TREA

Stripping compositions with mixtures of organic solvents and uses thereof

Follow

Information

  • Patent Grant
  • 5733380
  • Patent Number
    5,733,380
  • Date Filed
    Thursday, December 19, 1996
    28 years ago
  • Date Issued
    Tuesday, March 31, 1998
    26 years ago
Information
Abstract
Solvent assisted alkaline paint stripping can be speeded by using mixtures of (i) glycol and/or oligoglycol monoethers with (ii) unetherified glycols and oligoglycols and/or alkanolamines.
Description

BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates to compositions and processes for removing organic coatings, particularly paints and the like, from metal surfaces bearing such organic coatings, especially when the metal surfaces have been conversion coated, as with phosphate or chromate coatings, before being given an organic coating. Compositions that are effective in removing organic coatings in this way are often called "stripping compositions" or simply "strippers" and may be so denoted hereinafter. The compositions are at least partially aqueous and alkaline but also contain organic solvents, which may or may not be completely soluble in the aqueous part of the compositions. Additional details may be found in U.S. Pat. No. 3,308,066 of Mar. 7, 1967 to Murphy et al., the entire disclosure of which, except to the extent that it may be inconsistent with any explicit statement herein, is hereby incorporated herein by reference.
More particularly, this invention is concerned with compositions which include at least two chemically distinct types of organic solvents that act synergistically to achieve more rapid stripping than would be expected from the weighted average of stripping times of their individual components. In some of its embodiments, this invention is concerned with alkaline stripping compositions that eliminate or at least substantially reduce the potential for air pollution by excluding or substantially reducing any content of organic solvents recognized as significant contributors to air pollution when evaporated into the air, for example, any solvents listed as Hazardous Air Pollutants under the U.S. Clean Air Act.
2. Discussion of Related Art
Previously known alkaline stripping compositions are diverse, but the most effective previously known ones generally include ethylene glycol, one of the materials often known as "poly- �or oligo-!ethylene glycols" because the molecules thereof can be at least formally derived from two or more molecules of ethylene glycol by loss of one water molecule between each pair of ethylene glycol molecules to form an ether bond between the two molecules that replaces the --OH group formerly present in each molecule, and/or monoethers of ethylene glycol and/or its oligomers as defined above. Most if not all such materials have been implicated as significant sources of air pollution and are likely to be legally banned or severely restricted in use in the United States within the next few years.
DESCRIPTION OF THE INVENTION
Objects of the Invention
One major object of the invention is to provide compositions and processes that avoid using significant sources of air pollution while achieving adequate stripping capability compared with the established strippers using derivatives of ethylene glycol as noted above. Another alternative or concurrent object is to provide compositions containing at least two chemically distinct types of organic solvents that are more effective in stripping together than alone.
General Principles of Description
Except in the claims and the operating examples, or where otherwise expressly indicated, all numerical quantities in this description indicating amounts of material or conditions of reaction and/or use are to be understood as modified by the word "about" in describing the broadest scope of the invention. Practice within the numerical limits stated is generally preferred. Also, unless expressly stated to the contrary: percent, fraction of, "parts of", and ratio values are by weight; the term "polymer" includes "oligomer", "copolymer", "terpolymer", and the like; the description of a group or class of materials as suitable or preferred for a given purpose in connection with the invention implies that mixtures of any two or more of the members of the group or class are equally suitable or preferred; description of constituents in chemical terms refers to the constituents at the time of addition to any combination specified in the description, and does not necessarily preclude chemical interactions among the constituents of a mixture once mixed; specification of materials in ionic form implies the presence of sufficient counterions to produce electrical neutrality for the composition as a whole (any counterions thus implicitly specified should preferably be selected from among other constituents explicitly specified in ionic form, to the extent possible; otherwise such counterions may be freely selected, except for avoiding counterions that act adversely to the stated objects of the invention); and the term "mole" and its variations may be applied to elemental, ionic, and any other chemical species defined by number and type of atoms present, as well as to compounds with well defined molecules.
SUMMARY OF THE INVENTION
Compositions according to the invention may be working compositions suitable for direct use in stripping processes or concentrates, which contain some or all of the active ingredients of working compositions and are suitable for preparing working compositions thereof by dilution with water and/or mixing with other concentrates. Working compositions according to the invention comprise, preferably consist essentially of, or more preferably consist of, water and the following components:
(A) at least one dissolved alkali or alkaline earth metal hydroxide;
(B) at least one compound that is liquid at 25.degree. C. under normal atmospheric pressure and is selected from the group consisting of monoethers of (i) ethylene glycol, (ii) propylene glycol, (iii) butylene glycol, and (iv) "oligomers" as defined above of ethylene glycol, propylene glycol, and butylene glycol; and
(C) at least one compound that is liquid at 25.degree. C. under normal atmospheric pressure and is selected from the group consisting of (i) ethylene glycol, (ii) propylene glycol, (iii) butylene glycol, (iv) "oligomers" as defined above of ethylene glycol, propylene glycol, and butylene glycol, and (v) mono-, di-, and tri-alkanol amines; and, optionally, one or more of the following components:
(D) a component selected from the group consisting of gluconic acid, water soluble and water dispersible salts of gluconic acid, heptogluconic acid and its water soluble and water dispersible salts, and glucono-delta-lactone;
(E) surfactant (alternatively described as "wetting agent"); and
(F) alkaline salts exclusive of alkali metal and alkaline earth metal hydroxides.
Processes of utilizing working compositions according to the invention as defined above for stripping paint and like materials from metal surfaces are another embodiment of the invention.
DESCRIPTION OF PREFERRED EMBODIMENTS
It is normally preferred that compositions according to the invention as defined above should be substantially free from various ingredients. Specifically, it is increasingly preferred in the order given, independently for each preferably minimized component listed below, that primary compositions according to the invention, when directly contacted with coatings on metal in a process according to this invention, contain no more than 10, 5, 3, 2.0,1.0, 0.35, 0.10, 0.08, 0.04, 0.02, 0.01, 0.001, or 0.0002 percent of any of (i) hydrocarbons; (ii) any other compounds identified as carcinogenic; and (iii) any compound other than water that is not a hydrocarbon with a vapor pressure at 100.degree. C. that exceeds, with increasing preference in the order given, 500, 300, 200, 100, 70, 50, 30, 15, 10, 7, 5, 3, 1.5, or 0.7 millibars.
The alkali metal or alkaline earth metal hydroxide component (A) according to the invention preferably is selected from sodium and potassium hydroxide for a combination of economic and technical reasons. Sodium hydroxide is generally the least expensive among all the suitable hydroxides, and would normally be favored for that reason. However, potassium cations are compatible with larger concentrations of organic solvents in an aqueous phase than are sodium cations, and potassium hydroxide is not prohibitively expensive, so that when speed of stripping is more important than minimum cost of the stripping compositions, potassium is preferred because it can be used in higher concentrations that favor faster stripping. Lithium and alkaline earth cations are even less compatible with organic cosolutes than sodium and usually are not preferred for that reason, although workable at low concentrations. Rubidium and cesium hydroxides are expected to be highly effective in compositions according to the invention but are too expensive for ordinary use.
The concentration of component (A) in a working composition according to the invention may vary over quite wide limits. Generally, faster stripping will be achieved with higher concentrations of component (A), with all other factors equal. Thus, concentrations up to the solubility limit of the particular hydroxide used could be workable in various circumstances. However, very high concentrations of hydroxides may reduce the solubility of components (B) and (C) in the aqueous phase so much that stripping will actually be impeded. Generally, the concentration of component (A) preferably is, with increasing preference in the order given, at least 0.1, 0.3, 0.5, or 0.8 gram moles per kilogram (hereinafter usually abbreviated "M/kg"), and for removing difficult paints or similar coatings on alkali resistant metal surfaces still more preferably is, with increasing preference in the order given, at least 1.1, 1.4, 1.7, 2.0, 2.2, 2.4, 2.6, 2.7, 2.8, 2.9, or 3.0 M/kg of total working composition. Independently, in most circumstances the concentration of component (A) in a working composition according to the invention preferably is, with increasing preference in the order given, not more than 10, 8, 6, or 5 M/kg of total working composition and for one preferred embodiment still more preferably is not more than 4.5, 4.1, 3.8, 3.6, 3.5, 3.3, 3.2, or 3.1 M/kg of total working composition.
The total of components (B) and (C) in working compositions according to this invention preferably is, with increasing preference in the order given, at least 1, 3, 5, 7, 9, 10, 11, 12, 13, 14, or 15.0 percent and independently preferably is, with increasing preference in the order given, less than or equal to 50, 40, 30, 25, 22, 20, 19, 18, 17, 16.0, or 15.5 percent.
