Patent Grant
8206635
The present invention relates generally to manufacturing processes for forming or creating devices which are implantable within a patient, such as medical devices. More particularly, the present invention relates to methods and processes for forming or creating tubular substrates which may be further processed to create medical devices having various geometries suitable for implantation within a patient.
In recent years there has been growing interest in the use of artificial materials, particularly materials formed from polymers, for use in implantable devices that come into contact with bodily tissues or fluids particularly blood. Some examples of such devices are artificial heart valves, stents, and vascular prosthesis. Some medical devices such as implantable stents which are fabricated from a metal have been problematic in fracturing or failing after implantation. Moreover, certain other implantable devices made from polymers have exhibited problems such as increased wall thickness to prevent or inhibit fracture or failure. However, stents having reduced wall thickness are desirable particularly for treating arterial diseases.
Because many polymeric implants such as stents are fabricated through processes such as extrusion or injection molding, such methods typically begin the process by starting with an inherently weak material. In the example of a polymeric stent, the resulting stent may have imprecise geometric tolerances as well as reduced wall thicknesses which may make these stents susceptible to brittle fracture.
A stent which is susceptible to brittle fracture is generally undesirable because of its limited ability to collapse for intravascular delivery as well as its limited ability to expand for placement or positioning within a vessel. Moreover, such polymeric stents also exhibit a reduced level of strength. Brittle fracture is particularly problematic in stents as placement of a stent onto a delivery balloon or within a delivery sheath imparts a substantial amount of compressive force in the material comprising the stent. A stent made of a brittle material may crack or have a very limited ability to collapse or expand without failure. Thus, a certain degree of malleability is desirable for a stent to expand, deform, and maintain its position securely within the vessel.
Accordingly, it is desirable to produce a polymeric substrate having one or more layers which retains its mechanical strength and is sufficiently ductile so as to prevent or inhibit brittle fracture, particularly when utilized as a biocompatible and/or bioabsorbable polymeric stent for implantation within a patient body.
A number of casting processes described herein may be utilized to develop substrates, e.g., cylindrically shaped substrates, having a relatively high level of geometric precision and mechanical strength. These polymeric substrates can then be machined using any number of processes (e.g., high-speed laser sources, mechanical machining, etc.) to create devices such as stents having a variety of geometries for implantation within a patient, such as the peripheral or coronary vasculature, etc.
An example of such a casting process is to utilize a dip-coating process. The utilization of dip-coating to create a polymeric substrate having such desirable characteristics results in substrates which are able to retain the inherent properties of the starting materials. This in turn results in substrates having a relatively high radial strength which is retained through any additional manufacturing processes for implantation. Additionally, dip-coating the polymeric substrate also allows for the creation of substrates having multiple layers.
The molecular weight of a polymer is typically one of the factors in determining the mechanical behavior of the polymer. With an increase in the molecular weight of a polymer, there is generally a transition from brittle to ductile failure. A mandrel may be utilized to cast or dip-coat the polymeric substrate.
In dip-coating the polymeric substrate, one or more high molecular weight biocompatible and/or bioabsorbable polymers may be selected for forming upon the mandrel. The one or more polymers may be dissolved in a compatible solvent in one or more corresponding containers such that the appropriate solution may be placed under the mandrel. As the substrate may be formed to have one or more layers overlaid upon one another, the substrate may be formed to have a first layer of a first polymer, a second layer of a second polymer, and so on depending upon the desired structure and properties of the substrate. Thus, the various solutions and containers may be replaced beneath the mandrel between dip-coating operations in accordance with the desired layers to be formed upon the substrate such that the mandrel may be dipped sequentially into the appropriate polymeric solution.
Parameters such as the number of times the mandrel is immersed, the sequence and direction of dipping, the duration of time of each immersion within the solution, as well as the delay time between each immersion or the drying or curing time between dips and dipping and/or withdrawal rates of the mandrel to and/or from the solution may each be controlled to result in the desired mechanical characteristics. Formation via the dip-coating process may result in a polymeric substrate having half the wall thickness while retaining an increased level of strength in the substrate as compared to an extruded polymeric structure.
The immersion times as well as drying times may be uniform between each immersion or they may be varied as determined by the desired properties of the resulting substrate. Moreover, the substrate may be placed in an oven or dried at ambient temperature between each immersion or after the final immersion to attain a predetermined level of crystals, e.g., 60%, and a level of amorphous polymeric structure, e.g., 40%. Each of the layers overlaid upon one another during the dip-coating process are tightly adhered to one another and the wall thicknesses and mechanical properties of each polymer are retained in their respective layer with no limitation on the molecular weight and/or crystalline structure of the polymers utilized.
Dip-coating can be used to impart an orientation between layers (e.g., linear orientation by dipping; radial orientation by spinning the mandrel; etc.) to further enhance the mechanical properties of the formed substrate. As radial strength is a desirable attribute of stent design, post-processing of the formed substrate may be accomplished to impart such attributes. Typically, polymeric stents suffer from having relatively thick walls to compensate for the lack of radial strength, and this in turn reduces flexibility, impedes navigation, and reduces arterial luminal area immediately post implantation. Post-processing may also help to prevent material creep and recoil (creep is a time-dependent permanent deformation that occurs to a specimen under stress, typically under elevated temperatures) which are problems typically associated with polymeric stents.
