SUBSTANCE SURFACE PROPERTY PARAMETER MEASUREMENT METHOD AND SUBSTANCE SURFACE PROPERTY PARAMETER ANALYSIS SYSTEM THEREOF

Abstract

A universal method for jointly measuring surface property parameters of a material comprises the following steps: performing saturation processing on a surface of a material to be measured; mixing the material to be measured which has been processed by saturation with an indicating electrolyte solution; after the mixture solution achieves an balance by ion exchange, measuring the balanced concentration values of positive ions of the indicating electrolyte and H+ in the mixture solution; according to the balanced concentration values of positive ions of the indicating electrolyte, calculating surface potential of the material; and according to the surface potential of the material, calculating specific surface area and surface charge density of the material; according to surface charge density of the material, calculating surface electric field intensity; according to surface charge density and specific surface area of the material, calculating total surface charge of the material. The method could accurately measure different kinds of surface potentials under difference conditions. A system for measuring surface property parameters of a material based on the method is also disclosed.

Description

FIELD OF INVENTION

The present invention relates to colloidal chemistry, interface chemistry, and materials science. In particular, the present invention relates to a method for measuring substance surface property parameters and an analysis system of substance surface property parameters thereof.

BACKGROUND

Surface properties, such as surface potential, surface charge quantity, surface charge density, surface electric field strength and specific surface area of a substance not only are widely used in the scientific research in fields such as colloid and interface science, material science, life science, soil science, ecology and environment science, but also have extensive use in chemical engineering fields such as paper making, cement, ceramics, chemical mechanical polishing (CMP), coal slurry, coating, cosmetics, food industry, mixed dispersion system. Thus, it is important to measure such substance surface property parameters.

In the existing technologies, typically indicator ion adsorption and potential titration are adopted for measurement of substance surface charge quantity. With respect to the indicator ion adsorption, one must first know the percentage of the total adsorption of H⁻ or OH⁻ that involve electrostatic adsorption. However, since H⁺ and OH⁻ also participate in adsorption of chemical bond, it is impossible to tell the percentage that involves the electrostatic adsorption. Thus, this method cannot measure the surface charge quantity of a system that contains variable charge under any pH values, any electrolyte concentration and any temperatures. The potential titration not only is not suitable for measuring the charge quantity of a system that contains permanent charge, but also its reliability is questionable even for variable charge system. Thus, there is no common measurement method of substance surface charge quantity that suits for various conditions and different systems. Further, no analysis apparatus is available that can conduct such measurement.

In the existing technologies, one method for determining substance surface charge density is based on the following formula:

${\sigma }_0=\frac{T_C}{S}$

wherein, ω₀ is surface charge density, T_c is surface charge quantity, and S is specific surface area.

Since this method requires the parameter of surface charge quantity, the issue faced in measuring the surface charge quantity must exist in determining the surface charge density. In addition, in the above formula of determining surface charge density, a measured data of specific surface area is also required. However, different specific surface area measurement methods may result in wide difference in their measurements. Thus, the reliability of the measurement is hard to control for a surface charge density measurement method that relies on the parameter of specific surface area.

The second method for determining surface charge density is to indirectly obtain a surface charge density value by using relevant formula of Gouy-Chapman upon obtaining a surface potential value of the substance. However, since currently there is no accurate measurement method of surface potential available that can be widely used, there is still difficulties to apply this surface charge density measurement method.

In the existing technologies, the electric field strength is determined based on the following formula:

$E_0=\frac{4\pi }{\varepsilon }{\sigma }_0$

wherein, E₀ is surface electric field strength , ε is medium dielectric constant, in which ε of water is ε=8.9×10⁻¹⁰C²/Jdm. Due to the dependence to surface charge density, the same issue faced in determining surface charge density also exists in determining surface electric field strength.

In the existing technologies, there are various measurement methods, e.g., normally adopted inert gas adsorption, ion negative adsorption, glycol ethyl adsorption, or glycerine adsorption and the like, to determine substance specific surface area. However, same substance using the various measurement methods results in great difference in the measurement. Even though specific surface area analyzer has been developed based on inert gas adsorption, the analyzer does not suit for measuring specific surface area of expandable substance.

Substance surface potential in the present application refers to potential on the initial surface of diffuse layer or OHP (outer Helmholtz surface). The existing measurement methods for substance surface potential include charge density method, negative adsorption method, positive adsorption method, secondary resonance generation method, pH indicator molecular method, fluorescence generation method, atomic force microscopy, and Zeta potential method, etc. All of the above methods have their own limitations. Charge density method, negative adsorption method, positive adsorption method and secondary resonance generation method are all only suitable for measuring surface potential value of constant charge sample of single electrolyte system under neutral condition. pH indicator molecular method, fluorescence determination method and atomic force microscopy will damage the status of the substance surface per se, and thus the reliability of the measurements is hard to control. Zeta potential method does not measure the surface potential; rather, it measures the potential on the shear surface during electrophoresis. The shear surface is away from the surface defined in the present invention. Zeta potential can be measured under different pHs, electrolytes and temperatures. Thus, in view that currently there is no surface potential measurement method that can be widely used under various conditions and is accurate, Zeta potential is the only choice as a surrogate of surface potential. However, extensive studies in recent years have found that, using Zeta potential method to determine the surface potential only has qualitative meaning. In additional, Zeta potential method has very rigorous requirements to the substance to be measured, i.e., it requires that the particle density of suspension colloid cannot be too high, and the particle size cannot be too large. Even the Zetaprobe-model Zeta potentiometer newly launched by Colloidal Dynamics, LLC (US) can only allow the highest particle density of 60% (volume density). Thus, it is impossible to achieve “original state” measurement for a system having higher density or solid particulate substance.

