Sulfur tolerant lean NOx trap

Abstract
The present invention provides a composition and method for storing and reducing NOx for lean burn internal combustion engines. The present invention uses composite metal oxides, in spinel structure, in conjunction with a typical LNT formulation to form an integrated LNT. The composite metal oxides in spinel structure act primarily as a SOx trapping element and also a secondarily NOx trapping element within the integrated LNT. In this integrated LNT, the sulfur is trapped and released in a way that does not allow the sulfur to go to the primary NOx trapping element, i.e. the alkali or alkali earth metal oxides, to poison the integrated LNT; thereby, leaving more reactive sites for the NOx trapping and conversion.
Description


BACKGROUND OF INVENTION

[0001] The present invention relates to a composition and method for controlling exhaust emissions, especially nitrogen oxides emissions, from combustion engines. More specifically, the present invention relates to a series of composite metal oxides that significantly improve the sulfur tolerance of a Lean NOx Trap (LNT).


[0002] An approach for treating the NOx emissions from lean-burn engines is the use of NOx traps. A LNT typically contains precious metals, alkali or alkali earth metals, and alumina. A generally accepted pathway for reactions of LNT is that under lean conditions, NO is oxidized to NO2, which is followed by subsequent formation of a nitrate with alkali or alkali earth metal(s), e.g. Barium. Under stoichiometric or rich operation, the stored nitrate is thermodynamically unstable. The stored NOx is released. The NOx then catalytically reacts with reducing species in the exhaust gas to form N2.


[0003] The alkali or alkali earth metal(s) that are typically used for NOx sorption are readily poisoned by sulfur oxides in the exhaust gas. Over time, the sulfur oxides react with these trapping elements forming sulfates which are more stable than corresponding nitrates. The present invention provides a new series of composite metal oxides that, combined with the active components of a LNT, significantly improve the sulfur tolerance of the LNT while maintaining or improving the other performances of the LNT.



SUMMARY OF INVENTION

[0004] The present invention solves this problem by providing a composition and method for storing and reducing NOx from lean burn internal combustion engines. The present invention uses composite metal oxides, in spinel structure, in conjunction with a typical LNT formulation to form an integrated LNT. The composite metal oxides in spinel structure act primarily as a SOx trapping element and also a secondary NOx trapping element within the integrated LNT. In the application of this integrated LNT, the sulfur oxides are mainly attached to the composite metal oxides in spinel structure under a relatively low temperature (200 to 600° C.). When the integrated LNT is saturated with sulfur for a specified NOx conversion, the LNT will be desulfated under rich condition at a higher temperature (600 to 750° C.), so that the capacity of the LNT for NOx trapping and conversion is regenerated. In this integrated LNT, the sulfur is trapped and released in a way that does not allow the sulfur to go to the primary NOx trapping element, i.e. the alkali or alkali earth metal oxides, to poison the integrated LNT; thereby, leaving more reactive sites for the NOx trapping and conversion.


[0005] The present invention provides a composition and method comprising a typical LNT formulation treated with a composite metal oxide in spinel structure. In one embodiment, the composite metal oxide spinel is in powder form and made into a slurry then coated into an LNT after all the other materials have been coated. Then the LNT is dried and calcined. In another embodiment, the spinel oxide slurry is mixed with CeO2 powder in an amount of 4-15 (wt) % of CeO2 of the total mixture before coating onto the LNT. In yet another embodiment, the spinel oxide slurry is mixed with CeO2—ZrO2 powder, in an amount of 4-15 (wt) % of the total mixture before coating onto the LNT.


[0006] The method for removing NOx and SOx impurities from exhaust gases provides a composition comprising an integrated LNT treated with a composite metal oxide having the spinel structure (AB2O4), and passing exhaust gas containing NOx and SOx over the composition. The NOx is stored under lean condition between 200 to 600° C. and released and converted under stoichiometric and rich condition between 200 to 600° C. Meanwhile, SOx is stored between 200 to 600° C. under both lean and rich conditions and is desulfated at a temperature between 600 to 750° C. under rich condition, when the trapped sulfur oxides have saturated the composite metal oxides and have thus reduced the NOx trapping efficiency to a predetermined value.