For post-processing, a predetermined amount of force may be applied to the substrate where such a force may be generated by a number of different methods. One method is by utilizing an expandable pressure vessel placed within the substrate. Another method is by utilizing a braid structure, such as a braid made from a super-elastic or shape memory alloy like NiTi alloy, to increase in size and to apply the desirable degree of force against the interior surface of the substrate.
Yet another method may apply the expansion force by application of a pressurized inert gas such as nitrogen within the substrate lumen. A completed substrate may be placed inside a molding tube which has an inner diameter that is larger than the cast cylinder. A distal end or distal portion of the cast cylinder may be clamped or otherwise closed and a pressure source may be coupled to a proximal end of the cast cylinder. The entire assembly may be positioned over a nozzle which applies heat to either the length of the cast cylinder or to a portion of cast cylinder. The increase in diameter of the cast cylinder may thus realign the molecular orientation of the cast cylinder to increase its radial strength. After the diameter has been increased, the cast cylinder may be cooled.
Once the processing has been completed on the polymeric substrate, the substrate may be further formed or machined to create a variety of device. One example includes stents created from the cast cylinder by cutting along a length of the cylinder to create a rolled stent for delivery and deployment within the patient vasculature. Another example includes machining a number of portions to create a lattice or scaffold structure which facilitates the compression and expansion of the stent.
In other variations, in forming the stent, the substrate may be first formed at a first diameter, as described herein by immersing a mandrel into at least a first polymeric solution such that at least a first layer of a biocompatible polymer substrate is formed upon the mandrel and has a first diameter defined by the mandrel. In forming the substrate, parameters such as controlling a number of immersions of the mandrel into the first polymeric solution, controlling a duration of time of each immersion of the mandrel, and controlling a delay time between each immersion of the mandrel are controlled. With the substrate initially formed, the first diameter of the substrate may be reduced to a second smaller diameter and processed to form an expandable stent scaffold configured for delivery and deployment within a vessel, wherein the stent scaffold retains one or more mechanical properties of the polymer resin such that the stent scaffold exhibits ductility upon application of a load.
With the stent scaffold formed and heat set to have an initial diameter, it may be reduced to a second delivery diameter and placed upon a delivery catheter for intravascular delivery within a patient body comprising positioning the stent having the second diameter at a target location within the vessel, expanding the stent to a third diameter that is larger than the second diameter (and possibly smaller than the initial diameter) at the target location utilizing an inflation balloon or other mechanism, and allowing the stent to then self-expand into further contact with the vessel at the target location such that the stent self-expands over time back to its initial diameter or until it is constrained from further expansion by the vessel walls.
In manufacturing implantable devices from polymeric materials such as biocompatible and/or biodegradable polymers, a number of casting processes described herein may be utilized to develop substrates, e.g., cylindrically shaped substrates, having a relatively high level of geometric precision and mechanical strength. These polymeric substrates can then be machined using any number of processes (e.g., high-speed laser sources, mechanical machining, etc.) to create devices such as stents having a variety of geometries for implantation within a patient, such as the peripheral or coronary vasculature, etc.
An example of such a casting process is to utilize a dip-coating process. The utilization of dip-coating to create a polymeric substrate having such desirable characteristics results in substrates which are able to retain the inherent properties of the starting materials. This in turn results in substrates having a relatively high radial strength which is mostly retained through any additional manufacturing processes for implantation. Additionally, dip-coating the polymeric substrate also allows for the creation of substrates having multiple layers. The multiple layers may be formed from the same or similar materials or they may be varied to include any number of additional agents, such as one or more drugs for treatment of the vessel, as described in further detail below. Moreover, the variability of utilizing multiple layers for the substrate may allow one to control other parameters, conditions, or ranges between individual layers such as varying the degradation rate between layers while maintaining the intrinsic molecular weight and mechanical strength of the polymer at a high level with minimal degradation of the starting materials.
Because of the retention of molecular weight and mechanical strength of the starting materials via the casting or dip-coating process, polymeric substrates may be formed which enable the fabrication of devices such as stents with reduced wall thickness which is highly desirable for the treatment of arterial diseases. Furthermore these processes may produce structures having precise geometric tolerances with respect to wall thicknesses, concentricity, diameter, etc.
One mechanical property in particular which is generally problematic with, e.g., polymeric stents formed from polymeric substrates, is failure via brittle fracture of the device when placed under stress within the patient body. It is generally desirable for polymeric stents to exhibit ductile failure under an applied load rather via brittle failure, especially during delivery and deployment of a polymeric stent from an inflation balloon or constraining sheath, as mentioned above. Percent (%) ductility is generally a measure of the degree of plastic deformation that has been sustained by the material at fracture. A material that experiences very little or no plastic deformation upon fracture is brittle.
