Patent Grant
10193185
The present invention relates to a sulfide solid electrolyte material with high Li ion conductivity.
In accordance with a rapid spread of information relevant apparatuses and communication apparatuses such as a personal computer, a video camera and a portable telephone in recent years, the development of a battery to be utilized as a power source thereof has been emphasized. The development of a high-output and high-capacity battery for an electric automobile or a hybrid automobile has been advanced also in the automobile industry. A lithium battery has been presently noticed from the viewpoint of a high energy density among various kinds of batteries.
Liquid electrolyte containing a flammable organic solvent is used for a presently commercialized lithium battery, so that the installation of a safety device for restraining temperature rise during a short circuit and the improvement in structure and material for preventing the short circuit are necessary therefor. On the contrary, a lithium battery all-solidified by replacing the liquid electrolyte with a solid electrolyte layer is conceived to intend the simplification of the safety device and be excellent in production cost and productivity for the reason that the flammable organic solvent is not used in the battery. In addition, a sulfide solid electrolyte material has been known as a solid electrolyte material used for such a solid electrolyte layer.
The sulfide solid electrolyte material is so high in Li ion conductivity as to be useful for intending higher output of a battery, and various kinds of research have been conventionally made. For example, in Non Patent Literature 1, an LiI—Li2S—P2S5-based amorphous material obtained by a mechanical milling method is disclosed. In Non Patent Literature 2, an LiI—Li2S—P2S5-based amorphous material obtained by a mechanical milling method is disclosed. In Non Patent Literature 3, it is disclosed that an LiI—Li2S—P2S5-based sulfide solid electrolyte material is used for the anode side and another solid electrolyte material is used for the cathode side.
Also, in Patent Literature 1, Li2S—P2S5-based lithium ion conductor crystal glass and a battery using this as a solid electrolyte are disclosed. In Patent Literature 2, in order to restrain a reaction of a cathode active material and a solid electrolyte, a nonaqueous electrolyte battery selecting a combination of the solid electrolytes for a specific combination is disclosed.
A sulfide solid electrolyte material with high Li ion conductivity has been conventionally demanded. The present invention has been made in view of the above-mentioned actual circumstances, and the main object thereof is to provide a sulfide solid electrolyte material with high Li ion conductivity.
In a present invention, to solve the above-mentioned problem, there is provided a sulfide solid electrolyte material comprising an ion conductor with an ortho-composition, and LiI, characterized in that the sulfide solid electrolyte material is glass with a glass transition point.
The present invention allows a sulfide solid electrolyte material with high Li ion conductivity by reason of comprising LiI (LiI component) to become rich in Li. In addition, this sulfide solid electrolyte material is so high in amorphous nature as has a glass transition point as to allow Li ion conductivity to be improved.
In the above-mentioned invention, a content of the LiI is preferably within a range of 10 mol % to 30 mol %.
In the above-mentioned invention, the ion conductor preferably contains Li, X (X is P, Si, Ge, Al or B), and S. The reason therefor is to allow a sulfide solid electrolyte material with high Li ion conductivity.
In the above-mentioned invention, the ion conductor preferably contains Li, P, and S.
Furthermore, in the present invention, there is provided a sulfide solid electrolyte material comprising an ion conductor with an ortho-composition, and LiI, characterized in that the ion conductor contains oxygen.
The present invention allows a sulfide solid electrolyte material with high Li ion conductivity by reason of comprising LiI (LiI component) to become rich in Li. In addition, this sulfide solid electrolyte material may restrain chemical stability from deteriorating due to the influence of LiI for the reason that the above-mentioned ion conductor contains oxygen.
In the above-mentioned invention, the oxygen of the ion conductor is preferably derived from Li2O. The reason therefor is to introduce oxygen easily.
In the above-mentioned invention, the ion conductor preferably contains Li, X (X is P, Si, Ge, Al or B), S, and O. The reason therefor is to allow a sulfide solid electrolyte material with high Li ion conductivity.
In the above-mentioned invention, the ion conductor preferably contains Li, P, S, and O.
Furthermore, in the present invention, there is provided a lithium solid state battery comprising a cathode active material layer containing a cathode active material, an anode active material layer containing an anode active material, and a solid electrolyte layer formed between the cathode active material layer and the anode active material layer, characterized in that the cathode active material layer contains the cathode active material with an electric potential of 2.8 V (vs Li) or more, and a sulfide solid electrolyte material comprising an ion conductor with an ortho-composition and LiI.
The present invention allows a high-output lithium solid state battery for the reason that a cathode active material layer contains a sulfide solid electrolyte material comprising LiI (LiI component).
In the above-mentioned invention, the ion conductor preferably contains Li, X (X is P, Si, Ge, Al or B), and S. The reason therefor is to allow a sulfide solid electrolyte material with high Li ion conductivity.
In the above-mentioned invention, the ion conductor preferably contains Li, P, and S.
Furthermore, in the present invention, there is provided a lithium solid state battery comprising a cathode active material layer containing a cathode active material, an anode active material layer containing an anode active material, and a solid electrolyte layer formed between the cathode active material layer and the anode active material layer, characterized in that at least one of the cathode active material layer, the anode active material layer and the solid electrolyte layer contains the sulfide solid electrolyte material.
The present invention allows a high-output lithium solid state battery by reason of containing a sulfide solid electrolyte material comprising LiI (LiI component). In addition, the above-mentioned sulfide solid electrolyte material may restrain chemical stability from deteriorating due to the influence of LiI by reason of containing an ion conductor containing oxygen (O). As a result, the present invention allows a lithium solid state battery which restrains reaction resistance from increasing.
In the above-mentioned invention, the cathode active material layer preferably contains the cathode active material with an electric potential of 2.8 V (vs Li) or more, and the sulfide solid electrolyte material.
The present invention produces the effect such as to allow a sulfide solid electrolyte material with high Li ion conductivity.
A sulfide solid electrolyte material and a lithium solid state battery of the present invention are hereinafter described in detail.
A. Sulfide Solid Electrolyte Material
A sulfide solid electrolyte material of the present invention is first described. The sulfide solid electrolyte material of the present invention may be roughly divided into two embodiments. The sulfide solid electrolyte material of the present invention is hereinafter described while divided into a first embodiment and a second embodiment.
The sulfide solid electrolyte material of a first embodiment is a sulfide solid electrolyte material comprising an ion conductor with an ortho-composition, and LiI, characterized in that the sulfide solid electrolyte material is glass with a glass transition point.
The first embodiment allows a sulfide solid electrolyte material with high Li ion conductivity by reason of comprising LiI (LiI component) to become rich in Li. In addition, the sulfide solid electrolyte material of the first embodiment is so high in amorphous nature as has a glass transition point as to allow Li ion conductivity to be improved. Also, the first embodiment allows a sulfide solid electrolyte material which has resistance to deterioration (such as oxidative decomposition) for the reason that the above-mentioned ion conductor has an ortho-composition.
An xLiI.75Li2S.25P2S5-based amorphous material (amorphous substance) is described in FIG. 1 of the Non Patent Literature 1. This amorphous substance has an ion conductor with an ortho-composition of 75Li2S.25P2S5 and LiI. However, an amorphous substance ordinarily signifies an amorphous substance such that periodicity as a crystal is not observed in measuring X-ray diffraction or the like, and the amorphous nature exhibited by an amorphous substance ranges to a degree. Therefore, an amorphous substance with high amorphous nature and an amorphous substance with low amorphous nature exist among amorphous substances. Here, even though the synthesis of an amorphous substance by a mechanical milling method is described in Non Patent Literature 1, the details thereof are not clear and not specifically described, so that it is surmised that the mechanical milling method is a general dry-type mechanical milling.
