter D2 and prevent dissipation of molecular orientation.
The force applied to the substrate may be generated by a number of different methods. One method is by utilizing an expandable pressure vessel placed within the substrate. Another method is by utilizing a braid structure, such as a braid made from a super-elastic or shape memory alloy like NiTi alloy, to increase in size and to apply the desirable degree of force against the interior surface of the substrate.
Yet another method may apply the expansion force by application of a pressurized inert gas such as nitrogen within the substrate lumen, as shown in
A distal end or distal portion of cast cylinder 94 may be clamped 96 or otherwise closed and a pressure source may be coupled to a proximal end 98 of cast cylinder 94. The entire assembly may be positioned over a nozzle 102 which applies heat 104 to either the length of cast cylinder 94 or to a portion of cast cylinder 94. The pressurized inert gas 100, e.g., pressured to 10 to 400 psi, may be introduced within cast cylinder 94 to increase its diameter, e.g., 2 mm, to that of the inner diameter, e.g., 4 mm, of molding tube 90. The increase in diameter of cast cylinder 94 may thus realign the molecular orientation of cast cylinder 94 to increase its radial strength and to impart a circumferential orientation in the cast cylinder 94. Portion 92 illustrates radial expansion of the cast cylinder 94 against the inner surface of the molding tube 90 in an exaggerated manner to illustrate the radial expansion and impartation of circumferential strength. After the diameter has been increased, cast cylinder 94 may be cooled, as described above.
Once the substrate has been formed and reduced in diameter to its smaller second diameter, the stent may be processed, as described above. Alternatively, the stent may be processed from the substrate after initial formation. The stent itself may then be reduced in diameter to its second reduced diameter.
In either case, once the stent has been formed into its second reduced diameter, the stent may be delivered to a targeted location within a vessel of a patient. Delivery may be effected intravascularly utilizing known techniques with the stent in its second reduced delivery diameter positioned upon, e.g., an inflation balloon, for intravascular delivery. Once the inflation catheter and stent has been positioned adjacent to the targeted region of vessel, the stent may be initially expanded into contact against the interior surface of the vessel.
With the stent expanded into contact against the vessel wall at a third diameter which is larger than the second delivery diameter, the inflation balloon may be removed from the stent. Over a predetermined period of time and given the structural characteristics of the stent, the stent may then also self-expand further into contact against the vessel wall for secure placement and positioning.
Because thermoplastic polymers such as PLLA typically soften when heated, the cast cylinder 94 or a portion of the cast cylinder 94 may be heated in an inert environment, e.g., a nitrogen gas environment, to minimize its degradation.
Another method for post-processing a cast cylinder 110 may be seen in the example of
In other variations, the mandrel itself may be fabricated into alternative configurations aside from a cylindrical shape to impart these configurations directly into the substrates formed thereupon. An example is illustrated in the side view of
Another variation is shown in the side view of
Yet another variation is shown in the side view of
In yet another variation as illustrated in
As discussed above, another method for substrate and stent fabrication is to form a substrate having a variable wall thickness, as illustrated in the side view of
The dipping process does not require a high temperature. The operation is typically conducted under ambient or below ambient temperatures. At such a temperature, pharmaceutical agents can be distributed into the polymer matrix without thermal effects, which tends to denature most drugs. The drug may also be protected from oxidization by an inert dipping environment and vacuum drying at a very low temperature
Alternatively and as described above, a surface of the mandrel can be formed in a pattern configured to form holes or voids (e.g., cylindrically or rectangularly shaped) into the inner layer of polymer substrate. The formed holes or voids may be formed, for instance, to have a volume of 10-100 μl. These structures may function as reservoirs and can be used to hold various materials for delivery into the patient (e.g., drug molecules, peptides, biological reagents, etc.) by dip coating a substrate into a reservoir containing the material to be introduced into the holds or voids where the solution has a relatively low viscosity ranging from 1.0×10−3 to 50×10−3 Pa·s. Filling of the holes or voids can also be accomplished by directly inject the eluting material into the holes or voids along the substrate. By doing so, the drugs, peptide, biological agents, etc. that are sensitive to temperature can be incorporated directly into the substrate and/or stent for release from the implanted prosthesis. In some variations, the implanted prosthesis can optionally include at least one biologically active (“bioactive”) agent. The at least one bioactive agent can include any substance capable of exerting a therapeutic, prophylactic or diagnostic effect for a patient.
Examples of suitable bioactive agents include, but are not limited to, synthetic inorganic and organic compounds, proteins and peptides, polysaccharides and other sugars, lipids, and DNA and RNA nucleic acid sequences having therapeutic, prophylactic or diagnostic activities. Nucleic acid sequences include genes, antisense molecules that bind to complementary DNA to inhibit transcription, and ribozymes. Some other examples of other bioactive agents include antibodies, receptor ligands, enzymes, adhesion peptides, blood clotting factors, inhibitors or clot dissolving agents such as streptokinase and tissue plasminogen activator, antigens for immunization, hormones and growth factors, oligonucleotides such as antisense oligonucleotides and ribozymes and retroviral vectors for use in gene therapy. The bioactive agents could be designed, e.g., to inhibit the activity of vascular smooth muscle cells. They could be directed at inhibiting abnormal or inappropriate migration and/or proliferation of smooth muscle cells to inhibit restenosis.
In other variations, optionally in combination with one or more other variations described herein, the implantable prosthesis can include at least one biologically active agent selected from antiproliferative, antineoplastic, antimitotic, anti-inflammatory, antiplatelet, anticoagulant, antifibrin, antithrombin, antibiotic, antiallergic and antioxidant substances.
An antiproliferative agent can be a natural proteineous agent such as a cytotoxin or a synthetic molecule. Examples of antiproliferative substances include, but are not limited to, actinomycin D or derivatives and analogs thereof (manufactured by Sigma-Aldrich, or COSMEGEN available from Merck) (synonyms of actinomycin D include dactinomycin, actinomycin IV, actinomycin I1, actinomycin X1, and actinomycin C1); all taxoids such as taxols, docetaxel, and paclitaxel and derivatives thereof; all olimus drugs such as macrolide antibiotics, rapamycin, everolimus, structural derivatives and functional analogues of rapamycin, structural derivatives and functional analogues of everolimus, FKBP-12 mediated mTOR inhibitors, biolimus, perfenidone, prodrugs thereof, co-drugs thereof, and combinations thereof. Examples of rapamycin derivatives include, but are not limited to, 40-O-(2-hydroxy)ethyl-rapamycin (trade name everolimus from Novartis), 40-O-(2-ethoxy)ethyl-rapamycin (biolimus), 40-O-(3-hydroxy)propyl-rapamycin, 40-O-[2-(2-hydroxy)ethoxy]ethyl-rapamycin, 40-O-tetrazole-rapamycin, 40-epi-(N1-tetrazolyl)-rapamycin (zotarolimus, manufactured by Abbott Labs.), Biolimus A9 (Biosensors International, Singapore), AP23572 (Ariad Pharmaceuticals), prodrugs thereof, co-drugs thereof, and combinations thereof.
