Structural body of a vehicle having an energy absorbing device and a method of forming the energy absorbing device

Information

  • Patent Grant
  • 11603142
  • Patent Number
    11,603,142
  • Date Filed
    Monday, June 15, 2015
    9 years ago
  • Date Issued
    Tuesday, March 14, 2023
    a year ago
Abstract
In an embodiment, an energy-absorbing device can comprise: a polymer reinforcement structure, wherein the polymer reinforcement structure comprises a polymer matrix and chopped fibers; and a shell comprising 2 walls extending from a back and forming a shell channel, wherein the shell comprises continuous fibers and a resin matrix; wherein the polymer reinforcement structure is located in the shell channel.
Description
BACKGROUND

The present disclosure relates to the structural body of a vehicle and to weight reduction thereof, particularly while meeting high-speed front side and rollover vehicle crash countermeasures.


Automotive manufacturers are continuing to reduce the weight of passenger cars to meet the increasing government regulations on fuel efficiency and reducing emissions. The structural body of a vehicle (the structure forming what is commonly known as the body-in-white (BIW)), is a vehicle's largest structure, and therefore ideal for weight reduction considerations. Body-in-white refers to the welded sheet metal components which form the vehicle's structure to which the other components will be married, i.e., the engine, the chassis, the exterior and interior trim, the seats, etc. Reducing body weight, however, involves a trade-off with body stiffness, a key characteristic which influences vehicle dynamics, durability, and crash worthiness.


This generates the need to design a BIW having reduced weight, without sacrificing durability and crash worthiness.


BRIEF DESCRIPTION

Disclosed, in various embodiments are forming tools, laminates, shells, and energy absorbing devices and methods of making and using the same.


In an embodiment, an energy-absorbing device can comprise: a polymer reinforcement structure, wherein the polymer reinforcement structure comprises a polymer matrix and chopped fibers; and a shell comprising 2 walls extending from a back and forming a shell channel, wherein the shell comprises continuous fibers and a resin matrix; wherein the polymer reinforcement structure is located in the shell channel.


In an embodiment, a structural body of a vehicle can comprise: a hollow vehicle component comprising walls that define a cavity, wherein the vehicle component has a component length; and the energy-absorbing device; wherein the energy-absorbing device is located in the cavity.


In an embodiment, a vehicle can comprise: the structural vehicle component; and the energy-absorbing device located in the structural vehicle component; an engine; and a drive mechanism.


In another embodiment, a vehicle can comprise: the structural vehicle component, wherein the structural vehicle component is the energy-absorbing device, an engine; and a drive mechanism.


These and other non-limiting characteristics are more particularly described below.





BRIEF DESCRIPTION OF THE DRAWINGS

The following is a brief description of the drawings wherein like elements are numbered alike and which are presented for the purposes of illustrating the exemplary embodiments disclosed herein and not for the purposes of limiting the same.



FIG. 1 is a partial perspective view of exemplary areas of the BIW that can be reinforced.



FIG. 2 is a pictorial representation of exemplary locations for the reinforcement.



FIG. 3 is a perspective view of an embodiment of a polymer reinforcement structure.



FIG. 4 is a perspective view of an embodiment of a shell.



FIG. 5 is a perspective view of an embodiment of the polymer reinforcement structure of FIG. 3 located in the shell of FIG. 4.



FIG. 6 is an illustration of possible fiber orientation angles for the UD materials and laminates.



FIG. 7 is an illustration of one embodiment of making the energy-absorbing device.



FIG. 8 is an illustration of another embodiment of making the energy-absorbing device.



FIG. 9 is an illustration of another embodiment of a device and method for making the energy-absorbing device in, and in particular making the shell.



FIG. 10 is an illustration of an embodiment of an injection molding scheme showing the gate and hence reinforced polymer flow scheme.



FIG. 11 is an illustration of an example of energy-absorbing device having an irregular, varied shape that is complimentary to the shape of the structural vehicle component where it will be located.



FIG. 12 is a partial, cut-away, cross-section of an example of a structural vehicle component with the energy-absorbing device located in the hollow channel and wherein the channels of the honeycomb structures are oriented across (e.g., perpendicular) to the main axis.



FIGS. 13A and 13B are illustrations of an example of the energy absorbing device disclosed herein comprising openings that enable mechanical attachment between the shell and the polymer reinforcement structure.



FIG. 14 is a schematic drawing of an embodiment of a laminator.



FIG. 15 is a schematic view of a dynamic lamination process with a twin belt laminator.





DETAILED DESCRIPTION

Many attempts have been made to provide BIW component for automotive vehicles, which are lighter and could be able to absorb a major portion of impact energy during high-speed crashes. Use of high strength steel in BIW components has been increasing rapidly. Lighter metal like aluminum and magnesium have also been explored. The wall thickness of these various BIW components is sufficient to impart the desired structural integrity to that element to meet its desired function and various regulatory requirements.


With foam filled components, a hollow part is filled with foam to its full volume, and the expanded foam material provides the connection to the wall and thus the absorption of force and distribution of load. The reinforcement characteristics are based on the material properties of the foam. However, foam reinforcement systems require a chemical reaction that must be adapted to the production process of the vehicle, particularly in terms of the incident temperatures. The reinforcement function thus depends on accurate and constant adherence to the process parameters. Another disadvantage is that the structural parts can no longer be disconnected from one another easily, making recycling more difficult. In addition, completely filling the space with foam brings about a more or less homogeneous reinforcement effect, without the ability to take three-dimensional varying design requirements into account.


In crush countermeasure systems that include steel stampings fixed to sheet metal via thermoset adhesive, the adhesive will activate and expand as the body goes through the ovens that bake the paint. Therefore, this system is not optimal. The stampings are heavy and excessive adhesive would generally need to be applied to assure a solid bond from the countermeasure to the body.


Some crush countermeasure systems include steel stampings that are fixed to the sheet metal via thermoset adhesive. The adhesive will activate and expand as the body goes through the ovens that bake the paint. This system is not optimal. The stampings are heavy and excessive adhesive is applied to assure a solid bond from the countermeasure to the body. Another system includes steel stampings that are fixed to the sheet metal via over mold injection mold design. The steel structures were provided with draft and material overflow provision. Once part is cooled and there forms a physical/mechanical bonding between the steel and polymers.


It would be beneficial to provide lightweight BIW components comprising crush countermeasures that is lighter than aforementioned solutions and provide ability to absorb more impact energy and/or protecting motor vehicle occupants. The crush countermeasures, e.g., energy absorbing devices, can improve structural integrity, for example, by reducing excessive deformation and improving crashworthiness during a vehicle crash scenario. It would also be beneficial to provide a crush countermeasure that may be easily manufactured and used in a motor vehicle without the use of additional processing steps.


In addition to the BIW components, reducing the weight while retaining the structural integrity of other vehicle components is also desired. Some other vehicle components that can benefit from the energy-absorbing device disclosed herein include an instrument panel, cross-car member, door support bar, seat structure (e.g., frame), suspension controller (e.g., control arms), engine block, oil pump cover, as well as other components that can benefit from a reduced weight high structural integrity element. As with the BIW components, these vehicle components can either be replaced by the energy-absorbing device, or the energy-absorbing device can be located in a hollow portion of the component.


As mentioned above, it is desirable to reduce the weight of a vehicle without compromising structural integrity and durability. Therefore, it is desirable to reduce the amount of metal employed in the vehicle while not sacrificing strength. Employed throughout the vehicle are hollow metal structural elements (e.g., beams (e.g., bumper beam), rails (e.g., roof rail), pillars (e.g., “A” pillar, “B” pillar, “C” pillar, “D” pillar), rockers (e.g., floor rocker), bars (e.g., floor cross-bars, and cross bars in chassis ladder), and so forth). For example, refer to FIG. 1, which illustrates the locations of the roof rail 58, “A” pillar 50, “B” pillar 52, “C” pillar 54, “D” pillar 56, and floor rocker 60. Disclosed herein are energy-absorbing devices, e.g., reinforcement for BIW components. Some examples of possible locations for the energy-absorbing device are illustrated in FIG. 2, locations 70, which further illustrates a drive mechanism 76 and engine 74. Desirably, energy-absorbing devices are lighter than metal-plastic hybrid reinforcements and provide better crash resistance than all plastic reinforcement, metal-plastic hybrid reinforcement, or foam reinforcement.


The energy-absorbing device, e.g., BIW component, is a hybrid of continuous fiber reinforced-polymer composite and short/long chopped fiber reinforced composite material solution that can be positioned in hollow channels of the BIW components. This hybrid structure comprises a shell of continuous fiber, reinforced polymer over-molded with structure of chopped fiber (e.g., chopped short fiber (e.g., fibers having a length of less than 1 millimeters (mm)) and/or chopped long (e.g., fibers having a length of 1 to 10 mm, specifically, 3 to 5 mm) fiber) reinforced thermoplastic. The structure formed from the chopped fiber reinforced material can have various geometries that enable the desired energy absorption characteristics, e.g., rib pattern (for example a cross-rib pattern, honeycomb geometry, and so forth).


