Stent with anti-thrombogenic coating

Information

  • Patent Grant
  • 6602287
  • Patent Number
    6,602,287
  • Date Filed
    Wednesday, December 8, 1999
    25 years ago
  • Date Issued
    Tuesday, August 5, 2003
    21 years ago
Abstract
A glycocalyx-like material is applied to a stent in order to mimic the outer surface of the cells lining arteries and veins to prevent thrombogenesis. The glycocalyx material is applied over a base layer of a fluorocarbon that is applied directly to the stent surfaces.
Description




BACKGROUND OF THE INVENTION




This invention relates generally to expandable intraluminal vascular grafts, commonly referred to as stents, and more particularly pertains to the coating of stents in order to prevent acute thrombogenesis.




Stents are implanted within vessels in an effort to maintain the patency thereof by preventing collapse and/or impeding restenosis. Implantation of a stent is typically accomplished by mounting the stent on the expandable portion of a balloon catheter, maneuvering the catheter through the vasculature so as to position the stent at the treatment site within the body lumen, and inflating the balloon to expand the stent so as to engage the lumen wall. The stent automatically locks into its expanded configuration allowing the balloon to be deflated and the catheter to be removed to complete the implantation procedure. The use of self-expanding stents obviates the need for a balloon delivery device. Instead, a constraining sheath that is initially fitted about the stent is simply retracted once the stent is in position adjacent the treatment site.




A significant concern associated with the implantation of a stent within the vasculature is the potential for restenosis and thrombogenesis which may in fact be exacerbated by the presence of the stent. The pressure exerted by the stent on the vessel wall may increase the trauma that induces hyperplasia and the presence of the stent in the blood stream may induce a local or even systemic activation of the patient's hemostase coagulation system. Bound proteins of blood plasma, principally the adhesive proteins such albumin, fibronectin, fibrinogen and fibrin, are known to trigger coagulation. The result is typically the adhesion and aggregation of thrombocytes on the surface of the stent. These proteins include peptide structures, e.g. the RGD-peptides composed of amino acids, such as glycine, arginine and asparagine. The same structures are involved in the adhesion of thrombocytes as a consequence of receptors of the thrombocyte surface, e.g. collagen, von WilleBrand factor and fibrin interactions. The same result may arise with other biomaterials, generally of metal or plastic composition, which are inserted temporarily or implanted permanently in the patient. The deposit of blood clots on the surface of the biomaterial can result from a complex reaction of plasmatic and cellular mechanisms of coagulation that enhance and influence each other. Thus, the implantation of a stent to keep the lumen of the artery open may only hasten re-occlusion by promoting localized blood clotting and reactive inflammation. Indeed, studies indicate that stents and other untreated biomaterials can be covered with a relatively thick thrombus formation only minutes after contact with blood.




Various pharmacological agents have heretofore been used to address the problem both on a systemic as well as localized level. The latter approach is most often preferred and it has been found convenient to utilize the implanted stent for such purpose wherein the stent serves both as a support for the lumen wall as a well as delivery vehicle for the pharmacological agent. However, the metallic materials typically employed in the construction of stents in order to satisfy the mechanical strength requirements are not generally capable of carrying and releasing drugs. On the other hand, while various polymers are known that are quite-capable of carrying and releasing drugs, they generally do not have the requisite strength characteristics. Moreover, the structural and mechanical capabilities of a polymer may be significantly reduced as such polymer is loaded with a drug. A previously devised solution to such dilemma has therefore been the coating of a stent's metallic structure with a drug carrying polymer material in order to provide a stent capable of both supporting adequate mechanical loads as well as carrying and delivering drugs.




Various pharmacological agents have previously been employed to reduce or suppress thrombogenesis and various methods have been developed to load such pharmacological agents onto a stent in order to achieve the desired therapeutic effect. However, further improvement is desired both in terms of the anti-thrombogenic efficacy of materials that can be coated onto stents as well as the methods by which such materials are coated onto the stent.




SUMMARY OF THE INVENTION




The present invention overcomes the shortcomings of the prior art methods for imparting anti-thrombogenic characteristics to an implantable stent and more particularly provides a new method for coating a new anti-thrombogenic agent onto a stent. The resulting stent is deployed at the treatment site to simultaneously provide mechanical support to the lumen wall as well as to prevent thrombogenesis.