The glycol unit residues in components (B) and (C) as described above preferably are those of ethylene or propylene glycol. Propylene glycols and oligomers thereof with either or both of 1,2- or 1,3-propanediol structure or residues therefrom may be used, but molecules with the 1,2 substituted structure are usually preferred because they are usually less expensive. Independently, the molecules of component (B) preferably: either contain at least two glycol residues each or contain one glycol residue and a total of at least 5 carbon and oxygen atoms in their etherifying moiety; independently preferably contain, with increasing preference in the order given, at least 4, 5, 6, or 7 carbon atoms each, and independently preferably contain, with increasing preference in the order given, not more than 14, 12, 11, or 10 carbon atoms each. The glycols, glycol residues, and/or etherifying moieties in the molecules of components (B) and (C) may be straight or branched aliphatic, cycloaliphatic, aromatic, or heterocyclic and may include unsaturation and substituent groups such as ether groups and halogens that do not substantially dish paint stripping ability. Normally, however, primarily for reasons of economy, unsubstituted aliphatic glycols, glycol ethers, and etherifying moieties are preferred.
An important characteristic of many preferred embodiments of the invention is the existence of a synergistic effect, as defined below, between components (B) and (C). A synergistic effect for the purposes of this description is defined to exist whenever a composition according to this invention is found to strip paint more rapidly than would be expected from the weighted average of the stripping times of comparison compositions in which only component (B) or component (C) alone is used, with other constituents and physical conditions being kept constant. In mathematical terms, if (i) component (B) is present in the composition in a fraction "b" parts by weight of the total "t" pans by weight of components (B) and (C), (ii) the stripping time for a constant type and thickness of organic coating to be stripped from a constant metal substrate at a constant temperature by a composition containing t parts of component (B) and no component (C) is denoted as "S.sub.b " and the stripping time under the same conditions, except for using a composition containing t parts of component (C) and no component (B) is denoted as "S.sub.c ", then the weighted average expected stripping time, "W", for the composition containing both components (B) and (C) is defined as follows:
W=b.multidot.S.sub.b +(1-b).multidot.S.sub.c.
The "percent synergy" of the actual stripping time "S.sub.(b+c) " is defined to equal �100(W-S.sub.b+c)))W!. If this value is negative, the percentage is defined to represent "anti-synergy", because the mixture strips more slowly than would be expected from its individual constituents. Compositions according to this invention that have types and amounts of components (B) and (C) that have a positive percent synergy for stripping at least one type of organic coating from metal under at least one set of physical conditions are preferred embodiments of this invention, with compositions including combinations with higher positive percent synergy values increasingly more preferred.
Several specific preferred combinations for components (B) and (C) have been discovered for specific examples of components (B) and (C) identified by the following abbreviations: DEGMPE=diethylene glycol monopropyI ether; PG=propylene glycol; DPG=dipropylene glycol; TPG=tripropylene glycol; MEA=monoethanolamine; DEGMnBE=diethylene glycol monon-butyl ether; TEGMME=triethylene glycol monomethyl ether; TEGMEE=triethylene glycol monoethyl ether; TEGMnBE=triethylene glycol monon-butyl ether; DPGMPE=dipropylene glycol monopropyl ether; DPGMnBE=dipropylene glycol monon-butyl ether; TPGMnBE=tripropylene glycol monon-butyl ether; DPGMtBE=dipropylene glycol monot-butyl ether; EGMFE=ethylene glycol monofurfuryl ether; DEGMHE=diethylene glycol monohexyl ether; TPGMME=tripropylene glycol monomethyl ether; DPGMME=dipropylene glycol monomethyl ether. Some preferred combinations are:
EGMFE and TPG, with a fraction of TPG that preferably is at least, with increasing preference in the order given, 0.40, 0.50, 0.60, 0.70, or 0.80 and independently preferably is, with increasing preference in the order given, less than or equal to 0.95.0.90, 0.85, or 0.81;
DEGMPE and MEA, with a fraction of MEA that preferably is at least, with increasing preference in the order given, 0.10, 0.20, 0.30, 0.40, 0.50, or 0.55 and that independently preferably is less than or equal to, with increasing preference in the order given, 0.90, 0.80, 0.70, or 0.65;
DEGMPE and PG, with a fraction of PG that preferably is, with increasing preference in the order given, at least 0.50, 0.55, or 0.59 and independently preferably is, with increasing preference in the order given, less than or equal to, with increasing preference in the order given, 0.75, 0.65, or 0.61;
DEGMPE and DPG, with a fraction of DPG that preferably is, with increasing preference in the order given, at least 0.10, 0.19, and 0.39 and independently preferably is, with increasing preference in the order given, less than or equal to 0.90, 0.85, or 0.81;
TEGMME and MEA, with a fraction of MEA that preferably is, with increasing preference in the order given, at least 0.40, 0.45, 0.50, 0.55, or 0.60 and independently preferably is, with increasing preference in the order given, less than or equal to 0.80, 0.70, 0.65, or 0.61;
TEGMME and PG, with a fraction of PG that preferably is, with increasing preference in the order given, at least 0.15, 0.20, 0.30, or 0.39 and independently preferably is, with increasing preference in the order given, less than or equal to 0.80, 0.70, 0.65, or 0.60;
TEGMME and DPG, with a fraction of DPG that preferably is, with increasing preference in the order given, at least 0.35, 0.55, or 0.60 and independently preferably is, with increasing preference in the order given, less than or equal to 0.95, 0.90, 0.85, or 0.81;
DPGMME and PC, with a fraction of DPG that preferably is at least, with increasing preference in the order given, 0.05, 0.10, 0.15, or 0.20 and independently preferably is less than or equal to, with increasing preference in the order given, 0.90, 0.85, or 0.81 and in more weakly alkaline solutions still more preferably is, with increasing preference in the order given, less than or equal to 0.55, 0.41, 0.35, 0.30, 0.25, or 0.21;
DPGMME and DPG, with a fraction of DPG that preferably is, with increasing preference in the order given, at least 0.10, 0.15, or 0.20 and for removing paint less than or equal to 50 microns thick more preferably is, with increasing preference in the order given, less than or equal to 0.30, 0.40, 0.50, 0.60, 0.70, or 0.79 and independently preferably is, with increasing preference in the order given, less than or equal to 0.90, 0.85, or 0.81;
DPGMME and TPG, with a fraction of TPG that preferably is, with increasing preference in the order given, at least 0.25, 0.35, or 0.40 and in relatively weakly alkaline compositions at least 0.55 or 0.60 and independently preferably is, with increasing preference in the order given, less than or equal to 0.90, 0.85, or 0.81;
DEGMnBE and MEA, with a fraction of MEA that preferably is, with increasing preference in the order given, at least 0.15, 0.20, or 0.58 and independently preferably is, with increasing preference in the order given, less than or equal to 0.90, 0.85, 0.80, 0.70, or 0.61;
DEGMnBE and PC, with a fraction of PC that preferably is, with increasing preference in the order given, at least 0.20, 0.30, 0.35, or 0.40 and independently preferably is, with increasing preference in the order given, less than or equal to 0.90, 0.80, 0.70, or 0.62;
DEGMnBE and DPG, with a fraction of DPG that preferably is, with increasing preference in the order given, at least 0.50, 0.55, or 0.60 and independently preferably is, with increasing preference in the order given, less than or equal to 0.95, 0.90, 0.85, or 0.81;
TEGMEE and MEA, with a fraction of MEA that preferably is, with increasing preference in the order given, at least 0.12, 0.18, or 0.38 and independently preferably is, with increasing preference in the order given, less than or equal to 0.80, 0.60, 0.55, 0.50, 0.45, or 0.41;
TEGMEE and PC, with a fraction of PG that preferably either (i) is at least, with increasing preference in the order given, 0.10, 0.15, or 0.20 and independently preferably is, with increasing preference in the order given, not more than 0.45, 0.40, 0.35, 0.30, or 0.25 or (ii) is at least, with increasing preference in the order given, 0.50, 0.55, or 0.60 and independently preferably is, with increasing preference in the order given, less than or equal to 0.90, 0.85, 0.80, 0.75, 0.70, or 0.65;
TEGMEE and DPG, with a fraction of DPG that preferably is, with increasing preference in the order given, at least 0.10, 0.15, or 0.20 and independently preferably is, with increasing preference in the order given, less than or equal to 0.95, 0.90, 0.85, 0.80, 0.75, 0.70, 0.65, or 0.61;
TEGMEE and TPG, with a fraction of TPG that preferably is, with increasing preference in the order given, at least 0.10, 0.15, 0.18, or 0.19 and independently preferably is, with increasing preference in the order given, less than or equal to 0.90, 0.85, 0.81, 0.71, 0.55, 0.40, or 0.21;
DEGMHE and DPG, with a fraction of DPG that preferably is, with increasing preference in the order given, at least 0.20, 0.30, 0.35, or 0.39 and independently preferably is, with increasing preference in the order given, less than or equal to 0.81, 0.61, 0.50, 0.46, or 0.41;
TEGMnBE and MEA, with a fraction of MEA that preferably is, with increasing preference in the order given, at least 0.45, 0.50, 0.55, or 0.59 and independently preferably is, with increasing preference in the order given, less than or equal to 0.90, 0.81, 0.71, 0.66, or 0.61;
TEGMnBE and PG, with a fraction of PG that preferably is, with increasing preference in the order given, at least 0.45, 0.50, 0.55, or 0.59 and independently preferably is, with increasing preference in the order given, less than or equal to 0.90, 0.85, or 0.81;
TEGMnBE and DPG, with a fraction of DPG that preferably is, with increasing preference in the order given, at least 0.10, 0.15, 0.20, 0.30, or 0.40 and independently preferably is, with increasing preference in the order given, less than or equal to 0.81, 0.70, or 0.61;
TPGMME and DPG, with a fraction of DPG that preferably is, with increasing preference in the order given, at least 0.20, 0.40, 0.50, 0.60, 0.70, or 0.80 and independently preferably is, with increasing preference in the order given, less than or equal to 0.95, 0.90, 0.85, or 0.81; and
TPGMME and TPG, preferably with a fraction of TPG that is, with increasing preference in the order given, at least 0.50, 0.60, 0.70, or 0.80 and independently preferably is, with increasing preference in the order given, less than or equal to 0.95, 0.90, 0.85, or 0.81.