The energy-absorbing device can be formed, for example, by making shell structure of continuous fiber reinforced-polymer through various methods. The continuous fiber reinforced-polymer can comprise fiber fabrics and/or unidirectional (UD) tapes, collectively referred to as fiber structure. UD tapes can have greater than or equal to 90%, specifically, greater than or equal to 99% of the fibers oriented in the same direction. Fabrics have fibers in a single plane and oriented in at least two directions (e.g., a weave). The fiber structure (e.g., fabrics and tapes) can be formed into laminate(s) (also referred to as a sheet), wherein the laminate can be formed into intermediate(s), preform(s)), and the like. Individual layers comprise a ratio of resin matrix to fibers of 60/40 to 40/60 ratio by weight, specifically, 55/45 to 45/55, 60/40 to 40/60 ratio by weight, for example, 50/50 ratio by weight. This ratio can be attained by forming the layer using a volume ratio of resin to fibers of 70/30 to 30/70, preferably 65/35 to 35/65, for example, 60/40. For example, a resin matrix/fiber ratio by density of 40/60 can yield a 50/50 ratio by weight with a 3,000 tow or 3,000 twill weave. The specific ratio can be dependent on the materials used and the volume density of the fibers (e.g., the fabric). The specific amounts can readily be determined from the information herein.


When laying up the fiber structures, each subsequent layer can be oriented such that the fibers extend in the same direction as in the first layer (i.e., oriented at 0 degrees with respect to the first layer), or at a different angle than the fibers of the prior layer, e.g., at 45 degrees or 90 degrees with respect to the prior layer. Therefore, the layup (and/or the lamina) can be arranged in various orientations with respect to one another to attain a desired structural integrity, e.g. 0 degrees and 90 degrees (also referred to as “0/90”), (0/90/0), (0/45/−45), 0/60/−60), (0/45/90/0), and so forth, with an alternating 0 and 90 degree being desirable. Also desirable, the layup is a “balanced” layup comprising multiple layers with alternating fiber direction from one layer (i.e., fabric structure) to the next layer until the center of the layup then the alternation stops and reverses itself (e.g., (0/90/0/90/90/0/90/0), (0/90/45/0/0/45/90/0), (0/90/0/0/90/0) or (0/60/90/90/90/60/0)). FIG. 6 illustrates laminate/layup fiber orientations, wherein the first layer is considered to be oriented at 0 (i.e., zero degrees). Each subsequent fiber structure is oriented such that the fiber direction is at an angle with respect to the fiber direction of the first fiber structure. The desired combination of fiber angles is dependent upon the desired stiffness of the shell.


The number of layers employed is based upon the desired thickness and structural integrity of the shell. The shell can have a total thickness of 0.2 to 10 mm, specifically, 0.3 to 3 mm, more specifically, 0.5 mm to 2 mm, and still more specifically, 0.5 mm to 1.5 mm. Each layer can have a thickness of 0.1 to 0.4, for example, 0.1 to 0.2 mm.


Optionally, all of the fiber structures of the layup can have the same type of fibers (e.g., composition and/or diameter), or some fiber structure(s) can have a different type of fiber (e.g., composition and/or diameter).


The lay-up can be formed to produce a shell. The shell can then be overmolded with chopped fiber reinforced polymer material to form reinforcing elements (e.g., ribbed or honeycomb structure), in the shell.


The energy-absorbing device can then be used in a BIW component to provide structural integrity (e.g., in the B-pillar).


For high-speed front crash (e.g., a speed of greater than or equal to 29 kilometers per hour (kmph)), front portion of the vehicle chassis (e.g., bumper beam, energy absorber, and rails), absorbs maximum amount of impact energy. For high-speed side crashes B-pillar, floor rocker, and floor crossbars play key role in energy absorption. For rollover or roof-crush the A-pillar, B-pillar, and roof rails play key role in impact energy absorption. Generally above-mentioned components are hollow metal sections. Depending upon the necessary structural integrity of the particular element, the energy-absorbing device can replace the element, or can be inserted into the hollow cavity of the element. If the energy-absorbing device is located in the element, the thickness of the element can be reduced, thereby reducing vehicle weight. The disclosed crush countermeasure provides impact resistance and/or reinforcement characteristics in a lighter weight structure as compared to prior systems composed entirely of metal. The crush countermeasure provides a lightweight crush system having comparable protection to current all metal systems. As such, the overall weight of a vehicle is reduced without any compromise on the safety considerations to passengers.


Disclosed are energy-absorbing devices comprising a shell comprising continuous fibers in a polymeric matrix, and a polymer reinforcement structure inseparable from the shell, wherein the device can be located in a structural vehicle component (e.g., a BIW component). As used herein, “inseparable” refers to an inability to separate the components without damage to one or both of the components. The device can be located throughout the structural vehicle component, in strategic locations within the structural vehicle component (“localized”), or can replace the structural vehicle component. BIW components that can be reinforced include the beam(s), rail(s), pillar(s), chassis, floor rocker, and cross-bar(s), as well as combinations comprising at least one of the foregoing, e.g., the junction of the A-pillar and the floor rocker. Optionally, the device can be employed to reinforce other structural vehicle components besides the BIW components, such as an instrument panel, cross-car member, door support bar, seat structure (e.g., frame), suspension controller (e.g., control arms), engine block, oil pump cover, as well as other components, as well as combinations comprising at least one of the foregoing.


The shell can form a channel defined by greater than or equal to 1 wall for example 3 sided U channel. The channel can have, for example 3 sides, or 4 sides, with a channel therethrough, such that the channel is open on each end. Optionally, side wall can include opening though the wall such that, when the reinforcement is formed, molten polymer can pass from within the cavity, through the opening, and solidify to further secure the polymer reinforcement structure within the shell. Optionally, openings (e.g., small openings) around the free edges of channel, such that the molten plastic can flow over edges and solidify to further secure channel and reinforcement.


The number of holes can be greater than or equal to one, specifically greater than or equal to two, e.g., 2 to 4 holes, for ease of polymer flow inside out. The hole diameter (along a major axis) can be up to 20 mm (e.g., 0.5 mm to 20 mm), specifically, 1 mm to 10 mm, and more specifically, 2 mm to 7 mm (e.g., 5 mm).


The polymer reinforcement structure can have a honeycomb structure, e.g., an array of columns and channels. The combs of the structure can be a shape having greater than or equal to 5 sides, such as pentagonal, hexagonal, heptagonal, and octagonal, and so forth, geometries, as well as combinations comprising at least one of the foregoing geometries, and specifically a hexagonal geometry. Optionally, the channels of the honeycomb structure extend from one end of the structure to the other end of the structure, so that the structure is open on both ends, and wherein one end (e.g., the second end of the channel) can optionally be disposed in physical contact with a side of the shell, thereby effectively blocking the second end. Polymer honeycombs can be made by bonding extruded polymer tubes together, injection molding the polymer honeycombs, extruding the honeycomb structure, or otherwise formed. For example, the element can be a co-extruded component having combs of the same or different material, e.g., adjacent combs can comprise a different material composition. Optionally, some or all of the combs have foam therein. In other words, the combs can, individually, be hollow or filled, such that the structural integrity can be modified by filling particular combs, by using different polymer for particular combs, or a combination comprising at least one of the foregoing. One possible fill material is foam. Desirably, the honeycomb structure is formed by overmolding the shell using an injection molding process.


The polymer reinforcement structure can further or alternatively comprise a rib structure. For examples, ribs can extend across the channel of the shell, between sidewalls and/or a back wall. Various rib designs are possible, including triangular, wave, diagonal, crossed, and the like. For example, the ribs can form a triangular, rectangular, “X”, or other structure.


The shell and the polymer reinforcement structure can, independently, comprise various polymeric materials, e.g., thermoplastic, thermoset and combinations comprising at least one of the foregoing. The particular material can be chosen based upon its properties, the desired location in the vehicle, and the characteristics of that location. For example, in some embodiments, the material can have moderate stiffness (e.g., Young's modulus of 0.8 gigaPascals (GPa) to 30 GPa, specifically, 3 GPa to 15 GPa, for example 7.0 GPa), good elongation (e.g., greater than 1% elongation), chemical resistance and/or heat resistance under vehicle manufacturing conditions (e.g., welding, painting, etc., for example, at temperatures 400° F. for 30 minutes, which enables the polymer reinforcement structure to maintain integrity as the part travels with the auto body through paint bake). Examples of polymers include thermoplastic materials as well as combinations comprising thermoplastic materials. Possible thermoplastic materials include polycarbonate; polybutylene terephthalate (PBT); acrylonitrile-butadiene-styrene (ABS); polycarbonate; polycarbonate/PBT blends; polycarbonate/ABS blends; copolycarbonate-polyesters; acrylic-styrene-acrylonitrile (ASA); acrylonitrile-(ethylene-polypropylene diamine modified)-styrene (AES); phenylene ether resins; blends of polyphenylene ether/polyamide; polyamides; phenylene sulfide resins; polyvinyl chloride (PVC); high impact polystyrene (HIPS); polyethylene (e.g., low/high density polyethylene (L/HDPE)); polypropylene (PP) (e.g., expanded polypropylene (EPP)); polyetherimide; and thermoplastic olefins (TPO); as well as combinations comprising at least one of the foregoing. For example, the polymer reinforcement structure can comprise Noryl™ GTX resin, LEXAN™ resin, ULTEM™ resin, VALOX™ resin, CYCOLAC™ resin, and/or STAMAX™ resin, which are commercially available from SABIC. Desirably, the polymer reinforcement structure comprises polypropylene, and/or blends of polyphenylene ether/polyamide. The polymer reinforcement structure can optionally be reinforced, e.g., with fibers, particles, flakes, as well as combinations comprising at least one of the foregoing. These fibers may include glass, carbon, bamboo, aramid, kevelar etc., as well as combinations comprising at least one of the foregoing. For example, the polymer reinforcement structure can be formed from STAMAX™ materials, a long glass fiber reinforced polypropylene commercially available from SABIC. The polymer reinforcement structure and/or shell can also be made from combinations comprising at least one of any of the above-described materials and/or reinforcements, e.g., a combination with a thermoset material. Desirably, the shell comprises continuous fibers (e.g., glass, carbon, aramid, kevelar, as well as combinations comprising at least one of the foregoing in a polymeric matrix of polyetherimide, polyamide (nylon), polyphenylene oxide, polycarbonate, polypropylene, as well as combinations comprising at least one of the foregoing.