As described in the after-mentioned Comparative Example 1-3, dry-type mechanical milling does not allow a glassy sulfide solid electrolyte material having a glass transition point. It is probably conceived with regard to dry-type mechanical milling that the reason therefor is that a raw material composition anchors on a wall surface of a vessel to be sufficiently amorphized with difficulty. On the contrary, the sulfide solid electrolyte material of the first embodiment may be obtained by performing wet-type mechanical milling as described later. In wet-type mechanical milling, a raw material composition may be prevented from anchoring on a wall surface of a vessel and may be sufficiently amorphized. Therefore, a solid electrolyte material with as high amorphous nature as has a glass transition point is allowed. Glass in a strict sense signifies glass such as to be an amorphous substance and have an observable glass transition point. Also, in Non Patent Literature 1, the word amorphous is used but the word glass is not used. In the case of comparing glass with an amorphous substance except glass, an index for determining which is higher in Li ion conductivity does not exist generally.
(1) Sulfide Solid Electrolyte Material
The sulfide solid electrolyte material of the first embodiment is greatly characterized by being glass with a glass transition point. The presence or absence of a glass transition point may be confirmed by differential thermal analysis (DTA). It may be determined by X-ray diffraction (XRD) measurement using a CuKα ray that the sulfide solid electrolyte material is an amorphous substance.
The sulfide solid electrolyte material of the first embodiment is characterized by comprising an ion conductor with an ortho-composition, and LiI. The above-mentioned sulfide solid electrolyte material is glass, so that LiI ordinarily exists in a state of being incorporated into the structure of an ion conductor with an ortho-composition. Therefore, it is preferable that the above-mentioned sulfide solid electrolyte material does not have a peak of LiI in XRD measurement using a CuKα ray. The peak of LiI ordinarily appears at 2θ=26°, 30°, 43° and 51°. The content of the above-mentioned LiI is not particularly limited if it is a ratio for allowing glass with a glass transition point; for example, preferably 34 mol % or less, more preferably 30 mol % or less. On the other hand, the content of the above-mentioned LiI is, for example, preferably 1 mol % or more, more preferably 5 mol % or more, and far more preferably 10 mol % or more. The reason therefor is that too small content of the LiI brings a possibility of not contributing to the improvement of Li ion conductivity.
The above-mentioned ion conductor has an ortho-composition. Here, ortho generally signifies oxo acid which is the highest in degree of hydration among oxo acids obtained by hydrating the same oxide. In the first embodiment, a crystal composition to which Li2S (and Li2O) is added most among sulfides is called an ortho-composition. For example, Li3PS4 corresponds to an ortho-composition in the Li2S—P2S5 system, Li3AlS3 corresponds to an ortho-composition in the Li2S—Al2S3 system, Li3BS3 corresponds to an ortho-composition in the Li2S—B2S3 system, Li4SiS4 corresponds to an ortho-composition in the Li2S—SiS2 system, and Li4GeS4 corresponds to an ortho-composition in the Li2S—GeS2 system. In the first embodiment, part of sulfur (S) in the above-mentioned ortho-composition may be substituted with oxygen (O).
Also, in the first embodiment, “having an ortho-composition” means including not merely a strict ortho-composition but also a composition in the neighborhood thereof. Specifically, “having an ortho-composition” signifies that an anion structure in an ortho-composition (PS43− structure, SiS44− structure, GeS44− structure, AlS33− structure and BS33− structure) is the main component. The ratio of an anion structure in an ortho-composition is preferably 60 mol % or more, more preferably 70 mol % or more, far more preferably 80 mol % or more, and particularly preferably 90 mol % or more with respect to all anion structures in the ion conductor. The ratio of an anion structure in an ortho-composition may be determined by Raman spectroscopy, NMR, XPS or the like.
The composition of the above-mentioned ion conductor is not particularly limited, preferably containing Li, X (X is P, Si, Ge, Al or B), and S. The reason therefor is to allow a sulfide solid electrolyte material with high Li ion conductivity. The above-mentioned X is particularly preferably P. Also, the above-mentioned X may contain the above-mentioned element by two kinds or more.
The sulfide solid electrolyte material of the first embodiment is preferably obtained by amorphizing a raw material composition containing Li2S, sulfide of X (X is P, Si, Ge, Al or B), and LiI.
Li2S contained in a raw material composition preferably has fewer impurities. The reason therefor is to allow a side reaction to be restrained. Examples of a synthesis method for Li2S include a method described in Japanese Patent Application Publication No. H07-330312. In addition, Li2S is preferably purified by using a method described in WO2005/040039. On the other hand, examples of sulfide of the above-mentioned X contained in a raw material composition include P2S3, P2S5, SiS2, GeS2, Al2S3 and B2S3.
It is preferable that the above-mentioned sulfide solid electrolyte material does not substantially contain Li2S. The reason therefor is to allow a sulfide solid electrolyte material with less hydrogen sulfide generation amount. Li2S reacts with water to generate hydrogen sulfide. For example, a larger ratio of Li2S contained in a raw material composition survives Li2S more easily. The phrase “does not substantially contain Li2S” may be confirmed by X-ray diffraction. Specifically, in the case of not having a peak of Li2S (2θ=27.0°, 31.2°, 44.8° and) 53.1°, “does not substantially contain Li2S” may be determined.
It is preferable that the above-mentioned sulfide solid electrolyte material does not substantially contain cross-linking sulfur. The reason therefor is to allow a sulfide sol id electrolyte material with less hydrogen sulfide generation amount. The term “cross-linking sulfur” signifies cross-linking sulfur in a compound obtained by a reaction of Li2S and sulfide of the above-mentioned X. For example, cross-linking sulfur with an S3P—S—PS3 structure obtained by a reaction of Li2S and P2S5 corresponds thereto. Such cross-linking sulfur reacts easily with water to easily generate hydrogen sulfide. In addition, “does not substantially contain cross-linking sulfur” may be confirmed by measuring Raman spectroscopy. For example, in the case of an Li2S—P2S5-based sulfide solid electrolyte material, a peak of an S3P—S—PS3 structure ordinarily appears at 402 cm−1. Therefore, it is preferable that this peak is not detected. A peak of a PS43− structure ordinarily appears at 417 cm−1. In the first embodiment, the intensity I402 at 402 cm−1 is preferably smaller than the intensity I417 at 417 cm−1. More specifically, the intensity I402 is, for example, preferably 70% or less, more preferably 50% or less, and far more preferably 35% or less with respect to the intensity I417. Also, with regard to a sulfide solid electrolyte material except Li2S—P2S5-based, “does not substantially contain cross-linking sulfur” may be determined by specifying a unit containing cross-linking sulfur to measure a peak of the unit.
Also, in the case of an Li2S—P2S5-based sulfide solid electrolyte material, the ratio of Li2S and P2S5 for allowing an ortho-composition is Li2S:P2S5=75:25 on a molar basis. The case of an Li2S—Al2S3-based sulfide solid electrolyte material and the case of an Li2S—B2S3-based sulfide solid electrolyte material are similar thereto. On the other hand, in the case of an Li2S—SiS2-based sulfide solid electrolyte material, the ratio of Li2S and SiS2 for allowing an ortho-composition is Li2S:SiS2=66.7:33.3 on a molar basis. The case of an Li2S—GeS2-based sulfide solid electrolyte material is similar thereto.
