Patent Application
20100178523
The present invention relates to high-barrier packaging materials. More particularly, the present invention relates to high-barrier packaging materials including a substrate, coating and metalized film. Even more particularly, the present invention relates to high-barrier packaging materials having a metalized cellophane or metalized polylactic acid film and a polylactic acid heat seal layer.
High-barrier packaging materials find particular application in the food industry, including for example, bags, pouches and cups for storing food products for human or animal consumption. A high-barrier packaging material is defined as providing very low transmission rates for water vapor and oxygen gas at both standard and tropical conditions. Packages having low water vapor and oxygen transmission rates are linked to extended life of food stored therein. Water vapor and oxygen transmission are accelerated at higher temperature and humidity (tropical conditions). They act as the main culprits in degradation of food stored in packages.
High-barrier packaging materials in use today include a combination of plastic polymer films and metal foils, manufactured by lamination and extrusion technologies. These types of plastic and foil based high-barrier packaging materials have high material costs, as compared to lower cost materials such a paper and paperboard. Further, these conventional high-barrier materials are not biodegradable or recyclable. Paper based packaging materials are desirable because they have comparatively low material costs, and are recyclable and biodegradable. However, paper and paperboard, being hygroscopic and porous are considered unsuitable for high-barrier applications.
There is a need for a high-barrier packaging material that has low transmission rates for water vapor and oxygen gas at both standard and tropical conditions and which is recyclable, substantially biodegradable and/or compostable.
In accordance with the invention on improved biodegradable high-barrier packaging material products and methods of manufacturing are provided. The present packaging material products comprise a substrate having a print side and a back side, a coating on the print side including nano pigments, and a metalized film layer laminated to the back side of the substrate with a bonding layer. The bonding layer may comprise an adhesive, a polylactic acid resin layer, and/or an extruded tie layer. The metalized film layer may comprise either metalized cellophane film or metalized polylactic acid film. A heat seal layer is provided either as part of the metalized film layer and/or by laminating a heat seal layer over the metalized film layer.
A method for forming a bio-degradable, high-barrier packaging material is provided. The method includes the steps of unwinding a metalized film from a first unwind station and unwinding a coated paper substrate from a second unwind station. The substrate includes a nano pigment coating on its print side. A bonding layer is then applied to the metalized film. The metalized film is then laminated to the back side of the substrate to form a laminated web. A polylactic acid heat seal material is preferably extruded and laminated to the metalized film.
Referring now to the drawings where like features are identified by the same reference numerals, a first embodiment of a bio-based, high-barrier packaging material 10 of the invention includes a paper or paperboard substrate 12, a coating 14 having a nano pigment on the print side of the substrate, and a metalized film 16 laminated on the back side of the substrate with bonding layer 18. Film 16 is preferably a metalized polylactic acid (PLA) film, and alternatively can be a metalized cellophane film.
The substrate includes paper or paperboard formed by conventional paper making technology as is well known in the art. A preferred exemplary substrate is formed from a combination of about 40 percent softwood pulp, about 56 percent hardwood pulp, and about 4 percent base ash. The substrate has less than about 0.25 nm2 permeability, and has less than about 30% total porosity as measured using modified porosimetry techniques. The substrate porosity is also controlled to provide more than about 20 secs of Gurley porosity on the paper machine.
Porosity is controlled by manipulating refining, which is done separately for both softwood and hardwood. For softwood, refining is typically achieved using a low intensity refining plate specific edge load of about 2.2 watt-second/meter. For hardwood Kraft, low intensity refining is typically achieved using a low specific edge load of about 1.54 watt-second/meter. A mixed pulp of both hardwood and softwood is further refined, if necessary, with a medium intensity of about 1.84 watt-second/meter specific edge load using about 3-5 horsepower day/ton in a double-disc refiner. The substrate can have essentially any basis weight as may be required for different packaging applications, for example, from about 20 to about 55 pounds per 3,000 square foot ream.
A preferred substrate for packaging materials of the present invention is a pouch base substrate, for example, Point Flex pouch base, available from NewPage Corp., Stevens Point, Wis. Other substrates can be used in other embodiments of the present invention as would be appreciated by those skilled in the art.
At least one side, preferably the print side, of the substrate is machine glazed. As a result, the print side has a very smooth surface with good coating lay-down.