The molecular weight of a polymer is typically one of the factors in determining the mechanical behavior of the polymer. With an increase in the molecular weight of a polymer, there is generally a transition from brittle to ductile failure. An example is illustrated in the stress-strain plot 10 which illustrate the differing mechanical behavior resulting from an increase in molecular weight. The stress-strain curve 12 of a sample of polylactic acid (PLLA) 2.4 shows a failure point 18 having a relatively low tensile strain percentage at a high tensile stress level indicating brittle failure. A sample of PLLA 4.3, which has a relatively higher molecular weight than PLLA 2.4, illustrates a stress-strain curve 14 which has a region of plastic failure 20 after the onset of yielding and a failure point 22 which has a relatively lower tensile stress value at a relatively higher tensile strain percentage indicating a degree of ductility. Yield occurs when a material initially departs from the linearity of a stress-strain curve and experiences an elastic-plastic transition.
A sample of PLLA 8.4, which has yet a higher molecular weight than PLLA 4.3, illustrates a stress-strain curve 16 which has a longer region of plastic failure 24 after the onset of yielding. The failure point 26 also has a relatively lower tensile stress value at a relatively higher tensile strain percentage indicating a degree of ductility. Thus, a high-strength tubular material which exhibits a relatively high degree of ductility may be fabricated utilizing polymers having a relatively high molecular weight (e.g., PLLA 8.4, PLLA with 8.28 IV, etc.). Such a tubular material may be processed via any number of machining processes to form an implantable device such as a stent which exhibits a stress-strain curve which is associated with the casting or dip-coating process described herein.
An example of a mandrel which may be utilized to cast or dip-coat the polymeric substrate is illustrated in the side view of
The assembly 30 may be isolated on a vibration-damping or vibrationally isolated table to ensure that the liquid surface held within container 44 remains completely undisturbed to facilitate the formation of a uniform thickness of polymer material along mandrel 40 and/or substrate 50 with each deposition The entire assembly 30 or just a portion of the assembly such as the mandrel 40 and polymer solution may be placed in an inert environment such as a nitrogen gas environment while maintaining a very low relative humidity (RH) level, e.g., less than 30% RH, and appropriate dipping temperature, e.g., at least 20° C. below the boiling point of the solvent within container 44 so as to ensure adequate bonding between layers of the dip-coated substrate. Multiple mandrels may also be mounted along bracket arm 38 or directly to column 34.
The mandrel 40 may be sized appropriately and define a cross-sectional geometry to impart a desired shape and size to the substrate 50. Mandrel 40 may be generally circular in cross section although geometries may be utilized as desired. In one example, mandrel 40 may define a circular geometry having a diameter ranging from 1 mm to 20 mm to form a polymeric substrate having a corresponding inner diameter. Moreover, mandrel 40 may be made generally from various materials which are suitable to withstand dip-coating processes, e.g., stainless steel, copper, aluminum, silver, brass, nickel, titanium, etc. The length of mandrel 40 that is dipped into the polymer solution may be optionally limited in length by, e.g., 50 cm, to ensure that an even coat of polymer is formed along the dipped length of mandrel 40 to limit the effects of gravity during the coating process. Mandrel 40 may also be made from a polymeric material which is lubricious, strong, has good dimensional stability, and is chemically resistant to the polymer solution utilized for dip-coating, e.g., fluoropolymers, polyacetal, polyester, polyamide, polyacrylates, etc.
Moreover, mandrel 40 may be made to have a smooth surface for the polymeric solution to form upon. In other variations, mandrel 40 may define a surface that is coated with a material such as polytetrafluroethylene to enhance removal of the polymeric substrate formed thereon. In yet other variations, mandrel 40 may be configured to define any number of patterns over its surface, e.g., either over its entire length or just a portion of its surface, that can be mold-transferred during the dip-coating process to the inner surface of the first layer of coating of the dip-coated substrate tube. The patterns may form raised or depressed sections to form various patterns such as checkered, cross-hatched, cratered, etc. that may enhance endothelialization with the surrounding tissue after the device is implanted within a patient, e.g., within three months or of implantation.
The direction that mandrel 40 is dipped within polymeric solution 46 may also be alternated or changed between layers of substrate 50. In forming substrates having a length ranging from, e.g., 1 cm to 40 cm or longer, substrate 50 may be removed from mandrel 40 and replaced onto mandrel 40 in an opposite direction before the dipping process is continued. Alternatively, mandrel 40 may be angled relative to bracket arm 38 and/or polymeric solution 46 during or prior to the dipping process.
This may also be accomplished in yet another variation by utilizing a dipping assembly as illustrated in
Dipping mandrel 40 and substrate 50 in different directions may also enable the coated layers to have a uniform thickness throughout from its proximal end to its distal end to help compensate for the effects of gravity during the coating process. These values are intended to be illustrative and are not intended to be limiting in any manner. Any excess dip-coated layers on the linkages 56, 58 may simply be removed from mandrel 40 by breaking the layers. Alternating the dipping direction may also result in the polymers being oriented alternately which may reinforce the tensile strength in the axial direction of the dip coated tubular substrate 50.
