Sulfur compound containing lubricant composition for use in Flon atmosphere

FIELD OF THE INVENTION
This invention relates to a lubricant, and more particularly, to a lubricant composition for machines used in Flon atmosphere, such as refrigerating compressor and Flon expanding turbine.
BACKGROUND OF THE INVENTION
Attempts are being made to manufacture smaller, lighter and more energy-saving refrigerators. Today, an increasing number of refrigerators are used throughout the year. Another interesting fact is that reciprocating compressors that have been used in air conditioners for automobiles and houses are being replaced by rotary compressors. All of these phenomena are factors that put frictional and lubricated areas in the compressor (e.g., bearing, piston, seal unit and vane) under severer conditions, and it is important to take care to prevent excessive wear and seizure. More importantly, the friction loss in the lubricated area must be reduced. For these reasons, one requirement for lubricants to be used in refrigerators in Flon atmosphere is that they have good lubricating properties (e.g., wear resistance and seizure resistance) and low viscosity.
One must fully recognize the fact that lubricants for use at lubricated areas in apparatus that are exposed to a sealed Flon atmosphere and other lubricants (e.g., gasoline engine oil, diesel engine oil, industrial lubricants such as cutting oil, hydraulic oil, gear oil and other oils that are used in an oxygen-containing atmosphere such as air) require entirely different design philosophies in improving their lubricating properties such as wear resistance and seizure resistance. The former type must exhibit lubricating properties in Flon atmosphere whereas the latter must have lubricating properties in an oxygen-containing atmosphere. The extreme pressure tests specified in JIS or ASTM (e.g., the four ball test in ASTM D2266-78 or Falex test in ASTM D3233-73) assumes testing in an air atmosphere whether the lubricant under testing is actually used in such atmosphere or not. So, one who looks at the test data is apt to overlook the effect of the testing atmosphere in his evaluation of the performance of the lubricant. Some improvement in the wear resistance and load resistance is achieved by adding certain sulfur compounds (e.g., sulfurized olefin and sulfurized sperm oil) to the lubricant, but natural organic sulfur compounds in mineral oils are not effective for the wear resistance and load resistance.
In our study on the lubricant for use in machines operated in a sealed Flon atmosphere, we have found that the lubricating atmosphere itself has great effect on the wear behavior and that the presence of natural sulfur compound in mineral oils help provide improved wear resistance in a Flon gas atmosphere. Table 1 compares two mineral oils that were desulfurized to different extents and indicates that the presence of sulfur produces a large wear scar in air but that it proves effective against wear in a Flon atmosphere.
TABLE 1______________________________________ Abrasion Scar Atmosphere (mm)______________________________________Mineral oil (sulfur = 0.03 wt %) Air 0.51Mineral oil (sulfur = 0.03 wt %) Argon 0.42Mineral oil (sulfur = 0.03 wt %) Flon (R-22) 0.43Mineral oil (sulfur = 0.27 wt %) Air 0.62Mineral oil (sulfur = 0.27 wt %) Argon 0.38Mineral oil (sulfur = 0.27 wt %) Flon (R-22) 0.28______________________________________
As a result, we have found that the need of lower viscosity that had been considered incompatible with good lubricating properties can be met and a lubricant that retains good lubricating properties down to an extremely low viscosity range can be obtained by modification of sulfur content. This finding is not obvious at all in the prior art and is particularly unique to a Flon atmosphere.
So far, naphthenic mineral oils have been used with advantage as refrigerating oils, but because naphthene base crude oils are not easily available these days, mineral oils derived from more easily available paraffin or mixed base crude oils are preferred. These mineral oils do not have high ability to dissolve Flon at low temperatures, and to solve this problem, Japanese Patent Application (OPI) No. 139608/79 (the term "OPI" as used herein refers to a "published unexamined Japanese patent application") teaches the use of alkylbenzene. It also teaches the use of a phosphite ester for providing improved wear resistance. Japanese Patent Application (OPI) Nos. 54707/77 and 127904/77 teach that alkylbenzene lowers the critical dissolution temperature and provides higher heat resistance. But the lubricating properties, such as wear resistance, of alkylbenzene are not as good as those of mineral oils, and they fail to achieve the desired lubrication in compressor parts. The phosphite ester undergoes hydrolysis in the presence of a trace amount of water.
SUMMARY OF THE INVENTION
The basic concept of this invention is to use the combined effect of natural organic sulfur compounds in mineral oils and specific organic sulfur compounds to effectively lubricate machine components used in a Flon compound-containing atmosphere.
The term "Flon" as used herein is a generic term for halogen substituted compounds containing fluorinated methane or ethane hydrocarbons and having a chemical structure represented by the formula: C.sub.k H.sub.l Cl.sub.m F.sub.n (wherein k is an integer of 1 or 2, and 2k+2=l+m+n). Illustrative Flons are products sold under the trademark "Freon" from Du Pont such as Freon-11 (F-11), Freon-12 (F-12), Freon-13 (F-13), Freon-21 (F-21), Freon-22 (F-22), Freon-113 (F-113), Freon-114 (F-114), Freon-115 (F-115) and Freon-502 (F-502), and equivalents thereof. The Flon R-12 or Flon R-22, for example, is equivalent to Freon F-12 or Freon F-22, respectively, in the chemical composition and properties.
