Substrates and methods for fabricating the same

Abstract

An embodiment of the invention provides a substrate. The substrate comprises a single crystal substrate. An epitaxial buffer film is on the single crystal substrate. An epitaxial ZnGa2O4 is on the epitaxial buffer film.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The invention relates to substrates and methods for fabricating the same, and more particularly to epitaxial ZnGa₂O₄ substrates and methods for fabricating the same.

2. Description of the Related Art

Flat panel display devices, such as field emission displays (FEDs), plasma display panels (PDPs), and thin-film electroluminescent devices, require highly efficient phosphor material. Oxide phosphors offer potential advantages because of their superior stability under electron bombardment and excellent luminescent property.

ZnGa₂O₄ are oxide phosphors attractive for both cathodoluminescent and electroluminescent applications. ZnGa₂O₄ possesses a cubic spinel crystal structure and wide energy band gap of about 4.4 to 5.0 e.V. This material exhibits an intense green luminescence when doped with Mn and blue luminescence without doping via a transition of a self-activated center. It has been suggested that by doping with various activators, including Mn²⁺, Eu³⁺ and Ce³⁺ ZnGa₂O₄ phosphors can attain full color luminescence. ZnGa₂O₄ is also an interesting ultraviolet-transparent conductive oxide as moderate conductivity can be induced by annealing under a reducing atmosphere at high temperature.

There have been several studies on ZnGa₂O₄. For example, Yong Eui Lee et al. disclose “Enhanced ultraviolet photoconductivity in semiconducting ZnGa₂O₄ thin films” in JOURNAL OF APPLIED PHYSICS in volume 90, number 8. Yong Eui Lee et al. disclose “Blue photoluminescence in ZnGa₂O₄ thin film phosphors” in JOURNAL OF APPLIED PHYSICS in volume 89, number 3. Yong Eui Lee et al. disclose “Enhanced photoluminescence in epitaxial ZnGa₂O₄:Mn thin film phosphors using pulsed laser deposition” in APPLIED PHYSICS LETTER in volume 74, number 21.

Although numerous studies involve epitaxial ZnGa₂O₄ film, ZnGa₂O₄ can currently only be grown epitaxially on MgO substrates at high temperature. Unfortunately, MgO substrate is not only expensive, but also easily hydrolyzed in a moist ambient. Thus, devices and methods for overcoming obstacles to epitaxial growth of ZnGa₂O₄ film are desirable.

BRIEF SUMMARY OF THE INVENTION

A detailed description is given in the following embodiments with reference to the accompanying drawings.

Substrates are provided. An embodiment of a substrate comprises a single crystal substrate. An epitaxial buffer film is on the single crystal substrate. An epitaxial ZnGa₂O₄ film is on the epitaxial buffer film.

Methods for fabricating substrates are provided. An embodiment of a method for fabricating a substrate comprises providing a single crystal substrate. A buffer film is epitaxially grown on the single crystal substrate. A ZnGa₂O₄ film is epitaxially grown on the epitaxial buffer film.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention can be more fully understood by reading the subsequent detailed description and examples with references made to the accompanying drawings, wherein:

FIG. 1 is a schematic view showing a substrate with an epitaxial ZnGa₂O₄ film thereon according to an embodiment of the invention;

FIG. 2 is a schematic view showing a substrate with an epitaxial ZnGa₂O₄ film thereon according to another embodiment of the invention;

FIG. 3 a-3b are diagrams showing X-ray diffraction θ/2θ of the as-deposited ZnGa₂O₄ film and annealed ZnGa₂O₄ film according to embodiments of the invention; and

FIG. 4 is a diagram showing Photoluminescence (PL) emission spectra of ZnGa₂O₄ films with varied crystal orientations and annealing temperatures according to an embodiment of the invention.

DETAILED DESCRIPTION OF THE INVENTION

The following description is of the best-contemplated mode of carrying out the invention. This description is made for the purpose of illustrating the general principles of the invention and should not be taken in a limiting sense. The scope of the invention is best determined by reference to the appended claims.

Embodiment 1

FIG. 1 is a schematic view showing an exemplary embodiment of an epitaxial ZnGa₂O₄ substrate 10 and methods for fabricating the same. Referring to FIG. 1, a single crystal substrate 20 is provided. The single crystal substrate 20 may comprise Si, sapphire, MgO or other single crystal material.