Good adhesion between the shell and polymer reinforcement structure, can be attained with compatibility between the polymer matrix of the shell and the polymer of the polymer reinforcement structure. For example the shell can be made of continuous carbon fiber reinforced composite with base resin of nylon, and the polymer of the polymer reinforcement structure can also include nylon resin or any other resin blended with nylon like SABIC's Noryl™ GTX. Another example, the outer shell is made of continues glass fiber reinforced composite material with polypropylene as resin matrix, and polymer reinforcement structure can comprise a polypropylene based material or short/long fiber reinforced polypropylene composite like SABIC's STAMAX™ resin.


The honeycombs' orientation with respect to the channel in the support (and also with respect to the opening through the structural element) can also be chosen to attain the energy absorption characteristics of the reinforced component (e.g., BIW component). For example, the honeycomb can form channels that can be oriented 0 degrees (e.g., parallel) to 90 degrees (perpendicular), to the major axis of the shell. The major axis is the axis extending down the channel (e.g., see FIG. 3 axis Ax). In other words, in some embodiments, the honeycombs can have a common main axis with the channel and extend parallel thereto. In other embodiments, the honeycombs can extend perpendicular to the main axis of the channel. Consequently, when the reinforcement is disposed in the structural component (also referred to herein as structural vehicle component and vehicle component), in some embodiments, the honeycombs can have a common main axis with the opening through the structural component, while in other embodiments, the honeycombs can extend perpendicular to the opening through the structural component.


The overall size of the energy-absorbing device will depend upon its location within the BIW and the size of the associated opening in the structural component. Furthermore, the characteristics of the reinforcement will depend upon the energy absorption characteristics desired in the particular area, e.g., the number of combs or ribs per unit area, the thickness of the comb walls or ribs, and the specific material of the plastic reinforcement. The density of combs (number of combs per unit area) is dependent upon the desired stiffness, crush characteristics, and materials employed. In some embodiments, the density can be 1 to 20 combs per 100 mm2, specifically, 1 to 10 combs per 100 mm2, and more specifically 1 to 5 combs per 100 mm2. In various embodiments, the thickness of the walls of the plastic reinforcement can be 0.5 mm to 10 mm, specifically, 2 mm to 5 mm, and more specifically 2.5 mm to 4 mm. Generally, a reinforcement will comprise greater than or equal to 10 combs, specifically, greater than or equal to 20 combs, and more specifically, greater than or equal to 30 combs.


The length of the shell is dependent upon the particular area of the BIW, while the length of the polymer reinforcement structure is dependent upon the amount and location of enhanced structural integrity in the shell. The polymer reinforcement structure can have a length commensurate with the length of the shell or less than the length of the shell (e.g., can be localized; i.e., disposed only in a specific location to attain enhanced structural integrity of that location). Desirably, to maximize the weight reduction, the polymer reinforcement structure is localized so as to add the minimum amount of weight needed to attain a desired structural integrity (e.g., a structural integrity that this greater than or equal to the standard metal component without the thinner walls). The energy-absorbing device can have a length of less than or equal to 1,000 mm, specifically, less than or equal to 800 mm, and more specifically, less than or equal to 300 mm. The length of the reinforcement can be less than or equal to 80% of the length of the structural component, specifically, less than or equal to 60%, more specifically, less than or equal to 50%, and yet more specifically, 10% to 35% of the length of the structural component (i.e., the structural component that is reinforced by the energy-absorbing device). For example, the energy-absorbing device can have a length of 150 mm to 350 mm, specifically, 200 mm to 250 mm, such as for use in a pillar or rail. In other embodiments, the energy-absorbing device has a length of 500 mm to 800 mm, specifically, 600 mm to 700 mm, such as for use in a floor rocker. The structural component is a hollow metal element. The reinforcement is disposed in the hollow space. When the reinforcement is not located throughout the hollow space in the structural element, it can be attached to the structural element to inhibit the reinforcement from being dislodged during use of the vehicle or during an impact.


Some possible structural component material(s) include polymers (e.g., thermoplastic and/or thermoset), composite, metals, and combinations comprising at least one of the foregoing. Some metals include aluminum, titanium, chrome, magnesium, zinc, and steel, as well as combinations comprising at least one of the foregoing materials. The thickness of the walls of the structural component can all be the same or can be different to enhance stiffness in a desired direction. For example, one set of opposing walls can have a greater/lesser thickness than the other set of opposing walls. In some embodiments, the structural components have a wall thickness of less than or equal to 1.6 mm, specifically, 1.0 mm to 1.5 mm, and more specifically 1.3 mm to 1.4 mm. Generally, metal walls (e.g., floor rocker, rails, pillars, bumper beam, and so forth), have a wall thickness of greater than 1.8 mm. Therefore, the use of the energy-absorbing device enables a reduction in wall thickness (of the structural component) of greater than or equal to 10%, specifically, greater than or equal to 20%, and even greater than or equal to 25%.


As noted above, the reinforcement can be located in various areas of the vehicle, such as in the bumper beam(s) and/or the BIW component (such as rail(s), pillar(s), chassis, floor rocker, and cross-bar(s)), as well as combinations comprising at least one of the foregoing. The desired specific location of the reinforcement in the structural component can be determined using crash results.


The fixing measures to attach the energy-absorbing device in the structural component can be mechanical and/or chemical. Examples of mechanical fixing measures include snaps, hooks, screws, bolts (e.g., threaded bolt(s), rivets, welds, crimp(s) (e.g., the crimped metal wall). A friction fit can also be used to maintain the reinforcement in place. Chemical fixing measures can include bonding agents such as glues, adhesives, and so forth.


A more complete understanding of the components, processes, and apparatuses disclosed herein can be obtained by reference to the accompanying drawings. These FIGS. (also referred to herein as “FIG.”) are merely schematic representations based on convenience and the ease of demonstrating the present disclosure, and are, therefore, not intended to indicate relative size and dimensions of the devices or components thereof and/or to define or limit the scope of the exemplary embodiments. Although specific terms are used in the following description for the sake of clarity, these terms are intended to refer only to the particular structure of the embodiments selected for illustration in the drawings, and are not intended to define or limit the scope of the disclosure. In the drawings and the following description below, it is to be understood that like numeric designations refer to components of like function.



FIG. 1 is a pictorial representation of possible reinforcement locations in a vehicle. Here, the energy-absorbing device can be located in one or any combination of the identified locations. For example, A-Pillar 50 (e.g., near the center of the length of A-Pillar), B-Pillar 52 (e.g., near the center of the length of B-Pillar), C-Pillar 54 (e.g., near the center of the length of C-Pillar), D-Pillar 56 (e.g., near the center of D-Pillar), roof rail 58 (e.g., in multiple, separate locations along the length of the roof rail; such as centered over the window(s)), and/or floor rocker 60 (e.g., in the area where the B-Pillar meets the floor rocker), and junction of A pillar and floor rocker. For example, inserts that occupy about 10% to 30% of the length of the metal component can be located in A-Pillar 50, B-Pillar 52, the roof rail 58, and the floor rocker 60. The correct location of these reinforcements depends on crash worthiness performance for different high-speed impact requirements. As is clear from the illustrations (e.g., FIGS. 4-5), the honeycombs form channels 18. The channels can be oriented parallel to the main axis of the hollow opening formed in the body in white component, orienting the channels perpendicular to the main axis (Mx in FIG. 12) of the hollow opening formed in the body in white component provides further structural integrity.



FIG. 5 is a pictorial representation of a concept; in which localized reinforcements are proposed at identified locations of A-Pillar, B-Pillar, roof rail, and floor rocker and so forth. The details shown in FIG. 5 illustrate the formed structural component (e.g., from two metal structures welded together) formed from a hollow component (FIG. 4) with a reinforcement (FIG. 3) placed in the hollow component. The specific location of these reinforcements depends on crashworthiness performance for different high-speed impact requirements.