An anti-inflammatory drug can be a steroidal anti-inflammatory drug, a nonsteroidal anti-inflammatory drug (NSAID), or a combination thereof. Examples of anti-inflammatory drugs include, but are not limited to, alclofenac, alclometasone dipropionate, algestone acetonide, alpha amylase, amcinafal, amcinafide, amfenac sodium, amiprilose hydrochloride, anakinra, anirolac, anitrazafen, apazone, balsalazide disodium, bendazac, benoxaprofen, benzydamine hydrochloride, bromelains, broperamole, budesonide, carprofen, cicloprofen, cintazone, cliprofen, clobetasol, clobetasol propionate, clobetasone butyrate, clopirac, cloticasone propionate, cormethasone acetate, cortodoxone, deflazacort, desonide, desoximetasone, dexamethasone, dexamethasone acetate, dexamethasone dipropionate, diclofenac potassium, diclofenac sodium, diflorasone diacetate, diflumidone sodium, diflunisal, difluprednate, diftalone, dimethyl sulfoxide, drocinonide, endrysone, enlimomab, enolicam sodium, epirizole, etodolac, etofenamate, felbinac, fenamole, fenbufen, fenclofenac, fenclorac, fendosal, fenpipalone, fentiazac, flazalone, fluazacort, flufenamic acid, flumizole, flunisolide acetate, flunixin, flunixin meglumine, fluocortin butyl, fluorometholone acetate, fluquazone, flurbiprofen, fluretofen, fluticasone propionate, furaprofen, furobufen, halcinonide, halobetasol propionate, halopredone acetate, ibufenac, ibuprofen, ibuprofen aluminum, ibuprofen piconol, ilonidap, indomethacin, indomethacin sodium, indoprofen, indoxole, intrazole, isoflupredone acetate, isoxepac, isoxicam, ketoprofen, lofemizole hydrochloride, lomoxicam, loteprednol etabonate, meclofenamate sodium, meclofenamic acid, meclorisone dibutyrate, mefenamic acid, mesalamine, meseclazone, methylprednisolone suleptanate, morniflumate, nabumetone, naproxen, naproxen sodium, naproxol, nimazone, olsalazine sodium, orgotein, orpanoxin, oxaprozin, oxyphenbutazone, paranyline hydrochloride, pentosan polysulfate sodium, phenbutazone sodium glycerate, pirfenidone, piroxicam, piroxicam cinnamate, piroxicam olamine, pirprofen, prednazate, prifelone, prodolic acid, proquazone, proxazole, proxazole citrate, rimexolone, romazarit, salcolex, salnacedin, salsalate, sanguinarium chloride, seclazone, sermetacin, sudoxicam, sulindac, suprofen, talmetacin, talniflumate, talosalate, tebufelone, tenidap, tenidap sodium, tenoxicam, tesicam, tesimide, tetrydamine, tiopinac, tixocortol pivalate, tolmetin, tolmetin sodium, triclonide, triflumidate, zidometacin, zomepirac sodium, aspirin (acetylsalicylic acid), salicylic acid, corticosteroids, glucocorticoids, tacrolimus, pimecorlimus, prodrugs thereof, co-drugs thereof, and combinations thereof.
Alternatively, the anti-inflammatory agent can be a biological inhibitor of pro-inflammatory signaling molecules. Anti-inflammatory biological agents include antibodies to such biological inflammatory signaling molecules.
In addition, the bioactive agents can be other than antiproliferative or anti-inflammatory agents. The bioactive agents can be any agent that is a therapeutic, prophylactic or diagnostic agent. In some embodiments, such agents can be used in combination with antiproliferative or anti-inflammatory agents. These bioactive agents can also have antiproliferative and/or anti-inflammmatory properties or can have other properties such as antineoplastic, antimitotic, cystostatic, antiplatelet, anticoagulant, antifibrin, antithrombin, antibiotic, antiallergic, and/or antioxidant properties.
Examples of antineoplastics and/or antimitotics include, but are not limited to, paclitaxel (e.g., TAXOL® available from Bristol-Myers Squibb), docetaxel (e.g., Taxotere® from Aventis), methotrexate, azathioprine, vincristine, vinblastine, fluorouracil, doxorubicin hydrochloride (e.g., Adriamycin® from Pfizer), and mitomycin (e.g., Mutamycin® from Bristol-Myers Squibb).
Examples of antiplatelet, anticoagulant, antifibrin, and antithrombin agents that can also have cytostatic or antiproliferative properties include, but are not limited to, sodium heparin, low molecular weight heparins, heparinoids, hirudin, argatroban, forskolin, vapiprost, prostacyclin and prostacyclin analogues, dextran, D-phe-pro-arg-chloromethyl ketone (synthetic antithrombin), dipyridamole, glycoprotein IIb/IIIa platelet membrane receptor antagonist antibody, recombinant hirudin, thrombin inhibitors such as ANGIOMAX (from Biogen), calcium channel blockers (e.g., nifedipine), colchicine, fibroblast growth factor (FGF) antagonists, fish oil (e.g., omega 3-fatty acid), histamine antagonists, lovastatin (a cholesterol-lowering drug that inhibits HMG-CoA reductase, brand name Mevacor® from Merck), monoclonal antibodies (e.g., those specific for platelet-derived growth factor (PDGF) receptors), nitroprusside, phosphodiesterase inhibitors, prostaglandin inhibitors, suramin, serotonin blockers, steroids, thioprotease inhibitors, triazolopyrimidine (a PDGF antagonist), nitric oxide or nitric oxide donors, super oxide dismutases, super oxide dismutase mimetics, 4-amino-2,2,6,6-tetramethylpiperidine-1-oxyl (4-amino-TEMPO), estradiol, anticancer agents, dietary supplements such as various vitamins, and a combination thereof.
Examples of cytostatic substances include, but are not limited to, angiopeptin, angiotensin converting enzyme inhibitors such as captopril (e.g., Capoten® and Capozide® from Bristol-Myers Squibb), cilazapril and lisinopril (e.g., Prinivil® and Prinzide® from Merck).
Examples of antiallergic agents include, but are not limited to, permirolast potassium. Examples of antioxidant substances include, but are not limited to, 4-amino-2,2,6,6-tetramethylpiperidine-1-oxyl (4-amino-TEMPO). Other bioactive agents include anti-infectives such as antiviral agents; analgesics and analgesic combinations; anorexics; antihelmintics; antiarthritics, antiasthmatic agents; anticonvulsants; antidepressants; antidiuretic agents; antidiarrheals; antihistamines; antimigrain preparations; antinauseants; antiparkinsonism drugs; antipruritics; antipsychotics; antipyretics; antispasmodics; anticholinergics; sympathomimetics; xanthine derivatives; cardiovascular preparations including calcium channel blockers and beta-blockers such as pindolol and antiarrhythmics; antihypertensives; diuretics; vasodilators including general coronary vasodilators; peripheral and cerebral vasodilators; central nervous system stimulants; cough and cold preparations, including decongestants; hypnotics; immunosuppressives; muscle relaxants; parasympatholytics; psychostimulants; sedatives; tranquilizers; naturally derived or genetically engineered lipoproteins; and restenoic reducing agents.
Other biologically active agents that can be used include alpha-interferon, genetically engineered epithelial cells, tacrolimus and dexamethasone.
A “prohealing” drug or agent, in the context of a blood-contacting implantable device, refers to a drug or agent that has the property that it promotes or enhances re-endothelialization of arterial lumen to promote healing of the vascular tissue. The portion(s) of an implantable device (e.g., a stent) containing a prohealing drug or agent can attract, bind, and eventually become encapsulated by endothelial cells (e.g., endothelial progenitor cells). The attraction, binding, and encapsulation of the cells will reduce or prevent the formation of emboli or thrombi due to the loss of the mechanical properties that could occur if the stent was insufficiently encapsulated. The enhanced re-endothelialization can promote the endothelialization at a rate faster than the loss of mechanical properties of the stent.
The prohealing drug or agent can be dispersed in the body of the bioabsorbable polymer substrate or scaffolding. The prohealing drug or agent can also be dispersed within a bioabsorbable polymer coating over a surface of an implantable device (e.g., a stent).
“Endothelial progenitor cells” refer to primitive cells made in the bone marrow that can enter the bloodstream and go to areas of blood vessel injury to help repair the damage. Endothelial progenitor cells circulate in adult human peripheral blood and are mobilized from bone marrow by cytokines, growth factors, and ischemic conditions. Vascular injury is repaired by both angiogenesis and vasculogenesis mechanisms. Circulating endothelial progenitor cells contribute to repair of injured blood vessels mainly via a vasculogenesis mechanism.
