This invention relates to a support assembly for a stent and a method of coating a stent using the assembly.
Blood vessel occlusions are commonly treated by mechanically enhancing blood flow in the affected vessels, such as by employing a stent. Stents act as scaffoldings, functioning to physically hold open and, if desired, to expand the wall of the passageway. Typically, stents are capable of being compressed, so that they can be inserted through small lumens via catheters, and then expanded to a larger diameter once they are at the desired location.
Stents are used not only for mechanical intervention but also as vehicles for providing biological therapy. Biological therapy can be achieved by medicating the stents. Medicated stents provide for the local administration of a therapeutic substance at the diseased site. Local delivery of a therapeutic substance is a preferred method of treatment because the substance is concentrated at a specific site and thus smaller total levels of medication can be administered in comparison to systemic dosages that can produce adverse or even toxic side effects for the patient.
One method of medicating a stent involves the use of a polymeric carrier coated onto the surface of the stent. A composition including a solvent, a polymer dissolved in the solvent, and a therapeutic substance dispersed in the blend is applied to the stent by immersing the stent in the composition or by spraying the composition onto the stent. The solvent is allowed to evaporate, leaving on the stent surfaces a coating of the polymer and the therapeutic substance impregnated in the polymer.
A shortcoming of the above-described method of medicating a stent is the potential for coating defects. While some coating defects can be minimized by adjusting the coating parameters, other defects occur due to the nature of the interface between the stent and the apparatus on which the stent is supported during the coating process. A high degree of surface contact between the stent and the supporting apparatus can provide regions in which the liquid composition can flow, wick, and collect as the composition is applied. If the contact area between the stent and the supporting apparatus is fixed, as the solvent evaporates, the excess composition hardens to form excess coating at and around the contact area. Upon the removal of the coated stent from the supporting apparatus, the excess coating may stick to the apparatus, thereby removing some of the coating from the stent in the form of peels, or leaving bare areas. Alternatively, the excess coating may stick to the stent, thereby leaving excess coating as clumps or pools on the struts or webbing between the struts.
Thus, it is desirable to minimize the fixed interface between the stent and the apparatus supporting the stent during the coating process to minimize coating defects. Accordingly, the present invention provides for a device for supporting a stent during the coating application process. The invention also provides for a method of coating the stent supported by the device.
In accordance with aspects of the present invention, a method of coating a stent comprises positioning a stent on a mandrel, applying a coating composition to the stent, and moving the stent in a linear direction relative to the mandrel. In further aspects, the movement of the stent in a linear direction relative to the mandrel is performed simultaneously with the application of the composition. In other aspects, the application of the coating composition is performed in multiple cycles and the movement of the stent in the linear direction is performed between each cycle. The application of the coating composition is performed, in detailed aspects of the invention, by spraying a polymer dissolved in a solvent and optionally an active agent added thereto onto the stent. The stent can also be rotated about the axis of the stent, in some aspects of the invention. The movement of the stent in a linear direction relative to the mandrel can be performed, in other aspects of the invention, by tilting the mandrel or by applying a gas at a sufficient pressure to the stent.
The features and advantages of the invention will be more readily understood from the following detailed description which should be read in conjunction with the accompanying drawings.
Various types of coating defects can arise due to permanent contact points between a stent and its supporting apparatus. The present invention minimizes or eliminates such coating defects by eliminating permanent contact points between a stent and its supporting apparatus during the coating process. The type of stent used with the present invention is not of critical significance and the term stent is broadly intended to include stent-grafts and radially expandable stents, such as balloon-expandable stents or self-expandable type.
Referring to
Mandrel 22 can be connected to a motor 32 so as to provide rotational motion as depicted by arrow 34 about the longitudinal axis of stent 10 during the coating process. In addition, the present invention can include a means for moving stent 10 back and forth between end stops 24 and 26. In one embodiment, mandrel 22 can be tilted, back and forth, in an angular direction Φ relative to the horizontal plane X by use of a pivoting system 36. Pivoting system 36 can include, for example, motor 32 and a first pneumatic cylinder 38 and a second pneumatic cylinder 40 that are mounted on a platform 42. Cylinders 38 and 40 can be independently actuated by air supplied through a solenoid valve to raise and lower the ends of motor 32 as illustrated in
Referring to
A variety of sizes and shapes for sleeves 28 and 30 can be contemplated so as to provide adequate support for stent 10 without being in too much contact with the inner surface of stent 10 so as to cause coating defects. Sleeves 28 and 30 should be able to provide enough contact area and engagement with the inner surface of stent 10 to rotate stent 10 during the coating process. Accordingly, there is a tradeoff with, on the one hand, minimizing the contact area between the outer surface of sleeves 28 and 30 and the inner surface of stent 10, and on the other hand, for allowing sleeves 28 and 30 to adequately rotate stent 10.