This invention contemplates the following two lubricant compositions:
(1) A lubricant composition for use in a Flon atmosphere comprising a base mineral oil having a lubricating viscosity derived from paraffin, naphthene or mixed base crude oil, said base oil containing an organic sulfur compound to have a total sulfur content of at least 0.14 wt% (this type of lubricant is hereunder referred to as a mineral oil based lubricant composition);
and
(2) A lubricant composition for use in a Flon atmosphere comprising as a base oil an alkylbenzene or a mixture thereof with mineral oil, the ratio of alkylbenzene to mineral oil being in a range of from 20:80 to 100:0, said lubricant containing an organic sulfur compound in such an amount that the relation between the total sulfur content in weight percent (S) and the viscosity at 40.degree. C. of the lubricant (Vis in centistokes) satisfies either of the following three formulas:
(i) if Vis is from 5 to 25 cSt:
S.gtoreq.-0.022.times.(Vis)+0.65;
(ii) if Vis is more than 25 cSt and not more than 32 cSt:
S.gtoreq.-0.008.times.(Vis)+0.30;
and
(iii) if Vis is more than 32 cSt:
S.gtoreq.0.04
(this type of lubricant is hereunder referred to as an alkylbenzene based lubricant composition).

BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a graph showing the relation between the total sulfur content and the diameter of wear scar resulting in friction test, and in the graph, the circles represent the lubricants that were refined to different sulfur contents, and the crosses represent the lubricants whose total sulfur content was varied by blending a mineral oil of 0.12 wt% sulfur and different amounts of organic sulfur compounds;
FIG. 2 is a graph showing the relation between viscosity and the diameter of wear scar for three different values of total sulfur content;
FIG. 3 is a graph showing the relation between total sulfur content and the diameter of wear scar for a viscosity of 14 to 15 cSt (indicated by a dot) and a viscosity of 30 to 32 cSt (indicated by a cross);
FIG. 4 is a graph showing the minimum necessary level of total sulfur content to achieve good lubrication for a given viscosity, and the area above the curve represents good wear resistance; and
FIG. 5 is a graph showing the relation between the diameter of wear scar and the speed of friction tester for the lubricant of this invention and commercial product.

DETAILED DESCRIPTION OF THE INVENTION
The minerals oils used in this invention are hydrocarbon oils produced from paraffin, naphthene or mixed base crude oils by conventional refining methods for producing base oils for lubricants. Being referred to as first, second and third side cuts and also as bright stock, they generally have a viscosity at 40.degree. C. in the range of from about 5 to about 500 cSt (the viscosity at 40.degree. C. is hereunder sometimes indicated by cSt at 40.degree. C.) The refining methods include furfural extraction, hydrofining, and if necessary, dewaxing and clay treatment. Further viscosity modification may be performed by redistillation. It is not particularly necessary that the mineral oils to be used in this invention be highly desulfurized, for the natural sulfur compounds contained have good lubricating properties.
The properties of the mineral oils used in the lubricant composition of this invention are listed in Table 2 below.
TABLE 2______________________________________ n-d-M Ring Analysis by ASTM D3238-74 Viscosity C.sub.N C.sub.A (cSt at 40.degree. C.) (%) (%)______________________________________Paraffinic mineral oil A 22.0 27.4 5.4Paraffinic mineral oil B 15.4 28.4 4.3Paraffinic mineral oil C 34.8 33.4 0.1Paraffinic mineral oil D 8.8 28.0 10.8Paraffinic mineral oil E 102.7 27.5 4.8Paraffinic mineral oil F 470 22.5 8.1Paraffinic mineral oil G 5.5 29.0 14.0Naphthenic mineral oil A 54.8 43.5 14.5Naphthenic mineral oil B 32.8 46.1 2.6Naphthenic mineral oil C 29.3 44.6 13.8______________________________________
The alkylbenzene used in this invention is linear or branched, and one example is alkylbenzene bottoms (heavy alkylate) obtained as a by-product in the production of the material for detergent from lower olefin and benzene. The linear alkylbenzene means an alkylbenzene primarily consisting of a linear alkylbenzene, and the branched alkylbenzene means an alkylbenzene primarily consisting of a branched alkylbenzene. Both linear and branched alkylbenzenes generally have a viscosity of 4 to 50 cSt at 40.degree. C., which correspond to the alkylbenzenes for the Electrical Insulating Oil No. 2 specified by JIS-C2320, and commercially available products may be used depending on the case. The alkylbenzene generally has a total content of 0.01 wt% or less.
The total sulfur content as used in this invention means the amount of sulfur that constitutes the organic sulfur compounds contained in the lubricant composition. So, it is the amount of sulfur contained in the sum of the natural organic sulfur compounds present in the mineral oil or alkylbenzene used as base oil and a separately added organic sulfur compound, and is represented by S wt%. For the purposes of this invention, the sulfur content of the natural organic sulfur compound present in the mineral oil or alkylbenzene need not be distinguished from that of the separately added organic sulfur compound. So, if there is no need of addition of an organic sulfur compound, the total sulfur content of the lubricant composition is accounted for only by the organic sulfur compound naturally occurring in the base oil. The mineral oil based lubricant composition of this invention has a total sulfur content of at least 0.14 wt%, preferably between 0.14 and 0.6 wt%.