In view of above, currently there is no reliable and widely applicable method and apparatus that can measure substance surface charge quantity, specific surface area and substance surface potential. Thus, the measurement of substance surface electric field strength and surface charge density that relies on the measurements of substance surface charge quantity and specific surface area respectively also have same defects. Further, there is no method and apparatus in the existing technology that can be used to simultaneously measure the above five (5) parameters from a single experiment.

SUMMARY

In order to solve the above problems, the present invention provides a common measurement method for substance surface property parameters, to enable accurate measurement for surface potential of various types of substances under various conditions, so that simultaneous measurement of substance surface potential, surface charge quantity, surface charge density, surface electric field strength and specific surface area can be achieved.

To realize the objectives of the present invention, a measurement method for substance surface property parameters includes the following steps:

1) performing saturation treatment to a surface of a substance to be measured;

2) mixing the saturated substance to be measured with a solution containing indicator electrolytes; the indicator electrolyte solution includes at least one bivalent metallic positive ion A²⁺ and one monovalent metallic positive ion B⁺;

3) upon the mixture obtained from step 2) reaching ion-exchange equilibrium, measuring an equilibrium concentration value of the indicator electrolyte positive ion and hydrogen ion in a bulk solution of the mixture;

4) using the concentration value of the indicator electrolyte positive ion obtained from step 3) to the following formula, to obtain a substance surface potential φ₀:

${\varphi }_0=\frac{\mathrm{RT}}{\left(2{\beta }_A-{\beta }_B\right)F}\ln \frac{c_A^{\infty }\left(c_B^0-c_B^{\infty }\right)}{c_B^{\infty }\left(c_A^0-c_A^{\infty }\right)}$

Wherein, φ₀ is substance surface potential, R is gas constant, T is temperature, F is Faraday constant; c_B⁰ is initial concentration of B⁺ in solution of the system to be measured which equals to mole number of this added ion divided by total volume of water; c_A⁰ is initial concentration of A²⁺ in solution of the system to be measured which equals to mole number of this added ion divided by total volume of water. c_B^∞ is the concentration of B⁺ in the bulk solution when the exchange reaction reaches balance, and c_A^∞ is the initial concentration of A²⁺ in the bulk solution when the exchange reaction reaches balance. β_A is a relative effective charge coefficient of A²⁺ that associates with A²⁺ hydrated radius in a system containing “B⁺+A²⁺”; and β_B is a relative effective charge coefficient of B⁺ that associates with B⁺ hydrated radius in a system containing “B⁺+A²⁺”.

Yet, it further includes the following step after step 4):

5) obtaining a specific surface area of the substance based on the surface potential value from step 4);

Yet, it further includes the following step after step 4):

obtaining a surface charge density of the substance based on the surface potential value from step 4);

Yet, it further includes the following step after obtaining the substance surface charge density:

6) obtaining a surface electric field strength based on the surface charge density from step 5).

Yet, it further includes the following step after obtaining the substance surface charge density: obtaining a surface charge quantity of the substance based on the surface charge density and specific surface area from step 5).

Yet, in the step 1), using acid solution to perform saturation treatment to the surface of the substance through constant flow method.

Yet, the acid solution is HCl or HNO₃ solution.

Yet, step 1) comprises the following steps:

11) having HCl or HNO₃ solution of 0.1 mol/l to flow though the substance to be measured at uniform speed, so that the surface charges of the substance to be measured are all saturated by H⁺ and Cl⁻ (or NO⁻₃) ;

12) having water to flow though the substance to be measured at uniform speed, to wash off redundant H⁺ and Cl⁻ (or NO⁻₃) ;

13) drawing interstitial water out of the substance to be measured.

Yet, the negative ion of the indicator electrolyte is same as the acid radical.

Yet, the indicator electrolyte is “ACl₂ and BCl” or “A(NO₃)₂ and BNO₃”, wherein, A²⁺=Ca² or Mg²⁺; B⁺=K⁺ or Na⁺.

Yet, in step 3), the following steps are used to obtain the equilibrium concentration value of indicator electrolyte positive ion and hydrogen ion in the bulk solution:

31) measuring activity values a_H, a_B and a_A of B⁺, A²⁺ and H⁺ in the bulk solution.

32) using the activity values from step 31) as initial concentration values, and performing iterative operation through the following steps, to obtain activity coefficients and concentration of B⁺, A²⁺ and H⁺.

321) using the activity values from step 31) as initial concentration values of individual ions, and obtaining ionic strength of the system through the following operation:

$I_i=\frac{1}{2}\left(2c_i^H+2c_i^B+6c_i^A\right)$

Wherein, I_i is ionic strength of i_th iteration, c_i^H is concentration of H⁺ of i_th iteration, c_i^B is concentration of B⁺ of i_th iteration, and c_i^A is concentration of A²⁺ of i_th iteration.

322) Based on the ionic strength, calculating activity coefficients of B⁺, A²⁺ and H⁺ through the following formula:

$1g{\gamma }_i^H=1g{\gamma }_i^B=-\frac{2618.4\times T^{-\frac{3}{2}}\sqrt{I_i}}{1+\sqrt{I_i}}$ $1g{\gamma }_i^A=-\frac{10473.6\times T^{-\frac{3}{2}}\sqrt{I_i}}{1+\sqrt{I_i}}$

wherein, γ_i^H, γ_i^B and γ_i^A are activity coefficients of H⁺, B⁺ and A²⁺ of i_th iteration, respectively; and Tis temperature.