The method of the present invention requires the sequential application to a stent of a base layer and a biologically active top layer. The base layer preferably consists of a fluorocarbon coating while the active layer consists of a coating of glycocalyx or glycocalyx-like material. The fluorocarbon coating provides a sterile and carbon-rich substrate to attract and retain the glycocalyx material which in turn prevents the adhesion of proteins thereto. Glycocalyx is a naturally occurring substance that is found in the external region of the cell membrane in cells that line the walls of veins and arteries. The glycocalyx is dominated by glycosylated molecules, which direct specific interactions such as cell-cell recognition and contribute to the stearic repulsion that prevents undesirable non-specific adhesion of other molecules and cells. Bioengineered glycocalyx-like material mimics the biological characteristics of naturally occurring glycocalyx. The glycocalyx molecule as well as the molecules of bioengineered glycocalyx-type materials have a flexible backbone with two types of side chains, a sugar chain that has the anti-clotting properties and a water repellent chain. The water repellent chain attaches to the fluorocarbon coating and the sugar chain protrudes outwardly to form a dense layer that prevents the attachment of plasma proteins thereto.




These and other features and advantages of the present invention will become apparent from the following detailed description of preferred embodiments which illustrate by way of example the principles of the invention.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

is a perspective view of a coated stent of the present invention.





FIG. 2

is an enlarged cross-sectional view taken along lines


2





2


of FIG.


1


.











DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS




The coated stent of the present invention serves to support the walls of a body lumen while preventing the formation of thrombi thereon. The present invention is not limited to any particular stent configuration or delivery method nor is the construction of the stent structure limited to the use of any particular construction material.





FIG. 1

generally illustrates a coated stent


12


of the present invention. The particular stent shown is for illustrative purposes only as virtually any stent configuration can be coated in accordance with the present invention. In fact, the coating can be applied to any device to be implanted or introduced into the body. The coating does not interfere with the stent structure or construction in any way and does not affect its deployment. All known stent designs with attendant delivery systems can benefit from the coating of the present invention.





FIG. 2

is an enlarged cross-sectional view of a portion of the stent shown in FIG.


1


and illustrates the two layers that are applied to the stent in accordance with the present invention. A base layer


16


is applied directly to all of the stent surfaces


14


including all of its edges. Such base layer consists of a fluorocarbon coating that positively adheres to the stent surface and avails a carbon-rich substrate for the attachment of the top layer


18


thereto. Such top layer is applied to the base-coated stent and uniformly covers all surfaces including all edges.




The fluorocarbon coating is preferred for use as a base layer in the present invention as it forms a strong bond with a variety of materials of which stents are commonly formed. Moreover, the equipment and techniques need for uniformly applying predictable amounts of a fluorocarbon to various surfaces have been well developed and are well known. The fluorocarbon provides an ideal substrate for attracting and retaining glycocalyx material as the water repellant side chains of the glycocalyx material readily attach to the carbon-rich structure of the fluorocarbon base layer. The glycocalyx material provides an ideal top layer for stent applications as the sugar side chains form a dense layer that prevents the attachment of plasma proteins. Moreover, because the exposed sugar side chains avail a surface that is very similar to surface of the cells lining the walls of the veins and arteries, the presence of the stent is effectively masked and the initiation of various defense mechanisms otherwise relied upon by the body to combat the presence of foreign materials is thereby avoided.




The coating of the stent is a multi-step process wherein the stent is first thoroughly cleaned after its fabrication. This is achieved by immersing the stent in an ultrasonic bath for 20 minutes followed by air drying. The fluorocarbon coating is preferably applied by a method known in the art as radio-frequency glow discharge (RFGD) plasma deposition. The process is performed by first securing the stent in the reactor by attaching it to a rod with a wire. The reactor is then evacuated down to a pressure of 1 milliliter. Argon gas is introduced into the reactor at a flow rate of 34.3 milliliters per minute to produce a pressure of 20 milliliter. The power is set at 80 watts and argon plasma is generated. The argon etch is applied for 30 seconds after which the power and vacuum flow is shut off and vacuum is again lowered to 1 mililiter. A fluorocarbon monomer is introduced into the reactor at a flow rate of 2 milliliters per minute. Any one of three monomers that are suitable for this application may be used, namely C


3


F


8


, C


3


F


6


or C


2


F


6


. The monomer is applied at a pressure of 150 mililiter at a power of 20 watts for 8 to 10 minutes. The power is then turned off while the fluorocarbon monomer continues flowing for 10 minutes to quench the plasma process. The reactor is purged of fluorocarbon monomer and the reactor is returned to atmospheric pressure. The fluorocarbon coating forms a thin coating of about 0.05 microns in thickness. The stent is then placed in a sterile bag and is moved to a tissue culture hood.




