Patent Application
20120245273
The present invention, as expressed in the title of this specification, refers to structural profiles for the manufacture of household utensils and the process for obtaining those profiles.
These are structural profiles for the manufacture of household utensils and furniture, such as brooms and mop handles; ironing boards' supports, frameworks and legs, interior and exterior clothes dryers, shopping carts, cleaning carts, garden furniture, etc.
The structural profiles of the invention are manufactured with materials from plastic residues in which its major component is a polymer of high elastic modulus, such as PET, polyamide, ABS, etc, and high elastic modulus fiber residues such as fiberglass, carbon, boron, basalt, aramid, etc.
The structural profiles are obtained by kneading and subsequent extrusion with some particular characteristics.
Currently, profiles for the production of household utensils such as brooms and mop handles are made of steel, aluminium or wood, and generally with a diameter of around 22 mm; those made of steel being abundant because of their reduced cost and low weight which makes them very easy to handle.
The properties that are sought in these handles are:
a.—light
b.—easy to handle
c.—handle which is adaptable to the hands of the user
a.—rigidity
b.—resistance to corrosion
c.—durability
The profiles used as structural elements in other household utensils, such as ironing boards, clothes dryers, shopping carts, cleaning carts, are usually made of steel or aluminium because of their rigidity and their capacity to be welded.
On the other hand, there is multitude of residues in the market from food containers mainly formed by PET, mixed or non-mixed with other polymers, such as PE or PP and occasionally barrier polymers, such as EVOH. There are also large quantities of ABS residues from the scrapping of electrical appliances and computer equipment.
There is also a large amount of high elastic modulus fiber residues in the market due the difficulties encountered in its elimination, such as fiberglass or carbon from its own production or its utilization in the production of composites, before and after its impregnation with the resins used in the manufacture of those composites, such as resins of unsaturated polyester or epoxy resins. The residues of the composites themselves, once their service life is ended, are also abundant.
These residues, due to the difficulties of recycling, constitute a serious problem for the environment and consequently they are abundant and cheap.
The structural profiles for the manufacture of household utensils, such as brooms and mop handles, are characterized in that they are at least partly manufactured with some first residues and preferably with bottle residues and other PET pieces with remnants of fiberglass residues.
Those above mentioned first residues comprise parts of materials, such as the ones described in the background section of the invention. Structural profiles, manufactured with the residual composition described, have the following advantages with regard to what is currently available in the market:
They can be manufactured in greater diameters, with an important improvement of their ergonomics, without substantially increasing their weight.
They have a notably lower cost.
They do not rust, as they not have metals in their composition.
They can be recycled again at the end of their service life.
They protect the environment, as they contribute to the recycling of the aforementioned polymers and the fiberglass residues.
More specifically, the composition of the structural profiles of the invention to obtain the handles is the following:
The central tube comprises between 30% and 70% fiberglass and preferably between 40 and 60% fiberglass.
Between 30% and 70% of PET residues that can contain up to a 20% of PE to improve their resistance to impact. Preferably, between 40% and 60% of PET.
In the event that the residues contain proportions over 5% of other non-polar polymers, such as PE or PP, an adhesive polymer will be added. In a preferred embodiment, the adhesive polymer of the exterior and interior layers of the container or corresponding profile of the present invention is selected among the group comprising:
Polyethylene/polypropylene polymers, or mixes of both, containing graft polar groups;
Copolymers of ethylene and acrylic or methacrylic acid;
Copolymer of ethylene and acrylates or acetates;
Derivatives of glycidyl methacrylate; and
Copolymers of styrene-ethylene-butadiene-styrene (SEBS) containing graft polar groups.
In a more preferred embodiment, the graft polar groups are maleic anhydride or acrylic acid. In an even more preferred embodiment, the graft polar groups are in a proportion of less than 15% in weight with regard to the adhesive polymer.
In another preferred embodiment, the graft polar group is maleic anhydride and is in a smaller proportion than 5% in the adhesive polymer weight. In an even more preferred embodiment, the proportion of maleic anhydride is less than 3% in weight.