The above-noted preferred combinations of components (B) and (C) preferably are used as such, and not in mixtures among themselves. These preferred combinations may be formulated as concentrates according to the invention, in compositions containing no other essential ingredients, suitable for adding to any of the well established alkaline stripping agents for paint and the like. These combinations, with the same relative proportions among components (B) and (C), may also advantageously be used in complete concentrates, also containing water and component (A), which are suitable for use as working compositions after dilution with water only, or in working compositions according to the invention and processes of stripping coatings from metals therewith.
When both of components (B) and (C) contain at least six carbon atoms per molecule, there may be phase separation problems in complete concentrates if only the most preferred constituents as outlined above are used in the complete concentrates. If such phase separation problems are encountered, they may often be overcome by adding a third component, usually ethylene glycol or propylene glycol. For example, when the above noted preferred combination of TPGMME for component (B) and DPG for component (B) is used, a ratio of dipropylene glycol to propylene glycol in a working composition that preferably is, with increasing preference in the order given, not less than or equal to 1.0, 1.5, 2.0, 2.3, 2.6, 2.8, 2.9, 3.0, 3.1, or 3.15 and independently preferably is, with increasing preference in the order given, not more than 50, 25, 15, 10, 7.5, 5.0, 4.5, 4.2, 3.9, 3.7, 3.6, 3.5, 3.4, 3.3, or 3.25 has been found to yield exceptionally favorable results in a preferred complete concentrate according to the invention that contains potassium hydroxide as component (A).
Optional component (D) is believed to have at least two possibly favorable effects on working compositions according to the invention: mutual solubilization of hydroxide and the organic components and an ability to attack phosphate conversion coatings which often underlie the paint or similar coating to be stripped and thereby to speed the stripping process by undermining the bond between the paint film to be removed and the underlying metal. It is accordingly preferred in most such working compositions that the concentration of component (D) in a working composition according to this invention is, with increasing preference in the order given, not less than or equal to 0.01, 0.03, 0.05, 0.07, 0.09, 0.11, 0.13, 0.15, 0.16, 0.17, 0.18, 0.19, or 0.20 M/kg of total composition and independently preferably is, with increasing preference in the order given, not more than 2.0, 1.5, 1.0, 0.8, 0.6, 0.50, 0.45, 0.40, 0.37, 0.34, 0.31, 0.29, 0.27, 0.25, 0.24, 0.23, 0.22, or 0.21 M/kg of total composition. The most preferred chemical compound for use in preparing compositions according to the invention to provide component (D) is gluconic acid, although it is expected to be present in salt form in the highly alkaline working compositions.
Component (E) of surfactant or wetting agent is not generally needed, but may be useful in some cases for removing coatings that have an extraordinarily hydrophobic surface. Component (F) of alkaline salts other than hydroxides also is generally not needed, but may be advantageous in cases where the amount of component (A) is lower than is normally preferred, in order to protect the underlying metal surface from alkaline attack.
Speed of stripping is normally substantially increased at higher temperatures. Therefore, it is normally preferred that the temperature of working compositions when in actual contact with coatings to be stripped be maintained at a temperature of at least, with increasing preference in the order given, 75, 80, 85, 90, 92, 94, 95, 96, 97, 98, 99, 100, 101, 102, 103, or 104.degree. C., or at the boiling temperature of the working composition if that is higher. It is preferred that the working composition separate into two liquid phases at working temperatures, as this has been found to promote stripping action. However, the solubility of organic compounds in alkaline aqueous ionic solutions is often greater at lower temperatures, so that a preferred composition may form a single phase at normal ambient temperatures, i.e., 15.degree.-25.degree. C.





The invention may be further appreciated by consideration of the following examples and comparative examples.
Preparation of Test Substrates
Cold rolled steel sheets were first normally cleaned and activated and then either (i) phosphate conversion coated with BONDERITE.RTM. 1000 iron phosphate conversion coating forming composition and then painted with a thickness of about 20 micrometers (hereinafter usually abbreviated ".mu.m") of DURACRON.TM. 200 acrylic appliance paint (denoted type "A" below) or (ii) phosphate conversion coated with BONDERITE.RTM. 952 zinc-manganese-nickel phosphate conversion coating forming composition and then painted with a thickness of about 56 .mu.m of DURACRON.TM. 200 paint (denoted type "B" below).
Preparation of Working Compositions for Testing--Group 1
The working stripping compositions (not all of which are necessarily according to the invention) were prepared from two concentrates: An aqueous alkaline concentrate consisting of 46% potassium hydroxide, 8% of a solution of 50% of gluconic acid in water, and 46% of water and an organic additive concentrate with component(s) as shown in Table 1 below. The mount of the organic additive was 15% of each working composition in Table 1, the amount of the alkaline concentrate is listed in Table 1, and the balance of the working compositions was tap water. The working compositions were maintained at boiling temperature and normal ambient atmospheric pressure during the testing, with water replenishment as needed to maintain the original volume. (The boiling temperature is about 104.degree. C. for compositions that contained 30% of the alkaline concentrate and is about 109.degree. C. for compositions that contained 50% of the alkaline concentrate. All of the organic additives tested have boiling points so much higher than water that replenishing them was not needed to maintain substantially constant composition.)
Painted, pre-phosphated test panels prepared as described above were immersed in the working compositions and observed until the paint had been completely stripped, or, in a few cases, until a preset time limit had been exceeded. The time required for stripping was then taken from a timing device that had been started at the time of immersion; if stripping was not achieved, the time limit is shown instead, following a ">" sign in the tables below.
Results are shown in Table 1 below, along with some comparative tests with numbers beginning with "C" in which a single organic compound is used in the working composition and a few comparative examples in which two types of (oligo-)glycol ethers are mixed.
