Patent Application
20150111755
The present invention relates to a superconducting wire, a superconducting wire precursor body and a fabrication method thereof, and a superconducting multi-core conductor precursor body.
Magnesium diboride (MgB2) is a superconductor discovered in 2001. It has the highest critical temperature (39K) among superconductors using metal. Therefore, by using magnesium diboride, it is possible to operate a superconducting equipment, which has been operated by cooling to liquid helium temperature (4.2K), at higher temperature (10K to 20K) without using liquid helium. In particular, it is expected that magnesium diboride is applied to equipments such as a nuclear magnetic resonance spectrometer (an NMR equipment), a medical MRI equipment (medical magnetic resonance imaging equipment), which use a magnetic field having a very small temporal variation. This is because a problem of magnetic flux creep, which is significant in a superconductor etc. using copper oxide, is reduced in a superconductor using magnesium diboride.
A linearized superconductor (superconducting wire) is, for example, obtained by fabricating a wire by performing an area reduction process and firing the wire after filling a raw material powder into a metal sheath. The superconducting wire obtained in this manner has a critical current density suitable for a practical use. This fabrication method is referred to as a powder-in-tube method.
The powder-in-tube method is roughly divided into two methods in accordance with the raw material powder to be filled. That is, a method for producing magnesium diboride by using boron powder and magnesium powder as the raw material powder and firing in the metal sheath is referred to as an in-Situ method. Further, a method of using magnesium diboride as the raw material powder and strongly binding together the magnesium diboride in the metal sheath is referred to as an ex-Situ method.
In connection with such techniques, Patent Documents 1 and 2 are known.
{Patent Document 1}
Japanese Patent No. 4667638
{Patent Document 2}
Japanese Patent Application Publication No. 2003-031057
In a superconducting magnet using a superconducting wire containing magnesium diboride, in order to generate a predetermined magnetic field, it is important to increase the product of the critical current density and wire length of the superconducting wire. As a value of the product is larger, a range of the magnetic field which can be generated is larger. Therefore, it is required for the superconducting wire that the wire length is long enough and the critical current density is uniformly high over the entire length thereof.
The present invention has been made in view of the above problems, an object of the present invention is to provide a superconducting wire having a wire length which is sufficiently longer than that of the conventional one, and a critical current density which is uniformly high over the entire length thereof, a precursor of the superconducting wire and a fabrication method thereof, and a precursor of the superconducting multi-core conductor.
As a result of intensive studies in order to solve the above problems, the present inventors have found that it is possible to solve the above problems by satisfying a predetermined condition for magnesium diboride contained in the superconducting wire, and have completed the present invention.
According to the present invention, it is possible to provide a superconducting wire having a wire length which is sufficiently longer than that of the conventional one, and a critical current density which is uniformly high over the entire length thereof, a precursor of the superconducting wire and a fabrication method thereof, and a precursor of the superconducting multi-core conductor.
Hereinafter, an embodiment to implement the present invention (the present embodiment) will be described with reference to drawings as appropriate. For convenience of illustration, a reduction ratio or an enlargement factor in each drawing is not constant, and the same member is not necessarily shown in the same size in all drawings. Further, for convenience of description, in particular, some members may be shown enlarged or reduced in the same drawing.
As shown in
Physical property 1: The density of the magnesium diboride core 1 is 1.5 g/cm′ or higher.
Physical property 2: In a void which is present in an arbitrary longitudinal cross-section in the longitudinal direction of the superconducting wire 10, when a length of a line segment which connects the most distant two points in a closed curve forming the void is assumed to be L, among the voids with length L of 20 μm or more, the number of voids having angles of 45° or more, which is formed by the line segment and the axis in the longitudinal direction of the superconducting wire 10, is less than the number of voids having angles smaller than 45°, which is formed by the line segment and the axis in the longitudinal direction of the superconducting wire 10.
Physical property 3: In an arbitrary 100 μm region in the longitudinal direction of the longitudinal cross-section, when a virtual straight line approximated by the least squares method is drawn for a boundary curve between the magnesium diboride core 1 and the metal sheath 2, the distance between the approximate straight line and the boundary curve is 10 μm or less.