Providing sleeves 28 and 30 of small diameters, as compared to the inner diameter of stent 10, offsets the axis about which sleeves 28 and 30 rotate, away from the axis about which stent 10 rotates (i.e., the axis positioned longitudinally through the center of stent 10). Also, it is important that there is sufficient clearance between the outer surface of mandrel 22 and the inner surface of stent 10 to prevent mandrel 22 from obstructing the pattern of the stent body during the coating process. By way of example, stent 10 can have an inner diameter of about 0.059 inches (1.50 mm) to about 0.320 inches (8.13 mm), the outer diameter of mandrel 22 can be from about 0.010 inches (0.254 mm) to about 0.088 inches (2.235 mm), and the outer diameter of sleeves 28 and 30 can be from about 0.032 inches (0.813 mm) to about 0.2 inches (5.08 mm). The length of sleeves 28 and 30 will typically be significantly less than the length of mandrel 22. By way of example, the length of sleeves 28 and 30 will be about 0.01 inches (0.254 mm) to about 0.1 inches (2.54 mm), while the length of the mandrel 22 will be about 1 inch (25.4 mm) to about 6 inches (152.40 mm). Exemplary specifications that can be employed with stent 10 having a length of about 18 mm and an inner diameter of about 1.8 mm include:
Furthermore, sleeves 28 and 30 can have a variety of shapes. Representative examples include rectangular-, triangular-, octagonal-, or gear-shaped, having protruding teeth for engagement with stent 10. These shapes can further minimize contact between sleeves 28 and 30 and the inner surface of stent 10 while allowing for a forceful engagement between stent 10 and sleeves 28 and 30. In an alternative embodiment, sleeves 28 and 30 can be substantially circular.
Sleeves 28 and 30 can be fixed (e.g., by soldering or using an adhesive), or adjustably attached to mandrel 22 (e.g., by threading the sleeves over the mandrel). However, sleeves 28 and 30 should be firmly secured to mandrel 22 during the coating process in order to ensure that sleeves 28 and 30 rotate with mandrel 22. Mandrel 22 and sleeves 28 and 30 can be made of stainless steel, polyetheretherketone (PEEK), polytetrafluoroethylene (PTFE) (TEFLON™), DELRIN™, RULON™, PEBAX™, NYLON™ and fluorinated ethylene-propylene copolymer (FEP).
Referring to
Referring to
Stent 10 can be moved between end stops 24 and 26 in order to provide for the movement of the contact area between stent 10 and sleeves 28 and 30 in a linear direction along the axis of stent 10. Stent 10 can be moved as the composition is being applied. Alternatively, when the coating is applied in multiple repetitions, stent 10 can be moved in between each repetition. In other words, stent 10 can be moved while the spray coater is inactive, for example, during an intermediate drying step.
In one embodiment, tilting mandrel 22 up and down can move stent 10 between end stops 24 and 26. Referring back to
In another embodiment, stent 10 can be moved back and forth between end stops 24 and 26 by directing a gas to stent 10 during the coating process. Referring to
The following method of application is being provided by way of illustration and is not intended to limit the embodiments of the present invention. A spray apparatus, such as EFD 780S spray device with VALVEMATE 7040 control system (manufactured by EFD Inc., East Providence, R.I.), can be used to apply a composition to a stent. EFD 780S spray device is an air-assisted external mixing atomizer. The composition is atomized into small droplets by air and uniformly applied to the stent surfaces. The atomization pressure can be maintained at a range of about 5 psi to about 20 psi. The droplet size depends on such factors as viscosity of the solution, surface tension of the solvent, and atomization pressure. Other types of spray applicators, including air-assisted internal mixing atomizers and ultrasonic applicators, can also be used for the application of the composition.
