This application claims all benefits accruing under 35 U.S.C. § 119 from China Patent Application No. 201810712021.4, filed on Jun. 29, 2018, in the China National Intellectual Property Administration, the contents of which are hereby incorporated by reference. The application is also related to copending applications entitled, “METHOD FOR MAKING STRETCHABLE CAPACITOR ELECTRODE-CONDUCTOR STRUCTURE”, filed Apr. 9, 2019, Ser. No. 16/379,258. The application is also related to copending applications entitled, “STRETCHABLE CAPACITOR ELECTRODE-CONDUCTOR STRUCTURE”, filed Apr. 9, 2019, Ser. No. 16/379,264. The application is also related to copending applications entitled, “STRETCHABLE COMPOSITE ELECTRODE AND STRETCHABLE LITHIUM ION BATTERY USING THE SAME”, filed Apr. 9, 2019, Ser. No. 16/379,258. The application is also related to copending applications entitled, “METHOD OF MAKING STRETCHABLE COMPOSITE ELECTRODE”, filed Apr. 9, 2019, Ser. No. 16/379,258.
The present disclosure relates to stretchable film structures and a method of making the same.
Stretchable film structures can be applied to many fields, such as, stretchable energy-storage devices and flexible touch screens. Carbon nanotube film structures have excellent flexibility, and the carbon nanotube film structures are commonly used as stretchable film structures.
However, conventional carbon nanotube film structures is stretchable under little stress in a single direction, and can be easily broken when it is repeatedly stretched in different directions at the same time.
Therefore, there is a room for improvement.
Implementations of the present technology will now be described, by way of embodiments, with reference to the attached figures, wherein:
The disclosure is illustrated by way of example and not by way of limitation in the figures of the accompanying drawings in which like references indicate similar elements. It should be noted that references to “another,” “an,” or “one” embodiment in this disclosure are not necessarily to the same embodiment, and such references mean “at least one.”
It will be appreciated that for simplicity and clarity of illustration, where appropriate, reference numerals have been repeated among the different figures to indicate corresponding or analogous elements. In addition, numerous specific details are set forth in order to provide a thorough understanding of the embodiments described herein. However, it will be understood by those of ordinary skill in the art that the embodiments described herein can be practiced without these specific details. In other instances, methods, procedures, and components have not been described in detail so as not to obscure the related relevant feature being described. Also, the description is not to be considered as limiting the scope of the embodiments described herein. The drawings are not necessarily to scale, and the proportions of certain parts have been exaggerated to illustrate details and features of the present disclosure better.
Several definitions that apply throughout this disclosure will now be presented.
The term “substantially” is defined to be essentially conforming to the particular dimension, shape, or other feature which is described, such that the component need not be exactly or strictly conforming to such a feature. The term “comprise,” when utilized, means “include, but not necessarily limited to”; it specifically indicates open-ended inclusion or membership in the so-described combination, group, series, and the like.
step (S1), providing an elastic substrate, and pre-stretching the elastic substrate along a first direction and a second direction intersecting with the first direction, to obtain a pre-stretched elastic substrate;
step (S2), laying a carbon nanotube film structure on a surface of the pre-stretched elastic substrate, and the carbon nanotube film structure directly contacting with the pre-stretched elastic substrate and comprising a plurality of super-aligned carbon nanotube films stacked with each other, each of the plurality of super-aligned carbon nanotube films comprising a plurality of carbon nanotubes substantially parallel with each other; and
step (S3), releasing the pre-stretching of the elastic substrate to restore deformations of the elastic substrate, and forming a plurality of wrinkles on a surface of the carbon nanotube film structure to form the stretchable film structure.
In step (S1), an intersection angle of the first direction and the second direction is not limited. In one embodiment, the first direction is perpendicular with the second direction. When the first direction being perpendicular with the second direction, the elastic substrate can be evenly stretched during pre-stretching; and after the pre-stretching is released, the distribution, size, and shape of the plurality of wrinkles are uniform. Therefore, when the stretchable film structure is stretched in any direction, the plurality of wrinkles can be unfolded in a stress direction, and thus an ability of the stretchable film structure to resist stretching in different directions is improved.