FIGS. 3-5 illustrate the elements of the reinforcement. FIG. 5 illustrates the polymer reinforcement structure 4 to be located within the channel 20 of the shell (6, 12). As can be seen in FIG. 13, the shell 6 can comprise openings 14, such that the plastic of the polymer reinforcement structure 4 can pass through the opening 14 thereby forming a mechanical bond and locking the shell 6 and polymer reinforcement structure 4 together. The openings 14 can be preformed such that the continuous fibers are oriented around the openings. Alternatively, the opening 14 can be formed into the shell, by cutting through the side, and the fibers.


As is illustrated in FIG. 11, the energy-absorbing device 1 can have a shape that is complimentary to the shape of the opening through the structural component 72. The depth of the comb (e.g., length of the honeycomb channels 18) can be constant throughout the polymer reinforcement structure, or can vary along the length of the reinforcement, e.g., to follow the shape of the structural component 72 of the vehicle. For example, the depth of the combs of the polymer reinforcement structure 4 can decrease from one end of the polymer reinforcement structure to an opposite end of the polymer reinforcement structure.


The use of localized reinforcement (e.g., energy-absorbing device having hollow channels therethrough, located in the structural component) may enable the reduction in wall thickness of the structural component (e.g., BIW component) by greater than or equal to 15%, while retaining the structural integrity.



FIGS. 6 and 7 illustrate some examples of making the energy-absorbing device 1. FIG. 7 illustrates making the energy-absorbing device 1 by laying up unidirectional (UD) tapes 22 of continuous fiber reinforced plastic material in the injection molding tool. The tape layup can be automated or manual. The injection molding tool can be preheated so that the polymer matrix of UD tapes reaches its glass transition temperature. Then the heated layup can be compressed by a forming tool 24 for consolidation followed by solidification of the compressed lay up to form the shell 6. Then overmolding 26 of the polymer reinforcement structure 4 in the shell 6 is accomplished by injection of fiber reinforced polymer into the injection molding tool. Different orientation and number of layers of the can be designed to achieve different geometry and thickness of shell and customized properties of the shell.



FIG. 8 illustrates a process for forming an energy absorbing device. A preform laminate 28 comprising continuous fiber reinforced polymer, can be placed into a forming tool 30. The tool 30 is heated to make this laminate 28 formable, later it is compressed in the tool cavity to take required shape of shell 6. The formed shell 6 can then be placed into the injection molding tool wherein fiber reinforced plastic material can be injected to overmold the desired polymer reinforcement structure 4.


Now referring to FIG. 9, the shell 6 is made by laying-up UD layers or by using a laminate having a specific lay-up (e.g., with layers of continuous carbon fibers and/or glass fibers in a thermoplastic matrix). The shell can then be formed into a “U” shaped channel from the layup/laminate, e.g., using a special forming tool. The forming tool illustrated in FIG. 9, has a core 80 and cavity 82, wherein the cavity is located between a first platen 84 and a hinged platen 86, and the core 80 extends from the first platen 84 (e.g., is fixedly attached to the first platen 84), into the cavity 82, with a space remaining between the core 80 and the hinged platen 86. The hinged platen 86 comprises three sections 86A, 86B, and 86C. Movable sections 86A and 86B can move on about hinges 88A and 88B respectively, toward intermediate section 86C, to change a U shaped cavity having a size that is complementary to the size of the core 80. In other words, the two outside platen sections (86A,86B) can be rotated (e.g., 90 degrees) from a flat to a forming orientation (e.g., vertical orientation) adjacent the core 80, to form a U shaped cavity for forming the shell. The movable sections 86A and 86B can be moved from the rest position to the forming position using various methods such as manually, using hydraulic, using cylinders 90 (e.g., two gas (e.g., air) operated cylinders) to form the U shaped shell.


The process can comprise UD layers laid up in a desired layer orientation and consolidated to form a laminate. The consolidated laminate 92 can be located on the hinged platen 86 such that the area of the laminate intended to be the sides will be located over the hinged section 86A or 86B. The consolidated laminate 92 is heated to the glass transition temperature of the resin matrix. The shell 6 is then formed by lowering the core 80 into the forming position and rotating the movable sections 86A and 86B, e.g., actuating the hinged platen sections by the air cylinders 90, to rotate (e.g., 90 degrees) to a forming position, thereby bending the heated, consolidated laminate into a U shape. The degree of rotation of the movable sections 86A and 86B is dependent on the desired angles of the sides of the shell 6 (e.g., parallel sides, or sides oriented at a different angle). Once the core 80 and movable sections 86A and 86B are in the forming position, the heated consolidated laminate is cooled to solidify the laminate and form the shell 6.


For example, the layers used in the laminate can be formed by forming a film of the resin matrix (e.g., having a thickness or less than or equal to 300 micrometers (μm)). The pre-consolidated laminate can be heated above the Tg (glass transition temperature) of the resin matrix, allowing the resin to flow between the fibers in their bundle to form a resin-fiber structure. For example, Noryl™ GTX resin film (e.g., having a thickness of 76.2 micrometers (0.003 inch) and 127 micrometers (0.005 inch)) is heated into a fiber or fabric to form the layer. The film thickness is dictated by the desired laminate ratio by volume. A 60/40 ratio by volume, for example, will usually yield a 50/50 ratio by weight with a 3K toe weave or 3K twill weave. This is also dependent on the volume density of the fabric. The use of the GTX resin in the consolidated laminate will help promote better adhesion between the formed laminate shell and the plastic overmolded structure. Optionally, the layers for the laminate can be formed using a powder method. In this method, a powder (e.g., ground powder) is applied to the fiber structure, to form a powdered fiber. The powdered fabric is heated to semimelt the powder into the fabric, thereby impregnating (e.g., semi-impregnating) the powder into the fiber tape or fabric to form the layer. For example, the powder is distributed (e.g., evenly distributed) across the fabric and then by means of ultrasonics, air impingement is forced between the fiber bundles then heated above the Tg so the resin can coat the fiber bundles after which the fiber structure is rolled and the fibers are pre-coated or semi impregnated to form the resin-fiber structure. Possible powders can be formed from any of the above mention thermoplastic materials, such as Noryl™ GTX resin, LEXAN™ resin, ULTEM™ resin, VALOX™ resin, CYCOLAC™ resin, STAMAX™ resin, and combinations comprising at least one of the foregoing, such as an alloy some of these resins.


Once the layers (i.e., the resin-fiber structure) are prepared, the laminate can be formed. The layers (i.e., resin-fiber structure) can be laid-up and the lay-up can then be placed in a laminator. The layup is then dried, e.g., allowing residual moisture to surface and be removed. After drying, the layup is heated (e.g., to a resin melt temperature) under vacuum to enable the fiber to wet out. Pressure is then applied to the layup. The temperature is then reduced (e.g., rapidly to room temperature), the pressure is thereafter released and the laminate is then removed. For example, referring to FIG. 14, a layup 38 is placed between a first platen 32 and a laminate platen 34. The temperature in the laminator 40 is increased to a temperature sufficient to remove residual moisture (e.g., depending upon the resin matrix, 100° C. to 200° C., specifically, 125° C. to 165° C., e.g., 150° C.). This temperature can be held for enough time for residual moisture to surface on the layup (e.g., a hold time of up to 30 minutes, specifically, 2 to 20 minute, more specifically, 5-10 minutes). The actual time will depend upon the moisture content of the resin and the thickness of the layup. After drying hold time is complete, a vacuum is pulled in the vacuum chamber 36. The vacuum can be pulled (e.g., to a pressure of less than 30 inches of mercury (Hg), specifically, less than 28.8 Hg, and more specifically 10 Hg, and the process temperature can be increased. The temperature can be increased to greater than or equal to a melt temperature of resin in the layup (e.g. to greater than or equal 205° C., specifically, 218° C., and more specifically, 232 to 400° C., wherein the specific temperature is dependent upon the particular resin). Once the process temperature is reached, pressure is applied to the layup 38 by creating relative motion between the first platen 32 and the laminate platen 34. The pressure can be greater than or equal to 1 megaPascal (MPa), specifically, greater than or equal to 1.5 MPa, and more specifically, 1.75 MPa to 2.5 MPa, e.g., 2 MPa (e.g., about 300 pounds per square inch (psi)).


It is noted that the pressure is adjusted based upon the layup, wherein too much pressure will inhibit resin wet out of fibers, e.g., due to pressing fiber bundles tightly together restricting resin flow into the bundle, while too little pressure will inhibits the laminates attaining a desired thickness.


After the pressure is applied the temperature is reduced so that the laminate solidifies and can be removed from the laminator. For example the temperature can be reduced to less than or equal to 38° C., specifically, less than or equal to 33° C., and more specifically, less than or equal to 27° C. The temperature reduction can be by rapid cooling (e.g., reducing the temperature by greater than or equal to 25° F. per minute). Once cooled, the vacuum and pressure can be released and the laminate can be removed.