323) Base on the activity coefficients from step 322), calculating equilibrium concentration values of B⁺, A²⁺ and H⁺ through the following formula:

$c_i^H=\frac{a_H}{{\gamma }_i^H};c_i^B=\frac{a_B}{{\gamma }_i^B};c_i^A=\frac{a_A}{{\gamma }_i^A}$

wherein, c_i^H, c_i^Bc_i^A are equilibrium ion concentration of H⁺, B⁺ and A²⁺ of i_th iteration, respectively.

Yet, in step 31), using “H⁺—B⁺-A²⁺” combined electrode and detector to detect activity of A²⁺, B⁺ and H⁺ in the bulk solution.

Yet, in step 32), iterating until (i=k+1)th time, when (I_k+1−I_k)/I_k+1<0.001, terminating the iteration operation, and using the final result of step 323) as the equilibrium concentration value.

Yet, using the final value I of ionic strength from the iteration operation to calculate effective charge coefficient through the following formula:

$\hspace{1em}\{\begin{array}{c}{\beta }_B=0.0297\ln I+1\\ {\beta }_A=-0.0297\ln I+1\end{array}$

Yet, in step 5), calculating specific surface area of the substance through the following formula, based on the surface potential value from step 4):

$S=\frac{\kappa V\left(c_B^0-c_B^{\infty }\right){}^{\frac{{\beta }_B{\varphi }_0}{2\mathrm{RT}}}}{1.856c_B^0-c_B^{\infty }{}^{\frac{{\beta }_B{\varphi }_0}{2\mathrm{RT}}}}$

Wherein, V is total volume of water, the unit of which is 1; S is specific surface area, the unit of which is dm²/g; κ is Debye-Hückel parameter, the unit of which is dm⁻¹, and κ is calculated by the following formula:

$\kappa =\sqrt{\frac{8\pi F^2\left(c_H^{\infty }+c_B^{\infty }+3c_A^{\infty }\right)}{\varepsilon \mathrm{RT}}}$

Wherein, ε is medium dielectric constant, in which ε of water is 8.9×10⁻¹⁰C²/Jdm.

Yet, surface charge density of the substance is calculated through the following formula, based on the surface potential value from step 4):

${\sigma }_0=\pm \sqrt{\frac{\varepsilon \mathrm{RT}}{\pi }\left[\begin{array}{c}\left(c_H^{\infty }+c_B^{\infty }\right)\sinh \left(\frac{F{\varphi }_0}{\mathrm{RT}}\right)+\frac{1}{2}c_A^{\infty }{}^{-\frac{2F{\varphi }_0}{\mathrm{RT}}}+\\ c_A^{\infty }{}^{\frac{F{\varphi }_0}{\mathrm{RT}}}-\left(c_H^{\infty }+c_B^{\infty }+\frac{3}{2}c_A^{\infty }\right)\end{array}\right]}$

Wherein, σ₀ is surface charge density, the unit of which is C/dm².

Yet, in step 6), surface electric field strength of the substance is calculated through the following formula, based on the surface charge density from step 5):

$E_0=\frac{4\pi }{\varepsilon }{\sigma }_0$

Wherein, E₀ is substance surface electric field strength, the unit of which is V/dm.

Yet, surface charge quantity is calculated through the following formula, based on the surface charge density and specific surface area from step 5):

T _c =S×σ ₀

Wherein, T_c is surface charge quantity of the substance, the unit of which is C/g.

The present invention also provides an analysis system for substance surface property parameters based on the measurement method for substance surface property parameters as described above. The analysis system includes a detection system, the detection system comprises:

an ion activity detection unit, for detecting individual ion activity in a solution in a detecting sample container; and

a data processing unit, for receiving detecting results from the ion activity detection unit and analyzing surface parameters of a substance to be detected, including:

an ion concentration operation module, for calculating equilibrium ion concentration on the basis of the detecting results received from the ion activity detection unit; and

a surface parameter operation module, for receiving the ion concentration calculated from the ion concentration operation module and calculating a surface potential of the substance to be detected based on the ion concentration.

Yet, the surface parameter operation module further calculates specific surface area, surface charge density and surface electric field strength of the substance to be detected based on the surface potential of the substance to be detected, and calculates charge quantity based on the surface charge density and specific surface area.

Yet, the analysis system for substance surface property parameter further comprises a sample treatment unit, comprising:

a sample container, for containing the substance to be measured and liquid; and

a liquid intake pipe and a liquid offtake pipe, wherein the liquid offtake pipe is in communication with a bottom of the sample container, the liquid intake pipe is in communication with the sample container; and the liquid offtake pipe is connected to a constant-flow pump.

The sample container further includes a stirring unit.

Yet, the ion activity detection unit includes detecting electrode positioned in the sample container; and a millivoltmeter and an ion activity operator, wherein an input of the millivoltmeter is connected to the detecting electrode, an output of the millivoltmeter is connected to the ion activity operator, the ion activity operator receives potential data detected by the millivoltmeter and converts to ion activity data to output to the ion concentration operation module.

Yet, the activity operator converts potential value detected by the millivoltmeter to individual ion activity value through the following method: upon standardization of individual ions with standard solution of known activity, using Nernst equation to obtain individual ion activity value of the substance to be measured in the activity operator.

Yet, the detecting electrode is “H⁺-A²⁺-B⁺” combined electrode, in which A²⁺ is a bivalent metallic ion, and B⁺ is a monovalent metallic ion.

Yet, the detecting electrode is “H⁺—K⁺—Ca²⁺” combined electrode, the ion concentration operation module is “H⁺—K⁺—Ca²⁺” concentration operation module; the number of millivoltmeters is three (3), inputs of the three millivoltmeters are respectively connected to outputs of H⁺ electrode, K⁺ electrode, and Ca²⁺ electrode in the “H⁺—K⁺—Ca²⁺” combined electrode, outputs of the three millivoltmeters are respectively connected to inputs of pH operator, K⁺ activity operator and Ca²⁺ activity operator; upon the pH operator, K⁺ activity operator and Ca²⁺ activity operator respectively calculating activity of H⁺, K⁺ and Ca²⁺, the activity of H⁺, K⁺ and Ca²⁺ are outputted to “H⁺, K⁺ and Ca²⁺” concentration operation module.