After the fluorocarbon coating process has been completed, the glycocalyx-like material is applied. An appropriate glycocalyx-like material is available from researchers at Case Western Reserve University in Cleveland, Ohio. A solution is made by mixing glycocalyx-like material with dimethyl sulfoxide to make a solution concentration of between 1 and 10%. The desired concentration of glycocalyx is dependent on how thick a coating is desired. The fluorocarbon coated stent is dipped in the glycocalyx-like solution and dried at room temperature in a purified air box for 6 to 24 hours. The coated stent is then joined with the stent delivery system and is ready for deployment.




While a particular form of the invention has been illustrated and described, it will also be apparent to those skilled in the art that various modifications can be made without departing from the spirit and scope of the invention. Accordingly, it is not intended that the invention be limited except by the appended claims.



Claims
  • 1. A method for preventing thrombogenesis on a surface of an implantable medical device, comprising the steps of:providing a medical device configured for implantation in the body; applying a base layer of fluorocarbon material to said medical device wherein said fluorocarbon material is selected from the group consisting of C3F8, C3F6, and C2F6; and applying a glycocalyx material to said base layer, wherein said glycocalyx material includes a water repellent side chain that attaches to said fluorocarbon material and a sugar side chain that prevents the attachment of plasma proteins thereto.
  • 2. The method of claim 1, wherein said medical device comprises a stent.
  • 3. The method of claim 1, wherein said fluorocarbon material is applied by a radio-frequency discharge plasma deposition process.
  • 4. The method of claim 3, wherein said fluorocarbon material is applied to a depth of about 0.05 microns.
  • 5. The method of claim 1, wherein said glycocalyx material is applied by dipping said base layer coated medical device into a solution containing 1 to 10% of said glycocalyx material.
  • 6. The method of claim 5, wherein said solution comprises a mixture of said glycocalyx material and dimethyl sulfoxide.
  • 7. A stent, comprising:an expandable structure; a base coating of fluorocarbon material wherein said fluorocarbon material is selected from the group consisting of C3F8, C3F6, and C2F6; and a top coating of a glycocalyx material, wherein said glycocalyx material includes a water repellent side chain that attaches to said fluorocarbon material and a sugar side chain that prevents the attachment of plasma proteins thereto.
  • 8. The stent of claim 7, wherein said base coating is about 0.05 microns thick.
US Referenced Citations (60)
Number Name Date Kind
3288728 Gorham Nov 1966 A
3839743 Schwarz Oct 1974 A
4346028 Griffith Aug 1982 A
4633873 Dumican et al. Jan 1987 A
4656083 Hoffman et al. Apr 1987 A
4699611 Bowden Oct 1987 A
4718907 Karwoski et al. Jan 1988 A
4722335 Vilasi Feb 1988 A
4723549 Wholey et al. Feb 1988 A
4816339 Tu et al. Mar 1989 A
4877030 Beck et al. Oct 1989 A
4879135 Greco et al. Nov 1989 A
4943346 Mattelin Jul 1990 A
4994298 Yasuda Feb 1991 A
5047050 Arpesani Sep 1991 A
5053048 Pinchuk Oct 1991 A
5085629 Goldberg et al. Feb 1992 A
5108755 Daniels et al. Apr 1992 A
5116365 Hillstead May 1992 A
5156623 Hakamatsuka et al. Oct 1992 A
5192311 King et al. Mar 1993 A
5197977 Hoffman, Jr. et al. Mar 1993 A
5222971 Willard et al. Jun 1993 A
5226913 Pinchuk Jul 1993 A
5234456 Silvestrini Aug 1993 A
5234457 Andersen Aug 1993 A
5236447 Kubo et al. Aug 1993 A
5269802 Garber Dec 1993 A
5279594 Jackson Jan 1994 A
5282860 Matsuno et al. Feb 1994 A
5289831 Bosley Mar 1994 A
5290271 Jernberg Mar 1994 A
5304200 Spaulding Apr 1994 A
5306286 Stack et al. Apr 1994 A
5314472 Fontaine May 1994 A
5330500 Song Jul 1994 A
5336518 Narayanan et al. Aug 1994 A
5342348 Kaplan Aug 1994 A
5342621 Eury Aug 1994 A
5356433 Rowland et al. Oct 1994 A
5360443 Barone et al. Nov 1994 A
5364354 Walker et al. Nov 1994 A
5370684 Vallana et al. Dec 1994 A
5383927 De Goicoechea et al. Jan 1995 A
