Stress relief mechanism for optical interference coatings

Information

  • Patent Grant
  • 6710520
  • Patent Number
    6,710,520
  • Date Filed
    Thursday, August 24, 2000
    24 years ago
  • Date Issued
    Tuesday, March 23, 2004
    20 years ago
Abstract
An optical interference coating for reflecting infra-red radiation and transmitting visible light. The coating comprises alternating layers of high index of refraction material and low index of refraction material. As the total number of layers increases, the ratio of high index of refraction material to low index of refraction material must also increase.
Description




BACKGROUND OF THE INVENTION




Thin film optical coatings known as interference filters which comprise alternating layers of two or more materials of different indices of refraction are well known to those skilled in the art. Such coatings or films are used to selectively reflect or transmit light radiation from various portions of the electromagnetic radiation spectrum such as ultraviolet, visible and infrared radiation. These films or coatings are used in the lamp industry to coat reflectors and lamp envelopes. One application in which these thin film optical coatings are useful is to improve the illumination efficiency or efficacy of incandescent lamps by reflecting infrared energy emitted by a filament or arc back to the filament or arc while transmitting the visible light portion of the electromagnetic spectrum emitted by the filament. This lowers the amount of electrical energy required to be supplied to the filament to maintain its operating temperature.




In other applications where it is desired to transmit infrared radiation, such filters can reflect the shorter wavelength portions of the spectrum, such as ultraviolet and visible light portions emitted by the filament or arc and transmit primarily the infrared portion in order to provide heat radiation with little or no visible light radiation. Such an application of this latter type would include a typical radiant heater for residential or industrial use where visible radiation emitted by the heater is unwanted.




Such interference filters useful for applications where the filter will be exposed to high temperatures in excess of about 500° C. have been made of alternating layers of tantala (tantalum pentoxide Ta


2


O


5


) and silica (SiO


2


), wherein the silica is the low refractive index material and the tantala is the high refractive index material. These interference filters may be obtained by a low pressure chemical vapor deposition (LPCVD) process to produce the film on a suitable substrate as described in U.S. Pat. No. 4,949,005, the contents of which are hereby incorporated by reference.




Improvements in the performance of LPCVD Ta


2


O


5


:SiO


2


thin film systems have been largely limited by mechanical failure, due to excessive tensile stress in the coating. The limiting number of layers has historically been 46, above which the coatings spall off the substrates. Competitive pressures require the performance of halogen IR films to be improved, with respect to the lumens output per watt consumed, while keeping color quality high.




Previous approaches typically have been to (1) increase the number of layers, (2) switch to a material system with a larger difference in the indices of refraction (n) between the two selected materials, or (3) induce some form of stress relief in some of the layers.




Difficulty with the first approach has typically been with regard to stress. With an increasing number of layers for a given design, the stress (tensile for LPCVD) also increases, ultimately resulting in cohesive failure of the substrate.




Difficulty with the second approach has typically been with regard to finding compatible materials and processes. Relatively few material systems (combinations of high and low index materials) exist which are suited for the intended environment, and also lend themselves to practical processing techniques.




There are also difficulties with the third approach. For example, U.S. Pat. No. 5,680,001, the contents of which is hereby incorporated by reference, describes a method of depositing an adhesive layer between the substrate and the film. These adhesive layers are typically silica doped with either B


2


O


3


or phosphorous pentoxide. These films are hydroscopic, which can lead to detrimental effects on the film.




U.S. Pat. No. 4,949,005 describes a method of annealing tantala/silica structures as a means of relieving stress in the film. This technique is currently in practice for the 46 layer design deposited commercially on halogen filament tubes. The benefits of thermal annealing are supplementary to the invention disclosed presently.




Thus, there is a need to improve the performance of IR reflecting films. The thickness of the alternating layers of tantala and silica are designed such that the visible spectrum is transmitted through the coatings, and the IR energy is reflected, as disclosed in U.S. Pat. No. 5,138,219, the contents of which is hereby incorporated by reference. An increase in performance could be expected simply by increasing the number of layers. However, the internal stresses in the film also increase with the number of layers, for a given design.




SUMMARY OF THE INVENTION




An optical interference coating for reflecting infra-red radiation and transmitting visible light comprising alternating layers of high index of refraction material and low index of refraction material, wherein the total number of said layers is greater than 51.











BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWING





FIG. 1

is a side view of an elongated tungsten halogen lamp having a tantala-silica interference film according to the present invention on the outer surface.











DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION





FIG. 1

illustrates one embodiment of the present invention comprising a lamp, the outer surface of which contains a tantala-silica interference filter according to the present invention which reflects infrared radiation back to the filament wherein it is converted into visible radiation.