In the case where the above-mentioned raw material composition contains Li2S and P2S5, the ratio of Li2S to the total of Li2S and P2S5 is preferably within a range of 70 mol % to 80 mol %, more preferably within a range of 72 mol % to 78 mol %, and far more preferably within a range of 74 mol % to 76 mol %. The case where the above-mentioned raw material composition contains Li2S and Al2S3 and the case where the above-mentioned raw material composition contains Li2S and B2S3 are similar thereto. On the other hand, in the case where the above-mentioned raw material composition contains Li2S and SiS2, the ratio of Li2S to the total of Li2S and SiS2 is preferably within a range of 62.5 mol % to 70.9 mol %, more preferably within a range of 63 mol % to 70 mol %, and far more preferably within a range of 64 mol % to 68 mol %. The case where the above-mentioned raw material composition contains Li2S and GeS2 is similar thereto.
Examples of the shape of a sulfide solid electrolyte material of the first embodiment include a particulate. The average particle diameter of a particulate sulfide solid electrolyte material is, for example, preferably within a range of 0.1 μm to 50 μm. The above-mentioned sulfide solid electrolyte material is preferably high in Li ion conductivity, and Li ion conductivity at normal temperature is, for example, preferably 1×10−4 S/cm or more, and more preferably 1×10−3 S/cm or more.
A sulfide solid electrolyte material of the first embodiment may be used for optional uses in which Li ion conductivity is required. Above all, the above-mentioned sulfide solid electrolyte material is preferably used for a battery. In addition, in the case where the above-mentioned sulfide solid electrolyte material is used for a battery, it may be used for a cathode active material layer (a cathode body), an anode active material layer (an anode body) or an electrolyte layer.
(2) Producing Method for Sulfide Solid Electrolyte Material
Next, a producing method for a sulfide solid electrolyte material of the first embodiment is described. The producing method for a sulfide solid electrolyte material of the first embodiment is not particularly limited if it is a method for obtaining the above-mentioned sulfide solid electrolyte material. Examples of the producing method for the above-mentioned sulfide solid electrolyte material include a producing method having synthesis step of amorphizing a raw material composition containing Li2S, sulfide of X (X is P, Si, Ge, Al or B), and LiI by wet-type mechanical milling.
The mechanical milling is not particularly limited if it is a method for mixing a raw material composition while allowing mechanical energy thereto; examples thereof include ball mill, vibrating mill, turbo mill, mechano-fusion and disk mill, and ball mill is preferable among them and planetary ball mill is particularly preferable. The reason therefor is to efficiently obtain a desired sulfide solid electrolyte material.
Various kinds of the conditions of the mechanical milling are determined so as to obtain a desired sulfide solid electrolyte material. For example, in the case of using planetary ball mill, a raw material composition and a grinding ball are added and treated at predetermined number of revolutions and time. Generally, larger number of revolutions brings higher production rate of a sulfide solid electrolyte material, and longer treating time brings higher conversion ratio of a raw material composition into a sulfide solid electrolyte material. The number of weighing table revolutions in performing planetary ball mill is preferably within a range of 200 rpm to 500 rpm, for example, and within a range of 250 rpm to 400 rpm, above all. The treating time in performing planetary ball mill is preferably within a range of 1 hour to 100 hours, for example, and within a range of 1 hour to 50 hours, above all.
Liquid used for wet-type mechanical milling is preferably such as to have properties for not generating hydrogen sulfide in a reaction with the above-mentioned raw material composition. Hydrogen sulfide is generated in such a manner that a proton dissociated from a molecule of the liquid reacts with a raw material composition and a sulfide solid electrolyte material. Therefore, the above-mentioned liquid preferably has such aprotic properties as not to generate hydrogen sulfide. Ordinarily, aprotic liquid may be roughly divided into polar aprotic liquid and nonpolar aprotic liquid.
The polar aprotic liquid is not particularly limited; examples thereof include ketones such as acetone; nitriles such as acetonitrile; amides such as N,N-dimethylformamide (DMF); and sulfoxides such as dimethyl sulfoxide (DMSO).
Examples of the nonpolar aprotic liquid include alkane which is liquid at normal temperature (25° C.). The above-mentioned alkane may be chain alkane or cyclic alkane. The carbon number of the above-mentioned chain alkane is preferably 5 or more, for example. On the other hand, the upper limit of the carbon number of the above-mentioned chain alkane is not particularly limited if it is liquid at normal temperature. Specific examples of the above-mentioned chain alkane include pentane, hexane, heptane, octane, nonane, decane, undecane, dodecane and paraffin. The above-mentioned chain alkane may have a branch. On the other hand, specific examples of the above-mentioned cyclic alkane include cyclopentane, cyclohexane, cycloheptane, cyclooctane and cycloparaffin.
Other examples of the nonpolar aprotic liquid include aromatic hydrocarbons such as benzene, toluene and xylene; chain ethers such as diethyl ether and dimethyl ether; cyclic ethers such as tetrahydrofuran; alkyl halides such as chloroform, methyl chloride and methylene chloride; esters such as ethyl acetate; and fluorine-based compounds such as benzene fluoride, heptane fluoride, 2,3-dihydroperfluoropentane and 1,1,2,2,3,3,4-heptafluorocyclopentane. The added amount of the above-mentioned liquid is not particularly limited and may be such amount as to obtain a desired sulfide solid electrolyte material.
Next, a second embodiment of a sulfide solid electrolyte material of the present invention is described. The sulfide solid electrolyte material of the second embodiment is a sulfide solid electrolyte material comprising an ion conductor with an ortho-composition, and LiI, characterized in that the above-mentioned ion conductor contains oxygen (O).
The second embodiment allows a sulfide solid electrolyte material with high Li ion conductivity by reason of comprising LiI (LiI component) to become rich in Li. In addition, the sulfide solid electrolyte material of the second embodiment may restrain chemical stability from deteriorating due to the influence of LiI for the reason that the above-mentioned ion conductor contains oxygen (O). Also, the second embodiment allows a sulfide solid electrolyte material which has resistance to deterioration (such as oxidative decomposition) for the reason that the above-mentioned ion conductor has an ortho-composition. The sulfide solid electrolyte material of the second embodiment differs from the above-mentioned sulfide solid electrolyte material of the first embodiment, and may be glass, an amorphous substance except glass, a crystalline substance or a substance which is completely crystalline.
(1) Sulfide Solid Electrolyte Material
The sulfide solid electrolyte material of the second embodiment is greatly characterized in that the ion conductor with an ortho-composition contains oxygen (O). Ordinarily, O contained in the above-mentioned ion conductor exists in a position of S in an anion structure (such as PS43− structure) of an ortho-composition consisting essentially of S. Specific examples thereof include PS3O3−, PS2O23− and PSO33−. It may be confirmed by NMR, Raman spectroscopy, XPS or the like that the above-mentioned ion conductor contains O. In particular, in the case where the ion conductor contains P, it is preferable to measure by 31P MAS NMR. Oxygen in the above-mentioned ion conductor is preferably derived from an oxygen-containing compound and more preferably derived from Li2O. The reason therefor is to allow a sulfide solid electrolyte material with high chemical stability.
The sulfide solid electrolyte material of the second embodiment is characterized by comprising an ion conductor with an ortho-composition, and LiI. In the second embodiment, at least part of LiI preferably exists in a state of being incorporated into the structure of an ion conductor with an ortho-composition. The content of the above-mentioned LiI is not particularly limited; for example, preferably within a range of 1 mol % to 60 mol %, more preferably within a range of 5 mol % to 50 mol %, and far more preferably within a range of 10 mol % to 40 mol %.