The flow rate of the solution from the spray nozzle can be from about 0.01 mg/second to about 1.0 mg/second, more narrowly about 0.1 mg/second. Multiple repetitions for applying the composition can be performed, wherein each repetition can be, for example, about 1 second to about 10 seconds in duration. The amount of coating applied by each repetition can be about 0.1 micrograms/cm2 (of stent surface) to about 10 micrograms/cm2, for example less than about 2 micrograms/cm2 per 5-second spray. As described above, stent 10 can be moved as the composition is being applied. Alternatively, when the coating is applied in multiple repetitions, the stent can be moved in between the repetitions. It may be advantageous to move the stent after the composition has been applied so that the movement does not interfere with the uniformity of the spray coating.
Each repetition can be followed by removal of a significant amount of the solvent(s). Depending on the volatility of the particular solvent employed, the solvent can evaporate essentially upon contact with the stent. Alternatively, removal of the solvent can be induced by baking the stent in an oven at a mild temperature (e.g., 60° C.) for a suitable duration of time (e.g., 2-4 hours) or by the application of warm air. The application of warm air between each repetition prevents coating defects and minimizes interaction between the active agent and the solvent. The warm air applied to the stent to induce evaporation can also be used to move the stent to cause movement of the contact area in a linear direction along the axis of the stent. The temperature of the warm air can be from about 30° C. to about 60° C., more narrowly from about 40° C. to about 50° C. The flow rate of the warm air can be from about 20 cubic feet/minute (CFM) (0.57 cubic meters/minute (CMM)) to about 80 CFM (2.27 CMM), more narrowly about 30 CFM (0.85 CMM) to about 40 CFM (1.13 CMM). The warm air can be applied for about 3 seconds to about 60 seconds, more narrowly for about 10 seconds to about 20 seconds. By way of example, warm air applications can be performed at a temperature of about 50° C., at a flow rate of about 40 CFM, and for about 10 seconds. Any suitable number of repetitions of applying the composition followed by removing the solvent(s) can be performed to form a coating of a desired thickness or weight. Excessive application of the polymer in a single application can, however, cause coating defects.
Operations such as wiping, centrifugation, or other web clearing acts can also be performed to achieve a more uniform coating. Briefly, wiping refers to the physical removal of excess coating from the surface of the stent; and centrifugation refers to rapid rotation of the stent about an axis of rotation. The excess coating can also be vacuumed off of the surface of the stent.
The stent can be at least partially preexpanded prior to the application of the composition. For example, the stent can be radially expanded about 20% to about 60%, more narrowly about 27% to about 55%—the measurement being taken from the stent's inner diameter at an expanded position as compared to the inner diameter at the unexpanded position. The expansion of the stent, for increasing the interspace between the stent struts during the application of the composition, can further prevent “cob web” formation between the stent struts.
The coating substance can include a solvent and a polymer dissolved in the solvent and optionally a wetting fluid. The coating substance can also include an active agent. Representative examples of polymers that can be used to coat a stent in accordance with the present invention include ethylene vinyl alcohol copolymer (commonly known by the generic name EVOH or by the trade name EVAL), poly(hydroxyvalerate); poly(L-lactic acid); polycaprolactone; poly(lactide-co-glycolide); poly(hydroxybutyrate); poly(hydroxybutyrate-co-valerate); polydioxanone; polyorthoester; polyanhydride; poly(glycolic acid); poly(D,L-lactic acid); poly(glycolic acid-co-trimethylene carbonate); polyphosphoester; polyphosphoester urethane; poly(amino acids); cyanoacrylates; poly(trimethylene carbonate); poly(iminocarbonate); copoly(ether-esters) (e.g. PEO/PLA); polyalkylene oxalates; polyphosphazenes; biomolecules, such as fibrin, fibrinogen, cellulose, starch, collagen and hyaluronic acid; polyurethanes; silicones; polyesters; polyolefins; polyisobutylene and ethylene-alphaolefin copolymers; acrylic polymers and copolymers; vinyl halide polymers and copolymers, such as polyvinyl chloride; polyvinyl ethers, such as polyvinyl methyl ether; polyvinylidene halides, such as polyvinylidene fluoride and polyvinylidene chloride; polyacrylonitrile; polyvinyl ketones; polyvinyl aromatics, such as polystyrene; polyvinyl esters, such as polyvinyl acetate; copolymers of vinyl monomers with each other and olefins, such as ethylene-methyl methacrylate copolymers, acrylonitrile-styrene copolymers, ABS resins, and ethylene-vinyl acetate copolymers; polyamides, such as Nylon 66 and polycaprolactam; alkyd resins; polycarbonates; polyoxymethylenes; polyimides; polyethers; epoxy resins; polyurethanes; polybutylmethacrylate; rayon; rayon-triacetate; cellulose acetate; cellulose butyrate; cellulose acetate butyrate; cellophane; cellulose nitrate; cellulose propionate; cellulose ethers; and carboxymethyl cellulose.