Next, a buffer film 40 is epitaxially grown on the single crystal substrate 20. Preferably, there is little lattice mismatching between the buffer film 40 and a sequentially formed ZnGa₂O₄ film. For example, the buffer film 40 may comprise TiN_X(x≦1), referred to as rock salt TiN. Lattice mismatching between rock salt TiN and ZnGa₂O₄ is about 1.76%. Preferably, the buffer film 40 has a thickness of about 1 nm to about 50,000 nm. In one embodiment, the epitaxial growth of the buffer film 40 on the single substrate 20 is performed by reactive direct current (D.C.) sputtering or pulsed-laser deposition (PLD). For example, epitaxial rock salt TiN may be formed on the single crystal substrate 20 by reactive DC sputtering, wherein during the reactive DC sputtering process, a Ti target may be used and the single crystal substrate 20 may be heated to a temperature of about 600° C. in an ambiance containing N₂ and Ar gas.

Thereafter, a ZnGa₂O₄ film 60 is epitaxially grown on the buffer film 40. The ZnGa₂O₄ has a spinel crystal structure. Preferably, the ZnGa₂O₄ film 60 has a thickness of about 10 nm to about 50,000 nm. The epitaxial ZnGa₂O₄ film 60 may be formed on the buffer film 40 by, for example, DC sputtering which may use ZnGa₂O₄ as a target. In one embodiment, as-deposited ZnGa₂O₄ film is amorphous, an annealing process is further performed to transform the amorphous ZnGa₂O₄ film to an epitaxial film. The ZnGa₂O₄ film may be annealed at a heating rate of 20° C./second to a temperature ranging from about 200° C. to 700° C. for a duration of about 30 minutes. The single crystal substrate 20 with the buffer film 40 and the ZnGa₂O₄ film 60 formed thereon is then furnace-cooled to room temperature which may take about 30 minutes. Alternately, the annealing process may comprise rapid thermal annealing performed at a heating rate of 50° C./second to a temperature ranging from about 400° C. for a duration of about 10 seconds to 1 minute. The single crystal substrate 20 with the buffer film 40 and the ZnGa₂O₄ film 60 formed thereon is then furnace-cooled to room temperature. The as-deposited amorphous ZnGa₂O₄ (not shown) is transformed to the epitaxial ZnGa₂O₄ film 60 by one of the above-mentioned or another annealing process. In other embodiments, during deposition of the ZnGa₂O₄ film 60 on the buffer film 40, the single crystal substrate 20 and the buffer film 40 is simultaneously heated to about 200° C. or above, preferably about 200° C. to 1000° C. Then, the epitaxial ZnGa₂O₄ film 60 grown on the buffer film 40 is obtained after the ZnGa₂O₄ deposition process.

Embodiment 2

FIG. 2 is a schematic view showing another exemplary embodiment of an epitaxial ZnGa₂O₄ substrate 20 and methods for fabricating the same. The inventor has found that the epitaxial ZnGa₂O₄ film 60 may crack due to great stress produced during the time the epitaxial ZnGa₂O₄ film 60 is coherent with the buffer film 40. Thus, the second embodiment is provided for sake of preventing cracks in the epitaxial ZnGa₂O₄ film and/or the buffer film 40. Herein, the same structures or materials have the same labels as FIG. 1.

A substrate 15 with an epitaxial ZnGa₂O₄ film 60 thereon comprises a single crystal substrate 20, a buffer film 40 epitaxially grown on the single crystal substrate 20, a stress buffer film 50 epitaxially grown on the buffer film 40, and the ZnGa₂O₄ film 60 epitaxially grown on the stress buffer film 50. Material, thicknesses and fabrication of the single crystal substrate 20 and the buffer film 40 in this embodiment are approximately the same as those in the first embodiment, thus descriptions thereof are omitted for brevity.

After the buffer film 40 is epitaxially grown on the single crystal substrate 20, the stress buffer film 50 is epitaxially grown on the buffer film 40. Because the sequentially formed epitaxial ZnGa₂O₄ film 60 and the buffer film 40 such as TiN are hard and brittle, the ZnGa₂O₄ film 60 may easily crack. A soft material may be used as the stress buffer film 50 between the epitaxial ZnGa₂O₄ film 60 and the buffer film 40 to buffer stress in the ZnGa₂O₄ film 60 and the buffer film 40. Preferably, the stress buffer material 50 may comprise Zn₂TiO₄, and the stress buffer film 50 may have thickness of about 1 nm to 50,000 nm. In one embodiment, after forming the epitaxial buffer film 40 such as TiN on the single crystal substrate 20, the single crystal substrate 20 with the epitaxial TiN film 40 formed thereon is then disposed with ZnO in a thermal furnace containing O₂ and Ar. When the single crystal substrate 20 is heated to a temperature of about 600° C., the ZnGa₂O₄ film which functions as the stress buffer film 50 will be formed on the epitaxial TiN film. In another embodiment, a stress buffer film 50 may be formed on the buffer film 40 by a deposition process, such as sputtering. After the stress buffer film 50 is epitaxially grown on the buffer film 40, the ZnGa₂O₄ film 60 is then epitaxially grown on the stress buffer film 50. The fabrication method and thickness of the epitaxial ZnGa₂O₄ film 60 in this embodiment are the same as those in the first embodiment, thus descriptions thereof are omitted for brevity.