In the following, each of the physical properties will be described.
The density of the magnesium diboride core 1 contained in the superconducting wire 10 is 1.5 g/cm3 or higher. However, the density of the magnesium diboride core 1 is preferably 1.57 g/cm3 or higher, and an upper limit thereof is preferably 2.36 g/cm3 or lower, because of the facts that a true density of magnesium diboride is 2.62 g/cm3 and that when a packing density of powder exceeds 90%, liquidity of the powder is deteriorated to be linearized and wire fabrication becomes difficult. Note that, the density of the magnesium diboride core 1 can be measured for the magnesium diboride core 1 obtained by removing the metal sheath of the wire, by measuring a mass thereof by an electronic balance, calculating a volume from a size thereof by an electron microscope, and dividing the mass by the volume.
By allowing the density of the magnesium diboride core 1 to be in this range, it is possible to reduce the voids in the magnesium diboride core 1. Thus, in the superconducting wire 10 (magnesium diboride core 1), it is possible to increase paths in which superconducting current flows, thereby obtaining the superconducting wire 10 having an excellent critical current density.
As shown in
As shown in
Note that, in this specification, the size of the void 4 is denoted by the length L of the line segment. Further, such a longitudinal cross-section can be observed by a method described in an embodiment to be described below.
For example, in an example shown in
Further, it is preferred that the angle θ of the void 4 described above is as small as possible. Specifically, as a limit of the size of the angle θ, the angle θ is preferably less than 20°, and more preferably less than 10°.
Although the details are described below in the embodiment, as an example which is not applicable to the superconducting wire 10 of the present embodiment, a superconducting wire 11 (conventional superconducting wire) is, for example, shown in
As shown in
This distance is ideally 0 μm, that is, the boundary between the magnesium diboride core 1 and the metal sheath 2 is preferably in a completely flat state. However, since such a state is difficult in practice, the distance is normally 10 μm or less, but it is desired that the distance is preferably 5 μm or less, and more preferably 1 μm or less.
By allowing the distance between the approximate straight line 6 and the boundary curve 5 to be in this range, the boundary between the magnesium diboride core 1 and the metal sheath 2 is in a state close to the flat state. By allowing the boundary to be in the state close to the flat state, it is possible to obtain the excellent superconducting wire 10 having the uniform critical current density characteristics in the longitudinal direction.
Further, as described above, the hardness of magnesium diboride is, for example, higher than that of born, carbon, magnesium, and the like. Therefore, although details will be described below, in case that magnesium diboride is used as a part of raw material of the magnesium diboride core 1, when the raw material such as magnesium diboride is filled in the metal sheath 2 to be extended, the wire is sometimes cut off at a portion where magnesium diboride and the metal sheath 2 are in contact with each other. In other words, since the hardness of magnesium diboride is high, magnesium diboride excessively bites into the metal sheath 2 in some cases. As a result, the strength of the metal sheath 2 is reduced, and the wire is cut off. Therefore, to avoid such a phenomenon, a particle diameter of magnesium diboride is preferably 10 μm or less. In this manner, a distance L between the approximate straight line 6 and the boundary curve 5 can be 10 μm or less.
In case that the superconductive wire 10 satisfies the three physical properties described above, other physical properties are arbitrary. For example, the magnesium diboride core 1 constituting the superconducting wire 10 contains magnesium diboride as described above. However, a part of boron atom sites of magnesium diboride contained may be substituted with carbon atom. By configuring the superconducting wire 10 in this manner, it is possible to cause lattice distortion in a crystal, thereby increasing the critical current density in a high magnetic field region of the superconducting wire 10.
Note that, such a substitution can be caused by firing a material (carbon source) containing carbon such as boron carbide in addition to boron and magnesium when preparing magnesium diboride. Further, an amount of the substitution can be controlled by appropriately changing a usage amount of the material containing carbon or the kind of the materials.
Further, the material of the metal sheath 2 constituting the superconducting wire 10 is not particularly limited. However, as the material of the metal sheath 2, it is preferable to use a metal material which does not react with magnesium, boron, magnesium diboride, and the like. Further, when a material other than these is used in the metal sheath 2, it is preferable to use a metal material which does not react with such a material. Further, by the same reason, the metal material having low reactivity with these materials or having a critical current density which does not significantly decrease even after reaction with these materials is also applicable to the metal sheath 2.