FIG. 1 is a graph showing the relation between the total sulfur content and the diameter of wear scars developed in a friction test in a Flon atmosphere, and it explains one reason for the lower limit of the total sulfur content in the mineral oil based lubricant composition of this invention. Details of the method of modifying the total sulfur content in the lubricant composition of this invention will be given hereunder. In FIG. 1, the circles represent the lubricant samples that were refined to different sulfur contents, and the crosses represent the lubricant samples whose total sulfur content was varied by blending a mineral oil of 0.12 wt% and different amounts of certain organic sulfur compounds to be specified hereunder. As the figure shows, when the total sulfur content exceeds 0.13 wt%, wear resistance in a Flon atmosphere is improved greatly, and beyond 0.15 wt%, the high wear resistance is maintained. But a lubricant such as liquid paraffin which was highly desulfurized to a total sulfur content of 0.01 wt% caused seizure that provided a rough surface of the metal under lubrication. For a total sulfur content of less than 0.12 wt%, the diameter of wear scar was between 0.41 and 0.43 mm, but for a content of more than 0.15 wt%, the diameter remained the same within the range of from about 0.28 to 0.31 mm. The difference is from about 20 to 30%, but in terms of the volume of wear scar, the difference is from about 70 to 80%. This shows that the lubricant composition of this invention must have a total sulfur content of at least 0.14 wt%, preferably at least 0.15 wt%. The wear resisting effect of this amount of sulfur is characteristic of lubrication in a Flon atmosphere, and our experimence has shown that the increase in total sulfur content caused larger wear scars in lubrication in an air atmosphere.
Another reason for the lower limit of the total sulfur content is shown graphically in FIG. 2 which depicts the relation between the viscosity of lubricant composition and the diameter of wear scar for three diffeent values of total sulfur content. For the cases indicated by crosses which had a total sulfur content of from about 0.02 to about 0.1 wt% according to the prior art knowledge, appreciable wear took place at a viscosity of less than 100 cSt and seizure occurred at a viscosity of 7 cSt. The lubricant composition having a viscosity of 15 cSt according to ISO-VG 15 developed to wear scar of a diameter of about 0.5 mm. On the other hand, the samples indicated by circles which contained from 0.14 to 0.20 wt% of sulfur developed a wear scar of a diameter of only less than 0.35 mm. This enabled a significant reduction in viscosity. For the cases indicated by triangles that had a sulfur content of more than 0.25 wt%, good wear resistance was exhibited at a viscosity of 5 cSt at 40.degree. C. Therefore, suitable values of total sulfur content and viscosity can be selected according to the operating conditions of a specific refrigerator, and by modifying the total sulfur content, a lubricant of significantly low viscosity can be used in applications where viscosity could not be reduced without compromising wear resistance.
The upper limit of the total sulfur content is determined not by the desired lubricating performance but rather by the need of preventing the deposition of copper (cupper plating) from the cupreous material used in the piping and evaporator of the refrigerator or by the need of preventing an organic sulfur compound from coming out of solution at low temperatures. According to the experiment we conducted, good lubricating properties were exhibited in a Flon atmosphere by lubricants containing up to about 1.0 wt% of sulfur. In a copper deposition test in a Flon atmosphere to measure the amount of copper deposited on the surface of a ferrous material that was lubricated together with a cupreous material by lubricants of different total sulfur contents, no deleterious phenomenon occurred unless the total sulfur content exceeded about 0.6 wt%. Precipitation of an organic sulfur compound takes place only when the organic sulfur content specified hereunder is added to modify the total sulfur content of the lubricant of this invention. At a temperature between ordinary temperatures and about 50.degree. C., the sulfur compound comes out of solution if the total sulfur content exceeds a value between 0.5 and 0.7 wt% although the exact value varies with the type of the sulfur compound and the properties of the mineral oil to which it is added. But in the presence of Flon, Flon dissolves in the lubricant composition to increase the solubility of the sulfur compound and reduce its precipitation. If the viscosity of the lubricant composition is decreased, the solubility of the sulfur compound is increased and its precipitation decreases further. This consideration leads to the conclusion that there is no problem at all if the total sulfur content is between about 0.6 and 0.8 wt% inclusive of the sulfur content naturally occurring in the mineral oil. Therefore, the upper limit of the total sulfur content of the lubricant composition according to this invention is not limited to any particular value in view of lubricating performance, but to prevent copper deposition, it is preferably less than 0.6 wt%.
The alkylbenzene based lubricant composition according to this invention contains alkylbenzene and mineral oil at a weight ratio between 20:80 and 100:0. The alkylbenzene does not provide as high wear resistance as mineral oil but on the other hand, it has higher ability to dissolve Flon at low temperatures. If reasonably high ability to dissolve Flon at low temperatures is desired, less than 80 wt% of mineral oil is preferably mixed with the alkylbenzene. Table 3 below shows the data to support this limitation.
TABLE 3______________________________________ Alkylbenzene/Mineral Oil (weight ratio) 100/0 50/50 25/75 0/100 Critical Dissolution Tem-Mixed oil:Flon (R-22) perature of Flon (.degree.C.)______________________________________10:90 -67.dwnarw. -21 -6 720:80 -67.dwnarw. -13 4 2140:60 -67.dwnarw. -22 0 2060:40 -67.dwnarw. -35 -12 8______________________________________
(The lower value is preferable.)