The detection system also includes a temperature probe positioned in the sample container; and an electronic thermometer, an input of which is connected to the temperature probe, and outputs of which are respectively connected to inputs of the pH operator, K⁺ activity operator, Ca²⁺ activity operator, “H⁺, Ca²⁺ and K⁺” concentration operation module and surface parameter operation module.

The simultaneous measurement method for substance surface property parameter and analysis system for substrate surface property parameter of the present invention calculate substance surface potential by measuring the equilibrium ion concentration of the indicator electrolyte, so as to eliminate uncertainty caused by chemical reaction between H⁺ or non-indicator ion (i.e., any other ion except for A²⁺ and B⁺) and the substance surface. Under any pH, any electrolyte composition and any electrolyte concentration and temperature, the surface potential of equilibrium system and the concentration of indicator positive ion used always satisfy the following formula:

${\varphi }_0=\frac{\mathrm{RT}}{\left(2{\beta }_A-{\beta }_B\right)F}\ln \frac{c_A^{\infty }\left(c_B^0-c_B^{\infty }\right)}{c_B^{\infty }\left(c_A^0-c_A^{\infty }\right)}$

This ensures that the method and system of the present invention are common measurement method and system applicable for any conditions and any substance types. Accordingly, obtaining substance surface charge density, surface electric field strength, specific surface area and surface charge quantity based on the surface potential measurement suits for any conditions and any substance types. Further, different methods and systems need to be used to conduct measurement for different substance surface property parameters in the existing technology, such parameters can be simultaneously measured by using the method and system of the present invention.

Other advantages, objectives and features of the present invention will be described in the below description to some extent, and to a certain extent will be apparent to people skilled in the art based on the below studies, or can be taught by implementation of the present invention. The objectives and other advantages of the present invention can be achieved and implemented through the description, claims, and drawings that show specific structures.

BRIEF DESCRIPTION OF THE DRAWINGS

To have the objectives, technical solutions and advantages of the present invention more apparent, detailed description will be made in connection with the drawings, wherein:

FIG. 1 shows a structure diagram of a sample treatment device of a substance surface property parameter analysis system;

FIG. 2 shows a structure diagram of a detection system of the substance surface property parameter analysis system.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

Detailed description of the preferred embodiments of the present invention will be made in connection with the drawings.

The measurement method for substance surface property parameters of this embodiment includes the following steps:

1) Performing a saturation treatment to a surface of an object to be measured, comprising the following steps:

11) Taking 3-5 g sample to be measured into a sample container, and using 150-250 ml HCl solution of 0.1 ml/l to flow though the substance to be measured at a uniform speed of 1 ml/min, to have the surface charges of the object to be measured all saturated by H⁺ and Cl⁻; and, using HNO₃ solution to perform saturation treatment to the sample to be measured;

12) Using 150-250 ml water to flow though the object to be measured at a uniform speed of 1 ml/min, to wash off redundant H⁺ and Cl⁻;

13) Using a constant-flow pump to draw interstitial water out of the object to be measured, until no water flows out.

2) Adding 50 ml mixed solution of KCl, HCl (or KOH) and CaCl₂ with known concentration into the sample pool, stirring sufficiently, and then disposing and balancing for over 24 hours; wherein KCl and CaCl₂ use as indicator electrolytes, and HCl and KOH use for adjusting pH value. Concentration of the above individual electrolytes can be determined based on the requirements of the researcher, but it is preferred to control the ionic strength of the system during equilibrium within 0.2 mol/l. In this step, other indicator electrolytes can also be used, but there are at least two types of indicator electrolytes, including at least one type of bivalent metallic positive ion, such as Ca²⁺, Mg²⁺, and one type of monovalent metallic positive ion, such as Li⁺, Na⁺, Na⁺. The negative ion of the indicator electrolytes shall be same as the negative ion of the acid in step 11). For example, if using HNO₃ solution to perform saturation treatment to the surface of the sample to be measured in step 11), then in this step NaNO₃ and Ca(NO₃)₂ can be used as indicator electrolytes, and HNO₃ and NaOH are used to adjust pH value.

In the following context, description will be made to the present invention by using HCl solution to perform saturation treatment to the surface of the sample to be measured and using KCl and CaCl₂ as indicator electrolytes as an example:

3) Upon the mixture from step 2) reaching ion-exchange equilibrium (i.e., balancing for 24 hours under constant stirring; and, balancing for at least 72 hours under non-stirring condition, in which the balancing time may be vary based on the sample type), measuring the equilibrium concentration of the indicator electrolyte positive ion and hydrogen ion in the bulk solution of the mixture, comprising the following steps:

31) Measuring activity values a_H, a_K and a_Ca of H⁺, K⁺, and Ca²⁺ in the bulk solution;

32) using the activity values from step 31) as initial values of corresponding ion concentration, and performing iteration operation through the following steps to obtain activity coefficients and concentration of K⁺, Ca²⁺ and H⁺; iterating until to (i=k+1)th time, when (I_k+1−I_k)/I_k+1<0.001, terminating the iteration operation;

321) using the activity values from step 31) as initial values, and obtaining ionic strength of the system through the following formula:

$I_i=\frac{1}{2}\left(2c_i^H+2c_i^K+6c_i^{\mathrm{Ca}}\right)$

Wherein, I_i is the ionic strength of i_th iteration, the unit of which is mol/l; c_i^H is concentration of H⁺ at i_th iteration, c_i^K is concentration of K⁺ at i_th iteration, and c_i^Ca is concentration of Ca²⁺ at i_th iteration.