The above-mentioned ion conductor has an ortho-composition. As described above, Li3PS4 corresponds to an ortho-composition in the Li2S—P2S5 system, Li3AlS3 corresponds to an ortho-composition in the Li2S—Al2S3 system, Li3BS3 corresponds to an ortho-composition in the Li2S—B2S3 system, Li4SiS4 corresponds to an ortho-composition in the Li2S—SiS2 system, and Li4GeS4 corresponds to an ortho-composition in the Li2S—GeS2 system. In the second embodiment, part of sulfur (S) in the above-mentioned ortho-composition is substituted with oxygen (O).
The composition of the above-mentioned ion conductor is not particularly limited, preferably containing Li, X (X is P, Si, Ge, Al or B), S and O. The reason therefor is to allow a sulfide solid electrolyte material with high Li ion conductivity. The above-mentioned X is particularly preferably P.
The sulfide solid electrolyte material of the second embodiment is preferably obtained by using a raw material composition containing Li2S, Li2O, sulfide of X (X is P, Si, Ge, Al or B), and LiI. Li2S and sulfide of X contained in a raw material composition are as described above.
Also, in the case of an Li2S—Li2O—P2S5-based sulfide solid electrolyte material, the ratio of Li2S, Li2O and P2S5 for allowing an ortho-composition is (Li2S+Li2O):P2S5=75:25 on a molar basis. The case of an Li2S—Li2O—Al2S3-based sulfide solid electrolyte material and the case of an Li2S—Li2O—B2S3-based sulfide solid electrolyte material are similar thereto. On the other hand, in the case of an Li2S—Li2O—SiS2-based sulfide solid electrolyte material, the ratio of Li2S, Li2O and SiS2 for allowing an ortho-composition is (Li2S+Li2O):SiS2=66.7:33.3 on a molar basis. The case of an Li2S—Li2O—GeS2-based sulfide solid electrolyte material is similar thereto.
In the case where the above-mentioned raw material composition contains Li2S, Li2O and P2S5, the ratio of Li2S and Li2O to the total of Li2S, Li2O and P2S5 is preferably within a range of 70 mol % to 80 mol %, more preferably within a range of 72 mol % to 78 mol %, and far more preferably within a range of 74 mol % to 76 mol %. The case where the above-mentioned raw material composition contains Li2S, Li2O and Al2S3 and the case where the above-mentioned raw material composition contains Li2S, Li2O and B2S3 are similar thereto. On the other hand, in the case where the above-mentioned raw material composition contains Li2S, Li2O and SiS2, the ratio of Li2S and Li2O to the total of Li2S, Li2O and SiS2 is preferably within a range of 62.5 mol % to 70.9 mol %, more preferably within a range of 63 mol % to 70 mol %, and far more preferably within a range of 64 mol % to 68 mol %. The case where the above-mentioned raw material composition contains Li2S, Li2O and GeS2 is similar thereto.
The ratio of Li2O to the total of Li2S and Li2O is, for example, preferably within a range of 1 mol % to 40 mol %, more preferably within a range of 4 mol % to 27 mol %. The reason therefor is that too small ratio of the Li2O brings a possibility of not contributing to the improvement of chemical stability of a sulfide solid electrolyte material, and too high ratio of the Li2O brings a possibility of greatly deteriorating Li ion conductivity.
The content of Li2O in a sulfide solid electrolyte material of the second embodiment is, for example, preferably within a range of 1 mol % to 30 mol %, and more preferably within a range of 3 mol % to 20 mol %.
Other items with regard to a sulfide solid electrolyte material of the second embodiment are the same as the items described in the above-mentioned “1. First embodiment”; therefore, the description will not be repeated here.
(2) Producing Method for Sulfide Solid Electrolyte Material
Next, a producing method for a sulfide solid electrolyte material of the second embodiment is described. The producing method for a sulfide solid electrolyte material of the second embodiment is not particularly limited if it is a method for obtaining the above-mentioned sulfide solid electrolyte material. Examples of the producing method for the above-mentioned sulfide solid electrolyte material include a producing method having synthesis step of amorphizing a raw material composition containing Li2S, Li2O, sulfide of X (X is P, Si, Ge, Al or B), and LiI.
Examples of a method for amorphizing include mechanical milling and melt extraction, and mechanical milling is preferable among them. The reason therefor is that treatment at normal temperature can be performed to intend the simplification of production processes. The mechanical milling may be a dry-type mechanical milling or a wet-type mechanical milling, but yet the latter is preferable. The reason therefor is that a raw material composition may be prevented from anchoring on a wall surface of a vessel to obtain a sulfide solid electrolyte material with higher amorphous nature.
Heat-treating step of heat-treating the sulfide solid electrolyte material obtained in the synthesis step may be performed in the above-mentioned producing method. The reason therefor is to obtain a crystalline sulfide solid electrolyte material. The heating temperature is preferably a temperature equal to or higher than crystallizing temperature.
On the other hand, other examples of the above-mentioned producing method for a sulfide solid electrolyte material include a producing method comprising a first amorphizing step of amorphizing a raw material composition containing Li2S, sulfide of X (X is P, Si, Ge, Al or B) and LiI, and a second amorphizing step of amorphizing the material obtained by the above-mentioned first amorphizing step while adding Li2O thereto. The addition of Li2O in the second amorphizing step allows chemical stability of the sulfide solid electrolyte material to be efficiently improved. In the above-mentioned producing method, LiI is added in the first amorphizing step and LiI may be added in the second amorphizing step. In addition, the heat-treating step of heat-treating the sulfide solid electrolyte material obtained in the second amorphizing step may be performed in the above-mentioned producing method.
B. Lithium Solid State Battery
Next, a lithium solid state battery of the present invention is described. The lithium solid state battery of the present invention may be roughly divided into two embodiments. The lithium solid state battery of the present invention is hereinafter described while divided into a first embodiment and a second embodiment.
The lithium solid state battery of the first embodiment is a lithium solid state battery comprising a cathode active material layer containing a cathode active material, an anode active material layer containing an anode active material, and a solid electrolyte layer formed between the cathode active material layer and the anode active material layer, characterized in that the cathode active material layer contains the cathode active material with an electric potential of 2.8 V (vs Li) or more and a sulfide solid electrolyte material comprising anion conductor with an ortho-composition and LiI.
The first embodiment allows a high-output lithium solid state battery for the reason that the cathode active material layer contains a sulfide solid electrolyte material comprising LiI (LiI component). Conventionally, LiI is conceived to decompose in the vicinity of 2.8 V, so that a sulfide solid electrolyte material comprising LiI has not been used for the cathode active material layer. For example, in page 270 of Non Patent Literature 3, it is described that LiI—Li2S—P2S5 may not be combined with a cathode active material such as LiCoO2. Also, in paragraphs [0028] and [0029] of Patent Literature 2, it is described that electric potential at which an oxidation reaction of LiI is caused is so low as to be incapable of being combined with a cathode active material. In addition, according to the Nernst equation, LiI is subject to an oxidation reaction at 2.8 V.
E=ΔUelec/γF=270.29×103/1×96450=2.8 V (vs Li)
However, as described in (Verification of oxidative decomposition) of [Evaluation 1] of the after-mentioned examples, it was confirmed that LiI did not decompose unexpectedly even though a sulfide solid electrolyte material comprising LiI was contained in the cathode active material layer. The reason therefor is still unclear and it is conceived that LiI is stabilized by an interaction with the above-mentioned ion conductor.
The lithium solid state battery of the first embodiment is hereinafter described in each constitution.
(1) Cathode Active Material Layer
The cathode active material layer in the first embodiment contains a cathode active material with an electric potential of 2.8 V (vs Li) or more and a sulfide solid electrolyte material comprising an ion conductor with an ortho-composition and LiI.