The lamp illustrated in

FIG. 1

comprises envelope


10


made out of a vitreous, light transmissive material capable of withstanding high temperatures of about 800° C., preferably quartz. Each end of envelope


10


has a pinch seal portion


12


through which is sealed an inlead connector


13


electrically and mechanically attached by suitable means, such as welding, to molybdenum foil


14


which is hermetically sealed and embedded in the pinch seal portion


12


of the lamp. Leads


15


are made out of a suitable refractory metal, such as molybdenum or tungsten, and are attached to the other end of molybdenum foils


14


at one end and at the other end are connected to tungsten filament


17


which is supported on its axis within the envelope by a plurality of suitable supporting members


18


, such as tungsten spiral wire supports of the type disclosed in U.S. Pat. No. 3,168,670, the contents of which are hereby incorporated by reference. The thin film optical interference filter or film or coating


20


is on the outer surface of the lamp as a continuous coating. The coating


20


can be used on any type of electric lamp, such as preferably incandescent or arc lamps or less preferably fluorescent lamps. For example, the coating


20


can be used on incandescent halogen lamps such as shown in FIGS. 6 and 7 of U.S. Pat. No. 5,138,219, the contents of which are incorporated herein by reference.




As set forth above, film or coating


20


consists of alternating layers of tantala and silica arranged so as to adjust the pass-band and the stop-band characteristics of the emitted radiation of the lamp.




A ratio can be calculated between the high and low index materials for a given design. For an IR reflecting thin film design comprised of alternating tantala and silica layers, the Ta


2


O


5


:SiO


2


ratio can be defined as:








r=T/S








wherein T represents the total thickness of all the Ta


2


O


5


layers and S represents the total thickness of all the SiO


2


layers.




The overall tensile stress in a tantala-silica coating is determined by (1) the total thickness, and (2) the value of r. Mechanical stresses in the coatings are dependent on the value of r more than the optical performance is dependent on the value of r. As such, one can adjust the value of r for the film sufficiently to allow for more layers to be deposited without mechanical failure occurring.




It has been surprisingly found that as the value of r is increased for a given number of layers, the mechanical stresses decrease. As a result, for the first time, more than 51 layers can be used in the interference coating without suffering mechanical failure due to tensile stresses. Coatings can be produced having greater than 51, 55, 60, 65, 70, 75, 78, 80, 85 or 90 total layers. Optionally, the total number of layers will be less than 200. In order to use more than 51 layers, the Ta


2


O


5


:SiO


2


ratio must be increased as the number of layers (i.e. the total thickness) in the interference coating is increased, in order to maintain mechanical integrity. The value of the ratio may be at least 0.9, 0.95, 1.0, 1.1, 1.2, 1.3, 1.5, 2.0, 3.0 or 4.0.




The following Example further illustrates various aspects of the invention.




EXAMPLE




Various interference layers were produced. All the layers were 78-layer designs. The Ta


2


O


5


:SiO


2


ratio (r) was varied, and the mechanical stability was observed and rated as “pass” (mechanically stable) or “fail” (mechanical failure). The results are as follows.



















r




Pass/Fail



























0.63




Fail







0.66




Fail







0.69




Fail







0.76




Fail







0.91




Pass







1.09




Pass







1.3




Pass















Other 78-layer designs were produced with r values ranging between 0.91 and 1.3. All of those layers exhibited mechanical stability.




Although the preferred embodiments of the invention have been shown and described, it should be understood that various modifications may be resorted to without departing from the scope of the invention as disclosed and claimed herein.