In some embodiments, the elastic substrate is pre-stretched in three or more directions to make the elastic substrate be in a tensional state, and the three or more directions are symmetrical and intersecting.
A material of the elastic substrate can be selected from silicone rubber, polyvinyl chloride, polytetrafluoroethylene, polyurethane (PU), polyvinyl chloride (PVC), polydimethylsiloxane (PDMS) and the like. In one embodiment, the elastic substrate is a rectangular PDMS substrate.
In one embodiment, the elastic substrate is biaxial pre-stretched in each of the first direction the second direction. “Biaxial pre-stretched” refers that the elastic substrate is pre-stretched toward two ends in each of the first direction and the second direction. In one embodiment, the elastic substrate is uniaxial pre-stretched in the first direction and the second direction. “Uniaxial pre-stretched” refers that in each of the first direction and the second direction, one end of the elastic substrate is fixed, and only the other end is pre-stretched. In one embodiment, a shape of the elastic substrate is a rectangle, the elastic substrate is biaxial pre-stretched both in the first direction and the second direction, the first direction is parallel to a long side of the rectangle, and the second direction is parallel to a short side of the rectangle.
In one embodiment, a first pre-stretching capacity of the elastic substrate in the first direction is the same as a second pre-stretching capacity of the elastic substrate in the second direction. The first pre-stretching capacity refers a percentage of a length of the elastic substrate in the first direction after pre-stretching and a length of the elastic substrate in the first direction before pre-stretching. The second pre-stretching capacity refers a percentage of a length of the elastic substrate in the second direction after pre-stretching and a length of the elastic substrate in the second direction before pre-stretching.
In one embodiment, the first pre-stretching capacity of the elastic substrate in the first direction is different from the second pre-stretching capacity of the elastic substrate in the second direction.
The pre-stretching capacity of the elastic substrate needs to be controlled within an elastic range of the elastic substrate. The pre-stretching capacity of the elastic substrate can be selected according to the material of the elastic substrate and actual needs. In one embodiment, each of the first pre-stretching capacity and the second pre-stretching capacity is 150%. Pre-stretching the elastic substrate by applying an external force to the elastic substrate in both the first direction and the second direction, the external force causes the elastic substrate to be elastically deformed without being damaged. In one embodiment, pre-stretching the elastic substrate by a clamp.
In step (S2), in one embodiment, the plurality of carbon nanotubes are differently aligned between adjacent two of the super-aligned carbon nanotube films to form a grid structure, and alignment directions of the plurality of carbon nanotubes between adjacent two of the super-aligned carbon nanotube films intersect with each other/are different. A angle of the alignment directions of the plurality of carbon nanotubes between adjacent two of the super-aligned carbon nanotube films is not limited. In one embodiment, the angle of the alignment directions of the plurality of carbon nanotubes between adjacent two of the super-aligned carbon nanotube films is about 90 degrees.
Each of the plurality of super-aligned carbon nanotube films can be drawn from a super-aligned carbon nanotube array. A method of drawing the super-aligned carbon nanotube film from the super-aligned carbon nanotube array comprises step (a) of selecting carbon nanotube segments with a certain width from the super-aligned carbon nanotube array and, at a certain speed, and step (b) of stretching the carbon nanotube segments to be substantially perpendicular to a growth direction of the super-aligned carbon nanotube array. Thus, the super-aligned carbon nanotube film is obtained. The super-aligned carbon nanotube array comprises a plurality of carbon nanotubes, the plurality of carbon nanotubes are substantially parallel to each other and perpendicular to a surface of a substrate. The super-aligned carbon nanotube array is pure, referring that the super-aligned carbon nanotube array is free with impurities, such as amorphous carbon, residual catalyst metal particles or the like. Examples of the method of making the super-aligned carbon nanotube array are taught by U.S. Pat. No. 7,045,108 to Jiang et al. The plurality of carbon nanotubes of the super-aligned carbon nanotube film joined end to end by van der Waals forces and extend in the same direction. An arranged direction of the plurality of carbon nanotubes of the super-aligned carbon nanotube film is substantially parallel to a drawing direction of the super-aligned carbon nanotube film.