In some embodiments, the prohealing drug or agent can be an endothelial cell (EDC)-binding agent. In certain embodiments, the EDC-binding agent can be a protein, peptide or antibody, which can be, e.g., one of collagen type 1, a 23 peptide fragment known as single chain Fv fragment (scFv A5), a junction membrane protein vascular endothelial (VE)-cadherin, and combinations thereof. Collagen type 1, when bound to osteopontin, has been shown to promote adhesion of endothelial cells and modulate their viability by the down regulation of apoptotic pathways. S. M. Martin, et al., J. Biomed. Mater. Res., 70A:10-19 (2004). Endothelial cells can be selectively targeted (for the targeted delivery of immunoliposomes) using say A5. T. Volkel, et al., Biochimica et Biophysica Acta, 1663:158-166 (2004). Junction membrane protein vascular endothelial (VE)-cadherin has been shown to bind to endothelial cells and down regulate apoptosis of the endothelial cells. R. Spagnuolo, et al., Blood, 103:3005-3012 (2004).
In a particular embodiment, the EDC-binding agent can be the active fragment of osteopontin, (Asp-Val-Asp-Val-Pro-Asp-Gly-Asp-Ser-Leu-Ala-Tyr-Gly (SEQ ID NO: 1)). Other EDC-binding agents include, but are not limited to, EPC (epithelial cell) antibodies, RGD peptide sequences, RGD mimetics, and combinations thereof.
In further embodiments, the prohealing drug or agent can be a substance or agent that attracts and binds endothelial progenitor cells. Representative substances or agents that attract and bind endothelial progenitor cells include antibodies such as CD-34, CD-133 and vegf type 2 receptor. An agent that attracts and binds endothelial progenitor cells can include a polymer having nitric oxide donor groups.
The foregoing biologically active agents are listed by way of example and are not meant to be limiting. Other biologically active agents that are currently available or that may be developed in the future are equally applicable.
In a more specific embodiment, optionally in combination with one or more other embodiments described herein, the implantable device of the invention comprises at least one biologically active agent selected from paclitaxel, docetaxel, estradiol, nitric oxide donors, super oxide dismutases, super oxide dismutase mimics, 4-amino-2,2,6,6-tetramethylpiperidine-1-oxyl (4-amino-TEMPO), tacrolimus, dexamethasone, dexamethasone acetate, rapamycin, rapamycin derivatives, 40-O-(2-hydroxy)ethyl-rapamycin (everolimus), 40-O-(2-ethoxy)ethyl-rapamycin (biolimus), 40-O-(3-hydroxy)propyl-rapamycin, 40-O-[2-(2-hydroxy)ethoxy]ethyl-rapamycin, 40-O-tetrazole-rapamycin, 40-epi-(N1-tetrazolyl)-rapamycin (zotarolimus), Biolimus A9 (Biosensors International, Singapore), AP23572 (Ariad Pharmaceuticals), pimecrolimus, imatinib mesylate, midostaurin, clobetasol, progenitor cell-capturing antibodies, prohealing drugs, prodrugs thereof, co-drugs thereof, and a combination thereof. In a particular embodiment, the bioactive agent is everolimus. In another specific embodiment, the bioactive agent is clobetasol.
An alternative class of drugs would be p-para-agonists for increased lipid transportation, examples include feno fibrate.
In some embodiments, optionally in combination with one or more other embodiments described herein, the at least one biologically active agent specifically cannot be one or more of any of the bioactive drugs or agents described herein.
A prosthesis described above having one or more holes or voids can also be used to treat, prevent, or ameliorate any number of medical conditions located at the downstream vessel where the vessel is too narrow to allow any device to pass. By incorporation of the controlled release of various agents, these therapeutic agents may be delivered to the diseased area to provide for a regional therapy treatment carried out without the side effects that may be observed for a systematic treatment. Some exemplary treatments include delivering chemotherapeutical agents for tumor, anti inflammatory agents for kidney chronic glomerulonephritis, blood clot preventing agents for heart small vessel disease, small vessel arterial disease, small vessel peripheral arterial disease, and peripheral pulmonary vessel disease.
Once the processing has been completed on the polymeric substrate, the substrate may be further formed or machined to create a variety of device. One example is shown in the perspective view of
Aside from the design of stent 124 described above, other stent designs may be utilized which are particularly attuned to the physical and mechanical characteristics provided by the resulting polymeric substrate. Such stent designs may be mechanically optimized to take advantage of the ductility and strength characteristics provided by the polymeric material to result in a stent which is capable of experiencing between 10% to 80% material strain during the crimping process. For example, the starting diameter of a stent which is formed from a cured substrate may be initially at, e.g., 5 mm, and end with a crimped diameter of between, e.g., 2 to 2.8 mm. Further crimping to an even smaller diameter can increase the material strain above 100%.
Moreover, the optimized stent design may possess a relatively high fatigue life for a range of deformations by taking advantage of linear elastic properties possessed by the substrate prior to the initiation of any plastic deformation. The stent design may be modified based on physiologic conditions and materials selected so that when the stent is experiencing deformations caused by, e.g., physiologic conditions, the stent experiences material strain values that lie within the range of elastic deformation of the selected material.
Examples of some optimized stent designs which take advantage of the inherent material properties of the formed polymeric substrate are illustrated in the side views of
The stent designs may also accommodate relatively high levels of deformation in a variety of modes (radial, axial, bending, etc) while staying within, e.g., a 150% material strain limit, of various substrate materials. Examples of such high strain situations include crushing, shortening, stretching, and bending of the stent due to motion and external forces. The stent designs thus allow the stent to withstand such motion without fracturing by maintaining material strain below the ultimate strain of the material.
As shown in the side view of
Another variations is illustrated in the side view of
With stent 130 positioned upon delivery catheter 132, it may be advanced intravascularly within a vessel 136 until the delivery site is reached, as shown in
Once the stent 130 has been expanded to some intermediate diameter D3 and secured against the vessel wall, stent 130 may be allowed to then self-expand further over a period of time into further contact with the vessel wall such that stent 130 conforms securely to the tissue. This self-expansion feature ultimately allows for the stent 130 to expand back to its initial diameter D1 which had been heat set, as shown in
These examples are presented to be illustrative of the types of devices which may be formed and various other devices which may be formed from the polymeric substrate are also included within this disclosure.
The applications of the disclosed invention discussed above are not limited to certain processes, treatments, or placement in certain regions of the body, but may include any number of other processes, treatments, and areas of the body. Modification of the above-described methods and devices for carrying out the invention, and variations of aspects of the invention that are obvious to those of skill in the arts are intended to be within the scope of this disclosure. Moreover, various combinations of aspects between examples are also contemplated and are considered to be within the scope of this disclosure as well.
