Claims
- 1. An adhesive product comprising in substantially uncondensed admixture with each other, and in parts by weight, dry solids basis:
- Urea-Formaldehyde Resin: 50-90
- Spent Liquor from the Acid Sulfite Pulping of Lignocellulose: 10-50
- the adhesive product containing from 0.2 to 4.0% by weight ammonium ion (expressed as NH.sub.3) on a spent liquor solids basis,
- the spent liquor component of the mixture prior to mixing having a pH of from 3-9,
- the urea formaldehyde resin component of the mixture prior to mixing being characterized by a molar ratio of formaldehyde to urea of from 1.0-1.8 to 1; a pH of from 6-8; and a methylol content corresponding to a Witte number of from 1.0 to 1.8.
- 2. The adhesive product of claim 1 wherein the spent liquor comprises at least one member of the group consisting of the calcium base, magnesium base, sodium base and ammonium base spent liquors.
- 3. The adhesive product of claim 2 wherein the spent liquor comprises ammonium base acid sulfite spent liquor.
- 4. The adhesive product of claim 2 wherein the spent liquor comprises calcium base acid sulfite spent liquor.
- 5. The adhesive product of claim 2 wherein the spent liquor comprises magnesium base acid sulfite spent liquor.
- 6. The adhesive product of claim 2 wherein the spent liquor comprises sodium base acid sulfite spent liquor.
- 7. The adhesive product of claim 1 wherein the spent liquor comprises a calcium base acid sulfite spent liquor and a sufficient amount of a water soluble ammonium salt of a strong acid to provide from 0.2 to 4.0% by weight of ammonium ion (expressed as NH.sub.3) based on the spent liquor solids in the final adhesive product.
- 8. The adhesive product of claim 7 wherein the ammonium salt comprises ammonium chloride.
- 9. The adhesive product of claim 7 wherein the ammonium salt comprises ammonium sulfate.
- 10. The adhesive product of claim 1 wherein the spent liquor comprises a magnesium base acid sulfite spent liquor and a sufficient amount of a water soluble ammonium salt of a strong acid to provide from 0.2 to 4.0% by weight of ammonium ion (expressed as NH.sub.3) based on the spent liquor solids in the adhesive product.
- 11. The adhesive product of claim 10 wherein the ammonium salt comprises ammonium chloride.
- 12. The adhesive product of claim 10 wherein the ammonium salt comprises ammonium sulfate.
- 13. The adhesive product of claim 1 wherein the spent liquor comprises a sodium base acid sulfite spent liquor and a sufficient amount of a water soluble ammonium salt of a strong acid to provide from 0.2 to 4.0% by weight of ammonium ion (expressed as NH.sub.3) based on the spent liquor solids in the adhesive product.
- 14. The adhesive product of claim 13 wherein the ammonium salt comprises ammonium chloride.
- 15. The adhesive product of claim 13 wherein the ammonium salt comprises ammonium sulfate.
- 16. The adhesive product of claim 1 wherein the spent liquor has a pH of from 5-7 has a solids content of from 40-55% by weight, and wherein the urea formaldehyde resins has a solids content of from 50-72% by weight.
- 17. The method of making an adhesive product comprising combining, in substantially uncondensed admixture, spent acid sulfite pulping liquor and urea formaldehyde resin in the following proportions, expressed in parts by weight, dry solids basis:
- Urea-Formaldehyde Resin: 50-90
- Spent Liquor from the Acid Sulfite Pulping of Lignocellulose: 10-50
- the adhesive product containing from 0.2 to 4.0% by weight of ammonium ion (expressed as NH.sub.3) on a spent liquor solids basis,
- the spent liquor component of the mixture prior to mixing having a pH of from 3 to 9,
- the urea formaldehyde resin component of the mixture prior to mixing being characterized by a molar ratio of formaldehyde to urea of from 1.0-1.8 to 1; a pH of from 6-8, and a methylol content corresponding to a Witte number of from 1.0 to 1.8.
- 18. The method of making glued wood products which comprises applying to the surfaces of pieces of wood of bonding quantity of adhesive comprising in substantially uncondensed admixture with each other, and in parts by weight, dry solids basis:
- Urea-Formaldehyde Resin: 50-90
- Spent Liquor from the Acid Sulfite Pulping of Lignocellulose: 10-50
- the adhesive containing from 0.2 to 4.0 % by weight ammonium ion (expressed as NH.sub.3) on a spent liquor solids basis,
- the sulfite liquor component of the mixture prior to mixing having a pH of from 3-9,
- the urea formaldehyde resin component of the mixture prior to mixing being characterized by a molar ratio of formaldehyde to urea of from 1.0-1.8 to 1; a pH of from 6-8; and a methylol content corresponding to a Witte number of from 1.0 to 1.8 assembling and hot pressing the resulting adhesive-coated pieces of wood to form the glued wood product.
- 19. The method of claim 18 wherein the pieces of wood comprise wood particles.
- 20. The particle board produced by the process of claim 19.
BACKGROUND AND SUMMARY OF THE INVENTION
This application is a continuation-in-part of the patent application of Folke J. Edler, Ser. No. 738,370, filed Nov. 3, 1976, the same being a continuation of Ser. No. 574,515, filed May 5, 1975, both for METHOD OF MANUFACTURE OF ADHESIVE PRODUCTS and now abandoned.
US Referenced Citations (6)
Continuations (1)
|
Number |
Date |
Country |
Parent |
574515 |
May 1975 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
738370 |
Nov 1976 |
|