Alternatively, a laminate can be formed in a dynamic laminating process, e.g., using a heated twin belt laminator. In this process, alternating feeds of film and fabric (or tape) is fed into the laminator, with the number of films and fabrics dependent upon the desired thickness of the laminate. In the first stage, the drying stage, pressure is applied to allow moisture release. In the next stage, the melt zone, the temperature and pressure are increased to cause the resin to flow into the fabric. In the cooling zone, the layup is cooled under pressure to completely solidify the laminate. For example, referring to FIG. 15, films 102 and fabrics 104 are fed into the twin belt laminator 100. Pressure (e.g., a pressure of greater than or equal to 10 pounds per square inch (psi), for example 10 psi to 25 psi) is applied in the drying zone 106, e.g., during the first stage, allowing moisture to escape. In the next stage, the melt zone 108, the pressure and temperature are increased to allow the resin flow into the fabric. The temperature, which is dependent on the particular resin, can be within the melt process temperature of such resin. The pressure, which is also dependent upon the particular resin and particularly the melt viscosity thereof, can be greater than or equal to 50 psi, for example, the pressure can vary from 50 psi to 500 psi. From the melt zone 108, the layup enters the cooling zone 110 where it is solidified under pressure to form the laminate 114. The laminate 114 can then optionally be cut to the desired length. The continuous laminating process can yield sheet products four feet wide and cut to any length after which smaller pieces can be cut for a desired application.


As illustrated in FIG. 10, a sequential gate opening system in the injection molding tool can be incorporated to get favorable alignment of fibers (short and/or long fibers) and minimize weld lines in the polymer reinforcement structure 4 (e.g., honeycomb or ribbed geometry). As a result, the injection molding cavity can fill from one end to the other, enhancing the quality of the final product.


By uniting the structural component (e.g., any hollow, metal, load bearing component in the vehicle) and hybrid reinforcements as described herein, several advantages are realized: (i) the design is lighter compared to all metallic components, yet the same structural requirements are still met, (ii) the plastic reinforcements have a high stiffness by weight ratio compared to other reinforcements (e.g., compared to foam, expandable epoxy, and steel reinforcements), (iii) there is better thermal performance during paint cycle compared to foam or epoxy reinforcement solutions, and/or (iv) no changes are required in existing assembly line; e.g., the crush countermeasure can be manufactured and used in a motor vehicle without the use of additional processing steps. In addition, since the same structural integrity can be attained at a reduced weight, or better structural integrity can be attained at the same weight of standard, all steel structural components (e.g., BIW), this design is better suited to meet the carbon dioxide emission requirements due to be in effect by 2016, as well as meeting the safety requirements of the National Highway Traffic Safety Administration (NHTSA).


Set forth below are some embodiments of the tool, laminate, shell, energy absorbing device, vehicle, and structural components described herein.


Embodiment 1

An energy-absorbing device, comprising: a polymer reinforcement structure, wherein the polymer reinforcement structure comprises a polymer matrix and chopped fibers; and a shell comprising 2 walls extending from a back and forming a shell channel, wherein the shell comprises continuous fibers and a resin matrix; wherein the polymer reinforcement structure is located in the shell channel.


Embodiment 2

The device of Embodiment 1, wherein some of the polymer matrix is located in openings at edges of the shell, forming a mechanical bond between the shell and the polymer reinforcement structure.


Embodiment 3

The device of any of Embodiments 1-2, wherein the polymer reinforcement structure comprises honeycombs and/or ribs, e.g., cross-rib pattern or honeycomb.


Embodiment 4

The device of any of Embodiments 1-3, wherein the polymer reinforcement structure comprises honeycombs that extend in the same direction as the walls toward the back.


Embodiment 5

The device of any of Embodiments 1-4, wherein the shell channel has a major axis, and wherein the honeycomb structure comprises honeycomb channels, and wherein the honeycomb channels are oriented perpendicular to the major axis.


Embodiment 6

The device of any of Embodiments 1-5, wherein the polymer reinforcement structure is inseparably attached to the shell.


Embodiment 7

The device of any of Embodiments 1-6, wherein the plastic element has a hollow honeycomb structure with hexagonal comb geometry, and has a length of 150 mm to 350 mm.


Embodiment 8

The device of any of Embodiments 1-7, wherein the shell comprises a plurality of holes through the walls.


Embodiment 9

The device of any of Embodiments 1-8, wherein the device forms vehicle component comprising bumper beam, rail, pillar, chassis, floor rocker, cross-bar, an instrument panel, cross-car member, door support bar, seat structure, suspension controller, engine block, oil pump cover, and combinations comprising at least one of the foregoing.


Embodiment 10

The device of Embodiment 9, wherein, besides optional metal fibers, the device is metal free.


Embodiment 11

The device of Embodiment 9, wherein the device comprises no metal shell, coating, or housing.


Embodiment 12

The energy absorbing device of any of Embodiments 1-11, wherein energy-absorbing device is metal free.


Embodiment 13

The energy absorbing device of any of Embodiments 1-12, wherein the continuous fibers are unidirectional.


Embodiment 14

A structural body of a vehicle, comprising: a hollow structural vehicle component comprising walls that define a cavity, wherein the vehicle component has a component length; and the energy-absorbing device of any of Embodiments 1-13; wherein the energy-absorbing device is located in the cavity.


Embodiment 15

The structural body of Embodiment 14, wherein the structural vehicle component is selected from the group consisting of bumper beam, rail, pillar, chassis, floor rocker, cross-bar, an instrument panel, cross-car member, door support bar, seat structure, suspension controller, engine block, oil pump cover, as well as other components, as well as combinations comprising at least one of the foregoing.


Embodiment 16

The structural body of Embodiment 15, wherein the structural vehicle component is a floor rocker.


Embodiment 17

A vehicle, comprising: the structural vehicle component; and the energy-absorbing device of any of Embodiments 1-13, optionally located in the structural vehicle component; an engine; and a drive mechanism.


Embodiment 18

A vehicle, comprising: the structural vehicle component, wherein the structural vehicle component is the energy-absorbing device of any of Embodiments 1-13; an engine; and a drive mechanism.


Embodiment 19

A forming tool for forming a laminate shell, comprising: a first platen comprises a core; a hinged platen, comprising first movable section, second movable section, and intermediate section located between first movable section and second movable section; a first hinge connecting the first movable section and the intermediate section, such that the first movable section can move from a flat position to a forming position adjacent the core; and a second hinge connecting the second movable section and the intermediate section, such that the second movable section can move from a flat position to a forming position adjacent the core; wherein the core extends from the first platen, between the first platen and the hinged platen; and wherein the first platen and the hinged platen are configured to create relative motion therebetween to decrease a distance between the core and the intermediate section.


Embodiment 20

The forming tool of Embodiment 19, further comprising cylinders oriented to move the first movable section, or the second movable section, or the first movable section and the second movable section.


Embodiment 21

A method of forming a laminate, comprising: feeding fiber structure and resin film to a heated belt to form layup; optionally applying a drying pressure to allow moisture release to form a dried layup; increasing a temperature and the pressure to flow the resin into the fiber structure to form the laminate; and cooling the laminate to solidify the laminate.


Embodiment 22

The method of Embodiment 21, wherein the laminate is cooled under pressure.


Embodiment 23

The method of Embodiment 22, wherein the laminate is cooled under the pressure of greater than or equal to 30 psi, or a pressure of greater than or equal to 50 psi, or a pressure of 50 psi to 500 psi.


Embodiment 24

The method of any of Embodiments 21-23, wherein the drying pressure is greater than or equal to 10 psi.


Embodiment 25

The method of any of Embodiments 21-24, wherein increasing the temperature and the pressure to flow the resin comprises increasing the temperature to greater than or equal to a melt temperature of the resin, and the pressure to greater than or equal to 50 psi.


Embodiment 26

The method of any of Embodiments 21-25, wherein the layup comprises alternating layers of fiber structure and resin.


Embodiment 27

The method of any of Embodiments 21-26, wherein the layup comprises greater than or equal to 4 fiber structures.


Embodiment 28

The method of any of Embodiments 21-27, wherein the layup comprises greater than or equal to 6 fiber structures.


Embodiment 29

A method of forming a laminate, comprising: laying up resin-fiber structures in a laminator to form a layup; optionally drying the layup; pulling a vacuum in the laminator; increasing a temperature to a process temperature; creating relative motion between platens of the laminator to apply pressure to the layup at the process temperature to form the laminate; cooling the laminate.


Embodiment 30

The method of Embodiment 29, wherein the resin-fiber structure is formed by: applying powder to a fiber structure; forcing the powder into the fabric structure; heating to above a Tg of the resin to form a heated fiber structure; and rolling the heated fiber structure to form the resin fiber structure.


Embodiment 31

The method of Embodiment 30, wherein the powder is forced into the fiber structure with ultrasonic air impingement.


Embodiment 32

The method of any of Embodiments 21-31, further comprising laying up the fiber structures such that the layup has a fiber orientation of alternating 0 degrees and 90 degrees, (0/45/−45), (0/60/−60), (0/45/90/0), (0/90/0/90/90/0/90/0), (0/90/0/0/90/0), (0/90/45/0/0/45/90/0), or (0/60/90/90/90/60/0).


Embodiment 33

The method of an of Embodiments 21-32, further comprising laying up the fiber structures such that the layup has a fiber orientation forming a balanced layup.


Embodiment 34

A method of forming a laminate shell, comprising: placing the laminate of any of Embodiments 21-33 onto a hinged platen in a forming tool; heating the laminate; moving a first movable section and second movable section toward a core, and decreasing a distance between the core and an intermediate section, such that the laminate bends to form the shell; cooling the shell; and removing the shell from the forming tool.