This application is a divisional of U.S. patent application Ser. No. 12/488,453 filed Jun. 19, 2009, which is a continuation-in-part of U.S. patent application Ser. No. 12/143,659 filed Jun. 20, 2008, both of which are incorporated herein by reference in their entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4173689 | Lyman et al. | Nov 1979 | A |
| 4334327 | Lyman et al. | Jun 1982 | A |
| 4655771 | Wallsten | Apr 1987 | A |
| 4661530 | Gogolewski et al. | Apr 1987 | A |
| 4733665 | Palmaz | Mar 1988 | A |
| 4739762 | Palmaz | Apr 1988 | A |
| 4770664 | Gogolewski | Sep 1988 | A |
| 4776337 | Palmaz | Oct 1988 | A |
| 4834747 | Gogolewski | May 1989 | A |
| 4950258 | Kawai et al. | Aug 1990 | A |
| 4955899 | Della Corna et al. | Sep 1990 | A |
| 5061275 | Wallsten et al. | Oct 1991 | A |
| 5102417 | Palmaz | Apr 1992 | A |
| 5104400 | Berguer et al. | Apr 1992 | A |
| 5139480 | Hickle et al. | Aug 1992 | A |
| 5152782 | Kowligi et al. | Oct 1992 | A |
| 5163952 | Froix | Nov 1992 | A |
| 5258020 | Froix | Nov 1993 | A |
| 5288711 | Mitchell et al. | Feb 1994 | A |
| 5383887 | Nadal | Jan 1995 | A |
| 5421955 | Lau et al. | Jun 1995 | A |
| 5443458 | Eury | Aug 1995 | A |
| 5449373 | Pinchasik et al. | Sep 1995 | A |
| 5514154 | Lau et al. | May 1996 | A |
| 5516781 | Morris et al. | May 1996 | A |
| 5563146 | Morris et al. | Oct 1996 | A |
| 5607467 | Froix | Mar 1997 | A |
| 5630162 | Wilkinson et al. | May 1997 | A |
| 5630840 | Mayer | May 1997 | A |
| 5645559 | Hachtman et al. | Jul 1997 | A |
| 5665728 | Morris et al. | Sep 1997 | A |
| 5670161 | Healy et al. | Sep 1997 | A |
| 5716410 | Wang et al. | Feb 1998 | A |
| 5733303 | Israel et al. | Mar 1998 | A |
| 5741323 | Pathak et al. | Apr 1998 | A |
| 5744515 | Clapper | Apr 1998 | A |
| 5769816 | Barbut et al. | Jun 1998 | A |
| 5795318 | Wang et al. | Aug 1998 | A |
| RE35988 | Winston et al. | Dec 1998 | E |
| 5843089 | Sahatjian et al. | Dec 1998 | A |
| 5843120 | Israel et al. | Dec 1998 | A |
| 5848987 | Baudino et al. | Dec 1998 | A |
| 5922021 | Jang | Jul 1999 | A |
| 5935164 | Iversen | Aug 1999 | A |
| 5935506 | Schmitz et al. | Aug 1999 | A |
| 5954744 | Phan et al. | Sep 1999 | A |
| 5962004 | Jannetta | Oct 1999 | A |
| 5962007 | Cooper et al. | Oct 1999 | A |
| 5964744 | Balbierz et al. | Oct 1999 | A |
| 5972018 | Israel et al. | Oct 1999 | A |
| 5980552 | Pinchasik et al. | Nov 1999 | A |
| 5980555 | Barbut et al. | Nov 1999 | A |
| 5989281 | Barbut et al. | Nov 1999 | A |
| 6007573 | Wallace et al. | Dec 1999 | A |
| 6027525 | Suh et al. | Feb 2000 | A |
| 6059811 | Pinchasik et al. | May 2000 | A |
| 6066167 | Lau et al. | May 2000 | A |
| 6086605 | Barbut et al. | Jul 2000 | A |
| 6090097 | Barbut et al. | Jul 2000 | A |
| 6090134 | Tu et al. | Jul 2000 | A |
| 6117154 | Barbut et al. | Sep 2000 | A |
| 6117168 | Yang et al. | Sep 2000 | A |
| 6136016 | Barbut et al. | Oct 2000 | A |
| 6153252 | Hossainy et al. | Nov 2000 | A |
| 6160084 | Langer et al. | Dec 2000 | A |
| 6168619 | Dinh et al. | Jan 2001 | B1 |
| 6217815 | Sisbarro | Apr 2001 | B1 |
| 6224627 | Armstrong et al. | May 2001 | B1 |
| 6231326 | Sisbarro | May 2001 | B1 |
| 6231544 | Tsugita et al. | May 2001 | B1 |
| 6235045 | Barbut et al. | May 2001 | B1 |
| 6248129 | Froix | Jun 2001 | B1 |
| 6254632 | Wu et al. | Jul 2001 | B1 |
| 6267776 | O'Connell | Jul 2001 | B1 |
| 6273901 | Whitcher et al. | Aug 2001 | B1 |
| 6281262 | Shikinami | Aug 2001 | B1 |
| 6309412 | Lau et al. | Oct 2001 | B1 |
| 6309414 | Rolando et al. | Oct 2001 | B1 |
| 6315792 | Armstrong et al. | Nov 2001 | B1 |
| 6322847 | Zhong et al. | Nov 2001 | B1 |
| 6331188 | Lau et al. | Dec 2001 | B1 |
| 6338739 | Datta et al. | Jan 2002 | B1 |
| 6338793 | Putman | Jan 2002 | B1 |
| 6364904 | Smith | Apr 2002 | B1 |
| 6379383 | Palmaz et al. | Apr 2002 | B1 |
| 6423086 | Barbut et al. | Jul 2002 | B1 |
| 6423092 | Datta et al. | Jul 2002 | B2 |
| 6432133 | Lau et al. | Aug 2002 | B1 |
| 6443982 | Israel et al. | Sep 2002 | B1 |
| 6461381 | Israel et al. | Oct 2002 | B2 |
| 6464722 | Israel et al. | Oct 2002 | B2 |
| 6485511 | Lau et al. | Nov 2002 | B2 |
| 6500204 | Igaki | Dec 2002 | B1 |
| 6503270 | Richter et al. | Jan 2003 | B1 |
| 6508834 | Pinchasik et al. | Jan 2003 | B1 |
| 6517559 | O'Connell | Feb 2003 | B1 |
| 6520986 | Martin et al. | Feb 2003 | B2 |
| 6530950 | Alvarado et al. | Mar 2003 | B1 |
| 6533805 | Jervis | Mar 2003 | B1 |
| 6533808 | Thompson | Mar 2003 | B1 |
| 6537295 | Petersen | Mar 2003 | B2 |
| 6537311 | Cox et al. | Mar 2003 | B1 |
| 6537312 | Datta et al. | Mar 2003 | B2 |
| 6540774 | Cox | Apr 2003 | B1 |
| 6540775 | Fischell et al. | Apr 2003 | B1 |
| 6540776 | Sanders Millare et al. | Apr 2003 | B2 |
| 6540779 | Richter et al. | Apr 2003 | B2 |
| 6544279 | Hopkins et al. | Apr 2003 | B1 |
| 6547815 | Myers | Apr 2003 | B2 |
| 6547817 | Fischell et al. | Apr 2003 | B1 |
| 6551350 | Thornton et al. | Apr 2003 | B1 |
| 6554758 | Turnlund et al. | Apr 2003 | B2 |
| 6554858 | Dereume et al. | Apr 2003 | B2 |
| 6562063 | Euteneuer et al. | May 2003 | B1 |
| 6562065 | Shanley | May 2003 | B1 |
| 6565596 | White et al. | May 2003 | B1 |
| 6565598 | Lootz | May 2003 | B1 |
| 6565600 | Hojeibane | May 2003 | B2 |
| 6565602 | Rolando et al. | May 2003 | B2 |
| 6575887 | Schrayer | Jun 2003 | B1 |
| 6575994 | Marin et al. | Jun 2003 | B1 |
| 6579306 | Voelker et al. | Jun 2003 | B1 |
| 6579308 | Jansen et al. | Jun 2003 | B1 |
| 6579310 | Cox et al. | Jun 2003 | B1 |
| 6582447 | Patel et al. | Jun 2003 | B1 |