With dip-coating assembly 30, one or more high molecular weight biocompatible and/or bioabsorbable polymers may be selected for forming upon mandrel 40. Examples of polymers which may be utilized to form the polymeric substrate may include, but is not limited to, polyethylene, polycarbonates, polyamides, polyesteramides, polyetheretherketone, polyacetals, polyketals, polyurethane, polyolefin, or polyethylene terephthalate and degradable polymers, for example, polylactide (PLA) including poly-L-lactide (PLLA), poly-glycolide (PGA), poly(lactide-co-glycolide) (PLGA) or polycaprolactone, caprolactones, polydioxanones, polyanhydrides, polyorthocarbonates, polyphospliazenes, chitin, chitosan, poly(amino acids), and polyorthoesters, and copolymers, terpolymers and combinations and mixtures thereof.
Other examples of suitable polymers may include synthetic polymers, for example, oligomers, homopolymers, and co-polymers, acrylics such as those polymerized from methyl cerylate, methyl methacrylate, acrylic acid, methacrylic acid, acrylamide, hydroxyethy acrylate, hydroxyethyl methacrylate, glyceryl scrylate, glyceryl methacrylate, methacrylamide and ethacrylamide; vinyls such as styrene, vinyl chloride, binaly pyrrolidone, polyvinyl alcohol, and vinyls acetate; polymers formed of ethylene, propylene, and tetrfluoroethylene. Further examples may include nylons such as polycoprolactam, polylauryl lactam, polyjexamethylene adipamide, and polyexamethylene dodecanediamide, and also polyurethanes, polycarbonates, polyamides, polysulfones, poly(ethylene terephthalate), polyactic acid, polyglycolic acid, polydimethylsiloxanes, and polyetherketones.
Examples of biodegradable polymers which can be used for dip-coating process are polylactide (PLA), polyglycolide (PGA), poly(lactide-co-glycolide) (PLGA), poly(e-caprolactone), polydioxanone, polyanhydride, trimethylene carbonate, poly(β-hydroxybutyrate), poly(g-ethyl glutamate), poly(DTH iminocarbonate), poly(bisphenol A iminocarbonate), poly(ortho ester), polycyanoacrylate, and polyphosphazene, and copolymers, terpolymers and combinations and mixtures thereof. There are also a number of biodegradable polymers derived from natural sources such as modified polysaccharides (cellulose, chitin, chitosan, dextran) or modified proteins (fibrin, casein).
Other examples of suitable polymers may include synthetic polymers, for example, oligomers, homopolymers, and co-polymers, acrylics such as those polymerized from methyl cerylate, methyl methacrylate, acryli acid, methacrylic acid, acrylamide, hydroxyethy acrylate, hydroxyethyl methacrylate, glyceryl scrylate, glyceryl methacrylate, methacrylamide and ethacrylamide; vinyls such as styrene, vinyl chloride, binaly pyrrolidone, polyvinyl alcohol, and vinyls acetate; polymers formed of ethylene, propylene, and tetrfluoroethylene. Further examples may include nylons such as polycoprolactam, polylauryl lactam, polyjexamethylene adipamide, and polyexamethylene dodecanediamide, and also polyurethanes, polycarbonates, polyamides, polysulfones, poly(ethylene terephthalate), polyacetals, polyketals, polydimethylsiloxanes, and polyetherketones.
These examples of polymers which may be utilized for forming the substrate are not intended to be limiting or exhaustive but are intended to be illustrative of potential polymers which may be used. As the substrate may be formed to have one or more layers overlaid upon one another, the substrate may be formed to have a first layer of a first polymer, a second layer of a second polymer, and so on depending upon the desired structure and properties of the substrate. Thus, the various solutions and containers may be replaced beneath mandrel 40 between dip-coating operations in accordance with the desired layers to be formed upon the substrate such that the mandrel 40 may be dipped sequentially into the appropriate polymeric solution.
Depending upon the desired wall thickness of the formed substrate, the mandrel 40 may be dipped into the appropriate solution as determined by the number of times the mandrel 40 is immersed, the duration of time of each immersion within the solution, as well as the delay time between each immersion or the drying or curing time between dips. Additionally, parameters such as the dipping and/or withdrawal rate of the mandrel 40 from the polymeric solution may also be controlled to range from, e.g., 5 mm/min to 1000 mm/min. Formation via the dip-coating process may result in a polymeric substrate having half the wall thickness while retaining an increased level of strength in the substrate as compared to an extruded polymeric structure. For example, to form a substrate having a wall thickness of, e.g., 200 μm, built up of multiple layers of polylactic acid, mandrel 40 may be dipped between, e.g., 2 to 20 times or more, into the polymeric solution with an immersion time ranging from, e.g., 15 seconds (or less) to 240 minutes (or more. Moreover, the substrate and mandrel 40 may be optionally dried or cured for a period of time ranging from, e.g., 15 seconds (or less) to 60 minutes (or more) between each immersion. These values are intended to be illustrative and are not intended to be limiting in any manner.
Aside from utilizing materials which are relatively high in molecular weight, another parameter which may be considered in further increasing the ductility of the material is its crystallinity, which refers to the degree of structural order in the polymer. Such polymers may contain a mixture of crystalline and amorphous regions where reducing the percentage of the crystalline regions in the polymer may further increase the ductility of the material. Polymeric materials not only having a relatively high molecular weight but also having a relatively low crystalline percentage may be utilized in the processes described herein to form a desirable tubular substrate.