Embodiment 35

The method of Embodiment 34, wherein the shell has a total thickness of 0.2 to 10 mm, or 0.3 to 3 mm, or 0.5 mm to 2 mm, or 0.5 mm to 1.5 mm.


Embodiment 36

A method of forming an energy-absorbing device, comprising: overmolding the shell of any of Embodiments 34-35 with a polymer reinforcement structure to form the energy absorbing device.


Embodiment 37

The method of Embodiment 36, wherein the polymer reinforcement structure comprises honeycombs and/or ribs.


Embodiment 38

The method of any of Embodiments 36-37, wherein the polymer reinforcement structure has channels that extend parallel to the sides of the shell and perpendicular to an intermediate section of the shell.


Embodiment 39

An energy-absorbing device, comprising: a polymer reinforcement structure, wherein the polymer reinforcement structure comprises a polymer matrix and chopped fibers; and a shell comprising 2 walls extending from a back and forming a shell channel, wherein the shell comprises continuous fibers and a resin matrix, and wherein the resin matrix is a polymeric resin matrix; wherein the polymer reinforcement structure is located in the shell channel; wherein the shell comprises a laminate formed from a layup of fiber structures such that the layup has a fiber orientation of angles comprising at least two different angles.


Embodiment 40

The device of Embodiment 39, wherein the angles are selected from 0 degrees and 90 degrees, (0/45/−45), (0/60/−60), (0/45/90/0), (0/90/0/90/90/0/90/0), (0/90/0/0/90/0), (0/90/45/0/0/45/90/0), or (0/60/90/90/90/60/0).


Embodiment 41

The device of any of Embodiments 39-40, wherein the angle comprises a fiber orientation forming a balanced layup.


Embodiment 42

The device of any of Embodiments 39-41, wherein the polymer reinforcement structure comprises honeycombs and/or ribs.


Embodiment 43

The device of any of Embodiments 39-42, wherein the polymer reinforcement structure comprises honeycombs that extend in the same direction as the walls toward the back.


Embodiment 44

The device of any of Embodiments 39-43, wherein the shell channel has a major axis, and wherein the honeycomb structure comprises honeycomb channels, and wherein the honeycomb channels are oriented perpendicular to the major axis.


Embodiment 45

The device of any of Embodiments 39-44, wherein the polymer reinforcement structure is inseparably attached to the shell.


Embodiment 46

The device of any of Embodiments 39-45, wherein the plastic element has a hollow honeycomb structure with a hexagonal comb geometry.


Embodiment 47

The device of any of Embodiments 39-46, wherein the shell comprises a plurality of holes through the walls.


Embodiment 48

The device of any of Embodiments 39-47, wherein, besides optional metal fibers, the device is metal free.


Embodiment 49

The device of any of Embodiments 39-48, wherein the device comprises no metal shell, coating, or housing.


Embodiment 50

The device of any of Embodiments 39-49, wherein the polymeric resin matrix and the polymer matrix are independently selected from polycarbonate; polybutylene terephthalate; acrylonitrile-butadiene-styrene; polycarbonate; acrylic-styrene-acrylonitrile; acrylonitrile-(ethylene-polypropylene diamine modified)-styrene; phenylene ether resins; polyamides; phenylene sulfide resins; polyvinyl chloride; polystyrene; polyethylene; polypropylene; polyetherimide; and combinations comprising at least one of the foregoing.


Embodiment 51

The device of any of Embodiments 39-50, wherein the polymeric resin matrix and the polymer matrix are independently selected from polycarbonate blends; polycarbonate/PBT blends; polycarbonate/ABS blends; copolycarbonate-polyesters; blends of polyphenylene ether/polyamide; polyamides; and comprising at least one of the foregoing.


Embodiment 52

The device of any of Embodiments 39-51, wherein the polymeric resin matrix and the polymer matrix are independently selected from Noryl™ GTX resin, LEXAN™ resin, ULTEM™ resin, VALOX™ resin, CYCOLAC™ resin, and/or STAMAX™ resin.


Embodiment 53

The device of any of Embodiments 39-52, wherein the continuous fibers are selected from glass fibers, carbon fibers, bamboo fibers, aramid fibers, kevelar fibers, and combinations comprising at least one of the foregoing.


Embodiment 54

The device of any of Embodiments 39-53, wherein the chopped fibers are selected from glass fibers, carbon fibers, bamboo fibers, aramid fibers, kevelar fibers, and combinations comprising at least one of the foregoing.


Embodiment 55

The device of any of Embodiments 39-54, wherein the continuous fibers and the chopped fibers are independently selected from glass fibers, carbon fibers, and combinations comprising at least one of the foregoing.


Embodiment 56

The device of any of Embodiments 39-55, wherein device is metal free.


Embodiment 57

The device of any of Embodiments 39-56, wherein the continuous fibers are unidirectional.


Embodiment 58

A structural body of a vehicle, comprising: a hollow structural vehicle component comprising walls that define a cavity, wherein the structural vehicle component has a component length; and the energy-absorbing device of any of Embodiments 39-57; wherein the energy-absorbing device is optionally located in the cavity.


Embodiment 59

The structural body of Embodiment 58, wherein the structural vehicle component is selected from the group consisting of bumper beam, rail, pillar, chassis, floor rocker, cross-bar, an instrument panel, cross-car member, door support bar, seat structure, suspension controller, engine block, oil pump cover, as well as other components, as well as combinations comprising at least one of the foregoing.


Embodiment 60

The structural body of Embodiment 59, wherein the structural vehicle component is a floor rocker.


Embodiment 61

A vehicle, comprising: the structural vehicle component; and the energy-absorbing device of any of Embodiments 39-57, located in the structural vehicle component; an engine; and a drive mechanism.


All ranges disclosed herein are inclusive of the endpoints, and the endpoints are independently combinable with each other (e.g., ranges of “up to 25 wt. %, or, more specifically, 5 wt. % to 20 wt. %”, is inclusive of the endpoints and all intermediate values of the ranges of “5 wt. % to 25 wt. %,” etc.). “Combination” is inclusive of blends, mixtures, alloys, reaction products, and the like. Furthermore, the terms “first,” “second,” and the like, herein do not denote any order, quantity, or importance, but rather are used to identify one element from another. The terms “a” and “an” and “the” herein do not denote a limitation of quantity, and are to be construed to cover both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context. The suffix “(s)” as used herein is intended to include both the singular and the plural of the term that it modifies, thereby including one or more of that term (e.g., the film(s) includes one or more films). Reference throughout the specification to “one embodiment”, “another embodiment”, “an embodiment”, and so forth, means that a particular element (e.g., feature, structure, and/or characteristic) described in connection with the embodiment is included in at least one embodiment described herein, and may or may not be present in other embodiments. In addition, it is to be understood that the described elements may be combined in any suitable manner in the various embodiments. As used herein, “free” is intended to only include impurities and not intentionally added elements.


While particular embodiments have been described, alternatives, modifications, variations, improvements, and substantial equivalents that are or may be presently unforeseen may arise to applicants or others skilled in the art. Accordingly, the appended claims as filed and as they may be amended are intended to embrace all such alternatives, modifications variations, improvements, and substantial equivalents.

Claims
  • 1. A structural body of a vehicle, comprising: a body-in-white (BIW) structural vehicle component that is hollow and comprises walls that define a cavity, wherein the BIW structural vehicle component has a component length, and an energy-absorbing device located in the cavity, the energy-absorbing device, including:a polymer reinforcement structure,wherein the polymer reinforcement structure comprises a polymer matrix and chopped fibers; anda shell comprising two walls extending from a back and forming a U-shaped shell channel of a crush countermeasure of the BIW structural vehicle component,wherein the shell comprises a laminate formed of a layup of alternating layers of fibers structure and a resin matrix such that, for each layer in the layup, fibers of the fiber structures are oriented a different angle than the fibers of each adjacent layer;wherein the polymer matrix with chopped fibers is overmolded onto the shell to form the polymer reinforcement structure located in the shell channel, the polymer reinforcement structure being inseparably attached directly to the shell;wherein the polymer reinforcement structure comprises honeycombs and/or ribs; andwherein the fiber structure includes continuous fibers that comprise at least one of: fabric fibers, wherein the fabric fibers are located in a single plane and oriented in at least two directions; andunidirectional tape fibers, wherein greater than or equal to 90% of the unidirectional tape fibers are oriented in the same direction.
  • 2. The structural body of claim 1, wherein the continuous fibers comprise fabric fibers,wherein the fabric fibers are located in a single plane and oriented in at least two directions.
  • 3. The structural body of claim 1, wherein the continuous fibers comprise unidirectional tape fibers,wherein greater than or equal to 90% of the unidirectional tape fibers are oriented in the same direction.
  • 4. The structural body of claim 1, wherein: the shell comprises a plurality of holes through the two walls that extend from the back; andsome of the polymer matrix is located in the holes, forming a mechanical bond between the shell and the polymer reinforcement structure.
  • 5. The structural body of claim 1, wherein: the shell comprises a plurality of openings at edges of the shell; andsome of the polymer matrix is located in the openings, forming a mechanical bond between the shell and the polymer reinforcement structure.
  • 6. The structural body of claim 1, wherein the polymer reinforcement structure comprises honeycombs that extend in the same direction as the walls toward the back.
  • 7. The structural body of claim 6, wherein: the shell channel has a major axis;the honeycombs comprises honeycomb channels; andthe honeycomb channels are oriented perpendicular to the major axis.
  • 8. The structural body of claim 1, wherein the polymer reinforcement structure has a hollow honeycomb structure with hexagonal comb geometry.
  • 9. The structural body of claim 1, wherein: the resin matrix is a polymeric resin matrix.
  • 10. The structural body of claim 1, wherein the chopped fibers are selected from glass fibers, carbon fibers, bamboo fibers, aramid fibers, and combinations comprising at least one of the foregoing.
  • 11. The structural body of claim 1, wherein the device forms a structural vehicle component comprising bumper beam, rail, pillar, chassis, floor rocker, cross-bar, an instrument panel, cross-car member, door support bar, seat structure, suspension controller, engine block, oil pump cover, and combinations comprising at least one of the foregoing.
  • 12. The structural body of claim 1, wherein the device comprises metal fibers and is otherwise metal free.
  • 13. The structural body of claim 1, wherein the device comprises no metal shell, coating, or housing.
  • 14. The structural body of claim 1, wherein energy-absorbing device is metal free.
  • 15. A vehicle, comprising: the structural body of claim 1;an engine; anda drive mechanism.
  • 16. A method of forming the energy-absorbing device of claim 1, comprising: forming the shell by: feeding the fiber structure and resin film to a heated belt to form the layup;increasing a temperature and the pressure to flow the resin film into the fiber structure to form the laminate;cooling the laminate to solidify the laminate;placing the laminate onto a hinged platen in a forming tool;heating the laminate;moving a first movable section and second movable section toward a core, and decreasing a distance between the core and an intermediate section, such that the laminate bends to form the shell;cooling the shell;removing the shell from the forming tool; andovermolding the shell with the polymer reinforcement structure to form the energy absorbing device.
  • 17. The method of claim 16, further comprising applying a drying pressure to allow moisture release to form a dried layup.
Priority Claims (1)
Number Date Country Kind
1618/DEL/2014 Jun 2014 IN national
CROSS REFERENCE TO RELATED APPLICATIONS