“Solvent” is defined as a liquid substance or composition that is compatible with the polymer and is capable of dissolving the polymer at the concentration desired in the composition. Examples of solvents include, but are not limited to, dimethylsulfoxide, chloroform, acetone, water (buffered saline), xylene, methanol, ethanol, 1-propanol, tetrahydrofuran, 1-butanone, dimethylformamide, dimethylacetamide, cyclohexanone, ethyl acetate, methylethylketone, propylene glycol monomethylether, isopropanol, isopropanol admixed with water, N-methyl pyrrolidinone, toluene, and combinations thereof.
A “wetting” of a fluid is measured by the fluid's capillary permeation. Capillary permeation is the movement of a fluid on a solid substrate driven by interfacial energetics. Capillary permeation is quantitated by a contact angle, defined as an angle at the tangent of a droplet in a fluid phase that has taken an equilibrium shape on a solid surface. A low contact angle means a higher wetting liquid. A suitably high capillary permeation corresponds to a contact angle less than about 90°. Representative examples of the wetting fluid include, but are not limited to, tetrahydrofuran, dimethylformamide, 1-butanol, n-butyl acetate, dimethylacetamide, and mixtures and combinations thereof.
The active agent contained in the coating can be for inhibiting the activity of vascular smooth muscle cells. More specifically, the active agent can be aimed at inhibiting abnormal or inappropriate migration and/or proliferation of smooth muscle cells for the inhibition of restenosis. The active agent can also include any substance capable of exerting a therapeutic or prophylactic effect in the practice of the present invention. For example, the active agent can be for enhancing wound healing in a vascular site or improving the structural and elastic properties of the vascular site. Examples of active agents include antiproliferative substances such as actinomycin D, or derivatives and analogs thereof (manufactured by Sigma-Aldrich 1001 West Saint Paul Avenue, Milwaukee, Wis. 53233; or COSMEGEN available from Merck). Synonyms of actinomycin D include dactinomycin, actinomycin IV, actinomycin I1, actinomycin X1, and actinomycin C1. The active agent can also fall under the genus of antineoplastic, antiinflammatory, antiplatelet, anticoagulant, antifibrin, antithrombin, antimitotic, antibiotic, antiallergic and antioxidant substances. Examples of such antineoplastics and/or antimitotics include paclitaxel (e.g. TAXOL® by Bristol-Myers Squibb Co., Stamford, Conn.), docetaxel (e.g. TAXOTERE®, from Aventis S. A., Frankfurt, Germany), methotrexate, azathioprine, vincristine, vinblastine, fluorouracil, doxorubicin hydrochloride (e.g. ADRIAMYCIN from Pharmacia & Upjohn, Peapack, N.J.), and mitomycin (e.g. MUTAMYCIN from Bristol-Myers Squibb Co., Stamford, Conn.) Examples of such antiplatelets, anticoagulants, antifibrin, and antithrombins include sodium heparin, low molecular weight heparins, heparinoids, hirudin, argatroban, forskolin, vapiprost, prostacyclin and prostacyclin analogues, dextran, D-phe-pro-arg-chloromethylketone (synthetic antithrombin), dipyridamole, glycoprotein IIb/IIa platelet membrane receptor antagonist antibody, recombinant hirudin, and thrombin inhibitors such as ANGIOMAX™ (Biogen, Inc., Cambridge, Mass.) Examples of such cytostatic or antiproliferative agents include angiopeptin, angiotensin converting enzyme inhibitors such as captopril (e.g. CAPOTEN® and CAPOZIDE® from Bristol-Myers Squibb Co., Stamford, Conn.), cilazapril or lisinopril (e.g. PRINIVIL® and PRINZIDE® from Merck & Co., Inc., Whitehouse Station, N.J.), calcium channel blockers (such as nifedipine), colchicine, fibroblast growth factor (FGF) antagonists, fish oil (omega 3-fatty acid), histamine antagonists, lovastatin (an inhibitor of HMG-CoA reductase, a cholesterol lowering drug, brand name MEVACOR® from Merck & Co., Inc., Whitehouse Station, N.J.), monoclonal antibodies (such as those specific for Platelet-Derived Growth Factor (PDGF) receptors), nitroprusside, phosphodiesterase inhibitors, prostaglandin inhibitors, suramin, serotonin blockers, steroids, thioprotease inhibitors, triazolopyrimidine (a PDGF antagonist), and nitric oxide. An example of an antiallergic agent is permirolast potassium. Other therapeutic substances or agents which may be appropriate include alpha-interferon, genetically engineered epithelial cells, tacrolimus, dexamethasone, and rapamycin and structural derivatives or functional analogs thereof, such as 40-O-(2-hydroxy)ethyl-rapamycin (known by the trade name of EVEROLIMUS available from Novartis), 40-O-(3-hydroxy)propyl-rapamycin, 40-O-[2-(2-hydroxy)ethoxy]ethyl-rapamycin, and 40-O-tetrazole-rapamycin.
