Superconducting bearing device

Abstract

A superconducting bearing device comprises an annular permanent magnetic portion 2 disposed concentrically with a rotary body 1 in the form of a vertical shaft, and superconductors 8 opposed to the lower end face of the magnet portion 2 and vertically spaced apart therefrom. The permanent magnet portion 2 comprises a disk 4 fixedly mounted on the rotary body 1, and annular permanent magnets 6a, 6b arranged on the disk 4 at a spacing radially of the rotary body 1. Each of the magnets 6a, 6b has upper and lower ends magnetized to polarities opposite to each other, and the adjacent magnets 6a, 6b are magnetized to polarities opposite to each other at the upper ends, as well as at the lower ends. The radial spacing between the magnets 6a, 6b is optimized in accordance with the radial dimension (width) of the magnets 6a, 6b. This improves the device in load capacity and rigidity and prevents the deflection of axis of the rotary body 1, enabling the bearing device to support the rotary body 1 in a noncontact state with good stability.

Description

TECHNICAL FIELD

The present invention relates to superconducting bearing devices, for example, for use in hydraulic machines and machine tools which require high-speed rotation, power storage apparatus for storing excessive electric power as converted to kinetic energy of a flywheel, or gyroscopes.

BACKGROUND ART

In recent years, superconducting bearing devices capable of supporting a rotary body in a noncontact state have been developed as bearing devices permitting high-speed rotation of the rotary body and having high rigidity.

It is thought that such superconducting bearing devices comprise, for example, an annular permanent magnet disposed concentrically with a rotary body and having axially opposite ends magnetized to polarities opposite to each other, and an annular superconductor opposed to the end face of the magnet and spaced apart therefrom axially of the rotary body.

However, the superconducting bearing device has the problem of being insufficient in rigidity with respect to the direction of the rotation axis and in load capacity. Another problem encountered is that the device is unable to support the rotary body in a noncontact state with good stability because the axis of the rotary body deflects owing to insufficient rigidity.

These problems are thought attributable to the following reason. The magnetic field strength H and magnetic flux density B of the permanent magnet are in inverse proportion to the distance from the magnet and decrease with an increase in the distance. Suppose the distance between the superconductor and the permanent magnet is Z, the apparent magnetic susceptibility of the superconductor is M, the field strength of the permanent magnet is H and the flux density of the magnet is B. The force of magnetic repulsion between the superconductor and the permanent magnet is in proportion to the product of the susceptibility M and the gradient of field strength dH/dZ or to the product of the susceptibility M and the gradient of flux density dB/dZ. The rigidity is proportional to the product of the susceptibility M and d.sup.2 B/dZ.sup.2. However, the gradient of field strength dH/dZ or the gradient of flux density dB/dZ of the annular permanent magnet is not great sufficiently, hence insufficient rigidity and load capacity.

An object of the present invention is to overcome the foregoing problems and to provide a superconducting bearing device capable of supporting a rotary body in a noncontact state with good stability by preventing the deflection of the axis of the rotary body.

DISCLOSURE OF THE INVENTION

The present invention provides a superconducting bearing device which comprises an annular permanent magnet portion disposed concentrically with a rotary body, and a superconductor opposed to an end face of the permanent magnet portion and spaced apart therefrom axially of the rotary body, the permanent magnet portion comprising a disk fixedly mounted on the rotary body, and a plurality of annular permanent magnets arranged on the disk at a spacing radially of the rotary body, each of the permanent magnets having axially opposite ends magnetized to polarities opposite to each other, the permanent magnets adjacent to each other being magnetized to polarities opposite to each other at their ends positioned toward the same axial direction.

Preferably, the spacing between the annular permanent magnets is 0.2 to 10 times the width of the magnets as measured radially thereof.

The present invention further provides a superconducting bearing device which comprises an annular permanent magnet portion disposed concentrically with a rotary body, and a superconductor opposed to the outer periphery of the permanent magnet portion and spaced apart therefrom radially of the rotary body, the permanent magnet portion comprising a disk fixedly mounted on the rotary body, and a plurality of annular permanent magnets arranged on the disk at a spacing axially of the rotary body, each of the permanent magnets having radially opposite sides magnetized to polarities opposite to each other, the permanent magnets adjacent to each other being magnetized to polarities opposite to each other at their same sides with respect to the radial direction.

Preferably, the spacing between the annular permanent magnets is 0.2 to 1.0 times the thickness of the magnets as measured axially thereof.