This application is a 371 of International Application No. PCT/IB2015/054518, filed Jun. 15, 2015, which claims priority to United States Patent Application Nos. 62/012,515, filed Jun. 16, 2014 and 62/012,522, filed Jun. 16, 2014 and Indian Patent Application No. 1618/DEL/2014, filed Jun. 16, 2014 all of which are incorporated by reference in their entirety herein.

PCT Information
Filing Document Filing Date Country Kind
PCT/IB2015/054518 6/15/2015 WO
Publishing Document Publishing Date Country Kind
WO2015/193795 12/23/2015 WO A
US Referenced Citations (150)
Number Name Date Kind
2882564 Couse et al. Apr 1959 A
3162745 Rohr Dec 1964 A
3633934 Wilfert Jan 1972 A
3842944 Shiotani et al. Oct 1974 A
3887223 Bez Jun 1975 A
4227593 Bricmont et al. Oct 1980 A
4357040 Tomioka Nov 1982 A
4890877 Ashtiani-Zarandi et al. Jan 1990 A
5139297 Carpenter et al. Aug 1992 A
5139843 Murakami Aug 1992 A
5150935 Glance et al. Sep 1992 A
5164141 Becker et al. Nov 1992 A
5190803 Goldbach et al. Mar 1993 A
5306066 Saathoff Apr 1994 A
5354604 Blakeman et al. Oct 1994 A
5480729 Hattori et al. Jan 1996 A
5518802 Colvin May 1996 A
5529826 Tailor et al. Jun 1996 A
5618074 Weast Apr 1997 A
5682667 Flagg Nov 1997 A
5715917 Smallwood Feb 1998 A
5746419 McFadden et al. May 1998 A
5804511 Kelman et al. Sep 1998 A
5819408 Catlin Oct 1998 A
5836547 Koch Nov 1998 A
5975623 Shikimachi Nov 1999 A
6050631 Suzuki Apr 2000 A
6158771 Nusser Dec 2000 A
6168226 Wycech Jan 2001 B1
6299958 St. Julien et al. Oct 2001 B1
6336249 Plumley Jan 2002 B1
6394512 Schuster et al. May 2002 B1
6467822 Leng Oct 2002 B1
6494510 Okamura et al. Dec 2002 B2
6503585 Wagenblast et al. Jan 2003 B1
6513843 Frederick et al. Feb 2003 B1
6540275 Iwamoto et al. Apr 2003 B1
6547295 Vismara Apr 2003 B2
6592174 Rollin et al. Jul 2003 B1
6668513 Roberts et al. Dec 2003 B2
6685243 Evans Feb 2004 B1
6746061 Evans Jun 2004 B1
6866294 Horsch et al. Mar 2005 B2
6866331 Kropfeld Mar 2005 B2
6905136 Vidal et al. Jun 2005 B2
6938936 Moojiman et al. Sep 2005 B2
6942910 Roberts et al. Sep 2005 B2
7004502 Borroni-Bird et al. Feb 2006 B2
7008006 Steinhauser et al. Mar 2006 B2
7044514 Mustafa et al. May 2006 B2
7086690 Shuler et al. Aug 2006 B2
7134700 Evans Nov 2006 B2
7163243 Evans Jan 2007 B2
7222896 Evans May 2007 B2
7434872 Steller Oct 2008 B2
7517006 Kageyama et al. Apr 2009 B2
7520561 Nakamae et al. Apr 2009 B2
7520616 Ooba et al. Apr 2009 B2
7597383 Itou et al. Oct 2009 B2
7607720 Noyori et al. Oct 2009 B2
7699383 Fukukawa et al. Apr 2010 B2
7806448 Allen et al. Oct 2010 B2
7879435 Mett et al. Feb 2011 B2
8047603 Goral et al. Nov 2011 B2
8158539 Balthes Apr 2012 B2
8303743 Youn et al. Nov 2012 B2
8322780 Nagwanshi et al. Dec 2012 B2
8336933 Nagwanshi et al. Dec 2012 B2
8430437 Asakawa et al. Apr 2013 B2
8469417 Di Modugno Jun 2013 B2
8474583 Nagwanshi et al. Jul 2013 B2
8864216 Nagwanshi et al. Oct 2014 B2
9067550 Nagwanshi et al. Jun 2015 B2
9238347 Nelson et al. Jan 2016 B2
10053046 Villacres Mesias Aug 2018 B2
10072690 Fleischheuer et al. Sep 2018 B2
10232889 Kellner Mar 2019 B2
10328882 Schmitt Jun 2019 B2
20010026072 Sato et al. Oct 2001 A1
20020017805 Carroll, III et al. Feb 2002 A1
20020043809 Vismara Apr 2002 A1
20020050413 Renault May 2002 A1
20020070584 Carroll, III et al. Jun 2002 A1
20020121714 Preisler Sep 2002 A1
20020121718 Winget Sep 2002 A1
20020121723 Preisler Sep 2002 A1
20020121787 Tarahomi Sep 2002 A1
20020125725 Satou Sep 2002 A1
20020129981 Satou Sep 2002 A1
20020180223 Vismara et al. Dec 2002 A1
20030008105 Haack et al. Jan 2003 A1
20030034658 Cate et al. Feb 2003 A1
20030067179 Bastien et al. Apr 2003 A1
20030164618 Gentle Sep 2003 A1
20040037625 Corrias et al. Feb 2004 A1
20040051321 Hanai et al. Mar 2004 A1
20040094684 Sailer May 2004 A1
20040124643 Matsumoto et al. Jul 2004 A1
20040174025 Converse et al. Sep 2004 A1
20040232591 Dajek et al. Nov 2004 A1
20060032579 Ohata Feb 2006 A1
20060119116 Goertz Jun 2006 A1
20060181089 Andre et al. Aug 2006 A1
20070090666 Brennecke et al. Apr 2007 A1
20070122510 Mendiboure et al. May 2007 A1
20070134452 Merkle et al. Jun 2007 A1
20070175571 Rubin et al. Aug 2007 A1
20070257497 Heatherington et al. Nov 2007 A1
20080001434 Henkelmann Jan 2008 A1
20080048462 Zabik Feb 2008 A1
20080098601 Heinz et al. May 2008 A1
20080138586 Mooijman et al. Jun 2008 A1
20080156425 Howe et al. Jul 2008 A1
20080238140 Kejha Oct 2008 A1
20080246277 Gallagher et al. Oct 2008 A1
20080286522 Khan et al. Nov 2008 A1
20080317988 Mooijman et al. Dec 2008 A1
20090081462 Miyoshi et al. Mar 2009 A1
20090160203 Garg et al. Jun 2009 A1
20090167055 Niezur et al. Jul 2009 A1
20090309387 Goral et al. Dec 2009 A1
20100173126 Malek et al. Jul 2010 A1
20100187865 Malek et al. Jul 2010 A1
20100201040 Guichard et al. Aug 2010 A1
20100228001 Mortimer Sep 2010 A1
20100244472 Gonin et al. Sep 2010 A1
20100327630 Klimek et al. Dec 2010 A1
20110133517 Leanza Jun 2011 A1
20110316307 Di Modugno Dec 2011 A1
20120112479 Nagwanshi et al. May 2012 A1
20120153669 Nagwanshi et al. Jun 2012 A1
20120193939 Howe et al. Aug 2012 A1
20120269999 Kind et al. Oct 2012 A1
20120309247 Kleine et al. Dec 2012 A1
20130052392 Radlmayr et al. Feb 2013 A1
20130106139 Nagwanshi et al. May 2013 A1
20130164501 Jung et al. Jun 2013 A1
20130181373 Stock et al. Jul 2013 A1
20130257098 Matsuda et al. Oct 2013 A1
20130309442 Ruby et al. Nov 2013 A1
20140084633 Matsuda et al. Mar 2014 A1
20140103670 Iijima et al. Apr 2014 A1
20140190445 Reese et al. Jul 2014 A1
20140203577 Nagwanshi et al. Jul 2014 A1
20140203592 Nagwanshi et al. Jul 2014 A1
20150360733 Nagwanshi et al. Dec 2015 A1
20170008206 Schoenhammer et al. Jan 2017 A1
20170182874 Shimasaki et al. Jun 2017 A1
20170217393 Mohapatra et al. Aug 2017 A1
20170327157 Jaunasse et al. Nov 2017 A1
Foreign Referenced Citations (74)
Number Date Country
2361761 Oct 2000 CA
2394790 May 2001 CA
2044543 Sep 1989 CN
1479680 Mar 2004 CN
1747858 Mar 2006 CN
101346259 Jan 2009 CN
101529118 Sep 2009 CN
101679654 Mar 2010 CN
101797822 Aug 2010 CN