(i) Sulfide Solid Electrolyte Material
A sulfide solid electrolyte material in the first embodiment may be not merely the sulfide solid electrolyte material (glass with a glass transition point) described in the above-mentioned “A. Sulfide solid electrolyte material 1. First embodiment”, but also an amorphous substance except glass, a crystalline substance or a substance which is completely crystalline. In the first embodiment, at least part of LiI preferably exists in a state of being incorporated into the structure of an ion conductor with an ortho-composition. The content of the above-mentioned LiI is not particularly limited; for example, preferably within a range of 1 mol % to 60 mol %, more preferably within a range of 5 mol % to 50 mol %, and far more preferably within a range of 10 mol % to 40 mol %. The ion conductor with an ortho-composition is the same as the contents described in the above-mentioned “A. Sulfide solid electrolyte material 1. First embodiment”; therefore, the description will not be repeated here.
The content of the above-mentioned sulfide solid electrolyte material in the cathode active material layer is preferably, for example, within a range of 0.1% by volume to 80% by volume, above all, within a range of 1% by volume to 60% by volume, and particularly, within a range of 10% by volume to 50% by volume.
(ii) Cathode Active Material
A cathode active material in the first embodiment is not particularly limited if it has an electric potential of 2.8 V (vs Li) or more; examples thereof include rock salt bed type active material such as LiCoO2, LiMnO2, LiNiO2, LiVO2 and LiNi1/3Co1/3Mn1/3O2, spinel type active material such as LiMn2O4 and Li(Ni0.5Mn1.5)O4, and olivine type active material such as LiFePO4, LiMnPO4, LiNiPO4 and LiCuPO4. Also, Si-containing oxides such as Li2FeSiO4 and Li2MnSiO4 may be used as a cathode active material. In addition, the electric potential of a cathode active material is preferably higher, for example, 3.0 V (vs Li) or more.
Examples of the shape of a cathode active material include a particulate shape, preferably a spherical shape or an elliptically spherical shape, above all. In the case where a cathode active material is in a particulate shape, the average particle diameter thereof is, for example, preferably within a range of 0.1 μm to 50 μm. The content of a cathode active material in the cathode active material layer is, for example, preferably within a range of 10% by volume to 99% by volume, and more preferably within a range of 20% by volume to 99% by volume.
(iii) Cathode Active Material Layer
A cathode active material layer in the first embodiment may further contain at least one of a conductive material and a binder in addition to a cathode active material and a sulfide solid electrolyte material. Examples of the conductive material include acetylene black, Ketjen Black and carbon fiber. Examples of the binder include fluorine-containing binders such as PTFE and PVDF. The thickness of the above-mentioned cathode active material layer is, for example, preferably within a range of 0.1 μm to 1000 μm.
(2) Anode Active Material Layer
Next, an anode active material layer in the first embodiment is described. The anode active material layer in the first embodiment is a layer containing at least an anode active material, and may further contain at least one of a solid electrolyte material, a conductive material and a binder as required.
In the first embodiment, a solid electrolyte material contained in the anode active material layer is preferably the sulfide solid electrolyte material described in the above-mentioned “(1) Cathode active material layer (i) Sulfide solid electrolyte material”. The reason therefor is to allow a high-output battery. The content of the above-mentioned sulfide solid electrolyte material in the anode active material layer is preferably, for example, within a range of 0.1% by volume to 80% by volume, above all, within a range of 1% by volume to 60% by volume, and particularly, within a range of 10% by volume to 50% by volume.
Examples of the anode active material include a metal active material and a carbon active material. Examples of the metal active material include In, Al, Si, and Sn. On the other hand, examples of the carbon active material include mesocarbon microbeads (MCMB), high orientation property graphite (HOPG), hard carbon and soft carbon. The content of the anode active material in the anode active material layer is, for example, preferably within a range of 10% by volume to 99% by volume, and more preferably within a range of 20% by volume to 99% by volume. A conductive material and a binder are the same as are used for the above-mentioned cathode active material layer. The thickness of the anode active material layer is preferably within a range of 0.1 μm to 1000 μm, for example.
(3) Solid Electrolyte Layer
Next, a solid electrolyte layer in the first embodiment is described. The solid electrolyte layer in the first embodiment is a layer formed between the cathode active material layer and the anode active material layer, and a layer composed of a solid electrolyte material. The solid electrolyte material contained in the solid electrolyte layer is not particularly limited if it has Li ion conductivity.
In the first embodiment, a solid electrolyte material contained in the solid electrolyte layer is preferably the sulfide solid electrolyte material described in the above-mentioned “(1) Cathode active material layer (i) Sulfide solid electrolyte material”. The reason therefor is to allow a high-output battery. The content of the above-mentioned sulfide solid electrolyte material in the solid electrolyte layer is not particularly limited if it is a ratio for obtaining desired insulation properties, and is preferably, for example, within a range of 10% by volume to 100% by volume, above all, within a range of 50% by volume to 100% by volume. In particular, in the first embodiment, the solid electrolyte layer is preferably composed of only the above-mentioned sulfide solid electrolyte material.
The solid electrolyte layer may contain a binder. The reason therefor is that the solid electrolyte layer with flexibility may be obtained by containing a binder. Examples of the binder include fluorine-containing binders such as PTFE and PVDF. The thickness of the solid electrolyte layer is preferably within a range of 0.1 μm to 1000 μm, for example, and within a range of 0.1 μm to 300 μm, above all.
(4) Other Constitutions
A lithium solid state battery of the first embodiment comprises at least the above-mentioned cathode active material layer, anode active material layer and solid electrolyte layer, ordinarily further comprising a cathode current collector for collecting the cathode active material layer and an anode current collector for collecting the anode active material layer. Examples of a material for the cathode current collector include SUS, aluminum, nickel, iron, titanium and carbon, and preferably SUS among them. On the other hand, examples of a material for the anode current collector include SUS, copper, nickel and carbon, and preferably SUS among them. The thickness and shape of the cathode current collector and the anode current collector are preferably selected properly in accordance with uses of a lithium solid state battery. A battery case of a general lithium solid state battery may be used for a battery case used for the first embodiment. Examples of the battery case include a battery case made of SUS.
(5) Lithium Solid State Battery
A lithium solid state battery of the first embodiment may be a primary battery or a secondary battery, and preferably a secondary battery among them. The reason therefor is to be repeatedly charged and discharged and be useful as a car-mounted battery, for example. Examples of the shape of a lithium solid state battery of the first embodiment include a coin shape, a laminate shape, a cylindrical shape and a rectangular shape.
A producing method for a lithium solid state battery of the first embodiment is not particularly limited if it is a method for obtaining the above-mentioned lithium solid state battery, and the same method as a producing method for a general lithium solid state battery may be used. Examples of a producing method for a lithium solid state battery include a method such that a material composing a cathode active material layer, a material composing a solid electrolyte layer and a material composing an anode active material layer are sequentially pressed to thereby produce a power generating element and this power generating element is stored inside a battery case, which is swaged.
Next, a second embodiment of a lithium solid state battery of the present invention is described. The lithium solid state battery of the second embodiment is a lithium solid state battery comprising a cathode active material layer containing a cathode active material, an anode active material layer containing an anode active material, and a solid electrolyte layer formed between the cathode active material layer and the anode active material layer, characterized in that at least one of the cathode active material layer, the anode active material layer and the solid electrolyte layer contains the above-mentioned sulfide solid electrolyte material.