322) Based on the ionic strength, activity coefficients of Na⁺, Ca²⁺ and H⁺ can be calculated through the following formula:

$1g{\gamma }_i^H=1g{\gamma }_i^K=-\frac{2618.4\times T^{-\frac{3}{2}}\sqrt{I_i}}{1+\sqrt{I_i}}$ $1g{\gamma }_i^{\mathrm{Ca}}=-\frac{10473.6\times T^{-\frac{3}{2}}\sqrt{I_i}}{1+\sqrt{I_i}}$

Wherein, γ_i^H, γ_i^K and γ_i^Ca respectively are activity coefficients of H⁺, K⁺ and Ca²⁺ at i_th iteration, and T is temperature, the unit of which is K.

323) Base on the activity coefficients from step 322), the equilibrium concentration values of K⁺, Ca²⁺ and H⁺ can be calculated through the following formula:

$c_i^H=\frac{a_H}{{\gamma }_i^H};c_i^K=\frac{a_K}{{\gamma }_i^K};c_i^{\mathrm{Ca}}=\frac{a_{\mathrm{Ca}}}{{\gamma }_i^{\mathrm{Ca}}}$

Wherein, c^H, c_i^Kc_i^Ca respectively are the equilibrium ion concentration of H⁺, K⁺ and Ca²⁺ at i_th iteration;

4) Substituting the equilibrium ion concentration of K⁺ and Ca²⁺ (equilibrium concentration obtained from last iteration operation) from step 3) into the following formula, to obtain the substance surface potential φ₀:

${\varphi }_0=\frac{\mathrm{RT}}{\left(2{\beta }_{\mathrm{Ca}}-{\beta }_K\right)F}\ln \frac{c_{\mathrm{Ca}}^{\infty }\left(c_K^0-c_K^{\infty }\right)}{c_K^{\infty }\left(c_{\mathrm{Ca}}^0-c_{\mathrm{Ca}}^{\infty }\right)}$

wherein, φ₀ is substance surface potential, R is gas constant, T is temperature, F is Faraday constant, c_K⁰ is concentration of K⁺ in the system when beginning to add KCl, c_Ca⁰ is concentration of Ca²⁺ in the system when beginning to add CaCl₂, c_K^∞ is equilibrium concentration of K⁺, c_Ca^∞ is equilibrium concentration of Ca²⁺, β_K is the relative effective charge coefficient of K⁺ that associates with K⁺ hydrated radius in the system containing “K⁺+Ca²⁺”; and β_Ca is the relative effective charge coefficient of Ca²⁺ that associates with Ca²⁺ hydrated radius in the system containing “K⁺+Ca²⁺”. Using the final value I of ionic strength in the iteration operation to calculate the effective charge coefficient with the following formula:

$\hspace{1em}\{\begin{array}{c}{\beta }_K=0.0297\ln I+1\\ {\beta }_{\mathrm{Ca}}=-0.0297\ln I+1\end{array}$

5) Based on the surface potential value from step 4), specific surface area of the substance is calculated by the following formula:

$S=\frac{\kappa V\left(c_K^0-c_K^{\infty }\right){}^{\frac{{\beta }_K{\varphi }_0}{2\mathrm{RT}}}}{1.856c_K^0-c_K^{\infty }{}^{\frac{{\beta }_K{\varphi }_0}{2\mathrm{RT}}}}$

Wherein, V is total volume of water, the unit of which is 1; S is specific surface area, the unit of which is dm²/g; κ is Debye-Hückel parameter, the unit of which is dm⁻¹, and κ is calculated by the following formula:

$\kappa =\sqrt{\frac{8\pi F^2\left(c_H^{\infty }+c_K^{\infty }+3c_{\mathrm{Ca}}^{\infty }\right)}{\varepsilon \mathrm{RT}}}$

Wherein, ε is medium dielectric constant, in which ε of water is ε=8.9×10⁻¹⁰C²/Jdm.

Based on the surface potential value from step 4), the surface charge density of the substance is calculated by the following formula:

${\sigma }_0=\pm \sqrt{\frac{\varepsilon \mathrm{RT}}{\pi }\left[\begin{array}{c}\left(c_H^{\infty }+c_K^{\infty }\right)\sinh \left(\frac{F{\varphi }_0}{\mathrm{RT}}\right)+\frac{1}{2}c_{\mathrm{Ca}}^{\infty }{}^{-\frac{2F{\varphi }_0}{\mathrm{RT}}}+\\ c_{\mathrm{Ca}}^{\infty }{}^{\frac{F{\varphi }_0}{\mathrm{RT}}}-\left(c_H^{\infty }+c_K^{\infty }+\frac{3}{2}c_{\mathrm{Ca}}^{\infty }\right)\end{array}\right]}$

Wherein, σ₀ is surface charge density, the symbol of which is same as that of the surface potential and the unit of which is C/dm²;

6) Based on the surface charge density from step 5), the surface electric field strength of the substance is calculated by the following formula:

$E_0=\frac{4\pi }{\varepsilon }{\sigma }_0$

wherein, E₀ is surface electric field strength of the substance, the unit of which is V/dm.

Based on the surface charge density and specific surface area from step 5), the surface charge quantity is calculated by the following formula:

T _c =S×σ ₀

Wherein, T_c is the surface charge quantity of the substance, the unit of which is C/g.