101939558 Jan 2011 CN
102561230 Jul 2012 CN
102785438 Nov 2012 CN
4115831 Nov 1992 DE
102006032867 Jan 2008 DE
102007038087 Feb 2009 DE
102011104368 Mar 2012 DE
102011109514 Feb 2013 DE
0661198 Jul 1995 EP
0967138 Dec 1999 EP
1065108 Jan 2001 EP
1104857 Jun 2001 EP
1300293 Apr 2003 EP
1369309 Dec 2003 EP
1419936 May 2004 EP
1473197 Nov 2004 EP
1593872 Nov 2005 EP
1652733 May 2006 EP
1759959 Mar 2007 EP
2380782 Oct 2011 EP
2889187 Jul 2015 EP
2260998 Nov 2016 ES
2702432 Sep 1994 FR
2859970 Mar 2005 FR
2864811 Jul 2005 FR
2887508 Dec 2006 FR
2890361 Mar 2007 FR
2375328 Nov 2002 GB
2384217 Jul 2003 GB
2386937 Oct 2003 GB
S61261012 Nov 1986 JP
0454336 Feb 1992 JP
H04201412 Jul 1992 JP
H07132514 May 1995 JP
09020267 Jan 1997 JP
H1085842 Apr 1998 JP
2001208120 Aug 2001 JP
2004009726 Jan 2004 JP
2006247237 Sep 2006 JP
2010120167 Jun 2010 JP
19970023007 May 1997 KR
1020070122301 Dec 2007 KR
1020090042791 Apr 2009 KR
2010056402 May 2010 KR
20130031949 Apr 2013 KR
101396822 Dec 2013 KR
20140023757 Feb 2017 KR
2005044531 May 2005 WO
2005100100 Oct 2005 WO
2005105554 Nov 2005 WO
2006008150 Jan 2006 WO
2006065868 Jun 2006 WO
2006066966 Jun 2006 WO
2006119225 Nov 2006 WO
2006136743 Dec 2006 WO
2008016653 Feb 2008 WO
2008073522 Jun 2008 WO
2010103449 Sep 2010 WO
2010108015 Sep 2010 WO
2012014091 Feb 2012 WO
2012042396 Apr 2012 WO
2012085070 Jun 2012 WO
2013007386 Jan 2013 WO
2014060212 Apr 2014 WO
2014078499 May 2014 WO
Non-Patent Literature Citations (41)
Entry
Chinese Patent No. 101346259(A); Date of Publication: Jan. 14, 2009; Machine Translation; 17 Pages.
Chinese Patent No. 101529118(A); Date of Publication: Sep. 9, 2009; Machine Translation; 32 Pages.
Chinese Patent No. 101939558(A1); Date of Publication: Jan. 5, 2011; Machine Translation; 20 Pages.
Chinese Patent No. 1479680(A); Date of Pubiication: Mar. 3, 2004; Machine Translation; 14 Pages.
Chinese Patent No. 1747858(A); Date of Publication: Mar. 15, 2006; Machine Translation; 24 Pages.
English Abstract of KR2010056402(A); Date of Publication: May 27, 2010; 2 Pages.
European Patent No. 0661198 (A1); Publication Date: Jul. 5, 1995; Abstract Only; 2 Pages.
European Patent No. 1369309 (A1); Publication Date: Dec. 10, 2003; English Machine Translation; 13 pages.
European Patent No. 1419936 (A1); Publication Date: May 19, 2004; Abstract Only; 1 Page.
European Patent No. 1473197 (A1); Publication Date: Nov. 3, 2004; Abstract Only; 1 Page.
European Patent No. 1652733 (A1); Publication Date: May 3, 2006; Abstract Only; 1 Page.
European Patent No. 1759959 (A2); Publication Date: Mar. 7, 2007; Machine Translation; 18 Pages.
European Patent No. 2380782(A1); Date of Publication: Oct. 26, 2011; Machine Translation; 12 Pages.
French Patent No. 2702432 (A1); Publication Date: Sep. 16, 1994; Abstract Only; 1 Page.
French Patent No. 2859970 (A1); Publication Date: Mar. 25, 2005; Abstract Only; 1 Page.
French Patent No. 2864811 (A1); Publication Date: Jul. 8, 2005; Abstract Only; 1 Page.
French Patent No. 2887508 (A1); Publication Date: Dec. 29, 2006; Abstract Only; 1 Page.
German Patent No. 102007038087(A1); Date of Publication: Feb. 12, 2009; Abstract Only; 1 Page.
German Patent No. 102011104368(A1); Date of Publication: Mar. 15, 2012; Abstract Only; 1 Page.
German Patent No. 102011109514(A1); Date of Publication: Feb. 7, 2013; Machine Translation; 21 Pages.
Grujicic et al., “Investigation of a polymer metal inter-locking technology for use in load-bearing automotive components,” Multidiscipline Modeling in Materials and Structures (2010), vol. 6, No. 1, pp. 22-44.
International Patent No. 2006136743(A3); Date of Publication: Mar. 15, 2007; Abstract Only; 1 Page.
International Publication No. 2005100100 (A1); Publication Date: Oct. 27, 2005; Abstract Only; 1 Page.
International Publication No. 2006136743 (A1); Publication Date: Dec. 28, 2006; Abstract Only; 2 Pages.
International Publication No. 2013007386 (A1); Publication Date: Jan. 17, 2013; Abstract Only; 1 Page.
International Search Report for International Application No. PCT/IB2015/054518; International Filing Date: Jun. 15, 2015; dated Dec. 3, 2015; 7 Pages.
Japanese Patent No. 09020267 (A); Publication Date: Jan. 21, 1997; Abstract Only; 1 Page.
Japanese Patent No. 2006247237 (A); Date of Publication: Sep. 21, 2006; Abstract Only; 1 Page.
Machine Translation of CN102785438(A); Date of Publication: Nov. 21, 2012; 11 Pages.
Machine Translation of ES2260998B2; Date of Publication: Nov. 1, 2006; 4 Pages.
Machine Translation of JPH04201412(A); Date of Publication: Jul. 22, 1992; 5 Pages.
Machine Translation of KR101396822(A); Date of Publication: Dec. 12, 2013; 11 Pages.
Machine Translation of KR20140023757(A); Date of Publication: Feb. 27, 2017; 19 Pages.
Machine Translation of WO2012085070(A1); Date of Publication: Jun. 28, 2012; 12 Pages.
Machine Translation of WO2014060212A1; Date of Publication: Apr. 24, 2014; 17 Pages.
Witteman, Wiilibroordus J.; “improved Vehicle Crashworthiness Design by Control of the Energy Absorption of Different Collision Situations”; Dictoral Dissertation, Eindhoven University of Technology; 1999; 191 Pages.
Written Opinion of the International Searching Authority for International Application No. PCT/IB2015/054518; International Filing Date: Jun. 15, 2015; dated Dec. 3, 2015; 7 Pages.
Zoellner et al., “Plastic-Metal Hybrid—A New Development in the Injection Molding Technology,” ANTEC (2002), 5 Pages.
International Search Report for International Application No. PCT/IB2017/058459; International Filing Date: Dec. 28, 2017; dated Jun. 15, 2018; 6 Pages.
Written Opinion of the International Searching Authority for International Application No. PCT/IB2017/058459; International Filing Date: Dec. 28, 2017; dated Jun. 15, 2018; 7 Pages.
Extended European Search Report issued in Application No. EP 19155120.9 dated Sep. 20, 2019, 55 pages.
Related Publications (1)
Number Date Country
20170158252 A1 Jun 2017 US
Provisional Applications (2)
Number Date Country
62012522 Jun 2014 US
62012515 Jun 2014 US