X-ray Diffraction of an Epitaxial ZnGa₂O₄ Film

FIGS. 3 a-3b are diagrams showing X-ray diffraction θ/2θ of the as-deposited ZnGa₂O₄ film and annealed ZnGa₂O₄ film according to the aforementioned embodiments. FIGS. 3a-3b are diagrams demonstrating that the epitaxial ZnGa₂O₄ film is successfully grown on the buffer film by performing an annealing process. Herein, the dotted line shows X-ray diffraction θ/2θ of the as-deposited ZnGa₂O₄ film, while the solid line shows X-ray diffraction θ/2θ of the annealed ZnGa₂O₄ film. In FIG. 3a, the (111) epitaxial TiN film is grown on the (111) single crystal Si substrate. The ZnGa₂O₄ film deposits on the (111) TiN film on the (111) single crystal Si substrate; however the as-deposited ZnGa₂O₄ film is an amorphous film. The amorphous as-deposited ZnGa₂O₄ film is transformed to the epitaxial (111) and (222) ZnGa₂O₄ film after an annealing process. The annealing process is performed by at a heating rate of 20° C./second to a temperature of about 400° C. for a duration of about 30 minutes, and the single crystal Si substrate with the epitaxial TiN film and the ZnGa₂O₄ film formed thereon is then furnace-cooled to room temperature. In FIG. 3b, the (200) epitaxial TiN film is grown on the (100) single crystal Si substrate. The ZnGa₂O₄ film deposits on the (200) TiN film on the (100) single crystal Si substrate; however the as-deposited ZnGa₂O₄ film is an amorphous film. The amorphous as-deposited ZnGa₂O₄ film is transformed to the epitaxial (400) ZnGa₂O₄ film after an annealing process. The annealing process is performed by heating at a rate of 20° C./second to a temperature of about 400° C. for a duration of about 30 minutes, and then the single crystal Si substrate with the epitaxial TiN film and the ZnGa₂O₄ film formed thereon is then furnace-cooled to room temperature.

Photoluminescence (PL) Emission Spectra of ZnGa₂O₄ Films

FIG. 4 is a diagram showing PL emission spectra of ZnGa₂O₄ films with varied crystal orientations and annealing temperatures according to an embodiment of the invention. In FIG. 4, line A shows a PL emission spectrum of an epitaxial (100) ZnGa₂O₄ film according to an embodiment of the invention. The epitaxial (100) ZnGa₂O₄ film is grown on a TiN film which is formed on a Si substrate. The (100) ZnGa₂O₄/TiN/Si is formed by performing an annealing process at a temperature of about 400° C. Line B shows a PL emission spectrum of an epitaxial (100) ZnGa₂O₄ film according to an embodiment of the invention. The epitaxial (100) ZnGa₂O₄ film is grown on a TiN film which is formed on a Si substrate. The (100) ZnGa₂O₄/TiN/Si is formed by performing an annealing process at a temperature of about 700° C. Line C shows a PL emission spectrum of an epitaxial (111) ZnGa₂O₄ film according to an embodiment of the invention. The epitaxial (111) ZnGa₂O₄ film is grown on a TiN film which is formed on a Si substrate. The (111) ZnGa₂O₄/TiN/Si is formed by performing an annealing process at a temperature of about 400° C. Line D shows a PL emission spectrum of an epitaxial (111) ZnGa₂O₄ film according to an embodiment of the invention. The epitaxial (111) ZnGa₂O₄ film is grown on a TiN film which is formed on a Si substrate. The (111) ZnGa₂O₄/TiN/Si is formed by performing an annealing process at a temperature of about 700° C. Line E shows a PL emission spectrum of an conventional poly crystal ZnGa₂O₄ film, wherein an amorphous ZnGa₂O₄ film is formed on a glass substrate. An annealing process at a temperature of about 400° C. for 30 minutes is performed to transform the amorphous ZnGa₂O₄ film to the poly crystal ZnGa₂O₄ film. As shown in FIG. 4, the epitaxial ZnGa₂O₄ films formed by embodiments of the invention such as lines A, B, C and D have greater PL intensity than a conventional poly crystal ZnGa₂O₄ film such as line E. Furthermore, lines A, B, C and D have clearer peaks than line E, thus characteristic spectra may be separated in lines A, B, C and D.