The following Table 1 show examples of various polymeric materials (e.g., PLLA IV 8.28 and PDLLA 96/4) to illustrate the molecular weights of the materials in comparison to their respective crystallinity percentage. The glass transition temperature, Tg, as well as melting temperature, Tm, are given as well. An example of PLLA IV 8.28 is shown illustrating the raw resin and tube form as having the same molecular weight, Mw, of 1.70×106 gram/mol. However, the crystallinity percentage of PLLA IV 8.28 Resin is 61.90% while the corresponding Tube form is 38.40%. Similarly for PDLLA 96/4, the resin form and tube form each have a molecular weight, Mw, of 9.80×105 gram/mol; however, the crystallinity percentages are 46.20% and 20.90%, respectively.
As the resin is dip coated to form the tubular substrate through the methods described herein, the drying procedures and processing helps to preserve the relatively high molecular weight of the polymer from the starting material and throughout processing to substrate and stent formation. Moreover, the drying processes in particular may facilitate the formation of desirable crystallinity percentages, as described above.
Aside from the crystallinity of the materials, the immersion times as well as drying times may be uniform between each immersion or they may be varied as determined by the desired properties of the resulting substrate. Moreover, the substrate may be placed in an oven or dried at ambient temperature between each immersion or after the final immersion to attain a predetermined level of crystals, e.g., 60%, and a level of amorphous polymeric structure, e.g., 40%. Each of the layers overlaid upon one another during the dip-coating process are tightly adhered to one another and the mechanical properties of each polymer are retained in their respective layer with no limitation on the molecular weight of the polymers utilized.
Varying the drying conditions of the materials may also be controlled to effect desirable material parameters. The polymers may be dried at or above the glass transition temperature (e.g., 10° to 20° C. above the glass transition temperature, Tg) of the respective polymer to effectively remove any residual solvents from the polymers to attain residual levels of less than 100 ppm, e.g., between 20 to 100 ppm. Positioning of the polymer substrate when drying is another factor which may be controlled as affecting parameters, such as geometry, of the tube. For instance, the polymer substrate may be maintained in a drying position such that the substrate tube is held in a perpendicular position relative to the ground such that the concentricity of the tubes is maintained. The substrate tube may be dried in an oven at or above the glass transition temperature, as mentioned, for a period of time ranging anywhere from, e.g., 10 days to 30 days or more. However, prolonged drying for a period of time, e.g., greater than 40 days, may result in thermal degradation of the polymer material.
Additionally and/or optionally, a shape memory effect may be induced in the polymer during drying of the substrate. For instance, a shape memory effect may be induced in the polymeric tubing to set the tubular shape at the diameter that was formed during the dip-coating process. An example of this is to form a polymeric tube by a dip-coating process described herein at an outer diameter of 5 mm and subjecting the substrate to temperatures above its glass transition temperature, Tg. At its elevated temperature, the substrate may be elongated, e.g., from a length of 5 cm to 7 cm, while its outer diameter of 5 mm is reduced to 3 mm. Of course, these examples are merely illustrative and the initial diameter may generally range anywhere from, e.g., 3 mm to 9 mm, and the reduced diameter may generally range anywhere from, e.g., 1.5 mm to 5 mm, provided the reduced diameter is less than the initial diameter.
Once lengthened and reduced in diameter, the substrate may be quenched or cooled in temperature to a sub-Tg level, e.g., about 20° C. below its Tg, to allow for the polymeric substrate to transition back to its glass state. This effectively imparts a shape memory effect of self-expansion to the original diameter of the substrate. When such a tube (or stent formed from the tubular substrate) is compressed or expanded to a smaller or larger diameter and later exposed to an elevated temperature, over time the tube (or stent) may revert to its original 5 mm diameter. This post processing may also be useful for enabling self-expansion of the substrate after a process like laser cutting (e.g., when forming stents or other devices for implantation within the patient) where the substrate tube is typically heated to its glass transition temperature, Tg.
An example of a substrate having multiple layers is illustrated in
An example of this is illustrated in the cross-sectional end view of
Moreover, any one or more of the layers may be formed to impart specified mechanical properties to the substrate 50 such that the composite mechanical properties of the resulting substrate 50 may specifically tuned or designed. Additionally, although three layers are illustrated in this example, any number of layers may be utilized depending upon the desired mechanical properties of the substrate 50.
Moreover, as multiple layers may be overlaid one another in forming the polymeric substrate, specified layers may be designated for a particular function in the substrate. For example, in substrates which are used to manufacture polymeric stents, one or more layers may be designed as load-bearing layers to provide structural integrity to the stent while certain other layers may be allocated for drug-loading or eluting. Those layers which are designated for structural support may be formed from high-molecular weight polymers, e.g., PLLA or any other suitable polymer described herein, to provide a high degree of strength by omitting any drugs as certain pharmaceutical agents may adversely affect the mechanical properties of polymers. Those layers which are designated for drug-loading may be placed within, upon, or between the structural layers.