The total sulfur content of the alkylbenzene based lubricant composition according to this invention must satisfy the relation represented by either of the following three formulas, wherein Vis indicates the viscosity of the lubricant as expressed by centistokes (cSt) at 40.degree. C., and S indicates the total sulfur content of the lubricant as expressed by wt%.
(i) if Vis is from 5 to 25 cSt:
S.gtoreq.-0.022.times.(Vis)+0.65;
(ii) if Vis is more than 25 and not more than 32 cSt;
S.gtoreq.-0.008.times.(Vis)+0.30;
and
(iii) if Vis is more than 32 cSt:
S.gtoreq.0.04.
The criticality of the formulas (i) to (iii) is shown graphically by FIGS. 3 and 4. FIG. 3 is a graph showing the relation between total sulfur content and the diameter of wear scar developed by a viscosity test in a Flon atmosphere, and the dots represent the lubricant samples having a viscosity in the range of from 14 to 15 cSt and the crosses indicate the samples having a viscosity in the range of from 30 to 32 cSt. One can see from the figure that the total sulfur content required varies with viscosity. FIG. 4 depicts the minimum necessary level of total sulfur content to provide good wear resistance in a wear test wherein the total sulfur content of an alkylbenzene lubricant was varied over a range of from 9 to 50 cSt. It is not known why the presence of an organic sulfur compound in a Flon atmosphere is effective in achieving good wear resistance, but presumably, it is because the heat of local friction generated at the lubricated surface decomposes. Flon and the decomposed Flon form a reaction product with the sulfur compound, and the reaction product may act to improve the wear resistance.
The method of modifying the total sulfur content of the lubricant composition according to this invention is described hereunder. The first method is accomplished by changing the conditions for refining mineral oils. Ordinary paraffin base crude oil, mixed base crude oil or naphthene base crude oil is subjected to atmospheric distillation, and the resulting residual oil is subjected to vacuum distillation to obtain fractions having a boiling point in the range of from 240.degree. to 700.degree. C. (at atm. pressure), and these fractions may be subjected to further distillation according to the viscosity required. Needless to say, fractions having the desired viscosity may be directly obtained from vacuum distillation. Alternatively, the fractions may be subjected to redistillation after they are passed through a refining step to be described hereunder. It is also possible to obtain "bright stock" by solvent-deaspahlting the residual oil from vacuum distillation with propane or the like. The resulting distillate or oils (hereunder referred to as mineral oils) are sent to the conventional desulfurizing steps for lubricants, i.e., solvent extraction and/or hydrogenation, to thereby desulfurize the mineral oils to a desired sulfur content. If necessary, the mineral oils are subjected to clay treatment, solvent dewaxing or sulfuric acid treatment. Clay treatment is effective in selective removal of nitrogen compounds and is particularly preferred for the purpose of providing improved color and heat stability. Solvent dewaxing is performed to lower the flowing point of the mineral oils. For the purposes of this invention, modification of sulfur content is important and to achieve this, proper solvent extraction and/or hydrogenation is important. The order of solvent extraction and hydrogenation is not critical. In solvent extraction, sulfur compounds including a benzene ring, such as thiophene, benzothiophene and dibenzothiophene compounds, are removed with high selectivity, and in hydrogenation, mercaptan or disulfide compounds are removed and at the same time, a nuclear hydrogenated compound such as benzothiophene is produced. Therefore, the type and amount of sulfur compound to be contained or removed can be determined to some extent by controlling the order of solvent extraction and hydrogenation as well as the degree of desulfurization to be achieved in each treatment. In this invention, it does not matter which type of sulfur compound should be contained in the largest amount.
Distillates from Kuwait crude oil that had a sulfur content of about 2.4 wt% and a viscosity of 20 to 30 cSt at 40.degree. C. were subjected to furfural extraction and hydrogenation under the conditions indicated in Table 4. The total sulfur contents and n-d-M ring analysis of the resulting minerals are shown in Table 4.
TABLE 4______________________________________ TotalFurfural Hydrogenation Sulfur n-d-M Ring AnalysisRatio Temperature Content C.sub.A C.sub.N(vol %) (.degree.C.) (wt %) (%) (%)______________________________________210 300 0.15 3.7 30.6150 300 0.24 5.0 30.2330 300 0.14 3.3 28.3270 Not treated 0.69 5.8 20.4______________________________________
In one embodiment of the first method of modification of total sulfur content, the first mineral oil that has been desulfurized to high extent is blended with the slightly desulfurized second mineral oil. The blend may be mixed with a third mineral oil if required. By so doing, not only the total sulfur content but also the viscosity can be modified. Examples of modificaton of total sulfur content and viscosity using two mineral oils are listed in Table 5 below.