TABLE 1__________________________________________________________________________Test % AC Panel Type A Panel Type BNo. Organic Additive Composition in WC ST % S ST % S__________________________________________________________________________C-12 100% EGMFE 30 4.0 -- 6.0 --129 80% EGMFE + 20% TPG 30 6.5 -35 10.9 -49130 60% EGMFE + 40% TPG 30 4.2 25 8.7 -1131 40% EGMFE + 60% TPG 30 4.0 38 7.5 24132 20% EGMFE + 80% TPG 30 3.5 51 7.2 36C-4 100% TPG 30 8.0 -- 12.5 --C-1 100% DEGMPE 30 4.8 -- 9 -- 13 80% DEGMPE + 20% MEA 30 4.0 59 6.5 51 14 60% DEGMPE + 40% MEA 30 3.5 76 6.2 64 15 40% DEGMPE + 60% MEA 30 3.2 84 5.8 73 16 20% DEGMPE + 80% MEA 30 4.5 82 10 61C-5 100% MEA 30 >30* -- >30* --C-1.1 100% DEGMPE 30 4.8 -- 9.0 -- 1 80% DEGMPE + 20% PG 30 nm nm 7.0 22 2 60% DEGMPE + 40% PG 30 5.2 65 7.5 57 3.1 40% DEGMPE + 60% PG 30 4.0 80 6.2 71 4.1 20% DEGMPE + 80% PG 30 19 24 nm nmC-2.1 100% PG 30 >30* -- >30* --C-1.2 100% DEGMPE 50 4.0 -- 6.0 -- 3.2 40% DEGMPE + 60% PG 50 nm nm 3.0 85 4.2 20% DEGMPE + 80% PG 50 7.0 72 nm nmC-2.2 100% PG 50 >30 -- >30 -- 4.3 20% DEGMPE + 80% PG 70 4.0 nm 8.8 nmC-1.1 100% DEGMPE 30 4.8 -- 9.0 -- 5 80% DEGMPE + 20% DPG 30 3.0 52 7.5 29 6.1 60% DEGMPE + 40% DPG 30 nm nm 5.8 52 7.1 40% DEGMPE + 60% DPG 30 nm nm 6.5 52 8.1 20% DEGMPE + 80% DPG 30 3.5 66 6.3 58C-3.1 100% DPG 30 11.8 -- 16.5 --C-1.2 100% DEGMPE 50 4.0 -- 6.0 -- 6.2 60% DEGMPE + 40% DPG 50 nm nm 5.7 65 7.2 40% DEGMPE + 60% DPG 50 nm nm 4.7 62 8.2 20% DEGMPE + 80% DPG 50 nm nm 5 65C-3.2 100% DPG 50 8.0 -- 10.0 --C-1 100% DEGMPE 30 4.8 -- 9 -- 9 80% DEGMPE + 20% TPG 30 5.5 -1 9.2 5 10 60% DEGMPE + 40% TPG 30 5.8 5 9.5 9 11 40% DEGMPE + 60% TPG 30 5.5 18 9.8 12 12 20% DEGMPE + 80% TPG 30 6.2 16 11.5 3C-4 100% TPG 30 8.0 -- 12.5 --C-7.1 100% TEGMME 30 5.5 -- 9.4 -- 45 80% TEGMME + 20% MEA 30 6.5 38 13.0 4 46.1 60% TEGMME + 40% MEA 30 >18 nm 14.2 20 47.1 40% TEGMME + 60% MEA 30 >10 nm 16 26 48.1 20% TEGMME + 80% MEA 30 >10 nm 21 19C-5.1 100% MEA 30 >30* -- >30* --C-7.2 100% TEGMME 50 4.2 -- 6.2 -- 46.2 60% TEGMME + 40% MEA 50 4.0 72 5.2 67 47.2 40% TEGMME + 60% MEA 50 3.0 85 6.0 71 48.2 20% TEGMME + 80% MEA 50 4.2 83 9.0 64C-5.2 100% MEA 50 >30 -- >30 --C-7.1 100% TEGMME 30 5.5 -- 9.4 -- 41.1 80% TEGMME + 20% PG 30 10.0 -96 14.8 -74 42.1 60% TEGMME + 40% PG 30 10.0 35 21 -19 43.1 40% TEGMME + 60% PG 30 15 26 21.2 3 44.1 20% TEGMME + 80% PG 30 >15 nm 40 -55C-2.1 100% PG 30 >30* -- >30* --C-7.2 100% TEGMME 50 4.2 -- 6.2 -- 41.2 80% TEGMME + 20% PG 50 4.0 57 5.2 53 42.2 60% TEGMME + 40% PG 50 3.5 76 5.0 68 43.2 40% TEGMME + 60% PG 50 3.2 84 5.8 72 44.2 20% TEGMME + 80% PG 50 7.0 72 7.2 71C-2.2 100% PG 50 >30 -- >30 --C-7.1 100% TEGMME 30 5.5 -- 9.4 -- 37 80% TEGMME + 20% DPG 30 5.2 23 11 -2 38 60% TEGMME + 40% DPG 30 8.8 -10 12.8 -5 39.1 40% TEGMME + 60% DPG 30 >15 <-62 nm nm 40.1 20% TEGMME + 80% DPG 30 13.1 -24 16.8 -11C-3.1 100% DPG 30 11.8 -- 16.5 --C-7.2 100% TEGMME 50 4.2 -- 6.2 -- 39.2 40% TEGMME + 60% DPG 50 3.8 41 5.4 36 40.2 20% TEGMME + 80% DPG 50 4.2 42 6 35C-3.2 100% DPG 50 8 -- 10 --C-5 100% TEGMME 30 5.5 -- 9.4 -- 33 80% TEGMME + 20% TPG 30 7.0 -17 12 -20 34 60% TEGMME + 40% TPG 30 10 -54 14 -32 35 40% TEGMME + 60% TPG 30 6.8 3 12.6 -12 36 20% TEGMME + 80% TPG 30 5.0 33 12 -1C-4 100% TPG 30 8.0 -- 12.5 --C-15.1 100% DPGMME 30 30 -- 45.7 --159.1 80% DPGMME + 20% PG 30 8.8 66 60 -49160.1 60% DPGMME + 40% PG 30 9.3 69 60 -52161.1 40% DPGMME + 60% PG 30 35 -17 60 -65162.1 20% DPGMME + 80% PG 30 >60 -100 >60 -81C-2.1 100% PG 30 >30* -- >30* --C-15.2 100% DPGMME 50 13.3 -- 20.7 --159.2 80% DPGMME + 20% PG 50 7.8 53 11 51160.2 60% DPGMME + 40% PG 50 7.8 61 18.5 24161.2 40% DPGMME + 60% PG 50 6.0 74 12.7 52162.2 20% DPGMME + 80% PG 50 6.2 77 20 29C-2.2 100% PG 50 >30 -- >30 --C-15.1 100% DPGMME 30 30 -- 45.7 --163.1 80% DPGMME + 20% DPG 30 10 60 13.1 65164.1 60% DPGMME + 40% DPG 30 6.0 74 8.5 75165.1 40% DPGMME + 60% DPG 30 6.2 68 9.0 68166.1 20% DPGMME + 80% DPG 30 5.8 62 11.5 49C-3.1 100% DPG 30 11.8 -- 16.5 --C-15.2 100% DPGMME 50 13.3 -- 20.7 --163.2 80% DPGMME + 20% DPG 50 6.9 44 8.8 53164.2 60% DPGMME + 40% DPG 50 5.0 55 5.8 65165.2 40% DPGMME + 60% DPG 50 4.2 58 5.5 61166.2 20% DPGMME + 80% DPG 50 3.7 59 5.7 53C-3.2 100% DPG 50 8.0 -- 10.0 --C-15.1 100% DPGMME 30 30 -- 45.7 --167.1 80% DPGMME + 20% TPG 30 10.7 58 16.5 57168.1 60% DPGMME + 40% TPG 30 9.2 57 14 57169.1 40% DPGMME + 60% TPG 30 6.5 61 9.0 65170.1 20% DPGMME + 80% TPG 30 6.2 50 8.5 56C-4.1 100% TPG 30 8.0 -- 12.5 --C-15.2 100% DPGMME 50 13.3 -- 20.7 --167.2 80% DPGMME + 20% TPG 50 7.5 38 10.6 43168.2 60% DPGMME + 40% TPG 50 6.2 42 9.0 46169.2 40% DPGMME + 60% TPG 50 9.0 5 14 6170.2 20% DPGMME + 80% TPG 50 8.8 -7 12.1 6C-4.2 100% TPG 50 70 -- 11.0 --C-6 100% DEGMnBE 30 6.5 -- 11.6 -- 17 80% DEGMnBE + 20% MEA 30 5.5 51 11.5 25 18 60% DEGMnBE + 40% MEA 30 5.8 64 12 37 19 40% DEGMnBE + 60% MEA 30 4.8 77 9.8 57 20 20% DEGMnBE + 80% MEA 30 6 76 12.2 54C-5 100% MEA 30 >30* -- >30* --C-6 100% DEGMnBE 30 6.5 -- 11.6 -- 21 80% DEGMnBE + 20% PG 30 6.0 46 10.5 31 22 60% DEGMnBE + 40% PG 30 5.0 69 9.8 48 23 40% DEGMnBE + 60% PG 30 5.0 76 10.0 56 24 20% DEGMnBE + 80% PG 30 7.8 69 10.0 62C-2 100% PG 30 >30* -- >30* --C-6 100% DEGMnBE 30 6.5 -- 11.6 -- 25 80% DEGMnBE + 20% DPG 30 7.2 5 13.5 -7 26 60% DEGMnBE + 40% DPG 30 8.8 -2 11.0 19 27 40% DEGMnBE + 60% DPG 30 5.5 43 10.2 30 28 20% DEGMnBE + 80% DPG 30 5.5 49 7.5 52C-3 100% DPG 30 11.8 -- 16.5 --C-6 100% DEGMnBE 30 6.5 -- 11.6 -- 29 80% DEGMnBE + 20% TPG 30 8.0 -18 14.5 -23 30 60% DEGMnBE + 40% TPG 30 11.0 -55 15.8 -32 31 40% DEGMnBE + 60% TPG 30 6.2 16 12.5 -3 32 20% DEGMnBE + 80% TPG 30 9.0 -17 11.8 4C-4 100% TPG 30 80 -- 12.5 --C-7.1 100% TEGMEE 30 5.5 -- 9.4 -- 61 80% TEGMEE + 20% MEA 30 4.0 62 7.8 42 62 60% TEGMEE + 40% MEA 30 4.0 74 7.5 57 