Additionally, multiple layers of different drugs may be loaded within the various layers. The manner and rate of drug release from multiple layers may depend in part upon the degradation rates of the substrate materials. For instance, polymers which degrade relatively quickly may release their drugs layer-by-layer as each successive layer degrades to expose the next underlying layer. In other variations, drug release may typically occur from a multilayer matrix via a combination of diffusion and degradation. In one example, a first layer may elute a first drug for, e.g., the first 30 to 40 days after implantation. Once the first layer has been exhausted or degraded, a second underlying layer having a second drug may release this drug for the next 30 to 40 days, and so on if so desired. In the example of
In other examples, rather than having each successive layer elute its respective drug, each layer 62, 64 (optionally layer 60 as well), may elute its respective drug simultaneously or at differing rates via a combination of diffusion and degradation. Although three layers are illustrated in this example, any number of layers may be utilized with any practicable combination of drugs for delivery. Moreover, the release kinetics of each drug from each layer may be altered in a variety of ways by changing the formulation of the drug-containing layer.
Examples of drugs or agents which may be loaded within certain layers of substrate 50 may include one or more antipoliferative, antineoplastic, antigenic, anti-inflammatory, and/or antirestenotic agents. The therapeutic agents may also include antilipid, antimitotics, metalloproteinase inhabitors, anti-sclerosing agents. Therapeutic agents may also include peptides, enzymes, radio isotopes or agents for a variety of treatment options. This list of drugs or agents is presented to be illustrative and is not intended to be limiting.
Similarly certain other layers may be loaded with radio-opaque substances such as platinum, gold, etc. to enable visibility of the stent under imaging modalities such as fluoroscopic imaging. Radio-opaque substances like tungsten, platinum, gold, etc. can be mixed with the polymeric solution and dip-coated upon the substrate such that the radio-opaque substances form a thin sub-micron thick layer upon the substrate. The radio-opaque substances may thus become embedded within layers that degrade in the final stages of degradation or within the structural layers to facilitate stent visibility under an imaging modality, such as fluoroscopy, throughout the life of the implanted device before fully degrading or losing its mechanical strength. Radio-opaque marker layers can also be dip-coated at one or both ends of substrate 50, e.g., up to 0.5 mm from each respective end. Additionally, the radio-opaque substances can also be spray-coated or cast along a portion of the substrate 50 between its proximal and distal ends in a radial direction by rotating mandrel 40 when any form of radio-opaque substance is to be formed along any section of length of substrate 50. Rings of polymers having radio-opaque markers can also be formed as part of the structure of the substrate 50.
In an experimental example of the ductility and retention of mechanical properties, PLLA with Iv 8.4 (high molecular weight) was obtained and tubular substrates were manufactured utilizing the dip-coating process described herein. The samples were formed to have a diameter of 5 mm with a wall thickness of 200 μm and were comprised of 6 layers of PLLA 8.4. The mandrel was immersed 6 times into the polymeric solution and the substrates were dried or cured in an oven to obtain a 60% crystalline structure. At least two samples of tubular substrates were subjected to tensile testing and stress-strain plot 70 was generated from the stress-strain testing, as shown in
As shown in plot 70, a first sample of PLLA 8.4 generated a stress-strain curve 72 having a region of plastic failure 76 where the strain percentage increased at a relatively constant stress value prior to failure indicating a good degree of sample ductility. A second sample of PLLA 8.4 also generated a stress-strain curve 74 having a relatively greater region of plastic failure 78 also indicating a good degree of sample ductility.
Polymeric stents and other implantable devices made from such substrates may accordingly retain the material properties from the dip-coated polymer materials. The resulting stents, for instance, may exhibit mechanical properties which have a relatively high percentage ductility in radial, torsional, and/or axial directions. An example of this is a resulting stent having an ability to undergo a diameter reduction of anywhere between 5% to 70% when placed under an external load without any resulting plastic deformation. Such a stent may also exhibit high radial strength with, e.g., a 20% radial deformation when placed under a 0.1 N to 20 N load. Such a stent may also be configured to self-expand when exposed to normal body temperatures.
The stent may also exhibit other characteristic mechanical properties which are consistent with a substrate formed as described herein, for instance, high ductility and high strength polymeric substrates. Such substrates (and processed stents) may exhibit additional characteristics such as a percent reduction in diameter of between 5% to 70% without fracture formation when placed under a compressive load as well as a percent reduction in axial length of between 10% to 30% without fracture formation when placed under an axial load. Because of the relatively high ductility, the substrate or stent may also be adapted to curve up to 180° about a 1 cm curvature radius without fracture formation or failure. Additionally, when deployed within a vessel, a stent may also be expanded, e.g., by an inflatable intravascular balloon, by up to 5% to 70% to regain diameter without fracture formation or failure.
These values are intended to illustrate examples of how a polymeric tubing substrate and a resulting stent may be configured to yield a device with certain mechanical properties. Moreover, depending upon the desired results, certain tubes and stents may be tailored for specific requirements of various anatomical locations within a patient body by altering the polymer and/or copolymer blends to adjust various properties such as strength, ductility, degradation rates, etc.
A sample of 96/4 PDLLA was also formed and tested to generate stress-strain curve 75 having a point of failure 75′ which exhibited a relatively lower percent elongation characteristic of brittle fracture. The resulting load at failure was between 100 N to 300 N with an elastic modulus of between 1000 to 3000 MPa, which was similar to the PLLA 8.28 samples. However, the percent elongation was between 10% to 40% at failure.