BRIEF DESCRIPTION OF DRAWINGS

[0007]
FIG. 1 shows the NOx trapping performance of LNT A treated with and without 4 (wt) % of composite metal oxide MgAl2O4:


[0008]
FIG. 1

a
shows the temperature window of LNT A with MgAl2O4 and without MgAl2O4.


[0009]
FIG. 1

b
shows the sulfur tolerance of LNT A with MgAl2O4 and without MgAl2O4.


[0010]
FIG. 1

c
shows the desulfation performance of LNT A with MgAl2O4 and without MgAl2O4.


[0011]
FIG. 2 shows the NOx trapping performance of LNT B treated with and without the 4 (wt) % MgAl2O4—CeO2 mixture.


[0012]
FIG. 2

a shows the temperature window of LNT B with MgAl


2
O4.CeO2 and without MgAl2O4. CeO2.


[0013]
FIG. 2

b
shows the sulfur tolerance of LNT B with MgAl2O4.CeO2 and without MgAl2O4.CeO2.


[0014]
FIG. 2

c
shows the desulfation performance of LNT B with MgAl2O4.CeO2 and without MgAl2O4.CeO2.







DETAILED DESCRIPTION

[0015] The present invention teaches a series of composite metal oxides and a method to inhibit sulfur poisoning of lean NOx traps. A typical LNT can be doped with the current composite metal oxides, that are spinel in structure. These spinel oxides can also be added during the manufacturing of the typical LNT to form integrated new LNTs. The integrated new LNTs have significantly better sulfur tolerance than a LNT without the composite metal oxides. The composite metal oxide is made to be primarily a sulfur trapping element and also a secondary NOx trapping element within the integrated LNT.


[0016] As stated in the Background, a LNT trap typically contains precious metals, alkali or alkali earth metals, and alumina. A generally accepted pathway for reactions of LNT is that, under lean conditions, NO is oxidized to NO2, which is followed by subsequent formation of a nitrate with alkali or alkali earth metal(s), e.g. Barium. Thus, the alkali or alkali earth metal(s) “trap” the NOx. The trapped nitrate is decomposed, or released, into NOx under stoichiometric and rich conditions. This NOx is then reacted with reductants such as HC, CO, and H2 to form N2, CO2, and H2O. While the primary trapping elements are the alkali or alkali earth metals, the secondary trapping element is the composite metal oxide. The combination of the primary and secondary trapping elements, in conjunction with the precious metal, forms the sulfur tolerant integrated LNT.


[0017] The temperature for NOx trapping is around 200-600° C, with optimum performance at around 350 400° C. The wider the temperature range or window, the more versatile the trap and therefore easier to be put on a vehicle.


[0018] The composite spinel metal oxides in the integrated LNT can trap the sulfur under both lean and rich conditions between 200-600° C. Once the spinel is saturated with attached sulfur so that the NOx trapping efficiency is reduced to a specified value, e.g. 85%, then the LNT needs to be desulfated. This can be done by adjusting the exhaust to a rich condition, such as A/F=814, and raising the LNT temperature to about 600-750° C. for a short period of time, e.g. 15 minutes. The desulfated LNT will then have regenerated high NOx trapping efficiency.


[0019] The composite metal oxide is, for example, a stoichiometric spinel MgAl2O4, or a spinel MgAl2O4 having MgO on the surface (MgAl2O4.MgO), or a solid solution of stoichiometric spinel MgAl2O4 and excess MgO. It is believed that the spinel MgAl2O4 and/or the MgO on the surface of the composite metal oxide or in the solid solution forms a chemical bond with the absorbed SOx, forming surface sulfate and bulk complex sulfate with the composite metal oxides. Therefore, the primary NOx trapping element within the LNT is protected for NOx trapping. The sulfur tolerance of the LNT is thus improved. On the other hand, we found that surface sulfates and bulk complex sulfates are easier to remove under reducing conditions than those bulk sulfates formed with the primary NOx trapping element, in the case that no spinel oxides are included in the LNT. From these results, it is believed the desulfation of the integrated LNT with composite spinel metal oxides is also easier than the typical LNTs.