| 6582458 | White et al. | Jun 2003 | B1 |
| 6582467 | Teitelbaum et al. | Jun 2003 | B1 |
| 6585747 | Limon et al. | Jul 2003 | B1 |
| 6585757 | Callol | Jul 2003 | B1 |
| 6589264 | Barbut et al. | Jul 2003 | B1 |
| 6589266 | Whitcher et al. | Jul 2003 | B2 |
| 6589276 | Pinchasik et al. | Jul 2003 | B2 |
| 6589562 | Shefer et al. | Jul 2003 | B1 |
| 6592546 | Barbut et al. | Jul 2003 | B1 |
| 6592617 | Thompson | Jul 2003 | B2 |
| 6596021 | Lootz | Jul 2003 | B1 |
| 6596022 | Lau et al. | Jul 2003 | B2 |
| 6599308 | Amplatz | Jul 2003 | B2 |
| 6602279 | Nicholas | Aug 2003 | B1 |
| 6605107 | Klein | Aug 2003 | B1 |
| 6605110 | Harrison | Aug 2003 | B2 |
| 6605113 | Wilk | Aug 2003 | B2 |
| 6607501 | Gorsuch | Aug 2003 | B2 |
| 6607553 | Healy et al. | Aug 2003 | B1 |
| 6613073 | White et al. | Sep 2003 | B1 |
| 6616690 | Rolando et al. | Sep 2003 | B2 |
| 6623521 | Steinke et al. | Sep 2003 | B2 |
| 6626933 | Lau et al. | Sep 2003 | B1 |
| 6626934 | Blaeser et al. | Sep 2003 | B2 |
| 6626938 | Butaric et al. | Sep 2003 | B1 |
| 6626939 | Burnside et al. | Sep 2003 | B1 |
| 6629991 | Lau et al. | Oct 2003 | B1 |
| 6635082 | Hossainy et al. | Oct 2003 | B1 |
| 6635084 | Israel et al. | Oct 2003 | B2 |
| 6652558 | Patel et al. | Nov 2003 | B2 |
| 6652572 | Kugler et al. | Nov 2003 | B2 |
| 6652574 | Jayaraman | Nov 2003 | B1 |
| 6652575 | Wang | Nov 2003 | B2 |
| 6652579 | Cox et al. | Nov 2003 | B1 |
| 6652581 | Ding | Nov 2003 | B1 |
| 6653426 | Alvarado et al. | Nov 2003 | B2 |
| 6656219 | Wiktor | Dec 2003 | B1 |
| 6656220 | Gomez et al. | Dec 2003 | B1 |
| 6666883 | Seguin et al. | Dec 2003 | B1 |
| 6669722 | Chen et al. | Dec 2003 | B2 |
| D484979 | Fontaine | Jan 2004 | S |
| 6673106 | Mitelberg et al. | Jan 2004 | B2 |
| 6679910 | Granada | Jan 2004 | B1 |
| 6679911 | Burgermeister | Jan 2004 | B2 |
| 6685736 | White et al. | Feb 2004 | B1 |
| 6687553 | Erickson et al. | Feb 2004 | B2 |
| 6689158 | White et al. | Feb 2004 | B1 |
| 6689159 | Lau et al. | Feb 2004 | B2 |
| 6699256 | Logan et al. | Mar 2004 | B1 |
| 6699276 | Sogard et al. | Mar 2004 | B2 |
| 6699278 | Fischell et al. | Mar 2004 | B2 |
| 6702844 | Lazarus | Mar 2004 | B1 |
| 6702846 | Mikus et al. | Mar 2004 | B2 |
| 6702850 | Byun et al. | Mar 2004 | B1 |
| 6706062 | Vardi et al. | Mar 2004 | B2 |
| 6709425 | Gambale et al. | Mar 2004 | B2 |
| 6709453 | Pinchasik et al. | Mar 2004 | B2 |
| 6709454 | Cox et al. | Mar 2004 | B1 |
| 6716240 | Fischell et al. | Apr 2004 | B2 |
| 6719782 | Chuter | Apr 2004 | B1 |
| 6719934 | Stinson | Apr 2004 | B2 |
| 6736842 | Healy et al. | May 2004 | B2 |
| 6740114 | Burgermeister | May 2004 | B2 |
| 6746476 | Hojeibane | Jun 2004 | B1 |
| 6752829 | Kocur et al. | Jun 2004 | B2 |
| 6753071 | Pacetti | Jun 2004 | B1 |
| 6756094 | Wang et al. | Jun 2004 | B1 |
| 6758858 | McCrea et al. | Jul 2004 | B2 |
| 6758859 | Dang et al. | Jul 2004 | B1 |
| 6758860 | Penn et al. | Jul 2004 | B1 |
| 6764506 | Roubin et al. | Jul 2004 | B2 |
| 6764507 | Shanley et al. | Jul 2004 | B2 |
| 6770088 | Jang | Aug 2004 | B1 |
| 6770089 | Hong et al. | Aug 2004 | B1 |
| 6770091 | Richter et al. | Aug 2004 | B2 |
| 6773455 | Allen et al. | Aug 2004 | B2 |
| 6776022 | Kula et al. | Aug 2004 | B2 |
| 6780164 | Bergheim et al. | Aug 2004 | B2 |
| 6783543 | Jang | Aug 2004 | B2 |
| 6783544 | Lynch et al. | Aug 2004 | B2 |
| 6786929 | Gambale et al. | Sep 2004 | B2 |
| 6790226 | Edwin et al. | Sep 2004 | B2 |
| 6790227 | Burgermeister | Sep 2004 | B2 |
| 6790228 | Hossainy et al. | Sep 2004 | B2 |
| 6792979 | Konya et al. | Sep 2004 | B2 |
| 6793672 | Khosravi et al. | Sep 2004 | B2 |
| 6794485 | Shalaby et al. | Sep 2004 | B2 |
| 6796997 | Penn et al. | Sep 2004 | B1 |
| 6796999 | Pinchasik | Sep 2004 | B2 |
| 6802868 | Gambale et al. | Oct 2004 | B2 |
| 6805706 | Solovay et al. | Oct 2004 | B2 |
| 6805745 | Hong et al. | Oct 2004 | B2 |
| 6805898 | Wu et al. | Oct 2004 | B1 |
| 6808533 | Goodwin et al. | Oct 2004 | B1 |
| 6814746 | Thompson et al. | Nov 2004 | B2 |
| 6814748 | Baker et al. | Nov 2004 | B1 |
| 6814749 | Cox et al. | Nov 2004 | B2 |
| 6818013 | Mitelberg et al. | Nov 2004 | B2 |
| 6818014 | Brown et al. | Nov 2004 | B2 |
| 6818015 | Hankh et al. | Nov 2004 | B2 |
| 6833153 | Roorda et al. | Dec 2004 | B1 |
| 6835203 | Vardi et al. | Dec 2004 | B1 |
| 6846323 | Yip et al. | Jan 2005 | B2 |
| 6849086 | Cragg | Feb 2005 | B2 |
| 6855125 | Shanley | Feb 2005 | B2 |
| 6855162 | Parodi | Feb 2005 | B2 |
| 6858037 | Penn et al. | Feb 2005 | B2 |
| 6860898 | Stack et al. | Mar 2005 | B2 |
| 6860901 | Baker et al. | Mar 2005 | B1 |
| 6860946 | Hossainy et al. | Mar 2005 | B2 |
| 6863685 | Davila et al. | Mar 2005 | B2 |
| 6866805 | Hong et al. | Mar 2005 | B2 |
| 6875228 | Pinchasik et al. | Apr 2005 | B2 |
| 6875229 | Wilson et al. | Apr 2005 | B2 |
| 6881223 | Penn et al. | Apr 2005 | B2 |
| 6884258 | Verdi et al. | Apr 2005 | B2 |
| 6887264 | Penn et al. | May 2005 | B2 |
| 6890350 | Walak | May 2005 | B1 |
| 6893458 | Cox et al. | May 2005 | B2 |
| 6896697 | Yip et al. | May 2005 | B1 |
| 6896699 | Wilson et al. | May 2005 | B2 |
| 6899729 | Cox et al. | May 2005 | B1 |
| 6908479 | Lau et al. | Jun 2005 | B2 |
| 6908624 | Hossainy et al. | Jun 2005 | B2 |
| 6913619 | Brown et al. | Jul 2005 | B2 |
| 6920882 | Berg et al. | Jul 2005 | B2 |
| 6923828 | Wiktor | Aug 2005 | B1 |
| 6932832 | Patel et al. | Aug 2005 | B2 |
| 6932930 | DeSimone et al. | Aug 2005 | B2 |
| 6935404 | Duerig et al. | Aug 2005 | B2 |
| 6939371 | Kugler et al. | Sep 2005 | B2 |