The permanent magnet portion comprises a disk fixedly mounted on the rotary body, and a plurality of annular permanent magnets arranged on the disk at a spacing radially of the rotary body, each of the permanent magnets having axially opposite ends magnetized to polarities opposite to each other, the permanent magnets adjacent to each other being magnetized to polarities opposite to each other at their ends positioned toward the same axial direction. In this case, a magnetic flux produced from the positive pole of one magnet and directed toward the negative pole of the same magnet upon reversion is added to a magnetic flux produced from the positive pole of another pole. This gives a strengthened magnetic flux and increases the gradient of flux density dB/dZ and d.sup.2 B/d.sup.2 Z, consequently increasing the load capacity and the rigidity.

The permanent magnet portion comprises a disk fixedly mounted on the rotary body, and a plurality of annular permanent magnets arranged on the disk at a spacing axially of the rotary body, each of the permanent magnets having radially opposite sides magnetized to polarities opposite to each other, the permanent magnets adjacent to each other being magnetized to polarities opposite to each other at their same sides with respect to the radial direction. In this case, a magnetic flux produced from the positive pole of one magnet and directed toward the negative pole of the same magnet upon reversion is added to a magnetic flux produced from the positive pole of another pole. This affords a strengthened magnetic flux and increases the gradient of flux density dB/dZ and d.sup.2 B/d.sup.2 Z, consequently improving the load capacity and the rigidity.

In either case, therefore, the deflection of the axis of the rotary body can be prevented, enabling the device to support the rotary body in a noncontact state with good stability.

Experiments have shown that the reversion of the magnetic flux starts to become pronounced in a space at a distance of 0.3 times the magnet width from the magnetic pole in the axial direction and at least 0.2 times the width radially away therefrom. Accordingly when two magnets are arranged too closely, the magnetic flux produced from the positive pole of one of the magnets and the magnetic flux entering the negative pole of the other magnet will interfere with each other to produce an adverse effect.

Further with a single magnet, the space region where the flux density is great is limited to a distance corresponding to the width of the magnet from the center of the pole, so that the above effect of addition will disappear when the plurality of magnets are spaced apart by too large a distance.

With the magnetic portion comprising a plurality of annular permanent magnets in a concentric combination, the space region in which the gradient of flux density is great, for example, the region retaining 80% of the maximum value thereof, has an axial dimension corresponding to the width of the magnets. Further the radial dimension of the space region in which the gradient of magnetic flux is great is proportional to the spacing between the magnets, whereas the gradient of flux density decreases to a value nearly equal to that of the single magnet if the spacing between the magnet is not smaller than twice the width of the magnets. Since a great magnetic force is available when the superconductor is disposed in this space region of great flux density gradient, it is then possible to optimize the width of the magnets and the spacing therebetween in proportion to the clearance between the permanent magnet portion and the superconductor, whereby an increased load capacity and enhanced rigidity are obtained.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagram in vertical section showing the main portion of a superconducting bearing device as a first embodiment of the invention;

FIG. 2 is a graph showing the result of an experiment conducted with use of the device of the first embodiment;

FIG. 3 is a graph showing the result of an experiment conducted for comparison;

FIG. 4 is a graph showing the result obtained by checking the relationship between the diameter of bearings and the rigidity thereof;

FIG. 5 is a graph showing the result obtained by checking the effect of the spacing between magnets on the same plane; and

FIG. 6 is a diagram in vertical section showing the main portion of a superconducting bearing device as a second embodiment of the invention.

BEST MODE OF CARRYING OUT THE INVENTION

The present invention will be described below in greater detail with reference to the accompanying drawings. In the following description, like parts are designated by like reference numerals.

FIG. 1 schematically shows the main portion of a first embodiment, i.e., a superconducting bearing device.

With reference to FIG. 1, the superconducting bearing device has a rotary body 1 in the form of a vertical shaft. A permanent magnet portion 2 in the form of a horizontal disk is mounted on the rotary body 1 concentrically therewith. An annular superconductor portion 3 is disposed as opposed to the lower end face of the permanent magnet portion 2 and spaced apart therefrom in the direction of axis of rotation of the rotary body 1.