TABLE 5______________________________________ First Second Mineral Mineral Oil Oil______________________________________Solvent ExtractionFurfural Ratio (vol %) 270 150Temperature (.degree.C.) 100 80HydrogenationH.sub.2 Pressure (kg/cm.sup.2) 100 35Temperature (.degree.C.) 300 330LHSV (hr.sup.-1) 2 2PropertiesViscosity 32 8.4(cSt at 40.degree. C.)Sulfur Content (wt %) 0.09 0.35n-d-M Ring AnalysisC.sub.A (%) 4.3 10.8C.sub.N (%) 28.7 27.9______________________________________Mixing Ratio (vol %) TotalFirst Second SulfurMineral Mineral Content ViscosityOil Oil (Wt %) (cSt at 40.degree. C.)______________________________________100 0 0.09 3250 50 0.21 1530 70 0.27 12 0 100 0.35 8______________________________________
The alkylbenzene is a synthetic product and inherently contains little sulfur. Accordingly, it is effective for modification of total sulfur content to blend the alkylbenzene with mineral oil of high sulfur content.
The second method for modification of total sulfur content is to add to the base oil at least one of the organic sulfur compounds of the following three formulas (I), (II) and (III): ##STR1## (wherein R.sub.1 and R.sub.2 which may be the same or different are each an alkyl group having 1 to 8 carbon atoms or hydrogen);
R.sub.1 --S--R.sub.2 (II)
(wherein R.sub.1 and R.sub.2 which may be the same or different are each an alkyl group having 4 to 12 carbon atoms, phenyl group, phenol group, benzyl group, naphthalene group or a derivative thereof having an alkyl substituent); and ##STR2## (wherein R is an alkyl group having 4 to 8 carbon atoms or a phenyl group; n is an integer of 2 to 8).
The compounds of the formula (I) have a structure generally referred to as thiophene ring. They include alkyl substituted compounds, as well as benzothiophene having one aromatic ring bonded to the thiophene ring and dibenzothiophene having two aromatic rings bonded to the thiophene ring. The compounds of the formula (II) are generally referred to as sulfide and include aliphatic sulfide, aromatic sulfide, olefinic sulfide and alkyl substituted compounds thereof. A preferred aliphatic sulfide has a boiling point of more than about 200.degree. C. at atmospheric pressure. The compound of the formula (III) is thiocarboxylate.
Dibenzyl disulfide (DBDS) is an organic sulfur compound which does not have the formula (I), (II) or (III). When it is added in a very low concentration, say, 0.01 wt%, it is effective in achieving higher wear resistance but at a concentration of, say, 0.05 wt%, it causes accelerated wear.
As described above, the lubricant composition of this invention achieves good lubrication without using a special extreme-pressure modifier, and at the same time, it is capable of dissolving Flon at low temperatures. Therefore, it is particularly useful in the manufacture of low-viscosity lubricants. The lubricant composition of this invention reduces friction loss and withstands extended service. It is to be understood that the lubricant composition of this invention can be used together with a defoaming agent, other extreme-pressure additives, corrosion inhibitor, etc.
The construction and advantages of this invention are now described in greater detail by reference to the following examples and comparative examples which are given here for illustrative purposes only and are by no means intended to limit the scope of the invention.
EXAMPLES 1 TO 8 AND COMPARATIVE EXAMPLES 1 TO 4
The atmospheric residue of Kuwait crude oil was subjected to vacuum distillation to obtain distillates having a boiling point in the range of from 350.degree. to 550.degree. C. (atm. pressure). The distillates were desulfurized under the conditions indicated in Table 6 and then solvent-dewaxed to produce mineral oils 1, 2, 3, 4 and 5 having a sulfur content between 0.02 and 0.74 wt%. The atmospheric residue of another sample of Kuwait crude oil was subjected to vacuum distillation to obtain distillates having a boiling point in the range of from 250.degree. to 450.degree. C. (atm. pressure). The distillates were hydrogenated and solvent-extracted to produce a mineral oil 6 having a sulfur content of 0.31 wt%. Mineral oil 6 was subjected to vacuum distillation again to give the mineral oil 7 having a viscosity of 5.5 cSt and the mineral oil 8 having a viscosity of 13.0 cSt. The properties of mineral oils 1 to 8 are listed in Table 6. Twelve lubricant compositions having various total sulfur contents were prepared with use of the mineral oil 1, 2, 3, 4, 6 and 7 and liquid paraffin: eleven of them consisted of the mineral oils independently or in admixture in the proportions indicated in Table 8, and the remaining one was liquid paraffin. These compositions were subjected to a friction test under condition A indicated in Table 7. The results are shown in Table 8.