63.1 40% TEGMEE + 60% MEA 30 6.5 68 14.9 32 64.1 20% TEGMEE + 80% MEA 30 6.5 74 18 30C-5.1 100% MFA 30 >30* -- >30* --C-7.2 100% TEGMEE 50 4.2 -- 6.2 -- 63.2 40% TEGMEE + 60% MEA 50 3.5 82 6.7 67 64.2 20% TEGMEE + 80% MEA 50 4.2 83 6 76C-52 100% MEA 50 >30 -- >30 --C-7.1 100% TEGMEE 30 5.1 -- 9.1 -- 49 80% TEGMEE + 20% PG 30 4.0 60 9.0 32 50 60% TEGMEE + 40% PG 30 5.0 67 9.3 47 51.1 40% TEGMEE + 60% PG 30 >10 nm 15 31 52.1 20% TEGMEE + 80% PG 30 10.0 60 20 23C-2.1 100% PG 30 >30* -- >30* --C-7.2 100% TEGMEE 50 3.9 -- 6.0. -- 51.2 40% TEGMEE + 60% PG 50 2.8 86 6.0 71 52.2 20% TEGMEE + 80% PG 50 3.0 88 6.4 75C-2.2 100% PG 50 >30 -- >30 --C-7.1 100% TEGMEE 30 5.1 -- 9.1. -- 53 80% TEGMEE + 20% DPG 30 3.8 41 10.5 1 54 60% TEGMEE + 40% DPG 30 3.8 51 7.8 35 55.1 40% TEGMEE + 60% DPG 30 9.0 1 7.3 46 56.1 20% TEGMEE + 80% DPG 30 9.2 12 15.5 -3C-3.1 100% DPG 30 11.8 -- 16.5 --C-7.2 100% TEGMEE 50 3.9 -- 6.0 -- 55.2 40% TEGMEE + 60% DPG 50 6.0 6 5.2 38 56.2 20% TEGMEE + 80% DPG 50 4.8 33 5.7 38C-32 100% DPG 50 8.0 -- 10.0 --C-7 100% TEGMEE 30 5.1 -- 9.1 -- 57 80% TEGMEE + 20% TPG 30 4.2 26 8.5 13 58 60% TEGMEE + 40% TPG 30 5.0 20 8.8 16 59 40% TEGMEE + 60% TPG 30 5.5 20 12.3 -10 60 20% TEGMEE + 80% TPG 30 5.2 30 12.2 -3C-4 100% TPG 30 8.0 -- 12.5 --C-13 100% DEGMHE 30 9.0 -- 16.5 --141 80% DEGMHE + 20% PG 30 6.1 54 18.1 6142 60% DEGMHE + 40% PG 30 9.2 47 19.1 13143 40% DEGMHE + 60% PG 30 11.5 47 18.5 25144 20% DEGMHE + 80% PG 30 9.0 65 13 52C-2 100% PG 30 >30* -- >30* --C-13 100% DEGMHE 30 9.0 -- 16.5 --137 80% DEGMHE + 20% DPG 30 8.8 8 16.6 -1138 60% DEGMHE + 40% DPG 30 5.2 49 10.8 35139 40% DEGMHE + 60% DPG 30 6.0 44 11.7 29140 20% DEGMHE + 80% DPG 30 6.2 45 12.6 24C-3 100% DPG 30 11.8 -- 16.5 --C-13 100% DEGMHE 30 9.0 -- 16.5 --133 80% DEGMHE + 20% TPG 30 8.3 6 19 -21134 60% DEGMHE + 40% TPG 30 8.5 1 13.7 8135 40% DEGMHE + 60% TPG 30 8.8 -5 14 1136 20% DEGMHE + 80% TPG 30 9.2 -12 14.6 -10C-4 100% TPG 30 8.0 -- 12.5 --C-8 100% TEGMnBE 30 7.0 -- 12.2 -- 65 80% TEGMnBE + 20% MEA 30 7.0 40 14.3 9 66 60% TEGMnBE + 40% MEA 30 7.0 57 14.3 26 67 40% TEGMnBE + 60% MEA 30 4.7 77 9.2 60 68 20% TEGMnBE + 80% MEA 30 6.0 76 10.0 62C-5 100% MEA 30 >30* -- >30* --C-8 100% TEGMnBE 30 7.0 -- 12.2 -- 69 80% TEGMnBE + 20% PG 30 7.0 40 13 18 70 60% TEGMnBE + 40% PG 30 7.0 57 12.8 34 71 40% TEGMnBE + 60% PG 30 6.2 70 12.2 47 72 20% TEGMnBE + 80% PG 30 6.2 76 12.2 54C-2 100% PG 30 >30* -- >30* --C-8 100% TEGMnBE 30 7.0 -- 12.2 -- 73 80% TEGMnBE + 20% DPG 30 5.0 37 13.2 -1 74 60% TEGMnBE + 40% DPG 30 5.2 42 9.9 29 75 40% TEGMnBE + 60% DPG 30 5.0 49 9.8 34 76 20% TEGMnBE + 80% DPG 30 5.5 49 10.5 33C-3 100% DPG 30 11.8 -- 16.5 --C-8 100% TEGMnBE 30 7.0 -- 12.2 -- 77 80% TEGMnBE + 20% TPG 30 9.8 -36 11.3 8 78 60% TEGMnBE + 40% TPG 30 9.8 -32 11.5 7 79 40% TEGMnBE + 60% TPG 30 10.0 -32 12 3 80 20% TEGMnBE + 80% TPG 30 10.0 -28 12 4C-4 100% TPG 30 8.0 -- 12.5 --C-9 100% DPGMnBE 30 43 -- 52 -- 93 80% DPGMnBE + 20% MEA 30 30 26 34 29 94 60% DPGMnBE + 40% MEA 30 20 47 26 40 95 40% DPGMnBE + 60% MEA 30 18 49 24 38 96 20% DPGMnBE + 80% MEA 30 10.8 67 20 42C-5 100% MEA 30 >30* -- >30* --C-9.1 100% DPGMnBE 30 43 -- 52 -- 81.1 80% DPGMnBE + 20% PG 30 >10 nm 70 -31 82.1 60% DPGMnBE + 40% PG 30 >10 nm 71 -64 83.1 40% DPGMnBE + 60% PG 30 >10 nm 65 -68 84.1 20% DPGMnBE + 80% PG 30 >10 nm 125 -263C-2.1 100% PG 30 >30* -- >30* --C-9.2 100% DPGMnBE 50 37 -- 36 -- 81.2 80% DPGMnBE + 20% PG 50 >10 nm 60 -72 82.2 60% DPGMnBE + 40% PG 50 >10 nm 60 -79 83.2 40% DPGMnBE + 60% PG 50 >10 nm 45 -39 84.2 20% DPGMnBE + 80% PG 50 >10 nm 70 -124C-2.2 100% PG 50 >30 -- >30 --C-9 100% DPGMnBE 30 43 -- 52 -- 85 80% DPGMnBE + 20% DPG 30 17 54 45 0 86 60% DPGMnBE + 40% DPG 30 45 -47 57 -51 87 40% DPGMnBE + 60% DPG 30 20 18 25 19 88 20% DPGMnBE + 80% DPG 30 12 33 16 32C-3 100% DPG 30 11.8 -- 16.5 --C-9 100% DPGMnBE 30 43 -- 52 -- 89 80% DPGMnBE + 20% TPG 30 30 17 45 -2 90 60% DPGMnBE + 40% TPG 30 16.5 43 22 39 91 40% DPGMnBE + 60% TPG 30 9.8 55 20 29 92 20% DPGMnBE + 80% TPG 30 8.0 47 15.2 25C-4 100% TPG 30 8.0 -- 12.5 --C-11 100% DPGMtBE 30 46 -- 55 --125 80% DPGMtBE + 20% MEA 30 31 28 34 32126 60% DPGMtBE + 40% MEA 30 28 29 30 33127 40% DPGMtBE + 60% MEA 30 15 59 17 58128 20% DPGMtBE + 80% MEA 30 23 31 34 3C-5 100% MEA 30 >30* -- >30* --C-11 100% DPGMtBE 30 46 -- 55 --121 80% DPGMtBE + 20% PG 30 38 11 66 -32122 60% DPGMtBE + 40% PG 30 24 39 55 -22123 40% DPGMtBE + 60% PG 30 39 -7 45 -13124 20% DPGMtBE + 80% PG 30 49 -48 99 -183C-2 100% PG 30 >30* -- >30* --C-11 100% DPGMtBE 30 46 -- 55 --117 80% DPGMtBE + 20% DPG 30 38 3 49 -4118 60% DPGMtBE + 40% DPG 30 20 38 32 19119 40% DPGMtBE + 60% DPG 30 15 41 26 18120 20% DPGMtBE + 80% DPG 30 13 30 19 21C-3 100% DPG 30 11.8 -- 16.5 --C-11 100% DPGMtBE 30 46 -- 55 --113 80% DPGMtBE + 20% TPG 30 47 -22 54 -16114 60% DPGMtBE + 40% TPG 30 24 22 33 13115 40% DPGMtBE + 60% TPG 30 16 31 28 5116 20% DPGMtBE + 80% TPG 30 10.4 33 22 -5C-4 100% TPG 30 8.0 -- 12.5 --C-14.1 100% TPGMME 30 32.5 -- 45** --147.1 80% TPGMME + 26% PG 30 26 12 38.7 8148.1 60% TPGMME + 40% PG 36 18.4 42 29.6 24149.1 40% TPGMME + 60% PG 30 18.3 41 27.1 25150.1 20% TPGMME + 80% PG 30 17.3 43 24.2 27C-2.1 100% PG 30 >30* -- >30* --C-14.2 100% TPGMME 50 9.0 -- 19.3 --147.2 80% TPGMME + 20% PG 50 25 -89 39.3 -83148.2 60% TPGMME + 40% PG 50 17.5 -1 30.7 -30149.2 40% TPGMME + 60% PG 50 17 21 26.5 -3150.2 20% TPGMME + 80% PG 50 15.5 40 22.1 21C-2.2 100% PG 50 >30 -- >30 --C-14.1 100% TPGMME 30 32.5 -- 45** --151.1 80% TPGMME + 20% DPG 30 11.7 57 21.5 44152.1 60% TPGMME + 40% DPG 30 9.2 62 17 49153.1 40% TPGMME + 60% DPG 30 8.7 57 12.1 57154.1 20% TPGMME + 80% DPG 30 7.5 53 9.2 59C-3.1 100% DPG 30 11.8 -- 16.5 --C-14.2 100% TPGMME 50 9.0 -- 19.3 --151.2 80% TPGMME + 20% DPG 50 10.1 -15 16.6 5152.2 60% TPGMME + 40% DPG 50 6.5 24 12.5 20153.2 40% TPGMME + 60% DPG 50 6.0 29 8.1 41154.2 20% TPGMME + 80% DPG 50 4.5 45 5.0 58C-3.2 100% DPG 50 8 -- 10 --C-14.1 100% TPGMME 30 32.5 -- 45** --155.1 80% TPGMME + 20% TPG 30 20 28 41 -5156.1 60% TPGMME + 40% TPG 30 12.8 44 22.7 29157.1 40% TPGMME + 60% TPG 30 11.4 36 18.8 26158.1 20% TPGMME + 80% TPG 30 10.5 19 12.7 33C-4.1 100% TPG 30 8.0 -- 12.5 --C-14.2 100% TPGMME 50 9.0 -- 19.3 --155.2 80% TPGMME + 20% TPG 50 14 -63 19.5 -11156.2 60% TPGMME + 40% TPG 50 9.2 -12 15.5 3157.2 40% TPGMME + 60% TPG 50 6.5 17 11 23158.2 20% TPGMME + 80% TPG 50 6.0 19 8.0 37C-4.2 100% TPG 50 7.0 -- 11.0 --C-10 100% TPGMnBE 30 70 -- 150 -- 97 80% TPGMnBE + 20% MEA 30 40 35 70 44 98 60% TPGMnBE + 40% MEA 30 27 50 55 46 99 40% TPGMnBE + 60% MEA 30 19.6 57 41 47100 20% TPGMnBE + 80% MEA 30 14.1 63 29 46C-5 100% MEA 30 >30* -- >30* --C-10 100% TPGMnBE 30 70 -- 150 --101 80% TPGMriBE + 20% PG 30 56 10 65 48102 60% TPGMnBE + 40% PG 30 70 -30 80 22103 40% TPGMnBE + 60% PG 30 51 -11 60 23104 20% TPGMnBE + 80% PG 30 30 21 37 31C-2 100% PG 30 >30* -- >30* --C-10 100% TPGMnBE 30 70 -- 150 --105 80% TPGMnBE + 20% DPG 30 40 31 60 51106 60% TPGMnBE + 40% DPG 30 20 57 37 62107 40% TPGMnBE + 60% DPG 30 14 60 29.5 58108 20% TPGMnBE + 80% DPG 30 10.2 56 14.3 67C-3 100% DPG 30 11.8 -- 16.5 --C-10 100% TPGMnBE 30 70 -- 150 --109 80% TPGMnBE + 20% TPG 30 46 20 50 59110 60% TPGMnBE + 40% TPG 30 31 31 48 49111 40% TPGMnBE + 60% TPG 30 12 63 23 66112 20% TPGMnBE + 80% TPG 30 10.0 51 16 60C-4 100% TPG 30 80 -- 12.5 --C-13 100% DEGMHE 30 9.0 -- 16.5 --145 50% DEGMHE + 50% EGMFE 30 4.5 31 9.0 20146 65% DEGMHE + 35% EGMFE 30 5.0 31 10.0 22C-12 100% EGMFE 30 4.0 -- 6.0 -__________________________________________________________________________ Footnotes for Table 1 *This lower limit was not directly measured, but was inferred from the value measured with 50 % of alkaline concentrate and the inevitable observation that stripping times are longer for strippers with only 30% o alkaline concentrate, with all other active ingredients maintained the same. **About 5% of the coating remained after this time, but the test was nevertheless discontinued. Abbreviations for Table 1 "AC" = "Alkaline Concentrate"; "WC" = "Working Composition"; "ST" = "Stripping Time"; "% S" = "Percent Synergy" or if the value is negative, "Percent Antisynergy"; "Min" = "Minutes"; "nm" = "not measured", or, in columns where the values are calculated rather than directly measured, "not meaningful" (because at least one directly measured value required for the calcuIation was not measured at all or was merely given a lower limit rather than a complete measurement).
Claims
  • 1. A process for stripping an organic protective coating from a metal substrate by contacting the metal substrate with a heated aqueous liquid stripping composition maintained during the contacting at a temperature of at least about 90.degree. C., said aqueous liquid stripping composition comprising water and:
  • (A) a component selected from the group consisting of dissolved alkali metal hydroxides and alkaline earth metal hydroxides; and
  • (B) a component (B) selected from the group consisting of glycol monoethers, glycols, and alkanol,
  • wherein the improvement comprises utilizing as component (B) a mixture selected from the group consisting of:
  • EGMFE and TPG, with a fraction by weight of TPG that is from about 0.40 to about 0.95;
  • DEGMPE and MEA, with a fraction by weight of MEA that is from about 0.10 to about 0.90;
  • DEGMPE and PG, with a fraction by weight of PG that is from about 0.50 to about 0.75;
  • DEGMPE and DPG, with a fraction by weight of DPG that is from about 0.10 to about 0.90;
  • TEGMME and MEA, with a fraction by weight of MEA that is from about 0.40 to about 0.80;
  • TEGMME and PG, with a fraction by weight of PG that is from about 0.15 to about 0.80;
  • TEGMME and DPG, with a fraction by weight of DPG that is from about 0.35 to about 0.95;
  • TEGMME and PG, with a fraction by weight of PG that is from about 0.15 to about 0.80;
  • TEGMME and DPG, with a fraction by weight of DPG that is from about 0.10 to about 0.90;
  • DPGMME and TPG, with a fraction by weight of TPG that is from about 0.25 to about 0.90;
  • DEGMnBE and MEA, with a fraction by weight of MEA that is from about 0.15 to about 0.90;
  • DEGMnBE and PG, with a fraction by weight of PG that is from about 0.20 to about 0.90;
  • DEGMnBE and DPG, with a fraction by weight of DPG that is from about 0.50 to about 0.95;
  • TEGMEE and MEA, with a fraction by weight of MEA that is from about 0.12 to about 0.80;
  • TEGMEE and PG, with a fraction by weight of PG that is from about 0.10 to about 0.45 or from about 0.50 to about 0.90;
  • TEGMEE and DPG, with a fraction by weight of DPG that is from about 0.10 to about 0.95;
  • TEGMEE and TPG, with a fraction by weight of TPG that is from about 0.10 to about 0.90;
  • DEGMHE and PG, with a fraction by weight of PG that is from about 0.20;
  • DEGMHE and DPG, with a fraction by weight of DPG that is from about 0.20 to about 0.81;
  • TEGMnBE and MEA, with a fraction by weight of MEA that is from about 0.45 to about 0.90;
  • TEGMnBE and PG, with a fraction by weight of PG that is from about 0.45 to about 0.90;
  • TEGMnBE and DPG, with a fraction by weight of DPG that is from about 0.10 to about 0.81;
  • TPGMME and DPG, with a fraction by weight of DPG that is from about 0.20 to about 0.95;
  • TPGMME and TPG, with a fraction by weight of TPG that is from about 0.50 to about 0.95;
  • TPGMnBE and MEA, with a fraction by weight of MEA that is from about 0.20 to about 0.80; and
  • TPGMnBE and PG, with a fraction by weight of PG that is about 0.20 to about 0.80.