The permanent magnet portion 2 comprises a horizontal disk 4 made, for example, of copper and fixedly mounted on the rotary body 1. The disk 4 is formed in its bottom surface with a plurality of, for example two, annular grooves 5a, 5b concentrically with the rotary body 1. Annular permanent magnets 6a, 6b are fixedly fitted in the grooves 5a, 5b, respectively. The permanent magnets 6a, 6b used are those having a great energy product, such as samarium-cobalt magnets or neodymium-iron-boron magnets. Each of the permanent magnets 6a, 6b has upper and lower ends which are magnetized to polarities opposite to each other. The upper ends of the adjacent magnets 6a, 6b, as well as the lower ends thereof, are magnetized to opposite polarities. For example, the outer magnet 6a has an S pole at the upper end and an N pole at the lower end, and the inner magnet 6b has an N pole at the upper end and an S pole at the lower end. The magnetic flux distribution around the axis of rotation is so designed as to remain unaltered by rotation. Assuming that the radial dimension of the permanent magnets 6a, 6b is the width thereof, the spacing between the magnets 6a, 6b is preferably 0.2 to 1.0 times the width.

The superconductor portion 3 comprises a horizontal disk 7 having a bore 7a and made, for example, of copper, and a plurality of disklike type II superconductors 8 embedded in the annular portion of the disk 7 around its bore, arranged close to one another circumferentially of the disk and opposed to the permanent magnets 6a, 6b. All the disklike superconductors 8 are equal in volume.

The superconductors 8 comprise a substrate made of yttrium high-temperature superconducting material such as YBa.sub.2 Cu.sub.3 O.sub.x and incorporating normally conducting particles (Y.sub.2 Ba.sub.1 Cu.sub.1) as uniformly mixed with the material, and have properties to restrain the magnetic flux emitted by the permanent magnet portion 2 and penetrating thereinto. The superconductors 8 are arranged at a position spaced apart from the permanent magnet portion 2 and permitting a specified quantity of magnetic flux of the magnet portion 2 to penetrate thereinto, the position being such that the penetrating flux distribution will not be altered by the rotation of the rotary body 1.

The superconducting bearing device has a housing (not shown), which has fixedly provided therein a cooling case 11. This case 11 is cooled by a refrigerator 9 or the like by way of a temperature control unit 10, and has the superconductor portion 3 fixed thereto.

When the superconducting bearing device is operated, the superconductors 8 are cooled and maintained in a superconducting state with a refrigerant circulated through the cooling case 11. Accordingly, many of the magnetic fluxes emitted from the permanent magnet portion 2 on the rotary body 1 penetrate into the superconductors 8 and are thereby restrained (pinning phenomenon). With the particulate normal conductor uniformly present in the superconductors 8, the distribution of fluxes penetrating into the superconductors 8 is held constant, with the result that the rotary body 1 is arrested by the superconductors 8 along with the permanent magnet portion 2 as if the magnet portion 2 on the rotary body 1 is pierced with phantom pins extending upright from the superconductors 8. For this reason, the rotary body 1 is supported with respect to the radial and axial directions, as held levitated with high stability.

The magnetic fluxes of each of the adjacent permanent magnets 6a, 6b at the upper and lower ends of the magnet portion 2 are strengthened by those emitted by the other magnet and reversed to make the gradient of flux density dB/dZ and d.sup.2 B/d.sup.2 Z greater than when the permanent magnet portion comprises a single permanent magnet. This increases the force of magnetic repulsion between the magnet portion 2 and the superconductors 8. Moreover, a great force of magnetic attraction acts therebetween merely when the spacing between the magnet portion 2 and the superconductors 8 slightly increases toward the direction of axis of rotation from the distance at which the force of magnetic repulsion is in balance with the pinning force. Conversely, a great force of magnetic repulsion acts therebetween merely when the spacing slightly decreases from the distance of balance. Accordingly, a greater load capacity and improved rigidity are available.

A type I superconductor, i.e., a superconductor completely preventing the penetration of magnetic fluxes, may be used as the superconductor of the present embodiment. In this case, the rotary body is supported in a noncontact state with respect to the axial direction utilizing the complete diamagnetic phenomenon of the superconductor. It is desired in this case to provide a superconducting bearing at a suitable position for supporting the rotary body with respect to the radial direction.

Specific Experiment Example

Experiments were conducted with use of the device of FIG. 1.

The disk 4 of the permanent magnet portion 2 used was one made of copper. The outer annular permanent magnet 6a used was an annular rare earth magnet which was 90 mm in outside diameter, 70 mm in inside diameter, 10 mm in width (radial dimension), 10 mm in thickness (axial dimension) and 4000 gauss in surface flux. The inner annular permanent magnet 6b used was an annular rare earth magnet which was 60 mm in outside diameter, 40 mm in inside diameter, 10 mm in width, 10 mm in thickness and 4000 gauss in surface magnetic flux. The two magnets 6a, 6b were used in a heteropolar combination which means that the upper ends thereof, as well as the lower ends thereof, had poles of opposite polarities. The superconductors 8 used were those measuring 35 mm in diameter and 12 mm in thickness. These superconductors were embedded in the disk 7 with the center of each positioned on the circumference of a circle with a diameter of 75 mm.