An analysis system of substance surface property parameter of this embodiment comprises a sample treatment device and a detection system. Referring to FIG. 1, the sample treatment device includes a sample container 11 for containing the sample to be measured; and a liquid intake pipe 12 and a liquid offtake pipe 13, wherein the liquid offtake pipe 13 is in communication with a bottom of the sample container 11, the liquid intake pipe 12 is in communication with the sample container 11; and the liquid offtake pipe 13 is connected to a constant-flow pump. A stirring device 15 is provided in the sample container 11.

Referring to FIG. 2, the detection system includes:

an ion activity detecting unit for detecting individual ion activity in the solution in the sample container 11, including a detecting electrode 16 disposed in the sample container 11, millivoltmeters 22 and an ion activity operator; the detecting electrode is “H⁺—K⁺—Ca²⁺” combined electrode; inputs of three millivoltmeters 22 are respectively connected to outputs of H⁺ electrode, K⁺ electrode, and Ca²⁺ electrode of the “H⁺—K⁺—Ca²⁺” combined electrode; outputs of the three millivoltmeters 22 are respectively connected to inputs of pH operator 23, Na⁺ activity operator 24, and Ca²⁺ activity operator 25; the millivoltmeters preferably use high-impedance millivoltmeter; and

a data processing unit which can be programmable processor such as single chip microcomputer, the data processing unit receives detected results from the ion activity detecting unit and analyzes the surface parameters of the sample to be measured, comprising:

“H⁺, Ca²⁺, and K⁺” concentration operation module 26 connecting to outputs of the pH operator 23, K⁺ activity operator 24, and Ca²⁺ activity operator 25, to receive the detected results from the above operators, to calculate ion concentration, and

surface parameter operation module 27 for receiving the ion equilibrium concentration from the “H⁺, Ca²⁺, and K⁺” concentration operation module 26 to calculate surface potential, surface charge quantity, surface charge density, surface electric field strength, and specific surface area of the sample to be measured.

Referring to FIGS. 1 and 2, the analysis system of substance surface property parameter further includes a temperature probe 14 disposed in the sample container 11; and an electronic thermometer 21, input of which is connected to the temperature probe 14, and output of which is connected to inputs of the pH operator 23, K⁺ activity operator 24 and Ca²⁺ activity operator 25, concentration operator, and surface property parameter operator.

The pH operator 23, K⁺ activity operator 24 and Ca²⁺ activity operator 25 convert the potential values detected by the millivoltmeters into individual ion activity values through the following method: Upon individual ions are standardized by standard solution (the pH value of which shall be same as that of the solution to be measured) with known activity, the activity operator calculates individual ion activity values of the solution to be measured by using Nernst equation.

The “H⁺, Ca²⁺, and K⁺” concentration operation module 26 calculates concentration of K⁺, Ca²⁺, and H⁺ through the following method:

Using the activity values from the pH operator 23, K⁺ activity operator 24, and Ca²⁺ activity operator 25 as initial values of individual ion concentration, and performing iteration operation through the following steps:

a) Obtaining the ionic strength of the solution through operation of the following formula:

$I_i=\frac{1}{2}\left(2c_i^H+2c_i^K+6c_i^{\mathrm{Ca}}\right)$

Wherein, I_i is ionic strength at i_th iteration, the unit of which is mol/l; c_i^H is concentration of H⁺ at i_th iteration; c_i^K is concentration of K⁺ at i_th iteration; and c_i^Ca is concentration of Ca²⁺ at i_th iteration.

b) Based on the ionic strength, activity coefficients of K⁺, Ca²⁺ and H⁺ at i_th iteration can be calculated through the following formula:

$1g{\gamma }_i^H=1g{\gamma }_i^K=-\frac{2618.4\times T^{-\frac{3}{2}}\sqrt{I_i}}{1+\sqrt{I_i}}$ $1g{\gamma }_i^{\mathrm{Ca}}=-\frac{10473.6\times T^{-\frac{3}{2}}\sqrt{I_i}}{1+\sqrt{I_i}}$

Wherein, γ_i^H, γ_i^K and γ_i^Ca respectively are activity coefficients of H⁺, K⁺ and Ca²⁺ at i_th iteration; and T is temperature, the unit of which is K.

c) Base on the activity coefficients, concentration values of K⁺, Ca²⁺ and H⁺ for the next iteration operation can be obtained through the following formula:

$c_i^H=\frac{a_H}{{\gamma }_i^H};c_i^K=\frac{a_K}{{\gamma }_i^K};c_i^{\mathrm{Ca}}=\frac{a_{\mathrm{Ca}}}{{\gamma }_i^{\mathrm{Ca}}}$

wherein, c_i^H , c_i^Kc_i^Ca respectively are concentration of H⁺, K⁺ and Ca²⁺ of this iteration. Using such concentration values as the concentration for the next iteration, repeating steps a) to c) to perform iteration operation until the (i =k+1)th time, when (I_k+1−I_k)/I_k+1<0.001, terminating the iteration operation, and using individual ion concentration from last time iteration as the final output equilibrium ion concentration.

The surface parameter operation module 27 receives equilibrium ion concentration (final value of the iteration operation) of K⁺ and Ca²⁺ outputted from the “H⁺, Ca²⁺, and K⁺” concentration operation module 26 to substitute to the following formula, to obtain the substance surface potential φ₀:

${\varphi }_0=\frac{\mathrm{RT}}{\left(2{\beta }_{\mathrm{Ca}}-{\beta }_K\right)F}\ln \frac{c_{\mathrm{Ca}}^{\infty }\left(c_K^0-c_K^{\infty }\right)}{c_K^{\infty }\left(c_{\mathrm{Ca}}^0-c_{\mathrm{Ca}}^{\infty }\right)}$