| 6942689 | Majercak | Sep 2005 | B2 |
| 6945949 | Wilk | Sep 2005 | B2 |
| 6949117 | Gambale et al. | Sep 2005 | B2 |
| 6955686 | Majercak et al. | Oct 2005 | B2 |
| 6955687 | Richter et al. | Oct 2005 | B2 |
| 6955688 | Wilson et al. | Oct 2005 | B2 |
| 6960219 | Grudem et al. | Nov 2005 | B2 |
| 6960228 | Mitelberg et al. | Nov 2005 | B2 |
| 6962603 | Brown et al. | Nov 2005 | B1 |
| 6981985 | Brown et al. | Jan 2006 | B2 |
| 6981986 | Brown et al. | Jan 2006 | B1 |
| 6989071 | Kocur et al. | Jan 2006 | B2 |
| 6991642 | Petersen | Jan 2006 | B2 |
| 6991647 | Jadhav | Jan 2006 | B2 |
| 6997948 | Stinson | Feb 2006 | B2 |
| 6997949 | Tuch | Feb 2006 | B2 |
| 7001419 | DiCaprio et al. | Feb 2006 | B2 |
| 7001424 | Patel et al. | Feb 2006 | B2 |
| 7004966 | Edwin et al. | Feb 2006 | B2 |
| D516723 | Shanley | Mar 2006 | S |
| 7008446 | Amis et al. | Mar 2006 | B1 |
| 7008466 | Collins | Mar 2006 | B2 |
| 7011672 | Barbut et al. | Mar 2006 | B2 |
| 7018401 | Hyodoh et al. | Mar 2006 | B1 |
| 7029492 | Mitsudou et al. | Apr 2006 | B1 |
| 7029493 | Majercak et al. | Apr 2006 | B2 |
| 7037331 | Mitelberg et al. | May 2006 | B2 |
| 7048014 | Hyodoh et al. | May 2006 | B2 |
| 7052513 | Thompson | May 2006 | B2 |
| D523558 | Shanley | Jun 2006 | S |
| 7060088 | Fischell et al. | Jun 2006 | B1 |
| 7060089 | Ley et al. | Jun 2006 | B2 |
| 7063719 | Jansen et al. | Jun 2006 | B2 |
| RE39157 | Hess | Jul 2006 | E |
| 7070617 | Kula et al. | Jul 2006 | B2 |
| 7081130 | Jang | Jul 2006 | B2 |
| 7087078 | Hildebrand et al. | Aug 2006 | B2 |
| 7094255 | Penn et al. | Aug 2006 | B2 |
| 7097652 | Becker et al. | Aug 2006 | B2 |
| 7100617 | Maginot | Sep 2006 | B1 |
| 7101392 | Heath | Sep 2006 | B2 |
| 7105019 | Hojeibane | Sep 2006 | B2 |
| 7112298 | Kampa et al. | Sep 2006 | B2 |
| 7118593 | Davidson et al. | Oct 2006 | B2 |
| 7122049 | Banas et al. | Oct 2006 | B2 |
| 7135039 | De Scheerder et al. | Nov 2006 | B2 |
| 7137993 | Acosta et al. | Nov 2006 | B2 |
| 7141062 | Pinchasik et al. | Nov 2006 | B1 |
| 7147649 | Thomas | Dec 2006 | B2 |
| 7160592 | Rypacek et al. | Jan 2007 | B2 |
| 7166125 | Baker et al. | Jan 2007 | B1 |
| 7169170 | Widenhouse | Jan 2007 | B2 |
| 7169173 | Hossainy et al. | Jan 2007 | B2 |
| 7169174 | Fischell et al. | Jan 2007 | B2 |
| 7169177 | Obara | Jan 2007 | B2 |
| 7172623 | Hansen et al. | Feb 2007 | B2 |
| 7175654 | Bonsignore et al. | Feb 2007 | B2 |
| 7179266 | Lenz | Feb 2007 | B2 |
| 7179288 | Shanley | Feb 2007 | B2 |
| 7195648 | Jones et al. | Mar 2007 | B2 |
| 7204847 | Gambale | Apr 2007 | B1 |
| 7204848 | Brown et al. | Apr 2007 | B1 |
| 7208010 | Shanley et al. | Apr 2007 | B2 |
| 7208011 | Shanley et al. | Apr 2007 | B2 |
| 7214240 | Bonsignore et al. | May 2007 | B2 |
| 7220275 | Davidson et al. | May 2007 | B2 |
| 7226558 | Nieman et al. | Jun 2007 | B2 |
| 7232421 | Gambale et al. | Jun 2007 | B1 |
| 7252679 | Fischell et al. | Aug 2007 | B2 |
| 7252680 | Freitag | Aug 2007 | B2 |
| 7258697 | Cox et al. | Aug 2007 | B1 |
| 7264633 | Bonsignore | Sep 2007 | B2 |
| 7270668 | Andreas et al. | Sep 2007 | B2 |
| 7288111 | Holloway et al. | Oct 2007 | B1 |
| 7291166 | Cheng et al. | Nov 2007 | B2 |
| 7294146 | Chew et al. | Nov 2007 | B2 |
| 7294214 | Craig | Nov 2007 | B2 |
| 7300456 | Andreas et al. | Nov 2007 | B2 |
| 7311726 | Mitelberg et al. | Dec 2007 | B2 |
| 7311727 | Mazumder et al. | Dec 2007 | B2 |
| 7316710 | Cheng et al. | Jan 2008 | B1 |
| 7316711 | Allen et al. | Jan 2008 | B2 |
| 7320702 | Hammersmark et al. | Jan 2008 | B2 |
| 7323007 | Sano | Jan 2008 | B2 |
| 7326241 | Jang | Feb 2008 | B2 |
| 7326245 | Rosenthal et al. | Feb 2008 | B2 |
| 7329366 | Gale et al. | Feb 2008 | B1 |
| 7331984 | Tu et al. | Feb 2008 | B2 |
| 7338519 | Fischell et al. | Mar 2008 | B2 |
| 7341598 | Davidson et al. | Mar 2008 | B2 |
| 7347867 | Phelps et al. | Mar 2008 | B2 |
| 7357813 | Burgermeister | Apr 2008 | B2 |
| 7572287 | Stinson | Aug 2009 | B2 |
| 7618448 | Schmitz et al. | Nov 2009 | B2 |
| 7867988 | Yan et al. | Jan 2011 | B2 |
| 8088789 | Yan et al. | Jan 2012 | B2 |
| 8182890 | Zheng et al. | May 2012 | B2 |
| 8206635 | Ramzipoor et al. | Jun 2012 | B2 |
| 8206636 | Ramzipoor et al. | Jun 2012 | B2 |
| 8323780 | Zheng et al. | Dec 2012 | B1 |
| 8367081 | Yan et al. | Feb 2013 | B2 |
| 8404641 | Yan et al. | Mar 2013 | B2 |
| 8585753 | Scanlon et al. | Nov 2013 | B2 |
| 8636792 | Zheng et al. | Jan 2014 | B2 |
| 8814930 | Zheng et al. | Aug 2014 | B2 |
| 9492587 | Kleiner | Nov 2016 | B2 |
| 9675478 | Pacetti et al. | Jun 2017 | B2 |
| 20010014717 | Hossainy et al. | Aug 2001 | A1 |
| 20010029398 | Jadhav | Oct 2001 | A1 |
| 20010039432 | Whitcher et al. | Nov 2001 | A1 |
| 20020019661 | Datta et al. | Feb 2002 | A1 |
| 20020062134 | Barbut et al. | May 2002 | A1 |
| 20020077596 | McKenzie et al. | Jun 2002 | A1 |
| 20020077693 | Barclay et al. | Jun 2002 | A1 |
| 20020082682 | Barclay et al. | Jun 2002 | A1 |
| 20020143388 | Datta et al. | Oct 2002 | A1 |
| 20020165601 | Clerc | Nov 2002 | A1 |
| 20020169601 | Nishio | Nov 2002 | A1 |
| 20020188240 | Gorsuch | Dec 2002 | A1 |
| 20020193864 | Khosravi et al. | Dec 2002 | A1 |
| 20030004563 | Jackson et al. | Jan 2003 | A1 |
| 20030031699 | Van Antwerp | Feb 2003 | A1 |
| 20030040771 | Hyodoh et al. | Feb 2003 | A1 |
| 20030040772 | Hyodoh et al. | Feb 2003 | A1 |
| 20030045924 | Datta et al. | Mar 2003 | A1 |
| 20030050678 | Sierra et al. | Mar 2003 | A1 |
| 20030050687 | Schwade et al. | Mar 2003 | A1 |
| 20030060836 | Wang et al. | Mar 2003 | A1 |