  • 2. A process according to claim 1, wherein said aqueous liquid striping composition comprises:
  • (A) from about 0.1 to about 10 M/kg of total aqueous liquid stripping composition of dissolved alkali metal hydroxide selected from the group consisting of sodium, potassium, rubidium, and cesium hydroxides and mixtures thereof;
  • (B) from about 3 to about 30 percent of total aqueous liquid stripping composition of component (B); and
  • (C) from about 0.03 to about 2.0 M/kg of total aqueous liquid stripping composition of a component selected from the group consisting of gluconic acid, water soluble and water dispersible salts of gluconic acid, heptogluconic acid and its water soluble and water dispersible salts, and glucono-delta-lactone.
  • 3. A process according to claim 2, wherein the aqueous liquid striping composition comprises:
  • (A) from about 0.5 to about 5 M/kg of total aqueous liquid stripping composition of dissolved alkali metal hydroxide selected from the group consisting of sodium, potassium, rubidium, and cesium hydroxides and mixtures thereof;
  • (B) from about 5 to about 25 percent of total aqueous liquid stripping composition of component (B); and
  • (C) from about 0.07 to about 0.8 M/kg of total aqueous liquid stripping composition of a component selected from the group consisting of gluconic acid, water soluble and water dispersible salts of gluconic acid, heptogluconic acid and its water soluble and water dispersible salts, and glucono-delta-lactone.
  • 4. A process according to claim 3, wherein said aqueous liquid striping composition comprises:
  • (A) from about 1.1 to about 4.5 M/kg of total aqueous liquid stripping composition of dissolved alkali metal hydroxide selected from the group consisting of sodium, potassium, rubidium, and cesium hydroxides and mixtures thereof;
  • (B) from about 9 to about 18 percent of total aqueous liquid stripping composition of component (B); and
  • (C) from about 0.15 to about 0.45 M/kg of total aqueous liquid stripping composition of a component selected from the group consisting of gluconic acid and water soluble and water dispersible salts of gluconic acid.
  • 5. A process according to claim 4, wherein said aqueous liquid striping composition comprises:
  • (A) from about 2.6 to about 3.5 M/kg of the total composition of potassium hydroxide;
  • (B) from about 11 to about 17 percent of the total composition of component (B); and
  • (C) from about 0.17 to about 0.24 M/kg of total composition of a component selected from the group consisting of gluconic acid and water soluble and water dispersible salts of gluconic acid.
  • 6. A process according to claim 1, wherein the improvement comprises utilizing as component (B) a mixture selected from the group consisting of:
  • EGMFE and TPG, with a fraction by weight of TPG that is from about 0.60 to about 0.90;
  • DEGMPE and MEA, with a fraction by weight of MEA that is from about 0.30 to about 0.80;
  • DEGMPE and PG, with a fraction by weight of PG that is from about 0.55 to about 0.65;
  • DEGMPE and DPG, with a fraction by weight of DPG that is from about 0.19 to about 0.85;
  • TEGMME and MEA, with a fraction by weight of MEA that is from about 0.45 to about 0.70;
  • TEGMME and PG, with a fraction by weight of PG that is from about 0.20 to about 0.70;
  • TEGMME and DPG, with a fraction by weight of DPG that is from 0.55 to 0.90;
  • DPGMME and PG, with a fraction by weight of PG that is from about 0.10 to about 0.81;
  • DPGMME and DPG, with a fraction by weight of DPG that is from about 0.20 to about 0.85;
  • DPGMME and TPG, with a fraction by weight of TPG that is from about 0.35 to about 0.85;
  • DEGMnBE and MEA, with a fraction by weight of MEA that is from about 0.20 to about 0.85;
  • DEGMnBE and PG, with a fraction by weight of PG that is from about 0.30 to about 0.80;
  • DEGMnBE and DPG, with a fraction by weight of DPG that is from about 0.55 to about 0.90;
  • TEGMEE and MEA, with a fraction by weight of MEA that is from about 0.18 to about 0.60;
  • TEGMEE and PG, with a fraction by weight of PG that is from about 0.15 to about 0.40 or from about 0.55 to about 0.85;
  • TEGMEE and DPG, with a fraction by weight of DPG that is from about 0.15 to about 0.80;
  • TEGMEE and TPG, with a fraction by weight of TPG that is from about 0.15 to about 0.55;
  • DEGMHE and DPG, with a fraction by weight of DPG that is from about 0.30 to about 0.61;
  • TEGMnBE and MEA, with a fraction by weight of MEA that is from about 0.50 to about 0.81;
  • TEGMnBE and PG, with a fraction by weight of PG that is from about 0.50 to about 0.85;
  • TEGMnBE and DPG, with a fraction by weight of DPG that is from about 0.20 to about 0.70;
  • TPGMME and DPG, with a fraction by weight of DPG that is from about 0.60 to about 0.90; and
  • TPGMME and TPG, with a fraction by weight of TPG that is from about 0.60 to about 0.90.
  • 7. A process according to claim 6, wherein said aqueous liquid striping composition comprises:
  • (A) from about 0.1 to about 10 M/kg of total aqueous liquid stripping composition of dissolved alkali metal hydroxide selected from the group consisting of sodium, potassium, rubidium, and cesium hydroxides and mixtures thereof;
  • (B) from about 3 to about 30 percent of total aqueous liquid stripping composition of component (B); and
  • (C) from about 0.03 to about 2.0 M/kg of total aqueous liquid stripping composition of a component selected from the group consisting of gluconic acid, water soluble and water dispersible salts of gluconic acid, heptogluconic acid and its water soluble and water dispersible salts, and glucono-delta-lactone.
  • 8. A process according to claim 7, wherein said aqueous liquid striping composition comprises:
  • (A) from about 0.5 to about 5 M/kg of total aqueous liquid stripping composition of dissolved alkali metal hydroxide selected from the group consisting of sodium, potassium, rubidium, and cesium hydroxides and mixtures thereof;
  • (B) from about 5 to about 25 percent of total aqueous liquid stripping composition of component (B); and
  • (C) from about 0.07 to about 0.8 M/kg of total aqueous liquid stripping composition of a component selected from the group consisting of gluconic acid, water soluble and water dispersible salts of gluconic acid, heptogluconic acid and its water soluble and water dispersible salts, and glucono-delta-lactone.
  • 9. A process according to claim 8, wherein said aqueous liquid striping composition comprises:
  • (A) from about 1.1 to about 4.5 M/kg of total aqueous liquid stripping composition of dissolved alkali metal hydroxide selected from the group consisting of sodium, potassium, rubidium, and cesium hydroxides and mixtures thereof;
  • (B) from about 9 to about 18 percent of total aqueous liquid stripping composition of component (B); and
  • (C) from about 0.15 to about 0.45 M/kg of total aqueous liquid stripping composition of a component selected from the group consisting of gluconic acid and water soluble and water dispersible salts of gluconic acid.
  • 10. A process according to claim 9, wherein said aqueous liquid striping composition comprises:
  • (A) from about 2.6 to about 3.5 M/kg of the total composition of potassium hydroxide;
  • (B) from about 11 to about 17 percent of the total composition of component (B); and
  • (C) from about 0.17 to about 0.24 M/kg of total composition of a component selected from the group consisting of gluconic acid and water soluble and water dispersible salts of gluconic acid.