Coating 14 is applied to the print side of the substrate. The coating 14 includes a one or more pigments at least one of which is a nano pigment, and one or more binders. At least about 25% by dry weight of the total pigment comprises one or more nano pigments. The remaining pigments may include generic clays and generic talcs. A nano pigment is defined as a pigment having no greater than about 90 nanometers in dimension. Preferably, the nano pigment has a high aspect ratio (i.e., the pigment particles are platy, being very thin with a high surface area) which is equal to or greater than about 90:1 and more preferably about 100:1. The nano pigments pack to form a dense structure with low porosity, which enhances the water and oxygen barrier properties of the sheet. Increasing the amount of high aspect ratio pigments provides a higher level of tortuosity and further improves the barrier properties of the packaging material. Preferably, the coated paper of the invention has a permeability less than about 0.15-0.2 nm2 to provide good water vapor transmission rate barrier properties.
Suitable high aspect ratio nano pigments include nano clay, such as those available from Imerys, Inc. of Roswell, Ga., and hyperplatey nano talc, such as those available from Rio Tinto Minerals of Greenwood Village, Colo. Nano pigments that do not have a high aspect ratio may also be included in certain embodiments of the present packaging materials and include nano zinc oxide from Byk Chemie of Wesel, Germany, and nano titanium oxide from Millennium Inorganic Chemicals of Ashtabula, Ohio and Baltimore, Md.
The print side coating binder preferably includes a combination of a protein and polyvinyl alcohol. A preferred protein is a soy protein having a relatively medium molecular weight, such as Pro-Cote and Pro-Cote 200 available from The Solae Company, St. Louis, Mo. A preferred polyvinyl alcohol has a molecular weight of about 26,000 to 34,000 with a degree of polymerization of about 260-340. Polyvinyl alcohols for use in the present invention include Celvol 24-203, available from Celanese of Dallas, Tex. The combination of soy protein and polyvinyl alcohol exhibits improved film formation and is substantially fully biodegradable.
Alternatively, the binder may comprise a combination of low glass transition latex and polyvinyl alcohol. Latex is not bio-based, but has desirable high barrier properties and is substantially compostable and recyclable. Nano pigmented latex coatings may further reduce water vapor transmission rates, as compared to protein-based nano pigmented coatings. Other alternative binders comprise a mixture of ethylene acrylic acid and polyvinyl alcohol, or a mixture of ethylene acrylic acid and latex.
The print side coating 14 is preferably applied at a coat weight of about 5.5 to about 8 pounds per 3,000 square foot ream by a conventional blade or rod coater. The substrate and coating combination provides improved water vapor and oxygen barrier properties because the machine glazed substrate is smooth with a minimal amount of fibers protruding from the surface and the coating 14 includes nano pigments with a film forming binder that work together to desirably seal the surface.
Metalized film 16 is preferably a metalized polylactic acid (PLA) film that is extrusion or adhesive laminated onto the back side of the substrate. A suitable metalized PLA film 16 is 1 mil thick with a 22,100 in.2/lb yield available from Celplast Metalized Products Limited, 67 Commander Blvd, Unit 4, Toronto, Canada M1S 3M7. Alternatively, a metalized cellophane film can be used. A preferred metalized cellophane film is 0.92 mils thick with a 21,000 in.2/lb yield commercially available from Innovia Films, Inc., of Atlanta, Ga. The purpose of laminating a metalized film to the substrate is to further enhance the water vapor barrier properties of the packaging material to less than about 0.3 gms/100 inch2/day at tropical conditions and still maintain the whole package as substantially biodegradable, compostable and/or renewable. The metalized cellophane film is substantially biodegradable and compostable. The metalized PLA film is biodegradable in the presence of water, and is compostable.
Metalized film 16 is laminated to the substrate 12 with a bonding layer 18. Bonding layer 18 can comprise an adhesive adapted for dry or wet lamination, an extruded PLA tie layer, or any other bio-degradable and/or compostable bonding layers suitable for bonding metalized film 16 to substrate 12. The bonding layer may incorporate optional high barrier additives. Adhesive can be applied at approximately 2 lbs per ream. A suitable adhesive for dry lamination is a water based adhesive, Aqualam 444A-CR100, available from Rohm & Haas of Ringwood, Ill. or 2D5414M available from Henkel of Elgin, Ill. Exemplary laminating adhesives include R200v3 and 31401W, developed by Ecosynthetix, Inc., of Lansing, Mich. The advantage of these exemplary laminating adhesives is that they are substantially or completely biodegradable and/or compostable. The alternate PLA resin layer 18 has a thickness between about 0.5 to about 4 mils, with about 1.5 being preferable. In addition to bonding the metalized film 16 to the substrate 12, a PLA resin bonding layer enhances the barrier properties of the laminated product.