| 20030069629 | Jadhav et al. | Apr 2003 | A1 |
| 20030139765 | Patel et al. | Jul 2003 | A1 |
| 20030144730 | Datta et al. | Jul 2003 | A1 |
| 20030149475 | Hyodoh et al. | Aug 2003 | A1 |
| 20030153945 | Patel et al. | Aug 2003 | A1 |
| 20030157241 | Hossainy et al. | Aug 2003 | A1 |
| 20030163159 | Patel et al. | Aug 2003 | A1 |
| 20030176888 | O'Connell | Sep 2003 | A1 |
| 20030195628 | Bao et al. | Oct 2003 | A1 |
| 20030199918 | Patel et al. | Oct 2003 | A1 |
| 20030208227 | Thomas | Nov 2003 | A1 |
| 20030208259 | Penhasi | Nov 2003 | A1 |
| 20030216804 | DeBeer et al. | Nov 2003 | A1 |
| 20030225447 | Majercak et al. | Dec 2003 | A1 |
| 20040015187 | Lendlein et al. | Jan 2004 | A1 |
| 20040030377 | Dubson et al. | Feb 2004 | A1 |
| 20040033251 | Sparer et al. | Feb 2004 | A1 |
| 20040034403 | Schmitt | Feb 2004 | A1 |
| 20040034405 | Dickson | Feb 2004 | A1 |
| 20040047909 | Ragheb et al. | Mar 2004 | A1 |
| 20040086542 | Hossainy et al. | May 2004 | A1 |
| 20040113306 | Rapacki et al. | Jun 2004 | A1 |
| 20040127932 | Shah | Jul 2004 | A1 |
| 20040127970 | Saunders et al. | Jul 2004 | A1 |
| 20040127978 | Sparer et al. | Jul 2004 | A1 |
| 20040158276 | Barbut et al. | Aug 2004 | A1 |
| 20040162576 | Barbut et al. | Aug 2004 | A1 |
| 20040164030 | Lowe et al. | Aug 2004 | A1 |
| 20040170685 | Carpenter et al. | Sep 2004 | A1 |
| 20050004654 | Khosravi et al. | Jan 2005 | A1 |
| 20050004684 | Cribbs | Jan 2005 | A1 |
| 20050010170 | Shanley et al. | Jan 2005 | A1 |
| 20050010275 | Sahatjian et al. | Jan 2005 | A1 |
| 20050012171 | Hiyama | Jan 2005 | A1 |
| 20050021131 | Venkatraman et al. | Jan 2005 | A1 |
| 20050038505 | Shulze et al. | Feb 2005 | A1 |
| 20050100577 | Parker et al. | May 2005 | A1 |
| 20050112171 | Tang et al. | May 2005 | A1 |
| 20050143817 | Hunter et al. | Jun 2005 | A1 |
| 20050154451 | Hezi-Yamit et al. | Jul 2005 | A1 |
| 20050154452 | Hezi-Yamit et al. | Jul 2005 | A1 |
| 20050154455 | Hezi-Yamit et al. | Jul 2005 | A1 |
| 20050177246 | Datta et al. | Aug 2005 | A1 |
| 20050187608 | O'Hara | Aug 2005 | A1 |
| 20050233061 | Schwarz | Oct 2005 | A1 |
| 20050254451 | Grosbach | Nov 2005 | A1 |
| 20050254455 | Plehn et al. | Nov 2005 | A1 |
| 20060020330 | Huang et al. | Jan 2006 | A1 |
| 20060024373 | Shahar et al. | Feb 2006 | A1 |
| 20060025852 | Armstrong et al. | Feb 2006 | A1 |
| 20060036316 | Zeltinger et al. | Feb 2006 | A1 |
| 20060041271 | Bosma et al. | Feb 2006 | A1 |
| 20060045901 | Weber | Mar 2006 | A1 |
| 20060051390 | Schwarz | Mar 2006 | A1 |
| 20060051394 | Moore et al. | Mar 2006 | A1 |
| 20060052859 | Igaki | Mar 2006 | A1 |
| 20060058832 | Melzer et al. | Mar 2006 | A1 |
| 20060058863 | LaFont et al. | Mar 2006 | A1 |
| 20060063316 | Yamagata et al. | Mar 2006 | A1 |
| 20060067974 | Labrecque et al. | Mar 2006 | A1 |
| 20060069427 | Savage et al. | Mar 2006 | A1 |
| 20060076708 | Huang et al. | Apr 2006 | A1 |
| 20060085062 | Lee et al. | Apr 2006 | A1 |
| 20060122522 | Chavan et al. | Jun 2006 | A1 |
| 20060122686 | Gilad et al. | Jun 2006 | A1 |
| 20060136043 | Cully et al. | Jun 2006 | A1 |
| 20060142736 | Hissink et al. | Jun 2006 | A1 |
| 20060147491 | DeWitt et al. | Jul 2006 | A1 |
| 20060149365 | Fifer et al. | Jul 2006 | A1 |
| 20060193891 | Richard | Aug 2006 | A1 |
| 20060212064 | Shah | Sep 2006 | A1 |
| 20060229660 | Pal et al. | Oct 2006 | A1 |
| 20060229711 | Yan et al. | Oct 2006 | A1 |
| 20060241675 | Johnson et al. | Oct 2006 | A1 |
| 20060241676 | Johnson et al. | Oct 2006 | A1 |
| 20060241677 | Johnson et al. | Oct 2006 | A1 |
| 20060241678 | Johnson et al. | Oct 2006 | A1 |
| 20060241679 | Johnson et al. | Oct 2006 | A1 |
| 20060241680 | Johnson et al. | Oct 2006 | A1 |
| 20060248871 | Johnson et al. | Nov 2006 | A1 |
| 20060259133 | Sowinski et al. | Nov 2006 | A1 |
| 20060287715 | Atladottir et al. | Dec 2006 | A1 |
| 20070032816 | O'Connell et al. | Feb 2007 | A1 |
| 20070038226 | Galdonik et al. | Feb 2007 | A1 |
| 20070038241 | Pal | Feb 2007 | A1 |
| 20070038290 | Huang et al. | Feb 2007 | A1 |
| 20070050018 | Wainwright | Mar 2007 | A1 |
| 20070078513 | Campbell | Apr 2007 | A1 |
| 20070088383 | Pal et al. | Apr 2007 | A1 |
| 20070100430 | Rudakov et al. | May 2007 | A1 |
| 20070106361 | Epstein | May 2007 | A1 |
| 20070110889 | Sundar | May 2007 | A1 |
| 20070182041 | Rizk et al. | Aug 2007 | A1 |
| 20070185561 | Schmitz et al. | Aug 2007 | A1 |
| 20070202046 | Dave | Aug 2007 | A1 |
| 20070207186 | Scanlon et al. | Sep 2007 | A1 |
| 20070250153 | Cully et al. | Oct 2007 | A1 |
| 20070281117 | Kaplan et al. | Dec 2007 | A1 |
| 20070283552 | Gale et al. | Dec 2007 | A1 |
| 20070299510 | Venkatraman et al. | Dec 2007 | A1 |
| 20080051866 | Chen et al. | Feb 2008 | A1 |
| 20080091275 | Ducharme | Apr 2008 | A1 |
| 20080097620 | Venkatraman et al. | Apr 2008 | A1 |
| 20080103584 | Su et al. | May 2008 | A1 |
| 20080138375 | Yan et al. | Jun 2008 | A1 |
| 20080177373 | Huang et al. | Jul 2008 | A1 |
| 20080177374 | Zheng et al. | Jul 2008 | A1 |
| 20080208321 | Venkatraran et al. | Aug 2008 | A1 |
| 20080234309 | Yan et al. | Sep 2008 | A1 |
| 20090228094 | Yan et al. | Sep 2009 | A1 |
| 20090319028 | Ramzipoor et al. | Dec 2009 | A1 |
| 20100004734 | Ramzipoor et al. | Jan 2010 | A1 |
| 20100069946 | Cromack et al. | Mar 2010 | A1 |
| 20100086579 | Yan et al. | Apr 2010 | A1 |
| 20100130965 | Sibbitt et al. | May 2010 | A1 |
| 20110097364 | Yan et al. | Apr 2011 | A1 |
| 20120046756 | Wang et al. | Feb 2012 | A1 |
| 20120071500 | Yan et al. | Mar 2012 | A1 |