A minority of carbon nanotubes in the super-aligned carbon nanotube film may be randomly aligned. However, the number of randomly aligned carbon nanotubes is very small and does not affect the overall oriented alignment of the majority of carbon nanotubes in the super-aligned carbon nanotube film. The majority of the carbon nanotubes in the super-aligned carbon nanotube film substantially aligned along the same direction may not be exactly straight, and can be curved to a certain degree, or are not exactly aligned along the overall aligned direction, and can deviate from the overall aligned direction by a certain degree. Therefore, partial contacts can exist between the randomly aligned carbon nanotubes and adjacent carbon nanotubes.
In one embodiment, the super-aligned carbon nanotube film is directly laid on the surface of the pre-stretched elastic substrate after drawn from the carbon nanotube array. The method of laying the carbon nanotube film structure on the surface of the pre-stretched elastic substrate comprises: drawing a first carbon nanotube film from a carbon nanotube array and laying the first carbon nanotube film on the surface of the pre-stretched elastic substrate; drawing a second carbon nanotube film from the carbon nanotube array and laying the second carbon nanotube film on a surface of the first carbon nanotube film, to make the second carbon nanotube film stack with the first carbon nanotube film; and repeating above steps to a predetermined thickness of the carbon nanotube film structure.
In one embodiment, the plurality of super-aligned carbon nanotube films are stacked with each other to form the carbon nanotube film structure before laying on the surface of the pre-stretched elastic substrate. In one embodiment, laying six-layer stacked super-aligned carbon nanotube films on an aluminum frame of 75 mm×75 mm to form a carbon nanotube film structure, and adjacent super-aligned carbon nanotube films cross each other; and then removing the carbon nanotube film structure from the aluminum frame and laying the carbon nanotube film structure on the surface of the pre-stretched elastic substrate.
A first angle between the extending direction of the carbon nanotubes of the carbon nanotube film structure and the first direction is not limited; a second angle between the extending direction of the carbon nanotubes of the carbon nanotube film structure and the second direction is not limited. In one embodiment, the extending direction of the carbon nanotubes of the carbon nanotube film structure is parallel with the first direction or the second direction.
The number of the super-aligned carbon nanotube films of the carbon nanotube film structure is not limited. In one embodiment, the carbon nanotube film structure consists of six super-aligned carbon nanotube films stacked with each other.
The carbon nanotube film structure is pure and substantially free of impurities, and thus the carbon nanotube film structure has a large viscosity and can be fixed to the surface of the elastic substrate by its own viscosity.
In another embodiment, an organic solvent can be applied on the carbon nanotube film structure to soak the carbon nanotube film structure, after step (S2) and before step (S3). The organic solvent can be dropped onto the carbon nanotube film structure. After being soaked by the organic solvent, the adjacent paralleled carbon nanotubes in the carbon nanotube film structure will bundle together, due to the surface tension of the organic solvent as the organic solvent volatilizes. The carbon nanotubes in the carbon nanotube film structure can combine tightly via van der Waals attractive force. The carbon nanotube film structure can also combine with the elastic substrate tightly after being soaked by the organic solvent. The organic solvent can be volatile, such as ethanol, methanol, acetone, dichloromethane, chloroform, or any appropriate mixture thereof. When the carbon nanotube film structure is soaked by the organic solvent, step (S3) is performed after the organic solvent is evaporated to the absence of significant droplets.
In step (S3), since the carbon nanotube film structure is bonded to the surface of the elastic substrate, after releasing the pre-stretching of the elastic substrate, a length of the elastic substrate in the first direction and a length of the elastic substrate in the second direction are shortened, and the elastic substrate returns to an original form before the pre-stretching. The plurality of carbon nanotubes of the carbon nanotube film structure bend along a direction substantially perpendicular to the surface of the elastic substrate and form a number of wave shaped protuberances. Namely, some portions of the carbon nanotubes are higher than other portions of the carbon nanotubes.
Referring to
In one embodiment, further comprising a step of removing the elastic substrate after step (S3).