[0020] The composite metal oxide is in powder form. The powder is then made into a slurry in an amount between about 2-30 (wt) % of the total trap. Preferably, the powder is made into a slurry in an amount between about 2-20 (wt) % of the total trap. Most preferably, the powder is made into a slurry in an amount between about 5-15 (wt) % of the total trap. The trap is then dipped into the slurry, dried at 120° C. in 6 hours, and calcined under 600° C. for 10 hours. The coating of the slurry can be conducted after all the other components are fixed or in the same time with the primary NOx trapping elements.


[0021] Another option is to mix spinel oxide with CeO2 powder in an amount between about 0-20 (wt) % of CeO2 of the total mixture. Preferably, the CeO2 powder is mixed in an amount between about 2-15 (wt) % of the total mixture. Most preferably, the CeO2 powder is mixed in an amount between about 4-10 (wt) % of the total mixture. The trap is then dipped into the slurry of spinel oxide with CeO2, dried at 120° C. in 6 hours and calcined under 600° C. for 10 hours. Similarly, the coating of the slurry can be conducted after all the other components are fixed or in the same time with the primary NOx trapping elements. Using spinel/CeO2 (MgAl2O4.CeO2 ) provides better sulfur tolerance than using spinel alone. It is believed that CeO2 promotes the oxidation of SO2 through its surface and lattice oxygen thereby promoting the sulfur oxides oxidation and attachment to the spinels, thus improving the sulfur tolerance of the LNT.


[0022] Another option is to mix the oxide with CeO2—ZrO2 powder, in an amount between about 0-20 (wt) % of the total mixture. Preferably, the CeO2—ZrO2 powder is mixed in an amount between about 2-15 (wt) % of the total mixture. Most preferably, the CeO2—ZrO2 powder is mixed in an amount between about 4-10 (wt) % of the total mixture. The trap is then dipped into the slurry, dried at 120° C. in 6 hours and calcined under 600° C. for 10 hours. Again, the coating of the slurry can be conducted after all the other components are fixed or in the same time with the primary NOx trapping elements.


[0023] The method for removing NOx and SOx impurities from the exhaust gases involves adding a composite metal oxide in spinel structure to a typical LNT. The composite metal oxide is added in an amount between about 2-30 (wt) %. Preferably, the composite metal oxide is added in an amount between about 2-20 (wt) %. Most preferably, the composite metal oxide is added in an amount between about 5-15 (wt) %. The composite metal oxides are coated onto the typical LNT after all the other components are fixed or in the same time with the primary NOx trapping elements. The composite metal oxide is spinel in structure. The composite metal oxides are preferably MgAl2O4, MgAl2O4.xMgO, MgAl2O4.yCeO2, or MgAl2O4.zCeO2—ZrO2, where x, y, and z are a number which would provide a correct wt % in accordance with the amount of composite metal oxides that is added to the total mixture. The LNT is doped with the composite metal oxide comprising between about 70-98 wt % LNT and about 2-30 wt % composite metal oxide.


[0024] The SOx impurities are mostly attached to the composite metal oxide in the form of surface sulfate and bulk composite sulfate at a temperature between 200 to 6000 C. under lean and rich condition. The SOx impurities are released at a temperature between 600 to 750° C. under rich condition. For this integrated LNT with composite spinel oxides, the storage and release conditions for NOx are similar to a typical NOx trap application condition. For example, the NOx is stored under lean condition (A/F>15) between 200-600° C., and then released and converted under stoichiometric and rich conditions (A/F≦14.7) for a shorter period than the lean period between 200-600° C. This cycling continues and during these cycling, the sulfur are attached mainly to spinel oxides site. When the NOx efficiency is reduced to a predetermined value due to sulfur poisoning, the trap is ready for a desulfation cycle. The temperature of the trap is raised to about 600- 750° C. under a rich condition, the sulfur attached to the spinel oxides is thus released, probably in the form of H2S, and COS.