The second embodiment allows a high-output lithium solid state battery by reason of containing a sulfide solid electrolyte material comprising LiI (LiI component). In addition, the sulfide solid electrolyte material may restrain chemical stability from deteriorating due to the influence of LiI by reason of containing an ion conductor containing oxygen (O). As a result, the second embodiment allows a lithium solid state battery which restrains reaction resistance from increasing.
The lithium solid state battery of the second embodiment, similarly to the above-mentioned
In the second embodiment, at least the cathode active material layer 1 preferably contains the above-mentioned sulfide solid electrolyte material. As described above, the reason therefor is that conventionally a sulfide solid electrolyte material comprising LiI has not been used for the cathode active material layer. In addition, in the second embodiment, the electric potential of a cathode active material is not particularly limited and is preferably 2.8 V (vs Li) or more, for example. Other items with regard to a lithium solid state battery of the second embodiment are the same as the items described in the above-mentioned “B. Lithium solid state battery 1. First embodiment”; therefore, the description will not be repeated here.
The present invention is not limited to the above-mentioned embodiments. The above-mentioned embodiments are exemplification, and any is included in the technical scope of the present invention if it has substantially the same constitution as the technical idea described in the claim of the present invention and offers similar operation and effect thereto.
The present invention is described more specifically while showing examples hereinafter.
Lithium sulfide (Li2S), diphosphorus pentasulfide (P2S5) and lithium iodide (LiI) were used as a starting material. Next, Li2S and P2S5 were weighed in a glove box under an Ar atmosphere (a dew point of −70° C.) so as to become a molar ratio of 75Li2S.25P2S5 (Li3PS4, ortho-composition). Next, LiI was weighed so as to become 10 mol %. Projected into a vessel of planetary ball mill (45 cc, made of ZrO2) was 2 g of this mixture, dehydrated heptane (a moisture amount of 30 ppm or less, 4 g) was projected thereinto, and ZrO2 ball (ϕ=5 mm, 53 g) was projected thereinto to completely seal the vessel (an Ar atmosphere). This vessel was mounted on a planetary ball milling machine (P7™ manufactured by Fritsch Japan Co., Ltd.) to perform mechanical milling of 1-hour treatment and 15-minute intermission 40 times at the number of weighing table revolutions of 500 rpm. Thereafter, the obtained sample was dried on a hotplate so as to remove heptane to obtain a sulfide solid electrolyte material. The composition of the obtained sulfide solid electrolyte material was 10LiI.90 (0.75Li2S.0.25P2S5).
A sulfide solid electrolyte material was obtained in the same manner as Example 1-1 except for modifying the ratio of LiI into 30 mol %. The composition of the obtained sulfide solid electrolyte material was 30LiI.70 (0.75Li2S.0.25P2S5).
A sulfide solid electrolyte material was each obtained in the same manner as Example 1-1 except for modifying the ratio of LiI into 35 mol % and 40 mol %. The composition of the obtained sulfide solid electrolyte material was each 35LiI.65 (0.75Li2S.0.25P2S5) and 40LiI.60 (0.75Li2S.0.25P2S5).
An Li2S—P2S5—LiI-based amorphous material described in Non Patent Literature 1 was reproduced as strictly as possible. In Non Patent Literature 1, wet-type mechanical milling was not described at all and an ordinary dry-type mechanical milling was adopted. First, lithium sulfide (Li2S), diphosphorus pentasulfide (P2S5) and lithium iodide (LiI) were used as a starting material. Next, Li2S and P2S5 were weighed in a glove box under an Ar atmosphere (a dew point of −70° C.) so as to become a molar ratio of 75Li2S.25P2S5 (Li3PS4, ortho-composition). Next, LiI was weighed so as to become 30 mol %. Projected into a vessel of planetary ball mill (45 cc, made of ZrO2) was 1 g of this mixture, and ZrO2 ball (ϕ=10 mm, 10 pieces) was projected thereinto to completely seal the vessel (an Ar atmosphere). This vessel was mounted on a planetary ball milling machine (P7™ manufactured by Fritsch Japan Co., Ltd.) to perform mechanical milling of 1-hour treatment and 15-minute intermission 40 times at the number of weighing table revolutions of 370 rpm. Thus, a sulfide solid electrolyte material was obtained. The composition of the obtained sulfide solid electrolyte material was 30LiI.70 (0.75Li2S.0.25P2S5).
[Evaluation 1]
(X-Ray Diffraction Measurement)
X-ray diffraction (XRD) measurement using a CuKα ray was performed for the sulfide solid electrolyte material obtained in Example 1-1, 1-2 and Comparative Example 1-1 to 1-3. RINT UltimaIII™ manufactured by Rigaku Corporation was used for XRD measurement. The results are shown in
(Differential Thermal Analysis)
Differential thermal analysis (DTA) was performed for the sulfide solid electrolyte material obtained in Example 1-2 and Comparative Example 1-3. TGA/SDTA851e™ manufactured by Mettler-Toledo International Inc. was used for DTA. The results are shown in
(Li Ion Conductivity Measurement)
Li ion conductivity (room temperature) measurement by an alternating current impedance method was performed for the sulfide solid electrolyte material obtained in Example 1-1, 1-2. Li ion conductivity measurement was as follows. A sample of 100 mg added to a support tube (made of Macor) was held by electrodes made of SKD. Thereafter, the sample was pressed into powder at a pressure of 4.3 ton/cm2 to perform impedance measurement while constraining the sample at 6 Ncm. Solartron 1260™ was used for the measurement and the measurement conditions were an impressed voltage of 5 mV and a measuring frequency band of 0.01 MHz to 1 MHz. The results are shown in
(Raman Spectroscopy Measurement)
Raman spectroscopy measurement was performed for the sulfide solid electrolyte material obtained in Example 1-1, 1-2. Nanofinder SOLAR T II™ manufactured by Tokyo Instruments, Inc. was used for Raman spectroscopy measurement. The results are shown in
(Verification of Oxidative Decomposition)
Cyclic voltammetry (CV) was performed for the sulfide solid electrolyte material (30LiI.70 (0.75Li2S.0.25P2S5)) obtained in Example 1-2. A cell composed of Li/sulfide solid electrolyte material/SUS was prepared as an evaluation cell. This evaluation cell was a cell with a bipolar constitution such that Li was used for a reference electrode and a counter electrode and SUS was used for a working electrode. The potential scanning speed was 5 mV/s and the potential range was −0.3 V to 10 V. The results are shown in
With regard to a conventional amorphous sulfide solid electrolyte material, a synthesis method was only melt extraction, so that it was difficult to synthesize a sulfide solid electrolyte material with an ortho-composition. Through the view that decomposition potential of LiI is 2.7 V thermodynamically and bonding of an amorphous substance is firm, conventionally it has been widely conceived that LiI may not be used for a battery using a cathode active material with high electric potential by reason of being subject to oxidative decomposition. In recent years, mechanical milling is established as a new amorphizing method and a sulfide solid electrolyte material with an ortho-composition (an amorphous substance) may be synthesized, but it has been widely conceived that LiI is subject to oxidative decomposition, so that an ion conductor with an ortho-composition has not been doped with LiI. However, as described above, in the case where an ion conductor with an ortho-composition was doped with LiI, new knowledge that oxidative decomposition of LiI was not caused was found out.