While particular embodiments of the present invention have been shown and described, it will be apparent to those skilled in the art that changes and modifications can be made without departing from the scope of the invention. Therefore, the appended claims are to encompass within their scope all such changes and modifications as fall within the true spirit and scope of this invention.
This application is a divisional of prior application Ser. No. 10/304,669, filed Nov. 25, 2002, now U.S. Pat. No. 7,416,609, the entire disclosure of which is hereby incorporated by reference.
Number | Name | Date | Kind |
---|---|---|---|
3683505 | Graef | Aug 1972 | A |
4733665 | Palmaz | Mar 1988 | A |
4800882 | Gianturco | Jan 1989 | A |
4886062 | Wiktor | Dec 1989 | A |
4906423 | Frisch | Mar 1990 | A |
4928435 | Masaki et al. | May 1990 | A |
5037427 | Harada et al. | Aug 1991 | A |
5234457 | Andersen | Aug 1993 | A |
5537729 | Kolobow | Jul 1996 | A |
5628786 | Banas et al. | May 1997 | A |
5716981 | Hunter et al. | Feb 1998 | A |
5772864 | Møller et al. | Jun 1998 | A |
5788626 | Thompson | Aug 1998 | A |
5895407 | Jayaraman | Apr 1999 | A |
5897911 | Loeffler | Apr 1999 | A |
5922393 | Jayaraman | Jul 1999 | A |
5935135 | Bramfitt et al. | Aug 1999 | A |
6010573 | Bowlin | Jan 2000 | A |
6056993 | Leidner et al. | May 2000 | A |
6120847 | Yang et al. | Sep 2000 | A |
6126686 | Badylak et al. | Oct 2000 | A |
6153252 | Hossainy et al. | Nov 2000 | A |
6156373 | Zhong et al. | Dec 2000 | A |
6214115 | Taylor et al. | Apr 2001 | B1 |
6258121 | Yang et al. | Jul 2001 | B1 |
6322847 | Zhong et al. | Nov 2001 | B1 |
6364903 | Tseng et al. | Apr 2002 | B2 |
6387118 | Hanson | May 2002 | B1 |
6517889 | Jayaraman | Feb 2003 | B1 |
6521284 | Parsons et al. | Feb 2003 | B1 |
6527863 | Pacetti et al. | Mar 2003 | B1 |
6534112 | Bouchier et al. | Mar 2003 | B1 |
6544582 | Yoe | Apr 2003 | B1 |
6555157 | Hossainy | Apr 2003 | B1 |
6565659 | Pacetti et al. | May 2003 | B1 |
6572644 | Moein | Jun 2003 | B1 |
6605154 | Villareal | Aug 2003 | B1 |
6673154 | Pacetti et al. | Jan 2004 | B1 |
6695920 | Pacetti et al. | Feb 2004 | B1 |
6723373 | Narayanan et al. | Apr 2004 | B1 |
6818063 | Kerrigan | Nov 2004 | B1 |
20030215564 | Heller et al. | Nov 2003 | A1 |
Number | Date | Country | |
---|---|---|---|
20080305242 A1 | Dec 2008 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 10304669 | Nov 2002 | US |
Child | 12193583 | US |