In one embodiment, the plurality of carbon nanotubes are differently aligned between adjacent two of the super-aligned carbon nanotube films to form a grid structure, and alignment directions of the plurality of carbon nanotubes between adjacent two of the super-aligned carbon nanotube films intersect with each other/are different. A angle of the alignment directions of the plurality of carbon nanotubes between adjacent two of the super-aligned carbon nanotube films is not limited. In one embodiment, the angle of the alignment directions of the plurality of carbon nanotubes between adjacent two of the super-aligned carbon nanotube films is about 90 degrees.
In one embodiment, the first pre-stretching capacity of the elastic substrate and the second pre-stretching capacity of the elastic substrate of the elastic substrate during making the stretchable film structure are both 150%. Referring to
The first direction is defined as an X-axis, and the second direction is defined as a Y-axis. Referring to
Referring to
In some embodiments, when the stretchable film structure is applied, an angle is formed between the stretching direction and the extending direction of the carbon nanotubes of the stretchable film structure. In one embodiment, when the stretchable film structure is applied, the angle formed between the stretching direction and the extending direction of the carbon nanotubes of the stretchable film structure is larger than or equal to 30 degrees and less than or equal to 60 degrees. When the angle between the extending direction of the carbon nanotubes of the carbon nanotube film structure and the stretching direction is formed, the carbon nanotube film structure can absorb the stress by its own deformation, and thus the carbon nanotube film structure is not easy to be pulled broken, and an increasing rate of resistance is slowed down.
The elastic substrate 120 can be optional. In one embodiment, the stretchable film structure does not have the elastic substrate 120, just comprises the carbon nanotube film structure 140.
It is to be understood that the above-described embodiments are intended to illustrate rather than limit the present disclosure. Variations may be made to the embodiments without departing from the spirit of the present disclosure as claimed. Elements associated with any of the above embodiments are envisioned to be associated with any other embodiments. The above-described embodiments illustrate the scope of the present disclosure but do not restrict the scope of the present disclosure.
Depending on the embodiment, certain of the steps of a method described may be removed, others may be added, and the sequence of steps may be altered. The description and the claims drawn to a method may include some indication in reference to certain steps. However, the indication used is only to be viewed for identification purposes and not as a suggestion as to an order for the steps.
Number | Date | Country | Kind |
---|---|---|---|
201810712021.4 | Jun 2018 | CN | national |
Number | Name | Date | Kind |
---|---|---|---|
8288723 | Zhang | Oct 2012 | B2 |
20080299460 | Feng et al. | Dec 2008 | A1 |
20100047522 | Sivarajan et al. | Feb 2010 | A1 |
20110096465 | Zhou et al. | Apr 2011 | A1 |
20110097512 | Zhou et al. | Apr 2011 | A1 |
20110108545 | Wang et al. | May 2011 | A1 |
20110256451 | Cui et al. | Oct 2011 | A1 |
20130045413 | Wang et al. | Feb 2013 | A1 |
20130146215 | Liu et al. | Jun 2013 | A1 |
20130284695 | Feng et al. | Oct 2013 | A1 |
20140175087 | Feng et al. | Jun 2014 | A1 |
20150207143 | Wu et al. | Jul 2015 | A1 |
20180026258 | Yan et al. | Jan 2018 | A1 |
Number | Date | Country |
---|---|---|
1357899 | Jul 2002 | CN |
101315974 | Dec 2008 | CN |
102103935 | Jun 2011 | CN |
103159204 | Jun 2013 | CN |
103903870 | Jul 2014 | CN |
104538202 | Apr 2015 | CN |
107565091 | Jan 2018 | CN |
107611468 | Jan 2018 | CN |
107644977 | Jan 2018 | CN |
107747957 | Mar 2018 | CN |
108155387 | Jun 2018 | CN |
2011-088813 | May 2011 | JP |
2011-103293 | May 2011 | JP |
2015-138777 | Jul 2015 | JP |
201343950 | Nov 2013 | TW |
Number | Date | Country | |
---|---|---|---|
20200002170 A1 | Jan 2020 | US |