The sulfide solid electrolyte material (30LiI.70 (0.75Li2S.0.25P2S5)) obtained in Example 1-2 and LiCoO2 (a cathode active material) coated with LiNbO3 with a thickness of 7 nm were mixed at a weight ratio of cathode active material:sulfide solid electrolyte material=7:3 to obtain a cathode composite. Next, the sulfide solid electrolyte material obtained in Example 1-2 and graphite (an anode active material) were mixed at a weight ratio of anode active material:sulfide solid electrolyte material=5:5 to obtain an anode composite. Next, the sulfide solid electrolyte material obtained in Example 1-2 was prepared as a solid electrolyte layer-forming material. Projected into a cylinder were 16.2 mg of the cathode composite, 65 mg of the solid electrolyte layer-forming material and 12 mg of the anode composite to perform cold pressing at a pressure of 4.3 ton/cm2 and obtain a lithium solid state battery.
First, a sulfide solid electrolyte material was obtained in the same manner as Comparative Example 1-3 except for modifying the ratio of Li2S and P2S5 into a molar ratio of 67Li2S.33P2S5 (dry-type mechanical milling). The composition of the obtained sulfide solid electrolyte material was 30LiI.70 (0.67Li2S.0.33P2S5).
Next, a lithium solid state battery was obtained in the same manner as Example 2 except for modifying the cathode composite, the anode composite and the sulfide solid electrolyte material used for the solid electrolyte layer-forming material into the sulfide solid electrolyte material obtained above (30LiI.70 (0.67Li2S.0.33P2S5)).
[Evaluation 2]
(Evaluation of Charge-Discharge Cycle Characteristics)
The evaluation of charge-discharge cycle characteristics was performed by using the lithium solid state battery obtained in Example 2 and Comparative Example 2. The constant-current charge-discharge measurement was performed in a range of 3 V to 4.1 V for the lithium solid state battery. The charge-discharge rate was 0.1 C and the temperature was 25° C. The results are shown in
(Reaction Resistance Measurement)
Reaction resistance measurement was performed by using the lithium solid state batteries obtained in Example 2 and Comparative Example 2. After adjusting the electric potential of the lithium solid state batteries to 3.96 V, reaction resistance of the batteries was calculated by performing complex impedance measurement. Reaction resistance was calculated from a diameter of a circular arc of the impedance curve. The results are shown in
First, lithium sulfide (Li2S), lithium oxide (Li2O), diphosphorus pentasulfide (P2S5) and lithium iodide (LiI) were used as a starting material. Next, Li2S, P2S5 and LiI were weighed by predetermined amount in a glove box under an Ar atmosphere (a dew point of −70° C.). Projected into a vessel of planetary ball mill (45 cc, made of ZrO2) was 2 g of this mixture, dehydrated heptane (a moisture amount of 30 ppm or less, 4 g) was projected thereinto, and ZrO2 ball (ϕ=5 mm, 53 g) was projected thereinto to completely seal the vessel (an Ar atmosphere). This vessel was mounted on a planetary ball milling machine (P7™ manufactured by Fritsch Japan Co., Ltd.) to perform mechanical milling of 1-hour treatment and 15-minute intermission 20 times at the number of weighing table revolutions of 370 rpm. Next, Li2O was added to the obtained sample by predetermined amount to perform mechanical milling again on the same conditions. Thereafter, the obtained sample was dried on a hotplate so as to remove heptane to obtain a sulfide solid electrolyte material. The composition of the obtained sulfide solid electrolyte material was 30LiI.70 (0.69Li2S.0.06Li2O.0.25P2S5).
A sulfide solid electrolyte material was each obtained in the same manner as Example 3-1 except for modifying the ratio of LiI into x=10, 20, 40, 43, 60 in xLiI.(100−x) (0.69Li2S.0.06Li2O.0.25P2S5).
A sulfide solid electrolyte material was obtained in the same manner as Example 3-1 except for weighing Li2S and P2S5 at a molar ratio of 75Li2S.25P2S5 (ortho-composition) without using Li2O and LiI. The composition of the obtained sulfide solid electrolyte material was 75Li2S.25P2S5.
First, lithium sulfide (Li2S), lithium oxide (Li2O) and diphosphorus pentasulfide (P2S5) were used as a starting material. Next, Li2S and P2S5 were weighed in a glove box under an Ar atmosphere (a dew point of −70° C.) so as to become a molar ratio of 69Li2S.25P2S5. Projected into a vessel of planetary ball mill (45 cc, made of ZrO2) was 2 g of this mixture, dehydrated heptane (a moisture amount of 30 ppm or less, 4 g) was projected thereinto, and ZrO2 ball (ϕ=5 mm, 53 g) was projected thereinto to completely seal the vessel (an Ar atmosphere). This vessel was mounted on a planetary ball milling machine (P7™ manufactured by Fritsch Japan Co., Ltd.) to perform mechanical milling of 1-hour treatment and 15-minute intermission 20 times at the number of weighing table revolutions of 500 rpm. Li2O was added to the obtained sample so as to become 6 mol % to perform mechanical milling again on the same conditions. Thereafter, the obtained sample was dried on a hotplate so as to remove heptane to obtain a sulfide solid electrolyte material. The composition of the obtained sulfide solid electrolyte material was 69Li2S.6Li2O.25P2S5.
A lithium solid state battery was obtained in the same manner as Example 2 except for modifying the cathode composite, the anode composite and the sulfide solid electrolyte material used for the solid electrolyte layer-forming material into the sulfide solid electrolyte material obtained in Example 3-1 (30LiI.70 (0.69Li2S.0.06Li2O.0.25P2S5)).
A lithium solid state battery was each obtained in the same manner as Example 4 except for modifying the cathode composite, the anode composite and the sulfide solid electrolyte material used for the solid electrolyte layer-forming material into the sulfide solid electrolyte material obtained in Comparative Example 3-1 (75Li2S.25P2S5) and the sulfide solid electrolyte material obtained in Comparative Example 3-2 (69Li2S.6Li2O.25P2S5).
A lithium solid state battery was obtained in the same manner as Example 4 except for modifying the cathode composite, the anode composite and the sulfide solid electrolyte material used for the solid electrolyte layer-forming material into the sulfide solid electrolyte material obtained in Example 1-2 (30LiI.70 (0.75Li2S.0.25P2S5)).