TABLE 6__________________________________________________________________________ Mineral Mineral Mineral Mineral Mineral Mineral Oil 1 Oil 2 Oil 3 Oil 4 Oil 5 Oil 6 Mineral Oil Mineral Oil__________________________________________________________________________ 8Solvent ExtractionSolvent Furfural .rarw. .rarw. .rarw. .rarw. .rarw. Light fraction Heavy fractionSolvent/Oil 2.70 2.05 2.70 2.70 2.80 1.50 of mineral of mineral oilRatio (vol) No. 6 redistil- No. 6 redistil-Ext. Temp. (.degree.C.) 75 75 75 75 75 80 lation lationHydrogenationCatalyst Ni--Co--Mo .rarw. .rarw. (not Ni--Co--Mo .rarw.Reaction Temp. 340 320 300 treat- 340 335(.degree.C.) ed) 100 35Pressure 100 100 100(kg/cm.sup.2 Gage)LHSV (hr.sup.-1) 2.4 2.4 2.4 2.4 2.0Sulfur Cont. (wt %) 0.02 0.08 0.12 0.74 0.12 0.31 0.25 0.39Viscosity (cSt 32.3 32.7 31.8 32.1 102 7.5 5.5 13.0at 40.degree. C.)n-d-M RingAnalysisC.sub.N (%) 28.8 31.5 28.5 16.9 27.5 28.0 29.0 26.6C.sub.A (%) 2.9 2.8 3.8 9.2 4.8 10.8 14.0 8.0C.sub.P (%) 68.3 65.7 67.7 73.9 67.7 61.2 57.0 65.4__________________________________________________________________________
TABLE 7______________________________________Conditions for Friction Test______________________________________Apparatus 4-Ball tester (ASTM-D2266-78)Test Ball 1/2 in Cr steel ballOil Temperature 25-30.degree. C.Speed 1,500 rpmLoad 20 kg, 30 kgOperating Period 30 minutesAtmosphere Gas Under R-22 or R-12 gasOil Pretreatment Purged with R-22 before testingCondition A 1,500 rpm .times. 20 kg .times. 30 min (R-22)Condition B 1,500 rpm .times. 30 kg .times. 10 min (R-12)Wear Evaluation The diameter of wear scar on the surface of steel ball measured under microscope. The state of worn surface evaluated on the following three-grade basis: A: Almost circular and smooth B: Seizure in the center of the circle C: Generally rectangular dimples on rough surface with seizure______________________________________
TABLE 8__________________________________________________________________________ Sample Mixing Ratio (vol %) Mineral Mineral Mineral Mineral Mineral Liquid Mineral Oil 1 Oil 2 Oil 3 Oil 4 Oil 6 Paraffin Oil 7__________________________________________________________________________Comparative 100Example 1Comparative 100Example 2Comparative 100Example 3Comparative 100Example 4Example 1 100Example 2 100Example 3 90 10Example 4 70 30Example 5 50 50Example 6 50 50Example 7 90 10Example 8 100__________________________________________________________________________ Total Diameter of Volume of State of Sulfur Content Viscosity Wear Scar Wear Scar.sup.(1) Worn (wt %) (cSt at 40.degree. C.) (mm) (mm.sup.3) Surface__________________________________________________________________________Comparative 0.02 32.3 0.43 2.33 .times. 10.sup.-4 BExample 1Comparative 0.08 32.7 0.41 1.93 .times. 10.sup.-4 A-BExample 2Comparative 0.12 31.8 0.39 1.58 .times. 10.sup.- 4 A-BExample 3Comparative 0.01 34.8 Seizure -- CExample 4Example 1 0.74 32.1 0.30 1.58 .times. 10.sup.-5 AExample 2 0.31 7.5 0.30 1.58 .times. 10.sup.-5 AExample 3 0.14 27.2 0.32 2.04 .times. 10.sup.-5 AExample 4 0.17 20.6 0.29 1.38 .times. 10.sup.-5 AExample 5 0.21 15.5 0.30 1.58 .times. 10.sup.-5 AExample 6 0.52 15.8 0.30 1.58 .times. 10.sup.-5 AExample 7 0.15 32.0 0.31 1.80 .times. 10.sup.-5 AExample 8 0.25 5.5 0.38 1.54 .times. 10.sup.-4 A-B__________________________________________________________________________ Note- .sup.(1) The volume of wear scar was calculated by the following formula described in "A New Aproach in Interpreting the Four Ball Wear Results", Wear., 5, pp. 275-288 (1962). ##STR3## V: volume of wear scar (mm.sup.3), d: diameter of wear scar (mm), R: diameter of steel ball (R = 25.4 mm), a: radius of curvature of wear scar as determined by the diameter of wear scar and contact pressure. In Table 8, it is assumed 3,080 mm when d is 0.29-0.32 mm and 10 mm when is 0.39-0.43 mm.
As shown in Table 8, the diameter of wear scar was between 0.39 and 0.43 mm when the total sulfur content was less than 0.12 wt% and it was reduced to between 0.29 and 0.32 mm when the sulfur content was 0.14 wt% or more. The reduction was about 25%. The volume of wear scar as determined from its diameter was between 1.6.times.10.sup.-4 and 2.3.times.10.sup.-4 mm.sup.3 when the total sulfur content was less than 0.12 wt%, and it was decreased to between 1.4.times.10.sup.-5 and 2.0.times.10.sup.-5 mm.sup.3 when the sulfur content was 0.14 wt% or more. The reduction was about 90%.
EXAMPLE 9 AND COMPARATIVE EXAMPLE 5
Mineral oils 3 and 6 indicated in Table 6 were mixed at a ratio of 65:35 (v/v %) and the mixture was subjected to clay treatment. The resulting lubricant composition (Sample A) was subjected to a friction test in Flon gas (R-12) by changing the speed of the friction tester in a range of from 500 to 7,000 rpm. As a comparison, a commercial refrigerating oil (Commercial Product A) was also tested. The properties of the two samples are listed in Table 9, and the results of the friction test are shown in FIG. 5. In spite of its lower viscosity, Sample A (indicated by dot) exhibited good wear resistance (anti-wear performance) in a high rpm range as well as in a low rpm range in comparison with Commercial Product A (indicated by circle).