5389106 Tower Feb 1995 A
5423849 Engelson et al. Jun 1995 A
5464650 Berg et al. Nov 1995 A
5562621 Claude et al. Oct 1996 A
5562728 Lazarus et al. Oct 1996 A
5571166 Dinh et al. Nov 1996 A
5609629 Fearnot et al. Mar 1997 A
5618298 Simon Apr 1997 A
5624411 Tuch Apr 1997 A
5628755 Heller et al. May 1997 A
5628781 Williams et al. May 1997 A
5637113 Tartaglia et al. Jun 1997 A
5688516 Raad et al. Nov 1997 A
5716406 Farber Feb 1998 A
5718726 Amon et al. Feb 1998 A
5824048 Tuch Oct 1998 A
Foreign Referenced Citations (27)
Number Date Country
2008312 Jul 1990 CA
2007648 Apr 1991 CA
1322628 Oct 1993 CA
1336319 Jul 1995 CA
1338303 May 1996 CA
0 380 668 Apr 1989 EP
0 351 314 Jan 1990 EP
0 517 075 Dec 1992 EP
0540 290 May 1993 EP
0 565 251 Oct 1993 EP
0 604 022 Jan 1994 EP
0 621 017 Oct 1994 EP
0 649 637 Apr 1995 EP
0 701 802 Mar 1996 EP
0 716 836 Jun 1996 EP
0 832 618 Sep 1996 EP
0 756 853 Feb 1997 EP
SHO 49-48336 Dec 1974 JP
SHO 54-18317 Jul 1979 JP
SHO 60-28504 Jul 1985 JP
HEI 8-33718 Feb 1996 JP
HEI 10-151190 Jun 1998 JP
WO 9117789 Nov 1991 WO
WO 9306792 Apr 1993 WO
WO 9511817 May 1995 WO
WO 9628115 Sep 1996 WO
WO 9710011 Mar 1997 WO
Non-Patent Literature Citations (59)
Entry
Hollahan, et al., Attachment of Amino Groups to Polymer Surfaces by Radiofrequency Plasmas, Journal of Applied Polymer Science, vol. 13, pp. 807-816 (1969).
Inagaki, et al., Hydrophilic Surface Modification of Polyethylene by No-Plasma Treatment, Adhesion Science Technology, vol. 4, No. 2, pp. 99-107.
Gölander, et al., RF-Plasma-Modified Polystyrene Surfaces for Studying Complement Activation, J. Biomater. Sci. Polymer Edn., vol. 4, No. 1, pp. 25-30 (1992).
Poncin-Epaillard, et al., Reactivity of a Polypropylene Surface Modified in a Nirtogen Plasma, Plasma Surface Modification of Polymers, pp. 167-180 (1994).
Gengenbach, et al., Evolution of the Surface Composition and topography of Perfluorinated Polymers Following Ammonia-Plasma Treatment, Plasma Surface Modification of Polymers, pp. 123-146 (1994).
Lambert, et al., Localized Arterial Wall Drug Delivery From a Polymer-Coated Removable Metallic Stent, Circulation, vol. 90, No. 2 pp. 1003-1011 (Aug. 1994).
De Scheerder, et al., Biocompatibility of Polymer-Coated Oversized Metallic Stents Implanted in Normal Porcine Coronary Arteries, Atherosclerosis, vol. 114, pp. 105-114 (1995).
Union Carbide Technology Letter, New Busiiness Department—Parylene, Oct. 1973, No. 7 (8 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1973, No. 9 (23 pages).
Union Carbide Technology Letter, May 1974, No. 11 (12 pages).
Union Carbide Technology Letter, Oct. 1975, No. 15 (13 pages).
Union Carbide, Electronic Materials, Parylene Products, Mar. 1976, No. 16 (4 pages).
Eskin, et al., Growth of Cultured Calf Aortic Smooth Muscle Cells on Cardiovascular Prosthetic Materials, Journal of Biomedical Material Research, vol. 10, pp. 113-122 (1976).
Loeb, et al., Parylene as a Chronically Stable, Reproducible Microelectrode Insulator, IEEE Transactions on Biomedical Engineering, pp. 121-128 (Mar. 1977).
Union Carbide, Electronic Materials, Parylene Products, Aug. 1977, No. 18 (7 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 1, Revision 2 (7 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 2, Revision 1 (9 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 3 (21 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 4 (13 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 6 (12 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 7 Revision 1 (8 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 8, Edited (19 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 10 (50 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 11 (12 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 12, Revision 1 (6 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 13, Revision 1 (7 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 14, Revision 1 (11 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 15, Revision 1 (8 pages).
Union Carbide, Electronic Materials, Parylene Products, Oct. 1977, No. 17, Revision 1 (11 pages).