| 20120071962 | Huang et al. | Mar 2012 | A1 |
| 20120093891 | Yan et al. | Apr 2012 | A1 |
| 20120094932 | Yan et al. | Apr 2012 | A1 |
| 20120187606 | Zheng et al. | Jul 2012 | A1 |
| 20120226345 | Zheng et al. | Sep 2012 | A1 |
| 20120232643 | Ramzipoor et al. | Sep 2012 | A1 |
| 20120271396 | Zheng et al. | Oct 2012 | A1 |
| 20130026681 | Kleiner et al. | Jan 2013 | A1 |
| 20130035753 | Chen et al. | Feb 2013 | A1 |
| 20130150943 | Zheng et al. | Jun 2013 | A1 |
| 20130230571 | Yan et al. | Sep 2013 | A1 |
| 20130331927 | Zheng et al. | Dec 2013 | A1 |
| 20140039600 | Ramzipoor et al. | Feb 2014 | A1 |
| 20140188243 | Zheng et al. | Jul 2014 | A1 |
| 20140236285 | Ramzipoor et al. | Aug 2014 | A1 |
| 20170014250 | Kleiner | Jan 2017 | A1 |
| 20170157806 | Ramzipoor et al. | Jun 2017 | A1 |
| 20170281832 | Ramzipoor et al. | Oct 2017 | A1 |
| Number | Date | Country |
|---|---|---|
| 101621971 | Jan 2010 | CN |
| 4030998 | Apr 1991 | DE |
| 0894505 | Feb 1999 | EP |
| 0754017 | Jun 2002 | EP |
| 1287790 | Mar 2003 | EP |
| 1301221 | Apr 2003 | EP |
| 1372530 | Jan 2004 | EP |
| 1639962 | Mar 2006 | EP |
| 1977721 | Oct 2008 | EP |
| 2322118 | May 2011 | EP |
| 2355755 | Aug 2011 | EP |
| 2493419 | Sep 2012 | EP |
| 11-188110 | Jul 1999 | JP |
| 2002-525166 | Aug 2002 | JP |
| 2005-525170 | Aug 2005 | JP |
| 2007-517587 | Jul 2007 | JP |
| 2009-507528 | Feb 2009 | JP |
| WO 1997017100 | May 1997 | WO |
| WO 1997042879 | Nov 1997 | WO |
| WO 1998046297 | Oct 1998 | WO |
| WO 1999042528 | Aug 1999 | WO |
| WO 1999065420 | Dec 1999 | WO |
| WO 2000018328 | Apr 2000 | WO |
| WO 2000044308 | Aug 2000 | WO |
| WO 2000066031 | Nov 2000 | WO |
| WO 2001001886 | Jan 2001 | WO |
| WO 2001010342 | Feb 2001 | WO |
| WO 2001028454 | Apr 2001 | WO |
| WO 2002011812 | Feb 2002 | WO |
| WO 2002036045 | May 2002 | WO |
| WO 2002076340 | Oct 2002 | WO |
| WO 2003094796 | Nov 2003 | WO |
| WO 2004110315 | Dec 2004 | WO |
| WO 2005002646 | Jan 2005 | WO |
| WO 2005004249 | Jan 2005 | WO |
| WO 2005070335 | Aug 2005 | WO |
| WO 2005077303 | Aug 2005 | WO |
| WO 2005079301 | Sep 2005 | WO |
| WO 2006009883 | Jan 2006 | WO |
| WO 2006015161 | Feb 2006 | WO |
| WO 2006019634 | Feb 2006 | WO |
| WO 2006020425 | Feb 2006 | WO |
| WO 2006020616 | Feb 2006 | WO |
| WO 2006029012 | Mar 2006 | WO |
| WO 2006036982 | Apr 2006 | WO |
| WO 2006068981 | Jun 2006 | WO |
| WO 2006074163 | Jul 2006 | WO |
| WO 2006093608 | Sep 2006 | WO |
| WO 2006107939 | Oct 2006 | WO |
| WO 2007140320 | Dec 2007 | WO |
| WO 2008089434 | Jul 2008 | WO |
| WO 2007021558 | Sep 2008 | WO |
| WO 2009020797 | Feb 2009 | WO |
| WO 2009155560 | Dec 2009 | WO |
| WO 2010030928 | Mar 2010 | WO |
| WO 2010031050 | Mar 2010 | WO |
| WO 2000013737 | Jul 2010 | WO |
| WO 2010120583 | Oct 2010 | WO |
| WO 2011050979 | May 2011 | WO |
| WO 2012024328 | Feb 2012 | WO |
| WO 2012148452 | Nov 2012 | WO |
| WO 2013019726 | Jul 2013 | WO |
| Entry |
|---|
| De Scheerder et al., “Biocompatibility of polymer-coated oversized metallic stents implanted in normal porcine coronary arteries,” Atherosclerosis, vol. 114(1) pp. 105-114, Apr. 7, 1995. |
| Eliaz et al., “Characterization of a polymeric PLGA-injectable implant delivery system for the controlled release of proteins”; J. Biomed. Mater. Res., vol. 50(3), pp. 388-396, Jun. 5, 2000. |
| Kim et al., “Nonthrombogenic polymers: pharmaceutical approaches,” Am Soc Artif Intern Organs J, vol. 6, pp. 76-87, 1983. |
| Kruzynska-Frejtag et al., “Periostin is expressed within the developing teeth at the sites of epithelial-mesenchymal interaction”, Dev. Dyn., vol. 229(4), pp. 857-868, Apr. 2004. |
| Merrill et al., “Properties of materials affecting the behavior of blood at their surfaces,” Ann NY Acad Sci, vol. 283, pp. 6-16, Feb. 1977. |
| Petas et al., “Effects of biodegradable self-reinforced polyglycolic acid, poly-DL-lactic acid and stainless-steel spiral stents on uroepithelium after Nd:YAG laser irradiation of the canine prostate,” BR J. Urol., vol. 80(6), pp. 903-907, Dec. 1997. |
| Rafanan “Stenting of the tracheobronchial tree,” Radiol Clin North Am., vol. 38(2), pp. 395-408, Mar. 2000. |
| Schellhammer et al., “Poly-Lactic-Acid Coating for Endovascular Stents: Preliminary Results in Canine Experimental Arteriovenous Fistulae [Preliminary Report],”Invest Radiol., vol. 32(3), pp. 180-186, Mar. 1997. |
| Sofia Poly(Ethylene Glycol) Chemistry and Biological Applications, Ch. 22, pp. 342-360, American Chemical Society, vol. 680, Aug. 1997. |
| Szycher “Review of Cardiovascular Devices,” J. Biomat Appln, vol. 12, pp. 321-364, 1998. |
| Tamai et al, “Initial and 6-Month Results of Biodegradable Poly-I-Lactic Acid Coronary Stents in Humans,” Circulation, vol. 102(4), pp. 399-404, Jul. 25, 2000. |
| Tan et al., “Effect of plasticization on heparin release from biodegradable matrices”, Int. J. Pharm., vol. 283(102), pp. 89-96, Sep. 28, 2004. |
| Webb et al., “Relative importance of surface wettability and charged functional groups on NIH 3T3 fibroblast attachment, spreading, and cytoskeletal organization”, J. Biomed Mat Res, vol. 41(3), pp. 422-430, Sep. 5, 1998. |
| Middleton et al., “Synthetic biodegradable polymers as orthopedic devices”, Biomaterials 2000, vol. 21, pp. 2335-2346. |
| Number | Date | Country | |
|---|---|---|---|
| 20120232644 A1 | Sep 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12488453 | Jun 2009 | US |
| Child | 13476858 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12143659 | Jun 2008 | US |
| Child | 12488453 | US |