Claims
  • 1. An optical interference coating for reflecting infrared radiation and transmitting visible light comprising alternating layers of high index of refraction material and low index of refraction material, the total number of said layers being greater than 60, said optical interference coating having sufficiently low tensile stress such that said optical interference coating is not susceptible to cohesive failure from tensile stress, each of said alternating layers of high index of refraction material and low index of refraction material being a separate and distinct layer from adjacent layers.
  • 2. An optical interference coating as in claim 1, wherein the high index of refraction material is tantalum pentoxide and the low index of refraction material is silica.
  • 3. An optical interference coating as in claim 1, wherein a ratio of the total thickness of all of the layers of high index of refraction material to the total thickness of all of the layers of low index of refraction material, r, is at least 0.9.
  • 4. An optical interference coating as in claim 1, wherein a ratio of the total thickness of all of the layers of high index of refraction material to the total thickness of all of the layers of low index of refraction material, r, is at least 0.95.
  • 5. An optical interference coating as in claim 1, wherein a ratio of the total thickness of all of the layers of high index of refraction material to the total thickness of all of the layers of low index of refraction material, r, is at least 1.0.
  • 6. An optical interference coating as in claim 1, wherein a ratio of the total thickness of all of the layers of high index of refraction material to the total thickness of all of the layers of low index of refraction material, r, is at least 1.2.
  • 7. An optical interference coating as in claim 1, wherein the total number of layers is greater than 70.
  • 8. An optical interference coating as in claim 1, wherein the total number of layers is 78.
  • 9. An optical interference coating as in claim 1, wherein the total number of layers is less than 200.
  • 10. An electric lamp comprising a light transmissive envelope containing an electric light source within, wherein at least a portion of said envelope is coated with an optical interference coating for reflecting infrared radiation and transmitting visible light radiation, said coating comprising alternating layers of high index of refraction material and low index of refraction material, the total number of said layers being greater than 60, said optical interference coating having sufficiently low tensile stress such that said optical interference coating is not susceptible to cohesive failure from tensile stress, each of said alternating layers of high index of refraction material and low index of reaction material being a separate and distinct layer from adjacent layers.
  • 11. An electric lamp as in claim 10, wherein the high index of refraction material is tantalum pentoxide and the low index of refraction material is silica.
  • 12. An electric lamp as in claim 10, wherein a ratio of the total thickness of all of the layers of high index of refraction material to the total thickness of all of the layers of low index of refraction material, r, is at least 0.9.
  • 13. An electric lamp as in claim 10, wherein the total number of layers is 78.
  • 14. An electric lamp as in claim 10, wherein the total number of layers is less than 200.
  • 15. An optical interference coating as in claim 1, wherein a ratio of the total thickness of all of the layers of high index of refraction material to the total thickness of all of the layers of low index of refraction material, r, is at least 0.91, and the total number of said layers is at least 78.
  • 16. An optical interference coating as in claim 1, wherein a ratio of the total thickness of all of the layers of high index of refraction material to the total thickness of all of the layers of low index of refraction material, r, is at least 0.9.
  • 17. An electric lamp as in claim 10, wherein a ratio of the total thickness of all of the layers of high index of refraction material to the total thickness of all of the layers of low index of refraction material, r, is at least 0.91, and the total number of said layers is at least 78.
  • 18. An electric lamp as in claim 10, wherein a ratio of the total thickness of all of the layers of high index of refraction material to the total thickness of all of the layers of low index of refraction material, r, is at least 0.9.
  • 19. An optical interference coating for reflecting infrared radiation and transmitting visible light comprising alternating layers of high index of refraction material and low index of refraction material, each of said alternating layers of high index of refraction material and low index of refraction material being a separate and distinct layer from adjacent layers, the total number of said layers of high index of refraction material and low index of refraction material being greater than 51, wherein a ratio of the total thickness of all of the layers of high index of refraction material to the total thickness of all of the layers of low index of refraction material, r, is at least 0.9.
  • 20. An optical interference coating according to claim 19, said ratio, r, being at least 0.95.
  • 21. An optical interference coating according to claim 19, said ratio, r, being at least 1.0.
  • 22. An optical interference coating according to claim 19, the total number of layers of high index of refraction material and low index of refraction material being greater than 55.
  • 23. An electric lamp comprising a light transmissive envelope containing an electric light source within, wherein at least a portion of said envelope is coated with an optical interference coating for reflecting infrared radiation and transmitting visible light radiation, said coating comprising alternating layers of high index of refraction material and low index of refraction material, each of said alternating layers of high index of refraction material and low index of refraction material being a separate and distinct layer from adjacent layers, the total number of said layers of high index of refraction material and low index of refraction material being greater tan 51, wherein a ratio of the total thickness of all of the layers of high index of refraction material to tho total thickness of all of the layers of low index of refraction material, r, is at least 0.9.
  • 24. An electric lamp according to claim 23, said ratio, r, being at least 0.95.
  • 25. An electric lamp according to claim 23, said ratio, r, being at least 1.0.
  • 26. An electric lamp according to claim 23, the total number of layers of high index of refraction material and low index of refraction material being greater than 55.
  • 27. An optical interference coating according to claim 19, the total number of layers of high index of refraction material and low index of refraction material being greater than 60.
  • 28. An optical interference coating according to claim 19, said ratio, r, being effective to result in sufficiently low tensile stress in said optical interference coating such that said optical interference coating is not susceptible to cohesive failure from tensile stress.
  • 29. An optical interference coating according to claim 19, the total number of layers of high index of refraction material and low index of refraction material being greater than 60, and said ratio, r, being effective to result in sufficiently low tensile stress in said optical interference coating such that said optical interference coating is not susceptible to cohesive failure from tensile stress.
  • 30. An electric lamp according to claim 23, the total number of layers of high index of refraction material and low index of refraction material being greater than 60.
  • 31. An electric lamp according to claim 23, said ratio, r, being effective to result in sufficiently low tensile stress in said optical interference coating such that said optical interference coating is not susceptible to cohesive failure from tensile stress.
  • 32. An electric lamp according to claim 23, the total number of layers of high index of refraction material and low index of refraction material being greater than 60, and said ratio, r, being effective to result in sufficiently low tensile stress in said optical interference coating such that said optical interference coating is not susceptible to cohesive failure from tensile stress.
US Referenced Citations (10)
Number Name Date Kind
4652789 Kawakatsu et al. Mar 1987 A
4949005 Parham et al. Aug 1990 A
5138219 Krisl et al. Aug 1992 A
5569970 Dynys et al. Oct 1996 A
5680001 Mulder et al. Oct 1997 A
5681666 Treger et al. Oct 1997 A
5843518 Li et al. Dec 1998 A
5944964 Solberg et al. Aug 1999 A
5982078 Krisl et al. Nov 1999 A
6087775 Levinson et al. Jul 2000 A