Wherein, φ₀ is substance surface potential, R is gas constant, T is temperature, F is Faraday constant. c_K⁰ is the initial concentration of K⁺ in the system when beginning to add KCl; and c_Ca⁰ is the initial concentration of Ca²⁺ in the system when beginning to add CaCl₂. The two concentration values are calculated based on the total mole number of individual ions added into the system divided by the total volume of water. c_K^∞ is equilibrium concentration of K⁺; c_Ca^∞ is equilibrium concentration of Ca²⁺; β_K is the relative effective charge coefficient of K⁺ that associates with K⁺ hydrated radius in a system containing “K⁺+Ca²⁺”; and, β_Ca is the relative effective charge coefficient of Ca²⁺ that associates with Ca²⁺ hydrated radius in a system containing “K⁺+Ca²⁺”. Using the final value I of ionic strength from iteration operation, the effective charge coefficient is calculated through the following formula:

$\hspace{1em}\{\begin{array}{c}{\beta }_K=0.0297\ln I+1\\ {\beta }_{\mathrm{Ca}}=-0.0297\ln I+1\end{array}$

The surface parameter operation module 27 calculates the specific surface area of the substance through the following formula based on the substance surface potential φ₀:

$S=\frac{\kappa V\left(c_K^0-c_K^{\infty }\right){}^{\frac{{\beta }_K{\varphi }_0}{2\mathrm{RT}}}}{1.856c_K^0-c_K^{\infty }{}^{\frac{{\beta }_K{\varphi }_0}{2\mathrm{RT}}}}$

Wherein, V is the total volume of water, the unit of which is 1; S is specific surface area, the unit of which is dm²/g; κ is Debye-Hückel parameter, the unit of which is dm⁻¹, and κ is calculated through the following formula:

$\kappa =\frac{\sqrt{8\pi F^2\left(c_H^{\infty }+c_K^{\infty }+3c_{\mathrm{Ca}}^{\infty }\right)}}{\varepsilon \mathrm{RT}}$

Wherein, ε is medium dielectric constant, in which ε of water is ε=8.9×10⁻¹⁰C²/Jdm.

The surface parameter operation module 27 calculates surface charge density of the substance through the following formula based on the surface potential value:

${\sigma }_0=\pm \sqrt{\frac{\varepsilon \mathrm{RT}}{\pi }\left[\begin{array}{c}\left(c_H^{\infty }+c_K^{\infty }\right)\sinh \left(\frac{F{\varphi }_0}{\mathrm{RT}}\right)+\frac{1}{2}c_{\mathrm{Ca}}^{\infty }{}^{-\frac{2F{\varphi }_0}{\mathrm{RT}}}+\\ c_{\mathrm{Ca}}^{\infty }{}^{\frac{F{\varphi }_0}{\mathrm{RT}}}-\left(c_H^{\infty }+c_K^{\infty }+\frac{3}{2}c_{\mathrm{Ca}}^{\infty }\right)\end{array}\right]}$

Wherein, σ₀ is surface charge density, the symbol of which is same as that of surface potential and the unit of which is C/dm².

The surface parameter operation module 27 calculates surface electric field strength of the substance through the following formula based on the surface charge density:

$E_0=\frac{4\pi }{\varepsilon }{\sigma }_0$

Wherein, E₀ is substance surface electric field strength, the unit of which is V/dm.

The surface parameter operation module 27 calculates surface charge quantity through the following formula based on the surface charge density and specific surface area:

T _c =S×σ ₀

Wherein, T_c is surface charge quantity of a substance, the unit of which is C/g.

The above are only preferable embodiments of the present invention, and are not used to limit the present invention. Apparently, people skilled in the art can make various modifications and variations to the present invention without departing from the spirit and scope of the present invention. Therefore, the present invention intends to include all of the modifications and variations that fall into the appended claims or equivalence thereof.

Claims

1. A measurement method for substance surface property parameter, including the following steps: 1) performing saturation treatment to a surface of a substance to be measured;2) mixing the saturated substance to be measured with a solution containing indicator electrolyte; wherein the indicator electrolyte solution comprises at least one bivalent metallic positive ion of A2+ and one monovalent metallic positive ion of B+;3) upon the mixture from step 2) reaching ion-exchange equilibrium, measuring equilibrium concentration of the indicator electrolyte positive ion and hydrogen ion in a bulk solution of the mixture;4) substituting the concentration of the indicator electrolyte positive ion from step 3) into the below formula to obtain a substance surface potential φ0:

2. The measurement method for substance surface property parameter according to claim 1, wherein after step 4), further comprises the following step: 5) obtaining a specific surface area of the substance based on the surface potential from step 4).

3. The measurement method for substance surface property parameter according to claim 2, wherein: in step 5), the specific surface area of the substance is calculated by the following formula, based on the surface potential from step 4):

4. The measurement method for substance surface property parameter according to claim 1, wherein: after step 4), further comprising the following step: obtaining a surface charge density of the substance based on the surface potential from step 4).

5. The measurement method for substance surface property parameter according to claim 4, wherein: the surface charge density of the substance is calculated by the following formula based on the surface potential from step 4):

6. The measurement method for substance surface property parameter according to claim 4, wherein: upon obtaining the substance surface charge density, the method further comprising the following step: 6) obtaining a surface electric field strength based on the surface charge density from step 5).

7. The measurement method for substance surface property parameter according to claim 6, wherein: in step 6), the surface electric field strength of the substance is calculated by the following formula based on the surface charge density from step 5):

8. The measurement method for substance surface property parameter according to claim 4, wherein: upon obtaining the substance surface charge density, the method further comprising the following step: obtaining a surface charge quantity of the substance based on the surface charge density and the specific surface area.

9. The measurement method for substance surface property parameter according to claim 8, wherein: the surface charge quantity is calculated by the following formula based on the surface charge density and the specific surface area: Tc=S×σ0 wherein, Tc is surface charge quantity of the substance, a unit of which is C/g.