Such materials includes, for example, iron (Fe), niobium (Nb), tantalum (Ta), titanium (Ti), and the like. In particular, these are preferable as the material constituting the metal sheath 2. These may be used alone, or may be used in any ratio of two or more. Further, an alloy containing these as components may be used.
Further, an outer surface of the metal sheath 2 may be coated with a material containing copper (Cu). By coating the metal sheath 2 with such a material, workability of the superconducting wire 10 can be improved. Further, since copper has good conductivity and good thermal conductivity, by coating the metal sheath 2 with the material containing such a copper, it is possible to improve thermal instability inherent in the superconducting wire. Incidentally, as the material containing copper, either copper alone or a copper compound (copper alloy etc.) may be used. Further, as the material containing copper, a combination of copper alone and the copper compound may be used.
The superconducting wire 10 is obtained by firing a precursor of the superconducting wire 10. Hereinafter, a fabrication method of the superconducting wire 10 will be described, while describing firing conditions and physical properties of the precursor.
As the precursor, either a precursor A or a precursor B below is used. That is, the precursor A is a precursor, wherein the magnesium diboride core 1 constituting the superconducting wire 10 is formed by firing after filling magnesium and boron into the metal sheath 2, wherein the boron is crystalline, and wherein a volume average particle diameter of the boron is 2 μm or less.
Conventionally, so-called in-Situ method of firing after filling a mixture of magnesium and boron into the metal sheath has been used. However, according to this method, during reaction by firing magnesium and boron in the metal sheath, they shrink. As a result, since the packing density in the metal sheath is reduced (that is, many voids are present in some cases), the critical current density of the superconducting wire to be obtained has been low in some cases.
Further, conventionally, so-called ex-Situ method, in which after obtaining magnesium diboride by firing a mixture of magnesium and boron in advance, the obtained magnesium diboride is filled in the metal sheath, has also been used. However, according to this method, even in a case that magnesium diboride is filled in the metal sheath and extended, mutual electrical coupling of magnesium diboride has not been good in some cases. As a result, the critical current density of the superconducting wire has been low in some cases. Further, since the hardness of magnesium boride is high, when coarse magnesium diboride is present in the metal sheath, such magnesium diboride has excessively bitten into the metal sheath in some cases. As a result, the superconducting wire cannot be extended to a sufficient length during extending, and it has sometimes been cut off in the middle.
However, in the precursor A, crystalline boron with a volume average particle diameter of 2 μm or less is used as a part of the raw material. Therefore, also by the in-Situ method, it is possible to suppress volume shrinkage of the raw material powder in the metal sheath 2. This can make it possible to reduce an amount of voids which may be formed after firing. Therefore, there is no possibility that the critical current density of the superconducting wire 10 to be obtained becomes too low.
There is no particular limitation on an amount of magnesium and boron contained in the precursor A. However, based on the composition of magnesium diboride to be formed, it is preferred that 1 mol of magnesium per 2 mol of boron is filled in the metal sheath 2.
Further, as the precursor, the precursor B is a precursor, wherein the magnesium diboride core 1 constituting the superconducting wire 10 is formed by firing after filling magnesium, boron, and magnesium diboride into the metal sheath 2, and wherein a volume average particle diameter of magnesium diboride to be filled in the metal sheath 2 is 10 μm or less.
In the precursor B, as the raw material to form the magnesium diboride core 1, magnesium diboride with a volume average particle diameter of 10 μm or less is also used in addition to boron and magnesium. Magnesium diboride hardly shrinks any more even when fired. Therefore, it is possible to reduce the amount of voids which may be formed by performing the in-Situ method with magnesium and boron as the raw material. This can reduce the voids in the metal sheath 2, thereby increasing the packing density. As a result, an excellent critical current density of the superconducting wire 10 can be obtained.