[0025] Having described the invention in detail and by reference to preferred embodiments thereof, it will be apparent that modifications and variations are possible without departing from the scope of the invention defined in the appended claims. More specifically, although some aspects of the present invention are identified herein as preferred or particularly advantageous, it is contemplated that the present invention is not necessarily limited to these preferred aspects of the invention.



EXAMPLE 1

[0026] For a preformed LNT, LNT A, a piece of LNT A is cut. 3 (wt) % of the total trap, of the stoichiometric spinel MgAl2O4 is made into a slurry. LNT A piece is dipped into the slurry and dried at 120° C. for 6 hours. Then it is calcined in the oven at 600° C. for 12 hours. A core of the integrated LNT (LNT A doped with spinel) with ¾″ in diameter and 1″ in length was tested in a flow reactor. The feed gas contains 500 pm NO, 50 ppm hydrocarbons, 10% CO2, and 10% H2O. The feed gas also contains 6% O2 under lean conditions. When the feed gas is switched to rich condition, the O2 is replaced with a 1% CO/3300 ppm H2 mixture. The gas space velocity during this evaluation is 30,0001/hr. The LNT is run under a lean to rich cycle of 5 minutes lean and 3 minutes rich at 360° C.


[0027] For the sulfur tolerance test 9 ppm SO2 is added in the feed gas described above then the sample is tested under this new feed gas at 360° C. for 40 hours.


[0028] After sulfur poisoning test, the integrated LNT is switched for a desulfation test. Here, the inlet gas temperature is raised to 625° C., under N2 flow. Then, the feed gas composition is switched to the rich feed gas as described above. (No SO2 is in the feed gas) After 5 minutes, the LNT is cooled down gradually under N2 flow. The LNT is then tested at 360° C. under 5 minutes lean and 3 minutes rich cycle, as described above, for NOx trapping efficiency. This procedure is repeated for desulfation temperatures of 650°, 675°, 700°, 725°, 750° C.


[0029] Referring to the figures, FIG. 1a shows the temperature profile of LNT A with MgAl2O4 and without MgAl2O4. FIG. 1b shows the LNT A sulfur tolerance with MgAl2O4 and without MgAl2O4. FIG. 1c shows the LNT A desulfation with MgAl2O4 and without MgAl2O4. As can be seen from FIG. 1, the addition of spinel oxides expanded the temperature window slightly. The sulfur tolerance of the LNT A is significantly improved.


[0030] The desulfation characteristics were also improved. As can be seen, the desulfation temperature to reach a specified NOx conversion is lower with the addition of the spinel oxides then that without the spinel oxides.



EXAMPLE 2

[0031] For a preformed LNT, LNT B, a piece of LNT B is cut. 90 (wt) % of the stoichiometric spinel MgAl2O4 is mixed with 10 (wt) % of CeO20.4 (wt) % of the total LNT B of the mixture is then made into a slurry. The LNT B piece is dipped into the slurry and dried at 120° C. for 6 hours. Then it is calcined in the oven at 600° C. for 12 hours. A core of the integrated LNT (LNT B doped with spinel ) with ¾″ in diameter and 1″ in length is tested in a flow reactor. The formed LNT B is tested under the same conditions as described in Example 1.


[0032]
FIG. 2

a
shows the LNT B temperature window with MgAl2O4.CeO2 and without MgAl2O4.CeO2. FIG. 2b shows the LNT B sulfur tolerance with MgAl2O4.CeO2 and without MgAl2O4.CeO2. FIG. 2c shows the LNT B desulfation with MgAl2O4.CeO2 and without MgAl2O4. CeO2. As can be seen, the temperature window is widened slightly. The sulfur tolerance is improved significantly. The desulfation temperature is lower than without the addition of MgAl2O4.xCeO2.