10. The measurement method for substance surface property parameter according to claim 1, wherein: in step 1), using an acid solution to perform saturation treatment to the surface of the substance to be measured through constant-flow method.

11. The measurement method for substance surface property parameter according to claim 10, wherein: the acid solution is HCl or HNO3 solution.

12. The measurement method for substance surface property parameter according to claim 11, wherein: step 1) includes the following steps: 11) using HCl or HNO3 solution of 0.1 mol/l to flow though the substance to be measured at uniform speed, to have surface charges of the substance to be measured to be fully saturated by Cl− or NO−3 and H+;12) using water to flow though the substance to be measured at uniform speed to wash off redundant Cl− or NO−3 and H+;13) drawing interstitial water out of the substance to be measured.

13. The measurement method for substance surface property parameter according to claim 10, wherein: a negative ion of the indicator electrolyte is same as a radical of the acid.

14. The measurement method for substance surface property parameter according to claim 13, wherein: the indicator electrolyte is “ACl2 and BCl” or “A(NO3)2 and BNO3”; wherein, A2+=Ca2 or Mg2+; B+=K+ or Na+.

15. The measurement method for substance surface property parameter according to claim 1, wherein: in step 3), the equilibrium concentration of positive ion of indicator electrolyte and hydrogen ion in the bulk solution is obtain by the following steps: 31) measuring activity values aH, aB and aA of H+, B+ and A2+ in the bulk solution;32) using the activity values from step 31) as initial concentration values, and performing iteration operation with the following steps to obtain activity coefficients and concentration of B+, A2+ and H+:321) using the activity values from step 31) as initial concentration values of individual ions, to obtain ionic strength of the system with in the following formula:

16. The measurement method for substance surface property parameter according to claim 15, wherein: in step 31), using “H+-B+-A2+” combined electrode and detector to detect activity of A2+, B+ and H+ in the bulk solution.

17. The measurement method for substance surface property parameter according to claim 15, wherein: in step 32), iterating until (i=k+1)th time, when (Ik+1−Ik)/Ik+1<0.001, terminating iteration operation, and using the final results from step 323) as the equilibrium concentration value.

18. The measurement method for substance surface property parameter according to claim 15, wherein: using final value I of ionic strength from the iteration operation to calculate an effective charge coefficient with the following formula:

19. An analysis system for substance surface property parameter based on the measurement method for substance surface property parameter according to claim 1, the analysis system including a detecting system, comprising: ion activity detecting unit, for detecting individual ion activity in a solution contained in a sample container; anddata processing unit, for receiving detected results from the ion activity detecting unit and analyzing surface parameters of the substance to be measured, comprising:ion concentration operation module, for calculating an equilibrium ion concentration based on the detected results received from the ion activity detecting unit; andsurface parameter operation module, for receiving ion concentration value calculated from the ion concentration operation module and calculating a surface potential of the substance to be measured based on the ion concentration value.

20. The analysis system for substance surface property parameter according to claim 19, wherein: the surface parameter operation module further calculates a specific surface area, surface charge density and surface electric field strength of the substance to be measured based on the surface potential of the substance to be measured, and calculates a charge quantity based on the surface charge density and specific surface area.

21. The analysis system for substance surface property parameter according to claim 19, wherein: the analysis system for substance surface property parameter further includes a sample treatment unit, comprising: sample container, for containing the substance to be measured and liquid; andliquid intake pipe and liquid offtake pipe, wherein the liquid offtake pipe is in communication with a bottom of the sample container, the liquid intake pipe is in communication with the sample container; and the liquid offtake pipe is connected to a constant-flow pump;wherein the sample container further has a stirring device disposed therein.

22. The analysis system for substance surface property parameter according to claim 19, wherein: the ion activity detecting unit includes a detecting electrode disposed in the sample container, millivoltmeters and an ion activity operator, wherein inputs of the millivoltmeters are connected to the detecting electrode, outputs of the millivoltmeters are connected to the ion activity operator; the ion activity operator receives potential data detected by the millivoltmeters to convert into ion activity data and output to the ion concentration operation module.

23. The analysis system for substance surface property parameter according to claim 22, wherein: the activity operator converts the potential data detected by the millivoltmeters into individual ion activity values by the following method: upon standardizing individual ions with standard solution of known activity, using Nernst equation in the activity operator to obtain individual ion activity values of the solution to be measured.

24. The analysis system for substance surface property parameter according to claim 23, wherein: the detecting electrode is “H+-A2+-B+” combined electrode, wherein A2+ is bivalent metallic ion, and B+ is monovalent metallic ion.

25. The analysis system for substance surface property parameter according to claim 24, wherein: the detecting electrode is “H+-K+-Ca2+” combined electrode, the ion concentration operation module is “H+, K+ and Ca2+” concentration operation module; the number of millivoltmeters is three, the inputs of the three millivoltmeters are respectively connected to outputs of H+ electrode, K+ electrode and Ca2+ electrode of the “H+-K+-Ca2+” combined electrode, the outputs of the three millivoltmeters are respectively connected to inputs of pH operator, K+ activity operator and Ca2+ activity operator; upon the pH operator, K+ activity operator and Ca2+ activity operator respectively calculating activity of H+, K+ and Ca2+, the activity of H+, K+ and Ca2+ are output to the “H+, Ca2+ and K+” concentration operation module; the detecting system further includes a temperature probe provided in the sample container; and an electronic thermometer, input of the electronic thermometer is connected to the temperature probe, and output of the electronic thermometer is respectively connected to inputs of the pH operator, K+ activity operator, Ca2+ activity operator, “H+, Ca2+ and K+” concentration operation module and surface parameter operation module.