However, in the present specification, “volume average particle diameter” is a value defined by the following equation (1). That is, it can be calculated from a particle size distribution measured by a particle size distribution measuring apparatus (for example, LA950 manufactured by HORIBA, Ltd.). The measurement principle is based on laser diffraction scattering method. A volume average particle diameter MV is an average value of particle diameters which are weighted by volumes. That is, if each volume of n pieces of particles is assumed to be Vi (i=1, 2, 3, - - - , n) and each diameter of the particles is assumed to be di, the volume average particle diameter MV is calculated by the following equation (1).
MV=(d1·V1+d2V2+ - - - +dn·Vn)/(V1+V2+ - - - +Vn) (1)
Magnesium diboride with a volume average particle diameter of 10 μm or less is obtained (prepared) by classification using a sieve after grinding solid magnesium diboride. It is sufficient to obtain a mixture by mixing magnesium, boron, and magnesium diboride which is prepared in this manner, and fill the mixture into the metal sheath 2.
There is no particular limitation on an amount of magnesium and boron contained in the precursor B. However, based on the composition of magnesium diboride to be formed, it is preferred that 1 mol of magnesium per 2 mol of boron is filled in the metal sheath 2. Further, an amount of magnesium diboride contained in the precursor B is not particularly limited. However, in the raw material powder to be filled in the metal sheath 2 constituting the precursor B, it is preferred that content of magnesium diboride is 50 mass % or more and 90 mass % or less. By using such a composition, it is possible to obtain the superconducting wire 10 having a higher critical current density. Incidentally, magnesium diboride used as the raw material is, for example, obtained by mixing magnesium and boron, and firing them in an inert atmosphere.
Further, in magnesium diboride to be filled in the metal sheath 2 constituting the precursor B, a part of boron atom sites of magnesium diboride contained may be substituted with carbon atom. By using such a material, it is possible to increase the critical current density in the high magnetic field region of the superconducting wire to be obtained. Such magnesium diboride whose part is substituted can be prepared by the method and material described in the above [1. Superconducting wire]. Further, the reason why the critical current density is increased is similar to the reason described in the above [1. Superconducting wire].
Primary structures of the precursor A and the precursor B are as described above, however, in either the precursor A or the precursor B, other optional components may be used in any amount as the raw material to be filled. Such components include, for example, a material (carbon source) containing carbon such as boron carbide.
Further, there is no particular limitation on the structure of the metal sheath 2 in the precursor A and the precursor B. Therefore, it is sufficient to apply the same structure as the metal sheath 2 described in [1. Superconducting wire]. That is, the metal sheath 2 preferably contains one or more metals selected from a group consisting of iron, niobium, tantalum, and titanium. Further, the outer surface of the metal sheath 2 is preferably coated with a material containing copper.
By firing the precursor A or the precursor B having the structure described above, the superconducting wire 10 is obtained. Note that, the superconducting wire 10 can also be obtained by firing a precursor having physical properties of both the precursor A and the precursor B. Before firing, the precursor A or the precursor B is linearized by an area reduction process so that the superconducting wire 10 to be obtained has a desired length and thickness. Then, the linearized precursor A or precursor B is subjected to firing.
Conditions during firing are not particularly limited. For example, it is sufficient to obtain the precursor A or the precursor B, and arrange the obtained precursor A or the precursor B in an electric furnace, and then carry out firing at a predetermined temperature and for a predetermined time. Such temperature and time can be, for example, 800° C. and 12 hours. Temperature may be changed stepwise, or may be always constant. Further, an atmosphere during firing is not particularly limited, either. The atmosphere can be, for example, an inert atmosphere such as argon, nitrogen, or the like.
By the method described above, the superconducting wire 10 can be obtained. In particular, the fabrication method of the precursor B is summarized as follows. That is, the precursor B is obtained by going through at least the following steps, a step of obtaining magnesium diboride by mixing and firing magnesium and boron, a step of preparing the obtained magnesium diboride so that a volume average particle diameter thereof is 10 μm or less, a step of obtaining a mixture by mixing magnesium, boron, and magnesium diboride with a volume average particle diameter of 10 μm or less, and a step of fabricating a wire by the area reduction process after filling the mixture into the metal sheath 2.