Claims
  • 1. A composition comprising: a lean NOx trap treated with a composite metal oxide having the formula AB2O4, where A is Mg and B is Al.
  • 2. The composition of claim 1 wherein the composite metal oxide is spinel in structure.
  • 3. The composition of claim 1 wherein the composite metal oxide is selected from MgAl2O4, MgAl2O4. MgO, MgAl2O4. CeO2, or MgAl2O4.CeO2—ZrO2.
  • 4. The composition of claim 1 wherein said lean NOx trap is doped with said composite metal oxide to provide a composition comprising between about 70-98 wt % lean NOx trap and between about 2-30 wt % of said composite metal oxide.
  • 5. The composition of claim 4 wherein said lean NOx trap is doped with said composite metal oxide spinel to provide a composition comprising between about 80-98 wt % lean NOx trap and between about 2-20 wt % of said composite metal oxide.
  • 6. The composition of claim 4 wherein said lean NOx trap is doped with said composite metal oxide spinel to provide a composition comprising between about 85-95 wt % lean NOx trap and between about 5-15 wt % of said composite metal oxide.
  • 7. The composition of claim 1 wherein said lean NOx trap is doped with MgAl2O4. CeO2 or MgAl2O4. Ce—ZrO2 to provide a composition comprising between about 80-100 wt % lean NOx trap and between about 0-20 wt % of MgAl2O4. CeO2 or MgAl2O4. Ce—ZrO2.
  • 8. The composition of claim 7 wherein said lean NOx trap is doped with MgAl2O4. CeO2 or MgAl2O4. Ce—ZrO2 to provide a composition comprising between about 85-98 wt % lean NOx trap and between about 2-15 wt % of MgAl2O4. CeO2 or MgAl2O4. Ce—ZrO2.
  • 9. The composition of claim 7 wherein said lean NOx trap is doped with MgAl2O4. CeO2 or MgAl2O4. Ce—ZrO2 to provide a composition comprising between about 90-96 wt % lean NOx trap and between about 4-10 (wt) % of MgAl2O4. CeO2 or MgAl2O4. Ce—ZrO2.
  • 10. A method for removing NOx and SOx impurities from exhaust gases comprising: providing a composition comprising a lean NOx trap treated with a composite metal oxide having the formula AB2O4, where A is Mg and B is Al; and passing exhaust gas containing NOx and SOx over said composition.
  • 11. The method as claimed in claim 10, wherein the composite metal oxide is spinel in structure.
  • 12. The method as claimed in claim 10, wherein the composite metal oxide is selected from MgAl2O4, MgAl2O4. MgO, MgAl2O4. CeO2, or MgAl2O4. CeO2—ZrO2.
  • 13. The method as claimed in claim 10, wherein the SOx impurities are stored at a temperature of between 200 to 600° C. under lean and rich condition.
  • 14. The method as claimed in claim 10, wherein the SOx impurities are released at a temperature of between 600 to 750° C. under rich condition.
  • 15. The method as claimed 10 wherein said lean NOx trap is doped with said composite metal oxide to provide a composition comprising between about 70-98 wt % lean NOx trap and between about 2-30 wt % of said composite metal oxide.
  • 16. The method as claimed in claim 15 wherein said lean NOx trap is doped with said composite metal oxide to provide a composition comprising between about 80-98 wt % lean NOx trap and between about 2-20 wt % of said composite metal oxide.
  • 17. The method as claimed in claim 15 wherein said lean NOx trap is doped with said composite metal oxide to provide a composition comprising between about 85-95 wt % lean NOx trap and between about 5-15 wt % of said composite metal oxide.
  • 18. The method as claimed in claim 10 wherein said lean NOx trap is doped with MgAl2O4. CeO2 or MgAl2O4. Ce—ZrO2 to provide a composition comprising between about 80-100 wt % lean NOx trap and between about 0-20 wt % MgAl2O4. CeO2 or MgAl2O4. Ce—ZrO2.
  • 19. The method as claimed in claim 18 wherein said lean NOx trap is doped with MgAl2O4. CeO2 or MgAl2O4. Ce—ZrO2 to provide a composition comprising between about 85-98 wt % lean NOx trap and between about 2-15 wt % of MgAl2O4. CeO2 or MgAl2O4. Ce—ZrO2.
  • 20. The method as claimed in claim 18 wherein said lean NOx trap is doped with MgAl2O4. CeO2 or MgAl2O4. Ce—ZrO2 to provide a composition comprising between about 90-96 wt % lean NOx trap and between about 4-10 (wt) % MgAl2O4. CeO2 or MgAl2O4. Ce—ZrO2.