A heat seal PLA layer 20 is extrusion laminated to the outer or backside of the film 16. A preferred film thickness is 1.5 mils. The heat seal layer is adapted to be heat sealed to itself or another compatible layer of packaging material. The heat seal PLA layer 20 also functions as a protective coating for metalized PLA film 16 and provides enhanced heat seal functionality.
One or more alternate top coating 24 may be applied over coating 14 on the print side of the packaging material to improve printing characteristics or other properties of the packaging material, as will be apparent to persons skilled in the art.
Alternatively, a cellophane film with one side metalized and the other side having a heat seal coating can be used. A suitable heat seal coated, metalized film is Nature Flex, 90E-NE available from Innovia Films, Inc., of Atlanta, Ga. If such a film is used, layers 28 and 20 are unnecessary. The metalized cellophane film can be heat sealed to itself or another compatible packing material layer. However, the seal strength achieved in the
In any of the forgoing embodiments, an optional backside coating can be applied to the substrate 12 before lamination of the metalized film. A preferred backside coating is a PET emulsion. Alternatively, a nano clay coating composition with the formulation of coating layer 14 can be used.
The first and second embodiments 10, 20 of the invention are manufactured as follows. Coated substrate 12 is unwound at first unwind station 42. Bonding layer 18, in this example an adhesive for dry lamination, is applied to the back side of the substrate at adhesive applicator 44. The adhesive coating is dried at station 46. Metalized PLA film 16 is unwound from second unwind 48 and is dry laminated at adhesive laminator station 50. Alternatively and more preferably the adhesive can be applied to the metalized side of film 16 and then laminated to the substrate. Further, the adhesive coated, metalized side of the film can optionally and preferably be corona treated to increase the surface energy of the film prior to lamination. The web is then conveyed to a first extrusion laminator station 52. Station 52 comprises a first extruder 54, an optional second extruder 56, and a press nip 58 between a chill roll 60 and nip roll 62. PLA heat seal layer 20 is extruded from extruder 54 and laminated at 58 on to the exterior side of metalized film 16. The product is completed at this point and is wound at winder 66. In the case of the first and second embodiments the second tandem extruder 68 is not required.
Wet lamination can alternately be used in lieu of dry lamination. If wet lamination is employed, adhesive 18 is applied to the metalized side of film 16 at adhesive applicator 49 and proceeds to laminating station 50 were the film is laminated to the substrate 12. Next, the laminated web is dried at optional drier station 51 prior to proceeding to extrusion laminator 52. In the wet lamination process, applicator 44 and drier 46 are not required.
The third product embodiment 26 of the invention is manufactured as follows. Coated substrate 12 is unwound at first unwind station 42. Bonding layer 18, such as an adhesive, is applied to the back side of the substrate at adhesive applicator 44. As with the first two embodiments, metalized cellophane film 17 is unwound from second unwind 48 and is laminated to the substrate at adhesive laminator station 50. The web is then conveyed to an extrusion laminator station 52. A tie layer 28 is extruded from the first extruder 54 and a PLA heat seal layer 20 is extruded from second extruder 56 and is laminated at 58 over the exterior sided of metalized film 17. The product is completed at this point and is wound at winder 66.
The fourth product embodiment 30 of the invention does not utilize adhesive lamination and accordingly the adhesive laminating section, 44, 46, 49, 50, 51 are not required. Coated substrate 12 is unwound at first unwind station 42. The substrate proceeds to extrusion laminator station 52. Metalized PLA film 16 is unwound from third unwind 70. Tie layer 34 is extruded from first extruder 54, and metalized film 16, tie layer 34 and substrate 12 are laminated at 58. The laminated web then proceeds to second extrusion laminator 68. Laminator 68 includes one or more extruders 72, 74 and a laminating nip 76 as previously described with respect to extrusion laminator 52. PLA heat seal layer 20 is extruded from one of extruders 72, 74 and is laminated to exterior side of the metalized film 16. The laminated product is then wound at winder 66.