The superconducting wire 10, which is obtained by firing the precursor A or the precursor B, has a high critical current density, for example, even in high temperature range of 20 K or so. Therefore, by using such a superconducting wire 10, it is possible to drive more easily and inexpensively a superconducting magnet which is applied to a nuclear magnetic resonance analyzer, a medical magnetic resonance imaging diagnostic apparatus, or the like. That is, it is not necessary to cool to extremely low temperature by using expensive liquid helium for cooling the superconducting magnet, and it can be cooled by a refrigerator or the like. As a result, it is possible to reduce the running cost and manufacturing cost thereof.
Further, the above embodiment is described with an example of using a superconducting wire (single-core wire). However, a superconducting multi-core conductor can be, for example, formed by stopping once processing of the single-core wire at a thicker diameter thereof, and inserting such a plurality of single-core wires in the metal sheath by bundling them, and then performing the area reduction process. Further, for example, the superconducting multi-core conductor can also be formed by processing the single-core wire to a predetermined wire diameter, and twisting them together.
That is, the precursor A or the precursor B of the superconducting wire is obtained by the above-described fabrication method of the precursor A or the precursor B, and a precursor of the superconducting multi-core conductor can be obtained by twisting together the plurality of precursor A or precursor B of the superconducting wire. Then, by firing the precursor of the superconducting multi-core conductor which is obtained in this manner, the superconducting multi-core conductor can be obtained. Such superconducting multi-core conductor can have a current capacity higher than that of a superconducting single-core conductor (the superconducting wire 10 described above).
Hereinafter, the present embodiment will be described more specifically with examples.
A superconducting wire was produced by using magnesium powder, boron powder, and magnesium diboride powder as raw material powders. And, properties of the produced superconducting wire were evaluated.
The magnesium powder (Mg) with a volume average particle diameter of 40 μm was used. This volume average particle diameter was measured by the method described above. The same applies to the following materials. The boron powder (B) and the magnesium diboride powder (MgB2) are different for each superconducting wire which is produced, and those with volume average particle diameters listed in Table 1 below were used.
Note that, the magnesium diboride powder was obtained by mixing the magnesium powder with a volume average particle diameter of 40 μm and the boron powder with a volume average particle diameter of 2 μm, and filling them into a metal tube of material SUS304 and sealing both ends thereof, and then firing them in an argon atmosphere. Further, fine powders of the boron powder and the magnesium diboride powder were obtained by combining wet milling by a bead mill with dry milling by a planetary ball mill.
A composition was obtained by mixing the magnesium powder and the boron powder. The magnesium powder and the boron powder were mixed in a molar ratio of 1:2. Then, with this composition, the magnesium diboride powder obtained by the method described above was appropriately mixed so as to be each mixing ratio shown in Table 1. However, as for the superconducting wire of wire number 11, this composition was not used, but a composition of only magnesium diboride powder obtained by the method described above was used. Note that, “wt %” in Table 1 indicates “% by mass”.
The composition was filled in the metal sheath made of iron. An outer diameter of the metal sheath is 18 mm, and an inner diameter thereof is 13.5 mm. The metal sheath was thinned to a diameter φ0.5 mm by a drawing process, and a single-core wire was obtained. During the thinning, in wire #2 (wire number 2, the same for the other wires) and wire #5, the thinning was not easy, because breaking of wire occurred repeatedly during the drawing process. After all, a length of the wire has become shorter than that of other wires, although the wire was thinned to a diameter φ0.5 mm. As for the other wires, they were able to be thinned almost without breaking of wire.
By cutting off a length of 60 mm from the obtained single-core wire, and by firing it at 800° C. for 12 hours in an argon atmosphere, a powder filling portion of filament shape in the center was turned to magnesium diboride. That is, by firing, the superconducting wire 10 including the magnesium diboride core 1 shown in
With regard to the obtained superconducting wire 10, a relationship (Jc-B characteristics) between the critical current density (Jc (A/mm2)) and an external magnetic field (B (T)) at a temperature 20 K was evaluated by magnetization method. Specifically, the Jc-B characteristics was calculated by obtaining a magnetization curve by applying a magnetic field in a direction perpendicular to the longitudinal direction of the superconducting wire 10, and by applying an extended Bean model to an obtained magnetic hysteresis loop. Note that, the magnetization of the superconducting wire 10 was carried out by magnetic characteristic measuring apparatus MPMS of Quantum Design Japan, Inc.