As described, an epitaxial ZnGa₂O₄ film may be grown on any single crystal substrate through the buffer film underlying the ZnGa₂O₄ film. It is not necessary to grow an epitaxial ZnGa₂O₄ film on a MgO substrate, thereby reducing fabrication cost. An amorphous ZnGa₂O₄ film is transformed to an epitaxial ZnGa₂O₄ film by performing only an annealing process, thus the fabrication method is simplified.

While the invention has been described by way of example and in terms of the preferred embodiments, it is to be understood that the invention is not limited to the disclosed embodiments. To the contrary, it is intended to cover various modifications and similar arrangements (as would be apparent to those skilled in the art). Therefore, the scope of the appended claims should be accorded the broadest interpretation so as to encompass all such modifications and similar arrangements.

Claims

1. A substrate, comprising: a single crystal substrate;a buffer film epitaxially grown on the single crystal substrate;a ZnGa2O4 film epitaxially grown on the buffer film; anda stress buffer film epitaxially grown between the buffer film and the ZnGa2O4 film.

2. The substrate as claimed in claim 1, wherein the buffer film comprises rock salt structure TiN.

3. The substrate as claimed in claim 1, wherein the single crystal substrate comprises Si, MgO or sapphire.

4. The substrate as claimed in claim 1, wherein the stress buffer film comprises Zn2TiO4.

5. The substrate as claimed in claim 1, wherein the buffer film has a thickness of about 1 nm to about 50,000 nm.

6. The substrate as claimed in claim 1, wherein the ZnGa2O4 film has a thickness of about 10 nm to about 50,000 nm.

7. The substrate as claimed in claim 1, wherein the stress buffer film has a thickness of about 1 nm to about 50,000 nm.

8. The substrate as claimed in claim 1, wherein the ZnGa2O4 film comprises (100) or (111) oriented ZnGa2O4.

9. A method for fabricating the substrate as claimed in claim 1, comprising: providing a single crystal substrate;epitaxially growing a buffer film on the single crystal substrate;epitaxially growing a ZnGa2O4 film on the buffer film; andepitaxially growing a stress buffer film between the buffer film and the ZnGa2O4 film.

10. The method for fabricating the substrate as claimed in claim 9, wherein the buffer film comprises rock salt TiN.

11. The method for fabricating the substrate as claimed in claim 9, wherein the single crystal substrate comprises Si, MgO or sapphire.

12. The method for fabricating the substrate as claimed in claim 9, wherein the stress buffer film comprises Zn2TiO4.

13. The method for fabricating the substrate as claimed in claim 9, wherein the epitaxial growth of the ZnGa2O4 film on the buffer film comprises depositing an amorphous ZnGa2O4 film on the buffer film.

14. The method for fabricating the substrate as claimed in claim 9, wherein the epitaxial growth of the ZnGa2O4 film on the buffer film comprises performing an annealing process.

15. The method for fabricating the substrate as claimed in claim 14, wherein the annealing process is performed at a temperature ranging from 400° C. to 700° C.

16. The method for fabricating the substrate as claimed in claim 14, wherein the annealing process comprises a rapid thermal annealing process.

17. The method for fabricating the substrate as claimed in claim 13, wherein the amorphous ZnGa2O4 film is deposited on the buffer film by using DC sputtering.

18. The method for fabricating the substrate as claimed in claim 9, wherein the epitaxial growth of the buffer film on the single substrate is performed by reactive DC sputtering or pulsed-laser deposition.

19. The method for fabricating the substrate as claimed in claim 9, wherein the epitaxial growth of the stress buffer film between the buffer film the ZnGa2O4 film comprises reacting the buffer film with Zn in a furnace containing O2 and Ar gas.

20. The method for fabricating the substrate as claimed in claim 9, wherein the epitaxial growth of the ZnGa2O4 film on the buffer film comprises heating the substrate and the buffer film to a temperature of about 200° C. to 1000° C.