The fifth product embodiment 36 of the invention, as with the fourth embodiment, does not utilize adhesive lamination. Coated substrate 12 is unwound at first unwind station 42. The substrate proceeds to first extrusion laminator station 52. Metalized cellophane film 17 is unwound from third unwind station 70. A tie layer 34 is extruded from the first extruder 54 and the metalized film 17, tie layer 34 and substrate 12 are laminated at 58. The laminated web then proceeds to second extrusion laminator 68. Tie layer 28 is extruded from third extruder 72 and PLA heat seal layer 20 is extruded from the fourth extruder 74 and is laminated at 76 to exterior side of metalized film 17. The laminated product is then wound at winder 66.
Data showing paper porosity and permeability modifications through nano pigment and formulated coatings on the preferred substrate 12 with nano pigment coating 14, but without any back side coatings or laminated film is shown in Table 1. The control sample is a commercially available paper substrate, Glazewrap paper available from NewPage Corp., of Stevens Point, Wis.
The permeability of each of the samples, accounting for the effects of tortuosity is shown below in Graph 1. Permeability refers to calculations based on mercury poresymetry techniques conducted under vacuum on the paper substrates created in our examples.
The mean pore diameter of the samples is shown below in Graph 2. As shown in Graph 2, a control sample of the substrate, Glazewrap paper, was also compared.
It is also apparent that there is a relationship between the mean pore diameter and the pore volume, with respect to using a clay based sample versus a carbonate based sample. By varying the choice of pigments, the pore size distribution and void volume of the coatings can be altered. Thus, the coating type has an effect on the coating void volume and the coating pore size distribution to improve the water vapor transmission rate, as set forth below in Graph 3.
Examples of various constructions for the present packaging materials are listed in Table 2:
A bio-based, high-barrier packaging material was formed in accordance with the second embodiment of the invention, described above. The substrate 12 was Glazewrap paper, available from NewPage Corp. of Stevens Point, Wis., which had a basis weight of about thirty pounds per ream. A coating 14 for the print side included a styrene butadiene latex (Latex No. 8879 from Dow Chemicals, Inc. of Midland, Mich.), a polyvinyl alcohol (Celvol 24-203, available from Celanese of Dallas, Tex.) and a pigment comprising substantially 100% hyperplaty nano talc (available from Rio Tinto Minerals of Centennial, Colo.). The coating 14 was applied at a coat weight of about seven pounds per ream. In addition, a top coat 24 of a recyclable, waterborne PET emulsion was applied onto the coating 14 at a coat weight of about three pounds per ream. The PET emulsion based top coat 22 was PBH 55, available from Eka Chemicals, Inc. of Marietta, Ga.
The packaging material further included a metalized PLA film 16 laminated with high-barrier adhesive 18 to the back side of substrate 12. A water-based adhesive available from Rohm & Haas, Aqualam 444A-CR100, was used as the laminating adhesive and laminated at two pounds per ream. The metalized PLA film 16 was about a 1 millimeter film with about a 22,100 inches2/lb yield. About a 1.5 millimeter thick PLA heat seal layer 20 was extrusion laminated on the back side of the metalized PLA film 64.
A bio-degradable, high-barrier packaging material was formed of substantially the same structure as the material of Example 1, however a metalized cellophane film replaced the metalized PLA film. The metalized cellophane film had about a 0.92 millimeter thickness with about a 21,000 inches2/lb yield. About a 1.5 millimeter thick PLA heat seal layer was extrusion laminated on the back side onto the metalized cellophane film.
An alternative bio-degradable, high-barrier packaging material was formed in accordance with the second embodiment of the invention, described above. The substrate 12 was Glazewrap paper, available from NewPage Corp. of Stevens Point, Wis., which had a basis weight of about thirty pounds per ream. A coating 14 for the print side included a latex, a polyvinyl alcohol and a pigment comprising 100% hyperplatey nano talc. Coating 14 was applied at a coat weight of about seven pounds per ream. The latex, polyvinyl alcohol and hyperplatey nano talc were those used as above in Example 1. A top coat 24 was also applied at a coat weight of about three pounds per ream on the print side, comprising a soy polymer protein, a polyvinyl alcohol and a hyperplatey nano talc. The soy polymer protein was Pro Cote 200 available from The Solae Company, St. Louis, Mo., the polyvinyl alcohol used was Celvol 24-203, available from Celanese of Dallas, Tex., and the hyperplatey nano talc used was available from Rio Tinto Minerals of Centennial, Colo.