In another preferred embodiment, the graft polar group is acrylic acid and is in a proportion of less than 7% in the adhesive polymer weight.
The process to obtain the tubular structural profiles, such as handles for brooms and the like, with the defined recycled materials, has the following stages:
A first stage of pre-treatment of the raw materials.
In this first stage the polymer residue should be crushed by the use of grinding mills suitable for these materials and cleaned by means of the already known technologies of washing/drying or dry cleaning with air flow.
Fiberglass, if presented in remnants, should be cut to a measure of around 3 to 20 mm, preferably between 5 and 15 mm, so that it can be subsequently fed, in a continuous dosage, into an extrusion machine. In the event that it comes from resinated composites, these should be ground until defibrated, the resin turn into a powder form and the fiberglass at a size between 1 and 10 mm. The composite will be used in its entirety, without separating the two components.
A second stage of kneading.
In this stage the extrusion of the pre-treated materials can be carried out by melt-kneading, by means of well known devices such as the ones provided with twin screw extruders (sharp or not) although it is not entirely limited to this last possibility. Among other possibilities there is also double shaft extrusion equipment. On the other hand, equipment that has a single shaft extrusor may be preferred, following an intensive mixture or kneading device that carries out the kneading and granulating-extrusion operations.
Another possibility is using an extrusor/mixer, preferably with cutting shafts, and preferably with intermediate gas extraction by vacuum pump, being also adequate other types of multiple shafts extruders/mixers suitable for PET.
Depending on the composition of the polymer residue used, especially if it is a matter of mixtures of polar and non-polar polymers, such as PET+PE or PET+PP; it may be necessary, in the extrusion stage, to utilize some adhesive polymer among the ones already known and existing in the market, which facilitates the blend among the polymers of diverse polarity.
A third stage of co-extrusion.
In this stage, once the homogenized mixture of components is obtained, the profile can be finally shaped, either like a circular crown or other different geometric shapes, such as hexagonal, octagonal, ellipsoidal, etc., that will contribute to their gripping ergonomics or respond to the required design of the utensil that is going to be part of, either in a separate process, in a profile extrusion line from the mixture in a pellet shape or, preferably, following the process of kneading, with or without the aid of a molten pump to increase the pressure in the extrusion mouthpiece, if necessary.
With the purpose to embellish the surface of the profile and to be able to endow it of elements that contribute to its grip or are required for subsequent assembly operations, the extrusion mouthpiece will preferably have two or more layers in co-extrusion of total or partial coating of the handle with coloured or non coloured polymers of diverse nature such as PET, PP, PC, and TPE (thermoplastic elastomers).
These coating layers could also be applied later to the extrusion of the profile by means of the already known profile coating technologies through thermoplastics or coating processes with lacquer, immersion or spray painting or other known methods.
A first embodiment of a handle is the following:
Central profile of circular section:
PET flakes from bottles 48%
Cut fiberglass residues 48%
PTW Dupont Elvaloy compatibilizer Additive 2%
PET flakes from pigmented bottles
Total weight 212 g/m
Elastic Modulus of the profile: 15 GPa
A second embodiment of another handle is the following:
Central profile of circular section:
Flakes of residues from pizza containers formed by 75% of PET, 20% of PE and 5% of EVOH: 47%,
Cut fiberglass fiber residues: 50%
PTW Dupont Elvaloy compatibilizer Additive 3%
PET flakes from pigmented bottles
Total weight: 216 g/m
Elastic modulus of the profile: 9.7 GPa
On the other hand, although the abbreviations used for the polymers are internationally known, each one of them is described as follows:
PP, polypropylene; PE polyethylene; PEHD, high density polyethylene; PELD, low density polyethylene; PC, polycarbonate; PET polyethylene terephthalate; ABS, acrylonitrile.
| Number | Date | Country | Kind |
|---|---|---|---|
| P200930601 | Aug 2009 | ES | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/ES2010/070427 | 6/24/2010 | WO | 00 | 6/7/2012 |