Dip-coating can be used to impart an orientation between layers (e.g., linear orientation by dipping; radial orientation by spinning the mandrel; etc.) to further enhance the mechanical properties of the formed substrate. As radial strength is a desirable attribute of stent design, post-processing of the formed substrate may be accomplished to impart such attributes. Typically, polymeric stents suffer from having relatively thick walls to compensate for the lack of radial strength, and this in turn reduces flexibility, impedes navigation, and reduces arterial luminal area immediately post implantation. Post-processing may also help to prevent material creep and recoil (creep is a time-dependent permanent deformation that occurs to a specimen under stress, typically under elevated temperatures) which are problems typically associated with polymeric stents.
In further increasing the radial or circumferential strength of the polymeric substrate, a number of additional processes may be applied to the substrate after the dip-coating procedure is completed (or close to being completed). A polymer that is amorphous or that is partially amorphous will generally undergo a transition from a pliable, elastic state (at higher temperatures) to a brittle glass-like state (at lower temperature) as it transitions through a particular temperature, referred as the glass transition temperature (Tg). The glass transition temperature for a given polymer will vary, depending on the size and flexibility of side chains, as well as the flexibility of the backbone linkages and the size of functional groups incorporated into the polymer backbone. Below Tg, the polymer will maintain some flexibility, and may be deformed to a new shape. However, the further the temperature below Tg the polymer is when being deformed, the greater the force needed to shape it.
Moreover, when a polymer is in glass transition temperature its molecular structure can be manipulated to form an orientation in a desired direction. Induced alignment of polymeric chains or orientation improves mechanical properties and behavior of the material. Molecular orientation is typically imparted by application of force while the polymer is in a pliable, elastic state. After sufficient orientation is induced, temperature of the polymer is reduced to prevent reversal and dissipation of the orientation.
In one example, the polymeric substrate may be heated to increase its temperature along its entire length or along a selected portion of the substrate to a temperature that is at or above the Tg of the polymer. For instance, for a substrate fabricated from PLLA, the substrate may be heated to a temperature between 60° C. to 70° C. Once the substrate has reached a sufficient temperature such that enough of its molecules have been mobilized, a force may be applied from within the substrate or along a portion of the substrate to increase its diameter from a first diameter D1 to a second increased diameter D2 for a period of time necessary to set the increased diameter. During this setting period, the application of force induces a molecular orientation in a circumferential direction to align the molecular orientation of polymer chains to enhance its mechanical properties. The re-formed substrate may then be cooled to a lower temperature typically below Tg, for example, by passing the tube through a cold environment, typically dry air or an inert gas to maintain the shape at diameter D2 and prevent dissipation of molecular orientation.
The force applied to the substrate may be generated by a number of different methods. One method is by utilizing an expandable pressure vessel placed within the substrate. Another method is by utilizing a braid structure, such as a braid made from a super-elastic or shape memory alloy like NiTi alloy, to increase in size and to apply the desirable degree of force against the interior surface of the substrate.
Yet another method may apply the expansion force by application of a pressurized inert gas such as nitrogen within the substrate lumen, as shown in
A distal end or distal portion of cast cylinder 94 may be clamped 96 or otherwise closed and a pressure source may be coupled to a proximal end 98 of cast cylinder 94. The entire assembly may be positioned over a nozzle 102 which applies heat 104 to either the length of cast cylinder 94 or to a portion of cast cylinder 94. The pressurized inert gas 100, e.g., pressured to 10 to 400 psi, may be introduced within cast cylinder 94 to increase its diameter, e.g., 2 mm, to that of the inner diameter, e.g., 4 mm, of molding tube 90. The increase in diameter of cast cylinder 94 may thus realign the molecular orientation of cast cylinder 94 to increase its radial strength and to impart a circumferential orientation in the cast cylinder 94. Portion 92 illustrates radial expansion of the cast cylinder 94 against the inner surface of the molding tube 90 in an exaggerated manner to illustrate the radial expansion and impartation of circumferential strength. After the diameter has been increased, cast cylinder 94 may be cooled, as described above.
Once the substrate has been formed and reduced in diameter to its smaller second diameter, the stent may be processed, as described above. Alternatively, the stent may be processed from the substrate after initial formation. The stent itself may then be reduced in diameter to its second reduced diameter.
In either case, once the stent has been formed into its second reduced diameter, the stent may be delivered to a targeted location within a vessel of a patient. Delivery may be effected intravascularly utilizing known techniques with the stent in its second reduced delivery diameter positioned upon, e.g., an inflation balloon, for intravascular delivery. Once the inflation catheter and stent has been positioned adjacent to the targeted region of vessel, the stent may be initially expanded into contact against the interior surface of the vessel.
With the stent expanded into contact against the vessel wall at a third diameter which is larger than the second delivery diameter, the inflation balloon may be removed from the stent. Over a predetermined period of time and given the structural characteristics of the stent, the stent may then also self-expand further into contact against the vessel wall for secure placement and positioning.
Because thermoplastic polymers such as PLLA typically soften when heated, the cast cylinder 94 or a portion of the cast cylinder 94 may be heated in an inert environment, e.g., a nitrogen gas environment, to minimize its degradation.