  • 11. A process according to claim 1, wherein the improvement comprises utilizing as component (B) a mixture selected from the group consisting of:
  • EGMFE and TPG, with a fraction by weight of TPG that is from about 0.80 to about 0.85;
  • DEGMPE and MEA, with a fraction by weight of MEA that is from about 0.50 to about 0.65;
  • DEGMPE and PG, with a fraction by weight of PG that is from about 0.59 to about 0.61;
  • DEGMPE and DPG, with a fraction by weight of DPG that is from about 0.39 to about 0.81;
  • TEGMME and MEA, with a fraction by weight of MEA that is from about 0.55 to about 0.65;
  • TEGMME and PG, with a fraction by weight of PG that is from about 0.39 to about 0.60;
  • TEGMME and DPG, with a fraction by weight of DPG that is from about 0.60 to about 0.81;
  • DPGMME and PG, with a fraction by weight of PG that is from about 0.20 to about 0.81;
  • DPGGMME and DPG, with a fraction by weight of DPG that is from about 0.60 to about 0.81;
  • DPGMME and TPG, with a fraction by weight of TPG that is from about 0.40 to about 0.81;
  • DEGMnBE and MEA, with a fraction by weight of MEA that is from about 0.58 to about 0.70;
  • DEGMnBE and PG, with a fraction by weight of PG that is from about 0.40 to about 0.70;
  • DEGMnBE and DPG, with a fraction by weight of DPG that is from about 0.60 to about 0.81;
  • TEGMEE and MEA, with a fraction by weight of MEA that is from about 0.38 to about 0.45;
  • TEGMEE and PG, with a fraction by weight of PG that is from about 0.20 to about 0.30 or from about 0.55 to about 0.70;
  • TEGMEE and DPG, with a fraction by weight of DPG that is from about 0.20 to about 0.61;
  • TEGMEE and TPG, with a fraction by weight of TPG that is from about 0.18 to about 0.21;
  • DEGMHE and DPG, with a fraction by weight of DPG that is from about 0.39 to about 0.46;
  • TEGMnBE and MEA, with a fraction by weight of MEA that is from about 0.55 to about 0.66;
  • TEGMnBE and PG, with a fraction by weight of PG that is from about 0.59 to about 0.81;
  • TEGMnBE and DPG, with a fraction by weight of DPG that is from about 0.40 to about 0.61;
  • TPGMME and DPG, with a fraction by weight of DPG that is from about 0.70 to about 0.85; and
  • TPGMME and TPG, with a fraction by weight of TPG that is from about 0.70 to about 0.85.
  • 12. A process according to claim 11, wherein said aqueous liquid striping composition comprises:
  • (A) from about 0.1 to about 10 M/kg of total aqueous liquid stripping composition of dissolved alkali metal hydroxide selected from the group consisting of sodium, potassium, rubidium, and cesium hydroxides and mixtures thereof;
  • (B) from about 3 to about 30 percent of total aqueous liquid stripping composition of component (B); and
  • (C) from about 0.03 to about 2.0 M/kg of total aqueous liquid stripping composition of a component selected from the group consisting of gluconic acid, water soluble and water dispersible salts of gluconic acid, heptogluconic acid and its water soluble and water dispersible salts, and glucono-delta-lactone.
  • 13. A process according to claim 12, wherein the aqueous liquid striping composition comprises:
  • (A) from about 0.5 to about 5 M/kg of total aqueous liquid stripping composition of dissolved alkali metal hydroxide selected from the group consisting of sodium, potassium, rubidium, and cesium hydroxides and mixtures thereof;
  • (B) from about 5 to about 25 percent of total aqueous liquid stripping composition of component (B); and
  • (C) from about 0.07 to about 0.8 M/kg of total aqueous liquid stripping composition of a component selected from the group consisting of gluconic acid, water soluble and water dispersible salts of gluconic acid, heptogluconic acid and its water soluble and water dispersible salts, and glucono-delta-lactone.
  • 14. A process according to claim 13, wherein said aqueous liquid striping composition comprises:
  • (A) from about 1.1 to about 4.5 M/kg of the total aqueous liquid stripping composition of dissolved alkali metal hydroxide selected from the group consisting of sodium, potassium, rubidium, and cesium hydroxides and mixtures thereof;
  • (B) from about 9 to about 18 percent of the total aqueous liquid stripping composition of component (B); and
  • (C) from about 0.15 to about 0.45 M/kg of total aqueous liquid stripping composition of a component selected from the group consisting of gluconic acid and water soluble and water dispersible salts of gluconic acid.
  • 15. A process according to claim 14, wherein said aqueous liquid striping composition comprises:
  • (A) from about 2.6 to about 3.5 M/kg of the total composition of potassium hydroxide;
  • (B) from about 11 to about 17 percent of the total composition of component (B); and
  • (C) from about 0.17 to about 0.24 M/kg of total composition of a component selected from the group consisting of gluconic acid and water soluble and water dispersible salts of gluconic acid.
  • 16. A process according to claim 1, wherein the improvement comprises utilizing as component (B) a mixture selected from the group consisting of:
  • DPGMnE and PG, with a fraction by weight of PG that is from about 0.20 to about 0.25;
  • DPGMME and DPG, with a fraction by weight of DPG that is from about 0.70 to about 0.81;
  • DPGMME and TPG, with a fraction by weight of TPG that is from about 0.60 to about 0.81;
  • TPGMME and DPG, with a fraction by weight of DPG that is from about 0.80 to about 0.85; and
  • TPGMME and TPG, with a fraction by weight of TPG that is from about 0.80 to about 0.85.
  • 17. A process according to claim 16, wherein said aqueous liquid striping composition comprises:
  • (A) from about 0.1 to about 10 M/kg of total aqueous liquid stripping composition of dissolved alkali metal hydroxide selected from the group consisting of sodium, potassium, rubidium, and cesium hydroxides and mixtures thereof;
  • (B) from about 3 to about 30 percent of total aqueous liquid stripping composition of component (B); and
  • (C) from about 0.03 to about 2.0 M/kg of total aqueous liquid stripping composition of a component selected from the group consisting of gluconic acid, water soluble and water dispersible salts of gluconic acid, heptogluconic acid and its water soluble and water dispersible salts, and glucono-delta-lactone.
  • 18. A process according to claim 17, wherein said aqueous liquid striping composition comprises:
  • (A) from about 0.5 to about 5 M/kg of total aqueous liquid stripping composition of dissolved alkali metal hydroxide selected from the group consisting of sodium, potassium, rubidium, and cesium hydroxides and mixtures thereof;
  • (B) from about 5 to about 25 percent of total aqueous liquid stripping composition of component (B); and
  • (C) from about 0.07 to about 0.8 M/kg of total aqueous liquid stripping composition of a component selected from the group consisting of gluconic acid, water soluble and water dispersible salts of gluconic acid, heptogluconic acid and its water soluble and water dispersible salts, and glucono-delta-lactone.
  • 19. A process according to claim 18, wherein said aqueous liquid striping composition comprises:
  • (A) from about 1.1 to about 4.5 M/kg of total aqueous liquid stripping composition of dissolved alkali metal hydroxide selected from the group consisting of sodium, potassium, rubidium, and cesium hydroxides and mixtures thereof;
  • (B) from about 9 to about 18 percent of the total aqueous liquid stripping composition of component (B); and
  • (C) from about 0.15 to about 0.45 M/kg of total aqueous liquid stripping composition of a component selected from the group consisting of gluconic acid and water soluble and water dispersible salts of gluconic acid.
  • 20. A process according to claim 19, wherein said aqueous liquid striping composition comprises:
  • (A) from about 2.6 to about 3.5 M/kg of the total composition of potassium hydroxide;
  • (B) from about 11 to about 17 percent of the total composition of component (B); and
  • (C) from about 0.17 to about 0.24 M/kg of total composition of a component selected from the group consisting of gluconic acid and water soluble and water dispersible salts of gluconic acid.
CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation of application Ser. No. 08/450,593 filed May 25, 1995, now U.S. Pat. No. 5,591,702.

US Referenced Citations (14)
Number Name Date Kind
3058918 Gatza Oct 1962
3308066 Murphy et al. Mar 1967
3615827 Murphy Oct 1971
3663447 Murphy May 1972
3663476 Murphy May 1972
3671465 Murphy Jun 1972
3766076 Murphy Oct 1973
3847839 Murphy Nov 1974
4403029 Ward, Jr. et al. Sep 1983
4435305 Tsoukalas et al. Mar 1984
4537705 Mahoney et al. Aug 1985
5364551 Lentsch et al. Nov 1994
5380454 Griepenburg et al. Jan 1995
5591702 Murphy Jan 1997
Continuations (1)
Number Date Country
Parent 450593 May 1995