Wires #3 and #4 use a raw material which is refined by grinding the crystalline boron powder used in wire #2. It can be seen that wires #3 and #4 has a critical current density higher than that of wire #1 particularly in a low magnetic field region (0T to about 2T). It is considered that this is because wires #3 and #4 use highly crystalline boron as the raw material.
That is, when using good crystalline boron, it is possible to obtain magnesium diboride having a small amount of voids as described below compared to when amorphous boron powder is used. When the amount of voids is small, since the superconducting current path is increased, the critical current density in the low magnetic field region is increased. On the other hand, when using good crystalline magnesium diboride, the critical current density in the high magnetic field region is reduced. It is considered that since magnesium diboride has good crystallinity in wires #3 and #4, ratios of reduction of the critical current density in the high magnetic field region in wires #3 and #4 are larger than that of wire #1. In other words, it can be said that by using good crystalline boron in wires #3 and #4, the critical current density in the low magnetic field region is good, although the critical current density in the high magnetic field region is reduced. Note that, the critical current density in the high magnetic field region can be improved by a method of <Example 2> to be described below.
From these results, it can be seen that the superconducting wire having a sufficiently high critical current density can be obtained by using the crystalline boron powder which is refined by grinding, without using a high-purity amorphous boron powder which is expensive and hard to obtain. Further, it can be seen that in the low magnetic field region, the critical current density higher than when using amorphous boron powder can be obtained.
From these results, it is found that even without using the high-purity amorphous boron powder which is expensive and hard to obtain, by adding the magnesium diboride powder with a volume average particle diameter of 10 μm or less in addition to the magnesium powder and the boron powder, it is possible to obtain a superconducting wire having a sufficiently high critical current density.
In particular, when the mixing ratio of magnesium diboride is 50 wt % to 90 wt % as shown by wires #6, #9, and #10, it can be seen that the increasing effect is high. Further, as for the superconducting wires used in the evaluation in
By the above results, it can be seen that it is possible to increase the critical current density of the super conducting wire which is obtained, by using the raw material of the crystalline boron powder having a volume average particle diameter of 2 μm or less, or by mixing the magnesium diboride powder having a volume average particle diameter of 10 μm or less with the raw material.
Next, for the purpose of obtaining universal characteristics for obtaining a superconducting wire of high performance magnesium diboride, the wires described above were analyzed in detail.
In wires #1, #3, #5, #6, and #8 to #11, by removing an iron sheath very carefully, a columnar magnesium diboride core inside was taken out. The size and mass of the magnesium diboride core taken out were measured. A core density ρ of magnesium diboride is defined as a value obtained by dividing the mass of the magnesium diboride core by a volume thereof.
Further, in wires #6 and #8 to #11 which are mixed with the magnesium diboride powder, it is observed that the core density ρ is further increased. The density of magnesium diboride is as large as 2.62 g/cm3, whereas the density of magnesium is 1.74 g/cm3 and the density of crystalline boron is 2.37 g/cm3. Therefore, volume shrinkage occurs during firing, and the voids are formed in the magnesium diboride core. However, in these wires, it is considered that since magnesium diboride was mixed with the raw material in advance, an amount of the volume shrinkage was effectively reduced.
However, as for wire #5 in which the particle diameter of the magnesium diboride powder is large, the core density ρ thereof is lower than that of wire #3 which is not mixed with the magnesium diboride powder. It is considered that this is because the coarse magnesium diboride powder reduces the packing density.
As described above, by using as the raw material the crystalline boron powder having a volume average particle diameter of 2 μm or less, or by mixing the magnesium diboride powder having a volume average particle diameter of 10 μm or less with the raw material, the critical current density of the superconducting wire is improved. The reason is considered as follows. That is, it is considered that the current path is increased because the core density ρ is increased, and as a result, the critical current density is improved.