The packaging material further included a metalized PLA film 16 laminated with high-barrier adhesive 18 to the back side of substrate 12. The water based adhesive from Example 1 was used as the laminating adhesive 18 and laminated at two pounds per ream. The metalized PLA film 16 was about a 1 millimeter film with about a 22,100 inches2/lb yield. About a 1.5 millimeter thick PLA heat seal layer 20 was extrusion laminated to the back side of the metalized PLA film 16.
A bio-degradable, high-barrier packaging material was formed of substantially the same construction as Example 3, however a metalized cellophane film replaced the metalized PLA film. The metalized cellophane film was about 0.92 millimeter thick with about a 21,000 inches2/lb yield. A 1.5 millimeter thick PLA heat seal layer 20 was extrusion laminated onto the back side of the metalized cellophane film.
A bio-degradable, high-barrier packaging material was formed in accordance with the second embodiment of the invention, described above. The substrate 12 was Glazewrap paper, available from NewPage Corp. of Stevens Point, Wis., which had a basis weight of about thirty pounds per ream. A coating 14 for the print side included a soy polymer protein, a polyvinyl alcohol and a pigment comprising substantially 100% hyperplaty nano talc and was applied at a coat weight of about seven pounds per ream. The soy polymer protein used was Pro Cote 200, available from The Solae Company, St. Louis, Mo. The polyvinyl alcohol and hyperplatey nano talc were those used above in Example 1. In addition, a top coat 24 on the print side included a soy polymer protein, a polyvinyl alcohol and a hyperplatey nano talc and was applied at a coat weight of about three pounds per ream. The soy polymer protein was Pro Cote 200 available from The Solae Company, St. Louis, Mo. The polyvinyl alcohol and the hyperplatey nano talc were the same as those as used in Example 1.
The packaging material further included a metalized PLA film 16 laminated with high-barrier adhesive 18 to the back side of substrate 12. The water based adhesive from Example 1 was used as the laminating adhesive 18 and applied at two pounds per ream. The metalized PLA film 16 was about a 1 millimeter film with about a 22,100 inches2/lb yield. About a 1.5 millimeter thick PLA heat seal layer 20 was extrusion laminated on the back side onto the metalized PLA film 16.
Yet another bio-degradable, high-barrier packaging material was formed having substantially the same structure as Example 5, however a metalized cellophane film replaced the metalized PLA film. In addition, the protein based coating 14 replaced with a latex based coating. Coating 14 included a latex (Latex 8879 from Dow Chemical), a polyvinyl alcohol and a pigment comprising substantially 100% hyperplatey nano talc and was applied to the print side of substrate 12 with a coat weight of about seven pounds per ream. The metalized cellophane film was about a 0.92 millimeter film with about a 21,000 inches2/lb yield. About a 1.5 millimeter thick PLA heat seal layer was extrusion laminated onto the metalized cellophane film.
A bio-degradable, high-barrier packaging material was formed in accordance with the second embodiment of the invention, described above. The substrate 12 comprised a #35 Coated Pointflex pouch base, available from NewPage Corp. of Stevens Point, Wis. The print side of the pouch base included a nano pigment coating layer 14 and a top coat 24.
The packaging material further included a metalized PLA film 16 laminated with a high-barrier adhesive 18 to the substrate 12. The water based adhesive from Example 1 was used as the laminating adhesive 18 and applied at two pounds per ream. The metalized PLA film 16 was about a 1 millimeter film with about a 22,100 inches2/lb yield. About a 1.5 millimeter thick PLA heat seal layer 20 was extrusion laminated onto the metalized PLA film 16.
A bio-degradable, high-barrier packaging material was formed having substantially the same structure as Example 7, although a metalized cellophane film replaced the metalized PLA film. The metalized cellophane film was about a 0.92 millimeter film with about a 21,000 inches2/lb yield. About a 1.5 millimeter thick PLA heat seal layer 20 was extruded onto the metalized cellophane film.
While a particular embodiment of the present packaging materials have been described herein, it will be appreciated by those of ordinary skill in the art that changes and modifications may be made thereto without departing from the invention in its broader aspects and as set forth in the following claims.
This application claims priority from pending U.S. Provisional Patent Application Ser. No. 60/958,225 filed Jul. 3, 2007 and pending U.S. Provisional Patent Application Ser. No. 60/963,703 filed Aug. 7, 2007, the subject matter of both of which are incorporated herein by reference.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US08/66130 | 6/6/2008 | WO | 00 | 2/11/2009 |
| Number | Date | Country | |
|---|---|---|---|
| 60958225 | Jul 2007 | US | |
| 60963703 | Aug 2007 | US |