Another method for post-processing a cast cylinder 110 may be seen in the example of
Once the processing has been completed on the polymeric substrate, the substrate may be further formed or machined to create a variety of device. One example is shown in the perspective view of
With stent 130 positioned upon delivery catheter 132, it may be advanced intravascularly within a vessel 136 until the delivery site is reached, as shown in
Once the stent 130 has been expanded to some intermediate diameter D3 and secured against the vessel wall, stent 130 may be allowed to then self-expand further over a period of time into further contact with the vessel wall such that stent 130 conforms securely to the tissue. This self-expansion feature ultimately allows for the stent 130 to expand back to its initial diameter D1 which had been heat set, as shown in
These examples are presented to be illustrative of the types of devices which may be formed and various other devices which may be formed from the polymeric substrate are also included within this disclosure.
The applications of the disclosed invention discussed above are not limited to certain processes, treatments, or placement in certain regions of the body, but may include any number of other processes, treatments, and areas of the body. Modification of the above-described methods and devices for carrying out the invention, and variations of aspects of the invention that are obvious to those of skill in the arts are intended to be within the scope of this disclosure. Moreover, various combinations of aspects between examples are also contemplated and are considered to be within the scope of this disclosure as well.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4173689 | Lyman et al. | Nov 1979 | A |
| 4334327 | Lyman et al. | Jun 1982 | A |
| 4661530 | Gogolewski et al. | Apr 1987 | A |
| 4770664 | Gogolewski | Sep 1988 | A |
| 4834747 | Gogolewski | May 1989 | A |
| 4955899 | Della Corna et al. | Sep 1990 | A |
| 5104400 | Berguer et al. | Apr 1992 | A |
| 5152782 | Kowligi et al. | Oct 1992 | A |
| 5670161 | Healy et al. | Sep 1997 | A |
| 5935164 | Iversen | Aug 1999 | A |
| 5935506 | Schmitz et al. | Aug 1999 | A |
| 6090134 | Tu et al. | Jul 2000 | A |
| 6153252 | Hossainy et al. | Nov 2000 | A |
| 6217815 | Sisbarro | Apr 2001 | B1 |
| 6231326 | Sisbarro | May 2001 | B1 |
| 6322847 | Zhong et al. | Nov 2001 | B1 |
| 6635082 | Hossainy et al. | Oct 2003 | B1 |
| 6833153 | Roorda et al. | Dec 2004 | B1 |
| 6860946 | Hossainy et al. | Mar 2005 | B2 |
| 6866805 | Hong et al. | Mar 2005 | B2 |
| 6989071 | Kocur et al. | Jan 2006 | B2 |
| 7112298 | Kampa et al. | Sep 2006 | B2 |
| 7311727 | Mazumder et al. | Dec 2007 | B2 |
| 20030050687 | Schwade et al. | Mar 2003 | A1 |
| 20030060836 | Wang et al. | Mar 2003 | A1 |
| 20030157241 | Hossainy et al. | Aug 2003 | A1 |
| 20030195628 | Bao et al. | Oct 2003 | A1 |
| 20030225447 | Majercak et al. | Dec 2003 | A1 |
| 20040030377 | Dubson et al. | Feb 2004 | A1 |
| 20040113306 | Rapacki et al. | Jun 2004 | A1 |
| 20040127932 | Shah | Jul 2004 | A1 |
| 20040127970 | Saunders et al. | Jul 2004 | A1 |
| 20040164030 | Lowe et al. | Aug 2004 | A1 |
| 20050187608 | O'Hara | Aug 2005 | A1 |
| 20060025852 | Armstrong et al. | Feb 2006 | A1 |
| 20060122686 | Gilad et al. | Jun 2006 | A1 |
| 20060142736 | Hissink et al. | Jun 2006 | A1 |
| 20060149365 | Fifer et al. | Jul 2006 | A1 |
| 20060212064 | Shah | Sep 2006 | A1 |
| 20060259133 | Sowinski et al. | Nov 2006 | A1 |
| 20060287715 | Atladottir et al. | Dec 2006 | A1 |
| 20070038290 | Huang et al. | Feb 2007 | A1 |
| 20070100430 | Rudakov et al. | May 2007 | A1 |
| 20070106361 | Epstein | May 2007 | A1 |
| 20070110889 | Sundar | May 2007 | A1 |
| 20070185561 | Schmitz et al. | Aug 2007 | A1 |
| 20070202046 | Dave | Aug 2007 | A1 |
| 20070250153 | Cully et al. | Oct 2007 | A1 |
| 20070281117 | Kaplan et al. | Dec 2007 | A1 |
| 20070283552 | Gale et al. | Dec 2007 | A1 |
| 20080051866 | Chen et al. | Feb 2008 | A1 |
| 20080091275 | Ducharme | Apr 2008 | A1 |
| 20080103584 | Su et al. | May 2008 | A1 |
| 20100004734 | Ramzipoor et al. | Jan 2010 | A1 |
| Number | Date | Country |
|---|---|---|
| WO 2009155560 | Dec 2009 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20090319028 A1 | Dec 2009 | US |