When using the amorphous boron powder as the raw material, and not using the magnesium diboride powder, the packing ratio of the precursor of the superconducting wire into the metal sheath is about 90% even at the maximum. The density of magnesium is 1.74 g/cm3, and the density of amorphous boron is 1.7 g/cm3. That is, when filling magnesium and amorphous boron into the metal sheath, in view of the fact that the voids of about 34% are formed due to the packing ratio (about 90%) and the volume shrinkage associated with firing, the density of the magnesium diboride core obtained after firing is about 1.5 g/cm3 even at the maximum. The density of crystalline boron is greater than that of amorphous boron. Therefore, the density of the magnesium diboride core of the superconducting wire which is obtained from the raw material of crystalline boron is 1.5 g/cm3 or more. In other words, by using the crystalline boron powder, it is possible to increase the density of the magnesium diboride core as compared with a case of using the amorphous boron powder.
Further, wire #11 has a relatively high core density ρ, however, the critical current density thereof is low and the variation thereof is large. In order to clarify the reason, longitudinal cross-sections of wires #4 and #11 were observed by a scanning electron microscope (SEM). The results are schematically shown in
Note that, in order to observe the longitudinal cross-section by the SEM, after embedding the wire in resin, the longitudinal cross-section was obtained by cutting the wire in the current flow direction thereof by dry grinding, and the obtained longitudinal cross-section was further smoothed by ion milling, to observe a state thereof.
As shown in
The voids 4, which have angles θ larger than 45° and sizes not negligible compared to the diameter of the magnesium diboride core 1, narrow the current path locally. It is considered that such voids 4 cause a variation of the critical current density in addition to a decrease of the critical current density. Therefore, a reason why the critical current density of wire #11 is low is due to the fact that there are many voids 4 having angles of 45° or more.
Further, the boundary surface 5 between the magnesium diboride core 1 and the metal sheath 2 is linear, with exceptions of wires #2 and #5 in which breaking of the wires occurred. That is, in
Breaking of wires #2 and #5 is considered to be due to such a large undulation. That is, it is considered that a portion of locally thin thickness (weak strength) is formed in the metal sheath 2, and the portion became a starting point to cause breaking of the wire. Therefore, in order to obtain the superconducting wire of a long wire length, it is important that the boundary surface 5 between the magnesium diboride core 1 and the metal sheath 2 is linear. Here, “linear” means that the distance between the boundary curve 5 and the approximate straight line 6 is 10 μm or less.
Further, in wires #2 and #5 in which breaking of the wires occurred, the sizes of magnesium diboride 7 and boron 8 shown in
Note that, magnesium 9 shown in
As the raw materials, the magnesium powder, the boron powder, the magnesium diboride powder, and the boron carbide (B4C) powder were prepared. The volume average particle diameters of the magnesium powder, the boron powder, the magnesium diboride powder, and the boron carbide powder are respectively 40 μm, 2 μm, 10 μm, and 0.05 μm. Note that, the magnesium diboride powder was prepared by the same method as Example 1 described above, after mixing the magnesium powder with a volume average particle diameter of 40 μm, the boron powder with a volume average particle diameter of 2 μm, and the boron carbide powder with a volume average particle diameter of 0.05 μm in a molar ratio of 1:1.9:0.02.
Then, the magnesium powder, the boron powder, the boron carbide powder, and the obtained magnesium diboride powder were mixed together. In the mixed powders, the composition of these is 1:1.9:0.02:1 as a molar ratio. By using the mixed powders, superconducting wire #6C was obtained by the same method as Example 1 described above. Note that, the superconducting wire #6C is a wire that boron carbide is added to the above-described wire #6. With regard to the obtained superconducting wire #6C, the Jc-B characteristics were evaluated by the same method as Example 1.
The result is shown in
It is considered that this result is because a part of boron atom sites of magnesium diboride is substituted with carbon atom and thus a lattice distortion occurs. Then, it is considered that this result is because such a lattice distortion occurs and thus a coherence length is reduced and a pinning force in a grain boundary is increased. As described above, by adding to the raw material powder a material containing carbon in boron carbide or the like, it was found that the critical current density in the high magnetic field region can be improved. That is, it was found that the superconducting wire having a high critical current density in the magnetic field region of a wider range can be obtained.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2012-101572 | Apr 2012 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2013/062185 | 4/25/2013 | WO | 00 |