TABLE 9______________________________________ Example 9 Comparative Example 5______________________________________Sample Sample A Commercial Product ASpecific Gravity (15/4.degree. C.) 0.8612 0.9160Viscosity (cSt at 40.degree. C.) 15.0 30.6Flowing Point (.degree.C.) -30.0 -40.0C.sub.N (%) 6.2 13.9C.sub.A (%) 65.4 43.0Total Sulfur Content 0.19 0.04(wt %)______________________________________
EXAMPLES 10 TO 22 AND COMPARATIVE EXAMPLES 6 TO 11
Mineral oil 2 identified in Table 6 and naphthenic mineral oil (C.sub.N =43.3%, C.sub.A =13.8%, viscosity=33.6 cSt at 40.degree. C.) were blended with dibenzothiophene, benzothiophene, dibutyl sulfide, didodecyl sulfide, diphenyl sulfide, dibenzyl sulfide, 4,4'-thiobis(3-methyl-6-t-butyl)phenol, dilauryl thiodipropionate and dibenzyl disulfide. The resulting lubricant samples having their total sulfur contents modified to various levels were subjected to a friction test under condition A indicated in Table 7. The results are shown in Table 10.
EXAMPLES 23 TO 28 AND COMPARATIVE EXAMPLES 12 AND 13
Mineral oil 7 identified in Table 6 was blended with alkylbenzene at a volume ratio of 30:70 to prepare eight lubricant compositions having a viscosity of 15.0 cSt at 40.degree. C. and a sulfur content of 0.07 wt%. Seven of them were added (mixed) with one of the organic sulfur compounds listed in Table 11. The alkylbenzene was commercialy available from Mitsubishi Petrochemical Co., Ltd. It was the heavy alkylate that was obtained as a by-product in the production of straight chain monoalkylbenzene from .alpha.-olefin and benzene and which primarily consisted of dialkylbenzene. Its properties were as follow: sulfur content=less than 0.01 wt%, viscosity=34.7 cSt at 40.degree. C., n-d-M ring analysis=15.1% C.sub.N, 18.9% C.sub.A. The samples having various total sulfur contents were subjected to a friction test under condition B indicated in Table 7. The results are shown in Table 11.
TABLE 10__________________________________________________________________________ Result of Total Friction test Organic Sulfur Compound Sulfur Diameter of Mineral Addition Content Wear Scar State of Oil Name (wt %) (wt %) (mm) Surface__________________________________________________________________________Comparative Paraffinic (Not added) -- 0.12 0.42 A-BExample 6Example 10 " Dibenzothiophene 0.05 0.17 0.29 AExample 11 " Benzothiophene 0.05 0.17 0.30 AExample 12 " Dibutyl sulfide 0.05 0.17 0.28 AExample 13 " Didodecyl sulfide 0.02 0.14 0.31 AExample 14 " " 0.05 0.17 0.29 AExample 15 " " 0.30 0.42 0.30 AExample 16 " Diphenyl sulfide 0.05 0.17 0.30 AExample 17 " Dibenzyl sulfide 0.05 0.17 0.29 AExample 18 " 4,4'-Thiobis(3-methyl-6- 0.05 0.17 0.30 A t-butyl)phenolExample 19 " Dilauryl thiodipropionate 0.05 0.17 0.32 AComparative " Dibenzyl disulfide 0.01 0.13 0.37 A-BExample 7Comparative " " 0.30 0.42 0.46 CExample 8Comparative " Dibenzothiophene 0.01 0.13 0.37 BExample 9Comparative " Didodecyl sulfide 0.01 0.13 0.35 BExample 10Comparative Naphthenic (Not added) -- 0.07 0.41 A-BExample 11Example 20 " Benzothiophene 0.10 0.17 0.30 AExample 21 " Dibenzyl sulfide 0.10 0.17 0.31 AExample 22 " Didodecyl sulfide 0.30 0.37 0.29 A__________________________________________________________________________
TABLE 11__________________________________________________________________________ Comp. Comp. Ex. 12 Ex. 13 Ex. 23 Ex. 24 Ex. 25 Ex. 26 Ex. 27 Ex. 28__________________________________________________________________________Sample No. 1 No. 2 No. 3 No. 4 No. 5 No. 6 No. 7 No. 8Organic Sulfur CompoundAddedDi-n-dodecyl sulfide (no 0.10 0.25 0.35Dibenzothiophene addition) 0.30 0.20Dilauryl thiopropionate 0.30Benzothiophene 0.30Total sulfur content 0.06 0.16 0.31 0.41 0.36 0.36 0.36 0.26(wt %)Diameter of wear scar 0.42 0.40 0.34 0.31 0.31 0.30 0.32 0.34(mm)State of surface B-C B B A A A A B__________________________________________________________________________
As shown in Table 10, good wear resistance was exhibited when the total sulfur content was more than 0.30 wt% in the case of alkylbenzene and mineral oil mixture of viscosity 15.0 cSt.