The permanent magnet portion 2 and the superconductor portion 3 were positioned in place relative to each other, and the superconductors 8 were thereafter cooled and thereby maintained in a superconducting state. The distance Z between the permanent magnet portion 2 and the superconductor portion 3 was 3 mm at this time. Using a tensile compression tester, the permanent magnet portion 2 and the superconductor portion 3 were moved toward or away from each other to measure the loads required. FIG. 2 shows the result. When the distance Z was in the range of 2 to 4 mm, the rigidity was 3.9 kgf/mm.

For comparison, a permanent magnet portion comprising a single magnet, i.e., the outer magnet only, and the superconductor portion were moved toward or away from each other to measure the loads required. FIG. 3 shows the result. When the distance Z was in the range of 2 to 4 mm, the rigidity was 2.9 kgf/mm. Another experiment was also conducted in which the outer magnet and the inner magnet were used in a homopolar combination in which the corresponding ends thereof were made to have poles of the same polarity. Although not illustrated, the rigidity obtained in this case was 2.4 kgf/mm, and was lower than in the case of the single magnet.

To explore the optimum conditions for the arrangement of magnets, a superconductor portion with a diameter of 100 mm was prepared which was fully covered with superconductors, and magnets measuring 25 mm, 48 mm, 60 mm, 90 mm and 100 mm in outside diameter were used singly or in combinations as arranged on the same plane to measure the rigidity. Table 1 shows data as to the bearings. Table 2 shows the measurements of rigidity obtained.

TABLE 1______________________________________ Bearing Net bearingType Magnet O.D. (mm) area (cm.sup.2)______________________________________Single magnet 90S 90 50 60S 60 26 48S 48 30 25S 25 8 100S 100 62Heteropolar 90N + 60S 90 63combination 90N + 48S 90 75 90N + 25S 90 79 100N + 60S 100 70Homopolar 90N + 60N 90 63combination______________________________________ TABLE 2__________________________________________________________________________ Plane rigidityBearing data Rigidity (kgf/mm) (kgf/mm .multidot. cm.sup.2)Type Magnet Z = 2 mm Z = 3 mm Z = 5 mm Z = 3 mm__________________________________________________________________________Single magnet 90S 2.9 (1.8) 1.1 0.035 60S (0.65) 0.023 48S 25S (0.38) 0.035 100S 4.0Heteropolar 90N + 60S 3.9 (2.7) 1.5 0.043combination 90N + 48S (2.4) 0.032 90N + 25S (2.2) 0.028 100N + 60S 8.0Homopolar 90N + 60N 2.4 0.9 0.024combination__________________________________________________________________________

Each numerical value given in the columns of magnet in these tables indicates the outside diameter of the magnet, and S or N following the value stands for the polarity of its lower end. The disklike magnet with an outside diameter of 25 mm is 10 mm in thickness, the annular magnet with an outside diameter of 48 mm is 14 mm in width and 10 mm in thickness, the magnet with an outside diameter of 60 mm is 8 mm in width and 9 mm in thickness, the magnet with an outside diameter of 90 mm is 10 mm in width and 12 mm in thickness, and the magnet with an outside diameter of 100 mm is 10 mm in width and 10 mm in thickness. To expedite the experiment, the magnet or magnets were brought closer to the superconductors cooled in advance and moved upward and downward several times by 1 mm each time at Z=3 mm to measure the rigidity. Since the value of rigidity then obtained is somewhat different from the corresponding value obtained in the case where the parts are first set to Z=3 mm, followed by cooling, the measurement is given in the parentheses.

Regarding the outside diameter of the outer magnet as the diameter of the bearing, the bearing rigidity values are typically shown in FIG. 4, in which the single magnet is represented by a blank circle mark, the heteropolar combination by a dot-and-circle mark, and the homopolar combination by a double circle mark. The graph shows that with the single magnets, the rigidity does not increase so greatly as to be proportional to the bearing area, hence the need for the heteropolar combination. However, the homopolar combination exhibits lower rigidity than the single magnet, hence an adverse effect.