[Evaluation 3]
(Li Ion Conductivity Measurement)
Li ion conductivity (room temperature) measurement by an alternating current impedance method was performed for the sulfide solid electrolyte material obtained in Example 3-1 to 3-6. The measuring method is the same as the above. The results are shown in
(Reaction Resistance Measurement)
Reaction resistance measurement was performed by using the lithium solid state batteries obtained in Example 4, Comparative Example 4-1, 4-2 and Reference Example 4. The method for reaction resistance measurement is the same as the above-mentioned contents. The results are shown in
On the contrary, in Example 4, reaction resistance decreased greatly as compared with Comparative Example 4-1. This is considered as follows. That is to say, the reason therefor is conceived to be that the doping of LiI improved Li ion conductivity of the sulfide solid electrolyte material to restrain the defect of the doping of Li2O (the deterioration of Li ion conductivity), and the doping of Li2O improved chemical stability of the sulfide solid electrolyte material to restrain the defect of the doping of LiI (the deterioration of chemical stability). That is, it is conceived that the doping of both LiI and Li2O caused the synergistic effect of complementing mutual defects.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2010-189965 | Aug 2010 | JP | national |
This is a Continuation of application Ser. No. 13/818,495 filed Mar. 15, 2013, which in turn is a National Phase of International Patent Application No. PCT/JP2011/066174 filed Jul. 11, 2011, which claims the benefit of Japanese Patent Application No. 2010-189965 filed Aug. 26, 2010. The disclosure of the prior applications are hereby incorporated by reference herein in their entireties.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4599284 | Akridge | Jul 1986 | A |
| 5217826 | Yamamura et al. | Jun 1993 | A |
| 6322929 | Takada et al. | Nov 2001 | B1 |
| 6428935 | Takada et al. | Aug 2002 | B1 |
| 20060147806 | Kugai et al. | Jul 2006 | A1 |
| 20070160911 | Senga et al. | Jul 2007 | A1 |
| 20080081257 | Yoshida et al. | Apr 2008 | A1 |
| 20100297479 | Tsuchida et al. | Nov 2010 | A1 |
| 20110108642 | Hama et al. | May 2011 | A1 |
| 20110167625 | Hama et al. | Jul 2011 | A1 |
| 20130164631 | Ohtomo et al. | Jun 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 1790780 | Jun 2006 | CN |
| 0618632 | Oct 1994 | EP |
| S59-73850 | Apr 1984 | JP |
| S59-073851 | Apr 1984 | JP |
| 59-151770 | Aug 1984 | JP |
| S62-82665 | Apr 1987 | JP |
| 5-306117 | Nov 1993 | JP |
| H05-310417 | Nov 1993 | JP |
| 6-70905 | Mar 1994 | JP |
| H11-219722 | Aug 1999 | JP |
| 2001-328816 | Nov 2001 | JP |
| 2002-109955 | Apr 2002 | JP |
| 2002-329524 | Nov 2002 | JP |
| 2003-206111 | Jul 2003 | JP |
| 2003-217663 | Jul 2003 | JP |
| 2004-265685 | Sep 2004 | JP |
| 2005-228570 | Aug 2005 | JP |
| 2009-193727 | Aug 2009 | JP |
| 2009-193802 | Aug 2009 | JP |
| 2009-283344 | Dec 2009 | JP |
| 2010-040511 | Feb 2010 | JP |
| 0028608 | May 2000 | WO |
| 2010038313 | Apr 2010 | WO |
| Entry |
|---|
| Ohtomo, Takamasa, et al. “Electrical and Electrochemical Properties of Li2S—P2S5—P2O5 Glass-Ceramic Electrolytes”. Journal of Power Sources 146, 2005, pp. 715-718. |
| Minami, Keiichi, et al. “Structure and Properties of the 70Li2S—(30−x) P2S5—xP2O5 Oxysulfide Glasses and Glass-Ceramics”. Journal of Non-Crystalline Solids 354, 2008, pp. 370-373. |
| Minami, Keiichi, et al. “Electrical and Electrochemical Properties of the 70Li2S—(30−x) P2S5—xP2O5 Glass-Ceramic Electrolytes”. Solid State Ionics 179, 2008, pp. 1282-1285. |
| Takada, Kazunori, et al. “Lithium Ion Conductive Oxysulfide, Li3PO4—Li3PS4”. Solid State Ionics 176, 2005, pp. 2355-2359. |
| Nov. 10, 2015 Notice of Allowance issued in U.S. Appl. No. 13/818,495. |
| Ohtomo, Takamasa et al. “Characteristics of the Li2O—Li2S—P2S5 Glasses Synthesized by the Two-Step Mechanical Milling”. Journal of Non-Crystalline Solids, vol. 364, 2013, pp. 57-61. |
| May 21, 2015 Office Action issued in U.S. Appl. No. 13/516,496. |
| Machida Nobuya et al. “Mechano-chemical Synthesis of Lithium Ion Conducting Materials in the System Li2O—Li2S—P2S5”. J. Jpn. Soc. Powder Powder Metallurgy, vol. 51, No. 2, Dec. 12, 2003, pp. 91-97. |
| Visco et al., “Complex Plane and Li Nmr Studies of Highly Conductive Sulfide-Based Lithium Glasses,” Journal of the Eletrochemical Society, Apr. 1985, vol. 132, No. 4, pp. 751-753. |
| Mizuno et al., “Structure and Ionic Conductivity of Li2S—P2S5—P2O5 Glasses and Glass-Ceramics Prepared by Mechanical Milling,” Journal of the Ceramic Society of Japan, 2004, Supplement 112-1, pp. S709-S712. |
| Jul. 7, 2014 Office Action issued in U.S. Appl. No. 13/516,496. |
| Oct. 24, 2014 Office Action issued in U.S. Appl. No. 13/516,496. |
| Ménétrier et al; “Ionic conduction in B2S3—Li2S—LiI glasses;” Solid State Ionics; 1992; vol. 53-56; pp. 1208-1213. |
| Rao et al; “Oxysulfide glasses xLi2O-(1−x)(0.6Li2S-0.4P2S5);” Journal of Power Sources; 2006; vol. 159; pp. 258-262. |
| Tomei et al; “Preparation of Amorphous Materials in the system LiI—Li2S—P2S5 by Mechanical Milling and Their Lithium Ion Conducting Properties;” Summary of 29th Solid State Ionics Symposium; 2003; pp. 26-27. |
| Hayashi et al.; “Preparation of Li2S—P2S5 Amorphous Solid Electrolytes by Mechanical Milling;” J. Am. Ceram. Soc.; 2001; vol. 84; No. 2; pp. 477-479. |
| Tatsumisago et al; “New lithium ion conducting glass-ceramics prepared from mechanochemical Li2S—P2S5 gasses;” Solid State Ionics; 2002; vol. 154-155; pp. 635-640. |
| Suh et al; 11B NMR studies of the local environment of boron in B2S3—Li2S—LiI glasses; Journal of Non-Crystalline Solids; 1991; vol. 128; pp. 13-17. |
| Tatsumisago et al., “Lithium Ion Dendosei Kesshoka Glass (Lithium Ion Conductive Crystallized Glass),” Ceramics, 2008, vol. 43, No. 12, pp. 1051-1054. |
| Adachi et al., “Lithium Ion Dendotai to Sono Ouyou (Lithium Ion Conductor and its Application),” Ceramics, 1992, vol. 27, No. 2, pp. 117-121. |
| “21-Seiki no Lithium Nijidenchi Gijyutsu (Lithium Secondary Battery Technology in 21st Century),” Jan. 2002, pp. 182-184. |
| Ujiie et al., “Structure, ionic conductivity and electrochemical stability of Li2S—P2S5—LiI-glass and glass-ceramic electrolytes,” Solid State Ionics, 2012, vol. 211, pp. 42-45. |
| Ujiie et al., “Preparation and ionic conductivity of (100−x) (0.8Li2S−0.2P2S5)-xLiI glass-ceramic electrolytes,” Journal of Solid State Electrochemistry, Oct. 2012. |
| Partial Translation of Tomei et al.; “Preparation of Amorphous Materials in the system LiI—Li2S—P2S5 by Mechanical Milling and Their Lithium Ion Conducting Properties;” Summary of Solid State Ionics Symposium; vol. 23; 2003; pp. 26-27. |
| Mercier et al.; “Superionic Conduction in Li2S—P2S5—LiI—Glasses;” Solid State Ionics; vol. 5; 1981; pp. 663-666. |
| Takada et al.; “Solid-state lithium battery with graphite anode;” Solid State Ionics; vol. 158; 2003; pp. 269-274. |
| Sep. 14, 2016 Office Action issued in U.S. Appl. No. 13/516,496. |
| Feb. 1, 2016 Notice of Allowance issued in U.S. Appl. No. 13/818,495. |
| Feb. 21, 2018 Notice of Allowance issued in U.S. Appl. No. 13/516,496. |
| Oct. 21, 2015 Advisory Action issued in U.S. Appl. No. 13/516,496. |
| Number | Date | Country | |
|---|---|---|---|
| 20160028109 A1 | Jan 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13818495 | US | |
| Child | 14876379 | US |