ISEEE Transactions on Biomedical Engineering, vol. BME-27, No. 11, Nov. 1980 (5 pages).
Sadhir, et al., The Adhesion of Glow-Discharge Polymers, Silastic and Parylene to Implantable Platinum Electrodes: Results of Tensile Pull Tests After Exposure to Isotonic Sodium Chloride, vol. 2, Biomaterials, pp. 239-243 (Oct. 1981).
Hahn, et al., Glow Discharge Polymers as Coatings for Implanted Devices, John M. Dlaton Research Center, University of Missouri-Columbia and the Graduate Center for Materials Research, pp. 109-113 (1981).
Union Carbide, Electrode Materials, Parylene Products, Jan. 18, 1982, No. 5, Revision 4 (17 pages).
Hahn, et al., Biocompatibility of Glow-Discharge-Polymerized Films and Vacuum-Deposited Parylene, Journal of Applied Polymer Science: Applied Polymer Symposium 38, 55-64 (1984).
Casper, et al., Fiber-Reinforced Absorbable Compsite for Orthopedic Surgery, Polymeric Materials Science and Engineering, Proceedings of the ACS Division of Polymeric Materials: Science and Engineering, vol. 53, Fall Meeting 1985.
Kelly et al., Totally Resorbable High-Strength Composite Material, Advances in Biomedical Polymers, Edited by Charles G. Gebelein (1987).
Yuen, et al., Tissue Response to Potential Neuroprosthetic Materials Implanted Subdurally, Biomaterials, vol. 8, No. 8, pp. 57-62 (Mar. 1987).
Nichols, et al., Electrical Insulation of Implantable Devices by Composite Polymer Coatings, Dalton Research Center, University of Missouri, 1987.
Schmidt, et al., Long-Term Implant of Parylene-C Coated Microelectrodes, Medical & Biological Engineering and Computing, pp. 96-101 (Jan. 1988).
Olson, Parylene, A Biostable Coating for Medical Applications, for NOVA TRAN Parylene Coating Services (Jul. 25, 1988; Nov. 14, 1988).
Beach, et al., Xylylene Polymers, Encyclopedia of Polymer Science and Engineering, vol. 17, Second Edition, pp. 990-1025, 1989.
Muller, et al., Advanced in coronary Angioplasty: Endovascular Stents, Coronary Artery Disease, vol. 1, No. 4, Jul./Aug. 1990.
Loh, et al., Plasma Enhanced Parylene Deposition, Antec, pp. 1099-1103 (1991).
Gebelein, et al., Biomedical and Dental Applications of Polymers, Polymer Science and Technology, vol. 14, pp. 143-161 (No date).
The Parylene Press (A Publication of Specialty Coating Systems, Inc.), Winter 1992 (7 pages).
Charlson, et al., Temperature Selective Deposition of Parylene-C, IEEE Transactions on Biomedical Engineering, vol. 39, No. 2, pp. 202-206, (Feb. 1992).
Bull, Parylene Coating for Medical Applications Medical Product Manufacturing News, Mar. 1993 (2 pages).
The Parylene Press (A Publication of Specialty Coating Systems, Inc.), Spring 1993 (6 pages).
The Parylene Press (A Publication of Specialty Coating Systems, Inc.), Summer 1993 (4 pages).
Information Regarding Parylene-C Coating for ACS Metal Stent, In-Home Memorandum from Ed Newton to Joe Callol, Mike Clayman, Dennis Houlsby and Joe Tartaglia, Oct. 15, 1993 attaching Parylene, a Biostable Coating for Medical Application by Roger Olson.
Moody: Vacuum Coating Ultrasonic Transducers, Sensors, Dec. 1993 (1 page).
Parylene Conformal Coatings Specifications and Properties, Sales Brochure, Union Carbide Specialty Coating Systems (12 pages).
Parylene Environmentally Compatible Conformal Coatings for Electronic Components Assemblies and Precision Parts, Brochure, Union Carbide Electronics Division (14 pages).
Parylene and Nova Tran™ Parylene Coating Services, for Unmatched Conformal Coating Performance, Brochure, Union Carbide Specialty Coating Systems (21 pages).
Nova Tran™ Custom Coating Services, Parylene Conformal Coating, Brochure, Union Carbide (8 pages).
Parylene, a Biostable Coating for Medical Applications, Brochure, Union Carbide Specialty Systems (6 pages).
Typical Parylene Properties, Printout, Para Tech Coating Company; Lab Top® Parylene Deposition System Model 3000, Sales Brochure, Para Tech Coating Company (7 pages).
Application for U.S. Letters patent Ser. No. 08/559,931 filed Nov. 17, 1995.
Holland, Nolan B., et al., Biomimetic Engineering of Non-Adhesive Glycocalyx-Like Surfaces Using Oligosaccharide Surfactant Polymers, Nature, vol. 392, pp. 799-801, Apr. 23, 1998.