FIG. 5 shows the relationship between the plane rigidity (rigidity per unit area) and the spacing between the magnets as established for three different heteropolar combinations. When it is required that the plane rigidity in this case be manifestly above the plane rigidity of 0.035 in the case of the single magnet, the effective magnet spacing is in the range of 0.2 to 1.0 times the width. The lower limit was determined in view of the phenomenon that one of two magnets too closely arranged in heteropolar combination starts to offset the flux of the other magnet.

FIG. 6 schematically shows the main portion of another superconducting bearing device as a second embodiment.

In this case, a permanent magnet portion 20 has a disk 21 which is formed in its outer periphery with a plurality of, for example two, annular grooves 22a, 22b vertically spaced apart. Annular permanent magnets 23a, 23b are fixedly fitted in the grooves 22a, 22b, respectively. Each of the permanent magnets 23a, 23b has radially opposite sides which are magnetized to polarities opposite to each other. The radially outer sides, as well as the inner sides, of the adjacent permanent magnets 23a, 23b are magnetized to opposite polarities. For example, the upper magnet 23a has an N pole at the outer periphery and an S pole at the inner periphery, and the lower magnet 23b has an S pole at the outer periphery and an N pole at the inner periphery. The magnetic flux distribution around the axis of rotation is so designed as to remain unaltered by rotation. Assuming that the axial dimension of the permanent magnets 23a, 23b is the thickness thereof, the spacing between the magnets 23a, 23b is preferably 0.2 to 1.0 times the thickness.

A type II superconductor 24 is disposed as opposed to the outer periphery of the permanent magnet portion 20 and spaced apart therefrom radially of a rotary body 1. Incidentally, the superconductor 24 may be in the form of a complete ring or a segment of a ring.

In this case, as described with reference to the first embodiment, the magnetic fluxes of each of the adjacent permanent magnets 23a, 23b at the outer peripheral part of the magnet portion 20 are strengthened by those emitted by the other magnet and reversed to make the gradient of flux density dB/dZ and d.sup.2 B/d.sup.2 Z greater than when the permanent magnet portion comprises a single permanent magnet. This increases the force of magnetic repulsion between the magnet portion 20 and the superconductor 24. Moreover, a great force of magnetic attraction acts therebetween merely when the spacing between the magnet portion 20 and the superconductor 24 slightly increases toward the direction of axis of rotation from the distance at which the force of magnetic repulsion is in balance with the pinning force. Conversely, a great force of magnetic repulsion acts therebetween merely when the spacing slightly decreases from the distance of balance. Accordingly, a greater load capacity and improved rigidity are available.

A type I superconductor, i.e., a superconductor completely preventing the penetration of magnetic fluxes may be used as the superconductor also in this embodiment. In this case, the rotary body is supported in a noncontact state with respect to the radial direction utilizing the complete diamagnetic phenomenon of the superconductor. It is desired in this case to provide a superconducting bearing at a suitable position for supporting the rotary body with respect to the axial direction.

INDUSTRIAL APPLICABILITY

The superconducting bearing device embodying the present invention is suitable for use in hydraulic machines and machine tools which require high-speed rotation, power storage apparatus for storing excessive electric power as converted to kinetic energy of a flywheel, or gyroscopes.

Claims

1. A superconducting bearing device comprising:

a rotary body;

an annular permanent magnet portion disposed concentrically with the rotary body, the permanent magnet portion having an outer periphery, the permanent magnet portion being provided on the rotary body such that the magnetic flux distribution does not alter around the axis of the rotary body, the permanent magnet portion comprising a disk fixedly mounted on the rotary body and a plurality of annular permanent magnets arranged on the disk at a spacing axially of the rotary body, each of the permanent magnets having radially opposite ends magnetized to polarities opposite to each other, the permanent magnets adjacent to each other being magnetized to polarities opposite to each other at their same sides with respect to the radial direction, and the permanent magnets being spaced from each other 0.2 to 1.0 times their width as measured radially; and

a superconductor opposed to the outer periphery of the permanent magnet portion and spaced apart therefrom radially of the rotary body, the superconductor being arranged at a position spaced apart from the permanent magnet portion and permitting a specified quantity greater than zero of magnetic flux of the permanent magnet portion to penetrate thereinto.

2. A superconducting bearing device as defined in claim 1 wherein the disk is formed on its outer peripheral face with a plurality of annular grooves spaced apart axially of the rotary body, the annular permanent magnets being respectively fixedly fitted in the grooves.

3. A superconducting bearing device as defined in claim 1 wherein the superconductor has an upper end and a lower end and all the permanent magnets are arranged within a range between the upper and lower end of the superconductor in a vertical cross section.