EXAMPLES 29 TO 37, COMPARATIVE EXAMPLES 14 TO 20 AND REFERENCE EXAMPLE
Mineral oils 3, 5, 6 and 7 identified in Table 6 were blended with alkylbenzene (the same as used in Examples 23 to 28 and Comparative Examples 12 and 13), and except for Comparative Examples 15, 18, 19 and 20, Example 33 and Reference Example, the blends were mixed with the organic sulfur compounds indicated in Table 12. The Reference Example was commercial naphthene base refrigerating oil. The lubricants having their viscosity and total sulfur contents controlled to various levels were subjected to a friction test under condition A identified in Table 7. The results are shown in Table 12. In Examples 30 and 33 and Comparative Examples 15, 16 and 19, the samples were also subjected to a friction test in an air atmosphere replacing with R-22 atmosphere. As shown in Table 12, adequate control of total sulfur contents gave excellent anti-wear performance in the range of viscosity 7.7 cSt to 52 cSt of lubricants. Diameter of wear scar increased, as the total sulfur contents increase in the air atmosphere, and also the states of metal surface were darkened, black and rough with corrosive seizure.
TABLE 12__________________________________________________________________________ Comp. Comp. Comp. Comp. Comp. Ex. 14 Ex. 29 Ex. 15 Ex. 16 Ex. 17 Ex. 30 Ex. 31 Ex. 18 Ex. 32__________________________________________________________________________Sample No. No. 9 No. 10 No. 11 No. 12 No. 13 No. 14 No. 15 No. 16 No. 17Mixing Ratio (wt %)Alkylbenzene 30 .rarw. 50 .rarw. .rarw. .rarw. .rarw. 75 .rarw.Mineral Oil 6 70 .rarw.Mineral Oil 3 25 .rarw.Mineral Oil 5Mineral Oil 7 50 .rarw. .rarw. .rarw. .rarw.Organic Sulfur Compound (S wt %)Di-n-dodecyl sulfide 0.20 0.40 0.10 0.20 0.30Dibenzothiophene 0.30Dibenzyl sulfide 0.05Viscosity (cSt at 40.degree. C.) 10.4 .rarw. 13.8 .rarw. .rarw. .rarw. .rarw. 32.3 .rarw.Total Sulfur Content (wt %) 0.28 0.48 0.13 0.23 0.33 0.43 0.43 0.03 0.08Test in R-22 AtmosphereWear scar (mm) 0.38 0.31 0.42 0.40 0.35 0.31 0.31 0.33 0.30State of surface B A B-C B B A A A ATest in Air AtmosphereWear scar (mm) 0.65 0.66 0.89State of surface C C C__________________________________________________________________________ Comp. Comp. Ref. Ex. Ex. 33 Ex. 19 Ex. 34 Ex. 35 Ex. 20 Ex. 36 Ex. 37__________________________________________________________________________Sample No. Commercial No. 18 No. 19 No. 20 No. 21 No. 22 No. 23 No. 24 naphthene base refrig- erating oilMixing Ratio (wt %)Alkylbenzene 50 100 .rarw. .rarw. 70 .rarw. 20Mineral Oil 6 20 .rarw. 20Mineral Oil 3 10 .rarw.Mineral Oil 5 50Mineral Oil 7 60Organic Sulfur Compound (S wt %)Di-n-dodecyl sulfide 0.05 0.10 0.30DibenzothiopheneDibenzylsulfide 0.10Viscosity (cSt at 40.degree. C.) 30.6 52.0 34.7 .rarw. .rarw. 21.5 .rarw. 7.7Total Sulfur Content (wt %) 0.04 0.06 0.01.dwnarw. 0.05 0.10 0.07 0.17 0.15Test in R-22 AtmosphereWear scar (mm) 0.35 0.32 0.42 0.31 0.30 0.40 0.32 0.31State of surface B A C A A B A ATest in Air AtmosphereWear scar (mm) 0.46 0.54State of surface C C__________________________________________________________________________
EXAMPLE 38
Mineral oils 6 and 7 identified in Table 6 were blended with alkylbenzene (the same used in Examples 23 to 28) to prepare oils of Sample Nos. 19, 20 and 21 indicated in Table 13. The critical solution temperature of each of the oils was measured in the following manner.
Measurement of Critical Solution Temperature
A mixture of a sample oil and a cooling medium (R-22) in a weight proportion of 1:9 to 8:2 was charged into a glass tube having an inside diameter of 6 mm and a length of 250 mm, and the glass tube was tightly sealed. The glass tube was shaken at room temperature to allow the mixture to completely mix, and then, the resulting mixture was cooled at a rate of 1.degree. C./min. Thus, the temperature at which the mixture initiated to become cloudy or phase separation initiated was measured.
The results obtained are shown in Table 13.
TABLE 13______________________________________ Sample No. 19 20 21______________________________________Mixing Ratio of Basic Oils (vol %)Mineral Oil 7 25Mineral Oil 6 100 75Alkylbenzene 25 75Viscosity (cSt at 40.degree. C.) 13.0 17.5 19.0Critical Solution Temperature (.degree.C.)Ratio of oil to R-221:9 -20 -29 -422:8 -10 -20 -424:6 -10 -24 -426:4 -20 -34 -458:2 -34 -38 -45______________________________________
As is clear from Table 13, Sample Nos. 20 and 21 had an excellent property in Flon-dissolution as compared to Sample No. 19.
While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.

Number	Name	Date
4116812	Godar et al.	Sep 1978
4124514	Yaffe	Nov 1978
4125471	Vienna et al.	Nov 1978
4148737	Liston et al.	Apr 1979
4148739	Liston et al.	Apr 1979
4163006	Spivack	Jul 1979
4200543	Liston et al.	Apr 1980

Sulfur compound containing lubricant composition for use in Flon atmosphere

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (7)